Vacuum arc remelting apparatus and process

Information

  • Patent Grant
  • 6295309
  • Patent Number
    6,295,309
  • Date Filed
    Thursday, August 31, 2000
    24 years ago
  • Date Issued
    Tuesday, September 25, 2001
    23 years ago
Abstract
A VAR process is conducted in an apparatus characterized by a crucible wall that provides a stable shelf anchor. The VAR apparatus includes a furnace chamber, a consumable electrode formed of a material to be remelted within the furnace chamber and a crucible within the furnace chamber. The crucible has a wall that forms a vessel to collect melt material from the consumable electrode. At least part of the wall is textured to provide area for mechanical stabilization of the shelf as the underside of the shelf melts and the upperside of the shelf forms. In a vacuum arc remelting process, a consumable electrode is loaded into a furnace chamber above a cooled crucible having a textured wall that forms a vessel to collect melt material from the consumable electrode. The process includes striking a direct electric current between the electrode and a bottom of the crucible to cause melting of material from a tip of the electrode. Melt material is collected from the tip in the crucible. The melt material is cooled to form an ingot characterized by a shelf of solidified material forming adjacent the textured section of the crucible wall in advance of a lower boundary of solidifying material.
Description




BACKGROUND OF THE INVENTION




The present invention relates to a vacuum arc remelting (“VAR”) apparatus and process.




VAR is a process for controlled solidification of segregation-sensitive alloys. In the process, a cylindrically shaped, alloy electrode is loaded into a water-cooled, copper crucible of a furnace. The furnace is evacuated and a dc electrical arc is struck between the electrode (cathode) and some start material at the bottom of the crucible (anode). The arc heats both the start material and the electrode tip, eventually melting both. As the electrode tip is melted away, molten metal drips into the crucible below. The process maintains a liquid melt pool that extends down to a mushy region, which is a transition zone to a fully solidified ingot. The crucible diameter is larger than the electrode diameter. Consequently, the ever-shrinking electrode can be translated downwards toward the anode pool surface to keep constant a mean distance between the electrode tip and the pool. The mean distance from the electrode tip to the liquid metal pool surface is called the electrode gap (g


e


).




As cooling water extracts heat from the crucible wall, molten metal next to the wall solidifies. A solid layer of material solidifying against the crucible wall near the pool surface is called a “shelf.” At some distance below the molten pool surface, material becomes completely solidified, yielding a fully dense alloy ingot. After a sufficient period of time has elapsed, a steady-state situation evolves, consisting of a shelfed “bowl” of molten material situated on top of a fully solidified ingot base.




VAR converts material electrodes into ingots having refined grain size and improved chemical and physical homogeneity. VAR is particularly suited to melting nickel-based “superalloys” (such as Alloy 718). These materials contain substantial quantities of reactive elements. VAR reduces contained gases, especially hydrogen and oxygen, non-metallic inclusions and center porosity and segregation. Mechanical properties of the remelted alloy, such as ductility and fatigue strength, are improved.




During the VAR process, volatile contaminate species such as manganese, aluminum and chromium evaporate. The vapor species of these elements condense on cold surfaces such as the area of a crucible wall immediately above the shelf of freezing material. Additionally as the electrode arc moves about the surface of the electrode, some particles splatter out of the melt pool and against the crucible wall where they can be trapped by the forming skin of the condensing vapor species.




As the shelf forms, high-melting-point solute-lean material is the first liquid metal to freeze against the condensed volatile species and splatter that covers the crucible wall. Additionally, as a melt proceeds, oxide and nitride inclusions present on the surface of the liquid metal pool are commonly pushed off to the sides of the melt pool and are frozen into solidified material at the shelf.




As the electrode melts off and liquid metal fills the crucible, the ingot shelf melts from the underside while a new shelf forms on the upperside. If a steady state of melting and shelf forming is maintained, then the shelf progressively forms and melts and progresses upward with the surface of the melt pool. So long as the steady state persists, the shelf acts as a barrier between the freezing melt splatter and condensing vapor species against the crucible wall. However if the steady state cannot be maintained, the shelf becomes unstable, breaks off and falls into the melt pool, dragging along vapor species skin, splatter and high-melting-point solute-lean material. The solute-lean material will appear in the ingot as a shiny “white spot.” If the solute-lean material is accompanied by oxide species then the solute-lean material appears as a “dirty white spot.” These areas of solute-lean material and oxide species are sites for early failure initiation, resulting in reduced life of parts made from the material.




There is a need for a VAR furnace and process that avoid contamination of the melt with areas of splatter and oxide species.




BRIEF SUMMARY OF THE INVENTION




The invention provides a VAR process and furnace that avoid contamination by stabilizing the ingot shelf to prevent abrupt fracture. The VAR process is conducted in an apparatus of new design characterized by a crucible wall that provides an anchor so that the shelf does not become unstable. The VAR apparatus comprises a furnace chamber, a consumable electrode formed of a material to be remelted within the furnace chamber and a crucible within the furnace chamber. The crucible comprises a wall that forms a vessel to collect melt material from the consumable electrode. The wall is textured to provide increased surface area to mechanically stabilize solidifying melt material.




A vacuum arc remelting process comprises loading a consumable electrode into a furnace chamber above a cooled crucible comprising a textured wall that forms a vessel to collect melt material from the consumable electrode. The process includes striking a direct electric current between the electrode and a bottom of the crucible to cause melting of material from a tip of the electrode. Melt material is collected from the tip in the crucible. The melt material is cooled to form an ingot characterized by a shelf of solidified material forming adjacent the textured wall of the crucible in advance of a lower boundary of solidifying material.











BRIEF DESCRIPTION OF THE DRAWINGS





FIG. 1

is a schematic cut-away representation of a VAR furnace;





FIG. 2

is a schematic representation of a section of the furnace crucible wall and solidifying ingot;





FIG. 3

is a schematic top view of a grooved crucible wall;





FIG. 4

is a schematic top view of the grooved crucible wall with a portion of solidifying ingot;





FIG. 5

is a schematic elevation of a portion of a grooved crucible wall;





FIG. 6

is a top schematic view of the full circumference of a crucible;





FIG. 7

is a schematic representation of a section of a textured furnace crucible wall and solidifying ingot;





FIG. 8

is a photograph of the surface of an ingot with a test pattern of rib indentations; and





FIGS. 9

,


10


,


11


and


12


are schematic representations of alternative textured walls.











DETAILED DESCRIPTION OF THE INVENTION




In accordance with the invention, a VAR crucible wall is textured to provide increased surface area for mechanical stabilization of the shelf as the underside of the shelf melts and the upperside of the shelf forms. A textured surface is an uneven or disturbed surface that provides an increased surface area over a plane surface. The surface may be grooved as shown or patterned or corrugated with alternating ridges and ribs. The surface may be characterized by flutes, pleats, impressions such as grooves or indents or the surface can be contoured with furrows, ripples or ridges.




These and other features will become apparent from the drawings and following detailed discussion, which by way of example without limitation describe preferred embodiments of the present invention.




FIG,


1


is a schematic cut-away representation of a VAR furnace


10


and

FIG. 2

is a schematic representation of a section of the furnace crucible wall


381


showing a portion of a solidifying ingot. In

FIGS. 1 and 2

, a cylindrically shaped, alloy electrode


12


is loaded into the furnace chamber


14


above a water-cooled, copper crucible


16


. The furnace


10


includes direct current source


18


, vacuum port


20


, cooling water guide


22


, ram drive screw


24


and ram drive motor assembly


26


.




Referring to FIG.


1


and

FIG. 2

, in operation, the furnace chamber


14


is evacuated and a direct current (dc) electrical arc is struck between the electrode (cathode)


12


and start material (e.g., metal chips) at the bottom (anode) of the crucible


16


. An arc heats both the start material and electrode tip


28


, eventually melting both. As the electrode tip


28


is melted away, molten metal drips off, forming a melt pool


30


beneath. Because the crucible diameter is typically 50-150 mm larger than the electrode diameter, the electrode


18


can be translated downward toward the anode pool to maintain a mean distance between the electrode tip


28


and pool surface


32


.




As cooling water


36


extracts heat from crucible wall


38


, molten metal next to the wall solidifies. At some distance below the molten pool surface, the alloy becomes completely solidified, yielding a fully dense ingot


40


. After a period of time, a steady-state situation evolves characterized by a “bowl” of molten material situated on top of a fully solidified ingot base. The ingot


40


grows as more material solidifies.




As a melt proceeds, oxide and nitride inclusions present in the electrode float to the surface


32


of molten pool


30


. The oxides and nitride species are commonly pushed off to the sides of the melt pool


30


and are frozen into solidified material at the shelf


42


, which comprises solidified material at the melt interface directly below the melt pool surface


32


. Directly above the shelf


42


, splash and vapor species condensation forms a crusty ledge called the crown


44


.




During the melt sequence, conditions can cause the shelf


42


or crown


44


to become detached from the crucible wall


38


. The shelf


42


collapses and shelf material and crown material fall into the molten pool


30


. The materials can sink into the molten pool, where the shelf material becomes remelted leaving the crown oxide and nitride material as clustered defects. Or if the shelf is large in mass, it may be only partially remelted so that it freezes with oxide or nitride species attached.





FIGS. 3

,


4


,


5


,


6


and


7


illustrate a crucible wall


38


provided with a textured surface


52


according to the invention.

FIG. 3

is a schematic top view of a grooved crucible wall


38


.

FIG. 4

is a schematic representation of a section of the furnace crucible wall


38


, textured crucible wall surface


52


and solidifying ingot


40


.

FIG. 5

is a schematic elevation of a portion of a grooved crucible wall


38


.

FIG.6

is a schematic top view of the full circumference of a crucible where the textured surface


52


is provided by vertical grooves


46


.

FIG. 7

is a schematic top view of a section of a crucible


16


where the textured surface


52


is provided by vertical grooves


46


. In the FIGS., the crucible wall


38


is textured such that a supporting ligament or series of supporting ligaments solidify between the shelf and the underlying ingot. The ligaments provide for mechanical stabilization of the shelf as the underside of the shelf melts and the upperside of the shelf forms. Textured freezing surface of the ingot that is complementary to the textured wall surface


52


supports and mechanically stabilizes the shelf. The textured surface


52


also increases heat extraction from the forming shelf because of increased contact area between the water-cooled copper and the liquid metal pool. Increased heat extraction increases the thickness of the shelf and strengthens and further stabilizes the shelf. The thicker, supported and more stable shelf resists abrupt fracture and consequent contamination of the freezing ingot.




Shown in

FIGS. 3

,


4


,


5


,


6


and


7


is crucible wall


38


with grooves


46


, which comprise sloped side walls


48


and flattened bottoms


50


that impose into the otherwise planer crucible wall surface


52


. The shape, depth and spacing of the grooves


46


are chosen such that they readily fill with liquid metal, solidify into ribs, and do not completely re-melt as the shelf


42


melts from the underside and forms on the upperside.




The grooves


46


can be angled outwardly from a vertical line perpendicular to the base of the groove and grove corners can be rounded to allow for ease of groove fill and ease of ingot withdrawal from the crucible after solidifying the ingot. The grooves


46


can be angled at up to about 60° from the vertical and desirably from about 5 to 30 degrees from vertical. Preferably, the grooves


46


can be angled from about 10 to 20 degrees from vertical.




For any texture configuration, sharp comers can be rounded to provide for ease of ingot withdrawal and to prevent sharp comers on the resulting ingot. A measure of rounding can be described by the radius of the round comer measured from inside the arc of rounding. A wide range of radii for comer rounding is acceptable, up to ½ times groove width, desirably from about ⅛ to ½ times the groove and preferably from about ¼ to ½ times the groove width.




The groove shape can vary from rectangular to trapezoidal to semicircular. All shapes that fill readily and allow for withdraw of the ingot


40


from the crucible


16


after complete solidification of the ingot are acceptable. The groove depth can range from ⅛ to ¾ inch, with a preferred range from about ¼ to ½ inch. Typical groove widths can range from about ⅛ to 2 inches, with a preferred range from about ¼ to ½ inch. In most instances, the size of the groove will vary with the size of the crucible. Proportion of depth or width of grooves to crucible circumference can vary from about 0.001 to 0.05, desirably about 0.002 to 0.04 and preferably from about 0.006 to 0.02 and frequency of grooves per inch of inside circumference can vary from about 0.1 to 5, desirably about 0.3 to 4, and preferably 0.5 to 3.





FIGS. 3

,


4


,


5


,


6


and


7


illustrate a preferred embodiment, wherein the crucible wall


38


is grooved with trapezoidal grooves


46


. Other shapes varying from rectangular to semicircular can be used. For example, all shapes that fill readily and allow for withdraw of the ingot from the crucible after complete solidification of the ingot are acceptable.




These and other features will become apparent from FIG.


8


and the following detailed discussion, which by way of example without limitation describe a preferred embodiment of the present invention.




EXAMPLE





FIG. 8

is a photograph of a surface of an Alloy 718 (approximately Ni, 19% Cr, 18% Fe, 5% Nb, 3% Mo, 1% Ti, 0.6% Al) superalloy ingot solidified under standard commercial VAR melting conditions with a small test patch formed using a preferred version of the invention as an example. In this Example, an upper portion of a standard commercial-grade 20-inch diameter VAR crucible was modified to include two 90-degree arc textured wall test sections, separated by two 90-degree arc smooth-wall comparison sections.




The texture in the crucible wall was provided by a series of vertical grooves approximately ¼ inch deep by ¼ inch wide occurring at a spacing of one per ½ inch of inside circumference of the crucible wall. The depth and width were chosen such that the ribs that solidify within the grooves do not remelt as the liquid metal in the crucible rises. The frequency of position on the inside circumference was chosen to give rigid stabilization of the remelting shelf. The sidewall grooves were angled at approximately 14 degrees outward from a vertical line perpendicular to the base of the groove and grove comers were rounded to allow for ease of fill of the grooves with liquid metal and ease of ingot withdrawal from the crucible after solidifying the ingot.




The process was observed to produce a stabilized shelf during the molding process and the Alloy 718 casting shown in

FIG. 8

was characterized by lessened white spots and dirty white spots as compared to an ingot molded in a furnace without a textured wall.




While preferred embodiments of the invention have been described, the present invention is capable of variation and modification and therefore should not be limited to the precise details of the Example. For example, the invention can be used in conjunction with a process to mold any suitable material such as a highly-alloyed iron base steel or a highly alloyed titanium such as Ti-17 (Ti, 5% Al, 4% Cr, 4% Mo, 2% Sn, 2% Zr).

FIGS. 9

,


10


,


11


and


12


show further examples of textured wall surface


52


.

FIG. 9

shows a crevice


56


and peak


58


texture,

FIG. 10

shows a peak


58


with flattened bottom


50


,

FIG. 11

shows flattened top


60


with crevice


56


and

FIG. 12

shows another preferred structure comprising a rounded undulating topography


62


. The invention includes all changes and alterations that fall within the purview of the following claims.



Claims
  • 1. A vacuum arc remelting apparatus, comprising:a furnace chamber; a consumable electrode formed of a material to be remelted within said furnace chamber; and a crucible within said furnace chamber, said crucible comprising a wall that forms a vessel to collect melt material from said consumable electrode, wherein said wall is textured to provide increased surface area to mechanically stabilize solidifying melt material.
  • 2. The apparatus of claim 1, wherein said textured wall provides anchoring of a shelf of said solidifying melt material.
  • 3. The apparatus of claim 1, wherein said textured wall comprises an uneven or disturbed surface that provides an increased surface area over a plane surface.
  • 4. The apparatus of claim 1, wherein said textured wall comprises a ribbed, patterned or corrugated surface with alternating ridges and grooves.
  • 5. The apparatus of claim 1, wherein said textured wall comprises flutes, pleats, impressions, indents or grooves.
  • 6. The apparatus of claim 1, wherein said textured wall is contoured with furrows, ripples or ridges.
  • 7. The apparatus of claim 1, wherein said textured wall is contoured with substantially vertical grooves.
  • 8. The apparatus of claim 1, wherein said textured wall is contoured with grooves angled less than 60° from vertical.
  • 9. The apparatus of claim 1, wherein said textured wall is contoured with grooves angled about 10 to 20 degrees from vertical.
  • 10. The apparatus of claim 1, wherein said textured wall is contoured with substantially vertical grooves having a groove depth of from about ⅛ to ¾ inch, a width of from about ⅛ to 2 inches and a groove spacing of from about ⅜ to 4 inches.
  • 11. The apparatus of claim 1, wherein said textured wall is contoured with substantially vertical grooves having a groove depth of from about ¼ to ½ inch, a width of from about ¼ to ½ inch and a groove spacing from spacing from about ½ to ¾ inches.
  • 12. The apparatus of claim 1, wherein said textured wall is contoured with substantially vertical grooves that are rounded up to about ½ times the groove width.
  • 13. The apparatus of claim 1, wherein said textured wall is contoured with substantially vertical grooves that are rounded from about ¼ to ½ times groove width.
  • 14. The apparatus of claim 1, wherein said textured wall is contoured with substantially vertical grooves and proportion of depth or width of grooves to crucible circumference is from about 0.001 to 0.05 and frequency of grooves per inch of inside crucible circumference is from about 0.1 to 5.
  • 15. The apparatus of claim 1, wherein said textured wall is contoured with substantially vertical grooves and proportion of depth or width of grooves to crucible circumference is from about 0.002 to 0.04 and frequency of grooves per inch of inside crucible circumference is from about 0.3 to 4.
  • 16. The apparatus of claim 1, wherein said textured wall is contoured with substantially vertical grooves and proportion of depth or width of grooves to crucible circumference is from about 0.006 to 0.02 and frequency of grooves per inch of inside crucible circumference is from about 0.5 to 3.
  • 17. The apparatus of claim 1, wherein said textured wall comprises alternating crevices and peaks.
  • 18. The apparatus of claim 1, wherein said textured wall comprises alternating flattened bottoms and peaks.
  • 19. The apparatus of claim 1, wherein said textured wall comprises alternating flattened tops and crevices.
  • 20. The apparatus of claim 1, wherein said textured wall comprises a rounded undulating topography.
  • 21. A vacuum arc remelting process, comprisingloading a consumable electrode into a furnace chamber above a cooled crucible comprising a textured wall that forms a vessel to collect melt material from said consumable electrode; striking a direct electric current between said electrode and a bottom of said crucible to cause melting of material from a tip of said electrode; collecting melt material from said tip in said crucible; and cooling said melt material to form an ingot characterized by a shelf of solidified material forming adjacent said textured wall of said crucible in advance of a lower boundary of solidifying material.
  • 22. The process of claim 21, wherein said textured wall stabilizes said shelf to prevent abrupt dislodging of said shelf from said wall.
  • 23. The process of claim 21, wherein said textured wall comprises an uneven or disturbed surface that provides an increased surface area over a plane surface.
  • 24. The process of claim 21, wherein said textured wall is contoured with substantially vertical grooves.
  • 25. The process of claim 21, wherein said textured wall is contoured with grooves angled less than 60° from vertical.
  • 26. The process of claim 21, wherein said textured wall is contoured with grooves angled about 10 to 20 degrees from vertical.
  • 27. The process of claim 21, wherein said textured wall is contoured with substantially vertical grooves having a groove depth of from about {fraction (1/8)} to ¾ inch, a width of from about ⅛ to 2 inches and a groove spacing of from about ⅜ to 4 inches.
  • 28. The process of claim 21, wherein said textured wall is contoured with substantially vertical grooves having a groove depth of from about ¼ to ½ inch, a width of from about ¼ to ½ inch and a groove spacing from about ½ to ¾ inches.
  • 29. The process of claim 21, wherein said textured wall is contoured with substantially vertical grooves that are rounded up to about ½ times the groove width.
  • 30. The process of claim 21, wherein said textured wall is contoured with substantially vertical grooves that are rounded from about ¼ to ½ times groove width.
  • 31. The process of claim 21, wherein said textured wall comprises trapezoidal-shaped grooves at a frequency of a groove per about ⅜ inch to 4 inches of the inside crucible wall.
  • 32. The process of claim 21, wherein said textured wall comprises trapezoidal-shaped grooves and proportion of depth or width of grooves to crucible circumference is from about 0.001 to 0.05 and frequency of grooves per inch of inside crucible circumference is from about 0.1 to 5.
  • 33. The process of claim 21, wherein said textured wall comprises trapezoidal-shaped grooves and proportion of depth or width of grooves to crucible circumference is from about 0.002 to 0.04 and frequency of grooves per inch of inside crucible circumference is from about 0.3 to 4.
  • 34. The process of claim 21, wherein said textured wall comprises trapezoidal-shaped grooves and proportion of depth or width of grooves to crucible circumference is from about 0.006 to 0.02 and frequency of grooves per inch of inside crucible circumference is from about 0.5 to 3.
  • 35. The process of claim 21, wherein said textured wall comprises trapezoidal-shaped grooves at a frequency of a groove per about ½ inch to ¾ inch of the inside crucible wall.
  • 36. The process of claim 21, wherein said textured wall comprises alternating crevices and peaks.
  • 37. The process of claim 21, wherein said textured wall comprises alternating flattened bottoms and peaks.
  • 38. The process of claim 21, wherein said textured wall comprises alternating flattened tops and crevices.
  • 39. The process of claim 21, wherein said textured wall comprises a rounded undulating topography.
US Referenced Citations (6)
Number Name Date Kind
4450570 Weigartner et al. May 1984
4612649 Griebel, III et al. Sep 1986
5373429 Kasurinen Dec 1994
5610935 Auberger Mar 1997
5621751 Williamson et al. Apr 1997
5930284 Hysinger et al. Jul 1999