The invention relates to a valve for a high temperature liquid, more in particular liquid metal or a liquid of two or more metals.
In physical vapour deposition (PVD) a metal is vaporized and deposited on a substrate, such as a steel strip. In this process a liquid metal or a liquid of two or more metals is supplied to an evaporator in a vacuum chamber where it is vaporized. In PVD processes and more in particular in continuous or semi-continuous PVD processes on an industrial scale it is necessary to regularly supply liquid metal to the evaporator device to make up for the liquid metal evaporated from the evaporator.
For the supply of liquid metal to the evaporator a supply system is used comprising a feeding vessel with liquid metal, heated pipes between the vessel and evaporator, one or more valves to shut off and open the flow in the pipes and depending on the system one or more pumps to pump the liquid metal. The vessel with liquid metal is located outside the vacuum chamber.
In order to safely start and shut down the PVD installation it is essential that a valve is present in the piping between feeding vessel and the evaporator melt. This will assure that when the piping is empty the vacuum chamber will not be vented. Furthermore, during the shut down procedure or during an emergency situation the valve will make it possible to shut off the supply of liquid metal in a controlled and safe manner.
Liquid metal is used to provide an anti-corrosive coating on a steel strip and usually contains Zn or Zn and Mg which metals are both very reactive in the liquid phase. The material of the valve that comes into contact with the liquid ZnMg should not only be capable to withstand the corrosive action of this liquid metal but it should also be dense enough to prevent penetration of the liquid metal into the material, since such penetration could sooner or later lead to failure of the material.
Furthermore, it is not enough that the material of the valve is resistant against ZnMg. Oxides present on the material, formed by the material and any excess oxygen must be stable enough to liquid ZnMg to assure that the valve will continue to work.
It is an objective of the present invention to provide a valve that can be operated under high temperature conditions.
It is an objective of the present invention to provide a valve wherein the material of the valve is resistant against the corrosive action of liquid metal, more in particular liquid ZnMg.
It is another objective of the present invention to provide a valve wherein the material of the valve is dense enough to prevent penetration of the liquid metal into the material.
It is another objective of the present invention to provide a valve wherein the material of the valve is such that an oxide formed on the material will be stable under these conditions.
According to a first aspect of the invention one or more of the objectives of the invention are realized by providing a valve for high temperature liquid comprising a valve body, a valve seat, input and output connections, a valve closure member provided with a passageway, a valve cover member and a valve spindle connected to the valve closure member, wherein the parts of the valve that come into contact with the liquid are provided with a coating of a material or are made of a material that is resistant against the high temperature liquid.
To make a proper valve it is not only required that the used materials are resistant against liquid and or gaseous ZnMg, these materials should preferably also have the following features:
The list above has been used to select materials to produce valves from.
In a first embodiment according to the invention a valve is provided wherein the parts of the valve that come into contact with the liquid are provided with a coating selected from a group consisting of graphite, BN, ZrO, Al2O3 and Si3N4. The part to which the coating is applied is made from steel, stainless steel, bronze or any other metal or alloy that is strong enough at the specified temperature interval, does not react destructively with the coating and preferably can withstand atmospheric conditions.
In a second embodiment according the invention the valve closure member is made of graphite and the valve body is made of hot isostatic pressed boron nitride (HIP BN). The graphite is preferable a higher density grade of graphite, such as graphite with a porosity of 18% or less. Preferably graphite is used with a porosity lower than 18% in order to minimize penetration of ZnMg in the voids in the graphite as much as possible, for instance graphite with a porosity of 15% or 12% or even less. From the materials on the list these materials are the easiest to machine. It was found that a valve made of HIP BN parts that are to be moved with respect to each other will show fretting. Furthermore the thermal expansion of HIP BN is very anisotropic which will result in a valve that can not be operated at elevated temperatures. A valve made of a HIP BN and a high density graphite part has to proven to work but because of the use of graphite the working temperature of the valve is limited up to 500° C.
Furthermore by providing that the valve closure member of graphite is at least partially surrounded by HIP BN the oxidation of graphite, which will normally occur under atmospheric conditions, is suppressed. Because of this construction it is possible to use this valve under atmospheric conditions at temperatures up to 850° C.
For a valve with solid parts of a single material also Al2O3 could be used but this material has the disadvantage of a bad thermal shock resistance. Also Si3N4 could be used for the purpose but it is difficult to machine the material to the required dimensions for this kind of valve.
According to a further aspect of the invention it is provided that also the valve cover member is made of HIP BN. With a valve body and a valve cover member of HIP BN the graphite valve closure member is surrounded on all sides by HIP BN.
The invention will be further explained on hand of the example shown in the drawing, which shows a schematic drawing of the valve in cross-section.
The valve comprises a valve body 1 provided with an inlet connection 2 and an outlet connection 3 and a valve seat 4 which accommodates valve closure member 5. Valve closure member 5 is provided with a passageway which connects to inlet and outlet channels respectively when turned in a position corresponding with these channels. The valve closure member is provided with a spindle 6 which extends through valve cover member 7 and is to be operated by mechanical or electro-mechanical means. The valve closure member 5 is made from HIP BN and the valve body 1 and the valve cover member 7 from a high density graphite.
This is a two way valve but it is also possible to make a three way valve using the materials as disclosed.