Valve seats and valve assemblies for fluid end applications

Information

  • Patent Grant
  • 10954938
  • Patent Number
    10,954,938
  • Date Filed
    Friday, May 10, 2019
    5 years ago
  • Date Issued
    Tuesday, March 23, 2021
    3 years ago
Abstract
In one aspect, valve seats are described herein having structure and design addressing degradative stresses encountered by valve seats during installation and operation in fluid ends. In some embodiments, a valve seat for use in a fluid end comprises a first section for insertion into a fluid passageway of the fluid end and a second section extending longitudinally from the first section, the second section has an outer diameter greater than the outer diameter of the first section. The second section also comprises a frusto-conical valve mating surface, wherein the second section is encased in a ring imparting a compressive stress condition to the second section.
Description
FIELD

The present invention relates to valve seats and valve assemblies for fluid end applications and, in particular, to valve seats comprising sintered cemented carbide components.


BACKGROUND

Valves and associated valve assemblies play a critical role in fluid ends of high pressure pumps incorporating positive displacement pistons in multiple cylinders. Operating environments of the valves are often severe due to high pressures and cyclical impact between the valve body and the valve seat. These severe operating conditions can induce premature failure and/or leakage of the valve assembly. Moreover, fluid passing through the fluid end and contacting the valve assembly can include high levels of particulate matter from hydraulic fracturing operations. In hydraulic fracturing, a particulate slurry is employed to maintain crack openings in the geological formation after hydraulic pressure from the well is released. In some embodiments, alumina particles are employed in the slurry due to higher compressive strength of alumina relative to silica particles or sand. The particulate slurry can impart significant wear on contact surfaces of the valve and valve seat. Additionally, slurry particles can become trapped in the valve sealing cycle, resulting in further performance degradation of the valve assembly.


In view of these problems, valve seats have been fabricated from a variety of hard and wear resistant materials, including cemented carbide. While exhibiting high hardness and wear resistance, carbide valve seats can undergo occasional catastrophic failure due to stresses induced in the carbide from installation and removal forces, application loading and the press fit with the fluid end.


SUMMARY

In one aspect, valve seats are described herein having structure and design addressing degradative stresses encountered by the seats during installation and operation in fluid ends. In some embodiments, a valve seat for use in a fluid end comprises a first section for insertion into a fluid passageway of the fluid end and a second section extending longitudinally from the first section, the second section having an outer diameter greater than the outer diameter of the first section. The second section also comprises a frusto-conical valve mating surface, wherein the second section is encased in a ring imparting a compressive stress condition to the second section. In some embodiments, the second section is at least partially formed of sintered cemented carbide.


In another aspect, a valve seat comprises a first section for insertion into a fluid passageway of a fluid end and a second section extending longitudinally from the first section, the second section having an outer diameter greater than the outer diameter of the first section. The second section also includes a frusto-conical valve mating surface comprising sintered cemented carbide having surface roughness (Ra) of 1-15 μm. In some embodiments, the sintered cemented carbide of the valve mating surface is provided as an inlay ring coupled to a metal or alloy body. In other embodiments, the second section is formed of the sintered cemented carbide.


In another aspect, valve assemblies for use in fluid ends are provided. A valve assembly comprises a valve in reciprocating contact with a valve seat, the valve seat comprising a first section for insertion into a fluid passageway of the fluid end and a second section extending longitudinally from the first section. The second section has an outer diameter greater than the outer diameter of the first section and comprises a frusto-conical valve mating surface. The second section is also encased in a ring which imparts a compressive stress condition to the second section. In some embodiments, the second section is optionally encased in the ring, and the valve mating surface comprises sintered cemented carbide having surface roughness (Ra) of 1-15 μm. In other embodiments, the frusto-conical valve mating surface of the second section is provided as a sintered cemented carbide inlay coupled to a metal or alloy body, wherein the sintered cemented carbide has surface roughness (Ra) of 1-15 μm.


In a further aspect, fluid ends are described. A fluid end comprises a suction fluid passageway and a discharge fluid passageway. A valve assembly is positioned in at least one of the suction and discharge fluid passageways, the valve assembly comprising a valve in reciprocating contact with a valve seat. The valve seat comprises a first section for insertion into the suction or discharge fluid passageway and a second section extending longitudinally from the first section. The second section has an outer diameter greater than the outer diameter of the first section and comprises a frusto-conical valve mating surface. The second section is encased in a ring which imparts a compressive stress condition to the second section. In some embodiments, the second section is optionally encased in the ring, and the valve mating surface comprises sintered cemented carbide having surface roughness (Ra) of 1-15 μm. In other embodiments, the frusto-conical valve mating surface of the second section is provided as a sintered cemented carbide inlay coupled to a metal or alloy body, wherein the sintered cemented carbide has surface roughness (Ra) of 1-15 μm.


These and other embodiments are further described in the following detailed description.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is a cross-sectional schematic of a valve seat according to some embodiments.



FIG. 2 is a cross-sectional schematic of a valve seat according to some embodiments.



FIG. 3 is a bottom plan view of a valve seat according to some embodiments.



FIG. 4 is a top plan view of a valve seat according to some embodiments.



FIG. 5 is a perspective view of a valve seat according to some embodiments.



FIG. 6 is a side elevational view of a valve seat according to some embodiments.



FIG. 7 is a cross-sectional view of a sintered cemented carbide inlay according to some embodiments.



FIG. 8 is a cross-sectional view of valve seat comprising a sintered cemented carbide inlay coupled to an alloy body or casing according to some embodiments.





DETAILED DESCRIPTION

Embodiments described herein can be understood more readily by reference to the following detailed description and examples and their previous and following descriptions. Elements, apparatus and methods described herein, however, are not limited to the specific embodiments presented in the detailed description and examples. It should be recognized that these embodiments are merely illustrative of the principles of the present invention. Numerous modifications and adaptations will be readily apparent to those of skill in the art without departing from the spirit and scope of the invention.


In one aspect, valve seats for fluid end applications are described herein. In some embodiments, the valve seats can mitigate the severe operating conditions of hydraulic fracturing applications, leading to enhanced lifetimes and reductions in sudden seat failure. Referring now to FIG. 1, a valve seat 10 comprises a first section 11 for insertion into a fluid passageway of the fluid end. In the embodiment of FIG. 1, the first section 11 comprises a tapered outer surface 12 and an inner surface 13 that is generally parallel to the longitudinal axis 14 of the seat 10. In some embodiments, the inner surface 13 may also be tapered. The tapered outer surface 12 can present a variable outer diameter D1 of the first section 11. Alternatively, the outer surface 12 of the first section 11 is not tapered and remains parallel to the longitudinal axis 14. In such an embodiment, the first section 11 has a static outer diameter D1. The outer surface 12 of the first section may also comprise one or more recesses 15 for receiving an O-ring. One or more O-rings can aid in sealing with the fluid passageway wall.


A second section 16 is extends longitudinally from the first section 11. The second section has an outer diameter D2 that is larger than outer diameter D1 of the first section 11. A shoulder 17 is formed by the larger outer diameter D2 of the second section 16. In the embodiment of FIG. 1, the shoulder surface 17a is generally normal to the longitudinal axis 14 of the valve seat 10. In other embodiments, the shoulder surface 17a can taper and/or form an angle with the longitudinal axis having a value of 5-70 degrees. Design of the shoulder 17 can be selected according to several considerations including, but not limited to, entrance geometry of the fluid passageway and pressures experienced by the seat when in operation. In some embodiments, for example, taper of the shoulder can be set according to curvature of the fluid passageway entrance engaging the shoulder. The first section 11 transitions to the second section 16 at a curved intersection 18. The curved intersection can have any desired radius. Radius of the curved intersection, in some embodiments, can be 0.05 to 0.5 times the width of the shoulder. In other embodiments, a curved transition is not present between the first and second sections.


The second section 16 also comprises a frusto-conical valve mating surface 20, wherein the second section 16 is encased by a ring 19. In the embodiment of FIG. 1, the ring 19 is coupled to the outer surface of the second section 16 in a concentric arrangement. The ring 19 imparts a compressive stress condition to the second section 16. By placing the second section 16 in compressive stress, the ring 19 can assist in balancing or equalizing stress between the first section 11 and second section 16 when the first section 11 is press fit into a fluid passageway of the fluid end. A compressive stress condition can also inhibit crack formation and/or propagation in the second section 16, thereby enhancing lifetime of the valve seat and reducing occurrences of sudden or catastrophic seat failure. A compressive stress condition may also enable the use of harder and more brittle materials in the second section 16, such as harder and more wear resistant grades of cemented carbide forming the valve mating surface.


In the embodiment of FIG. 1, the ring 19 forms a planar interface with the outer surface or perimeter of the second section 16. In other embodiments, the ring 19 may comprise one or more protrusions or flanges residing on the inner annular surface of the ring 19. A protrusion or flange on the inner ring surface may fit into a recess or groove along the perimeter of the second section 16. This structural arrangement can assist in proper engagement between the ring 19 and second section 16. This structural arrangement may also assist in retaining the second section 16 within the ring 19 during operation of the fluid end. In a further embodiment, the second section 16 can comprise one or more protrusions of flanges for engaging one or more recesses in the interior annular surface of the ring 19.



FIG. 2 is a schematic illustrating another embodiment of a valve seat described herein. The valve seat of FIG. 2 comprises the same structural features illustrated in FIG. 1. However, the ring 19 in FIG. 2 at least partially covers the shoulder 17. The ring 19, for example, can be provided a radial flange 19a for interfacing the shoulder 17 of the second section 16. In some embodiments, the ring 19 fully covers the shoulder 17. FIG. 3 is a perspective view of a valve seat having the architecture of FIG. 2. As illustrated in FIG. 3, the ring 19 is coupled to the perimeter of the second section and partially covers the shoulder 17. FIG. 4 is another perspective view of a valve seat having the architecture of FIG. 2. The frusto-conical valve mating surface 20 transitions into the bore 21 of the valve seat 10. The ring 19 encases the second section 16, imparting a compressive stress condition to the second section 16. Accordingly, a compressive stress condition is imparted to the valve mating surface 20, which can assist in resisting crack formation and/or crack propagation in the mating surface 20. FIGS. 3 and 4 illustrate bottom and top plan views of the valve seat of FIG. 2 respectively. Moreover, FIG. 5 illustrates a perspective view of the valve seat of FIG. 2. FIG. 6 illustrates a side elevational view of a valve seat according to some embodiments, wherein a curved intersection does not exist between the first section 11 and second section 16.


As described herein, the valve seat can comprise sintered cemented carbide. In some embodiments, the first and second section of the valve seat are each formed of sintered cemented carbide. Alternatively, the first section can be formed of metal or alloy, such as steel or cobalt-based alloy, and the second section is formed of sintered cemented carbide. Forming the second section of sintered cemented carbide can impart hardness and wear resistance to the valve mating surface relative to other materials, such as steel.


In some embodiments, the second section is formed of a composite comprising sintered cemented carbide and alloy. For example, a sintered cemented carbide inlay can be coupled to a steel substrate, wherein the sintered cemented carbide inlay forms a portion or all of the valve mating surface, and the steel substrate forms the remainder of the second section. In such embodiments, the sintered carbide inlay can extend radially to contact the ring encasing the second section, thereby permitting the ring to impart a compressive stress condition to the sintered carbide inlay. In other embodiments, the steel or alloy substrate comprises a recess in which the sintered carbide inlay is positioned. In this embodiment, the outer rim of the recess is positioned between the sintered carbide inlay and ring, wherein compressive stress imparted by the ring is transmitted through the outer rim to the sintered carbide inlay.


Sintered cemented carbide of the valve seat can comprise tungsten carbide (WC). WC can be present in the sintered carbide in an amount of at least 70 weight percent or in an amount of at least 80 weight percent. Additionally, metallic binder of cemented carbide can comprise cobalt or cobalt alloy. Cobalt, for example, can be present in the sintered cemented carbide in an amount ranging from 3 weight percent to 20 weight percent. In some embodiments, cobalt is present in sintered cemented carbide of the valve seat in an amount ranging from 5-12 weight percent or from 6-10 weight percent. Further, sintered cemented carbide valve seat may exhibit a zone of binder enrichment beginning at and extending inwardly from the surface of the substrate. Sintered cemented carbide of the valve seat can also comprise one or more additives such as, for example, one or more of the following elements and/or their compounds: titanium, niobium, vanadium, tantalum, chromium, zirconium and/or hafnium. In some embodiments, titanium, niobium, vanadium, tantalum, chromium, zirconium and/or hafnium form solid solution carbides with WC of the sintered cemented carbide. In such embodiments, the sintered carbide can comprise one or more solid solution carbides in an amount ranging from 0.1-5 weight percent.


In some embodiments, a single grade of sintered cemented carbide can be employed to form the first and second sections of the valve seat. In other embodiments, one or more compositional gradients can exist between sintered cemented carbide of the first section and second section. For example, sintered cemented carbide of the first section may have larger average grain size and/or higher metallic binder content to increase toughness. In contrast, sintered cemented carbide of the second section may have smaller average grain size and less binder for enhancing hardness and wear resistance. Additionally, a compositional gradient can exist within the first and/or second section of the valve seat. In some embodiments, sintered cemented carbide forming the valve mating surface comprises small average grain size and lower metallic binder content for enhancing hardness and wear resistance. Progressing away from the valve mating surface, the sintered cemented carbide composition of the second section can increase in grain size and/or binder content to enhance toughness and fracture resistance. In some embodiments, for example, sintered cemented carbide of high hardness and high wear resistance can extend to a depth of 50 μm-1 mm or 75-500 μm in the second section. Once the desired depth is reached, the sintered cemented carbide composition changes to a tougher, fracture resistant composition.


When the valve mating surface is formed of sintered cemented carbide, the sintered cemented carbide can have surface roughness (Ra) of 1-15 μm, in some embodiments. Surface roughness (Ra) of the sintered cemented carbide can also be 5-10 μm. Surface roughness of sintered cemented carbide forming the valve mating surface may be obtained via mechanical working including, but not limited to, grinding and/or blasting techniques. Moreover, sintered cemented carbide forming the second section of the valve seat, including the valve mating surface, can exhibit a compressive stress condition of at least 500 MPa. In some embodiments, sintered cemented carbide forming the second section can have a compressive stress condition selected from Table I.









TABLE I





Sintered Cemented Carbide Compressive Stress (GPa)















≥1


≥1.5


≥2


0.5-3


1-2.5










Compressive stress condition of the sintered cemented carbide can result from compression imparted by the ring encasing the second section and/or mechanically working the sintered cemented carbide to provide a valve mating surface of desired surface roughness. Compressive stress of the sintered cemented carbide may be determined via X-ray diffraction according to the Sin2 ψ method. Sintered cemented carbide of the valve seat may also exhibit hardness of 88-94 HRA.


The ring encasing the second section can be formed of any suitable material operable to impart a compressive stress condition to the second section. In some embodiments, the ring is formed of metal or alloy, such as steel. The ring may also be formed of ceramic or cermet.


In another aspect, a valve seat comprises a first section for insertion into a fluid passageway of a fluid end and a second section extending longitudinally from the first section, the second section having an outer diameter greater than the outer diameter of the first section. The second section also includes a frusto-conical valve mating surface comprising sintered cemented carbide having surface roughness (Ra) of 1-15 μm. The second section of the valve seat may optionally be encased by a ring as described herein.


Alternatively, the frusto-conical valve mating surface can be provided as a sintered cemented carbide inlay coupled to a metal or alloy body, wherein the sintered cemented carbide has surface roughness (Ra) of 1-15 μm. FIG. 7 illustrates a sintered cemented carbide inlay according to some embodiments. The sintered cemented carbide inlay 70 comprises a frusto-conical valve mating surface 71. Sintered cemented carbide forming the inlay 70 can have any composition and/or properties described above. The sintered cemented carbide inlay can be coupled to a metal or alloy body or casing. The metal or alloy body can form the first section of the valve seat and a portion of the second section. FIG. 8 is a cross-sectional view of valve seat comprising a sintered cemented carbide inlay coupled to an alloy body or casing according to some embodiments. In the embodiment of FIG. 8, the alloy body 82 forms the first section 81 of the valve seat 80 for insertion into a fluid passageway of a fluid end. The alloy body 82 also forms a portion of the second section 86 and defines a recess 83 in which the sintered cemented carbide inlay 70 is positioned. As in FIG. 7, the sintered cemented carbide inlay 70 comprises a frusto-conical valve mating surface 71 having surface roughness of (Ra) of 1-15 μm. In some embodiments, Ra of the valve mating surface 71 is 5-10 μm. The sintered cemented carbide inlay 70 can be coupled to the alloy body 82 by any desired means including brazing, sintering, hot isostatic pressing and/or press fit. In some embodiments, the inner annular surface of the alloy body in the second section 86 comprises one or more protrusions for engaging a groove on the perimeter of the sintered cemented carbide inlay 70. In some embodiments, the alloy body 82 can impart a compressive stress condition to the sintered cemented carbide inlay 70. The sintered cemented carbide inlay 70, for example, can exhibit compressive stress having a value selected from Table I above, in some embodiments. The alloy body 82 can be formed of any desired alloy including, but not limited to, steel and cobalt-based alloy. The alloy body 82 also provides a portion of the second section 86 having an outer diameter D2 greater than the outer diameter D1 of the first section 81. The outer diameter D1 may vary with taper of the outer surface 84 of the first section 81, in some embodiments. A curved intersection 88 exists at the transition of the first section 81 and the second section 86. Additionally, the larger outer diameter D2 of the second section 86 creates a shoulder 87. The shoulder 87 may have a construction as described in FIGS. 1-2 herein.


In another aspect, valve assemblies for use in fluid ends are provided. A valve assembly comprises a valve in reciprocating contact with a valve seat, the valve seat comprising a first section for insertion into a fluid passageway of the fluid end and a second section extending longitudinally from the first section. The second section has an outer diameter greater than the outer diameter of the first section and comprises a frusto-conical valve mating surface. The second section is also encased in a ring which imparts a compressive stress condition to the second section. In some embodiments, the second section is optionally encased in the ring, and the valve mating surface comprises sintered cemented carbide having surface roughness (Ra) of 1-15 μm. In other embodiments, the frusto-conical valve mating surface of the second section is provided as a sintered cemented carbide inlay coupled to a metal or alloy body, wherein the sintered cemented carbide has surface roughness (Ra) of 1-15 μm. In some embodiments, the metal or alloy body forms the first section of the valve seat and provides a recess for the sintered cemented carbide inlay in the second section. The valve seat can have any features, composition and/or properties described herein.


In a further aspect, fluid ends are described. A fluid end comprises a suction fluid passageway and a discharge fluid passageway. A valve assembly is positioned in at least one of the suction and discharge fluid passageways, the valve assembly comprising a valve in reciprocating contact with a valve seat. The valve seat comprises a first section for insertion into the suction or discharge fluid passageway and a second section extending longitudinally from the first section. The second section has an outer diameter greater than the outer diameter of the first section and comprises a frusto-conical valve mating surface. The second section is encased in a ring which imparts a compressive stress condition to the second section. In some embodiments, the second section is optionally encased in the ring, and the valve mating surface comprises sintered cemented carbide having surface roughness (Ra) of 1-15 μm. In other embodiments, the frusto-conical valve mating surface of the second section is provided as a sintered cemented carbide inlay coupled to a metal or alloy body, wherein the sintered cemented carbide has surface roughness (Ra) of 1-15 μm. In some embodiments, the metal or alloy body foul's the first section of the valve seat and provides a recess for the sintered cemented carbide inlay in the second section. The valve seat can have any features, composition and/or properties described herein. In some embodiments, the compressive stress condition of the first section is substantially equal to the compressive stress condition of the second section. In being substantially equal, compressive stress conditions of the first and second sections are within 10 percent of one another.


Various embodiments of the invention have been described in fulfillment of the various objectives of the invention. It should be recognized that these embodiments are merely illustrative of the principles of the present invention. Numerous modifications and adaptations thereof will be readily apparent to those skilled in the art without departing from the spirit and scope of the invention.

Claims
  • 1. A valve seat comprising: a first section for insertion into a fluid passageway of a fluid end; anda second section extending longitudinally from the first section, the second section having an outer diameter greater than the outer diameter of the first section and including a frusto-conical valve mating surface comprising sintered cemented carbide having surface roughness (Ra) of 1-15 μm, wherein the first section and second section are formed of sintered cemented carbides of differing composition.
  • 2. The valve seat of claim 1, wherein the sintered cemented carbide of the valve mating surface is mechanically worked.
  • 3. The valve seat of claim 1, wherein the sintered cemented carbide of the valve mating surface is in the form of an inlay ring.
  • 4. The valve seat of claim 1, wherein the sintered cemented carbide of the second section has higher hardness and/or wear resistance than the sintered cemented carbide of the first section.
  • 5. The valve seat of claim 1, wherein the sintered cemented carbide of the second section has smaller average grain size than the sintered cemented carbide of the first section.
  • 6. The valve seat of claim 1, wherein the sintered cemented carbide of the second section has lower metallic binder content than the sintered cemented carbide of the first section.
  • 7. The valve seat of claim 1, wherein the second section comprises sintered cemented carbide having a hardness gradient.
  • 8. The valve seat of claim 7, wherein the sintered cemented carbide of the valve mating surface has higher hardness than sintered cemented carbide 50 μm to 1 mm below the valve mating surface.
  • 9. The valve seat of claim 2, wherein the valve mating surface has a blasted condition.
  • 10. A valve assembly for use in a fluid end comprising: a valve in reciprocating contact with a valve seat, the valve seat comprising a first section for insertion into a fluid passageway of the fluid end and a second section extending longitudinally from the first section, the second section having an outer diameter greater than the outer diameter of the first section and including a frusto-conical valve mating surface comprising sintered cemented carbide having surface roughness (Ra) of 1-15 μm, wherein the first section and second section are formed of sintered cemented carbides of differing composition.
  • 11. The valve assembly of claim 10, wherein the sintered cemented carbide of the valve mating surface is mechanically worked.
  • 12. The valve assembly of claim 10, wherein the sintered cemented carbide of the valve mating surface is in the form of an inlay ring.
  • 13. The valve assembly of claim 10, wherein the sintered cemented carbide of the second section has higher hardness and/or wear resistance than the sintered cemented carbide of the first section.
  • 14. The valve assembly of claim 10, wherein the sintered cemented carbide of the second section has smaller average grain size than the sintered cemented carbide of the first section.
  • 15. The valve assembly of claim 10, wherein the sintered cemented carbide of the second section has lower metallic binder content than the sintered cemented carbide of the first section.
  • 16. The valve assembly of claim 10, wherein the second section comprises sintered cemented carbide having a hardness gradient.
  • 17. The valve assembly of claim 16, wherein the sintered cemented carbide of the valve mating surface has higher hardness than sintered cemented carbide 50 μm to 1 mm below the valve mating surface.
  • 18. The valve assembly of claim 11, wherein the valve mating surface has a blasted condition.
RELATED APPLICATION DATA

The present application is a continuation application pursuant to 35 U.S.C. § 120 of U.S. patent application Ser. No. 15/875,758 filed Jan. 19, 2018.

US Referenced Citations (89)
Number Name Date Kind
1478673 Parker Dec 1923 A
2103503 White Dec 1937 A
2745631 Shellman May 1956 A
2969951 Walton Jan 1961 A
2982515 Rule May 1961 A
3063467 Roberts, Jr. Nov 1962 A
4076212 Leman Feb 1978 A
4425699 Nordin Jan 1984 A
4572298 Weston Feb 1986 A
4911410 Baker Mar 1990 A
4951707 Johnson Aug 1990 A
4997162 Baker Mar 1991 A
5002834 Smith et al. Mar 1991 A
5062450 Bailey Nov 1991 A
5249600 Blume Oct 1993 A
5275204 Rogers Jan 1994 A
5345965 Blume Sep 1994 A
5501424 Williams Mar 1996 A
6139599 Takahashi et al. Oct 2000 A
6382940 Blume May 2002 B1
6464749 Kawase et al. Oct 2002 B1
6641779 Kawase et al. Nov 2003 B2
6712871 Oh Mar 2004 B2
6802883 Henmi et al. Oct 2004 B2
6916444 Liang Jul 2005 B1
6951579 Koyama Oct 2005 B2
6955181 Blume Oct 2005 B1
7070166 Blume Jul 2006 B1
7273508 Sato et al. Sep 2007 B2
7478673 Boyd Jan 2009 B2
7540470 Blume Jun 2009 B1
7572312 Kawata et al. Aug 2009 B2
D607091 Weston Dec 2009 S
7661935 Kellar Feb 2010 B2
D614271 Weston Apr 2010 S
7726026 Blume Jun 2010 B1
7730905 Suzuki Jun 2010 B2
8210542 Gilstad Jul 2012 B1
8221517 Mirchandani Jul 2012 B2
8317498 Gambier et al. Nov 2012 B2
D700682 Bayyouk Mar 2014 S
8707853 Dille Apr 2014 B1
8790439 Mirchandani Jul 2014 B2
8844903 Takahashi et al. Sep 2014 B2
8870554 Kent Oct 2014 B2
8915722 Blume Dec 2014 B1
9169707 Gilstad Oct 2015 B1
9175584 Lee et al. Nov 2015 B2
9222154 Dolman Dec 2015 B2
D748228 Bayyouk Jan 2016 S
9273385 Dolman Mar 2016 B2
D754817 Dille Apr 2016 S
9359921 Hashimoto et al. Jun 2016 B2
9435454 Blume Sep 2016 B2
9581056 Koyama et al. Feb 2017 B2
9631739 Belshan Apr 2017 B2
D796632 Bayyouk Sep 2017 S
D802104 Nagahamaya Nov 2017 S
9822894 Bayyouk Nov 2017 B2
9849532 Zheng et al. Dec 2017 B2
9927036 Dille Mar 2018 B2
20040234404 Vicars Nov 2004 A1
20070095443 Dolman May 2007 A1
20090278069 Blanco Nov 2009 A1
20110079302 Hawes Apr 2011 A1
20110278490 Maruno Nov 2011 A1
20120286183 McCarty Nov 2012 A1
20130017108 Kellar et al. Jan 2013 A1
20130020521 Byrne Jan 2013 A1
20130037179 Dolman Feb 2013 A1
20130181154 Robison Jul 2013 A1
20130202458 Byrne Aug 2013 A1
20130259733 Lee et al. Oct 2013 A1
20130269647 Pandey Oct 2013 A1
20130319220 Luharuka et al. Dec 2013 A1
20140070127 Blume Mar 2014 A1
20140124692 Baumann May 2014 A1
20150144826 Bayyouk et al. May 2015 A1
20150219096 Jain et al. Aug 2015 A1
20160101600 Potts et al. Apr 2016 A1
20160238156 Hubenschmidt Aug 2016 A1
20170009890 Vu Jan 2017 A1
20170059052 Abouelleil Mar 2017 A1
20170067459 Bayyouk Mar 2017 A1
20170089228 Shimada Mar 2017 A1
20170145875 Hashimoto May 2017 A1
20170298932 Wagner Oct 2017 A1
20170341148 Faust et al. Nov 2017 A1
20180290933 Shetty Oct 2018 A1
Foreign Referenced Citations (18)
Number Date Country
2861553 Jan 2007 CN
2861553 Jan 2007 CN
101737317 Jun 2010 CN
101737317 Jun 2010 CN
202001288 Oct 2011 CN
202001288 Oct 2011 CN
106996368 Aug 2017 CN
106996368 Aug 2017 CN
855956 Dec 1960 GB
855956 Dec 1960 GB
1020775 Dec 2003 NL
1020775 Dec 2003 NL
2015077001 May 2015 WO
WO-2015077001 May 2015 WO
WO-WG2015077001 May 2015 WO
2016201020 Jan 2016 WO
WO-2016118879 Jul 2016 WO
WO-2016201020 Dec 2016 WO
Non-Patent Literature Citations (7)
Entry
SPM 2.0 Valve and Seat.
Jun. 15, 2018 Office action (3 months) (US Only) U.S. Appl. No. 10/391,557.
Oct. 9, 2018 Office action (3 months) (US Only) U.S. Appl. No. 10/344,757.
Dec. 17, 2018 Notice of Allowance U.S. Appl. No. 10/391,557.
Apr. 10, 2019 Notice of Allowance U.S. Appl. No. 10/391,557.
Apr. 10, 2019 Notice of Allowance U.S. Appl. No. 10/344,757.
Mar. 30, 2020 Non-Final OA.
Related Publications (1)
Number Date Country
20190264682 A1 Aug 2019 US
Continuations (1)
Number Date Country
Parent 15875758 Jan 2018 US
Child 16408822 US