Patent Grant
8322298
Not applicable
Not applicable
1. Field of the Invention
The present invention relates to valves and valve wear, particularly valve nut wear for a valve having a valve stem and a valve stem nut that moves the valve stem responsive to a rotation of the valve stem nut. More particularly, the present invention relates to a method and apparatus for detecting valve stem nut wear for any valve that has a valve stem operated by rotation of a valve stem nut and wherein this apparatus is not an as-manufactured part of the valve to be inspected.
2. General Background of the Invention
A motor operated valve or “MOV” apparatus can employ a rising stem. This rising stem is operated by a rotating stem nut. One of the problems that plagues users of such valves (e.g. chemical plants, nuclear plants and other such facilities) is the failure of the stem nut after it has been in service for a long time.
A motor operated valve stem nut is typically made of a softer material (such as a bronze alloyed material) than the material used to make the stem (usually steel). Over a period of time, the stem nut threads will wear when opening and closing the valve. The wear can be influenced by several factors. These factors can include the stem nut material, normal operating loads, and maximum loads as examples. The wear can also be influenced by the number of stem nut rotations that occur during the valve stroke. Another factor that influences wear is the number and frequency of valve strokes. Yet other features that contribute to wear include stem nut manufacture and threaded length, stem-to-stem-nut fit, valve stem thread nut condition, and stem lubricant. Other factors include the lubrication method and frequency as well as environmental conditions for the lubricant.
Since the valve stem is typically made of a harder material such as stainless steel or carbon steel, it is typical and expected that all thread wear will occur on the valve stem nut threads and not on the valve stem. This is preferential to having wear occur on the valve stem (as the stem nut is typically much easier to change out than the valve stem).
On rising stem valves, a stem nut transfers rotational motion (torque) of a motor operated or manual valve to axial stem movement or “thrust”. Stem nut failure will prevent valve operation and may cause valve position indication to be incorrectly displayed in a control room. If the motor operated valve is electrically interlocked, its failure can also interfere with the operation of other plant equipment resulting in a potentially costly or catastrophic failure event.
Unfortunately, many facilities, plants, chemical refineries and the like do not take a proactive approach to maintaining these valve stem nuts. One reason that these facilities do not take a proactive approach is that it is difficult to predict failure of any particular valve. In some cases, a failure may take many years to occur.
Another problem with a proactive approach to maintaining valve stem nuts is that direct inspection of the stem nut threads is intrusive and requires taking the valve out of service to remove and inspect.
On smaller diameter stems, measuring the stem nut thread wear on a removed stem nut can be very difficult. There is limited space inside the stem nut to get a direct measurement with dial calipers.
Excessive stem nut thread wear represents a potential common cause failure mode that could impact all rising stem valves. The unexpected failure of valve stem nuts, and resulting consequence emphasizes the importance of improving conditions, monitoring maintenance practice activities, and identifying, quantifying and minimizing stem nut thread wear. Periodic stem nut removal and inspection or measuring thread backlash may be beneficial to prevent failure. It is important for any maintenance program to detail proper stem cleaning and lubrication procedures.
The valves to be tested are not always gate valves, but any valve using a threaded stem and nut.
An assumption is that the stem is cut properly (which is not always the case)—thus, as part of the method, it is preferable to also measure stem threads to make sure that the assumption is correct.
At some facilities, the stems tend to corrode instead of wearing.
The tool of the present invention was validated in lab tests, where it appears that the tool can predict wear with 3-11% accuracy.
Typically, stems are made of hardened steel, but some facilities use 17-4 PH stainless steel for replacement stems.
The stem nuts can be aluminum bronze (softer), but some are manganese bronze (harder).
Some stem nuts may be as hard as the stems (that is not desirable, as the stems may wear as fast as the nuts, and they are more difficult to replace).
The stems at some facilities are 29 degree Acme thread with double leads.
The following table lists possibly relevant patents and applications, the order of listing being chronological, the order of listing otherwise having no significance.
General Discussion of the Present Invention
The stem nut analysis protractor tool of the present invention was developed to provide a non-intrusive and quick means of quantifying stem nut thread wear without having to remove the valve from service. This process measures the backlash between the stem and stem nut threads on rising stem valves. Using the apparatus and method of the present invention, it is possible to quantify the remaining stem nut thread metal.
Generally speaking, nonintrusive stem nut wear detection can find its roots in nuclear plant “MOV” diagnostics. “MOV” diagnostics are required by the Nuclear Regulatory Commission as necessary to prove operability of valves needed to safely shut down a nuclear plant during an emergency event. As early as the mid 1990's, the backlash “zero” region in the stem thrust/time trace could provide an indication that excessive stem nut wear existed.
The apparatus of the present invention can be used to measure the same area but uses a much less complicated process to perform.
The stem nut area of interest is identified as X=P−Fcs (base of the stem nut thread indicated by arrow X) in
X=P−Fcs
Fcs=0.3707*P−0.259*P.D.(where P.D. Allowance on External Thread=(0.008*sqrt(D))
Lead=Inches of Axial Stem Movement Per 360° Revolution
Inches Per Degree=Lead/360
100% Stem Nut Thread Inches*Inches Per Degree=100% Wear in Degrees were used to calculate P−Fcs then convert it to its rotational percentage of backlash and is valid for all General Purpose Acme Threads with one, two, three, or four thread starts. The linear relationship between stem nut rotation and stem axial movement can be found in the definition of “Stem Lead”—the distance a stem thread advances axially in one turn of the stem nut. X (P−Fcs) equals 100% of the thickest part of the stem nut thread; this is where the backlash is measured. As the stem nut thread wears, its backlash will increase, allowing more free rotation. The purpose of the method and apparatus of the present invention is to measure thread wear percent or “backlash percent” (see
In an example of the method of the present invention, it is assumed that the valve stem threads are properly manufactured with a 29 degree angle to the dimensions detailed in the Machinery's Handbook 25 for ACME Thread Design.
Protractor Development:
“Lead”, defined as the distance a stem travels axially with one stem nut rotation, is the basis for using the protractor for measuring stem nut wear.
Example: Using the formula for lead, a 1.5″ (3.8 cm) Diameter stem with a ¼ Pitch and ½ Lead will result in 0.500″ (1.27 cm) of axial stem movement for one rotation of the drive stem nut. 0.500″/360°=0.0013888 in/deg. (1.27 cm/360°=0.0035277 cm/deg.)
If “P−Fcs of this thread equals 0.1548” (0.3932 cm) and is 100% of the stem nut thread then 0.1548″/0.0013888 in/deg.=111.46° (0.3932 cm/0.0035277 cm/deg.=111.46)°
To find percent wear per degree measured; 100%/111.46°=0.8971576%/deg. Confirmation that this protractor scale can be used on other two thread-start stems can be found below:
3.0″ (7.6 cm) Diameter stem with 2/5 Pitch and 4/5 lead with 0.800″ (2.032 cm) per rotation;
0.800″/360°=0.0022222 in/deg. (2.032 cm/360°=0.0056444 cm/deg);
0.248131″ (100% thread width)/0.0022222 in/deg.=111.66° (0.630253 cm (100% thread width)/0.0056444 cm/deg.=111.66)°;
100%/111.66°=0.8955753%/deg.
Assuming that the stem threads are cut accurately, measuring percent wear is substantially equal to the stem nut thread wear. This measurement can be used for a variety of Acme thread starts, pitch and lead. Examples are for double thread start general purpose (G.P.) Acme thread stems.
Calculations for Different Acme Thread Options
The following formulae variables are identified as follows (Reference: Machinery's Handbook 25 General Purpose Acme Threads pp 1716-1724):
P=Stem Thread Pitch
Fcs=Basic Flat at Stem Thread Crest (
D=Stem Thread Diameter
L=Stem Thread Lead
Total Degrees for 100% Wear=(P−Fcs)/(L/360°)
Where:
Fcs=(0.3707*P−0.259*(0.008 √D)) for General Purpose Acme
Fcs=(0.4224*P−0.259*(0.008 √D)) for Stub Acme
Each of the below 100% wear calculations used an average of eight common stem diameters and thread configurations (Attachment 6) for general purpose and stub acme threaded stems.
a. One-Thread Start Degrees in 100% wear; [(P−(Fcs)/L/360°]
b. Two-Thread Start Degrees in 100% wear; [(P−(Fcs)/L/360°]
c. Three-Thread Start Degrees in 100% wear; [(P−(Fcs)/L/360°]
d. Four-Thread Start Degrees in 100% wear; [(P−(Fcs)/L/360°]
a. One-Thread Start Degrees in 100% wear; [(P−(Fcs)/L/360°]
b. Two-Thread Start Degrees in 100% wear; [(P−(Fcs)/L/360°]
c. Three-Thread Start Degrees in 100% wear; [(P−(Fcs)/L/360°]
d. Four-Thread Start Degrees in 100% wear; [(P−(Fcs)/L/360°]
The “Average calculated degrees per 100% wear” is divided into readable increments indicating smaller wear percentages. Individual gauges can be manufactured for each of the above thread start types or one protractor could be made with all GP Acme types on one side and Stub Acme types on the other.
Stems with additional thread-starts will require recalculation using above applicable formula and protractor made to measure stem nut thread wear.
In general, installation of the tool of the present invention requires removal of the stem protector and indication rod, if installed, to provide access to the top of the stem and stem nut. The tool should be mounted where it will freely rotate with the stem nut. Cleaning the top of the stem nut may be necessary to facilitate the tool installation. The presence of hardened grease, broken thread material or any other solid contaminant between the threads may mask the true backlash measured by the tool of the present invention; therefore, cleaning the stem may be necessary. The tool of the present invention preferably also contains a dial indicator, or any similar instrument capable of detecting axial stem movement (other devices that could be used to detect axial stem movement/displacement could include, but are not limited to a linear variable differential transformer (LVDT), laser, or switch). A stylus extension may be required to allow the dial indicator to contact the top (when oriented vertically—otherwise, the exposed end) of the closed valve stem. In some instances, the top of the stem may have imperfections that could affect smooth dial indication reading; a smooth circular disk can be placed on top of the stem for the stylus to ride.
When the wear indicator dial is mounted on a tool which rests on the stem nut, the pointer is mounted to anything independent of the stem nut to indicate the backlash rotation percent on the tool. When the stem does not rise vertically when actuated, then preferably the pointer and dial indicator are mounted on a post which is connected to the stem nut, and the wear indication protractor is preferably mounted on some portion of the valve which does not rotate as the valve stem nut rotates.
For a further understanding of the nature, objects, and advantages of the present invention, reference should be made to the following detailed description, read in conjunction with the following drawings, wherein like reference numerals denote like elements and wherein:
Stem nut analysis protractor apparatus 10 is used to measure valve stem nut wear on any valve 90 having a stem 25 and a stem nut 28 that moves the stem 25 (see
To perform the method of the present invention, the stem protector and indication rod (if installed) are removed. The apparatus 10 preferably includes tool body 15 which is preferably mounted where it will rotate freely with the stem nut 28 (see
A dial indicator 20 is used to detect axial stem movement in the setup shown in
Pointer 14 is a stationary pointer which indicates backlash rotation as a percent. The pointer 14 should be mounted on any structure that is independent of valve stem nut 28 rotation (see
Tool body 15 can be generally circular or cylindrical as shown in
Tool body 15 has an upper face 17 with indicia 23 thereon (a scale) to indicate wear, such as a percentage of stem nut wear between 0 and 100 percent (see
Post 19 is supported by tool body 15. Post 19 supports dial indicator 20 which can be any instrument that indicates axial stem movement. Post 19 can have a laterally extending bracket 21 that supports dial indicator 20 and stylus or rod 22. Dial indicator 20 can provide a pointer or arrow 29 indicating a value for axial stem movement (see
Installation of the apparatus 10 of the present invention requires removal of the stem protector and indication rod, if installed, to provide access to the top of the stem and stem nut. It should be mounted where it will freely rotate with the stem nut 28. Cleaning the valve stem 25 and the top of the stem nut may be desirable to facilitate the tool 10 installation. The apparatus 10 contains a dial indicator 20, or any similar instrument capable of detecting axial stem movement. A 90° dial indicator (not shown, but it could for example be a Starrett brand 90° dial indicator) can be used in situations where a visual line of sight is not convenient from the top of stem 25 (looking vertically downward)—i.e. reading would be taken from the side of the actuator/tool assembly instead of from the top of everything. This 90° dial indicator could be installed onto holding clamp 21. The stylus extension 22 (see
In
Effective operation of the system of the present invention requires minimal training; however, having a basic mechanical understanding of valve designs would help the technician 40 modify his technique to successfully perform the test. Certain dynamics that could make backlash measuring difficult are:
To perform the method of the present invention with apparatus 10, operator 40 would preferably perform the following steps. With the apparatus 10 in place on the stem nut 28 of a closed valve 90, declutch the actuator if necessary, and rotate the handwheel 39 open. The valve actuator usually goes through a lost-motion region as the worm gear advances around the drive sleeve until it contacts lugs on the drive sleeve (defined as hammer blow). The drive sleeve/stem nut 28 will then start turning. At this point, the threads will immediately pass through backlash, or the stem 25 will start rising and soon pass through backlash. While in the backlash region, the stem nut 28 will turn and the stem 25 will not move. Operator 40 continues turning wheel 39 until the stem nut 28 takes up the backlash and stem movement is detected on the dial indicator. The operator 40 then stops rotation of wheel 39 (see
Empirical data from stem nut threads measured by the apparatus 10 is currently being obtained (see Attachment 1 attached to U.S. Provisional Patent Application No. 61/235,204, filed 19 Aug. 2009, which shows wear percentages from 0 to 82%). Stem nuts determined to have excessive wear (≧40%, for example) can be replaced and have a detailed physical examination of the remaining thread widths performed. Validation of all calculations used to develop the apparatus 10 can also be completed. The initial validation of the formula X=P−Fcs on a General Purpose Acme thread with a ½ pitch was calculated at 0.31245 inch (0.79362 cm). Validation of this calculation was done by measuring a 29° 2N Acme Thread Gauge. Continued field validation was performed by recording the percent wear as indicated on the apparatus 10 then removing and cutting the stem nut to measure the thickness of the remaining thread.
In
As an alternate, a post 19 could be directly affixed to the stem nut 28 (see
Certain valve stem orientations will make it more difficult to use the tool shown in
Instead of using a tool body 15 and adapter(s) 11, 12, 13, 45, 46, 47, 48, a tool post 19 is mounted directly to the top of the stem nut 28 (actually, to the exposed end of the stem nut 28, which might be horizontally disposed or even upside down). This can be accomplished by drilling and tapping the stem nut 28 to receive the tool post 19 threads. A post clamp 72 is affixed to the tool post 19. This post clamp holds the dial indicator 20 and pointer. The dial indicator 20 is positioned adjacent the center of the exposed end 36 of valve stem 25 where it will detect axial stem movement and the pointer 14 is positioned on the post 19 where it will freely rotate with valve 28 to indicate the protractor reading on protractor scale 23. The stylus strike disk 37 can be adhered to the exposed end of the stem nut by adhesive putty, double-stick tape, or any other type of adhesive method. The protractor scale 23 can be on a rigid disk that can be adhered to the upper housing (such as top edge 92—see
When the apparatus of the present invention is used on a vertically rising valve stem, large adapter 11, medium adapter 12, small adapter 13, and tool body 15 of the apparatus shown in
Tool Application
The following is a step-by-step example of how one can use the apparatus of the present invention to measure stem nut wear, and should be read in conjunction with
To test a stem nut 28 using the method of the present invention, it is best that the valve stem 25 remains stationary. Factors that could cause the stem 25 to move would be system pressure (stem ejection effect) and gravity. These forces can be neutralized by:
Clamp down apparatus 80 includes a ram adaptor 110, a yoke 111, side rod connecting nuts 112, side rod hexagonal nuts 113, clip/washers 114, cap screws 115, side rods 116, an end block 117, and nuts 118.
In
After stem 25 is clamped down with clamp apparatus 80, testing of nut 28 with apparatus 10 would proceed as discussed above.
Because a preferred method of the present invention involves cleaning the valve stem prior to testing and re-lubricating the valve stem after testing is performed, the method of the present invention helps to maintain valves in good working order.
The following is a list of parts and materials suitable for use in the present invention:
All measurements disclosed herein are at standard temperature and pressure, at sea level on Earth, unless indicated otherwise.
The foregoing embodiments are presented by way of example only; the scope of the present invention is to be limited only by the following claims.
LABAT, Chris, A., a US citizen, of 104 Autumn Ridge Drive, Thibodaux, La. 70301, US; and REAMES, JR., Carter, a U.S. citizen, of 12509 Palmer Road, Gonzales, La. 70737, US. Incorporated herein by reference are our prior U.S. provisional patent application No. 61/370,739, filed 4 Aug. 2010, and our prior U.S. provisional patent application No. 61/235,204, filed 19 Aug. 2009. Priority of these applications is hereby claimed.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US2010/045914 | 8/18/2010 | WO | 00 | 11/21/2011 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2011/022496 | 2/24/2011 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 2880518 | Wilhelm Settele | Apr 1959 | A |
| 3651831 | Gardner | Mar 1972 | A |
| 3721133 | Denkowski | Mar 1973 | A |
| 3857547 | Profet | Dec 1974 | A |
| 4255967 | Grymonprez et al. | Mar 1981 | A |
| 4337649 | Stagg | Jul 1982 | A |
| 5224512 | Nogami et al. | Jul 1993 | A |
| 5487302 | Casada et al. | Jan 1996 | A |
| 5620166 | Lord et al. | Apr 1997 | A |
| 6799928 | Port-Robach | Oct 2004 | B2 |
| 7549440 | Campbell | Jun 2009 | B1 |
| 20020095986 | Ito et al. | Jul 2002 | A1 |
| Number | Date | Country |
|---|---|---|
| 04-296268 | Oct 1992 | JP |
| 09-005064 | Jan 1997 | JP |
| 10234155 | Sep 1998 | JP |
| 2004-144604 | May 2004 | JP |
| 2010261587 | Nov 2010 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20120060745 A1 | Mar 2012 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61235204 | Aug 2009 | US | |
| 61370739 | Aug 2010 | US |