Variable stiffness coil for vasoocclusive devices

Information

  • Patent Grant
  • 6656201
  • Patent Number
    6,656,201
  • Date Filed
    Thursday, November 15, 2001
    22 years ago
  • Date Issued
    Tuesday, December 2, 2003
    20 years ago
Abstract
The variable stiffness vasoocclusive coil is given variable stiffness along the length of the coil by selectively heat treating certain segments of a primary or secondary coil. The primary coil can be selectively heat treated to form soft or deformable segments along the length of the coil, and can then be shaped into a secondary shape that is set by a heat treatment process. Distal regions of the coil can also be heat treated to make the distal ends of the coil softer, more deformable, or less traumatic.
Description




BACKGROUND OF THE INVENTION




1. Field of the Invention




This invention relates generally to implantable devices for interventional therapeutic treatment or vascular surgery, and more particularly concerns a variable stiffness vasoocclusive coil that exhibits variable stiffness along the length of the coil.




2. Description of Related Art




The art and science of interventional therapy and surgery has continually progressed towards treatment of internal defects and diseases by use of ever smaller incisions or access through the vasculature or body openings in order to reduce the trauma to tissue surrounding the treatment site. One important aspect of such treatments involves the use of catheters to place therapeutic devices at a treatment site by access through the vasculature. Examples of such procedures include transluminal angioplasty, placement of stents to reinforce the walls of a blood vessel or the like and the use of vasoocclusive devices to treat defects in the vasculature. There is a constant drive by those practicing in the art to develop new and more capable systems for such applications. When coupled with developments in biological treatment capabilities, there is an expanding need for technologies that enhance the performance of interventional therapeutic devices and systems.




One specific field of interventional therapy that has been able to advantageously use recent developments in technology is the treatment of neurovascular defects. More specifically, as smaller and more capable structures and materials have been developed, treatment of vascular defects in the human brain which were previously untreatable or represented unacceptable risks via conventional surgery have become amenable to treatment. One type of non-surgical therapy that has become advantageous for the treatment of defects in the neurovasculature has been the placement by way of a catheter of vasoocclusive devices in a damaged portion of a vein or artery.




Vasoocclusion devices are therapeutic devices that are placed within the vasculature of the human body, typically via a catheter, either to block the flow of blood through a vessel making up that portion of the vasculature through the formation of an embolus or to form such an embolus within an aneurysm stemming from the vessel. The vasoocclusive devices can take a variety of configurations, and are generally formed of one or more elements that are larger in the deployed configuration than when they are within the delivery catheter prior to placement. One widely used vasoocclusive device is a helical wire coil having a deployed configuration which may be dimensioned to engage the walls of the vessels. One anatomically shaped vasoocclusive device that forms itself into a shape of an anatomical cavity such as an aneurysm and is made of a pre-formed strand of flexible material that can be a nickel-titanium alloy is known from U.S. Pat. No. 5,645,558, which is specifically incorporated by reference herein. That vasoocclusive device comprises one or more vasoocclusive members wound to form a generally spherical or ovoid shape in a relaxed state. The vasoocclusive members can be a helically wound coil or a co-woven braid formed of a biocompatible material, and the device is sized and shaped to fit within a vascular cavity or vesicle, such as for treatment of an aneurysm or fistula. The vasoocclusive member can be first helically wound or braided in a generally linear fashion, and is then wound around an appropriately shaped mandrel or form, and heat treated to retain the shape after removal from the heating form. Radiopacity can be provided in the vasoocclusive members by weaving in synthetic or natural fibers filled with powdered radiopaque material, such as powdered tantalum, powdered tungsten, powdered bismuth oxide or powdered barium sulfate, which can potentially be released during vascular surgery.




The delivery of such vasoocclusive devices can be accomplished by a variety of means, including via a catheter in which the device is pushed through the catheter by a pusher to deploy the device. The vasoocclusive devices, which can have a primary shape of a coil of wire that is then formed into a more complex secondary shape, can be produced in such a way that they will pass through the lumen of a catheter in a linear shape and take on a complex shape as originally formed after being deployed into the area of interest, such as an aneurysm. A variety of detachment mechanisms to release the device from a pusher have been developed and are known in the art.




For treatment of areas of the small diameter vasculature such as a small artery or vein in the brain, for example, and for treatment of aneurysms and the like, micro-coils formed of very small diameter wire are used in order to restrict, reinforce, or to occlude such small diameter areas of the vasculature. A variety of materials have been suggested for use in such micro-coils, including nickel-titanium alloys, copper, stainless steel, platinum, tungsten, various plastics or the like, each of which offers certain benefits in various applications. Nickel-titanium alloys are particularly advantageous for the fabrication of such micro coils, in that they can have super-elastic or shape memory properties, and thus can be manufactured to easily fit into a linear portion of a catheter, but attain their originally formed, more complex shape when deployed.




One known technique for filling wide neck aneurysms involves breaking a coil or permanently deforming a coil within a vessel utilizing a balloon. However, substantial risks to a patient are involved in such a procedure, and a coil which has soft or deformable segments may offer less risk to a patient. As a coil is inserted into the aneurysm, the coil deforms and sets it shape, but over time a coil will typically assume its original shape, which is unlikely to correspond to the shape of the vessel being filled. Filling of a variety of types of aneurysms of various sizes and shapes may benefit by use of a variable stiffness coil that can deform more readily at certain predetermined sections. As such a variable stiffness coil is inserted into the aneurysm, the coil will deform to conform to the shape and size of the vessel being filled, and will set its shape, but unlike a helical coil which over time takes on its original shape, a variable stiffness, deformable coil will permanently deform in a random configuration, to thereby fill an aneurysm more evenly and completely over long periods of time.




A variable cross-section conical vasoocclusive coil is known that can achieve variations in stiffness of the coil by variation of the diameter in different regions of the coil or variations in the composition of the coil. Methods are also known for construction of a stent with a varying radial spring force, by heat treatments, by varying the stent frame thickness, selectively machining stent ring frames, using different alloys of the ring frames, and varying the Austenite finish transformation temperature (Af) of a shape memory alloy such as Nitinol. A guide wire is also known that is formed from one or more heat activated memory alloys, with intermediate portions that are selectively annealed to have variously curved shapes while the remainder of the wire remains straight when heated, and a stent is known that has U-shaped loop portions that are provided with greater flexibility by selective annealing to impart selective degrees of hardness to different portions.




It would be desirable to provide an vasoocclusive coil with primary and secondary shapes with variable stiffness along the length of the coil that can permanently deform in a random configuration that will permanently deform in a random configuration in order to fill an aneurysm more evenly and completely over long periods of time. The present invention meets these and other needs.




SUMMARY OF THE INVENTION




Briefly, and in general terms, the present invention provides for a variable stiffness vasoocclusive coil that exhibits variable stiffness along the length of the coil. Variable stiffness is accomplished by selectively heat treating certain segments of a primary or secondary coil. The primary coil can be selectively heat treated to form soft or deformable segments along the length of the coil, and can then be shaped into a secondary shape that is set by a heat treatment process. A secondary coil such as a three dimensional coil can be produced with variable stiffness through a selective heating of localized segments of the coil. Distal regions of the coil can also be heat treated to make the distal ends of the coil softer, more deformable, or less traumatic. Upon deployment, the coil will take on its preformed three dimensional shape, and will deform in a random three-dimensional shape to conform to the shape of the vessel or malformation into which the coil is introduced. The variable stiffness coil is advantageously formed of a shape memory metal, and variable stiffness can be achieved through aging of desired segments of the shape memory metal coil to raise the parent phase or Austenite phase finish temperature, thus making the treated segments of shape memory metal softer and more flexible.




The invention accordingly provides for an occlusive device for use in interventional therapy and vascular surgery adapted to be inserted into a portion of a vasculature for occluding the portion of the vasculature of a patient. The occlusive device comprises a variable stiffness coil formed from one or more flexible strands of a shape memory metal having a primary coil configuration, the coil having a plurality of segments heat treated to cause the plurality of segments to have reduced stiffness. In one presently preferred embodiment, the variable stiffness coil has an expanded secondary coil configuration with a secondary three dimensional shape, such as a spherical or helical shape. In a preferred aspect, the flexible strand comprises a super-elastic material, which can be a shape memory metal such as a nickel titanium alloy. The shape memory nickel-titanium alloy is preferably heat treated such that the alloy is highly flexible at a temperature appropriate for introduction into the vasculature via a catheter, and after placement, the device will take on a shape designed to optimize the therapeutic purposes desired for the device.




The invention also provides for a method for making a variable stiffness occlusive coil for use in interventional therapy and vascular surgery adapted to be inserted into a portion of a vasculature for occluding the portion of the vasculature of a patient, comprising the steps of providing a coil formed from one or more flexible strands of a shape memory metal, the coil having a primary coil configuration and an initial stiffness; and heat treating a plurality of segments of the coil to cause the plurality of segments to have reduced stiffness. In one presently preferred embodiment, the step of providing a coil comprises heating the coil in a desired three dimensional configuration to set the three dimensional shape. In a preferred aspect of the method of the invention, the shape memory metal has an Austenite phase finish temperature, and the step of heating the coil comprises heating the coil at about 475° C. to 525° C. for about 1 to 20 minutes to set the Austenite phase finish temperature of the coil to about −5° C. to 10° C. The step of heat treating the coil can be accomplished by artificially aging a plurality of segments of the coil to raise the Austenite phase finish temperature to about 35° C. to 50° C., such as by heating a plurality of segments of the coil to a temperature of about 400° C. for a period of about 5 seconds to 30 minutes.




These and other aspects and advantages of the invention will become apparent from the following detailed description and the accompanying drawings, which illustrate by way of example the features of the invention.











BRIEF DESCRIPTION OF THE DRAWINGS





FIG. 1

is a primary helical vasoocclusive coil showing areas of heat treatment according to the invention.





FIG. 2

is a secondary helical vasoocclusive structure formed using the primary helical coil of FIG.


1


.





FIG. 3

is a secondary spherical vasoocclusive structure formed using the primary helical coil of FIG.


1


.





FIG. 4

is a graph illustrating the reduction in stiffness of a shape memory coil by heat treatment according to the principles of the invention.





FIG. 5

is a schematic diagram of an apparatus for applying heat to segments of a vasoocclusive coil to form a variable stiffness vasoocclusive coil according to the invention.











DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS




Modern techniques for filling wide neck aneurysms typically involve breaking a coil or permanently deforming a coil within a vessel utilizing a balloon, with attendant substantial risks to a patient, and a coil which has soft or deformable segments may offer less risk to a patient. While modern vasoocclusive coils deform and set their shape when they are introduced into a vessel, over time such coils will typically assume their original shape rather than to the shape of the vessel being filled. Filling of a variety of types of aneurysms of various sizes and shapes may benefit by use of a variable stiffness coil that can deform more readily at certain predetermined sections to fill an aneurysm more evenly and completely over long periods of time.




As is illustrated in the drawings, the invention is embodied in an occlusive device for use in interventional therapy and vascular surgery adapted to be inserted into a portion of a vasculature for occluding a selected portion of the vasculature of a patient. In a presently preferred embodiment of the invention illustrated in

FIG. 1

, the occlusive device


10


is made from a strand of wire of approximately 0.001 inch to approximately 0.006 inch in diameter and comprises a coil


12


formed from one or more flexible strands of a super-elastic, shape memory metal such as nickel-titanium alloy, for example. While the above stated range of diameters is presently known to be compatible with the invention, larger or smaller diameters may be useful for particular applications. The occlusive device typically has at least a primary coil configuration illustrated in

FIG. 1

, with a plurality of segments


14


being heat treated to cause the plurality of segments to have reduced stiffness.




In one presently preferred embodiment shown in

FIG. 2

, the variable stiffness coil has an expanded secondary coil configuration with a secondary helical three dimensional shape


16


, with localized heat treated segments


18


, although the variable stiffness coil can also have an expanded secondary coil configuration with a secondary spherical three dimensional shape


20


, with localized heat treated segments


22


, as illustrated in FIG.


3


. The shape memory metal is preferably heat treated to be highly flexible at a temperature appropriate for introduction into the vasculature via a catheter, and such that after placement, the device will take on a shape designed to optimize the therapeutic purposes desired for the device.




The invention also provides for a method for making the variable stiffness occlusive coil. In a presently preferred embodiment, the variable stiffness occlusive coil can be formed from a coil


12


of one or more flexible strands of a superelastic shape memory metal. The coil preferably has at least a primary coil configuration and an initial stiffness, as is illustrated in

FIG. 4

, representing the change in stiffness of a heat treated segment of such a coil by application of heat to the segment, such as by the apparatus shown in FIG.


5


. Variable stiffness of the heat treated segment can be achieved through artificial aging of the shape memory metal, such as Nitinol. The shape memory behavior of the shape memory metal can be modified by artificial aging of the material by heat treatment affecting the Austenitic transformation temperatures. When a shape memory alloy such as nickel titanium alloy is deformed, and then heated to recover its original parent or Austenite shape, the original shape corresponds to the shape of the alloy in the relatively high temperature range of the parent phase. Once the Austenite phase finish temperature (Af) is reached, the nickel titanium alloy becomes stiffened. However, artificial aging of the nickel titanium alloy can raise the Af temperature, thus making the material act softer at higher temperatures. The coil is preferably initially heated in a desired three dimensional configuration to set the three dimensional by heating the coil, such as in a salt pot, at about 475° C. to 525° C. for about 1 to 20 minutes to set the Austenite phase finish temperature of the coil to about −5° C. to 10° C. As is illustrated in

FIG. 5

, heat treating of a segment of the coil will cause the segment to have reduced stiffness, such as by artificially aging the segment of the coil to raise the Austenite phase finish temperature to about 35° C. to 50° C., by heating a plurality of segments of the coil to a temperature of about 400° C. for a period of about 5 seconds to 30 minutes. This can be accomplished by placing the primary or secondary shape coil in a heated air box


26


supplying hot air from a source of heated air (not shown). The air box, typically made of brass, for example, has a channel


30


in which the coil can be placed to expose the coil


28


to a flow of hot air from a port


32


that is typically 0.020 inches to 0.500 inches in diameter, conveyed to the port through a conduit


34


that extends through the air box. In this manner, localized heating can be provided to desired portions of the coil, at controlled temperatures for prescribed periods of time. Alternatively, heating of segments of the coil can be achieved by other means, such as by a laser, or by electrical heating, or other common types of heating elements.




It will be apparent from the foregoing that while particular forms of the invention have been illustrated and described, various modifications can be made without departing from the spirit and scope of the invention. Accordingly, it is not intended that the invention be limited, except as by the appended claims.



Claims
  • 1. A method for making a variable stiffness occlusive coil for use in interventional therapy and vascular surgery adapted to be inserted into a portion of a vasculature for occluding the portion of the vasculature of a patient, comprising the steps of:providing a coil formed from at least one flexible strand of a shape memory metal, said coil having a primary coil configuration and an initial stiffness; and heat treating a plurality of segments of said coil to cause said plurality of segments to have reduced stiffness.
  • 2. The method of claim 1, wherein said step of providing a coil comprises heating said coil in a desired three dimensional configuration to set said three dimensional configuration.
  • 3. The method of claim 2, wherein said shape memory metal has an Austenite phase finish temperature, and said step of heating said coil comprises heating said coil at about 475° C. to 525° C. for about 1 to 20 minutes to set the Austenite phase finish temperature of the coil to about −5° C. to 10° C.
  • 4. The method of claim 1, wherein said step of heat treating comprises artificially aging a plurality of segments of said coil to raise the Austenite phase finish temperature to about 35° C. to 50° C.
  • 5. The method of claim 1, wherein said step of heat treating comprises heating a plurality of segments of said coil to a temperature of about 375° C. to 425° C. for a period of about 5 seconds to 30 minutes.
  • 6. The method of claim 1, wherein said step of heat treating comprises heat treating a distal segment of said coil to cause said distal segment to have reduced stiffness.
RELATED APPLICATIONS

This application is a divisional of Ser. No. 09/211,783 filed Dec. 15, 1998.

US Referenced Citations (127)
Number Name Date Kind
1341052 Gale May 1920 A
1667730 Green May 1928 A
2078182 MacFarland Apr 1937 A
2549335 Rahthus Apr 1951 A
3334629 Cohn Aug 1967 A
3452742 Muller Jul 1969 A
3649224 Anderson et al. Mar 1972 A
3868956 Alfidi et al. Mar 1975 A
4494531 Gianturco Jan 1985 A
4503569 Dotter Mar 1985 A
4512338 Balko et al. Apr 1985 A
4553545 Maass et al. Nov 1985 A
4638803 Rand Jan 1987 A
4655771 Wallsten Apr 1987 A
4695426 Nylund Sep 1987 A
4718907 Karwoski et al. Jan 1988 A
4748986 Morrison et al. Jun 1988 A
4768507 Fischell et al. Sep 1988 A
4795458 Regan Jan 1989 A
4800882 Gianturco Jan 1989 A
4813925 Anderson, Jr. et al. Mar 1989 A
4820298 Leveen et al. Apr 1989 A
4830003 Wolff et al. May 1989 A
4850960 Grayzel Jul 1989 A
4856516 Hillstead Aug 1989 A
4950258 Kawai et al. Aug 1990 A
4954126 Wallsten Sep 1990 A
4957479 Roemer Sep 1990 A
4957501 Lahille et al. Sep 1990 A
4990155 Wilkoff Feb 1991 A
4994069 Ritchart et al. Feb 1991 A
5026377 Burton et al. Jun 1991 A
5041084 DeVries et al. Aug 1991 A
5064435 Porter Nov 1991 A
5071407 Termin et al. Dec 1991 A
5104404 Wolff Apr 1992 A
5108407 Geremia et al. Apr 1992 A
5122136 Guglielmi et al. Jun 1992 A
5133731 Butler et al. Jul 1992 A
5133732 Wiktor Jul 1992 A
5139243 Balsells Aug 1992 A
5141502 Macaluso, Jr. Aug 1992 A
5143085 Wilson Sep 1992 A
5147370 McNamara et al. Sep 1992 A
5151105 Kwan-Gett Sep 1992 A
5160341 Brenneman et al. Nov 1992 A
5176625 Brisson Jan 1993 A
5176661 Evard et al. Jan 1993 A
5183085 Timmermans Feb 1993 A
5186992 Kite, III Feb 1993 A
5203772 Hammerslag et al. Apr 1993 A
5211183 Wilson May 1993 A
5217484 Marks Jun 1993 A
5222969 Gillis Jun 1993 A
5226911 Chee et al. Jul 1993 A
5228453 Sepetka Jul 1993 A
5234437 Sepetka Aug 1993 A
5234456 Silvestrini Aug 1993 A
5250071 Palermo Oct 1993 A
5256146 Ensminger et al. Oct 1993 A
5261916 Engelson Nov 1993 A
5269752 Bennett Dec 1993 A
5304194 Chee et al. Apr 1994 A
5304195 Twyford, Jr. et al. Apr 1994 A
5312356 Engelson et al. May 1994 A
5312415 Palermo May 1994 A
5334210 Gianturco Aug 1994 A
5336205 Zenzen et al. Aug 1994 A
5342387 Summers Aug 1994 A
5350397 Palermo et al. Sep 1994 A
5354295 Guglielmi et al. Oct 1994 A
5380304 Parker Jan 1995 A
5382259 Phelps et al. Jan 1995 A
5417708 Hall et al. May 1995 A
5421338 Crowley et al. Jun 1995 A
5437282 Koger et al. Aug 1995 A
5441516 Wang et al. Aug 1995 A
5443478 Purdy Aug 1995 A
5514176 Bosley, Jr. May 1996 A
5522822 Phelps et al. Jun 1996 A
5522836 Palermo Jun 1996 A
5527338 Purdy Jun 1996 A
5536274 Neuss Jul 1996 A
5540680 Guglielmi et al. Jul 1996 A
5549624 Mirigian et al. Aug 1996 A
5562641 Flomenblit et al. Oct 1996 A
5562698 Parker Oct 1996 A
5569245 Guglielmi et al. Oct 1996 A
5582619 Ken Dec 1996 A
5601600 Ton Feb 1997 A
5607445 Summers Mar 1997 A
5624449 Pham et al. Apr 1997 A
5624461 Mariant Apr 1997 A
5637113 Tartaglia et al. Jun 1997 A
5639277 Mariant et al. Jun 1997 A
5643254 Scheldrup et al. Jul 1997 A
5645082 Sung et al. Jul 1997 A
5645558 Horton Jul 1997 A
5649949 Wallace et al. Jul 1997 A
5667522 Flomenblit et al. Sep 1997 A
5669905 Scheldrup et al. Sep 1997 A
5669931 Kupiecki et al. Sep 1997 A
5676697 McDonald Oct 1997 A
5690643 Wijay Nov 1997 A
5690666 Berenstein et al. Nov 1997 A
5690667 Gia Nov 1997 A
5690671 McGurk et al. Nov 1997 A
5693067 Purdy Dec 1997 A
5697948 Marin et al. Dec 1997 A
5700258 Mirigian et al. Dec 1997 A
5718711 Berenstein et al. Feb 1998 A
5725546 Samson Mar 1998 A
5733329 Wallace et al. Mar 1998 A
5743905 Eder et al. Apr 1998 A
5746769 Ton et al. May 1998 A
5749891 Ken et al. May 1998 A
5749894 Engelson May 1998 A
5766160 Samson et al. Jun 1998 A
5800453 Gia Sep 1998 A
5800455 Palermo et al. Sep 1998 A
5800520 Fogarty et al. Sep 1998 A
5807404 Richter Sep 1998 A
5824037 Fogarty et al. Oct 1998 A
5830230 Berryman et al. Nov 1998 A
5843118 Sepetka et al. Dec 1998 A
5944733 Engelson Aug 1999 A
6013084 Ken et al. Jan 2000 A
Foreign Referenced Citations (14)
Number Date Country
32 03 410 Nov 1982 DE
197 04 269 Nov 1997 DE
0 183372 Jun 1986 EP
0 382014 Aug 1990 EP
0 747 012 Nov 1996 EP
0 747 014 Nov 1996 EP
0 820 726 Jan 1998 EP
2 066 839 Jul 1981 GB
WO 9410936 May 1994 WO
WO 9416629 Aug 1994 WO
WO 9518585 Jul 1995 WO
WO 9748351 Dec 1997 WO
WO 9907294 Feb 1999 WO
WO 9929260 Jun 1999 WO
Non-Patent Literature Citations (22)
Entry
Tottle, C.R., “An Encyclopaedia of Metallurgy and Materials”, pp. 3, 11, 323-4 1985.*
“Dictionary of Metallurgy” by D. Birchon, p. 182 1965.*
Christos A. Athanasoulis, M.D. The New England Journal of Medicine, May 15, 1980 “Therapeutic Applications of Angiography” pp. 1117-1125.
Christos A. Athanasoulis, M.D. The New England Journal of Medicine, May 22, 1980 “Therapeutic Applications of Angiography” pp. 1174-1179.
Alex Berenstein, M.D. and Irvin I. Kricheff, M.D. “Catheter and Material Selection for Transarterial Embolization: Technical Considerations” Radiology, Sep. 1979; pp. 631-639.
O.A. Battista, et al. Journal of Applied Polymer Science 1967 “Colloidal Macromolecular Phenomena. Part II. Novel Microcrystals of Polymers” PA 481-498.
Sadek K. Hilal, M.D. et al. Journal of Neurological Surgery “Therapeutic Percutaneous Embolization for Extra-Axial Vascular Lesions of the Head, Neck and Spine” Sep., 1975; pp. 275-287.
Stephen L. Kaufman, M.D. et al. Investigative Radiology, May-Jun. 1978 “Transcatheter Embolization with Microfibrillar Collagen in Swine”; pp. 200-204.
Ashok J. Kumar, et al., Journal of Neuroradiology (1982) “Preoperative Embolization of Hypervascular Head and Neck Neoplasms Using Microfibrillator Collagen”, pp. 163-168.
Richard E. Latchaw, M.D. et al., Radiology (1979) “Polyvinyl Foam Embolization of Vascular and Neoplastic Lesions of the Head, Neck and Spine” pp. 669-67.
Stewart R. Reuter, M.D. et al. American Journal of Radiology, Sep. 1975 “Selective Arterial Embolization for Control of Massive Upper Gastrointestinal Bleeding” pp. 119-126.
Glenn H. Roberson, et al., American Journal of Radiology, Oct. 1979 “Therapeutic Embolization of Juvenile Angiofibroma” pp. 657-663.
Sidney Wallace, M.D. et al., Cancer, Oct. 1979 “Arterial Occlusion of Pelvic Bone Tumors”; pp. 322-325 & 661-663.
“Mechanical Devices for Arterial Occlusion” by C. Gianturco, M.D., et al., Jul. 19 pp. 428-435.
“Therapeutic Vascular Occlusion Utilizing Steel Coil Technique: Clinical Applications” by Sidney Wallace, et al., Am J. Roentgenol (1976); pp. 381-387.
“Transcatheter Intravascular Coil Occlusion of Experimental Arteriovenous Fistulas”, by James H. Anderson, et al., Am. J. Roentgenol, Nov. 1977, pp. 795-798.
“‘Mini’ Gianturco Stainless Steel Coils for Transcatheter Vascular Occlusion” James H. Anderson, et al., from the Department of Diagnostic Radiology at the University of Texas System Cancer Center, Aug. 1978, pp. 301-303.
“A New Improved Coil for Tapered-Tip Catheter for Arterial Occlusion” by Vince P. Chuang, M.D., et al., May 1980, pp. 507-509.
“Neurosurgery Interactive Article Part 2—Clinical Studies Embolization of Cerebral Arteriovenous Malformations: Part II—Aspects of Complications and Late Outcome” by Christer Lunqvist, M.D., Ph.D., et al., Sep. 96, pp. 1-16.
“Shape Memory Alloys” by Jeff Perkins, pp. 1095-1096.
Y. Pierre Gobin, M.D., et al., “Treatment of Large and Giant Fusiform Intracranial Aneurysms with Guglielmi Detachable Coils,” J. Neurosurg., Jan. 1996, pp. 55-62, vol. 84.
Cameron G. McDougall, M.D., et al., “Endovascular Treatment of Basilar Tip Aneurysms Using Electrolytically Detachable Coils,” J. Neurosurg., Mar. 1996, pp. 393-399, vol. 84.