The present invention relates to a vehicular exterior member and a far-infrared camera equipped vehicular exterior member.
In recent years, various automatic sensors have been attached for the purpose of improving safety of vehicles in some cases. Examples of the sensors attached to vehicles include cameras, light detecting and ranging (LiDAR) sensors, millimeter wave radars, and infrared sensors.
Infrared rays are classified into near-infrared rays (e.g., wavelength ranging from 0.7 μm to 2 μm), mid-infrared rays (e.g., wavelength ranging 3 μm to 5 μm), and far-infrared rays (e.g., wavelength ranging 8 μm to 13 μm). Examples of the infrared sensors that detect those infrared rays include touch sensors, near-infrared cameras, and LiDAR sensors for detecting near-infrared rays, gas analyzers and mid-infrared spectroscopic analyzers (functional group analyzers) for detecting mid-infrared rays, and night visions and thermo viewers (hereinafter, referred to as far-infrared cameras) for detecting far-infrared rays.
Windowpanes of vehicles generally do not transmit far-infrared rays having a wavelength ranging from 8 μm to 13 μm. The far-infrared cameras have been often installed inside front grilles outside vehicle cabins such as a case described in Patent Literature 1. The far-infrared cameras to be installed outside vehicle cabins require more complex structures for achieving robustness, a water proof property, a dust proof property, and the like. As a result, the costs are increased. Such a problem can be solved by installing the far-infrared cameras inside vehicle cabins, particularly in working areas of windshield wipers, because the far-infrared cameras are protected by windowpanes. The far-infrared cameras, however, have not been installed inside vehicle cabins because of a far-infrared ray transmittance of the windowpanes as described above.
To cope with such problems, Patent Literature 2 discloses a window member including a member that can transmit infrared rays and is charged into a through hole opened on a part of a windshield.
In the window member described in Patent Literature 2, a through hole being too large causes a decrease in strength of the window member and an increase in amount of charged infrared ray transmissible member, resulting in an increase in a cost. In contrast, a through hole being too small causes a decrease in radiation amount of far-infrared rays that reach the far-infrared camera. As a result, a luminance reduction and a blur occur in obtained thermal images. In other words, sharpness of the thermal image is decreased. In Patent Literature 2, the size of the through hole is, however, not sufficiently examined. It has not yet been clear about a concrete structure of the window member that has practically sufficient strength, cost, and a viewing field of the far-infrared camera.
In view of such problems, the present invention is made and aims to provide a vehicular exterior member such as a window member that is excellent in strength and cost, and sufficiently ensures sharpness of a thermal image obtained by a far-infrared camera.
The present invention also aims to provide a far-infrared camera equipped vehicular exterior member, which is the vehicular exterior member to which a far-infrared camera is attached.
To solve the problem above, a vehicular exterior member of the present disclosure includes a light blocking region and is configured to be attached to a vehicle equipped with a far-infrared camera. The vehicular exterior member includes: in the light blocking region, a far-infrared ray transmitting region having an opening, and a far-infrared ray transmitting member that is disposed in the opening, wherein an average transmittance of far-infrared rays having a wavelength ranging from 8 to 13 μm of the far-infrared ray transmitting member is equal to or larger than 25%, a length of the longest straight line, in straight lines connecting any desired two points on a surface on a vehicle exterior side of the far-infrared ray transmitting member, is equal to or smaller than 80 mm, and a diameter of the largest circle, in circles formed in a projected shape obtained by projecting the far-infrared ray transmitting member in an optical axis direction of the far-infrared camera, is equal to or larger than 12 mm, and an average thickness of the far-infrared ray transmitting member is equal to or larger than 1.5 mm.
In one aspect of the vehicular exterior member of the present disclosure, the vehicular exterior member may be a vehicular window member.
In one aspect of the vehicular exterior member of the present disclosure, the vehicular exterior member may be an exterior member for a vehicular pillar.
In one aspect of the vehicular exterior member of the present disclosure, the far-infrared ray transmitting member may include at least one material selected from the group consisting of ZnS, Ge, Si, and chalcogenide glass.
In one aspect of the vehicular exterior member of the present disclosure, at least one of the surface on the vehicle exterior side and a surface on a vehicle interior side of the far-infrared ray transmitting member may be provided with an antireflection film including one to twelve layers, and the layer on the most vehicle exterior side of the antireflection film is a diamond-like carbon film.
In one aspect of the vehicular exterior member of the present disclosure, the surface on the vehicle exterior side of the far-infrared ray transmitting member may be formed flush with a surface on the vehicle exterior side of the light blocking region.
In one aspect of the vehicular exterior member of the present disclosure, the far-infrared ray transmitting member may be attached with at least one of a urethane-based adhesive and an acrylic adhesive.
In one aspect of the vehicular exterior member of the present disclosure, an area of the opening on a surface on a vehicle interior side may be smaller than the area of the opening on a surface on the vehicle exterior side.
In one aspect of the vehicular exterior member of the present disclosure, a visible light transmitting region may be provided in the light blocking region having a visible light transmittance equal to or larger than 70%.
A far-infrared camera equipped vehicular exterior member of the present disclosure comprises: the vehicular exterior member; and a far-infrared camera, wherein the far-infrared camera is attached to the vehicular exterior member in such a manner as to be capable of imaging an external thermal image through the far-infrared ray transmitting region.
The far-infrared camera equipped vehicular exterior member in one aspect of the present disclosure, may comprises the vehicular exterior member; a far-infrared camera; and a visible light camera, wherein the far-infrared camera is attached to the vehicular exterior member in such a manner as to be capable of imaging an external thermal image through the far-infrared ray transmitting region, and the visible light camera is attached to the vehicular exterior member in such a manner as to be capable of imaging an external image through the visible light transmitting region.
In one aspect of the far-infrared camera equipped vehicular exterior member of the present disclosure, an optical axis of the far-infrared camera and the optical axis of the visible light camera may be substantially in parallel, and a distance between the optical axes is equal to or smaller than 20 cm.
In one aspect of the far-infrared camera equipped vehicular exterior member of the present disclosure, the visible light camera may be a stereo camera including a first camera and a second camera, and the far-infrared camera is positioned between the first and the second cameras.
In one aspect of the far-infrared camera equipped vehicular exterior member of the present disclosure, the far-infrared camera may be attached to the vehicular exterior member with a bracket interposed therebetween, and an inside of the bracket is kept vacuum or filled with a heat insulator.
In one aspect of the far-infrared camera equipped vehicular exterior member of the present disclosure, the far-infrared camera is attached to the vehicular exterior member with a bracket interposed therebetween, and the far-infrared camera equipped vehicular exterior member further includes a temperature controller for adjusting a temperature inside the bracket.
The present invention provides the vehicular exterior member such as the window member that is excellent in strength and cost, and sufficiently ensures the sharpness of the thermal image obtained by the far-infrared camera. The present invention provides the far-infrared camera equipped vehicular exterior member, which is the vehicular exterior member to which the far-infrared camera is attached.
The following describes embodiments according to the present invention. The present invention is not limited to the following embodiments. The embodiments are schematically illustrated on the accompanying drawings for clearly describing the present invention. The drawings do not necessarily correctly illustrate the actual sizes and scales.
The embodiment of the vehicular exterior member of the present invention is not limited to the window member applied to the front windshield of a vehicle. For example, the window member may be applied to a rear windshield or a side windshield. The vehicular exterior member may be applied to an exterior member for other than the window member, for example may be applied to an exterior member or a pillar.
A glass base body 2 included in a window member 1 in the embodiment may be a single plate glass or a laminated glass. The glass base body 2 may be subjected to strengthening processing such as physical strengthening and chemical strengthening.
The window member 1 in the embodiment includes a light blocking region 3. The window member 1 generally includes a light transmitting region 4 at its central portion for ensuring the driver's viewing field and the light blocking region 3 surrounding the light transmitting region 4. As illustrated in
The light blocking region 3 is formed by providing a light blocking layer 5 on the glass base body 2 constituting the window member 1. The light blocking region 3 corresponds to the region in which the light blocking layer 5 is provided on the glass base body 2 in a plan view of the window member 1.
A ceramic light blocking layer or a light blocking film can be used for the light blocking layer 5, for example. For the ceramic light blocking layer, a ceramic layer can be used that includes a known material, such as a black ceramic layer. For the light blocking film, a light blocking polyethylene terephthalate (PET) film, a light blocking polyethylene naphthalate (PEN) film, and a light blocking polymethylmethacrylate (PMMA) film can be used, for example.
The light blocking layer 5, which is generally formed on the surface on a vehicle interior side of the glass base body 2, may be formed on the surface on a vehicle exterior side of the glass base body 2. When the glass base body 2 is a laminated glass, the light blocking layer 5 may be formed between two glasses forming the laminated glass.
The window member 1 in the embodiment includes a far-infrared ray transmitting region 6 in the light blocking region 3.
The far-infrared ray transmitting region 6 has an opening 7 formed in the light blocking region 3 and a far-infrared ray transmitting member 8 disposed in the opening 7.
When an average transmittance of far-infrared rays having a wavelength ranging from 8 to 13 μm of the far-infrared ray transmitting member 8 is smaller than 15%, the far-infrared ray transmittance in the far-infrared ray transmitting region 6 is insufficient. As a result, the far-infrared camera does not sufficiently demonstrate its performance. The average transmittance of the far-infrared rays having a wavelength ranging from 8 to 13 μm of the far-infrared ray transmitting member 8 in the embodiment is equal to or larger than 25%, preferably equal to or larger than 40%, more preferably equal to or larger than 50%, furthermore preferably equal to or larger than 70%, and particularly preferably equal to or larger than 85%. It is essential for increasing the average transmittance of far-infrared rays 85% or more to provide an antireflection film.
The material of the far-infrared ray transmitting member is not limited to a specific one as long as the transmittance described above is satisfied. Examples of the material include ZnS, Ge, Si, and chalcogenide glass.
A preferable composition, which is expressed as an atomic percentage, of the chalcogenide glass is as follows:
The method of attaching the far-infrared ray transmitting member 8 to the opening 7 is not limited to a specific one. For example, both can be attached to each other with an adhesive such as a urethane-based adhesive and/or an acrylic adhesive. In general, a difference in thermal expansion between the windowpane of the vehicle and the far-infrared ray transmitting member is large. It is thus preferable to select an adhesive that can lessen the difference, and is excellent in adhesive strength, impact resistance, and environmental resistance. The adhesion surface on the vehicle exterior side may be covered with a resin, for example, to enhance the environmental resistance.
A gap of 0.2 to 1.5 mm is preferably provided between the far-infrared ray transmitting member 8 and the opening 7. When the gap is smaller than 0.2 mm, the thermal expansion difference between the windowpane of the vehicle and the far-infrared ray transmitting member may cause the windowpane to be optically distorted or the windowpane and/or the far-infrared ray transmitting member to be damaged. The gap is more preferably equal to or larger than 0.3 mm, and furthermore preferably equal to or larger than 0.5 mm. When the gap is larger than 1.5 mm, the adhesive strength and the impact resistance may be lessened. The gap is more preferably equal to or smaller than 1.2 mm, and furthermore preferably equal to or smaller than 1.0 mm.
As illustrated in
The surface on the vehicle exterior side and/or the surface on the vehicle interior side of the far-infrared ray transmitting member 8 may be coated. For example, the surface on the vehicle exterior side or the vehicle interior side, or both sides, i.e., at least one of the surfaces on the vehicle exterior side and the surface on the vehicle interior side may be provided with an antireflection film. The antireflection film is preferably including one to twelve layers. The material is not limited to a specific one. Preferable examples of the material include Ge, Si, ZnS, ZnSe, As2S3, As2Se3, metal oxides (Al2O3, Bi2O3, CeO2, CuO, HfO2, MgO, SiO, SiO2, TiO, TiO2, Ti2O3, Y2O3, and ZrO2), hydrogenated carbon, diamond-like carbon (DLC), and metal fluorides (MgF2, CaF2, SrF2, BaF2, PbF2, LaF3, and YF3). The layer on the most vehicle exterior side is preferably a film that has a Mohs hardness of 7 or more and a high far-infrared ray transmittance from the viewpoint of scratch resistance. The layer on the most vehicle exterior side is particularly preferable a diamond-like carbon film.
The shape of the far-infrared ray transmitting member 8 is not limited to a specific one. The shape is preferably a plate-like shape corresponding to the shape of the opening 7. For example, when the shape of the opening 7 is circle, the far-infrared ray transmitting member 8 preferably has a disk (columnar) shape.
As illustrated in
The thickness of the far-infrared ray transmitting member 8 is equal to or larger than 1.5 mm, preferably equal to or larger than 2.0 mm, and more preferably equal to or larger than 3.0 mm from the viewpoint of strength. The thickness of the far-infrared ray transmitting member 8 is not limited to a specific one as long as the average transmittance of the far-infrared rays having a wavelength ranging from 8 to 13 μm is secured. The thickness is typically equal to or smaller than 5.0 mm.
The far-infrared ray transmitting member may have a lens shape to achieve both widening a viewing angle of the far-infrared camera and improving mechanical characteristics thereof, for example. Such a structure is preferable because far-infrared rays can be efficiently converged even when the area of the far-infrared ray transmitting member is small. In this case, the number of far-infrared ray transmitting members having a lens shape is preferably one to three. Typically, two is preferable. It is particularly preferable that the far-infrared ray transmitting member having a lens shape be preliminarily aligned and modularized, and be integrated with a housing or a bracket that adhesively bonds the far-infrared camera to the vehicular exterior member.
When the surface on the vehicle exterior side of the far-infrared ray transmitting member 8 is too large, the strength of the window member is insufficient. The length of the longest straight line, in the straight lines connecting any desired two points on the surface on the vehicle exterior side of the far-infrared ray transmitting member 8 in the embodiment, is equal to or smaller than 80 mm, preferably equal to or smaller than 70 mm, and more preferably equal to or smaller than 65 mm. When the shape of the surface on the vehicle exterior side of the far-infrared ray transmitting member 8 is circle, the length is the diameter of the circle.
A radiation amount of far-infrared rays reaching the far-infrared camera attached to the window member 1 in the embodiment depends on the size of a largest circle, the largest circle is largest in circles formed inside a projected shape obtained by projecting the far-infrared ray transmitting member 8 in an optical axis of the far-infrared camera. The details are described below with reference to the drawings.
The inventors had repeated experiments and found that, when the diameter of the circle 12, which is the largest circle in the circles formed inside the projected shape 11, is smaller than 12 mm, the radiation amount of far-infrared rays reaching the far-infrared camera 9 is reduced, causing the occurrence of luminance reduction and a blur in the obtained thermal image, thereby making it difficult to sufficiently ensure sharpness of the thermal image.
In the window member 1 in the embodiment, the diameter of the circle 12, which is the largest circle in the circles formed inside the projected shape 11 obtained by projecting the far-infrared ray transmitting member 8 in the optical axis direction X of the far-infrared camera 9, is equal to or larger than 12 mm, preferably equal to or larger than 20 mm, and more preferably equal to or larger than 30 mm.
The projected shape 11 obtained by projecting the far-infrared ray transmitting member 8 in the optical axis X direction of the far-infrared camera 9 is the drawing obtained by projecting, in the optical axis X, the shape of the surface on the vehicle exterior side of the far-infrared ray transmitting member 8 on the plane perpendicular to the optical axis X.
Although depending on the size of the far-infrared ray transmitting member 8 and the thickness of the glass base body 2, the following inconveniences occur when an angle α is too small that is the tilt of the window member 1 in the embodiment with respect to the horizontal line when the window member 1 is attached to the vehicle. In a case where the angle α is too small, a region where only the far-infrared ray transmitting member 8 is included, i.e., a region where the glass base body and the light blocking layer are not included (a region Y in
As illustrated in
The window member 1 in the embodiment preferably further includes, in the light blocking region 3, a visible light transmitting region 13 having a visible light transmittance equal to or larger than 70%. Provision of the visible light transmitting region 13 allows attaching of a visible light camera that images the outside through the visible light transmitting region 13.
The attaching of the visible light camera in addition to the far-infrared camera makes it possible to combine pieces of information obtained by the two cameras and recognize information about the outside of the vehicle, thereby helping with increasing accuracy of object recognition. When the far-infrared ray transmitting region 6 and the visible light transmitting region 13 are arranged in the light blocking region 3, the far-infrared camera and the visible light camera can be attached close to each other, which reduces a load in arithmetic processing of pieces of data obtained from each camera, and allows preferable routing of a power source and signal cables.
The visible light transmitting region 13 is a region where the light blocking layer 5 is not provided in part of the light blocking region 3.
The window member 1 in the embodiment may further include a LiDAR sensor and a millimeter wave radar besides the visible light camera.
<Far-Infrared Camera Equipped Vehicular Exterior Member>
The following describes a far-infrared camera equipped vehicular exterior member of the present invention.
The vehicular exterior member in the embodiment is not limited to the window member applied to the front windshield of the vehicle, likewise as described above.
The far-infrared camera equipped window member 100 in the embodiment includes the window member 1 and the far-infrared camera 9. The window member 1 is already described. The far-infrared camera 9 is attached to the window member 1 in such a manner as to be capable of imaging external thermal images through the far-infrared ray transmitting region of the window member 1.
The type of the far-infrared camera 9 is not limited to a specific type, and known far-infrared cameras can be used. The far-infrared camera 9 is attached to the window member 1 with a bracket 14, for example. The far-infrared camera 9 is generally attached such that the optical axis X is substantially horizontal.
In order to make the image (thermal image) obtained by the far-infrared camera 9 sharp, the temperature of the far-infrared camera 9 is preferably kept constant.
One of the methods of keeping the temperature of the far-infrared camera 9 constant is to achieve high heat insulating property inside the bracket 14. For achieving a high heat insulating property inside the bracket 14, the inside of the bracket 14 may be kept vacuum or the inside of the bracket 14 may be filled with a heat insulator. It is preferable for the far-infrared camera equipped window member 100 in the embodiment that the far-infrared camera 9 be attached to the window member 1 via through bracket 14 and the inside of the bracket 14 be kept vacuum or filled with a heat insulator.
Another method of keeping the temperature of the far-infrared camera 9 constant is to adjust the temperature inside the bracket 14 by a temperature controller. It is preferable for the far-infrared camera equipped window member 100 in the present embodiment to include the far-infrared camera 9 that is attached to the window member through the bracket 14 and further include a temperature controller to adjust the temperature inside the bracket 14.
When the window member 1 has the visible light transmitting region 13, it is preferable for the far-infrared camera equipped window member 100 in the present embodiment to further include the visible light camera that is attached to the window member 1 so as to be able to image external images through the visible light transmitting region 13.
Providing the visible light camera in addition to the far-infrared camera makes it possible to combine pieces of information obtained by the two cameras and recognize information about the outside of the vehicle, as described above.
In this case, it is preferable that the optical axis of the far-infrared camera and the optical axis of the visible light camera be substantially in parallel, and the distance between the optical axes be equal to or smaller than 20 cm. The term substantially in parallel includes not only a case where those optical axes are completely in parallel but also a case where those optical axes are slightly out of parallel within a degree of an error. Being substantially in parallel allows the optical axis of the far-infrared camera and the center of the viewing field of the visible light camera to substantially coincide, and is preferable for information processing with images obtained from those cameras being combined.
The visible light camera may be a stereo camera including a first camera and a second camera. In this case, the far-infrared camera is preferably disposed between the first and the second cameras. It is also preferable that the optical axes of the far-infrared camera and the first and second cameras be substantially in parallel, and the distance between the optical axes of any two of the three cameras be equal to or smaller than 20 cm.
The LiDAR sensor and a millimeter wave radar may be further included beside the visible light camera, for example. In this case, those sensors are preferably arranged adjacent to one another while signal interference is prevented.
The following describes the present invention specifically with examples. The present invention is, however, not limited to the examples.
<Preparation of Far-Infrared Ray Transmitting Member>
Cylindrical far-infrared ray transmitting members (far-infrared ray transmitting members A to Q), each of which includes any one of Si, Ge, ZnS, and chalcogenide glass, and shaped in a column with a different size, were prepared. The material, a diameter L, and a thickness t of each of the far-infrared ray transmitting members are illustrated in Tables 1 to 3.
The far-infrared ray transmitting member J was made as follows. A glass raw material was mixed to have a composition expressed as an atomic percentage as follows: Ga is 6.0%, Sb is 24.0%, Sn is 4.0%, S is 62.0%, Cs is 2.0%, and Cl is 2.0%. The mixed material was sealed in a quartz glass tube having an inner diameter of 25 mm, and then heated to 750° C. and melted for four hours. The melted glass was rapidly cooled and then slowly cooled. The resulting ingot was cut together with the quartz glass tube and polished. As a result, the far-infrared ray transmitting member J was obtained.
A five-layer antireflection film including Ge, Si, and YF3 was formed on the surface on the vehicle exterior side of the far-infrared ray transmitting member O by a vapor deposition method. A two-layer antireflection film including DLC and Si was formed on the surface on the vehicle exterior side of the far-infrared ray transmitting member P, and a five-layer antireflection film including ZnS and Ge was formed on the surface on the vehicle interior side of the far-infrared ray transmitting member P by the vapor deposition method. A single layer of antireflection film including DLC was formed on the surface on the vehicle exterior side of the far-infrared ray transmitting member Q and a two-layer antireflection film including ZnS and Ge was formed on the surface on the vehicle interior side of the far-infrared ray transmitting member Q by the vapor deposition method.
<Measuring Average Transmittance of Far-Infrared Rays Having a Wavelength Ranging from 8 to 13 μm>
An infrared ray transmission spectrum of each far-infrared ray transmitting member was measured by a Fourier transformation infrared spectroscopy (product name: Nicolet iS10 manufactured by Thermo Scientific) and the average transmittance of far-infrared rays having a wavelength ranging 8 to 13 μm was obtained from the infrared ray transmission spectrum. The results are illustrated in Tables 1 and 2.
<Manufacturing of Window Member>
A laminated glass was prepared that included two soda lime glass sheets each having a size of 300 mm square and a thickness of 2.0 mm, and PVB having a thickness of 0.76 mm interposed between the two glass sheets. A through hole having a diameter of 14 mm was formed at the position apart from the center of the laminated glass by 100 mm in the direction toward the side of the glass sheet, the position serving as the center of the through hole.
The far-infrared ray transmitting member A was attached to the through hole in such a manner as to be flush with the surface on the outside of the glass sheet with a urethane-based adhesive. As a result, the window member in example 1 was obtained. The urethane-based adhesive was dried for 5 days at ordinary temperature to be hardened.
The window members in examples 2 and 3 were obtained in the same manner as example 1 except for that the diameter of the through hole was 26.5 mm and the far-infrared ray transmitting member B and C were attached respectively.
The window member in example 4 was obtained in the same manner as example 3 except for that an acrylic adhesive was used. The acrylic adhesive was dried at 120° C. for 1 hour, and was dried at ordinary temperature for 5 days to be hardened.
The window members in examples 5 to 8 were obtained in the same manner as example 2 except for that the far-infrared ray transmitting members D to G were attached respectively.
The window member in example 9 was obtained in the same manner as example 8 except for that an acrylic adhesive was used. The acrylic adhesive was dried at 120° C. for 1 hour, and was dried at ordinary temperature for 5 days to be hardened.
The window members in examples 10 to 13 were obtained in the same manner as example 2 except for that the far-infrared ray transmitting members H to K were attached respectively.
The window members in examples 14 and 15 were obtained in the same manner as example 1 except for that the diameter of the through hole was 51.5 mm and the far-infrared ray transmitting members L and M were attached respectively.
The window member in example 16 was obtained in the same manner as example 1 except for that the diameter of the through hole was 91.5 mm and the far-infrared ray transmitting member N was attached.
The window members in examples 17 to 19 were obtained in the same manner as example 1 except for that the diameter of the through hole was 51.5 mm and the far-infrared ray transmitting members O, P, and Q were attached respectively.
<Ball Drop Strength Evaluation>
Ball drop strength evaluations 1 and 2 described below were done using the window members in examples 1 to 19. The window material that was passed in both tests was evaluated as “passed” while the window material that was failed in either one of the tests was evaluated as “failed”. The evaluation results are illustrated in Tables 1 and 2. (Ball drop strength evaluation 1)
The evaluation was done using a ball drop device and a supporting frame in compliance with the impact resistance test in JIS R3211 and 3212-2015.
The window member was kept in a room under conditions of a temperature of 23° C. and a relative humidity of 50% for 4 hours, and then was fixed by the supporting frame such that the surface outside the window member faces upward. A steel ball of 226 g was dropped onto the center of the window member from a height of 10 m. When the steel ball did not pass through the window member and the total weight of peeled off fragments from the side opposite the impacted surface was equal to or smaller than 15 g, the window member was determined to be accepted. (Ball drop strength evaluation 2)
The test was done in the same manner as the ball drop evaluation 1 except for that a steel ball of 509 g was used. When the far-infrared ray transmitting member was not broken or was not removed from the window member, and the total weight of peeled off fragments from the side opposite the impacted surface was equal to or smaller than 15 g, the window member was determined to be accepted.
<Thermal Image Visual Recognition Evaluation>
The following thermal image recognition evaluation was done using the window members in examples 1 to 19.
The window member was disposed in such a manner as to make an angle of α with respect to the horizontal surface. A far-infrared ray camera was disposed such that the optical axis was horizontal and coincided with the center of the far-infrared ray transmitting member, and the housing thereof was in contact with the window member. The far-infrared camera was Cube 417 manufactured by Wuhan Guide Infrared Co. Ltd. (resolution: 400×300, horizontal angle of view: 20°, vertical angle of view: 15°, and focal distance: 19 mm).
As illustrated
The window member in example 1 was tested at α=30°, 60°, and 90°.
The window members in example 2, 5, 7, 10, 12, 13, and 19 were tested at α=30° and 45°.
The window members in example 3, 6, 8, 11, and 14 to 18 were tested at α=30°.
The window members in examples 4 and 9, in which only the type of the adhesive is different from that in examples 3 and 8, were not tested because it was considered that the window members in examples 4 and 9 have the same thermal image visual recognition evaluation results as those in examples 3 and 8.
Tables 1 and 2 illustrate the values of α, the values of the diameter R of the largest circle in the circles formed inside the projected shape obtained by projecting the far-infrared ray transmitting member in the optical axis direction, and the values of the thermal image contrast.
The following describes the results of the ball drop strength evaluation of the examples.
The strength was insufficient in example 2, 7, and 14, which used the far-infrared ray transmitting members B, F, and L, each having the thickness t of 1 mm, respectively.
The strength was insufficient in example 16, which used the far-infrared ray transmitting member N having the diameter L of 90 mm and the thickness t of 3 mm.
In contrast, the strength was sufficiently high in examples 1, 3 to 6, 8 to 13, 15, and 17 to 19, which used the far-infrared ray transmitting members A, C to E, G to K, M, and O to Q, each having the thickness t of 1.5 mm or more and the diameter L of 80 mm or less, respectively.
The following describes the results of the thermal image visual recognition evaluation of the examples.
In example 1, the thermal image contrast was insufficient and the sharpness of the thermal image was low as illustrated in
The thermal image contrast was insufficient in the test in example 6 where the far-infrared ray transmitting member E was used. The average transmittance of far-infrared rays having a wavelength ranging from 8 to 13 μm of the far-infrared ray transmitting member E was 14%.
The thermal image contrast was sufficient in the tests in examples 2, 3, 5, 7, 8, and from 10 to 19, in each of which R was 12 mm or more, and the average transmittance of far-infrared rays having a wavelength ranging from 8 to 13 μm of the far-infrared ray transmitting member was 25% or more.
As apparent from the results described above, the far-infrared ray transmitting member had both high strength and sufficient thermal image contrast when the far-infrared ray transmitting member satisfied the following conditions. The thickness t was equal to or larger than 1.5 mm, the diameter L was equal to or smaller than 80 mm, the average transmittance of far-infrared rays having a wavelength ranging from 8 to 13 μm was equal to or larger than 25%, and the diameter R of the largest circle in the circles formed inside the projected shape obtained by projecting the far-infrared ray transmitting member in the optical axis direction was equal to or larger than 12 mm.
The international application claims the priority of Japanese Patent Application No. 2019-136326, filed on Jul. 24, 2019, and all contents of which are incorporated herein.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2019-136326 | Jul 2019 | JP | national |
This application is a continuation of International Application No. PCT/JP2020/024384, filed on Jun. 22, 2020, the entire contents of which are incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 8544933 | Fuller | Oct 2013 | B1 |
| 10336163 | Sakamoto et al. | Jul 2019 | B2 |
| 20030169491 | Bender et al. | Sep 2003 | A1 |
| 20070216768 | Smith et al. | Sep 2007 | A1 |
| 20110249344 | Nagatoshi | Oct 2011 | A1 |
| 20160259102 | Taka | Sep 2016 | A1 |
| 20160284075 | Phan | Sep 2016 | A1 |
| 20170015180 | Sakamoto | Jan 2017 | A1 |
| 20200401010 | Watanabe | Dec 2020 | A1 |
| 20210122671 | Hart | Apr 2021 | A1 |
| Number | Date | Country |
|---|---|---|
| 101037099 | Sep 2007 | CN |
| 106103158 | Nov 2016 | CN |
| 2 271 139 | Apr 1994 | GB |
| 2008-236062 | Oct 2008 | JP |
| 2015-175745 | Oct 2015 | JP |
| 2016-001870 | Jan 2016 | JP |
| 2018-119856 | Aug 2018 | JP |
| WO 2015137518 | Sep 2015 | WO |
| Entry |
|---|
| International Search Report dated Aug. 11, 2020 in PCT/JP2020/024384 filed on Jun. 22, 2020, 3 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20220132047 A1 | Apr 2022 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP2020/024384 | Jun 2020 | WO |
| Child | 17647193 | US |