The disclosure generally pertains to vertically lapped (perpendicular-laid) nonwoven applications in eyewear, and more specifically the use of nonwoven layers for enhanced antifogging and moisture absorbency in eyewear.
Fogging in eyewear is frequently caused by differences in temperature and humidity between the inner and outer surfaces of the lens. When the warm air (e.g. from the body heat or exhaled breath traveling upward while wearing a mask, etc.) hits the inside of a lens and the outer surface of the lens is exposed to lower temperature simultaneously, the water in the air condenses into droplets that cling to the inside surface of the lens, obscuring the vision. The fogging on the inside surface of the lens worsens as the accumulation of sweat and body fluids increases due to poor moisture management. In particular, with a specific type of eyewear that seals around or fits snugly to the wearer's face (e.g. sports goggles), the condensation is held by the portion of the eyewear and the increased humidity inside further promotes fogging, which can be wiped clean only by removing the eyewear from the face. In goggles, for example, use of foam materials, e.g. polyurethane foam, etc., for a sealing layer of the goggle exacerbates the moisture retention, as the foam is known for good resiliency yet poor breathability, and requires extensive air-drying after use.
Current strategies of antifogging in goggles generally involve three approaches. One is to ventilate around the rims of eyewear to keep the temperature of inside and outside of the eyewear consistent. Another method is to build double pane lenses harboring a layer of air between each lens in efforts to keep the temperature the same. Yet another way of controlling fogging is to coat the lenses with hydrophilic material that absorbs moisture. One example of coating the lens is disclosed in U.S. Pat. No. 5,476,682 (Evans); both the inside and outside of the lens surfaces are coated with materials known for anti-reflection, anti-static, and anti-fog functions. U.S. Pat. No. 4,317,240 (Angerman) discloses a pair of sports goggles that have a slot at the top portion of a lens for assisting airflow to pass and to prevent fogging. U.S. Pat. No. 6,282,728 (Baragar) describes a dual lens structure of goggles that permits fluid to flow between the anterior and posterior lenses.
Such strategies, however, do not provide solutions for some known concerns caused by modifying lenses; e.g., poor optical clarity, cracking, streaking or haziness, opalescence, poor adhesion, oily surface, and unevenly coated lenses. Other strategies of antifogging, such as a dual lens structure or adding a venting gap in the frame, have similarly failed to provide the most desired results in that these methods are not effective in removing condensation and moisture. There is a need in the art for improved antifogging methods and more specifically to prevent fogging and to remove moisture caused by perspiration while wearing the eyewear in the most comfortable and efficient manner.
An object of the invention is to use vertically lapped nonwoven as a replacement of a foam sealing layer in eyewear to reduce fogging and moisture retention. In a particular preferred embodiment, the eyewear disclosed herein provides a lens, a frame, vertically lapped nonwoven layers and a strap. To enhance antifogging and fast-drying after use, additional lenses and/or frame with additional venting system may be further assembled into the eyewear.
One aspect of the disclosure provides nonwoven layers that are in a multi-layered system, and most preferably, in a dual layer in which each layer is completely or partially formed from hydrophobic or hydrophilic materials. Dual layer of hydrophilic and hydrophobic materials offers numerous advantages over commonly used polyurethane foam as a sealing layer including: versatility, higher cushioning, high resiliency, higher breathability, superior cooling, eco-friendly and excellent mechanical properties. As noted above, the vertically lapped nonwovens comprising different “wettability” materials may be further folded and bonded together to create a multi-layer, and most preferably a dual layer, providing further superiority in air permeability and efficient moist air circulating system.
In one embodiment, hydrophilic fibers (e.g. cellulosic fibers) and hydrophobic fibers (e.g. polyester fibers) are used for the inner and the outer layer, respectively. As such, the inner layer with hydrophilic materials absorbs and wicks moisture and/or perspiration from wearer's face and transfers the moisture to the hydrophobic outer layer for efficient evaporation of the condensation, thus managing wetness at the source as well as keeping the surface dry for comfortable wear. In addition, the nonwoven dual layer disclosed herein is environmentally friendly (completely or partially made from recycled materials), odorless and does not emit volatile organic compounds.
Additional features and advantages of the present invention will be set forth in the description of disclosure that follows, and in part will be apparent from the description of may be learned by practice of the disclosure. The disclosure will be realized and attained by the compositions and methods particularly pointed out in the written description and claims hereof.
The preferred embodiments of the present disclosure are directed toward antifogging layers of vertically lapped nonwovens in eyewear. These embodiments benefit from an absorbency, breathability, as well as a cushioning functionality which can be achieved with vertically lapped nonwovens incorporated into various types of eyewear. As used herein, by “eyewear”, it is meant one or a plurality of devices that are used for protection of the eyes. Some exemplary types of eyewear include, but are not limited to, safety goggles, sports goggles, eyeglasses, sunglasses, etc. The present nonwoven layers are highly suited as a replacement of a foam (e.g. polyurethane)-based sealing layer in eyewear where the one side of the layer comes in direct contact with the face of the wearer. All or portions of the nonwoven layers disclosed herein are vertically lapped.
As used herein, the term “vertically lapped” is meant that one or a plurality of materials is in the form of a web that has been folded in on itself in a corrugated fashion to produce a three-dimensional structure that has been thermally bonded and often is referred to as perpendicular laid. A “vertical lapper” is also referred to as a “STRUTO” or a “V-LAP” and some examples of machinery which may be used to make vertically lapped nonwovens for use in the invention are herein incorporated by reference (WO 2015176099 to Cooper and U.S. Pat. No. 7,591,049 to Cooper). Vertically lapped nonwovens are higher in compressional thermal resistance and lighter in weight than those made of fibers horizontally lapped, horizontally cross-lapped, horizontally woven and/or polyurethane foams. The vertically lapped nonwoven process takes a carded fiber web and laps it vertically (i.e. pleating) rather than horizontally laying the fibers. The size, shape and arrangement of the material of nonwovens may vary widely as long as nonwovens are made directly from separate fibers, molten plastic or plastic films, but not made by weaving or knitting. In an exemplary embodiment, the nonwoven is manufactured by hot-air thermal bonding using low-melt and/or elastomeric binder fibers. The binding fibers serve to mix readily with the other fibers of a nonwoven, and to melt on application of heat and then to re-solidify on cooling to hold the other fibers in the nonwoven together. In some applications, the binding fibers might have a core-sheath configuration where the sheath melts on application of heat and functions to hold the other fibers of the nonwoven together.
In particular, the nonwoven can have a basis weight ranging from 0.1-5.0 oz/ft2; however, the basis weight of the nonwoven can vary widely depending on the intended application and desired characteristics of the nonwoven. A plurality of fibers, from natural to synthetic, may be used for manufacture of vertically lapped nonwovens. The nonwoven can include combinations of two or more different natural fibers; two or more different man-made synthetic fibers; blends containing one or more natural fibers and one or more man-made fibers. Exemplary fibers which can be used in the practice of the invention include but are not limited to:
cotton, kapok, flax, ramie, kenaf, abaca, coir, hemp, jute, sisal, rayon, bamboo fiber, Tencel®, and Modal® fibers, glass fibers, basalt fibers, Kevlar® fibers, aramid fibers, polyester fibers (e.g., which can function both as a binder fiber but, depending on the polyester, as part of the nonwoven blend), wool (which may be obtained, for example, from one of the forty or more different breeds of sheep, and which currently exists in about two hundred types of varying grades), silk, rayon (a man-made fiber that may include viscose rayon and cuprammonium rayon), acetate (a man-made fiber), nylon (a man-made fiber), acrylic (a man-made fiber), polyester (a man-made fiber), triacetate (a man-made fiber), spandex (an elastomeric man-made fiber such as Lycra®), polyolefin/polypropylene (man-made olefin fibers), microfibers and microdeniers, lyocell (a man-made fiber), vegetable fiber (a textile fiber of vegetable origin, such as cotton, kapok, jute, ramie, polylactic acid (PLA) or flax), vinyl fiber (a manufactured fiber), alpaca, angora, carbon fiber (suitable for textile use); (t) glass fiber (suitable for textile use), raffia, ramie, vinyon fiber (a manufactured fiber), Vectran® fibers (manufactured fiber spun from Celanese Vectra® liquid crystal polymer), and waste fiber. Fibers are commercially available from sources known by those of skill in the art, for example, E.I. Du Pont de Nemours & Company, Inc. (Wilmington, Del.), American Viscose Company (Markus Hook, Pa.), Teijin Frontier Co., Ltd. (Osaka, Japan), Tintoria Piana USA (Cartersville, Ga.), and Celanese Corporation (Charlotte, N.C.).
The nonwoven can be formed using fibers that are treated with chemicals (e.g., dyes (for coloring of some or all of the fibers), fire retardant chemicals (e.g., phosphates, sulfates, silicates, etc.), scent's (perfumes, etc.), topical additives such as phase change material particles, talc, carbon nanotubes, etc.). Alternatively, a plurality of chemicals (e.g., dyes, scents, fire retardant chemicals, addition of microparticles, etc.) may be used to treat the nonwoven after completion of the final assembly of a structure.
In some embodiments, the vertically lapped nonwoven layers may be arranged as a single layer or multiple layers. It is preferred that the vertically lapped nonwoven layer has a height/thickness within the range of 0.125 to 1 inch, more preferably 0.125 to 0.75 inches, e.g. 0.25 to 0.5 inches. The preferred thickness is around 0.25 inches. The aforementioned thicknesses are preferred for the sealing layer, where the layer is in a single layer form. In dual layer form, each layer of nonwoven may be and is preferably made in the same or different thicknesses. The aforementioned thicknesses may also be for the combined multilayer construction.
In a particularly preferred embodiment of the invention, the vertically lapped nonwovens are in a dual layer system 13, as shown in
In
Instead of commonly used polymeric foam material, a two or more layers (e.g. 2, 3, 4, 5, or 6 or more layers) of nonwovens 28 are placed between the frame 23 and the wearer's face. The nonwoven dual layer 28 is essentially the same as the dual layer 13 depicted in
As shown in
The dual layer system preferably has the length, width, depth and shape which are complementary to the size and shape of the rim of the frame so as to assist in positioning and securing the eyewear on the face without disturbing the view range. The vertically lapped nonwoven dual layer has a thickness within the range of 0.125 to 1.5 inch, more preferably 0.125 to 1 inches, and most preferably 0.125 to 0.5 inches. The preferred thickness is around 0.25 inches. In a dual layer, the size and/or thickness of the inner hydrophilic layer may be smaller, equal or larger than that of the outer hydrophobic layer. Preferably, the thickness of the inner layer matches the thickness of the outer layer. In a preferred dual layer embodiment, as shown in
In some embodiments, as shown in
Referring to
In particularly preferred embodiments, the nonwovens layers disclosed herein are environmentally-friendly as the nonwovens are recyclable after proper treatment in the appropriate facilities. In addition, 10-100% of the nonwovens and materials for the nonwovens used for the goggle layers may be from recycled fabrics and the percentage of recycled fabrics varies based upon the strength of material needed for the intended applications and desired characteristics of the eyewear.
It is to be understood that this invention is not limited to particular embodiments described, as such may, of course, vary. It is also to be understood that the terminology used herein is for the purpose of describing particular embodiments only, and is not intended to be limiting, since the scope of the present invention will be limited only by the appended claims.
Where a range of values is provided it is understood that each intervening value, to the tenth of the unit of the lower limit unless the context clearly dictates otherwise, between the upper and lower limit of that range and any other stated or intervening value in that state range, is encompassed within the invention. The upper and lower limits of these smaller ranges may independently be included in the smaller ranges and are also encompassed within the invention, subject to any specifically excluded limit in the stated range. Where the stated range includes one or both of the limits, ranges excluding either or both of those included limits are also included in the invention.
It is noted that, as used herein and in the appended claims, the singular forms “a”, “an”, and “the” include plural referents unless the context clearly dictates otherwise. It is further noted that the claims may be drafted to exclude any optional element. As such, this statement is intended to serve as antecedent basis for use of such exclusive terminology as “solely”, “only” and the like in connection with the recitation of claim elements, or use of a “negative” limitation.
As will be apparent to those of skill in the art upon reading this disclosure, each of the individual embodiments described and illustrated herein has discrete components and features which may be readily separated from or combined with the features of any of the other several embodiments without departing from the scope or spirit of the present invention. Any recited method can be carried out in the order of events recited or in any other order which is logically possible.
While the invention has been described in terms of its preferred embodiments, those skilled in the art will recognize that the invention can be practiced with modification within the spirit and scope of the appended claims. Accordingly, the present invention should not be limited to the embodiments as described above, but should further include all modifications and equivalents thereof within the spirit and scope of the description provided herein.
This application claims priority to U.S. Provisional Application 62/975,241 filed on Feb. 12, 2020. The complete content thereof is herein incorporated by reference.