Vibration-proof damping polymer material

The present invention relates to vibration-proof damping polymer materials.
Conventionally, structural members of rolling stock, ships, automotive parts, apparatus, machines, building materials, acoustic materials, etc. are prevented from vibration on the rear side thereof and from producing noise due to vibration by giving an increased thickness to the member, improving the device or material itself or using damping materials. Various damping materials have heretofore been proposed. For example, materials are well known which are prepared by admixing rubber, resin or asphalt with an inorganic filler such as graphite, carbon black, mica, asbestos, calcium carbonate, talc or metal powder. Damping materials primarily incorporating asbestos have an effect to prevent noise due to vibration, i.e., a damping effect, whereas they are deficient in an effect to prevent acoustic radiation, i.e., in noise insulating property, because they are low in specific gravity. On the other hand, noise insulating materials chiefly incorporating a metal powder are deficient in damping effect and therefore unsatisfactory although having a noise insulating property. Further in the case where the noise insulating material is attached directly to machines or devices mentioned above which produce vibration and noise and which are likely to become heated to a temperature as high as 80.degree. to 120.degree. C., the material exhibits a lower damping effect or softens itself to exhibit impaired shape retentivity at high temperatures. Thus, the material is usable for only greatly limited applications.
An object of the present invention is to provide a polymer material which has excellent vibration-proofness, damping property and stability in shape over a wide low to high temperature range.
Another object of the present invention is to provide a vibration-proof damping polymer material which is excellent in workability, transparency, resistance to heat, weather, chemicals, oils, solvents, water and abrasion, water and oil repellency, nonflammability, etc. and which is excellent also in vibration-proof damping characteristics.
The above and other objects of the invention will become apparent from the following description.
The present invention provides a vibration-proof damping polymer material characterized in that the material is prepared from a polymer substance obtained by dissolving an amorphous fluorine-containing polymer in an acrylic monomer, and polymerizing the monomer with or without permitting the resulting polymer to form an interpenetrating polymer network.
The present invention further provides a vibration-proof damping polymer material characterized in that the material is prepared from a blend of (a) and (b), (a) being an amorphous fluorine-containing polymer or crystalline polymer containing vinylidene fluoride, and (b) being an acrylic polymer.
The amorphous fluorine-containing polymers to be used in the present invention are, for example, copolymers containing vinylidene fluoride, fluoroalkene/olefin copolymers, fluoro(alkyl vinyl ether)(including those having multiple ether bonds)/olefin copolymers, fluorosilicon elastomers and fluorophosphazene elastomers. Among some of these polymers, those having an iodine atom or bromine atom bonded to the polymer chain thereof (see, for example, JP-A-53-125491 and JP-A-59-20310, and JP-B-53-4115) are highly amenable to polymerization reaction and are therefore desirable.
In the present invention, the above amorphous copolymer containing vinylidene fluoride is preferably 500 to a million in number average molecular weight and is obtained by copolymerizing vinylidene fluoride with at least one other copolymerizable monomer. Examples of other monomers are tetrafluoroethylene, chlorotrifluoroethylene, trifluoroethylene, vinyl fluoride, hexafluoropropylene, pentafluoropropylene, hexafluoroisobutene, perfluorocyclobutene, perfluoro(methylcyclopropylene), perfuluoroallene, .alpha., .beta., .beta.-trifluorostyrene, perfluorostyrene, polyfluoroalkyl vinyl ethers [e.g., perfluoro(methyl vinyl ether), perfluoro(propyl vinyl ether)], polyfluoroacrylic acid or ester thereof, polyfluorovinyl acetic acid or ester thereof, polyfluorovinyl ether sulfonic acid, polyfluorodienes, ethylene, propylene, acrylic acid or ester thereof and vinyl acetic acid or ester thereof. The content of the monomer is not particularly limited but is preferably 10 to 60 wt %. Among some of these polymers, those having an iodine atom or bromine atom bonded to the polymer chain thereof (see, for example, JP-A-53-125491 and JP-A-59-20310, and JP-B-53-4115) are highly amenable to polymerization reaction and are therefore desirable. Further, these copolymers containing vinylidene fluoride may be those crosslinked by a usual manner.
Fluoroalkene/olefin copolymers used in the present invention include a copolymer of tetrafluoroethylene and propylene, and copolymers of the above two components and other copolymerizable monomer. Examples of useful other copolymerizable monomers are vinylidene fluoride, perfluoro(alkyl vinyl ether)[e.g., perfluoro(methyl vinyl ether), perfluoro(propyl vinyl ether)], ethylene, isobutene, 2-chloroethyl vinyl ether, acrylic acid glycidyl vinyl ether and vinyl acetic acid.
Fluoro(alkyl vinyl ether)/olefin copolymers include ethylene/perfluoro(methyl vinyl ether) copolymers, ethylene/perfluoro(propyl vinyl ether) copolymer and ethylene/perfluoro(polyether vinyl ether) copolymer.
Examples of fluorosilicon elastomers are a copolymer of methyltrifluoropropylsiloxane and vinylmethylsiloxane, and examples of fluorophosphazene elastomers are a reaction product of a long-chain elastomer with trifluoroethanol, pentafluoropropanol or heptafluorobutanol, the elastomer being obtained by thermal degradation of dichlorophosphonitrile trimer.
Acrylic monomers useful for the present invention are not limited in kind and include mono- and poly-functional monomers. The monomer is used singly or in a mixture of at least two of them. The polyfunctional monomer is preferably used in a small amount, conjointly with the monofunctional monomer. Examples of preferred monomers are methyl methacrylate (MMA), ethyl methacrylate (EMA), butyl methacrylate (BMA), 2-hydroxyethyl methacrylate (HEMA), 3-(trimethoxysilyl)propyl methacrylate (MSPM), 2-(phenylphosphoryl)ethyl methacrylate (phenyl-P), 2-hydroxy-3-(.beta.-napthoxy)propyl methacrylate (HNPM), N-phenyl-N-(2-hydroxy-3-methacryloxy)propylglycine (NPG-GMA), ethylene glycol dimethacrylate (EDMA or 1 G), diethylene glycol dimethacrylate (DiEDMA or 2 G), triethylene glycol dimethacrylate (TriEDMA or 3 G), 1,4-butanediol dimethacrylate (1,4-BuDMA), 1,3-butanediol dimethacrylate (1,3-BuDMA), neopentyl glycol dimethacrylate, 1,6-hexanediol dimethacrylate, 2,2-bis[4-(2-hydroxy-3-methacryloxypropoxy)phenyl]propane (Bis-GMA), 2,2-bis(4-methacryloxyphenyl)propane (BPDMA), 2,2-bis(4-methacryloxyethoxyphenyl)propane (Bis-MEPP), 2,2-bis(4-methacryloxypolyethoxyphenyl)propane (Bis-MPEPP), di(methacryloxyethyl)trimethylhexamethylenediurethane (UDMA), trimethylolpropanetrimethacrylate (TMPT), glycidyl methacrylate,
CH.sub.2 .dbd.C(CH.sub.3)COOCH.sub.2 CF.sub.3 (3FMA),
CH.sub.2 .dbd.C(CH.sub.3)COOCH.sub.2 CF.sub.2 CF.sub.2 H(4FMA),
CH.sub.2 .dbd.C(CH.sub.3)COOCH.sub.2 CF.sub.2 CF.sub.2 H(5FMA),
CH.sub.2 .dbd.C(CH.sub.3)COOCH.sub.2 (CF.sub.2).sub.2 CF.sub.3 (7FMA),
CH.sub.2 .dbd.C(CH.sub.3)COOCH.sub.2 (CF.sub.2).sub.3 CF.sub.2 H(8FMA),
acrylates and .alpha.-fluoroacrylates corresponding to such compounds.
Examples of .alpha.-fluoroacrylates are
CH.sub.2 .dbd.CFCOOCH.sub.2 CF.sub.2 CF.sub.2 H(4FFA),
CH.sub.2 .dbd.CFCOOCH.sub.2 CF.sub.2 CF.sub.3 (5FFA),
CH.sub.2 .dbd.CFCOOCH.sub.2 (CF.sub.2).sub.3 CF.sub.2 H(8FFA) and
CH.sub.2 .dbd.CFCOOCH.sub.2 (CF.sub.2).sub.5 CF.sub.2 H(12FFA).
According to the invention, the fluorine-containing polymer is dissolved in such an acrylic monomer, and the solution is then subjected to polymerization, whereby the polymer substance is prepared. The polymerization is conducted in the presence of a polymerization initiator. A polymerization inhibitor, reducing agent, transfer agent, etc. can be added to the polymerization system. Examples of useful polymerization initiators are light, heat, benzoyl peroxide, azoisobutyronitrile (AIBN), camphorquinone (CQ), 9-fluorenone, tributylborane (TBB), benzophenone and the like. Examples of useful reducing agents are dimethylaminoethyl methacrylate (DMAEMA), dimethyl-p-toluidine (DMPT) and the like. Examples of useful polymerization inhibitors are hydroquinone, hydroquinone methyl ester and the like. Examples of useful transfer agents include lauryl mercaptan.
When heat polymerization is resorted to, it is desirable to heat the solution at a temperature of about 40.degree. to about 100.degree. C. for about 10 to about 150 minutes. When to be subjected to photopolymerization, the solution is preferably irradiated with visible rays or ultraviolet rays for several minutes to tens of minutes.
The substances of the present invention include those obtained by forming such a polymer substance into an IPN (interpenetrating polymer network). IPN is a polymer obtained by mixing two linear polymers together each in the form of a liquid (or solution) and crosslinking one or both of the polymers to interlock the respective molecular chains. This method is utilized in the present invention as modified into several different methods. According to a first method, a polymer substance is first made into a film, a monomer serving as a guest polymer is injected in the state of vapor phase into the film, or the film is immersed in a solution of the monomer to inject the monomer into the film, and the film is thereafter polymerized or crosslinked as by heating or irradiation with light. A second method, like the usual IPN forming method, comprises dissolving a polymer substance in a suitable solvent, admixing a guest component with the solution for reaction, casting the resulting solution into a film, and heat-treating the film when so required. Other methods are also usable.
For the formation of IPN, crosslinking must be effected. This can be accomplished, for example, by using as the fluorine-containing polymer such a compound having an iodine atom or bromine atom bonded to the polymer chain thereof, or by using as the acrylic monomer at least bifunctional monomer, or by using a crosslinking agent.
For this purpose, the fluorine-contaning polymers and acrylic monomers already exemplified are usable. Useful crosslinking agents include, for example, triallyl isocyanurate, triallyl cyanurate, triacryl formal, triallyl trimellitate, diallyl phthalate and like poly-unsaturated compounds. Further, an organic peroxide is also usable as a radical source.
The vibration-proof damping polymer material defined in claim 2 of the present invention is described below. The same amorphous fluorine-containing polymer as above is usable. Examples of crystalline polymer containing vinylidene fluoride are a homopolymer and copolymers of vinylidene fluoride. Copolymerizable monomers include tetrafluoroethylene, trifluoroethylene, chlorotrifluoroethylene and trichlorofluoroethylene.
Acrylic polymers include a homopolymer of acrylic monomer and copolymers of acrylic monomer and other monomer. The same acrylic monomer as above is usable. Examples of other monomers are vinyl acetate, styrene, acrylonitrile, butadiene and 2-chloroethyl vinyl ether.
As the above fluorine-containing polymer and acrylic polymer are usable those obtained by a usual method.
The polymer substance for use in the present invention is excellent in processability, transparency, resistance to heat, weather, chemicals, oils, solvents and water, water and oil repellency, abrasion resistance and nonflammability and has outstanding vibration-proof damping characteristics.
The polymer substance is molded in a desired shape, for example, by extrusion, injection molding or compression molding, or is dissolved or dispersed in a suitable solvent to obtain a coating composition, which is then made into a desired shape. The polymer material thus prepared is used for applications mentioned later. Additives for rubbers and plastics may be added to the polymer substances. Examples of such additives are fillers, reinforcing agents, softening agents, plasticizers, compatibility imparting agents, seed of crystallization, antiaging agents, antioxidants, antiozonants, ultraviolet absorbers, pigments, dyes, tackifier resins and the like.
The vibration-proof damping polymer material of the present invention is useful as such for ceilings, floors, side walls, bonnets and the like of vehicles such as motor vehicles, trains, aircraft and ships. The present material is widely usable for building machines, agricultural machines, civil engineering machines and other industrial machines; for noise sources in factories or plants such as metal working machines, ducts, hoppers and chutes; for noise sources in houses and offices such as roofs (especially iron plate roofs), ceilings, floors and walls; for office machines such as calculators and printers; for household electric applicances such as air conditioners, washing machines and vacuum cleaners; for acoustic systems such as stereo sound reproduction systems and record players, pianos, organs and the like.
The present invention will be described below with reference to the following examples.

EXAMPLE 1
In a monomer mixture of 9.9 g of methyl methacrylate (MMA) and 0.1 g of ethylene glycol dimethacrylate (1 G) were dissolved camphorquinone (CQ) and dimethylaminoethyl methacrylate (DMAEMA) each in an amount of 0.5 wt % based on the mixture. Further dissolved in the solution were 20 g of fluoroelastomer (Dai-el.RTM. G801, iodine-containing elastic copolymer containing vinylidene fluoride), and 0.5 wt % of Perhexa 2.5 B (product of Nippon Oils & Fats Co., Ltd., peroxide) and 0.2 wt % of triallyl isocyanurate (TAIC) based on G801 to prepare a uniform solution, which was irradiated with visible rays for photopolymerization. The sample obtained was heat-treated at 160.degree. C. for 10 minutes to crosslink the rubber.
The polymer material obtained was 10.01 HV (25.degree. C.) in Vickers hardness.
For a material to exhibit vibration-proof damping characteristics, the material needs to have characteristics to effectively convert vibration energy to thermal energy for dissipation. As a measure of the ratio of conversion from the vibration energy to the thermal energy, tan.delta. can be mentioned which is obtained by measuring the dynamic modulus in tension. The greater the value of tan.delta., the greater is the conversion ratio. The value tan.delta. and the dynamic modulus in tension E' were measured at a frequency of 3.5 Hz while raising the temperature at a rate of 2.degree. C./min. The results are given in Table 1.
TABLE 1______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________-50 0.023 2.60 .times. 10.sup.10-25 0.027 2.20 .times. 10.sup.10 0 0.039 1.82 .times. 10.sup.1025 0.079 1.42 .times. 10.sup.1050 0.49 0.47 .times. 10.sup.1068 1.32 0.50 .times. 10.sup.975 1.18 0.47 .times. 10.sup.9100 0.60 0.54 .times. 10.sup.9______________________________________
TEST EXAMPLE 1
A steel panel, 3 mm in thickness, 30 mm in width and 200 mm in length and pretreated with resin and by sandblasting, was coated over the entire surface thereof with the above mixture to a thickness of 3 mm, and the coating was polymerized and crosslinked in the same manner as above. An aluminum sheet, 0.05 mm in thickness, 30 mm in width and 200 mm in length adhered to the resin layer with use of an epoxy adhesive. The adhesive layer was up to 20 .mu.m in thickness. Table 2 shows the result obtained by subjecting the test piece prepared to a modal analysis.
TABLE 2______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________ 60 1.08 413100 1.64 400140 1.02 387______________________________________
EXAMPLE 2
To G801 were added 4 wt % of TAIC and 1.5 wt % of Perhexa 2.5 B based on the G801, followed by kneading and heat treatment at 160.degree. C. for 10 minutes to obtain crosslinked G801. On the other hand, in MMA were dissolved CQ and DMAEMA each in an amount of 0.5 wt % based on the MMA, and the crosslinked G801 was immersed in the solution for swelling so that the swollen mass contained 55 wt % of the crosslinked G801 and 45 wt % of MMA. The mixture was then subjected to photopolymerization in the same manner as in Example 1.
The tan.delta. and E' values of the polymer material prepared were measured in the same manner as in Example 1. Table 3 shows the result.
TABLE 3______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________-100 0.04 3 .times. 10.sup.10-50 0.04 2.6 .times. 10.sup.10 0 0.07 1.95 .times. 10.sup.10 50 0.09 1.2 .times. 10.sup.10100 0.98 4.3 .times. 10.sup.8105 1.1 2 .times. 10.sup.8150 0.4 1.2 .times. 10.sup.8200 0.18 1.3 .times. 10.sup.8______________________________________
TEST EXAMPLE 2
A sheet of G801, 2 mm in thickness and crosslinked in the same manner as above, was immersed for swelling in MMA having dissolved therein CQ and DMAEMA each in an amount of 0.5 wt % so that the swollen sheet contained 55 wt % of crosslinked G801 and 45 wt % of MMA. The sheet was then placed on a steel panel of the same size as used in Test Example 1 and subjected to photopolymerization. An aluminum sheet, 0.05 mm in thickness, 30 mm in width and 200 mm in length adhered to the resin layer with use of an epoxy adhesive. The adhesive layer was up to 20 .mu.m in thickness. Table 4 shows the result obtained by subjecting the test piece to a modal analysis.
TABLE 4______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________ 60 1.05 397 80 1.34 390100 1.26 382120 1.04 374______________________________________
EXAMPLE 3
Two parts by weight of Dai-el.RTM. G801 (iodine-containing vinylidene fluoride elastic copolymer) was dissolved in 1 part by weight of methyl methacrylate (MMA), followed by photopolymerization by the method described below to obtain a cured polymer. To the solution were added camphorquinone (CQ) and dimethylaminoethyl methacrylate (DMAEMA) each in an amount of 0.5 wt % based on the monomer, and the mixture was irradiated with visible rays at room temperature for 10 minutes for polymerization.
The polymer material obtained was 10.0 HV (25.degree. C.) in Vickers hardness.
The tan.delta. and E' values of the material were measured in the same manner as in Example 1. Table 5 shows the result.
TABLE 5______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________-50 0.030 2.80 .times. 10.sup.10-25 0.035 2.45 .times. 10.sup.10 0 0.047 2.22 .times. 10.sup.1025 0.063 1.67 .times. 10.sup.1050 0.30 0.65 .times. 10.sup.1060 1.35 2.26 .times. 10.sup.870 1.55 2.01 .times. 10.sup.780 0.71 3.15 .times. 10.sup.6______________________________________
TEST EXAMPLE 3
The above mixture was coated and photopolymerized in the same manner as in Test Example 1. An aluminum sheet, 0.05 mm in thickness, 30 mm in width and 200 mm in length adhered to the resin layer with use of an epoxy adhesive. The adhesive layer was up to 20 .mu.m in thickness. Table 6 shows the results obtained by subjecting the test piece to a modal analysis.
TABLE 6______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________ 60 1.07 412100 1.62 399140 1.00 388______________________________________
EXAMPLE 4
The same photopolymerization process as in Example 3 was practiced except that the ratio of G801 to MMA was 55:45 by weight.
The tan.delta. and E' values of the polymer material obtained were measured in the same manner as in Example 1. Table 7 shows the result.
TABLE 7______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________-150 0.017 4.3 .times. 10.sup.10-100 0.031 3.7 .times. 10.sup.10-50 0.024 2.9 .times. 10.sup.10 0 0.036 2.2 .times. 10.sup.10 50 0.125 1.02 .times. 10.sup.10 60 0.40 2.0 .times. 10.sup.8100 1.70 4.1 .times. 10.sup.6150 1.02 1.1 .times. 10.sup.6______________________________________
TEST EXAMPLE 4
A test piece was prepared from the above mixture in the same manner as in Test Example 3. Table 8 shows the results obtained by subjecting the test piece to a modal analysis.
TABLE 8______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________ 60 1.06 398 80 1.35 391100 1.27 384120 1.05 375______________________________________
EXAMPLE 5
Tetrafluoroethylene-propylene copolymer was dissolved in a monomer mixture of 5 FMA and EDMA in the proportions listed in Table 9, followed by thermal polymerization in the manner described below to obtain a cured polymer. To the solution was added 0.5 wt % of azobisisobutyronitrile (AIBN) based on the monomer, and the mixture was heated at 60.degree. C. for 2 hours and 80.degree. C. for 1 hour for thermal polymerization.
The polymer material obtained was 2.7 HV (25.degree. C.) in Vickers hardness. The material was 237 kgf/cm.sup.2 in tensile strength as measured by an autograph, product of Shimadzu Seisakusho, Ltd. under the conditions of crosshead speed of 100 mm/min and dumbell No. 2 sample.
Table 10 shows the result obtained by measuring the tan.delta. and E' values of the polymer material in the same manner as in Example 1.
TABLE 9______________________________________Tetrafluoroethylene/propylene (60/40) copolymer 5 FMA EDMA______________________________________33 50 17______________________________________
TABLE 10______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________-50 0.020 2.0 .times. 10.sup.10-25 0.027 1.88 .times. 10.sup.10 0 0.055 1.70 .times. 10.sup.10 7.5 0.134 1.22 .times. 10.sup.1025 0.082 0.74 .times. 10.sup.1050 0.087 0.53 .times. 10.sup.1075 0.130 0.37 .times. 10.sup.1090 0.300 0.03 .times. 10.sup.10100 1.45 6.00 .times. 10.sup.7110 1.37 3.35 .times. 10.sup.7______________________________________
TEST EXAMPLE 5
The above mixture was subjected to thermal polymerization in the same manner as in the above to obtain a film, 0.2 mm in thickness, 30 mm in width and 200 mm in length. The film was sandwiched between two steel panels, 1.6 mm in thickness, 30 mm in width and 200 mm in length. The panels were adhered to the film with the use of an epoxy adhesive. The adhesive layer was up to 20 .mu.m in thickness. Table 11 shows the results obtained by subjecting the test piece to a modal analysis.
TABLE 11______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________19 6.21 41140 17.1 32160 15.8 262______________________________________
EXAMPLE 6
Tetrafluoroethylene-propylene copolymer was dissolved in 5 FMA in the ratio given in Table 12 and subjected to thermal polymerization in the following manner to obtain a cured polymer. To the solution was added azobisisobutyronitrile (AIBN) in an amount of 0.5 wt % based on the monomer, and the mixture was heated at 60.degree. C. for 2 hours and then at 80.degree. C. for 1 hour for polymerization.
The polymer material obtained was 1.6 H V (25.degree. C.) in Vickers hardness, and was 215 kgf/cm.sup.2 in tensile strength as measured under the same conditions as in Example 5.
Table 13 shows the result obtained by measuring the tan.delta. and E' values of the material in the same manner as in Example 1.
TABLE 12______________________________________Tetrafluorethylene/propylene (60/40) copolymer 5 FMA______________________________________37 63______________________________________
TABLE 13______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________-50 0.007 2.25 .times. 10.sup.10-25 0.010 1.95 .times. 10.sup.10 0 0.072 1.32 .times. 10.sup.1010 0.360 4.0 .times. 10.sup.925 0.143 1.85 .times. 10.sup.950 0.210 1.3 .times. 10.sup.9______________________________________
TEST EXAMPLE 6
A test piece was prepared from the above mixture in the same manner as in Test Example 5. Table 14 shows the results obtained by subjecting the test piece to a modal analysis.
TABLE 14______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________40 2.3 37560 11.0 30580 3.5 259______________________________________
EXAMPLE 7
Dai-el.RTM. G801 (iodine-containing vinylidene fluoride elastic copolymer) and acrylic resin (homopolymer of ethyl methacrylate) in the ratio of 1:1 by weight were dissolved in ethyl acetate, followed by stirring for 24 hours. The solution obtained was cast into a film of polymer. The polymer material thus prepared was 63 HDA in Shore hardness.
Table 15 shows the result obtained by measuring the tan.delta. and E' values of the material in the same manner as in Example 1.
TABLE 15______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________-100 0.022 2.75 .times. 10.sup.10-75 0.017 2.60 .times. 10.sup.10-50 0.026 2.25 .times. 10.sup.10-25 0.078 1.85 .times. 10.sup.10 0 0.205 1.03 .times. 10.sup.1025 0.910 1.05 .times. 10.sup.940 1.050 0.73 .times. 10.sup.950 0.89 6.10 .times. 10.sup.860 0.62 5.81 .times. 10.sup.8______________________________________
Test Example 7
The above mixture was made into a film, 0.2 mm in thickness, 30 mm in width and 200 mm in length. The film was sandwiched between two steel panels, 1.6 mm in thickness, 30 mm in width and 200 mm in length. The panels adhered to the film with use of an epoxy adhesive. The adhesive layer was up to 20 .mu.m in thickness. Table 16 shows the results obtained by subjecting the test piece to a modal analysis.
TABLE 16______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________60 13.3 26580 18.5 235100 18.0 217______________________________________
Example 8
Tetrafluoroethylene/propylene (60/40, mole %) copolymer and 4 FMA polymer in the ration of 67:33 by weight were dissolved in a fluorine-containing solvent, i.e., CF.sub.2 Cl--CF.sub.2 Cl, followed by stirring for 24 hours. The solution obtained was dried in a vacuum at 45.degree. C. to obtain a transparent film, 260 .mu.m in thickness.
Table 17 shows th result obtained by measuring the tan.delta. and E' values of the polymer material thus prepared.
TABLE 17______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________-100 0.038 1.95 .times. 10.sup.10-80 0.026 1.70 .times. 10.sup.10-60 0.015 1.55 .times. 10.sup.10-40 0.016 1.40 .times. 10.sup.10-20 0.056 1.10 .times. 10.sup.10-10 0.270 0.52 .times. 10.sup.10 0 0.52 0.95 .times. 10.sup.9 10 0.38 0.11 .times. 10.sup.9 20 0.26 0.07 .times. 10.sup.9______________________________________
Test Example 8
The above film was subjected to a modal analysis in the same manner as in Test Example 7. The results are given in Table 18.
TABLE 18______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________19 2.1 41940 8.2 32860 11.5 275______________________________________
Example 9
Polyvinylidene fluoride and acrylic resin (homopolymer of ethyl methacrylate) were blended in a molten state at 200.degree. C. in the ratio of 2:1 by weight and then quenched to prepare a film having a thickness of 100 .mu.m. The polymer material obtained was 5.1 HV (25.degree. C.) in Vickers hardness.
Table 19 shows the tan.delta. and E' values of the material measured in the same manner as in Example 1.
TABLE 19______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________-50 0.012 8.4 .times. 10.sup.10-25 0.022 6.8 .times. 10.sup.10 0 0.054 4.7 .times. 10.sup.1025 0.158 2.45 .times. 10.sup.1050 0.250 0.81 .times. 10.sup.1075 0.160 0.38 .times. 10.sup.10100 0.115 0.26 .times. 10.sup.10______________________________________
Test Example 9
The above film was subjected to a modal analysis in the same manner as in Test Example 7. The results are given in Table 20.
TABLE 20______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________60 2.8 26780 5.0 236100 7.6 218120 5.4 211______________________________________
Example 10
Polyvinylidene fluoride and acrylic resin (homopolymer of ethyl methacrylate) in the ratio of 1:1 by weight were dissolved in dimethylformamide, followed by stirring for 24 hours. The solution was cast into a film of polymer. The polymer material obtained was 7.4 HV (25.degree. C.) in Vickers hardness.
Table 21 shows the tan.delta. and E' values of the material measured in the same manner as in Example 1.
TABLE 21______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________-50 0.020 3.5 .times. 10.sup.10-25 0.046 2.55 .times. 10.sup.10 0 0.128 1.40 .times. 10.sup.1025 0.380 4.58 .times. 10.sup.943 0.610 0.98 .times. 10.sup.950 0.580 0.57 .times. 10.sup.975 0.330 0.05 .times. 10.sup.9100 0.200 0.32 .times. 10.sup.7______________________________________
Test Example 10
The above film was subjected to a modal analysis in the same manner as in Test Example 7. The results are given in Table 22.
TABLE 22______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________ 80 13.3 238100 15.4 217120 12.0 212______________________________________
Example 11
In 30 g of methyl acrylate (MAc) were dissolved CQ and DMAEMA each in an amount of 0.5 wt % based on the MAc. Firther dissolved in the solution were 70 g of G801, and Perhexa 2.5 B and TAIC in amounts of 1.5 wt % and 4 wt %, respectively, based on the G801 to prepare a uniform solution, which was irradiated with visible rays to effect photopolymerization. The sample obtained was heat-treated at 160.degree. C. for 10 minutes to crosslink the rubber. Table 23 shows the result obtained by measuring the tan.delta. and E' values of the polymer material prepared in the same manner as in Example 1.
TABLE 23______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________ 0.7 0.14 1.17 .times. 10.sup.1010.7 0.43 6.95 .times. 10.sup.916.7 1.32 2.16 .times. 10.sup.920.7 2.13 7.13 .times. 10.sup.824.7 2.05 3.27 .times. 10.sup.828.7 1.48 2.53 .times. 10.sup.832.8 1.20 2.39 .times. 10.sup.836.7 0.96 2.44 .times. 10.sup.8______________________________________
Test Example 11
The above mixture was photopolymerized. A test piece was obtained in the same manner as in Test Example 7. Table 24 shows the results obtained by subjecting the test piece to a modal analysis.
TABLE 24______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________60 13.1 23980 19.2 214100 13.8 213______________________________________
Example 12
A test piece was obtained in the same manner as in Example 11 except that a monomer mixture of MAc (29 g) and 1 G (1 g) was used in place of MAc (30 g). Table 25 shows the result obtained by measuring the tan.delta. and E' values of the polymer material prepared in the same manner as in Example 1.
TABLE 25______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________ 0.7 0.14 1.15 .times. 10.sup.1010.7 0.44 6.93 .times. 10.sup.916.7 1.33 2.17 .times. 10.sup.920.7 2.10 7.14 .times. 10.sup.824.7 2.03 3.35 .times. 10.sup.828.7 1.47 2.60 .times. 10.sup.832.8 1.23 2.45 .times. 10.sup.836.7 0.99 2.47 .times. 10.sup.8______________________________________
Test Example 12
A test piece was prepared from the above mixture in the same manner as in Test Example 11. Table 26 shows the results obtained by subjecting the test piece to a modal analysis.
TABLE 26______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________ 80 13.1 239100 15.2 218120 11.8 214______________________________________
EXAMPLE 13
In a monomer mixture of 27 g of i-butyl acrylate (i-BuAc) and 3 g of 1 G were dissolved CQ and DMAEMA each in an amount of 0.5 wt. % based on the monomer mixture. Further dissolved in the solution were 70 g of G801 to prepare a uniform solution, which was irradiated with visible rays to effect photopolymerization. Table 27 shows the result obtained by measuring the tan.delta. and E' values of the polymer material prepared in the same manner as in Example 1.
TABLE 27______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________0.8 1.32 7.4 .times. 10.sup.84.7 1.71 3.92 .times. 10.sup.86.7 1.71 3.70 .times. 10.sup.810.7 1.43 3.20 .times. 10.sup.816.7 1.07 3.30 .times. 10.sup.8______________________________________
TEST EXAMPLE 13
A test piece was prepared from the above mixture in the same manner as in Test Example 11. Table 28 shows the results obtained by subjecting the test piece to a modal analysis.
TABLE 28______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________40 13.3 23770 18.5 21680 15.1 215______________________________________
EXAMPLE 14
In 30 g of i-butyl acrylate (i-BuAc) were dissolved CQ and DMAEMA each in an amount of 0.5 wt % based on the i-BuAc. Further dissolved in the solution were 70 g of G801 to prepare a uniform solution, which was irradiated with visible rays to effect photopolymerization. Table 29 shows the result obtained by measuring the tan.delta. and E' values of the polymer material prepared in the same manner as in Example 1.
TABLE 29______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________0.8 1.31 7.3 .times. 10.sup.84.7 1.70 3.85 .times. 10.sup.86.7 1.75 3.63 .times. 10.sup.810.7 1.45 3.15 .times. 10.sup.816.7 1.09 3.21 .times. 10.sup.8______________________________________
TEST EXAMPLE 14
A test piece was prepared from the above mixture in the same manner as in Test Example 11. Table 30 shows the results obtained by subjecting the test piece to a modal analysis.
TABLE 30______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________40 13.5 23860 18.3 21580 14.9 214______________________________________
EXAMPLE 15
In 30 g of methyl methacrylate (MMA) were dissolved CQ and DMAEMA each in an amount of 0.5 wt % based on the MMA. Further dissolved in the solution were 70 g of G912 to prepare a uniform solution, which was irradiated with visible rays to effect photopolymerization. Table 31 shows the result obtained by measuring the tan.delta. and E' values of the polymer material prepared in the same manner as in Example 1. G912 is a polymer of three components, namely tetrafluoroethylene, vinylidene fluoride and hexafluoropropylene.
TABLE 31______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________50 0.25 0.88 .times. 10.sup.1060 1.15 3.20 .times. 10.sup.870 1.50 2.21 .times. 10.sup.780 0.91 3.10 .times. 10.sup.6______________________________________
TEST EXAMPLE 15
A test piece was prepared from the above mixture in the same manner as in Test Example 3. Table 32 shows the results obtained by subjecting the test piece to a modal analysis.
TABLE 32______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________ 60 1.08 411100 1.59 400140 1.01 387______________________________________
EXAMPLE 16
G801 and PMMA in the ratio of 1:1 by weight were dissolved in acetylacetone, followed by stirring for 24 hours. The solution was cast into a film of polymer. Table 33 shows the tan.delta. and E' values of the material measured in the same manner as in Example 1.
TABLE 33______________________________________Temp. (.degree.C.) tan.delta. E' (dyne/cm.sup.2)______________________________________30 0.51 3.0 .times. 10.sup.940 0.84 3.7 .times. 10.sup.850 1.0 1.5 .times. 10.sup.760 0.92 8.0 .times. 10.sup.670 0.66 5.5 .times. 10.sup.6______________________________________
TEST EXAMPLE 16
The above film was subjected to a modal analysis in the same manner as in Test Example 7. The results are given in Table 34.
TABLE 34______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________ 80 14.3 229100 18.9 217120 16.3 209______________________________________
EXAMPLE 17
Fifty five parts by weight of Dai-el.RTM. G801 was dissolved in 45 parts of MMA having dissolved therein CQ and DMAEMA each in an amount of 0.5 wt %. The solution was applied to a steel panel, 200.times.30.times.3 mm in a thickness of 2.5 mm, and the coating was polymerized with the irradiation of visible rays.
The above resin layer was further coated with a mixture of G801/MMA/1 G (110/45/45) to a thickness of 1 mm and over an area of 30 mm in width and 200 mm in length, and the coating was irradated with light for polymerization. Table 35 shows the result achieved by subjecting the test piece obtained by a modal analysis.
TABLE 35______________________________________Temp. Attenuation Frequency(.degree.C.) constant (%) (Hz)______________________________________60 1.19 40080 1.23 391100 0.79 385______________________________________
EXAMPLE 18
Dai-el G801 was dissolved in an acrylic monomer having CQ and DMAEMA dissolved therein each in an amount of 0.5 wt % so that the resulting solution contained 70 wt % of G801 and 30 wt % of the acrylic monomer and the initiator combined. The solution was pressed as sandwiched between two glass plates, 1 mm in thickness and 120 mm in length and width, and thereafter irradiated with visible light for polymerization. Table 36 shows the result achieved by subjecting the sample obtained to a modal analysis at 25.degree. C.
TABLE 36______________________________________Acrylic Resin layer Attenuation Frequencymonomer thickness (.mu.m) constant (%) (Hz)______________________________________EtMA 260 0.52 547EtAc 270 13.2 540n-BuMA 280 1.8 524n-BuAc 320 20.3 453MMA 270 2.6 542i-PrMA 270 0.5 546______________________________________
COMPARATIVE EXAMPLE 1
Table 37 shows attenuation constant of the steel panel used in examples.
TABLE 37______________________________________Steel panel (mm) Attenuation FrequencyThickness Width Length constant (%) (Hz)______________________________________3 30 200 0.43 3941.6 30 200 0.49 547______________________________________
TEST EXAMPLE 17
There are two characteristics required of vibration-proof rubber: increased loss tangent (tan.delta.) and decreased magnification (dynamic spring constant/static shear elastic modulus).
The vibration-proof characteristics of the samples of Examples were evaluated in terms of loss tangent (tan.delta.) at 25.degree. C., 11 Hz and complex elastic modulus (E*) at 25.degree. C., 110 Hz which were determined using a viscoelasticity spectrometer (product of Orientec Co., Ltd.), and magnification, E*/Es, wherein Es is a static elastic modulus determined from the static shear modulus (Gs) according to JIS K6301.
The sample of Example 14 was 0.629 in tan.delta. and 1.70 in magnification as determined in the above manner.
WEATHER-RESISTANCE TEST
To 3 g of MMA was dissolved 7 g of G801 and the monomer was polymerized in the same manner as in Example 3. The obtained cured polymer was checked for weather-resistance by measuring gloss of a sample after weather-resistance promoting test. Test conditions are given in Table 38.
______________________________________Eyesuper UV tester[SUV-W13, Iwasaki Electronic Co., Ltd.]Lamp illuminance 100 mW/cm.sup.2Cycle 96 hr/time______________________________________
TABLE 38______________________________________Kind of test Temp. Humidity______________________________________Light 6 hr. 63.degree. C. 70%Dew 5 hr. 30.degree. C. 100%Rest 1 hr. 63.degree. C. 70%______________________________________
GLOSS TEST
The sample after the above weather-resistance test was checked for 60.degree. specular gloss with use of a degital variable glossmeter [UGV-5D, product of Suga Test Instruments Co., Ltd.]. The results were shown in Table 39.
TABLE 39______________________________________Time (hr) 0 96 192 288 384Gloss 451.0 463.6 454.5 464.9 470.5______________________________________

Number	Date	Country
1-81683	Mar 1989	JPX
1-81684	Mar 1989	JPX
1-81685	Mar 1989	JPX
1-81686	Mar 1989	JPX
1-81687	Mar 1989	JPX
1-81688	Mar 1989	JPX
1-81689	Mar 1989	JPX

Number	Name	Date
3257334	Chen et al.	Jun 1966
3644577	Lee et al.	Feb 1972
3790645	Murayama et al.	Feb 1974
4877839	Conti-Ramsdev et al.	Oct 1989

Number	Date	Country
0332141	Sep 1989	EPX
0358195	Mar 1990	EPX
385443	Sep 1990	EPX
2228377	Sep 1990	EPX

Vibration-proof damping polymer material

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (7)

US Referenced Citations (4)

Foreign Referenced Citations (4)