Patent Application
20110003070
The invention relates to the field of electrochromic devices. The invention particularly relates to new viologen-based electrochromic compositions which can be formulated and applied at room temperature, which allow preparing electrochromic devices with heat-sensitive substrates, particularly with fully plastic substrates, with a high degree of transparency and high optical contrast.
As is well known in the state of the art, a traditional or first-generation electrochromic device is formed by 7 different layers, 3 of them (the innermost ones of
The main material on which the device is designed is electrochromic material. Electrochromic materials are classified as cathodic or anodic depending on whether they become colored during a reduction or oxidation process, respectively. Therefore, depending on the color and on the nature of the redox process by which the electrochromic material is colored, a material which is complementary in color and redox process will be necessary. This second material is referred to as ion storage material. Searching for a complementary material is not easy since, in addition to meeting these indicated requirements, both materials must have the same charge content for a correct operation of the device (suitable optical contrast and cyclability). On the other hand, on many occasions liquid electrolytes give rise to solvent leakages or evaporation, whereas solid electrolytes usually have a slower ion and electron transport inside the device.
In the state of the art there are electrochromic devices which are based on solid state films, using a cathodic and anodic electrochromic material of an inorganic or organic nature. Electrochromic devices based on inorganic materials have the main limitations of the deposition techniques used, which require high temperature and high pressure, increasing the price of the end devices (JP 63262624). However, simpler and more cost-effective syntheses are possible by preparing devices based on organic materials since traditional techniques used in paint deposition, with subsequent solvent evaporation, are used (U.S. Pat. No. 3,873,185). Depending on the nature thereof, the need to evaporate the solvent can be a significant limitation since it increases the cost of the end device.
All these limitations have given rise to the search for new configurations of electrochromic devices with only 5 layers (second-generation devices), such that 3 of the active layers are simplified in a single electrochromic layer prepared from a single electrochromic composition (
The first second-generation electrochromic devices were devices with the electrochromic mixture in solution, in which said solution was injected between two completely sealed conductive crystals through a small hole. The active electrochromic materials in these systems are usually viologen derivatives which become darker when a negative potential is applied and become lighter in the absence of potential with transition times of the order of milliseconds. Said technology, which has reached commercial application, is described in U.S. Pat. Nos. 3,453,038, 5,115,346 and 5,151,816. The main limitations of said devices are focused on the difficulty of assembling them (possibility of solvent leakages, reducing the lifetime of the devices) and the possibility of breakages of the device. A strategy used to overcome the limitations of the devices in solution has been proposed by Donnelly in patent US 2005/0079326, which claims an electrochromic solid film prepared by curing electrochromic monomer compositions by exposure to electromagnetic radiation. Another interesting strategy is disclosed patent WO 2006/008776, which claims a solid film containing active electrochromic materials. Said formulation is prepared under hot conditions, by melting a polymer matrix having embedded therein an electrochromic material, an electron mediator and a solvent with a high boiling point. After a cooling process, said mixture has the appearance of a plastic membrane. The main drawback found in the patent is the need to prepare both the electrochromic mixture and the end device at temperatures above 100° C. If the original method described in patent WO 2006/008776 on a plastic substrate of the type of PET [poly(ethylene terephthalate)] coated with ITO (indium tin oxide, a reference material in the preparation of fully plastic electrochromic devices) is followed, such substrate is rippled due to the application of heat, causing a distortion of the images which are observed through it and giving rise to a very poor final appearance of the device. Similar consequences would occur in heat-sensitive substrates, such as paper or fabrics (coated with ITO).
Therefore, it is still necessary in the state of the art to prepare electrochromic compositions which can be formulated and applied at room temperature, particularly indicated for the development of fully plastic second-generation electrochromic devices.
The present invention provides a solution to the aforementioned problems and particularly describes new viologen-based electrochromic compositions, such viologens being embedded in a polymer matrix, which can be formulated and applied at room temperature as a result of the use of ionic liquid plasticizers combined with a particular mixture of solvents. Said compositions therefore comprise viologen derivatives embedded in a polymer matrix together with plasticizers, electron mediators and a small percentage of solvents, at least one of them having a high boiling point, which are miscible at room temperature with all the components. These electrochromic compositions have the final appearance of a slightly viscous gel and allow preparing electrochromic devices with heat-sensitive substrates, particularly with fully plastic substrates, with a high degree of transparency and high optical contrast.
The object of the present invention is, therefore, to provide new viologen-based electrochromic compositions which can be formulated and applied at room temperature.
Another object of the invention is to provide a method for preparing said electrochromic compositions.
Finally, another object is to provide a method for preparing electrochromic devices based on said electrochromic compositions.
The present invention provides an electrochromic composition comprising:
wherein R1 and R2 independently represent a linear or branched C1-C20 alkyl, benzyl, phenyl, p-cyanophenyl or C3-C12 cycloalkyl group; and X− represents Cl4−, Br−, Cl−, I−, PF6, NO3−, triflate or AsF6−; and
wherein R3 represents H or a linear or branched C1-C10 alkyl group; X−1 represents Cl−, Br−, ClO4−, (CF3SO3)−, (CF3SO2)2N−, (CF3CF2SO2)2N−, BF4−, PF6−, dodecylbenzene sulfonate or p-toluenesulfonate; and n≧2;
wherein R4 and R5 independently represent H, a linear or branched C1-C10 alkyl or vinyl group; and X−2 represents Cl−, Br−, ClO4−, (CF3SO3)−, (CF3SO2)2N−, (CF3CF2SO2)2N−, BF4−, PF6−, dodecylbenzene sulfonate or p-toluenesulfonate; and
In the context of the invention, the term “electrochromic composition” relates to a solution in which the components thereof are completely or partially dissolved or in suspension, which is formed by at least an electrochromic material and an electron mediator, which is deposited between two conductive substrates and which, by applying a potential, changes color.
As has been indicated above, in the context of the invention, the term “viologen derivative” relates to an active electrochromic material which becomes darker when a negative potential is applied and becomes lighter in the absence of potential. The viologen derivatives used in the present invention have, as a generic formula, formula (I):
wherein R1 and R2 independently represent a linear or branched C1-C20 alkyl, benzyl, phenyl, p-cyanophenyl or C3-C12 cycloalkyl group; and X− represents ClO4−, Br−, Cl−, BF4−, PF6, NO3−, triflate or AsF6−;
In a particular embodiment of the electrochromic composition of the invention, in the viologen of formula (I), R1 and R2 are identical and represent a C1-C9 alkyl group. In this case, the electrochromic composition of the invention allows preparing blue devices. In a preferred embodiment, R1 and R2 are identical and represent an ethyl group.
In another particular embodiment of the electrochromic composition of the invention, in the viologen of formula (I), R1 and R2 are identical and represent a C10-C20 alkyl group. In this case, the electrochromic composition of the invention allows preparing red/violet devices.
In another particular embodiment of the electrochromic composition of the invention, in the viologen of formula (I), R1 and R2 are identical and represent a benzyl, phenyl or p-cyanophenyl group. In this case, the electrochromic composition of the invention allows preparing green devices.
Said viologen of formula (I) will be used in the electrochromic composition of the invention in a ratio of 3-20% with respect to the total weight of the composition.
The polymer matrix of the present invention, the role of which is to provide suitable mechanical properties to the final mixture, preferably has the chemical structure represented by formula (II):
wherein R3 represents H or a linear or branched C1-C10 alkyl group; X−1 represents Cl−, Br−, ClO4−, (CF3SO3)−, (CF3SO2)2N−, (CF3CF2SO2)2N−, BF4−, PF6−, dodecylbenzene sulfonate or p-toluenesulfonate; and n≧2
In a particular embodiment of the electrochromic composition of the invention, in the polymer compound of formula (II) R3 represents a C1-C4 alkyl group and X−1 represents ClO4−, (CF3SO3)− or BF4−. In a preferred embodiment, R3 represents ethyl and X−1 represents BF4−.
Conventional polymers, of the poly(vinylpyrrolidone) type, soluble at room temperature in the mixture of organic solvents used, can optionally be used.
Said polymer compound of formula (II) will be used in the electrochromic composition of the invention in a ratio of 35-45% with respect to the total weight of the composition.
In the present invention, the plasticizer has the dual function of providing optimal adhesion properties and, furthermore, of favoring the mobility of charges inside the electrochromic mixture. A novel aspect of the invention is the use of ionic liquid-based plasticizers having, as a general formula, formula (III):
wherein R4 and R5 independently represent H, a linear or branched C1-C10 alkyl or vinyl group; and X−2 represents Cl−, Br−, ClO4−, (CF3SO3)−, (CF3SO2)2N−, (CF3CF2SO2)2N−, PF6−, dodecylbenzene sulfonate or p-toluenesulfonate.
In a particular embodiment of the electrochromic composition of the invention, in the plasticizer of formula (III) R4 and R5 independently represent a C1-C4 alkyl group and X−2 represents ClO4−, (CF3SO3)− or BF4−. In a preferred embodiment, R4 represents butyl, R5 represents methyl and X−2 represents BF4−.
The plasticizer of formula (III) will be used in the electrochromic composition of the invention in a ratio of 35-59% with respect to the total weight of the composition.
As has been indicated above, in the context of the invention, the term “electron mediator” relates to the component necessary for the redox reaction to occur in the electrochromic device, which must be complementary in redox behavior with the active electrochromic material of the invention, i.e., with the viologen derivative of general formula I. In the present invention any suitable electron mediator of the art can be used.
Thus, in a particular embodiment of the electrochromic composition of the invention, the electron mediator is selected from among hexacyanoferrate (II), periodate, Fe2+, and hydroquinone. The person skilled in the art will select the suitable counterion of the first three. In a preferred embodiment, the electron mediator is hydroquinone.
Said electron mediator will be used in the electrochromic composition of the invention in a ratio of 0.9-6% with respect to the total weight of the composition.
In the electrochromic composition of the present invention, a mixture of at least two miscible solvents which dissolve the aforementioned components (a) to (d) at room temperature, at least one of them being a solvent with a high boiling point, is used.
In the context of the invention, the term “solvent with a high boiling point” relates to a solvent the boiling point of which is above 150° C.
Thus, in a particular embodiment of the electrochromic composition of the invention, the solvent with a high boiling point is selected from among dimethylformamide and 1-hexanol.
Acetone, butanone or tetrahydrofuran (THF), among others, must be mentioned as additional solvents with a low boiling point to be used in small amounts together with the mentioned solvents with a high boiling point. The skilled person will select the suitable solvent with a low boiling point from among those known in the state of the art.
In a preferred embodiment of the electrochromic composition of the invention, the mixture of solvents is a mixture of dimethylformamide and acetone.
In the electrochromic composition of the invention, a volume of the solvent with a high boiling point of the order of 0.5-1 ml and a volume of the solvent with a low boiling point of the order of 0.2-0.6 ml are used, the preferred ratio between them being of the order of 2:1.
A small amount of glass spacers having a suitable diameter can additionally be used to limit the thickness of the active electrochromic layer during the construction of the electrochromic device. Thus, in a particular embodiment of the invention, the electrochromic composition additionally comprises glass spacers with a diameter of 1-10 μm.
In another aspect of the invention, a method for preparing the electrochromic composition described above is provided, in which components (a) to (e) are mixed at room temperature and with stirring.
The preparation of the electrochromic composition at room temperature includes dissolving the components described above in the smallest possible amount of solvents, under stirring, until obtaining a homogeneous mixture which does not need curing. The final appearance of the composition, of a gel type, has a viscosity that is very suitable for handling it at room temperature. This viscosity makes it very easy to deposit the mixture using common deposition techniques used in paints.
In another aspect of the invention, an electrochromic device comprising the electrochromic composition described above is provided.
In another aspect of the invention, a method for preparing an electrochromic device is provided, which method comprises the steps of: (i) depositing the electrochromic composition described above on a conductive substrate; and (ii) depositing another conductive substrate on the assembly.
The conductive substrate can be a substrate made of any conductive material such as plastic coated with ITO, textile material, paper or glass, which is furthermore transparent so that the color change of the device can be observed.
The deposition of the electrochromic composition of the invention is performed at room temperature by means of techniques of the state of the art which allow a homogeneous and optimal deposition. Thus, in a particular embodiment, the deposition of step (i) is performed by spin-coating, doctor blade coating or dip-coating techniques.
The typical thickness of the gel type layer is comprised between 20 and 200 μm depending on the technology and conditions of application of the formulation. This makes it comfortable and easy to assemble the device, eliminating possible bubbles and defects which might arise.
Once the electrochromic composition of the invention is deposited, another conductive substrate, preferably of the same type as the one used in the first substrate, is deposited thereon. The device thus prepared is optionally pressed at room temperature to assure a homogeneous thickness. In the event of using spacers, the final thickness will be determined by the diameter of the spacers placed and will be of the order of 1.5-10 μm. Finally, the electrochromic device can be encapsulated in a suitable manner following conventional techniques in order to obtain good values of stability and cyclability of the device.
The following example illustrates the invention and must not be considered as limiting the scope thereof.
An electrochromic composition was prepared by dissolving the following compounds in a 2:1 (v/v) DMF/acetone mixture (0.76 ml of DMF from Aldrich, 99% purity, and 0.4 ml of acetone from Panreac, purity PA-ACS-ISO) at room temperature: 40% by weight of the polymer poly(1-vinyl-3-ethyl-imidazolium tetrafluoroborate) (synthesized in CIDETEC according to the method described in Journal of Polymer Science Part A: Polymer Chemistry 42 (2004) 208), 40% by weight of 1-butyl-3-methyl-imidazolium tetrafluoroborate (Solvionic, 98% purity), 16% by weight of ethylviologen diperchlorate (Aldrich, 98% purity), and 4% by weight of hydroquinone (Riedel-de Haën, 99.5% purity).
The mixture was left stirring for 30 minutes at room temperature until obtaining a completely homogeneous and slightly viscous solution. Glass spacers with a diameter or 1.5 μm were subsequently added under stirring.
The mixture was applied on plastic ITO by means of the traditional doctor blade paint deposition technique. The excess of solvent with a low boiling point was subsequently left to evaporate at room temperature. Then, a second layer of plastic ITO was placed on the electrochromic mixture (see
The device thus constructed showed a maximum optical contrast of 80% and transition times of 5.5 and 5.6 seconds during the coloring and bleaching processes, respectively. The device was subjected to cyclability studies (above 2·103 cycles) with highly satisfactory results.
| Number | Date | Country | Kind |
|---|---|---|---|
| P200800258 | Jan 2008 | ES | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/ES08/00703 | 11/13/2008 | WO | 00 | 7/30/2010 |