Patent Grant
8304486
The present invention relates to a water-base adhesive mix for producing tyres.
In tyre manufacturing, adhesive mixes or so-called cements are normally organic-solvent-based mixes, which provide for extremely strong grip and are easy to use, mainly on account of the ability of rubber to dissolve in the organic solvents and so blend with other rubber to form practically one piece when the organic solvent evaporates.
The major drawback of adhesive mixes of this sort is the large amount of organic solvent they contain.
Recent European regulations have imposed a drastic reduction in the use of organic solvents in the tyre industry, thus forcing tyre manufacturers to seek alternative solutions to ensure firm adhesion of the various layers of rubber.
A demand therefore exists for adhesive mixes, for use in the tyre industry, containing no organic solvents, and which ensure adequate adhesion of the various rubber parts of the tyre.
It is an object of the present invention to provide a water-base adhesive mix for producing tyres, characterized by comprising, by weight, 20 to 80% water, 10 to 40% of a cross-linkable unsaturated-chain polymer base, 0.2 to 1% sulphur, 1 to 25% of a reinforcing filler, 1 to 10% of emulsifiers, 2 to 8% of a resin which cross-links by reaction with polyisocyanates, and 0.5 to 5% of an aqueous dispersion comprising blocked aromatic polyisocyanates with an activation temperature of 120 to 160° C.; said blocked aromatic polyisocyanates being produced by reaction of a polyisocyanate (a), a blocking agent (b), and a nonionic diol alkoxylate (c) of the general formula (I)
R1CH2O(CH2CH2O)n(CH2CHCH3O)mR2 (I)
where
R1 is
R2 and R3 are the same or different, and are selected from methyl, ethyl, n-propyl, i-propyl, n-butyl, i-butyl;
n is a whole number from 0 to 40
m is a whole number from 0 to 40
n+m is a whole number from 20 to 80.
The polyisocyanate (a) is preferably an aromatic polyisocyanate.
Said resin which cross-links by reaction with polyisocyanates is preferably a polyurethane resin.
The blocking agent (b) is preferably methyl ethyl ketoxime.
The aqueous dispersion contained in the water-base adhesive mix according to the present invention is described in Patent Application WO2004/050736, the content of which is included herein by way of reference.
The water-base adhesive mix according to the present invention preferably comprises a phenol-base adhesive resin.
The cross-linkable, unsaturated-chain polymer base preferably ranges between 15 and 30%.
The reinforcing filler preferably comprises 8 to 16% of carbon black.
The following non-limiting examples are purely indicative, for a clear understanding of the invention
Three adhesive mixes (A, B, C) in accordance with the present invention were produced containing different amounts of polyurethane resin and aqueous dispersion.
As will be clear to anyone skilled in the art, in addition to natural rubber, the adhesive mixes according to the present invention may comprise any cross-linkable-chain polymer base obtained by polymerization of conjugate dienes and/or aliphatic or aromatic vinyl monomers. For example, possible polymer bases are selected from the group comprising natural rubber; 1,4-cis polyisoprene; isoprene-isobutene copolymers, possibly halogenated; butadiene-acrylonitrile; styrene-butadiene; styrene-butadiene-isoprene terpolymers in solution or emulsion; and ethylene-propylene-diene terpolymers. The above polymer bases may be used singly or mixed.
In addition to polyurethane resin, the adhesive mixes according to the present invention may comprise other resin capable of cross-linking with polyisocyanates.
To better assess the advantages of the invention, two control adhesive mixes were produced: a first control adhesive mix (D) in the form of a known organic-solvent-based adhesive mix; and a second control adhesive mix (E) of the same composition as the present invention, but without the aqueous dispersion of blocked aromatic polyisocyanates and the polyurethane resin.
The adhesive mixes according to the invention and the control adhesive mixes were adhesion tested relative to both green and cured rubber.
Table I shows the compositions, in percentages by weight, of the adhesive mixes according to the invention.
Table II shows the compositions, in percentages by weight, of the control adhesive mixes.
The polyurethane resin used is manufactured by BAYER and marketed by the trade name DISPERCOLL U54.
The aqueous dispersion is manufactured by CESALPINIA CHEMICALS and marketed by the trade name ROLFLEX BK8.
The mixes were produced using standard known procedures.
Laboratory Tests
Each of the mixes produced was tested on both green and cured rubber. Table III shows the results of adhesion testing in accordance with ASTM Standard D1876.
The rheometric properties and viscosity of each mix were tested in accordance with ASTM Standard D5289 and ISO Standard 1652 respectively. The results are shown in Table III.
As shown in Table III, the adhesive mixes according to the present invention have good adhesion characteristics, while impairing none of the other characteristics, such as viscosity and geometry.
| Number | Date | Country | Kind |
|---|---|---|---|
| TO2006A0512 | Jul 2006 | IT | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2007/057216 | 7/12/2007 | WO | 00 | 7/9/2009 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2008/006894 | 1/17/2008 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4477619 | Lattimer et al. | Oct 1984 | A |
| 5326853 | Hayes | Jul 1994 | A |
| 7582698 | Lubnin et al. | Sep 2009 | B2 |
| Number | Date | Country |
|---|---|---|
| 2004-300617 | Oct 2004 | JP |
| 2004050736 | Jun 2004 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20090318601 A1 | Dec 2009 | US |