Water-based cement for producing tyres

Abstract

A water-based cement for producing tires, having water as solvent, cross-linkable unsaturated-chain polymer base, of sulphur, reinforcing filler, zinc oxide, accelerators, and an emulsifier of the general formula (I) [R1R2R3NR5(N(R4)3)n](n+1)+(n+1)X−  (I)where:X is an anionic atom or groupR1, R2 and R3, which may be the same or different, are each CmH2m+1, where m ranges between 1 and 3, or CH2CHCH2 or CHCHCH3 R4 is CH2CHCH2 or CHCHCH3 n is 0 or 1R5 is an aliphatic group C15-C22 when n is 0; and is an aliphatic group C8-C16 when n is 1when n is 0, at least one of R1, R2, R3 and R5 has a double bond.

Description

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a National Stage of International Application No. PCT/EP2009/064251 filed Oct. 29, 2009, which claims priority from European Patent Application No. 08167989.6 filed Oct. 30, 2008, the contents of all of which are incorporated herein by reference in their entirety.

TECHNICAL FIELD

The present invention relates to a water-based cement for producing tyres.

BACKGROUND ART

In tyre manufacturing, cements are normally organic-solvent-based. Cements of this sort are highly adhesive and easy to use, mainly on account of rubber dissolving readily in organic solvents and so blending with other rubber to form practically one piece once the organic solvent evaporates.

For environmental reasons, recent European directives have imposed a drastic reduction in the use of organic solvents in the tyre industry, thus forcing manufacturers to devise alternative solutions to ensure correct adhesion of rubber layers.

One alternative to traditional cements is water-based cements, in which organic solvent is replaced by water as solvent, and which poses the problem of ensuring dispersion in water of intrinsically hydrophobic ingredients. This is done using emulsifiers which, as is known, comprise a hydrophobic group capable of bonding the ingredient in question, and a hydrophilic group capable of ensuring its dispersion in water. Since emulsifiers are normally selectively effective as regards a particular compound, the making of water-based cement calls for using different types of emulsifiers.

Tests show that the presence of large quantities and different types of emulsifiers may impair the adhesive strength of the cement, hence the strong demand for water-based cement emulsifiers that are effective over a wide range of ingredients, to reduce both the quantity and the number of types of emulsifiers used.

The Applicant has surprisingly discovered a particular class of emulsifiers that is universally effective over the various ingredients of water-based cement.

According to the present invention, there is provided a water-based cement for producing tyres, comprising water as solvent, a cross-linkable unsaturated-chain polymer base, sulphur, reinforcing filler, zinc oxide, and accelerators; said cement being characterized by comprising an emulsifier of the general formula (I)[R₁R₂R₃NR₅(N(R₄)₃)_n]⁽ⁿ⁺¹⁾⁺(n+1)X⁻  (I)

where:

X is an anionic atom or group

R₁, R₂ and R₃, which may be the same or different, are each C_mH_2m+1, where m ranges between 1 and 3, or CH₂CHCH₂ or CHCHCH₃

R₄ is CH₂CHCH₂ or CHCHCH₃

n is 0 or 1

R₅ is an aliphatic group C₁₅-C₂₂ when n is 0; and is an aliphatic group C₈-C₁₆ when n is 1

when n is 0, at least one of R₁, R₂, R₃ and R₅ comprises a double bond.

Preferably, the water-based cement comprises by weight 5 to 80% of water, 10 to 60% of a cross-linkable unsaturated-chain polymer base, 0.2 to 1% of sulphur, 1 to 25% of reinforcing filler, 0.1 to 3% of zinc oxide, and 0.1 to 1% of accelerators; said cement being characterized by comprising 0.1 to 10% of an emulsifier of the general formula (I).

Preferably, R₁, R₂ and R₃ are CH₂CHCH₂.

Preferably, R₁, R₂ and R₃ are CH₂CHCH₂, R₅ comprises a double bond, and n is 0.

Preferably, R₁, R₂ and R₃ are CH₂CHCH₂, n is 1, and R₅ is a saturated aliphatic group.

Preferably, the quantity of emulsifier in the cement ranges between 0.5 and 5% by weight.

The examples below are purely indicative and non-limiting, for a clearer understanding of the invention.

EXAMPLES

Six water-based cements (A, B, C, D, E, F) in accordance with the present invention were prepared.

Table I shows the compositions, in percentage by weight, of the six cements.

	TABLE I
	A	B	C	D	E	F
WATER	50	50	50	50	50	50
NATURAL RUBBER	25	25	25	25	25	25
CARBON BLACK	13	13	13	13	13	13
ZINC OXIDE	1	1	1	1	1	1
ADHESIVE RESIN	3.6	3.6	3.6	3.6	3.6	3.6
SULPHUR	0.5	0.5	0.5	0.5	0.5	0.5
SULPHONAMIDE	0.5	0.5	0.5	0.5	0.5	0.5
EMULSIFIER (a)	2	—	—	—	—	—
EMULSIFIER (b)	—	2	—	—	—	—
EMULSIFIER (c)	—	—	2	—	—	—
EMULSIFIER (d)	—	—	—	2	—	—
EMULSIFIER (e)	—	—	—	—	2	—
EMULSIFIER (f)	—	—	—	—	—	2

The emulsifier (a) according to the present invention used in cement A is of the formula [(CH₃)₃N (CH₂)₈CHCH(CH₂)₇CH₃]⁺ I⁻.

The emulsifier (b) according to the present invention used in cement B is of the formula [(CH₂CHCH₂)₃N(CH₂)₁₅CH₃]⁺ Br⁻.

The emulsifier (c) according to the present invention used in cement C is of the formula [(CH₃)(CH₂CHCH₂)₂N (CH₂)₁₅CH₃]⁺ I⁻.

The emulsifier (d) according to the present invention used in cement D is of the formula [(CH₂CHCH₂)(CH₃)₂N (CH₂)₁₅CH₃]⁺ I⁻.

The emulsifier (e) according to the present invention used in cement E is of the formula [(CH₂CHCH₂)₃N (CH₂)₈CHCH(CH₂)₇CH₃]⁺ I⁻.

The emulsifier (f) according to the present invention used in cement F is of the formula [(CH₂CHCH₂)₃N(CH₂)₁₂N(CH₂CHCH₂)₃]²⁺ 2Br⁻.

To accurately assess the advantages of the cements according to the present invention, two comparison cements (G and H) were prepared. Cement G is a solvent-based cement, and cement H a known water-based cement.

Table II shows the compositions, in percentage by weight, of cements G and H.

	TABLE II
	G	H
	WATER	—	50.0
	HEPTANE	70.0	—
	NATURAL RUBBER	18.0	25.0
	CARBON BLACK	9.0	13.0
	STEARIC ACID	0.6	—
	ZINC OXIDE	0.3	1.0
	ADHESIVE RESIN	2.0	5.0
	SULPHUR	0.3	0.5
	SULPHONAMIDE	0.3	0.5
	STANDARD EMULSIFIERS	—	5.0

The standard emulsifiers used in cement H are: naphthylsulphonic acid for dispersing zinc oxide, sulphur, and accelerators; ethoxylated aliphatic amines and ethoxylated fatty acids for dispersing carbon black.

As will be clear to an expert, in addition to natural rubber, the cements according to the present invention may comprise any cross-linkable chain polymer base obtained by polymerization of conjugate dienes and/or aliphatic or aromatic vinyl monomers. For example, usable polymer bases are selected from the group comprising natural rubber, 1,4-cis polyisoprene, polybutadiene, isoprene-isobutene copolymers, possibly halogenated, butadiene-acrylonitrile copolymers, styrene-butadiene copolymers and styrene-butadiene-isoprene terpolymers, both in solution and emulsion, and ethylene-propylene-diene terpolymers. The above polymer bases may be used singly or mixed.

Laboratory Tests

Each cement was adhesion-tested on both green and cured rubber, as per ASTM Standard D624, was tested for rheometric properties as per ASTM Standard D5289, and was viscosity-tested as per ASTM Standard D6080. Table III shows the test results.

	TABLE III
	A	B	C	D	E	F	G	H
Viscosity	100	100	100	100	100	100	100	100
(cps)
ML (dNm)	2.1	2.1	2.4	2.5	2.6	3.0	2.1	2.0
MH (dNm)	18.0	20.8	19.1	19.4	20.5	25.1	18.0	16.8
T10 (min)	0.7	0.7	0.8	0.8	0.6	1.0	0.7	0.5
T50 (min)	1.1	1.3	1.4	1.2	1.7	1.6	1.1	1.1
T90 (min)	2.9	2.7	2.9	3.0	2.5	3.5	2.9	3.0
Green-rubber	1.5	1.6	1.5	1.8	2.0	2.1	2.0	1.20
adhesion
(N/mm)
Cured-rubber	19.7	23.0	21.0	20.6	23.5	25.0	20.0	10.0
adhesion*
(N/mm)
*The cured rubber was obtained as per ASTM Standard 1382, by curing for 10 minutes at a constant temperature of 160° C.

As shown in Table III, the cements according to the present invention using emulsifiers of formula (I) need less emulsifier as compared with water-based cements of the prior art, and as such are highly stable and of even greater adhesion strength than solvent-based cements.

In short, using a universal emulsifier, different types of emulsifier need no longer be used, and the amount of emulsifier used can be greatly reduced.

As shown by the results in Table III, using an emulsifier as claimed in no way impairs the other characteristics of the cement, such as viscosity and rheometric properties.

Claims

1. A water-based cement for producing tyres, comprising water as solvent, a cross-linkable unsaturated-chain polymer base, sulphur, reinforcing filler, zinc oxide, accelerators; said cement being characterized by comprising an emulsifier of the general formula (I) [R1R2R3NR5(N(R4)3)n](n+1)+(n+1)X−  (I)where:X is an anionic atom or group;R1, R2 and R3, which may be the same or different, are each CmH2m+1, where m ranges between 1 and 3, or CH2CHCH2 or CHCHCH3;R4 is CH2CHCH2 or CHCHCH3;n is 0 or 1;R5 is an aliphatic group C15-C22 when n is 0; and is an aliphatic group C8-C16 when n is 1;when n is 0, at least one of R1, R2, R3 and R5 comprises a double bond.

2. A water-based cement for producing tyres as claimed in claim 1, characterized by comprising by weight 5 to 80% of water, 10 to 60% of a cross-linkable unsaturated-chain polymer base, 0.2 to 1% of sulphur, 1 to 25% of reinforcing filler, 0.1 to 3% of zinc oxide, and 0.1 to 1% of accelerators; said cement being characterized by comprising 0.1 to 10% of an emulsifier of the general formula (I).

3. A water-based cement for producing tyres, as claimed in claim 1, characterized in that R1, R2 and R3 are CH2CHCH2.

4. A water-based cement for producing tyres, as claimed in claim 1, characterized in that R1, R2 and R3 are CH2CHCH2, R5 comprises a double bond, and n is 0.

5. A water-based cement for producing tyres, as claimed in claim 4, characterized in that said emulsifier is [(CH2CHCH2)3N(CH2)8CHCH(CH2)7CH3]+X−.

6. A water-based cement for producing tyres, as claimed in claim 1, characterized in that R1, R2 and R3 are CH2CHCH2, n is 1, and R5 is a saturated aliphatic group.

7. A water-based cement for producing tyres, as claimed in claim 6, characterized in that said emulsifier is [(CH2CHCH2)3N(CH2)12N(CH2CHCH2)3]2+2X−.

8. A tyre produced using a water-based cement as claimed in claim 1.