Patent Grant
8809243
This application is a 371 of PCT/EP2010/005157, filed Aug. 23, 2010.
1. Field of the Invention
This invention relates to water-based lubricants. In particular, the invention relates to the use of water-based lubricants for the lubrication of frictional partners in drive elements, as well as their use.
2. Description of Related Art
The development of new lubricants must go along with the general further development of technology, which imposes new and more stringent requirements on the lubricant compositions, this in particular also with respect to environmental protection and carbon dioxide emissions. The known lubricants based on mineral oil or synthetic oil no longer measure up to these requirements.
Lubricants are used in particular in drive elements, such as, e.g., chains, gears, roller bearings, and plain bearings or seals on rotating shafts. These lubricants are based on mineral oil or synthetic hydrocarbons. In particular, in roller bearings and plain bearings, the lubricants cause a separating, load-transferring lubricating film to be built up between the parts that slide or roll on one another. It is thus achieved that the metal surfaces do not touch, and thus, also no friction occurs. The lubrication means must therefore satisfy high requirements with respect to:
Cooling of the friction site,
Extreme operating conditions, such as very high and very low speeds,
High temperatures that are caused by high speeds and loads and associated internal or external heating,
Very low temperatures in a cold environment,
Special user requirements as regards the running features, e.g., low friction, noise attenuation,
Extremely long running times without interim relubrication,
Biodegradability.
A ready-to-use gear, an operating fluid for such a gear, and a method for its start-up are known from International Patent Application Publication WO 2007/098523 A2. The operating fluid is formed of a mixture of water and an aliphatic hydrocarbon, in which graphite particles are suspended as a solid lubricant. This solid lubricant is in the form of flocculent graphite particles which have a grain size of less than 50 μm. Other components of these lubricating and cooling fluids are dispersing additives, anti-foaming agents, and corrosion inhibitors. In this operating fluid, it is disadvantageous that the graphite particles that are present in solid or flocculent form settle out of the suspension and thus can adhere to the working parts to be lubricated. Another drawback is the persistent fouling of components that come into contact with graphite-containing lubricants. If filtration of the lubricating oil during operation is necessary, the graphite can result in a clogging of the filter pores. In addition, the operating fluid has a very low viscosity, which in the case of high loads, can result in a failure of the lubricating film.
A primary object of this invention is therefore to prepare a water-based lubricant that meets the above-mentioned requirements, in particular is biodegradable, and contributes to significantly reducing the production of carbon dioxide.
This object is achieved according to the invention in that a lubricant is used that comprised of water, water-soluble polyalkylene glycols, water-soluble emulsifiers, and additives conventionally used in lubricants. The water-soluble polyalkylene glycols are selected from the group of statistically distributed polyoxyethylene units and polyoxypropylene units and/or other polyoxyalkylene components with one or more hydroxyl end groups and from a block polymer that consists of polyoxyethylene units and/or polyoxypropylene units, and/or other polyoxyalkylene components. As emulsifiers, anionic surfactants, e.g., sulfonates, non-ionic surfactants, e.g., fatty alcohol ethoxylates, or NPE or cationic surfactants, e.g., quaternary ammonium compounds, water-soluble or water-emulsifiable carboxylic acid esters are used.
It was found, surprisingly enough, that certain water-based formulations (water content >10%) exceed the lubrication output of conventional lubricants and significantly reduce friction coefficients. Because of this and owing to the good intrinsic cooling action, reduced temperature development occurs in the tribological system. Such water-based lubricants are readily biodegradable and are environmentally compatible in an aquatic environment. In addition, they are distinguished by good compatibility with rubber-elastic materials.
Depending on the application, for example, the low-temperature behavior of water-based lubricants can be considerably improved by, for example, addition of anti-icing additives, e.g., low-molecular glycols, glycerol, salts, or ionic liquids.
In addition, additives can be added to influence the properties of the lubricant in a targeted manner. The latter can be present in soluble, or dispersed, colloidal or nanoscale form.
If desired, water-based lubricants can also be formulated in a foaming manner. The application as spray foam is of special interest in this connection, since as a result, a visual monitoring of the lubricant application is made possible. In the case of a contamination of textiles or machine parts with water-based lubricating fluids, the latter are easy to clean.
To dye lubricants based on mineral oil or synthetic oil, in most cases harmful and/or ecotoxicological dyes are necessary. In the case of water-based lubricants, a number of toxicologically harmless water-soluble dyes up to food coloring can be used. The “base oil” according to the invention can also be transformed by mixing with soap or urea powders, sheet silicates or other current lubricant thickeners to form a lubrication fat or a lubrication paste.
The sole FIGURE of the drawings is a graph showing torque of a roller bearing with foamed and grease lubricants.
A preferred embodiment of the water-based lubricant according to the invention contains:
5 to 80% by weight of water-soluble polyalkylene glycol that is selected from the group that consists of statistically distributed polyoxyethylene units and/or polyoxypropylene units and/or other polyoxyalkylene components, a block polymer that consists of polyoxyethylene units and/or polyoxypropylene units and/or other polyoxyalkylene components,
0.5 to 20% by weight of foaming or non-foaming emulsifiers from the class of anionic surfactants (e.g., sulfonates), non-ionic surfactants (e.g., fatty alcohol ethoxylates or else NPE) or cationic surfactants (e.g., quaternary ammonium compounds), or water-soluble or water-emulsifiable carboxylic acid esters,
0.5 to 50% by weight of anti-icing additives, selected from the group that consists of alkylene glycol, glycerol, salts or ionic liquids,
0.05 to 10% by weight of corrosion additives, such as alkanolamines, boric acid or carboxylic acid derivatives,
0.001 to 1% by weight of additives for preventing the formation of foam, e.g., polydimethylsiloxanes or acrylate polymers, and
0.05 to 5% by weight of wear protection agents
Water added to make 100% by weight.
In addition, the lubricant composition can contain the following components:
0.001 to 0.5% by weight of biocides, e.g., sorbic acid and/or
0.05 to 5% by weight of nanoparticles.
In addition, the lubricant composition can contain
0.5 to 40% by weight of lubricant thickener, selected from the group that is comprised of metal soaps that are formed of monocarboxylic acids and/or dicarboxylic acids, ureas, sheet silicates, solid lubricants, and aerosil.
For the production of a gear oil, the following components are mixed:
This is a virtually colorless, limpid solution of ISO VG 32 with little foaming tendency. The lubricant remains liquid up to temperatures of −35° C.
The friction level that is drastically reduced in comparison to conventional lubricants results in considerably improved energy efficiency and a lower noise level as well as extended service life during operation. Because of the replacement of mineral oil or a base oil that corresponds thereto by water, the advantage lies in the sustainability of this lubricant.
In particular because of the solid lubricant-free design, such a composite lubricant is suitable for applications in which the lubricant is filtered continuously, such as, e.g., gears in wind power plants.
In Table 1, properties of sample formulation 1 are cited in comparison to a mineral-oil-based product.
For the production of a heavy-duty gear oil, the following components are mixed with one another:
The advantages of the lubricant that are already described in Example 1 are also present here. By the addition of nanoparticles, further improved protection against wear is ensured.
In Table 2, properties of sample formulation 2 are cited in comparison to a mineral-oil-based product. Despite considerably lower viscosity, the aqueous formulation has a significantly improved protection against wear (higher achievable surface pressing) according to Reichert.
An oil foam consists of:
The advantages of the lubricant that are already described in Example 1 are also present here; the pour point of the formulation is approximately −20° C.
This composition has a high foam formation, which makes possible the application by means of spray/pump spray as a foam.
Such an application has the advantage that the lubricant on the surface can be easily detected visually, even with a minimal amount of lubrication immediately after application, e.g., with the focus on quality assurance. Another advantage of the application as a foam is the improved wetting of the entire surface of the tribological system, which makes possible a shortened intake time and an improved intake behavior.
In the FIGURE, the torque of a roller bearing lubricated with known grease lubricant and a foam lubricant in accordance with the present invention are show. As can be seen, a roller bearing that is provided with foamed (not water-based) lubricant experiences a considerably lower torque within the first 60 minutes of running time than the grease lubricant.
Production of a water-based fat with low-temperature suitability containing:
In Table 2, properties of sample formulation 4 are cited.
Lubricant consisting of:
This lubricant is suitable for lubrication of seals on rotating shafts and, in contrast to the known lubricating agents that consist of mineral oils or synthetic hydrocarbons, it is readily biodegradable and therefore can be disposed of in an environmentally compatible way. It is distinguished by a low friction, good cooling action, good compatibility with rubber-elastic materials, and it has a low potential of water contamination. Advantageously, in the case of dilution with water, it changes the viscosity only slightly and therefore makes possible the formation of an active lubricating film.
The water-based lubricant according to the invention can be used for lubrication of drive elements in chains, gears, roller bearings and plain bearings or for lubrication of seals on rotating shafts in the form of a foam, spray or emulsion, which is applied by means of spray or pump spray systems with the focus of better surface wetting and better detectability of thin lubricating films.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2009 039 626 | Sep 2009 | DE | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2010/005157 | 8/23/2010 | WO | 00 | 2/20/2012 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2011/026576 | 3/10/2011 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 8258086 | Patel et al. | Sep 2012 | B2 |
| 20020095021 | Pollmann et al. | Jul 2002 | A1 |
| 20050256014 | Sherman et al. | Nov 2005 | A1 |
| 20060270569 | Athans | Nov 2006 | A1 |
| 20070027037 | Easter | Feb 2007 | A1 |
| 20110046027 | Zhamu et al. | Feb 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| 9715643 | May 1997 | WO |
| 2004007651 | Jan 2004 | WO |
| 2005113640 | Dec 2005 | WO |
| 2007098523 | Sep 2007 | WO |
| Entry |
|---|
| R. Van Voorst and F. Alam , Polyglycols as Base Fluids for Environmentally-Friendly Lubricants, Journal of Synthetic Lubrication, Leaf Coppin Publishing Ltd., Deal,Kent, GB, BD. 16, NR. 4, Jan. 1, 2000; 16-4, pp. 313-322, ISSN 0265-6582, XP007909273. |
| Number | Date | Country | |
|---|---|---|---|
| 20120149616 A1 | Jun 2012 | US |