Water-dispersible and multicomponent fibers from sulfopolyesters

Information

  • Patent Grant
  • 8435908
  • Patent Number
    8,435,908
  • Date Filed
    Monday, December 13, 2010
    13 years ago
  • Date Issued
    Tuesday, May 7, 2013
    11 years ago
Abstract
Disclosed are water-dispersible fibers derived from sulfopolyesters having a Tg of at least 25° C. The fibers may contain a single sulfopolyester or a blend of a sulfopolyester with a water-dispersible or water-nondispersible polymer. Also disclosed are multicomponent fibers comprising a water dispersible sulfopolyester having a Tg of at least 57° C. and a water non-dispersible polymer. The multicomponent fibers may be used to produce microdenier fibers. Fibrous articles may be produced from the water-dispersible fibers, multicomponent fibers, and microdenier fibers. The fibrous articles include water-dispersible and microdenier nonwoven webs, fabrics, and multilayered articles such as wipes, gauze, tissue, diapers, panty liners, sanitary napkins, bandages, and surgical dressings. Also disclosed is a process for water-dispersible fibers, nonwoven fabrics, and microdenier webs. The fibers and fibrous articles have further applications in flushable personal care and cleaning products, disposable protective outerwear, and laminating binders.
Description
FIELD OF THE INVENTION

The present invention pertains to water-dispersible fibers and fibrous articles comprising a sulfopolyester. The invention further pertains to multicomponent fibers comprising a sulfopolyester and the microdenier fibers and fibrous articles prepared therefrom. The invention also pertains to processes for water-dispersible, multicomponent, and microdenier fibers and to nonwoven fabrics prepared therefrom. The fibers and fibrous articles have applications in flushable personal care products and medical products.


BACKGROUND OF THE INVENTION

Fibers, melt blown webs and other melt spun fibrous articles have been made from thermoplastic polymers, such as poly(propylene), polyamides, and polyesters. One common application of these fibers and fibrous articles are nonwoven fabrics and, in particular, in personal care products such as wipes, feminine hygiene products, baby diapers, adult incontinence briefs, hospital/surgical and other medical disposables, protective fabrics and layers, geotextiles, industrial wipes, and filter media. Unfortunately, the personal care products mades from conventional thermoplastic polymers are difficult to dispose of and are usually placed in landfills. One promising alternative method of disposal is to make these products or their components “flushable”, i.e., compatible with public sewerage systems. The use of water-dispersible or water-soluble materials also improves recyclability and reclamation of personal care products. The various thermoplastic polymers now used in personal care products are not inherently water-dispersible or soluble and, hence, do not produce articles that readily disintegrate and can be disposed of in a sewerage system or recycled easily.


The desirability of flushable personal care products has resulted in a need for fibers, nonwovens, and other fibrous articles with various degrees of water-responsivity. Various approaches to addressing these needs have been described, for example, in U.S. Pat. Nos. 6,548,592; 6,552,162; 5,281,306; 5,292,581; 5,935,880; and 5,509,913; U.S. patent application Ser. Nos. 09/775,312; and 09/752,017; and PCT International Publication No. WO 01/66666 A2. These approaches, however, suffer from a number of disadvantages and do not provide a fibrous article, such as a fiber or nonwoven fabric, that possesses a satisfactory balance of performance properties, such as tensile strength, absorptivity, flexibility, and fabric integrity under both wet or dry conditions.


For example, typical nonwoven technology is based on the multidirectional deposition of fibers that are treated with a resin binding adhesive to form a web having strong integrity and other desirable properties. The resulting assemblies, however, generally have poor water-responsivity and are not suitable for flushable applications. The presence of binder also may result in undesirable properties in the final product, such as reduced sheet wettability, increased stiffness, stickiness, and higher production costs. It is also difficult to produce a binder that will exhibit adequate wet strength during use and yet disperse quickly upon disposal. Thus, nonwoven assemblies using these binders may either disintegrate slowly under ambient conditions or have less than adequate wet strength properties in the presence of body fluids. To address this problem, pH and ion-sensitive water-dispersible binders, such as lattices containing acrylic or methacrylic acid with or without added salts, are known and described, for example, in U.S. Pat. No. 6,548,592 B1. Ion concentrations and pH levels in public sewerage and residential septic systems, however, can vary widely among geographical locations and may not be sufficient for the binder to become soluble and disperse. In this case, the fibrous articles will not disintegrate after disposal and can clog drains or sewer laterals.


Multicomponent fibers containing a water-dispersible component and a thermoplastic water non-dispersible component have been described, for example, in U.S. Pat. Nos. 5,916,678; 5,405,698; 4,966,808; 5,525282; 5,366,804; 5,486,418. For example, these multicomponent fibers may be a bicomponent fiber having a shaped or engineered transverse cross section such as, for example, an islands-in-the-sea, sheath core, side-by-side, or segmented pie configuration. The multicomponent fiber can be subjected to water or a dilute alkaline solution where the water-dispersible component is dissolved away to leave the water non-dispersible component behind as separate, independent fibers of extremely small fineness. Polymers which have good water dispersibility, however, often impart tackiness to the resulting multicomponent fibers, which causes the fiber to stick together, block, or fuse during winding or storage after several days, especially under hot, humid conditions. To prevent fusing, often a fatty acid or oil-based finish is applied to the surface of the fiber. In addition, large proportions of pigments or fillers are sometimes added to water dispersible polymers to prevent fusing of the fibers as described, for example, in U.S. Pat. No. 6,171,685. Such oil finishes, pigments, and fillers require additional processing steps and can impart undesirable properties to the final fiber. Many water-dispersible polymers also require alkaline solutions for their removal which can cause degradation of the other polymer components of the fiber such as, for example, reduction of inherent viscosity, tenacity, and melt strength. Further, some water-dispersible polymers can not withstand exposure to water during hydroentanglement and, thus, are not suitable for the manufacture of nonwoven webs and fabrics.


Alternatively, the water-dispersible component may serve as a bonding agent for the thermoplastic fibers in nonwoven webs. Upon exposure to water, the fiber to fiber bonds come apart such that the nonwoven web loses its integrity and breaks down into individual fibers. The thermoplastic fiber components of these nonwoven webs, however, are not water-dispersible and remain present in the aqueous medium and, thus, must eventually be removed from municipal wastewater treatment plants. Hydroentanglement may be used to produce disintegratable nonwoven fabrics without or with very low levels (<5 wt %) of added binder to hold the fibers together. Although these fabrics may disintegrate upon disposal, they often utilize fibers that are not water soluble or water-dispersible and may result in entanglement and plugging within sewer systems. Any added water-dispersible binders also must be minimally affected by hydroentangling and not form gelatinous buildup or cross-link, and thereby contribute to fabric handling or sewer related problems.


A few water-soluble or water-dispersible polymers are available, but are generally not applicable to melt blown fiber forming operations or melt spinning in general. Polymers, such as polyvinyl alcohol, polyvinyl pyrrolidone, and polyacrylic acid are not melt processable as a result of thermal decomposition that occurs at temperatures below the point where a suitable melt viscosity is attained. High molecular weight polyethylene oxide may have suitable thermal stability, but would provide a high viscosity solution at the polymer interface resulting in a slow rate of disintegration. Water-dispersible sulfopolyesters have been described, for example, in U.S. Pat. Nos. 6,171,685; 5,543,488; 5,853,701; 4,304,901; 6,211,309; 5,570,605; 6,428,900; and 3,779,993. Typical sulfopolyesters, however, are low molecular weight thermoplastics that are brittle and lack the flexibility to withstand a winding operation to yield a roll of material that does not fracture or crumble. Sulfopolyesters also can exhibit blocking or fusing during processing into film or fibers, which may require the use of oil finishes or large amounts of pigments or fillers to avoid. Low molecular weight polyethylene oxide (more commonly known as polyethylene glycol) is a weak/brittle polymer that also does not have the required physical properties for fiber applications. Forming fibers from known water-soluble polymers via solution techniques is an alternative, but the added complexity of removing solvent, especially water, increases manufacturing costs.


Accordingly, there is a need for a water-dispersible fiber and fibrous articles prepared therefrom that exhibit adequate tensile strength, absorptivity, flexibility, and fabric integrity in the presence of moisture, especially upon exposure to human bodily fluids. In addition, a fibrous article is needed that does not require a binder and completely disperses or dissolves in residential or municipal sewerage systems. Potential uses include, but are not limited to, melt blown webs, spunbond fabrics, hydroentangled fabrics, dry-laid non-wovens, bicomponent fiber components, adhesive promoting layers, binders for cellulosics, flushable nonwovens and films, dissolvable binder fibers, protective layers, and carriers for active ingredients to be released or dissolved in water. There is also a need for multicomponent fiber having a water-dispersible component that does not exhibit excessive blocking or fusing of filaments during spinning operations, is easily removed by hot water at neutral or slightly acidic pH, and is suitable for hydroentangling processes to manufacture nonwoven fabrics. Other extrudable and melt spun fibrous materials are also possible.


SUMMARY OF THE INVENTION

We have unexpectedly discovered that flexible, water-dispersible fibers may be prepared from sulfopolyesters. Thus the present invention provides a water-dispersible fiber comprising:

  • (A) a sulfopolyester having a glass transistion temperature (Tg) of at least 25° C., the sulfopolyester comprising:
    • (i) residues of one or more dicarboxylic acids;
    • (ii) about 4 to about 40 mole %, based on the total repeating units, of residues of at least one sulfomonomer having 2 functional groups and one or more sulfonate groups attached to an aromatic or cycloaliphatic ring wherein the functional groups are hydroxyl, carboxyl, or a combination thereof;
    • (iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

      H—(OCH2—CH2)n-OH
      • wherein n is an integer in the range of 2 to about 500; and
    • (iv) 0 to about 25 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof;
  • (B) optionally, a water-dispersible polymer blended with the sulfopolyester; and
  • (C) optionally, a water-nondispersible polymer blended with the sulfopolyester with the proviso that the blend is an immiscible blend;


    wherein the fiber contains less than 10 weight percent of a pigment or filler, based on the total weight of the fiber.


    The fibers of the present invention may be unicomponent fibers that rapidly disperse or dissolve in water and may be produced by melt-blowing or melt-spinning. The fibers may be prepared from a single sulfopolyester or a blend of the sulfopolyester with a water-dispersible or water-nondispersible polymer. Thus, the fiber of the present invention, optionally, may include a water-dispersible polymer blended with the sulfopolyester. In addition, the fiber may optionally include a water-nondispersible polymer blended with the sulfopolyester, provided that the blend is an immiscible blend. Our invention also includes fibrous articles comprising our water-dispersible fibers. Thus, the fibers of our invention may be used to prepare various fibrous articles, such as yarns, melt-blown webs, spunbonded webs, and nonwoven fabrics that are, in turn, water-dispersible or flushable. Staple fibers of our invention can also be blended with natural or synthetic fibers in paper, nonwoven webs, and textile yarns.


Another aspect of the present invention is a water-dispersible fiber comprising:

  • A) a sulfopolyester having a glass transistion temperature (Tg) of at least 25° C., the sulfopolyester comprising:
    • (i) about 50 to about 96 mole % of one or more residues of isophthalic acid or terephthalic acid, based on the total acid residues;
    • (ii) about 4 to about 30 mole %, based on the total acid residues, of a residue of sod iosulfoisophthalic acid;
    • (iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

      H—(OCH2—CH2)n-OH
      • wherein n is an integer in the range of 2 to about 500;
    • (iv) 0 to about 20 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof;
  • (B) optionally, a first water-dispersible polymer blended with the sulfopolyester; and
  • (C) optionally, a water-nondispersible polymer blended with the sulfopolyester to form a blend with the proviso that the blend is an immiscible blend;


    wherein the fiber contains less than 10 weight percent of a pigment or filler, based on the total weight of the fiber.


    The water-dispersible, fibrous articles of the present invention include personal care articles such as, for example, wipes, gauze, tissue, diapers, training pants, sanitary napkins, bandages, wound care, and surgical dressings. In addition to being water-dispersible, the fibrous articles of our invention are flushable, that is, compatible with and suitable for disposal in residential and municipal sewerage systems.


The present invention also provides a multicomponent fiber comprising a water-dispersible sulfopolyester and one or more water non-dispersible polymers. The fiber has an engineered geometry such that the water non-dispersible polymers are present as segments substantially isolated from each other by the intervening sulfopolyester, which acts as a binder or encapsulating matrix for the water non-dispersible segments. Thus, another aspect of our invention is a multicomponent fiber having a shaped cross section, comprising:

    • A) a water dispersible sulfopolyester having a glass transistion temperature (Tg) of at least 57° C., the sulfpolyester comprising:
      • (i) residues of one or more dicarboxylic acids;
      • (ii) about 4 to about 40 mole %, based on the total repeating units, of residues of at least one sulfomonomer having 2 functional groups and one or more sulfonate groups attached to an aromatic or cycloaliphatic ring wherein the functional groups are hydroxyl, carboxyl, or a combination thereof;
      • (iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

        H—(OCH2—CH2)n—OH
        • wherein n is an integer in the range of 2 to about 500; and
      • (iv) 0 to about 25 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof; and
    • B) a plurality of segments comprising one or more water-nondispersable polymers immiscible with the sulfopolyester, wherein the segments are substantially isolated from each other by the sulfopolyester intervening between the segments;
    • wherein the fiber contains less than 10 weight percent of a pigment or filler, based on the total weight of the fiber.


      The sulfopolyester has a glass transistion temperature of at least 57° C. which greatly reduces blocking and fusion of the fiber during winding and long term storage. The sulfopolyester may be removed by contacting the multicomponent fiber with water to leave behind the water non-dispersible segments as microdenier fibers. Our invention, therefore, also provides a process for microdenier fibers comprising:
  • A. spinning a water dispersible sulfopolyester having a glass transistion temperature (Tg) of at least 57° C. and one or more water-nondispersable polymers immiscible with the sulfopolyester into multicomponent fibers, the sulfpolyester comprising:
    • (i) about 50 to about 96 mole % of one or more residues of isophthalic acid or terephthalic acid, based on the total acid residues;
    • (ii) about 4 to about 30 mole %, based on the total acid residues, of a residue of sod iosulfoisophthalic acid;
    • (iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

      H—(OCH2—CH2)n—OH
      • wherein n is an integer in the range of 2 to about 500; and
    • (iv) 0 to about 20 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof;
    • wherein the fibers have a plurality of segments comprising the water-nondispersable polymers wherein the segments are substantially isolated from each other by the sulfopolyester intervening between the segments and the fibers contain less than 10 weight percent of a pigment or filler, based on the total weight of the fibers; and
  • B. contacting the multicomponent fibers with water to remove the sulfopolyester thereby forming microdenier fibers.


The water non-dispersible polymers may be biodistintegratable as determined by DIN Standard 54900 and/or biodegradable as determined by ASTM Standard Method, D6340-98. The multicomponent fiber also may be used to prepare a fibrous article such as a yarn, fabric, melt-blown web, spun-bonded web, or non-woven fabric and which may comprise one or more layers of fibers. The fibrous article having multicomponent fibers, in turn, may be contacted with water to produce fibrous articles containing microdenier fibers. Thus, another aspect of the invention is a process for a microdenier fiber web, comprising:

  • A. spinning a water dispersible sulfopolyester having a glass transition temperature (Tg) of at least 57° C. and one or more water-nondispersable polymers immiscible with the sulfopolyester into multicomponent fibers, the sulfpolyester comprising:
    • (i) about 50 to about 96 mole % of one or more residues of isophthalic acid or terephthalic acid, based on the total acid residues;
    • (ii) about 4 to about 30 mole %, based on the total acid residues, of a residue of sod iosulfoisophthalic acid;
    • (iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

      H—(OCH2—CH2)n—OH
      • wherein n is an integer in the range of 2 to about 500; and
    • (iv) 0 to about 20 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof.
    • wherein the multicomponent fibers have a plurality of segments comprising the water-nondispersable polymers and the segments are substantially isolated from each other by the sulfopolyester intervening between the segments and the fibers contain less than 10 weight percent of a pigment or filler, based on the total weight of said fibers;
  • B. overlapping and collecting the multicomponent fibers of Step A to form a nonwoven web; and
  • C. contacting the nonwoven web with water to remove the sulfopolyester thereby forming a microdenier fiber web.


Our invention also provides a process for a process for water-dispersible, nonwoven fabric comprising:

  • I. heating a water-dispersible polymer composition to a temperature above its flow point, wherein the polymer composition comprises
    • (A) a sulfopolyester having a glass transistion temperature (Tg) of at least 25° C., the sulfopolyester comprising:
      • (i) residues of one or more dicarboxylic acids;
      • (ii) about 4 to about 40 mole %, based on the total repeating units, of residues of at least one sulfomonomer having 2 functional groups and one or more metal sulfonate groups attached to an aromatic or cycloaliphatic ring wherein the functional groups are hydroxyl, carboxyl, or a combination thereof;
      • (iii) one or more diol residues wherein at least 20 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

        H—(OCH2—CH2)n-OH
        • wherein n is an integer in the range of 2 to about 500;
      • (iv) 0 to about 25 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof;
    • (B) optionally, a water-dispersible polymer blended with the sulfopolyester; and
    • (C) optionally, a water-nondispersible polymer blended with the sulfopolyester to form a blend with the proviso that the blend is an immiscible blend;


      wherein the polymer composition contains less than 10 weight percent of a pigment or filler, based on the total weight of the polymer composition;
  • II. melt spinning filaments; and
  • III. overlapping and collecting the filaments of Step II to form a nonwoven web.


Our invention thus offers a novel and inexpensive process for a water-dispersible nonwoven fabric by melt-spinning a water-dispersible sulfopolyester and forming a nonwoven web. The nonwoven fabric may be in the form of a flat fabric or a 3-dimensional shape and may be incorporated into a variety of fibrous articles such as the personal care articles noted hereinabove or used for the manufacture of water-dispersible and/or flushable protective outerware such as, for example, surgical gowns and protective clothing for chemical and biohazard cleanup and laboratory work.







DETAILED DESCRIPTION

The present invention provides water-dispersible fibers and fibrous articles that show tensile strength, absorptivity, flexibility, and fabric integrity in the presence of moisture, especially upon exposure to human bodily fluids. The fibers and fibrous articles of our invention do not require the presence of oil, wax, or fatty acid finishes or the use of large amounts (typically 10 wt % or greater) of pigments or fillers to prevent blocking or fusing of the fibers during processing. In addition, the fibrous articles prepared from our novel fibers do not require a binder and readily disperse or dissolve in home or public sewerage systems. In a general embodiment, our invention provides a water-dispersible fiber comprising a sulfopolyester having a glass transistion temperature (Tg) of at least 25° C., wherein the sulfpolyester comprises: (i) residues of one or more dicarboxylic acids; (ii) about 4 to about 40 mole %, based on the total repeating units, of residues of at least one sulfomonomer having 2 functional groups and one or more sulfonate groups attached to an aromatic or cycloaliphatic ring wherein the functional groups are hydroxyl, carboxyl, or a combination thereof; (iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

H—(OCH2—CH2)n—OH

wherein n is an integer in the range of 2 to about 500; and (iv) 0 to about 25 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof. Our fiber may optionally include a water-dispersible polymer blended with the sulfopolyester and, optionally, a water-nondispersible polymer blended with the sulfopolyester with the proviso that the blend is an immiscible blend. Our fiber contains less than 10 weight percent of a pigment or filler, based on the total weight of the fiber. The present invention also includes fibrous articles comprising these fibers and may include personal care products such as wipes, gauze, tissue, diapers, adult incontinence briefs, training pants, sanitary napkins, bandages, and surgical dressings. The fibrous articles may have one or more absorbent layers of fibers.


The fibers of our invention may be unicomponent fibers, bicomponent or multicomponent fibers. For example, the fibers of the present invention may be prepared by melt spinning a single sulfopolyester or sulfopolyester blend and include staple, monofilament, and multifilament fibers with a shaped cross-section. In addition, our invention provides multicomponent fibers, such as described, for example, in U.S. Pat. No. 5,916,678, which may be prepared by extruding the sulfopolyester and one or more water non-dispersible polymers, which are immiscible with the sulfopolyester, separately through a spinneret having a shaped or engineered tranverse geometry such as, for example, an “islands-in-the-sea”, sheath-core, side-by-side, or segmented pie configuration. The sulfopolyester may be later removed by dissolving the interfacial layers or pie segments and leaving the smaller filaments or microdenier fibers of the water non-dispersible polymer(s). For example, the sulfopolyester and water non-dispersible polymers may be fed to a polymer distribution system where the polymers are introduced into a segmented spinneret plate. The polymers follow separate paths to the fiber spinneret and are combined at the spinneret hole which comprises either two concentric circular holes thus providing a sheath-core type fiber, or a circular spinneret hole divided along a diameter into multiple parts to provide a fiber having a side-by-side type. Alternatively, the immiscible water dispersible sulfopolyester and water non-dispersible polymers may be introduced separately into a spinneret having a plurality of radial channels to produce a multicomponent fiber having a segmented pie cross section. Typically, the sulfopolyester will form the “sheath” component of a sheath core configuration. In fiber cross sections having a plurality of segments, the water non-dispersible segments, typically, are substantially isolated from each other by the sulfopolyester. Alternatively, multicomponent fibers may be formed by melting the sulfopolyester and water non-dispersible polymers in separate extruders and directing the polymer flows into one spinneret with a plurality of distribution flow paths in form of small thin tubes or segments to provide a fiber having an islands-in-the-sea shaped cross section. An example of such a spinneret is described in U.S. Pat. No. 5,366,804. In the present invention, typically, the sulfopolyester will form the “sea” component and the water non-dispersible polymer will for the “islands” component.


Unless otherwise indicated, all numbers expressing quantities of ingredients, properties such as molecular weight, reaction conditions, and so forth used in the specification and claims are to be understood as being modified in all instances by the term “about.” Accordingly, unless indicated to the contrary, the numerical parameters set forth in the following specification and attached claims are approximations that may vary depending upon the desired properties sought to be obtained by the present invention. At the very least, each numerical parameter should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques. Further, the ranges stated in this disclosure and the claims are intended to include the entire range specifically and not just the endpoint(s). For example, a range stated to be 0 to 10 is intended to disclose all whole numbers between 0 and 10 such as, for example 1, 2, 3, 4, etc., all fractional numbers between 0 and 10, for example 1.5, 2.3, 4.57, 6.1113, etc., and the endpoints 0 and 10. Also, a range associated with chemical substituent groups such as, for example, “C1 to C5 hydrocarbons”, is intended to specifically include and disclose C1 and C5 hydrocarbons as well as C2, C3, and C4 hydrocarbons.


Notwithstanding that the numerical ranges and parameters setting forth the broad scope of the invention are approximations, the numerical values set forth in the specific examples are reported as precisely as possible. Any numerical value, however, inherently contain certain errors necessarily resulting from the standard deviation found in their respective testing measurements.


The unicomponent fibers and fibrous articles of the present invention are water-dispersible and, typically, completely disperse at room temperature. Higher water temperatures can be used to accelerate their dispersibility or rate of removal from the nonwoven or multicomponent fiber. The term “water-dispersible”, as used herein with respect to unicomponent fibers and fibrous articles prepared from unicomponent fibers, is intended to be synonymous with the terms “water-dissipatable”, “water-disintegratable”, “water-dissolvable”, “water-dispellable”, “water soluble”, water-removable”, “hydrosoluble”, and “hydrodispersible” and is intended to mean that the fiber or fibrous article is therein or therethrough dispersed or dissolved by the action of water. The terms “dispersed”, “dispersible”, “dissipate”, or “dissipatable” mean that, using a sufficient amount of deionized water (e.g., 100:1 water:fiber by weight) to form a loose suspension or slurry of the fibers or fibrous article, at a temperature of about 60° C., and within a time period of up to 5 days, the fiber or fibrous article dissolves, disintegrates, or separates into a plurality of incoherent pieces or particles distributed more or less throughout the medium such that no recognizable filaments are recoverable from the medium upon removal of the water, for example, by filtration or evaporation. Thus, “water-dispersible”, as used herein, is not intended to include the simple disintegration of an assembly of entangled or bound, but otherwise water insoluble or nondispersible, fibers wherein the fiber assembly simply breaks apart in water to produce a slurry of fibers in water which could be recovered by removal of the water. In the context of this invention, all of these terms refer to the activity of water or a mixture of water and a water-miscible cosolvent on the sulfopolyesters described herein. Examples of such water-miscible cosolvents includes alcohols, ketones, glycol ethers, esters and the like. It is intended for this terminology to include conditions where the sulfopolyester is dissolved to form a true solution as well as those where the sulfopolyester is dispersed within the aqueous medium. Often, due to the statistical nature of sulfopolyester compositions, it is possible to have a soluble fraction and a dispersed fraction when a single sulfopolyester sample is placed in an aqueous medium.


Similarly, the term “water-dispersible”, as used herein in reference to the sulfopolyester as one component of a multicomponent fiber or fibrous article, also is intended to be synonymous with the terms “water-dissipatable”, “water-disintegratable”, “water-dissolvable”, “water-dispellable”, “water soluble”, “water-removable”, “hydrosoluble”, and “hydrodispersible” and is intended to mean that the sulfopolyester component is sufficiently removed from the multicomponent fiber and is dispersed or dissolved by the action of water to enable the release and separation of the water non-dispersible fibers contained therein. The terms “dispersed”, “dispersible”, “dissipate”, or “dissipatable” mean that, using a sufficient amount of deionized water (e.g., 100:1 water:fiber by weight) to form a loose suspension or slurry of the fibers or fibrous article, at a temperature of about 60° C., and within a time period of up to 5 days, sulfopolyester component dissolves, disintegrates, or separates from the multicomponent fiber, leaving behind a plurality of microdenier fibers from the water non-dispersible segments.


The water-dispersible fiber of the present invention is prepared from polyesters or, more specifically sulfopolyesters, comprising dicarboxylic acid monomer residues, sulfomonomer residues, diol monomer residues, and repeating units. The sulfomonomer may be a dicarboxylic acid, a diol, or hydroxycarboxylic acid. Thus, the term “monomer residue”, as used herein, means a residue of a dicarboxylic acid, a diol, or a hydroxycarboxylic acid. A “repeating unit”, as used herein, means an organic structure having 2 monomer residues bonded through a carbonyloxy group. The sulfopolyesters of the present invention contain substantially equal molar proportions of acid residues (100 mole %) and diol residues (100 mole %) which react in substantially equal proportions such that the total moles of repeating units is equal to 100 mole %. The mole percentages provided in the present disclosure, therefore, may be based on the total moles of acid residues, the total moles of diol residues, or the total moles of repeating units. For example, a sulfopolyeseter containing 30 mole % of a sulfomonomer, which may be a dicarboxylic acid, a diol, or hydroxycarboxylic acid, based on the total repeating units, means that the sulfopolyester contains 30 mole % sulfomonomer out of a total of 100 mole % repeating units. Thus, there are 30 moles of sulfomonomer residues among every 100 moles of repeating units. Similarly, a sulfopolyeseter containing 30 mole % of a dicarboxylic acid sulfomonomer, based on the total acid residues, means the sulfopolyester contains 30 mole % sulfomonomer out of a total of 100 mole % acid residues. Thus, in this latter case, there are 30 moles of sulfomonomer residues among every 100 moles of acid residues.


The sulfopolyesters described herein have an inherent viscosity, abbreviated hereinafter as “Ih.V.”, of at least about 0.1 dL/g, preferably about 0.2 to 0.3 dL/g, and most preferably greater than about 0.3 dL/g, measured in a 60/40 parts by weight solution of phenol/tetrachloroethane solvent at 25° C. and at a concentration of about 0.5 g of sulfopolyester in 100 mL of solvent. The term “polyester”, as used herein, encompasses both “homopolyesters” and “copolyesters” and means a synthetic polymer prepared by the polycondensation of difunctional carboxylic acids with difunctional hydroxyl compound. As used herein, the term “sulfopolyester” means any polyester comprising a sulfomonomer. Typically the difunctional carboxylic acid is a dicarboxylic acid and the difunctional hydroxyl compound is a dihydric alcohol such as, for example glycols and diols. Alternatively, the difunctional carboxylic acid may be a hydroxy carboxylic acid such as, for example, p-hydroxybenzoic acid, and the difunctional hydroxyl compound may be a aromatic nucleus bearing 2 hydroxy substituents such as, for example, hydroquinone. The term “residue”, as used herein, means any organic structure incorporated into the polymer through a polycondensation reaction involving the corresponding monomer. Thus, the dicarboxylic acid residue may be derived from a dicarboxylic acid monomer or its associated acid halides, esters, salts, anhydrides, or mixtures thereof. As used herein, therefore, the term dicarboxylic acid is intended to include dicarboxylic acids and any derivative of a dicarboxylic acid, including its associated acid halides, esters, half-esters, salts, half-salts, anhydrides, mixed anhydrides, or mixtures thereof, useful in a polycondensation process with a diol to make a high molecular weight polyester.


The sulfopolyester of the present invention includes one or more dicarboxylic acid residues. Depending on the type and concentration of the sulfomonomer, the dicarboxylic acid residue may comprise from about 60 to about 100 mole % of the acid residues. Other examples of concentration ranges of dicarboxylic acid residues are from about 60 mole % to about 95 mole %, and about 70 mole % to about 95 mole %. Examples of dicarboxylic acids that may be used include aliphatic dicarboxylic acids, alicyclic dicarboxylic acids, aromatic dicarboxylic acids, or mixtures of two or more of these acids. Thus, suitable dicarboxylic acids include, but are not limited to succinic; glutaric; adipic; azelaic; sebacic; fumaric; maleic; itaconic; 1,3-cyclohexanedicarboxylic; 1,4-cyclohexanedicarboxylic; diglycolic; 2,5-norbornanedicarboxylic; phthalic; terephthalic; 1,4-naphthalenedicarboxylic; 2,5-naphthalenedicarboxylic; diphenic; 4,4′-oxydibenzoic; 4,4′-sulfonyldibenzoic; and isophthalic. The preferred dicarboxylic acid residues are isophthalic, terephthalic, and 1,4-cyclohexanedicarboxylic acids, or if diesters are used, dimethyl terephthalate, dimethyl isophthalate, and dimethyl-1,4-cyclohexanedicarboxylate with the residues of isophthalic and terephthalic acid being especially preferred. Although the dicarboxylic acid methyl ester is the most preferred embodiment, it is also acceptable to include higher order alkyl esters, such as ethyl, propyl, isopropyl, butyl, and so forth. In addition, aromatic esters, particularly phenyl, also may be employed.


The sulfopolyester includes about 4 to about 40 mole %, based on the total repeating units, of residues of at least one sulfomonomer having 2 functional groups and one or more sulfonate groups attached to an aromatic or cycloaliphatic ring wherein the functional groups are hydroxyl, carboxyl, or a combination thereof. Additional examples of concentration ranges for the sulfomonomer residues are about 4 to about 35 mole %, about 8 to about 30 mole %, and about 8 to about 25 mole %, based on the total repeating units. The sulfomonomer may be a dicarboxylic acid or ester thereof containing a sulfonate group, a diol containing a sulfonate group, or a hydroxy acid containing a sulfonate group. The term “sulfonate” refers to a salt of a sulfonic acid having the structure “—SO3M” wherein M is the cation of the sulfonate salt. The cation of the sulfonate salt may be a metal ion such as Li+, Na+, K+, Mg++, Ca++, Ni++, Fe++, and the like. Alternatively, the cation of the sulfonate salt may be non-metallic such as a nitrogenous base as described, for example, in U.S. Pat. No. 4,304,901. Nitrogen-based cations are derived from nitrogen-containing bases, which may be aliphatic, cycloaliphatic, or aromatic compounds. Examples of such nitrogen containing bases include ammonia, dimethylethanolamine, diethanolamine, triethanolamine, pyridine, morpholine, and piperidine. Because monomers containing the nitrogen-based sulfonate salts typically are not thermally stable at conditions required to make the polymers in the melt, the method of this invention for preparing sulfopolyesters containing nitrogen-based sulfonate salt groups is to disperse, dissipate, or dissolve the polymer containing the required amount of sulfonate group in the form of its alkali metal salt in water and then exchange the alkali metal cation for a nitrogen-based cation.


When a monovalent alkali metal ion is used as the cation of the sulfonate salt, the resulting sulfopolyester is completely dispersible in water with the rate of dispersion dependent on the content of sulfomonomer in the polymer, temperature of the water, surface area/thickness of the sulfopolyester, and so forth. When a divalent metal ion is used, the resulting sulfopolyesters are not readily dispersed by cold water but are more easily dispersed by hot water. Utilization of more than one counterion within a single polymer composition is possible and may offer a means to tailor or fine-tune the water-responsivity of the resulting article of manufacture. Examples sulfomonomers residues include monomer residues where the sulfonate salt group is attached to an aromatic acid nucleus, such as, for example, benzene; naphthalene; diphenyl; oxydiphenyl; sulfonyldiphenyl; and methylenediphenyl or cycloaliphatic rings, such as, for example, cyclohexyl; cyclopentyl; cyclobutyl; cycloheptyl; and cyclooctyl. Other examples of sulfomonomer residues which may be used in the present invention are the metal sulfonate salt of sulfophthalic acid, sulfoterephthalic acid, sulfoisophthalic acid, or combinations thereof. Other examples of sulfomonomers which may be used are 5-sodiosulfoisophthalic acid and esters thereof. If the sulfomonomer residue is from 5-sodiosulfoisophthalic acid, typical sulfomonomer concentration ranges are about 4 to about 35 mole %, about 8 to about 30 mole %, and about 8 to 25 mole %, based on the total moles of acid residues.


The sulfomonomers used in the preparation of the sulfopolyesters are known compounds and may be prepared using methods well known in the art. For example, sulfomonomers in which the sulfonate group is attached to an aromatic ring may be prepared by sulfonating the aromatic compound with oleum to obtain the corresponding sulfonic acid and followed by reaction with a metal oxide or base, for example, sodium acetate, to prepare the sulfonate salt. Procedures for preparation of various sulfomonomers are described, for example, in U.S. Pat. Nos. 3,779,993; 3,018,272; and 3,528,947.


It is also possible to prepare the polyester using, for example, a sodium sulfonate salt, and ion-exchange methods to replace the sodium with a different ion, such as zinc, when the polymer is in the dispersed form. This type of ion exchange procedure is generally superior to preparing the polymer with divalent salts insofar as the sodium salts are usually more soluble in the polymer reactant melt-phase.


The sulfopolyester includes one or more diol residues which may include aliphatic, cycloaliphatic, and aralkyl glycols. The cycloaliphatic diols, for example, 1,3- and 1,4-cyclohexanedimethanol, may be present as their pure cis or trans isomers or as a mixture of cis and trans isomers. As used herein, the term “diol” is synonymous with the term “glycol” and means any dihydric alcohol. Examples diols include ethylene glycol; diethylene glycol; triethylene glycol; polyethylene glycols; 1,3-propanediol; 2,4-dimethyl-2-ethylhexane-1,3-diol; 2,2-dimethyl-1,3-propanediol; 2-ethyl-2-butyl-1,3-propanediol; 2-ethyl-2-isobutyl-1,3-propanediol; 1,3-butanediol; 1,4-butanediol; 1,5-pentanediol; 1,6-hexanediol; 2,2,4-trimethyl-1,6-hexanediol; thiodiethanol; 1,2-cyclohexanedimethanol; 1,3-cyclohexanedimethanol; 1,4-cyclohexanedimethanol; 2,2,4,4-tetramethyl-1,3-cyclobutanediol; p-xylylenediol, or combinations of one or more of these glycols.


The diol residues may include from about 25 mole % to about 100 mole %, based on the total diol residues, of residue of a poly(ethylene glycol) having a structure

H—(OCH2—CH2)n—OH

wherein n is an integer in the range of 2 to about 500. Non-limiting examples of lower molecular weight polyethylene glycols, e.g., wherein n is from 2 to 6, are diethylene glycol, triethylene glycol, and tetraethylene glycol. Of these lower molecular weight glycols, diethylene and triethylene glycol are most preferred. Higher molecular weight polyethylene glycols (abbreviated herein as “PEG”), wherein n is from 7 to about 500, include the commercially available products known under the designation CARBOWAX®, a product of Dow Chemical Company (formerly Union Carbide). Typically, PEG's are used in combination with other diols such as, for example, diethylene glycol or ethylene glycol. Based on the values of n, which range from greater than 6 to 500, the molecular weight may range from greater than 300 to about 22,000 g/mol. The molecular weight and the mole % are inversely proportional to each other; specifically, as the molecular weight is increased, the mole % will be decreased in order to achieve a designated degree of hydrophilicity. For example, it is illustrative of this concept to consider that a PEG having a molecular weight of 1000 may constitute up to 10 mole % of the total diol, while a PEG having a molecular weight of 10,000 would typically be incorporated at a level of less than 1 mole % of the total diol.


Certain dimer, trimer, and tetramer diols may be formed in situ due to side reactions that may be controlled by varying the process conditions. For example, varying amounts of diethylene, triethylene, and tetraethylene glycols may be formed from ethylene glycol from an acid-catalyzed dehydration reaction which occurs readily when the polycondensation reaction is carried out under acidic conditions. The presence of buffer solutions, well-known to those skilled in the art, may be added to the reaction mixture to retard these side reactions. Additional compositional latitude is possible, however, if the buffer is omitted and the dimerization, trimerization, and tetramerization reactions are allowed to proceed.


The sulfopolyester of the present invention may include from 0 to about 25 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof. Non-limiting examples of branching monomers are 1,1,1-trimethylol propane, 1,1,1-trimethylolethane, glycerin, pentaerythritol, erythritol, threitol, dipentaerythritol, sorbitol, trimellitic anhydride, pyromellitic dianhydride, dimethylol propionic acid, or combinations thereof. Further examples of branching monomer concentration ranges are from 0 to about 20 mole % and from 0 to about 10 mole %. The presence of a branching monomer may result in a number of possible benefits to the sulfopolyester of the present invention, including but not limited to, the ability to tailor rheological, solubility, and tensile properties. For example, at a constant molecular weight, a branched sulfopolyester, compared to a linear analog, will also have a greater concentration of end groups that may facilitate post-polymerization crosslinking reactions. At high concentrations of branching agent, however, the sulfopolyester may be prone to gelation.


The sulfopolyester used for the fiber of the present invention has a glass transition temperature, abbreviated herein as “Tg”, of at least 25° C. as measured on the dry polymer using standard techniques, such as differentical scanning calorimetry (“DSC”), well known to persons skilled in the art. The Tg measurements of the sulfopolyesters of the present invention are conducted using a “dry polymer”, that is, a polymer sample in which adventitious or absorbed water is driven off by heating to polymer to a temperature of about 200° C. and allowing the sample to return to room temperature. Typically, the sulfopolyester is dried in the DSC apparatus by conducting a first thermal scan in which the sample is heated to a temperature above the water vaporization temperature, holding the sample at that temperature until the vaporization of the water absorbed in the polymer is complete (as indicated by an a large, broad endotherm), cooling the sample to room temperature, and then conducting a second thermal scan to obtain the Tg measurement. Further examples of glass transition temperatures exhibited by the sulfopolyester are at least 30° C., at least 35° C., at least 40° C., at least 50° C., at least 60° C., at least 65° C., at least 80° C., and at least 90° C. Although other Tg's are possible, typical glass transition temperatures of the dry sulfopolyesters our invention are about 30° C., about 48° C., about 55° C., about 65° C., about 70° C., about 75° C., about 85° C., and about 90° C.


Our novel fibers may consist essentially of or, consist of, the sulfopolyesters described hereinabove. In another embodiment, however, the sulfopolyesters of this invention may be a single polyester or may be blended with one or more supplemental polymers to modify the properties of the resulting fiber. The supplemental polymer may or may not be water-dispersible depending on the application and may be miscible or immiscible with the sulfopolyester. If the supplemental polymer is water-nondispersible, it is preferred that the blend with the sulfopolyester is immiscible. The term “miscible”, as used herein, is intended to mean that the blend has a single, homogeneous amorphous phase as indicated by a single composition-dependent Tg. For example, a first polymer that is miscible with second polymer may be used to “plasticize” the second polymer as illustrated, for example, in U.S. Pat. No. 6,211,309. By contrast, the term “immiscible”, as used herein, denotes a blend that shows at least 2, randomly mixed, phases and exhibits more than one Tg. Some polymers may be immiscible and yet compatible with the sulfopolyester. A further general description of miscible and immiscible polymer blends and the various analytical techniques for their characterization may be found in Polymer Blends Volumes 1 and 2, Edited by D. R. Paul and C. B. Bucknall, 2000, John Wiley & Sons, Inc.


Non-limiting examples of water-dispersible polymers that may be blended with the sulfopolyester are polymethacrylic acid, polyvinyl pyrrolidone, polyethylene-acrylic acid copolymers, polyvinyl methyl ether, polyvinyl alcohol, polyethylene oxide, hydroxy propyl cellulose, hydroxypropyl methyl cellulose, methyl cellulose, ethyl hydroxyethyl cellulose, isopropyl cellulose, methyl ether starch, polyacrylamides, poly(N-vinyl caprolactam), polyethyl oxazoline, poly(2-isopropyl-2-oxazoline), polyvinyl methyl oxazolidone, water-dispersible sulfopolyesters, polyvinyl methyl oxazolidimone, poly(2,4-dimethyl-6-triazinylethylene), and ethylene oxide-propylene oxide copolymers. Examples of polymers which are water-nondispersible that may be blended with the sulfopolyester include, but are not limited to, polyolefins, such as homo- and copolymers of polyethylene and polypropylene; poly(ethylene terephthalate); poly(butylene terephthalate); and polyamides, such as nylon-6; polylactides; caprolactone; Eastar Bio® (poly(tetramethylene adipate-co-terephthalate), a product of Eastman Chemical Company); polycarbonate; polyurethane; and polyvinyl chloride.


According to our invention, blends of more than one sulfopolyester may be used to tailor the end-use properties of the resulting fiber or fibrous article, for example, a nonwoven fabric or web. The blends of one or more sulfopolyesters will have Tg's of at least 25° C. for the water-dispersible, unicomponent fibers and at least 57° C. for the multicomponent fibers. Thus, blending may also be exploited to alter the processing characteristics of a sulfopolyester to facilitate the fabrication of a nonwoven. In another example, an immiscible blend of polypropylene and sulfopolyester may provide a conventional nonwoven web that will break apart and completely disperse in water as true solubility is not needed. In this latter example, the desired performance is related to maintaining the physical properties of the polypropylene while the sulfopolyester is only a spectator during the actual use of the product or, alternatively, the sulfopolyester is fugitive and is removed before the final form of the product is utilized.


The sulfopolyester and supplemental polymer may be blended in batch, semicontinuous, or continuous processes. Small scale batches may be readily prepared in any high-intensity mixing devices well-known to those skilled in the art, such as Banbury mixers, prior to melt-spinning fibers. The components may also be blended in solution in an appropriate solvent. The melt blending method includes blending the sulfopolyester and supplemental polymer at a temperature sufficient to melt the polymers. The blend may be cooled and pelletized for further use or the melt blend can be melt spun directly from this molten blend into fiber form. The term “melt” as used herein includes, but is not limited to, merely softening the polyester. For melt mixing methods generally known in the polymers art, see Mixing and Compounding of Polymers (I. Manas-Zloczower & Z. Tadmor editors, Carl Hanser Verlag Publisher, 1994, New York, N.Y.).


Our invention also provides a water-dispersible fiber comprising a sulfopolyester having a glass transistion temperature (Tg) of at least 25° C., wherein the sulfpolyester comprises: (i) about 50 to about 96 mole % of one or more residues of isophthalic acid or terephthalic acid, based on the total acid residues; (ii) about 4 to about 30 mole %, based on the total acid residues, of a residue of sodiosulfoisophthalic acid; (iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

H—(OCH2—CH2)n—OH

wherein n is an integer in the range of 2 to about 500; (iv) 0 to about 20 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof. As described hereinabove, the fiber may optionally include a first water-dispersible polymer blended with the sulfopolyester; and, optionally, a water-nondispersible polymer blended with the sulfopolyester such that the blend is an immiscible blend. Our fiber contains less than 10 weight percent of a pigment or filler, based on the total weight of the fiber. The first water-dispersible polymer is as described hereinabove. The sulfopolyester should have a glass transition temperature (Tg) of at least 25° C., but may have, for example, a Tg of about 35° C., about 48° C., about 55° C., about 65° C., about 70° C., about 75° C., about 85° C., and about 90° C. The sulfopolyester may contain other concentrations of isophthalic acid residues, for example, about 60 to about 95 mole %, and about 75 to about 95 mole %. Further examples of isophthalic acid residue concentrations ranges are about 70 to about 85 mole %, about 85 to about 95 mole % and about 90 to about 95 mole %. The sulfopolyester also may comprise about 25 to about 95 mole % of the residues of diethylene glycol. Further examples of diethylene glycol residue concentration ranges include about 50 to about 95 mole %, about 70 to about 95 mole %, and about 75 to about 95 mole %. The sulfopolyester also may include the residues of ethylene glycol and/or 1,4-cyclohexanedimethanol, abbreviated herein as “CHDM”. Typical concentration ranges of CHDM residues are about 10 to about 75 mole %, about 25 to about 65 mole %, and about 40 to about 60 mole %. Typical concentration ranges of ethylene glycol residues are are about 10 to about 75 mole %, about 25 to about 65 mole %, and about 40 to about 60 mole %. In another embodiment, the sulfopolyester comprises is about 75 to about 96 mole % of the residues of isophthalic acid and about 25 to about 95 mole % of the residues of diethylene glycol.


The sulfopolyesters of the instant invention are readily prepared from the appropriate dicarboxylic acids, esters, anhydrides, or salts, sulfomonomer, and the appropriate diol or diol mixtures using typical polycondensation reaction conditions. They may be made by continuous, semi-continuous, and batch modes of operation and may utilize a variety of reactor types. Examples of suitable reactor types include, but are not limited to, stirred tank, continuous stirred tank, slurry, tubular, wiped-film, falling film, or extrusion reactors. The term “continuous” as used herein means a process wherein reactants are introduced and products withdrawn simultaneously in an uninterrupted manner. By “continuous” it is meant that the process is substantially or completely continuous in operation and is to be contrasted with a “batch” process. “Continuous” is not meant in any way to prohibit normal interruptions in the continuity of the process due to, for example, start-up, reactor maintenance, or scheduled shut down periods. The term “batch” process as used herein means a process wherein all the reactants are added to the reactor and then processed according to a predetermined course of reaction during which no material is fed or removed into the reactor. The term “semicontinuous” means a process where some of the reactants are charged at the beginning of the process and the remaining reactants are fed continuously as the reaction progresses. Alternatively, a semicontinuous process may also include a process similar to a batch process in which all the reactants are added at the beginning of the process except that one or more of the products are removed continuously as the reaction progresses. The process is operated advantageously as a continuous process for economic reasons and to produce superior coloration of the polymer as the sulfopolyester may deteriorate in appearance if allowed to reside in a reactor at an elevated temperature for too long a duration.


The sulfopolyesters of the present invention are prepared by procedures known to persons skilled in the art. The sulfomonomer is most often added directly to the reaction mixture from which the polymer is made, although other processes are known and may also be employed, for example, as described in U.S. Pat. Nos. 3,018,272, 3,075,952, and 3,033,822. The reaction of the sulfomonomer, diol component and the dicarboxylic acid component may be carried out using conventional polyester polymerization conditions. For example, when preparing the sulfopolyesters by means of an ester interchange reaction, i.e., from the ester form of the dicarboxylic acid components, the reaction process may comprise two steps. In the first step, the diol component and the dicarboxylic acid component, such as, for example, dimethyl isophthalate, are reacted at elevated temperatures, typically, about 150° C. to about 250° C. for about 0.5 to about 8 hours at pressures ranging from about 0.0 kPa gauge to about 414 kPa gauge (60 pounds per square inch, “psig”). Preferably, the temperature for the ester interchange reaction ranges from about 180° C. to about 230° C. for about 1 to about 4 hours while the preferred pressure ranges from about 103 kPa gauge (15 psig) to about 276 kPa gauge (40 psig). Thereafter, the reaction product is heated under higher temperatures and under reduced pressure to form sulfopolyester with the elimination of diol, which is readily volatilized under these conditions and removed from the system. This second step, or polycondensation step, is continued under higher vacuum and a temperature which generally ranges from about 230° C. to about 350° C., preferably about 250° C. to about 310° C. and most preferably about 260° C. to about 290° C. for about 0.1 to about 6 hours, or preferably, for about 0.2 to about 2 hours, until a polymer having the desired degree of polymerization, as determined by inherent viscosity, is obtained. The polycondensation step may be conducted under reduced pressure which ranges from about 53 kPa (400 torr) to about 0.013 kPa (0.1 torr). Stirring or appropriate conditions are used in both stages to ensure adequate heat transfer and surface renewal of the reaction mixture. The reactions of both stages are facilitated by appropriate catalysts such as, for example, alkoxy titanium compounds, alkali metal hydroxides and alcoholates, salts of organic carboxylic acids, alkyl tin compounds, metal oxides, and the like. A three-stage manufacturing procedure, similar to that described in U.S. Pat. No. 5,290,631, may also be used, particularly when a mixed monomer feed of acids and esters is employed.


To ensure that the reaction of the diol component and dicarboxylic acid component by an ester interchange reaction mechanism is driven to completion, it is preferred to employ about 1.05 to about 2.5 moles of diol component to one mole dicarboxylic acid component. Persons of skill in the art will understand, however, that the ratio of diol component to dicarboxylic acid component is generally determined by the design of the reactor in which the reaction process occurs.


In the preparation of sulfopolyester by direct esterification, i.e., from the acid form of the dicarboxylic acid component, sulfopolyesters are produced by reacting the dicarboxylic acid or a mixture of dicarboxylic acids with the diol component or a mixture of diol components. The reaction is conducted at a pressure of from about 7 kPa gauge (1 psig) to about 1379 kPa gauge (200 psig), preferably less than 689 kPa (100 psig) to produce a low molecular weight, linear or branched sulfopolyester product having an average degree of polymerization of from about 1.4 to about 10. The temperatures employed during the direct esterification reaction typically range from about 180° C. to about 280° C., more preferably ranging from about 220° C. to about 270° C. This low molecular weight polymer may then be polymerized by a polycondensation reaction.


The water dispersible and multicomponent fibers and fibrous articles of this invention also may contain other conventional additives and ingredients which do not deleteriously affect their end use. For example, additives such as fillers, surface friction modifiers, light and heat stabilizers, extrusion aids, antistatic agents, colorants, dyes, pigments, fluorescent brighteners, antimicrobials, anticounterfeiting markers, hydrophobic and hydrophilic enhancers, viscosity modifiers, slip agents, tougheners, adhesion promoters, and the like may be used. The fibers and fibrous articles of our invention do not require the presence of additives such as, for example, pigments, fillers, oils, waxes, or fatty acid finishes, to prevent blocking or fusing of the fibers during processing. The terms “blocking or fusing”, as used herein, is understood to mean that the fibers or fibrous articles stick together or fuse into a mass such that the fiber cannot be processed or used for its intended purpose. Blocking and fusing can occur during processing of the fiber or fibrous article or during storage over a period of days or weeks and is exacerbated under hot, humid conditions. In one embodiment of the invention, the fibers and fibrous articles will contain less than 10 wt % of such anti-blocking additives, based on the total weight of the fiber or fibrous article. For example, the fibers and fibrous articles may contain less than 10 wt % of a pigment or filler. In other examples, the fibers and fibrous articles may contain less than 9 wt %, less than 5 wt %, less than 3 wt %, less than 1 wt %, and 0 wt % of a pigment or filler, based on the total weight of the fiber. Colorants, sometimes referred to as toners, may be added to impart a desired neutral hue and/or brightness to the sulfopolyester. When colored fibers are desired, pigments or colorants may be included in the sulfopolyester reaction mixture during the reaction of the diol monomer and the dicarboxylic acid monomer or they may be melt blended with the preformed sulfopolyester. A preferred method of including colorants is to use a colorant having thermally stable organic colored compounds having reactive groups such that the colorant is copolymerized and incorporated into the sulfopolyester to improve its hue. For example, colorants such as dyes possessing reactive hydroxyl and/or carboxyl groups, including, but not limited to, blue and red substituted anthraquinones, may be copolymerized into the polymer chain. When dyes are employed as colorants, they may be added to the copolyester reaction process after an ester interchange or direct esterification reaction.


For the purposes of this invention, the term “fiber” refers to a polymeric body of high aspect ratio capable of being formed into two or three dimensional articles such as woven or nonwoven fabrics. In the context of the present invention, the term “fiber” is synonymous with “fibers” and intented to mean one or more fibers. The fibers of our invention may be unicomponent fibers, bicomponent, or multicomponent fibers. The term “unicomponent fiber”, as used herein, is intended to mean a fiber prepared by melt spinning a single sulfopolyester, blends of one or more sulfopolyesters, or blends of one or more sulfopolyesters with one or more additional polymers and includes staple, monofilament, and multifilament fibers. “Unicomponent” is intended to be synonymous with the term “monocomponent” and includes “biconstituent” or “multiconstituent” fibers, and refers to fibers which have been formed from at least two polymers extruded from the same extruder as a blend. Unicomponent or biconstituent fibers do not have the various polymer components arranged in relatively constantly positioned distinct zones across the cross-sectional area of the fiber and the various polymers are usually not continuous along the entire length of the fiber, instead usually forming fibrils or protofibrils which start and end at random. Thus, the term “unicomponent” is not intended to exclude fibers formed from a polymer or blends of one or more polymers to which small amounts of additives may be added for coloration, anti-static properties, lubrication, hydrophilicity, etc. By contrast, the term “multicomponent fiber”, as used herein, intended to mean a fiber prepared by melting the two or more fiber forming polymers in separate extruders and by directing the resulting multiple polymer flows into one spinneret with a plurality of distribution flow paths but spun together to form one fiber. Multicomponent fibers are also sometimes referred to as conjugate or bicomponent fibers. The polymers are arranged in substantially constantly positioned distinct zones across the cross-section of the conjugate fibers and extend continuously along the length of the conjugate fibers. The configuration of such a multicomponent fiber may be, for example, a sheath/core arrangement wherein one polymer is surrounded by another or may be a side by side arrangement, a pie arrangement or an “islands-in-the-sea” arrangement. For example, a multicomponent fiber may be prepared by extruding the sulfopolyester and one or more water non-dispersible polymers separately through a spinneret having a shaped or engineered tranverse geometry such as, for example, an “islands-in-the-sea” or segmented pie configuration. Unicomponent fibers, typically, are staple, monofilament or multifilament fibers that have a shaped or round cross-section. Most fiber forms are heatset. The fiber may include the various antioxidants, pigments, and additives as described herein.


Monofilament fibers generally range in size from about 15 to about 8000 denier per filament (abbreviated herein as “d/f”). Our novel fibers typically will have d/f values in the range of about 40 to about 5000. Monofilaments may be in the form of unicomponent or multicomponent fibers. The multifilament fibers of our invention will preferably range in size from about 1.5 micrometers for melt blown webs, about 0.5 to about 50 d/f for staple fibers, and up to about 5000 d/f for monofilament fibers. Multifilament fibers may also be used as crimped or uncrimped yarns and tows. Fibers used in melt blown web and melt spun fabrics may be produced in microdenier sizes. The term “microdenier”, as used herein, is intended to mean a d/f value of 1 d/f or less. For example, the microdenier fibers of the instant invention typically have d/f values of 1 or less, 0.5 or less, or 0.1 or less. Nanofibers can also be produced by electrostatic spinning.


As noted hereinabove, the sulfopolyesters also are advantageous for the preparation of bicomponent and multicomponent fibers having a shaped cross section. We have discovered that sulfopolyesters or blends of sulfopolyesters having a glass transistion temperature (Tg) of at least 57° C. are particularly useful for multicomponent fibers to prevent blocking and fusing of the fiber during spinning and take up. Thus, our invention provides a multicomponent fiber having shaped cross section, comprising:

  • A) a water dispersible sulfopolyester having a glass transistion temperature (Tg) of at least 57° C., the sulfpolyester comprising:
    • (i) residues of one or more dicarboxylic acids;
    • (ii) about 4 to about 40 mole %, based on the total repeating units, of residues of at least one sulfomonomer having 2 functional groups and one or more sulfonate groups attached to an aromatic or cycloaliphatic ring wherein the functional groups are hydroxyl, carboxyl, or a combination thereof;
    • (iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

      H—(OCH2—CH2)n—OH
      • wherein n is an integer in the range of 2 to about 500; and
    • (iv) 0 to about 25 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof; and
  • B) a plurality of segments comprising one or more water-nondispersable polymers immiscible with the sulfopolyester, wherein the segments are substantially isolated from each other by the sulfopolyester intervening between the segments;


    wherein the fiber has an islands-in-the-sea or segmented pie cross section and contains less than 10 weight percent of a pigment or filler, based on the total weight of the fiber.


    The dicarboxylic acids, diols, sulfopolyester, sulfomonomers, and branching monomers residues are as described previously for other embodiments of the invention. For multicomponent fibers, it is advantageous that the sulfopolyester have a Tg of at least 57° C. Further examples of glass transition temperatures that may be exhibited by the sulfopolyester or sulfopolyester blend of our multicomponent fiber are at least 60° C., at least 65° C., at least 70° C., at least 75° C., at least 80° C., at least 85° C., and at least 90° C. Further, to obtain a sulfopolyester with a Tg of at least 57° C., blends of one or more sulfopolyesters may be used in varying proportions to obtain a sulfopolyester blend having the desired Tg. The Tg of a sulfopolyester blend may be calculated by using a weighted average of the Tg's of the sulfopolyester components. For example, sulfopolyester having a Tg of 48° C. may be blended in a 25:75 wt:wt ratio with another sulfopolyester having Tg of 65° C. to give a sulfopolyester blend having a Tg of approximately 61° C.


The multicomponent fiber comprises a plurality of segments one or more water-nondispersable polymers immiscible with the sulfopolyester in which the segments are substantially isolated from each other by the sulfopolyester intervening between the segments. The term “substantially isolated”, as used herein, is intended to mean that the segments are set apart from each other to permit the segments to form individual fibers upon removal of the sulfopolyester. For example, the segments may be touching each others as in, for example, a segmented pie configuration but can be split apart by impact or when the sulfopolyester is removed.


The ratio by weight of the sulfopolyester to water non-dispersible polymer component in the multicomponent fiber of the invention is generally in the range of about 60:40 to about 2:98 or, in another example, in the range of about 50:50 to about 5:95. Typically, the sulfopolyester comprises 50% by weight or less of the total weight of the mulicomponent fiber.


The segments of multicomponent fiber may comprise one of more water non-dispersible polymers. Examples of water-nondispersible polymers which may be used in segments of the multicomponent fiber include, but are not limited to, polyolefins, polyesters, polyamides, polylactides, polycaprolactone, polycarbonate, polyurethane, and polyvinyl chloride. For example, the water non-dispersible polymer may be polyester such as poly(ethylene) terephthalate, poly(butylene) terephthalate, poly(cyclohexylene) cyclohexanedicarboxylate, poly(cyclohexylene) terephthalate, poly(trimethylene) terephthalate, and the like. In another example, the water-nondispersible polymer biodistintegratable as determined by DIN Standard 54900 and/or biodegradable as determined by ASTM Standard Method, D6340-98. Examples of biodegradable polyesters and polyester blends are disclosed in U.S. Pat. Nos. 5,599,858; 5,580,911; 5,446,079; and 5,559,171. The term “biodegradable”, as used herein in reference to the water non-dispersible polymers of the present invention, is understood to mean that the polymers are degraded under environmental influences such as, for example, in a composting environment, in an appropriate and demonstrable time span as defined, for example, by ASTM Standard Method, D6340-98, entitled “Standard Test Methods for Determining Aerobic Biodegradation of Radiolabeled Plastic Materials in an Aqueous or Compost Environment”. The water non-dispersible polymers of the present invention also may be “biodisintegratable”, meaning that the polymers are easily fragmented in a composting environment as defined, for example, by DIN Standard 54900. For example, the biodegradable polymer is initially reduced in molecular weight in the environment by the action of heat, water, air, microbes and other factors. This reduction in molecular weight results in a loss of physical properties (tenacity) and often in fiber breakage. Once the molecular weight of the polymer is sufficiently low, the monomers and oligomers are then assimilated by the microbes. In an aerobic environment, these monomers or oligomers are ultimately oxidized to CO2, H2O, and new cell biomass. In an anaerobic environment, the monomers or oligomers are ultimately converted to CO2, H2, acetate, methane, and cell biomass.


For example, water-nondispersible polymer may be an aliphatic-aromatic polyester, abbreviated herein as “AAPE”. The term “aliphatic-aromatic polyester”, as used herein, means a polyester comprising a mixture of residues from aliphatic or cycloaliphatic dicarboxylic acids or diols and aromatic dicarboxylic acids or diols. The term “non-aromatic”, as used herein with respect to the dicarboxylic acid and diol monomers of the present invention, means that carboxyl or hydroxyl groups of the monomer are not connected through an aromatic nucleus. For example, adipic acid contains no aromatic nucleus in its backbone, i.e., the chain of carbon atoms connecting the carboxylic acid groups, thus is “non-aromatic”. By contrast, the term “aromatic” means the dicarboxylic acid or diol contains an aromatic nucleus in the backbone such as, for example, terephthalic acid or 2,6-naphthalene dicarboxylic acid. “Non-aromatic”, therefore, is intended to include both aliphatic and cycloaliphatic structures such as, for example, diols and dicarboxylic acids, which contain as a backbone a straight or branched chain or cyclic arrangement of the constituent carbon atoms which may be saturated or paraffinic in nature, unsaturated, i.e., containing non-aromatic carbon-carbon double bonds, or acetylenic, i.e., containing carbon-carbon triple bonds. Thus, in the context of the description and the claims of the present invention, non-aromatic is intended to include linear and branched, chain structures (referred to herein as “aliphatic”) and cyclic structures (referred to herein as “alicyclic” or “cycloaliphatic”). The term “non-aromatic”, however, is not intended to exclude any aromatic substituents which may be attached to the backbone of an aliphatic or cycloaliphatic diol or dicarboxylic acid. In the present invention, the difunctional carboxylic acid typically is a aliphatic dicarboxylic acid such as, for example, adipic acid, or an aromatic dicarboxylic acid such as, for example, terephthalic acid. The difunctional hydroxyl compound may be cycloaliphatic diol such as, for example, 1,4-cyclohexanedimethanol, a linear or branched aliphatic diol such as, for example, 1,4-butanediol, or an aromatic diol such as, for example, hydroquinone.


The AAPE may be a linear or branched random copolyester and/or chain extended copolyester comprising diol residues which comprise the residues of one or more substituted or unsubstituted, linear or branched, diols selected from aliphatic diols containing 2 to about 8 carbon atoms, polyalkylene ether glycols containing 2 to 8 carbon atoms, and cycloaliphatic diols containing about 4 to about 12 carbon atoms. The substituted diols, typically, will comprise 1 to about 4 substituents independently selected from halo, C6-C10 aryl, and C1-C4 alkoxy. Examples of diols which may be used include, but are not limited to, ethylene glycol, diethylene glycol, propylene glycol, 1,3-propanediol, 2,2-dimethyl-1,3-propanediol, 1,3-butanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, polyethylene glycol, diethylene glycol, 2,2,4-trimethyl-1,6-hexanediol, thiodiethanol, 1,3-cyclohexanedimethanol, 1,4-cyclohexanedimethanol, 2,2,4,4-tetramethyl-1,3-cyclobutanediol, triethylene glycol, and tetraethylene glycol with the preferred diols comprising one or more diols selected from 1,4-butanediol; 1,3-propanediol; ethylene glycol; 1,6-hexanediol; diethylene glycol; or 1,4-cyclohexanedimethanol. The AAPE also comprises diacid residues which contain about 35 to about 99 mole %, based on the total moles of diacid residues, of the residues of one or more substituted or unsubstituted, linear or branched, non-aromatic dicarboxylic acids selected from aliphatic dicarboxylic acids containing 2 to about 12 carbon atoms and cycloaliphatic acids containing about 5 to about 10 carbon atoms. The substituted non-aromatic dicarboxylic acids will typically contain 1 to about 4 substituents selected from halo, C6-C10 aryl, and C1-C4 alkoxy. Non-limiting examples of non-aromatic diacids include malonic, succinic, glutaric, adipic, pimelic, azelaic, sebacic, fumaric, 2,2-dimethyl glutaric, suberic, 1,3-cyclopentanedicarboxylic, 1,4-cyclohexanedicarboxylic, 1,3-cyclohexanedicarboxylic, diglycolic, itaconic, maleic, and 2,5-norbornanedicarboxylic. In addition to the non-aromatic dicarboxylic acids, the AAPE comprises about 1 to about 65 mole %, based on the total moles of diacid residues, of the residues of one or more substituted or unsubstituted aromatic dicarboxylic acids containing 6 to about 10 carbon atoms. In the case where substituted aromatic dicarboxylic acids are used, they will typically contain 1 to about 4 substituents selected from halo, C6-C10 aryl, and C1-C4 alkoxy. Non-limiting axamples of aromatic dicarboxylic acids which may be used in the AAPE of our invention are terephthalic acid, isophthalic acid, salts of 5-sulfoisophthalic acid, and 2,6-naphthalenedicarboxylic acid. More preferably, the non-aromatic dicarboxylic acid will comprise adipic acid, the aromatic dicarboxylic acid will comprise terephthalic acid, and the diol will comprise 1,4-butanediol.


Other possible compositions for the AAPE's of our invention are those prepared from the following diols and dicarboxylic acids (or polyester-forming equivalents thereof such as diesters) in the following mole percentages, based on 100 mole percent of a diacid component and 100 mole percent of a diol component:

  • (1) glutaric acid (about 30 to about 75%); terephthalic acid (about 25 to about 70%); 1,4-butanediol (about 90 to 100%); and modifying diol (0 about 10%);
  • (2) succinic acid (about 30 to about 95%); terephthalic acid (about 5 to about 70%); 1,4-butanediol (about 90 to 100%); and modifying diol (0 to about 10%); and
  • (3) adipic acid (about 30 to about 75%); terephthalic acid (about 25 to about 70%); 1,4-butanediol (about 90 to 100%); and modifying diol (0 to about 10%).


The modifying diol preferably is selected from 1,4-cyclohexanedimethanol, triethylene glycol, polyethylene glycol and neopentyl glycol. The most preferred AAPE's are linear, branched or chain extended copolyesters comprising about 50 to about 60 mole percent adipic acid residues, about 40 to about 50 mole percent terephthalic acid residues, and at least 95 mole percent 1,4-butanediol residues. Even more preferably, the adipic acid residues comprise about 55 to about 60 mole percent, the terephthalic acid residues comprise about 40 to about 45 mole percent, and the diol residues comprise about 95 mole percent 1,4-butanediol residues. Such compositions are commercially available under the trademark EASTAR B10® copolyester from Eastman Chemical Company, Kingsport, Tenn., and under the trademark ECOFLEX® from BASF Corporation.


Additional, specific examples of preferred AAPE's include a poly(tetramethylene glutarate-co-terephthalate) containing (a) 50 mole percent glutaric acid residues, 50 mole percent terephthalic acid residues, and 100 mole percent 1,4-butanediol residues, (b) 60 mole percent glutaric acid residues, 40 mole percent terephthalic acid residues, and 100 mole percent 1,4-butanediol residues or (c) 40 mole percent glutaric acid residues, 60 mole percent terephthalic acid residues, and 100 mole percent 1,4-butanediol residues; a poly(tetramethylene succinate-co-terephthalate) containing (a) 85 mole percent succinic acid residues, 15 mole percent terephthalic acid residues, and 100 mole percent 1,4-butanediol residues or (b) 70 mole percent succinic acid residues, 30 mole percent terephthalic acid residues, and 100 mole percent 1,4-butanediol residues; a poly(ethylene succinate-co-terephthalate) containing 70 mole percent succinic acid residues, 30 mole percent terephthalic acid residues, and 100 mole percent ethylene glycol residues; and a poly(tetramethylene adipate-co-terephthalate) containing (a) 85 mole percent adipic acid residues, 15 mole percent terephthalic acid residues, and 100 mole percent 1,4-butanediol residues; or (b) 55 mole percent adipic acid residues, 45 mole percent terephthalic acid residues, and 100 mole percent 1,4-butanediol residues.


The AAPE preferably comprises from about 10 to about 1,000 repeating units and preferably, from about 15 to about 600 repeating units. The AAPE may have an inherent viscosity of about 0.4 to about 2.0 dL/g, or more preferably about 0.7 to about 1.6 dL/g, as measured at a temperature of 25° C. using a concentration of 0.5 gram copolyester in 100 ml of a 60/40 by weight solution of phenol/tetrachloroethane.


The AAPE, optionally, may contain the residues of a branching agent. The mole percentage ranges for the branching agent are from about 0 to about 2 mole %, preferably about 0.1 to about 1 mole %, and most preferably about 0.1 to about 0.5 mole % based on the total moles of diacid or diol residues (depending on whether the branching agent contains carboxyl or hydroxyl groups). The branching agent preferably has a weight average molecular weight of about 50 to about 5000, more preferably about 92 to about 3000, and a functionality of about 3 to about 6. The branching agent, for example, may be the esterified residue of a polyol having 3 to 6 hydroxyl groups, a polycarboxylic acid having 3 or 4 carboxyl groups (or ester-forming equivalent groups) or a hydroxy acid having a total of 3 to 6 hydroxyl and carboxyl groups. In addition, the AAPE may be branched by the addition of a peroxide during reactive extrusion.


Each segment of the water non-dispersible polymer may be different from others in fineness and may be arranged in any shaped or engineered cross-sectional geometry known to persons skilled in the art. For example, the sulfopolyester and a water-nondispersible polymer may be used to prepare a bicomponent fiber having an engineered geometry such as, for example, a side-by-side, “islands-in-the-sea”, segmented pie, other splitables, sheath/core, or other configurations known to persons skilled in the art. Other multicomponent configurations are also possible. Subsequent removal of a side, the “sea”, or a portion of the “pie” can result in very fine fibers. The process of preparing bicomponent fibers also is well known to persons skilled in the art. In a bicomponent fiber, the sulfopolyester fibers of this invention may be present in amounts of about 10 to about 90 weight % and will generally be used in the sheath portion of sheath/core fibers. The other component may be from a wide range of other polymeric materials such as, for example, poly(ethylene) terephthalate, poly(butylene) terephthalate, poly(trimethylene) terephthalate, polylactides and the like as well as polyolefins, cellulose esters, and polyamides. Typically, when a water-insoluble or water-nondispersible polymer is used, the resulting bicomponent or multicomponent fiber is not completely water-dispersible. Side by side combinations with significant differences in thermal shrinkage can be utilized for the development of a spiral crimp. If crimping is desired, a saw tooth or stuffer box crimp is generally suitable for many applications. If the second polymer component is in the core of a sheath/core configuration, such a core optionally may be stabilized.


The sulfopolyesters are particularly useful for fibers having an “islands-in-the-sea” or “segmented pie” cross section as they only requires neutral or slightly acidic (i.e., “soft” water) to disperse, as compared to the caustic-containing solutions that are sometimes required to remove other water dispersible polymers from multicomponent fibers. Thus another aspect of our invention is a multicomponent fiber, comprising:

    • A) a water dispersible sulfopolyester having a glass transistion temperature (Tg) of at least 57° C., the sulfopolyester comprising:
      • (i) about 50 to about 96 mole % of one or more residues of isophthalic acid or terephthalic acid, based on the total acid residues;
      • (ii) about 4 to about 30 mole %, based on the total acid residues, of a residue of sodiosulfoisophthalic acid;
      • (iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

        H—(OCH2—CH2)n—OH
        • wherein n is an integer in the range of 2 to about 500;
      • (iv) 0 to about 20 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof; and
    • (B) a plurality of segments comprising one or more water-nondispersible polymers immiscible with the sulfopolyester, wherein the segments are substantially isolated from each other by the sulfopolyester intervening between the segments;
    • wherein the fiber has an islands-in-the-sea or segmented pie cross section and contains less than 10 weight percent of a pigment or filler, based on the total weight of the fiber.


      The dicarboxylic acids, diols, sulfopolyester, sulfomonomers, branching monomers residues, and water non-dispersible polymers are as described previously. For multicomponent fibers, it is advantageous that sulfopolyester have a Tg of at least 57° C. The sulfopolyester may be a single sulfopolyester or a blend of one or more sulfopolyester polymers. Further examples of glass transition temperatures that may be exhibited by the sulfopolyester or sulfopolyester blends are at least 65° C., at least 70° C., at least 75° C., at least 85° C., and at least 90° C. For example, the sulfopolyester may comprise about 75 to about 96 mole % of one or more residues of isophthalic acid or terephthalic acid and about 25 to about 95 mole % of a residue of diethylene glycol. As described hereinabove, examples of the water-nondispersible polymers are polyolefins, polyesters, polyamides, polylactides, polycaprolactone, polycarbonate, polyurethane, and polyvinyl chloride. In addition, the water-nondispersible polymer may be biodegradable or biodisintegratable. For example, the water-nondispersible polymer may be an aliphatic-aromatic polyester as described previously.


Our novel multicomponent fiber may be prepared by any number of methods known to persons skilled in the art. The present invention thus provides a process for a multicomponent fiber having a shaped cross section comprising: spinning a water dispersible sulfopolyester having a glass transistion temperature (Tg) of at least 57° C. and one or more water-nondispersable polymers immiscible with the sulfopolyester into a fiber, the sulfopolyester comprising:

  • (i) residues of one or more dicarboxylic acids;
  • (ii) about 4 to about 40 mole %, based on the total repeating units, of residues of at least one sulfomonomer having 2 functional groups and one or more sulfonate groups attached to an aromatic or cycloaliphatic ring wherein the functional groups are hydroxyl, carboxyl, or a combination thereof;
  • (iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

    H—(OCH2—CH2)n—OH
    • wherein n is an integer in the range of 2 to about 500; and
  • (iv) 0 to about 25 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof;


    wherein the fiber has a plurality of segments comprising the water-nondispersable polymers and the segments are substantially isolated from each other by the sulfopolyester intervening between the segments and the fiber contains less than 10 weight percent of a pigment or filler, based on the total weight of the fiber. For example, the multicomponent fiber may be prepared by melting the sulfopolyester and one or more water non-dispersible polymers in separate extruders and directing the individual polymer flows into one spinneret or extrusion die with a plurality of distribution flow paths such that the water non-dispersible polymer component form small segments or thin strands which are substantially isolated from each other by the intervening sulfopolyester. The cross section of such a fiber may be, for example, a segmented pie arrangement or an islands-in-the-sea arrangement. In another example, the sulfopolyester and one or more water non-dispersible polymers are separately fed to the spinneret orifices and then extruded in sheath-core form in which the water non-dispersible polymer forms a “core” that is substantially enclosed by the sulfopolyester “sheath” polymer. In the case of such concentric fibers, the orifice supplying the “core” polymer is in the center of the spinning orifice outlet and flow conditions of core polymer fluid are strictly controlled to maintain the concentricity of both components when spinning. Modifications in spinneret orifices enable different shapes of core and/or sheath to be obtained within the fiber cross-section. In yet another example, a multicomponent fiber having a side-by-side cross section or configuration may be produced by coextruding the water dispersible sulfopolyester and water non-dispersible polymer through orifices separately and converging the separate polymer streams at substantially the same speed to merge side-by-side as a combined stream below the face of the spinneret; or (2) by feeding the two polymer streams separately through orifices, which converge at the surface of the spinneret, at substantially the same speed to merge side-by-side as a combined stream at the surface of the spinneret. In both cases, the velocity of each polymer stream, at the point of merge, is determined by its metering pump speed, the number of orifices, and the size of the orifice.


The dicarboxylic acids, diols, sulfopolyester, sulfomonomers, branching monomers residues, and water non-dispersible polymers are as described previously. The sulfopolyester has a glass transistion temperature of at least 60° C. Further examples of glass transition temperatures that may be exhibited by the sulfopolyester or sulfopolyester blend are at least 65° C., at least 70° C., at least 75° C., at least 85° C., and at least 90° C. In one example, the sulfopolyester may comprise about 50 to about 96 mole % of one or more residues of isophthalic acid or terephthalic acid, based on the total acid residues; and about 4 to about 30 mole %, based on the total acid residues, of a residue of sodiosulfoisophthalic acid; and 0 to about 20 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof. In another example, the sulfopolyester may comprise about 75 to about 96 mole % of one or more residues of isophthalic acid or terephthalic acid and about 25 to about 95 mole % of a residue of diethylene glycol. As described hereinabove, examples of the water-nondispersible polymers are polyolefins, polyesters, polyamides, polylactides, polycaprolactone, polycarbonate, polyurethane, and polyvinyl chloride. In addition, the water-nondispersible polymer may be biodegradable or biodisintegratable. For example, the water-nondispersible polymer may be an aliphatic-aromatic polyester as described previously. Examples of shaped cross sections include, but are not limited to, islands-in-the-sea, side-by-side, sheath-core, or segmented pie configurations.


Typically, upon exiting the spinneret, the fibers are quenched with a cross flow of air whereupon the fibers solidify. Various finishes and sizes may be applied to the fiber at this stage. The cooled fibers, typically, are subsequently drawn and wound up on a take up spool. Other additives may be incorporated in the finish in effective amounts like emulsifiers, antistatics, antimicrobials, antifoams, lubricants, thermostabilizers, UV stabilizers, and the like.


Optionally, the drawn fibers may be textured and wound-up to form a bulky continuous filament. This one-step technique is known in the art as spin-draw-texturing. Other embodiments include flat filament (non-textured) yarns, or cut staple fiber, either crimped or uncrimped.


The sulfopolyester may be later removed by dissolving the interfacial layers or pie segments and leaving the smaller filaments or microdenier fibers of the water non-dispersible polymer(s). Our invention thus provides a process for microdenier fibers comprising:

  • A. spinning a water dispersible sulfopolyester having a glass transistion temperature (Tg) of at least 57° C. and one or more water-nondispersable polymers immiscible with the sulfopolyester into multicomponent fibers, the sulfopolyester comprising:
    • (i) about 50 to about 96 mole % of one or more residues of isophthalic acid or terephthalic acid, based on the total acid residues;
    • (ii) about 4 to about 30 mole %, based on the total acid residues, of a residue of sod iosulfoisophthalic acid;
    • (iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

      H—(OCH2—CH2)n—OH
      • wherein n is an integer in the range of 2 to about 500; and
    • (iv) 0 to about 20 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof;
    • wherein the fibers have a plurality of segments comprising the water-nondispersable polymers wherein the segments are substantially isolated from each other by the sulfopolyester intervening between the segments and the fibers contain less than 10 weight percent of a pigment or filler, based on the total weight of the fibers; and
  • B. contacting the multicomponent fibers with water to remove the sulfopolyester thereby forming microdenier fibers.


    Typically, the multicomponent fiber is contacted with water at a temperature of about 25° C. to about 100° C., preferably about 50° C. to about 80° C. for a time period of from about 10 to about 600 seconds whereby the sulfopolyester is dissipated or dissolved. After removal of the sulfopolyester, the remaining microfibers typically will have an average fineness of 1 d/f or less, typically, 0.5 d/f or less, or more typically, 0.1 d/f or less. Typical applications of these remaining microfibers include artificial leathers, suedes, wipes, and filter media. The ionic nature of sulfopolyesters also results in advantageously poor “solubility” in saline media, such as body fluids. Such properties are desirable in personal care products and cleaning wipes that are flushable or otherwise disposed in sanitary sewage systems. Selected sulfopolyesters have also been utilized as dispersing agents in dye baths and soil redeposition preventative agents during laundry cycles.


The instant invention also includes a fibrous article comprising the water-dispersible fiber, the multicomponent fiber, or the microdenier fibers described hereinabove. The term “fibrous article” is understood to mean any article having or resembling fibers. Non-limiting examples of fibrous articles include multifilament fibers, yarns, cords, tapes, fabrics, melt blown webs, spunbonded webs, thermobonded webs, hydroentangled webs, nonwoven webs and fabrics, and combinations thereof; items having one or more layers of fibers, such as, for example, multilayer nonwovens, laminates, and composites from such fibers, gauzes, bandages, diapers, training pants, tampons, surgical gowns and masks, feminine napkins; and the like. Further, the fibrous articles may include replacement inserts for various personal hygiene and cleaning products. The fibrous article of the present invention may be bonded, laminated, attached to, or used in conjunction with other materials which may or may not be water-dispersible. The fibrous article, for example, a nonwoven fabric layer, may be bonded to a flexible plastic film or backing of a water-nondispersible material, such as polyethylene. Such an assembly, for example, could be used as one component of a disposable diaper. In addition, the fibrous article may result from overblowing fibers onto another substrate to form highly assorted combinations of engineered melt blown, spunbond, film, or membrane structures.


The fibrous articles of the instant invention include nonwoven fabrics and webs. A nonwoven fabric is defined as a fabric made directly from fibrous webs without weaving or knitting operations. For example, the multicomponent fiber of the present invention may be formed into a fabric by any known fabric forming process like knitting, weaving, needle punching, and hydroentangling. The resulting fabric or web may be converted into a microdenier fiber web by exerting sufficient force to cause the multicomponent fibers to split or by contacting the web with water to remove the sulfopolyester leaving the remaining microdenier fibers behind. Our invention thus provides a process for a microdenier fiber web, comprising:

  • A. spinning a water dispersible sulfopolyester having a glass transistion temperature (Tg) of at least 57° C. and one or more water-nondispersable polymers immiscible with the sulfopolyester into multicomponent fibers, the sulfpolyester comprising:
    • (i) about 50 to about 96 mole % of one or more residues of isophthalic acid or terephthalic acid, based on the total acid residues;
    • (ii) about 4 to about 30 mole %, based on the total acid residues, of a residue of sod iosulfoisophthalic acid;
    • (iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

      H—(OCH2—CH2)n—OH
      • wherein n is an integer in the range of 2 to about 500; and
    • (iv) 0 to about 20 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof.
    • wherein the multicomponent fibers have a plurality of segments comprising the water-nondispersable polymers wherein the segments are substantially isolated from each other by the sulfopolyester intervening between the segments; and the fiber contains less than 10 weight percent of a pigment or filler, based on the total weight of the fiber;
  • B. overlapping and collecting the multicomponent fibers of Step A to form a nonwoven web; and
  • C. contacting the nonwoven web with water to remove the sulfopolyester thereby forming a microdenier fiber web.


The nonwoven assembly is held together by 1) mechanical fiber cohesion and interlocking in a web or mat; 2) various techniques of fusing of fibers, including the use of binder fibers, utilizing the thermoplastic properties of certain polymers and polymer blends; 3) use of a binding resin such as starch, casein, a cellulose derivative, or a synthetic resin, such as an acrylic latex or urethane; 4) powder adhesive binders; or 5) combinations thereof. The fibers are often deposited in a random manner, although orientation in one direction is possible, followed by bonding using one of the methods described above.


The fibrous articles of our invention further also may comprise one or more layers of water-dispersible fibers, multicomponent fibers, or microdenier fibers. The fiber layers may be one or more nonwoven fabric layers, a layer of loosely bound overlapping fibers, or a combination thereof. In addition, the fibrous articles may include personal and health care products such as, but not limited to, child care products, such as infant diapers; child training pants; adult care products, such as adult diapers and adult incontinence pads; feminine care products, such as feminine napkins, panty liners, and tampons; wipes; fiber-containing cleaning products; medical and surgical care products, such as medical wipes, tissues, gauzes, examination bed coverings, surgical masks, gowns, bandages, and wound dressings; fabrics; elastomeric yarns, wipes, tapes, other protective barriers, and packaging material. The fibrous articles may be used to absorb liquids or may be pre-moistened with various liquid compositions and used to deliver these compositions to a surface. Non-limiting examples of liquid compositions include detergents; wetting agents; cleaning agents; skin care products, such as cosmetics, ointments, medications, emollients, and fragrances. The fibrous articles also may include various powders and particulates to improve absorbency or as delivery vehicles. Examples of powders and particulates include, but are not limited to, talc, starches, various water absorbent, water-dispersible, or water swellable polymers, such as super absorbent polymers, sulfopolyesters, and poly(vinylalcohols), silica, pigments, and microcapsules. Additives may also be present, but are not required, as needed for specific applications. Examples of additives include, but are not limited to, oxidative stabilizers, UV absorbers, colorants, pigments, opacifiers (delustrants), optical brighteners, fillers, nucleating agents, plasticizers, viscosity modifiers, surface modifiers, antimicrobials, disinfectants, cold flow inhibitors, branching agents, and catalysts.


In addition to being water-dispersible, the fibrous articles described above may be flushable. The term “flushable” as used herein means capable of being flushed in a conventional toilet, and being introduced into a municipal sewage or residential septic system, without causing an obstruction or blockage in the toilet or sewage system.


The fibrous article may further comprise a water-dispersible film comprising a second water-dispersible polymer. The second water-dispersible polymer may be the same as or different from the previously described water-dispersible polymers used in the fibers and fibrous articles of the present invention. In one embodiment, for example, the second water-dispersible polymer may be an additional sulfopolyester which, in turn, comprises: (i) about 50 to about 96 mole % of one or more residues of isophthalic acid or terephthalic acid, based on the total acid residues; (ii) about 4 to about 30 mole %, based on the total acid residues, of a residue of sodiosulfoisophthalic acid; (iii) one or more diol residues wherein at least 15 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

H—(OCH2—CH2)n—OH

wherein n is an integer in the range of 2 to about 500; (iv) 0 to about 20 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof. The additional sulfopolyester may be blended with one or more supplemental polymers, as described hereinabove, to modify the properties of the resulting fibrous article. The supplemental polymer may or may not be water-dispersible depending on the application. The supplemental polymer may be miscible or immiscible with the additional sulfopolyester.


The additional sulfopolyester may contain other concentrations of isophthalic acid residues, for example, about 60 to about 95 mole %, and about 75 to about 95 mole %. Further examples of isophthalic acid residue concentrations ranges are about 70 to about 85 mole %, about 85 to about 95 mole % and about 90 to about 95 mole %. The additional sulfopolyester also may comprise about 25 to about 95 mole % of the residues of diethylene glycol. Further examples of diethylene glycol residue concentration ranges include about 50 to about 95 mole %, about 70 to about 95 mole %, and about 75 to about 95 mole %. The additional sulfopolyester also may include the residues of ethylene glycol and/or 1,4-cyclohexanedimethanol. Typical concentration ranges of CHDM residues are about 10 to about 75 mole %, about 25 to about 65 mole %, and about 40 to about 60 mole %. Typical concentration ranges of ethylene glycol residues are about 10 to about 75 mole %, about 25 to about 65 mole %, and about 40 to about 60 mole %. In another embodiment, the additional sulfopolyester comprises is about 75 to about 96 mole % of the residues of isophthalic acid and about 25 to about 95 mole % of the residues of diethylene glycol.


According to the invention, the sulfopolyester film component of the fibrous article may be produced as a monolayer or multilayer film. The monolayer film may be produced by conventional casting techniques. The multilayered films may be produced by conventional lamination methods or the like. The film may be of any convenient thickness, but total thickness will normally be between about 2 and about 50 mil.


The film-containing fibrous articles may include one or more layers of water-dispersible fibers as described above. The fiber layers may be one or more nonwoven fabric layers, a layer of loosely bound overlapping fibers, or a combination thereof. In addition, the film-containing fibrous articles may include personal and health care products as described hereinabove.


As described previously, the fibrous articles also may include various powders and particulates to improve absorbency or as delivery vehicles. Thus, in one embodiment, our fibrous article comprises a powder comprising a third water-dispersible polymer that may be the same as or different from the water-dispersible polymer components described previously herein. Other examples of powders and particulates include, but are not limited to, talc, starches, various water absorbent, water-dispersible, or water swellable polymers, such as poly(acrylonitiles), sulfopolyesters, and poly(vinyl alcohols), silica, pigments, and microcapsules.


Our novel fiber and fibrous articles have many possible uses in addition to the applications described above. One novel application involves the melt blowing a film or nonwoven fabric onto flat, curved, or shaped surfaces to provide a protective layer. One such layer might provide surface protection to durable equipment during shipping. At the destination, before putting the equipment into service, the outer layers of sulfopolyester could be washed off. A further embodiment of this general application concept could involve articles of personal protection to provide temporary barrier layers for some reusable or limited use garments or coverings. For the military, activated carbon and chemical absorbers could be sprayed onto the attenuating filament pattern just prior to the collector to allow the melt blown matrix to anchor these entities on the exposed surface. The chemical absorbers can even be changed in the forward operations area as the threat evolves by melt blowing on another layer.


A major advantage inherent to sulfopolyesters is the facile ability to remove or recover the polymer from aqueous dispersions via flocculation or precipitation by adding ionic moieties (i.e., salts). Other methods, such as pH adjustment, adding nonsolvents, freezing, and so forth may also be employed. Therefore, fibrous articles, such as outer wear protective garments, after successful protective barrier use and even if the polymer is rendered as hazardous waste, can potentially be handled safely at much lower volumes for disposal using accepted protocols, such as incineration.


Undissolved or dried sulfopolyesters are known to form strong adhesive bonds to a wide array of substrates, including, but not limited to fluff pulp, cotton, acrylics, rayon, lyocell, PLA (polylactides), cellulose acetate, cellulose acetate propionate, poly(ethylene) terephthalate, poly(butylene) terephthalate, poly(trimethylene) terephthalate, poly(cyclohexylene) terephthalate, copolyesters, polyamides (nylons), stainless steel, aluminum, treated polyolefins, PAN (polyacrylonitriles), and polycarbonates. Thus, our nonwoven fabrics may be used as laminating adhesives or binders that may be bonded by known techniques, such as thermal, radio frequency (RF), microwave, and ultrasonic methods. Adaptation of sulfopolyesters to enable RF activation is disclosed in a number of recent patents. Thus, our novel nonwoven fabrics may have dual or even multifunctionality in addition to adhesive properties. For example, a disposable baby diaper could be obtained where a nonwoven of the present invention serves as both an water-responsive adhesive as well as a fluid managing component of the final assembly.


Our invention also provides a process for water-dispersible fibers comprising (I) heating a water-dispersible polymer composition to a temperature above its flow point, wherein the polymer composition comprises (i) residues of one or more dicarboxylic acids; (ii) about 4 to about 40 mole %, based on the total repeating units, of residues of at least one sulfomonomer having 2 functional groups and one or more metal sulfonate groups attached to an aromatic or cycloaliphatic ring wherein the functional groups are hydroxyl, carboxyl, or a combination thereof; and (iii) one or more diol residues wherein at least 20 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

H—(OCH2—CH2)n—OH

wherein n is an integer in the range of 2 to about 500; (iv) 0 to about 25 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof; wherein the polymer composition contains less than 10 weight percent of a pigment or filler, based on the total weight of the polymer composition; and (II) melt spinning filaments. As described hereinabove, a water-dispersible polymer, optionally, may be blended with the sulfopolyester. In addition, a water-nondispersible polymer, optionally, may be blended with the sulfopolyester to form a blend such that blend is an immiscible blend. The term “flow point”, as used herein, means the temperature at which the viscosity of the polymer composition permits extrusion or other forms of processing through a spinneret or extrusion die. The dicarboxylic acid residue may comprise from about 60 to about 100 mole % of the acid residues depending on the type and concentration of the sulfomonomer. Other examples of concentration ranges of dicarboxylic acid residues are from about 60 mole % to about 95 mole % and about 70 mole % to about 95 mole %. The preferred dicarboxylic acid residues are isophthalic, terephthalic, and 1,4-cyclohexanedicarboxylic acids or if diesters are used, dimethyl terephthalate, dimethyl isophthalate, and dimethyl-1,4-cyclohexanedicarboxylate with the residues of isophthalic and terephthalic acid being especially preferred.


The sulfomonomer may be a dicarboxylic acid or ester thereof containing a sulfonate group, a diol containing a sulfonate group, or a hydroxy acid containing a sulfonate group. Additional examples of concentration ranges for the sulfomonomer residues are about 4 to about 25 mole %, about 4 to about 20 mole %, about 4 to about 15 mole %, and about 4 to about 10 mole %, based on the total repeating units. The cation of the sulfonate salt may be a metal ion such as Li+, Na+, K+, Mg++, Ca++, Ni++, Fe++, and the like. Alternatively, the cation of the sulfonate salt may be non-metallic such as a nitrogenous base as described previously. Examples examples of sulfomonomer residues which may be used in the process of the present invention are the metal sulfonate salt of sulfophthalic acid, sulfoterephthalic acid, sulfoisophthalic acid, or combinations thereof. Another example of sulfomonomer which may be used is 5-sod iosulfoisophthalic acid or esters thereof. If the sulfomonomer residue is from 5-sodiosulfoisophthalic acid, typical sulfomonomer concentration ranges are about 4 to about 35 mole %, about 8 to about 30 mole %, and about 10 to 25 mole %, based on the total acid residues.


The sulfopolyester of our includes one or more diol residues which may include aliphatic, cycloaliphatic, and aralkyl glycols. The cycloaliphatic diols, for example, 1,3- and 1,4-cyclohexanedimethanol, may be present as their pure cis or trans isomers or as a mixture of cis and trans isomers. Non-limiting examples of lower molecular weight polyethylene glycols, e.g., wherein n is from 2 to 6, are diethylene glycol, triethylene glycol, and tetraethylene glycol. Of these lower molecular weight glycols, diethylene and triethylene glycol are most preferred. The sulfopolyester may optionally include a branching monomer. Examples of branching monomers are as described hereinabove. Further examples of branching monomer concentration ranges are from 0 to about 20 mole % and from 0 to about 10 mole %. The sulfpolyester of our novel process has a Tg of at least 25° C. Further examples of glass transition temperatures exhibited by the sulfopolyester are at least 30° C., at least 35° C., at least 40° C., at least 50° C., at least 60° C., at least 65° C., at least 80° C., and at least 90° C. Although other Tg's are possible, typical glass transition temperatures of the dry sulfopolyesters our invention are about 30° C., about 48° C., about 55° C., about 65° C., about 70° C., about 75° C., about 85° C., and about 90° C.


The water-dispersible fibers are prepared by a melt blowing process. The polymer is melted in an extruder and forced through a die. The extrudate exiting the die is rapidly attenuated to ultrafine diameters by hot, high velocity air. The orientation, rate of cooling, glass transition temperature (Tg), and rate of crystallization of the fiber are important because they affect the viscosity and processing properties of the polymer during attenuation. The filament is collected on a renewable surface, such as a moving belt, cylindrical drum, rotating mandrel, and so forth. Predrying of pellets (if needed), extruder zone temperature, melt temperature, screw design, throughput rate, air temperature, air flow (velocity), die air gap and set back, nose tip hole size, die temperature, die-to-collector (DCP) distance, quenching environment, collector speed, and post treatments are all factors that influence product characteristics such as filament diameters, basis weight, web thickness, pore size, softness, and shrinkage. The high velocity air also may be used to move the filaments in a somewhat random fashion that results in extensive interlacing. If a moving belt is passed under the die, a nonwoven fabric can be produced by a combination of over-lapping laydown, mechanical cohesiveness, and thermal bonding of the filaments. Overblowing onto another substrate, such as a spunbond or backing layer, is also possible. If the filaments are taken up on an rotating mandrel, a cylindrical product is formed. A water-dispersible fiber lay-down can also be prepared by the spunbond process.


The instant invention, therefore, further provides a process for water-dispersible, nonwoven fabric comprising (A) heating a water-dispersible polymer composition to a temperature above its flow point, wherein the polymer composition comprises: (i) residues of one or more dicarboxylic acids; (ii) about 4 to about 40 mole %, based on the total repeating units, of residues of at least one sulfomonomer having 2 functional groups and one or more metal sulfonate groups attached to an aromatic or cycloaliphatic ring wherein the functional groups are hydroxyl, carboxyl, or a combination thereof; (iii) one or more diol residues wherein at least 20 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure

H—(OCH2—CH2)n—OH

wherein n is an integer in the range of 2 to about 500; (iv) 0 to about 25 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein the functional groups are hydroxyl, carboxyl, or a combination thereof; wherein the sulfopolyester has a glass transistion temperature (Tg) of at least 25° C.; wherein the polymer composition contains less than 10 weight percent of a pigment or filler, based on the total weight of the polymer composition; (B) melt-spinning filaments; and (C) overlapping and collecting the filaments of Step B to form a nonwoven fabric. As described hereinabove, a water-dispersible polymer, optionally, may be blended with the sulfopolyester. In addition, a water-nondispersible polymer, optionally, may be blended with the sulfopolyester to form a blend such that blend is an immiscible blend. The dicarboxylic acid, sulfomonomer, and branching monomer residues are as described previously. The sulfpolyester has a Tg of at least 25° C. Further examples of glass transition temperatures exhibited by the sulfopolyester are at least 30° C., at least 35° C., at least 40° C., at least 50° C., at least 60° C., at least 65° C., at least 80° C., and at least 90° C. Although other Tg's are possible, typical glass transition temperatures of the dry sulfopolyesters our invention are about 30° C., about 48° C., about 55° C., about 65° C., about 70° C., about 75° C., about 85° C., and about 90° C. The invention is further illustrated by the following examples.


EXAMPLES

All pellet samples were predried under vacuum at room temperature for at least 12 hours. The dispersion times shown in Table 3 are for either complete dispersion or dissolution of the nonwoven fabric samples. The abbreviation “CE”, used in Tables 2 and 3 mean “comparative example”.


Example 1

A sulfopolyester containing 76 mole %, isophthalic acid, 24 mole % of sodiosulfoisophthalic acid, 76 mole % diethylene glycol, and 24 mole % 1,4-cyclohexanedimethanol with an Ih.V. of 0.29 and a Tg of 48° C. was meltblown through a nominal 6-inch die (30 holes/inch in the nosepiece) onto a cylindrical collector using the conditions shown in Table 1. Interleafing paper was not required. A soft, handleable, flexible web was obtained that did not block during the roll winding operation. Physical properties are provided in Table 2. A small piece (1″×3″) of the nonwoven fabric was easily dispersed in both room temperature (RT) and 50° C. water with slight agitation as shown by data in Table 3.









TABLE 1







Melt Blowing Conditions










Operating Condition
Typical Value










Die Configuration











Die tip hole diameter
0.0185
inches










Number of holes
120











Air gap
0.060
inches



Set back
0.060
inches







Extruder Barrel Temperatures (° F.)










Zone 1
350



Zone 2
510



Zone 3
510







Die Temperatures (° F.)










Zone 4
510



Zone 5
510



Zone 6
510



Zone 7
510



Zone 8
510







Air Temperatures (° F.)










Furnace exit 1
350



Furnace exit 2
700



Furnace exit 3
700



Die
530-546







Extrusion Conditions











Air pressure
3.0
psi



Melt pressure after pump
99-113
psi







Take Up Conditions











Throughput
0.3
g/hole/min




0.5
g/hole/min



Basis weight
36
g/m2



Collector speed
20
ft/min



Collector distance
12
inches
















TABLE 2







Physical Properties of Nonwovens













Tg/Tm (° C.)



Filament Diameter (μm)
IhV
(sulfopoly./












Example
Minimum
Maximum
Average
(before/after)
PP)















1
5
18
8.7
0.29/0.26
39/not







applicable


2
3
11
7.7
0.40/0.34
36/not







applicable


CE 1
2
20
8
Not
36/163






measured



CE 2
4
10
7
Not
36/164






measured



CE 3
4
11
6
Not
35/161






measured
















TABLE 3







Dispersbility of Nonwovens












Water
Initial
Significant
Complete



Temperature
Disintegration
Disintegration
Dispersion


Example
(° C.)
(minutes)
(minutes)
(minutes)














1
23
<0.25
1
2



50
<0.17
0.5
1


2
23
8
14
19 



50
<0.5
5
8



80
<0.5
2
5


CE 1
23
0.5
>15
No






dispersion of






PP



50
0.5
>15
No






dispersion of






PP


CE 2
23
0.5
>15
No






dispersion of






PP



50
0.5
>15
No






dispersion of






PP


CE 3
23
<0.5
6
No






dispersion of






PP



50
<0.5
4
No






dispersion of






PP









Example 2

A sulfopolyester containing 89 mole %, isophthalic acid, 11 mole % of sodiosulfoisophthalic acid, 72 mole % diethylene glycol, and 28 mole % ethylene glycol with an Ih.V. of 0.4 and a Tg of 35° C. was meltblown through a 6-inch die using conditions similar to those in Table 1. A soft, handleable, flexible web was obtained that did not block during a roll winding operation. Physical properties are provided in Table 2. A small piece (1″×2″) of the nonwoven fabric was easily and completely dispersed at 50° C. and 80° C.; at RT (23° C.), the fabric required a longer period of time for complete dispersion as shown by the data in Table 3.


It was found that the compositions in Examples 1 and 2 can be overblown onto other nonwoven substrates. It is also possible to condense and wrap shaped or contoured forms that are used instead of conventional web collectors. Thus, it is possible to obtain circular “roving” or plug forms of the webs.


Comparative Examples 1-3

Pellets of a sulfopolyester containing 89 mole %, isophthalic acid, 11 mole % of sodiosulfoisophthalic acid, 72 mole % diethylene glycol, and 28 mole % ethylene glycol with an Ih.V. of 0.4 and a Tg of 35° C. were combined with polypropylene (BaseII PF 008) pellets in bicomponent ratios (by wt %) of:

    • 75 PP: 25 sulfopolyester (Example 3)
    • 50 PP: 50 sulfopolyester (Example 4)
    • 25 PP: 75 sulfopolyester (Example 5)
    • The PP had a MFR (melt flow rate) of 800. A melt blowing operation was performed on a line equipped with a 24-inch wide die to yield handleable, soft, flexible, but nonblocking webs with the physical properties provided in Table 2. Small pieces (1″×4″) of nonwoven fabric readily disintegrated as reported in Table 3. None of the fibers, however, were completely water-dispersible because of the insoluble polypropylene component.


Example 3

A circular piece (4″ diameter) of the nonwoven produced in Example 2 was used as an adhesive layer between two sheets of cotton fabric. A Hannifin melt press was used to fuse the two sheets of cotton together by applying a pressure 35 psig at 200° C. for 30 seconds. The resultant assembly exhibited exceptionally strong bond strength. The cotton substrate shredded before adhesive or bond failure. Similar results have also been obtained with other cellulosics and with PET polyester substrates. Strong bonds were also produced by ultrasonic bonding techniques.


Comparative Example 4

A PP (Exxon 3356G) with a 1200 MFR was melt blown using a 24″ die to yield a flexible nonwoven fabric that did not block and was easily unwound from a roll. Small pieces (1″×4″) did not show any response (i.e., no disintegration or loss in basis weight) to water when immersed in water at RT or 50° C. for 15 minutes.


Example 4

Unicomponent fibers of a sulfopolyester containing 82 mole % isophthalic acid, 18 mole % of sodiosulfoisophthalic acid, 54 mole % diethylene glycol, and 46 mole % 1,4-cyclohexanedimethanol with a Tg of 55° C. were melt spun at melt temperatures of 245° C. (473° F.) on a lab staple spinning line. As-spun denier was approximately 8 d/f. Some blocking was encountered on the take-up tubes, but the 10-filament strand readily dissolved within 10-19 seconds in unagitated, demineralized water at 82° C. and a pH between 5 and 6.


Example 5

Unicomponent fibers obtained from a blend (75:25) of a sulfopolyester containing 82 mole % isophthalic acid, 18 mole % of sodiosulfoisophthalic acid, 54 mole % diethylene glycol, and 46 mole % 1,4-cyclohexanedimethanol (Tg of 55° C.) and a sulfopolyester containing 91 mole % isophthalic acid, 9 mole % of sodiosulfoisophthalic acid, 25 mole % diethylene glycol, and 75 mole % 1,4-cyclohexanedimethanol (Tg of 65° C.), respectively, were melt spun on a lab staple spinning line. The blend has a Tg of 57° C. as calculated by taking a weighted average of the Tg's of the component sulfopolyesters. The 10-filament strands did not show any blocking on the take-up tubes, but readily dissolved within 20-43 seconds in unagitated, demineralized water at 82° C. and a pH between 5 and 6.


Example 6

The blend described in Example 5 was co-spun with PET to yield bicomponent islands-in-the-sea fibers. A configuration was obtained where the sulfopolyester “sea” is 20 wt % of the fiber containing 80 wt % of PET “islands”. The spun yarn elongation was 190% immediately after spinning. Blocking was not encountered as the yarn was satisfactorily unwound from the bobbins and processed a week after spinning. In a subsequent operation, the “sea” was dissolved by passing the yarn through an 88° C. soft water bath leaving only fine PET filaments.


Example 7

This prophetic example illustrates the possible application of the multicomponent and microdenier fibers of the present invention to the preparation of specialty papers. The blend described in Example 5 is co-spun with PET to yield bicomponent islands-in-the-sea fibers. The fiber contains approximately 35 wt % sulfopolyester “sea” component and approximately 65 wt % of PET “islands”. The uncrimped fiber is cut to ⅛ inch lengths. In simulated papermaking, these short-cut bicomponent fibers are added to the refining operation. The sulfopolyester “sea” is removed in the agitated, aqueous slurry thereby releasing the microdenier PET fibers into the mix. At comparable weights, the microdenier PET fibers (“islands”) are more effective to increase paper tensile strength than the addition of coarse PET fibers.

Claims
  • 1. A fibrous article comprising at least one multicomponent fiber having a shaped cross section, wherein said multicomponent fiber comprises: A) a water dispersible sulfopolyester having a glass transition temperature (Tg) of at least 57° C., said sulfpolyester comprising: (i) residues of one or more dicarboxylic acids;(ii) about 4 to about 40 mole %, based on the total repeating units, of residues of at least one sulfomonomer having 2 functional groups and one or more sulfonate groups attached to an aromatic or cycloaliphatic ring wherein said functional groups are hydroxyl, carboxyl, or a combination thereof;(iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure H—(OCH2—CH2)n—OHwherein n is an integer in the range of 2 to about 500; and(iv) 0 to about 25 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein said functional groups are hydroxyl, carboxyl, or a combination thereof; andB) a plurality of segments comprising at least one water-nondispersable polymer immiscible with said sulfopolyester, wherein said segments are substantially isolated from each other by said sulfopolyester intervening between said segments; wherein said fibrous article is selected from the group consisting of papers, multifilament fibers, nonwoven webs, textile yarns, personal care products, health care products, medical and surgical care products, laminates, fiber-containing cleaning products, replacement inserts for personal hygiene and cleaning products, packaging materials, personal protection products, laminating adhesives, protective layers, and binders.
  • 2. A fibrous article comprising at least one multicomponent fiber having a shaped cross section, wherein said multicomponent fiber comprises: A) at least one water dispersible sulfopolyester having a glass transition temperature (Tg) of at least 57° C., said sulfopolyester comprising: (i) about 50 to about 96 mole % of one or more residues of isophthalic acid or terephthalic acid, based on the total acid residues;(ii) about 4 to about 30 mole %, based on the total acid residues, of a residue of sodiosulfoisophthalic acid;(iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure H—(OCH2—CH2)n—OHwherein n is an integer in the range of 2 to about 500;(iv) 0 to about 20 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein said functional groups are hydroxyl, carboxyl, or a combination thereof; andB) a plurality of segments comprising at least one water-nondispersable polymer[s] immiscible with said sulfopolyester, wherein said segments are substantially isolated from each other by said sulfopolyester intervening between said segments; wherein said fibrous article is selected from the group consisting of papers, multifilament fibers, nonwoven webs, textile yarns, personal care products, health care products, medical and surgical care products, laminates, fiber-containing cleaning products, replacement inserts for personal hygiene and cleaning products, packaging materials, personal protection products, laminating adhesives, protective layers, and binders.
  • 3. The fibrous article according to claim 1 or 2 wherein said fibrous article is selected from the group consisting of wipes, gauzes, tissues, diapers, child training pants, adult incontinence briefs, adult diapers, sanitary napkins, panty liners, tampons, bandages, wound care dressings, and surgical dressings, examination bed coverings, medical gowns, surgical gowns and masks, tapes, and other protective barriers.
  • 4. The fibrous article according to claim 1 or 2 wherein said fibrous article is bonded, laminated, attached to, or used in conjunction with other materials which may or may not be water-dispersible.
  • 5. The fibrous article according to claim 1 or 2 wherein said fibrous article is pre-moistened with at least one liquid composition and used to deliver said liquid composition to a surface.
  • 6. The fibrous article according to claim 5 wherein said liquid composition is selected from the group consisting of detergents, wetting agents, cleaning agents, and skin care products.
  • 7. The fibrous article according to claim 6 wherein said skin care product is selected from the group consisting of cosmetics, ointments, medications, emollients, and fragrances.
  • 8. The fibrous article according to claim 1 or 2 wherein said fibrous article further comprises at least one powder or particulate.
  • 9. The fibrous article according to claim 8 wherein said powder or particulate is selected from the group consisting of talcs; starches; water absorbent, water dispersible or water swellable polymers; silicas; pigments; and microcapsules.
  • 10. The fibrous article according to claim 9 wherein said water absorbent, water dispersible or water swellable polymer is selected from the group consisting of super absorbent polymers, poly(acrylonitriles), sulfopolyesters, and poly(vinylalcohols).
  • 11. The fibrous article according to claim 1 or 2 further comprising at least one additive selected from the group consisting of oxidative stabilizers, UV absorbers, colorants, pigments, opacifiers, optical brighteners, fillers, nucleating agents, plasticizers, viscosity modifiers, surface modifiers, antimicrobials, disinfectants, cold flow inhibitors, branching agents, and catalysts.
  • 12. The fibrous article according to claim 1 or 2 further comprising a least one water-dispersible film; wherein said water-dispersible film comprises a second water-dispersible polymer.
  • 13. A process comprising melt blowing at least one nonwoven fabric comprising multicomponent fibers onto a surface to produce a protective layer; wherein said multicomponent fiber comprises: A) a water dispersible sulfopolyester having a glass transition temperature (Tg) of at least 57° C., said sulfpolyester comprising: (i) residues of one or more dicarboxylic acids;(ii) about 4 to about 40 mole %, based on the total repeating units, of residues of at least one sulfomonomer having 2 functional groups and one or more sulfonate groups attached to an aromatic or cycloaliphatic ring wherein said functional groups are hydroxyl, carboxyl, or a combination thereof;(iii) one or more diol residues wherein at least 25 mole %, based on the total diol residues, is a poly(ethylene glycol) having a structure H—(OCH2—CH2)n—OHwherein n is an integer in the range of 2 to about 500; and(iv) 0 to about 25 mole %, based on the total repeating units, of residues of a branching monomer having 3 or more functional groups wherein said functional groups are hydroxyl, carboxyl, or a combination thereof; andB) a plurality of segments comprising at least one water-nondispersable polymer immiscible with said sulfopolyester, wherein said segments are substantially isolated from each other by said sulfopolyester intervening between said segments.
  • 14. The process according to claim 13 wherein said surface is a garment.
CROSS REFERENCES TO RELATED APPLICATIONS

This application is a continuation application claiming priority to application Ser. No. 11/204,868 filed on Aug. 16, 2005 now allowed, which is a divisional of application Ser. No. 10/850,548, filed May 20, 2004, now issued as U.S. Pat. No. 6,989,193, which is a continuation-in-part of application Ser. No. 10/465,698, filed Jun. 19, 2003, abandoned; all of which are hereby incorporated by reference to the extent they do contradict the statements herein.

US Referenced Citations (617)
Number Name Date Kind
1814155 Haughey Jul 1931 A
2862251 Kalwaites Dec 1958 A
2999788 Morgan Sep 1961 A
3018272 Griffing et al. Jan 1962 A
3033822 Kibler et al. May 1962 A
3049469 Davison et al. Aug 1962 A
3075952 Coover et al. Jan 1963 A
3372084 Arledter Mar 1968 A
3485706 Evans Dec 1969 A
3528947 Lappin et al. Sep 1970 A
3556932 Coscia et al. Jan 1971 A
3592796 Trapasso et al. Jul 1971 A
3772076 Keim Nov 1973 A
3779993 Kibler et al. Dec 1973 A
3783093 Gallacher et al. Jan 1974 A
3803210 Rod et al. Apr 1974 A
3833457 Misumi et al. Sep 1974 A
3846507 Thomm et al. Nov 1974 A
3998740 Bost et al. Dec 1976 A
4008344 Okamoto et al. Feb 1977 A
4073777 O'Neill et al. Feb 1978 A
4073988 Nishida et al. Feb 1978 A
4100324 Anderson et al. Jul 1978 A
4104262 Schade Aug 1978 A
4121966 Amano et al. Oct 1978 A
4127696 Okamoto Nov 1978 A
4137393 Sidebotham et al. Jan 1979 A
4145469 Newkirk et al. Mar 1979 A
4233355 Sato et al. Nov 1980 A
4234652 Vanoni et al. Nov 1980 A
4239720 Gerlach et al. Dec 1980 A
4240918 Lagasse et al. Dec 1980 A
4243480 Hernandez et al. Jan 1981 A
4288503 Goldberg Sep 1981 A
4288508 Goldberg Sep 1981 A
4297412 Achard et al. Oct 1981 A
4299654 Tlach et al. Nov 1981 A
4302495 Marra Nov 1981 A
4304901 O'Neill et al. Dec 1981 A
4342801 Gerlach et al. Aug 1982 A
4350006 Okamoto et al. Sep 1982 A
4365041 Okamoto et al. Dec 1982 A
4381335 Okamoto Apr 1983 A
4410579 Johns Oct 1983 A
4427557 Stockburger Jan 1984 A
4460649 Park et al. Jul 1984 A
4480085 Larson Oct 1984 A
4496619 Okamoto Jan 1985 A
4517715 Yoshida et al. May 1985 A
4569343 Kimura et al. Feb 1986 A
4618524 Groitzsch et al. Oct 1986 A
4647497 Weeks Mar 1987 A
4699845 Oikawa et al. Oct 1987 A
4738785 Langston et al. Apr 1988 A
4755421 Manning et al. Jul 1988 A
4795668 Krueger et al. Jan 1989 A
4804719 Weaver et al. Feb 1989 A
4810775 Bendix et al. Mar 1989 A
4863785 Berman et al. Sep 1989 A
4873273 Allan et al. Oct 1989 A
4910292 Blount Mar 1990 A
4921899 Phan et al. May 1990 A
4940744 Tortorici et al. Jul 1990 A
4943477 Kanamura et al. Jul 1990 A
4946932 Jenkins Aug 1990 A
4966808 Kawano Oct 1990 A
4973656 Blount Nov 1990 A
4990593 Blount Feb 1991 A
4996252 Phan et al. Feb 1991 A
5006598 Adams et al. Apr 1991 A
5039339 Phan et al. Aug 1991 A
5057368 Largman et al. Oct 1991 A
5069970 Largman et al. Dec 1991 A
5073436 Antonacci et al. Dec 1991 A
5108820 Kaneko et al. Apr 1992 A
5124194 Kawano Jun 1992 A
5158844 Hagens et al. Oct 1992 A
5162074 Hills Nov 1992 A
5162399 Sharma et al. Nov 1992 A
5171767 Buckley et al. Dec 1992 A
5176952 Joseph et al. Jan 1993 A
5218042 Kuo et al. Jun 1993 A
5242640 Butler et al. Sep 1993 A
5258220 Joseph Nov 1993 A
5262460 Suzuki et al. Nov 1993 A
5274025 Stockl et al. Dec 1993 A
5277976 Hogle et al. Jan 1994 A
5281306 Kakiuchi et al. Jan 1994 A
5286843 Wood Feb 1994 A
5290626 Nishioi et al. Mar 1994 A
5290631 Fleury et al. Mar 1994 A
5290654 Sacripante et al. Mar 1994 A
5292581 Viazmensky et al. Mar 1994 A
5292855 Krutak et al. Mar 1994 A
5296286 Allen et al. Mar 1994 A
5308697 Muramoto et al. May 1994 A
5336552 Strack et al. Aug 1994 A
5338406 Smith Aug 1994 A
5342863 Buckley et al. Aug 1994 A
5366804 Dugan Nov 1994 A
5368928 Okamura et al. Nov 1994 A
5369210 George et al. Nov 1994 A
5369211 George et al. Nov 1994 A
5374357 Comstock et al. Dec 1994 A
5375306 Roussin-Moynier Dec 1994 A
5378757 Blount, Jr. et al. Jan 1995 A
5382400 Pike et al. Jan 1995 A
5386003 Greene et al. Jan 1995 A
5389068 Keck Feb 1995 A
5395693 Cho et al. Mar 1995 A
5405698 Dugan Apr 1995 A
5416156 Kamen May 1995 A
5423432 Krutak et al. Jun 1995 A
5431994 Kozulla Jul 1995 A
5446079 Buchanan et al. Aug 1995 A
5456982 Hansen et al. Oct 1995 A
5466410 Hills Nov 1995 A
5466518 Isaac et al. Nov 1995 A
5472600 Ellefson et al. Dec 1995 A
5482772 Strack et al. Jan 1996 A
5486418 Ohmory et al. Jan 1996 A
5496627 Bagrodia et al. Mar 1996 A
5498468 Blaney Mar 1996 A
5502091 Dasgupta Mar 1996 A
5508101 Patnode et al. Apr 1996 A
5509913 Yeo Apr 1996 A
5525282 Dugan Jun 1996 A
5530059 Blount, Jr. et al. Jun 1996 A
5536811 Wood Jul 1996 A
5543488 Miller et al. Aug 1996 A
5545481 Harrington Aug 1996 A
5552495 Miller et al. Sep 1996 A
5559171 Buchanan et al. Sep 1996 A
5559205 Hansen et al. Sep 1996 A
5567510 Patnode et al. Oct 1996 A
5571620 George et al. Nov 1996 A
5575918 Virnig et al. Nov 1996 A
5580911 Buchanan et al. Dec 1996 A
5593778 Kondo et al. Jan 1997 A
5593807 Sacripante et al. Jan 1997 A
5599858 Buchanan et al. Feb 1997 A
5605746 Groeger et al. Feb 1997 A
5607491 Jackson et al. Mar 1997 A
5607765 Hansen et al. Mar 1997 A
5620785 Watt et al. Apr 1997 A
5630972 Patnode et al. May 1997 A
5635071 Al-Samadi Jun 1997 A
5637385 Mizuki et al. Jun 1997 A
5643662 Yeo et al. Jul 1997 A
5646237 George et al. Jul 1997 A
5652048 Haynes et al. Jul 1997 A
5654086 Nishijima et al. Aug 1997 A
5658704 Patel et al. Aug 1997 A
5660965 Mychajlowskij et al. Aug 1997 A
5672415 Sawyer et al. Sep 1997 A
5688582 Nagaoka et al. Nov 1997 A
5698331 Matsumura et al. Dec 1997 A
5709940 George et al. Jan 1998 A
5736083 Dugan Apr 1998 A
5750605 Blumenthal et al. May 1998 A
5753351 Yoshida et al. May 1998 A
5759926 Pike et al. Jun 1998 A
5763065 Patnode et al. Jun 1998 A
5779736 Frederick et al. Jul 1998 A
5783503 Gillespie et al. Jul 1998 A
5785725 Cusick et al. Jul 1998 A
5798078 Myers Aug 1998 A
5817740 Anderson et al. Oct 1998 A
5820982 Salsman Oct 1998 A
5837658 Stork Nov 1998 A
5843311 Richter et al. Dec 1998 A
5853701 George et al. Dec 1998 A
5853944 Foucher et al. Dec 1998 A
5871845 Dahringer et al. Feb 1999 A
5883181 Cicchiello et al. Mar 1999 A
5888916 Tadokoro et al. Mar 1999 A
5895710 Sasse et al. Apr 1999 A
5916678 Jackson et al. Jun 1999 A
5916687 Takanashi et al. Jun 1999 A
5916725 Patel et al. Jun 1999 A
5916935 Wiggins et al. Jun 1999 A
5935880 Wang et al. Aug 1999 A
5935883 Pike Aug 1999 A
5935884 Williams et al. Aug 1999 A
5948710 Pomplun et al. Sep 1999 A
5952251 Jackson et al. Sep 1999 A
5954967 Egraz et al. Sep 1999 A
5970583 Groten et al. Oct 1999 A
5976694 Tsai et al. Nov 1999 A
5993668 Duan Nov 1999 A
5993834 Shah et al. Nov 1999 A
6004673 Nishijima Dec 1999 A
6007910 Miller et al. Dec 1999 A
6020420 George Feb 2000 A
6037055 Aneja et al. Mar 2000 A
6057388 Wiggins et al. May 2000 A
6080471 Shigematsu et al. Jun 2000 A
6090731 Pike et al. Jul 2000 A
6110249 Duane et al. Aug 2000 A
6110588 Perez et al. Aug 2000 A
6110636 Foucher et al. Aug 2000 A
6114407 Myers Sep 2000 A
6120889 Turner et al. Sep 2000 A
6121170 Tsai et al. Sep 2000 A
6162340 Zakikhani Dec 2000 A
6162890 George et al. Dec 2000 A
6168719 Shimokawa et al. Jan 2001 B1
6171685 George et al. Jan 2001 B1
6174602 Matsui et al. Jan 2001 B1
6177193 Tsai et al. Jan 2001 B1
6177607 Blaney et al. Jan 2001 B1
6183648 Kozak et al. Feb 2001 B1
6200669 Marmon et al. Mar 2001 B1
6211309 McIntosh et al. Apr 2001 B1
6218321 Lorcks et al. Apr 2001 B1
6225243 Austin May 2001 B1
6235392 Luo et al. May 2001 B1
6248809 Buckley et al. Jun 2001 B1
6294645 Allen et al. Sep 2001 B1
6296933 Goda et al. Oct 2001 B1
6300306 Firkins et al. Oct 2001 B1
6316592 Bates et al. Nov 2001 B1
6322887 Matsui et al. Nov 2001 B1
6331606 Sun Dec 2001 B1
6332994 Karageorgiou Dec 2001 B1
6348679 Ryan et al. Feb 2002 B1
6352948 Pike et al. Mar 2002 B1
6355137 Staib Mar 2002 B1
6361784 Brennan et al. Mar 2002 B1
6365697 Kim et al. Apr 2002 B1
6369136 Sorriero et al. Apr 2002 B2
6381817 Moody, III May 2002 B1
6384108 Breton et al. May 2002 B1
6402870 Groten et al. Jun 2002 B1
6403677 Walker Jun 2002 B1
6417251 Brady Jul 2002 B1
6420024 Perez et al. Jul 2002 B1
6420027 Kimura et al. Jul 2002 B2
6428900 Wang Aug 2002 B1
6429253 Guerro et al. Aug 2002 B1
6430348 Asano et al. Aug 2002 B1
6432532 Perez et al. Aug 2002 B2
6432850 Susumu et al. Aug 2002 B1
6436855 Iwata et al. Aug 2002 B1
6440556 Matsui et al. Aug 2002 B2
6441267 Dugan Aug 2002 B1
6471910 Haggard Oct 2002 B1
6488731 Schultheiss et al. Dec 2002 B2
6506853 Duan Jan 2003 B2
6509092 Dugan Jan 2003 B1
6512024 Lundgard et al. Jan 2003 B1
6533938 Dilorio et al. Mar 2003 B1
6541175 Jiang et al. Apr 2003 B1
6548592 Lang et al. Apr 2003 B1
6550622 Koslow Apr 2003 B2
6551353 Baker et al. Apr 2003 B1
6552123 Katayama et al. Apr 2003 B1
6552162 Wang et al. Apr 2003 B1
6554881 Healey Apr 2003 B1
6573204 Philipp et al. Jun 2003 B1
6576716 Wo Jun 2003 B1
6579466 David et al. Jun 2003 B1
6583075 Dugan Jun 2003 B1
6586529 Mumick et al. Jul 2003 B2
6589426 Husain et al. Jul 2003 B1
6602955 Soerens et al. Aug 2003 B2
H2086 Amsler Oct 2003 H
6638677 Patel et al. Oct 2003 B2
6657017 Wo et al. Dec 2003 B2
6664437 Sawyer et al. Dec 2003 B2
6692825 Qin et al. Feb 2004 B2
6706652 Groten et al. Mar 2004 B2
6720063 Kobayashi et al. Apr 2004 B2
6730387 Rezai et al. May 2004 B2
6743506 Bond et al. Jun 2004 B2
6746766 Bond et al. Jun 2004 B2
6746779 Hayes et al. Jun 2004 B2
6759124 Royer et al. Jul 2004 B2
6764802 Maric et al. Jul 2004 B2
6767498 Talley, Jr. et al. Jul 2004 B1
6776858 Bansal et al. Aug 2004 B2
6780560 Farrugia et al. Aug 2004 B2
6780942 Leon et al. Aug 2004 B2
6787245 Hayes Sep 2004 B1
6815382 Groten et al. Nov 2004 B1
6838172 Yoon et al. Jan 2005 B2
6838403 Tsai et al. Jan 2005 B2
6841038 Horenziak et al. Jan 2005 B2
6844062 Matsui et al. Jan 2005 B2
6844063 Matsui et al. Jan 2005 B2
6849329 Perez et al. Feb 2005 B2
6855422 Magill et al. Feb 2005 B2
6860906 Malisz et al. Mar 2005 B2
6861142 Wilkie et al. Mar 2005 B1
6890649 Hobbs et al. May 2005 B2
6893711 Williamson et al. May 2005 B2
6900148 Yoneda et al. May 2005 B2
6902796 Morell et al. Jun 2005 B2
6946506 Bond et al. Sep 2005 B2
6949288 Hodge et al. Sep 2005 B2
6953622 Tsai et al. Oct 2005 B2
6989193 Haile et al. Jan 2006 B2
6989194 Bansal et al. Jan 2006 B2
7008485 Heikkila et al. Mar 2006 B2
7011653 Imsangjan et al. Mar 2006 B2
7011885 Chang et al. Mar 2006 B2
7014803 Perez et al. Mar 2006 B2
7022201 Anderson et al. Apr 2006 B2
7025885 Cote et al. Apr 2006 B2
7026033 Fujimori et al. Apr 2006 B2
7070695 Husain et al. Jul 2006 B2
7087301 Musgrave et al. Aug 2006 B2
7091140 Ferencz et al. Aug 2006 B1
7097904 Ochi et al. Aug 2006 B2
7144614 Nakajima et al. Dec 2006 B2
7160612 Magill et al. Jan 2007 B2
7163744 Nightingale et al. Jan 2007 B2
7166225 Pitt et al. Jan 2007 B2
7179376 Kaleem et al. Feb 2007 B2
7186343 Rabie et al. Mar 2007 B2
7186344 Hughes Mar 2007 B2
7193029 Hayes Mar 2007 B2
7194788 Clark et al. Mar 2007 B2
7195814 Ista et al. Mar 2007 B2
7214765 Ringeisen et al. May 2007 B2
7220815 Hayes May 2007 B2
7238415 Rodriguez et al. Jul 2007 B2
7238423 Calhoun et al. Jul 2007 B2
7241497 Magill et al. Jul 2007 B2
7276139 Katai et al. Oct 2007 B2
7285209 Yu et al. Oct 2007 B2
7291270 Gibson et al. Nov 2007 B2
7291389 Bitler et al. Nov 2007 B1
7304125 Ibar Dec 2007 B2
7306735 Baggott et al. Dec 2007 B2
7309372 Kahlbaugh et al. Dec 2007 B2
7314497 Kahlbaugh et al. Jan 2008 B2
7329723 Jernigan et al. Feb 2008 B2
7338664 Tseng et al. Mar 2008 B2
7344775 Stevens et al. Mar 2008 B2
7347947 Nakamura et al. Mar 2008 B2
7357985 Kurian et al. Apr 2008 B2
7358022 Farrugia et al. Apr 2008 B2
7358323 Maeda et al. Apr 2008 B2
7358325 Hayes Apr 2008 B2
7361700 Sunamori et al. Apr 2008 B2
7365118 McCleskey et al. Apr 2008 B2
7371701 Inagaki May 2008 B2
7387976 Baba et al. Jun 2008 B2
7388058 Kaku et al. Jun 2008 B2
7405171 Tsujiyama et al. Jul 2008 B2
7405266 Bentley et al. Jul 2008 B2
7432219 Strandqvist et al. Oct 2008 B2
7442277 Kupper et al. Oct 2008 B2
7462386 Yamasaki et al. Dec 2008 B2
7497895 Sabottke Mar 2009 B2
7513004 Luckman et al. Apr 2009 B2
7560159 Goda et al. Jul 2009 B2
7576019 Bond et al. Aug 2009 B2
7588688 Butters et al. Sep 2009 B2
7622188 Kamiyama et al. Nov 2009 B2
7635745 Gupta et al. Dec 2009 B2
7655070 Dallas et al. Feb 2010 B1
7666500 Magill et al. Feb 2010 B2
7666502 Magill et al. Feb 2010 B2
7666504 Ochi et al. Feb 2010 B2
7674510 Kamiya Mar 2010 B2
7687143 Gupta et al. Mar 2010 B2
7695812 Peng et al. Apr 2010 B2
7696111 Mangold et al. Apr 2010 B2
7704595 Morin Apr 2010 B2
7718104 MacDonald et al. May 2010 B2
7727627 Sen et al. Jun 2010 B2
7732557 Phelps et al. Jun 2010 B2
7736737 Van Dun et al. Jun 2010 B2
7737060 Strickler et al. Jun 2010 B2
7744807 Berrigan et al. Jun 2010 B2
7754123 Verdegan et al. Jul 2010 B2
7757811 Fox et al. Jul 2010 B2
7765647 Smith et al. Aug 2010 B2
7772456 Zhang et al. Aug 2010 B2
7820568 Horiguchi et al. Oct 2010 B2
7837814 Minami et al. Nov 2010 B2
7858732 Bruchmann et al. Dec 2010 B2
7883604 Dyer et al. Feb 2011 B2
7884037 Sirovatka et al. Feb 2011 B2
7887526 Van Gompel et al. Feb 2011 B2
7892672 Nishikawa Feb 2011 B2
7892992 Kamada et al. Feb 2011 B2
7892993 Gupta et al. Feb 2011 B2
7896940 Sundet et al. Mar 2011 B2
7897078 Petersen et al. Mar 2011 B2
7897248 Barrera et al. Mar 2011 B2
7902094 Haile et al. Mar 2011 B2
7902096 Brandner et al. Mar 2011 B2
7910207 Kamiyama et al. Mar 2011 B2
7914866 Shannon et al. Mar 2011 B2
7918313 Gross et al. Apr 2011 B2
7919419 Hurley et al. Apr 2011 B2
7922959 Jones et al. Apr 2011 B2
7923143 Tanaka et al. Apr 2011 B2
7928025 Shipley et al. Apr 2011 B2
7931457 Johnson et al. Apr 2011 B2
7932192 Fujisawa et al. Apr 2011 B2
7935645 Pourdeyhimi et al. May 2011 B2
7947142 Fox et al. May 2011 B2
7947864 Damay et al. May 2011 B2
7951313 Matsubayashi et al. May 2011 B2
7951452 Nakayama et al. May 2011 B2
7959848 Reneker et al. Jun 2011 B2
8021457 Dema et al. Sep 2011 B2
8057567 Webb et al. Nov 2011 B2
8129019 Pourdeyhimi et al. Mar 2012 B2
20020009590 Matsui et al. Jan 2002 A1
20020030016 Schmidt Mar 2002 A1
20020079121 Ryan et al. Jun 2002 A1
20020106510 Deguchi et al. Aug 2002 A1
20020123290 Tsai et al. Sep 2002 A1
20020127937 Lange et al. Sep 2002 A1
20020127939 Hwo et al. Sep 2002 A1
20020146552 Mumick et al. Oct 2002 A1
20020187329 Ista et al. Dec 2002 A1
20030026986 Matsui et al. Feb 2003 A1
20030057155 Husain et al. Mar 2003 A1
20030077444 Bond et al. Apr 2003 A1
20030091822 Bond et al. May 2003 A1
20030092343 Bond et al. May 2003 A1
20030104204 Bond et al. Jun 2003 A1
20030111763 Jen Jun 2003 A1
20030166370 Harris et al. Sep 2003 A1
20030166371 Fingal et al. Sep 2003 A1
20030168191 Hansen et al. Sep 2003 A1
20030176132 Moriyasu et al. Sep 2003 A1
20030194558 Anderson Oct 2003 A1
20030196955 Hughes Oct 2003 A1
20040081829 Klier et al. Apr 2004 A1
20040157037 Yamaguchi et al. Aug 2004 A1
20040194558 Nagase Oct 2004 A1
20040209058 Chou et al. Oct 2004 A1
20040211729 Sunkara et al. Oct 2004 A1
20040242106 Rabasco et al. Dec 2004 A1
20040242838 Duan Dec 2004 A1
20040258910 Haile et al. Dec 2004 A1
20040260034 Haile et al. Dec 2004 A1
20050026527 Schmidt et al. Feb 2005 A1
20050027098 Hayes Feb 2005 A1
20050032450 Haggard et al. Feb 2005 A1
20050079781 Tsujimoto et al. Apr 2005 A1
20050115902 Kaleem et al. Jun 2005 A1
20050125908 Pourdeyhimi Jun 2005 A1
20050148261 Close et al. Jul 2005 A1
20050171250 Hayes Aug 2005 A1
20050208300 Magill et al. Sep 2005 A1
20050221709 Jordan et al. Oct 2005 A1
20050222956 Bristow et al. Oct 2005 A1
20050227068 Dugan Oct 2005 A1
20050239359 Jones et al. Oct 2005 A1
20050282008 Haile et al. Dec 2005 A1
20050287895 Bansal Dec 2005 A1
20060011544 Sharma et al. Jan 2006 A1
20060019570 Groten et al. Jan 2006 A1
20060021938 Diallo Feb 2006 A1
20060030230 Nagaoka et al. Feb 2006 A1
20060035556 Yokoi et al. Feb 2006 A1
20060049386 Kody et al. Mar 2006 A1
20060051575 Yoon et al. Mar 2006 A1
20060057350 Ochi et al. Mar 2006 A1
20060057373 Inagaki et al. Mar 2006 A1
20060060529 Cote et al. Mar 2006 A1
20060065600 Sunkara et al. Mar 2006 A1
20060081330 Minami et al. Apr 2006 A1
20060083917 Dugan Apr 2006 A1
20060093814 Chang May 2006 A1
20060093819 Atwood et al. May 2006 A1
20060113033 Bruner Jun 2006 A1
20060128247 Skoog et al. Jun 2006 A1
20060135020 Weinberg et al. Jun 2006 A1
20060147709 Mizumura et al. Jul 2006 A1
20060155094 Meckel et al. Jul 2006 A1
20060159918 Dugan et al. Jul 2006 A1
20060177656 Kolmes et al. Aug 2006 A1
20060189956 Catalan Aug 2006 A1
20060194027 Pourdeyhimi et al. Aug 2006 A1
20060194047 Gupta et al. Aug 2006 A1
20060204753 Simmonds et al. Sep 2006 A1
20060210797 Masuda et al. Sep 2006 A1
20060230731 Kalayci et al. Oct 2006 A1
20060234049 Van Dun et al. Oct 2006 A1
20060234050 Frankel Oct 2006 A1
20060234587 Horiguchi et al. Oct 2006 A1
20060263601 Wang et al. Nov 2006 A1
20060281383 Schmitt et al. Dec 2006 A1
20070009736 Chuang et al. Jan 2007 A1
20070020453 Sen et al. Jan 2007 A1
20070021021 Verdegan et al. Jan 2007 A1
20070031637 Anderson Feb 2007 A1
20070031668 Hietpas et al. Feb 2007 A1
20070039889 Ashford Feb 2007 A1
20070048523 Pollet et al. Mar 2007 A1
20070056906 Kaleem et al. Mar 2007 A1
20070062872 Parker et al. Mar 2007 A1
20070074628 Jones et al. Apr 2007 A1
20070077427 Dugan Apr 2007 A1
20070098982 Nishida et al. May 2007 A1
20070102361 Kiefer et al. May 2007 A1
20070110980 Shah May 2007 A1
20070110998 Steele et al. May 2007 A1
20070114177 Sabottke May 2007 A1
20070122613 Stevens et al. May 2007 A1
20070122614 Peng et al. May 2007 A1
20070128404 Tung et al. Jun 2007 A1
20070167096 Scott Jul 2007 A1
20070179275 Gupta et al. Aug 2007 A1
20070182040 Suzuki et al. Aug 2007 A1
20070190319 Kalayci Aug 2007 A1
20070232179 Polat et al. Oct 2007 A1
20070232180 Polat et al. Oct 2007 A1
20070243377 Nishida et al. Oct 2007 A1
20070254153 Nadkarni et al. Nov 2007 A1
20070258935 McEntire et al. Nov 2007 A1
20070259029 McEntire et al. Nov 2007 A1
20070259177 Gupta et al. Nov 2007 A1
20070264520 Wood et al. Nov 2007 A1
20070278151 Musale Dec 2007 A1
20070278152 Musale Dec 2007 A1
20080000836 Wang et al. Jan 2008 A1
20080003400 Tseng Jan 2008 A1
20080003912 Pourdeyhimi et al. Jan 2008 A1
20080009574 Huenefeld et al. Jan 2008 A1
20080009650 Sluijmers et al. Jan 2008 A1
20080011680 Partridge et al. Jan 2008 A1
20080038974 Eagles Feb 2008 A1
20080039540 Reitz Feb 2008 A1
20080064285 Morton et al. Mar 2008 A1
20080134652 Lim et al. Jun 2008 A1
20080160278 Cheng et al. Jul 2008 A1
20080160856 Chen et al. Jul 2008 A1
20080160859 Gupta et al. Jul 2008 A1
20080170982 Zhang et al. Jul 2008 A1
20080188151 Yokoi et al. Aug 2008 A1
20080207833 Bear et al. Aug 2008 A1
20080207883 Janjic et al. Aug 2008 A1
20080229672 Woo et al. Sep 2008 A1
20080233850 Woo et al. Sep 2008 A1
20080245037 Rogers et al. Oct 2008 A1
20080287026 Chakravarty et al. Nov 2008 A1
20080311815 Gupta et al. Dec 2008 A1
20090025895 Cowman Jan 2009 A1
20090036015 Nhan et al. Feb 2009 A1
20090042475 Pourdeyhimi et al. Feb 2009 A1
20090163449 Wempe Jun 2009 A1
20090249956 Chi et al. Oct 2009 A1
20090258182 Okamoto et al. Oct 2009 A1
20090274862 Nakayama et al. Nov 2009 A1
20090294435 Nhan et al. Dec 2009 A1
20090305592 Shi et al. Dec 2009 A1
20100018660 Varnell Jan 2010 A1
20100035500 Kimura et al. Feb 2010 A1
20100072126 Tsujimoto et al. Mar 2010 A1
20100133173 Inagaki Jun 2010 A1
20100136312 Inagaki Jun 2010 A1
20100143717 Sakamoto et al. Jun 2010 A1
20100173154 Shimotsu et al. Jul 2010 A1
20100180558 Ito et al. Jul 2010 A1
20100187712 Gupta et al. Jul 2010 A1
20100197027 Zhang et al. Aug 2010 A1
20100200512 Chase et al. Aug 2010 A1
20100203788 Kimura et al. Aug 2010 A1
20100247894 Beard Sep 2010 A1
20100272938 Mitchell et al. Oct 2010 A1
20100273947 Miyauchi et al. Oct 2010 A1
20100282682 Eaton et al. Nov 2010 A1
20100285101 Moore et al. Nov 2010 A1
20100291213 Berrigan et al. Nov 2010 A1
20100310921 Hayakawa et al. Dec 2010 A1
20110020590 Yoneda et al. Jan 2011 A1
20110030885 Anneaux et al. Feb 2011 A1
20110033705 Komura et al. Feb 2011 A1
20110036487 Rajala et al. Feb 2011 A1
20110039055 Fujisawa et al. Feb 2011 A1
20110039468 Baldwin, Jr. et al. Feb 2011 A1
20110040277 Rajala et al. Feb 2011 A1
20110041471 Sebastian et al. Feb 2011 A1
20110045042 Sasaki et al. Feb 2011 A1
20110045231 Kajiwara et al. Feb 2011 A1
20110045261 Sellars Feb 2011 A1
20110046461 McKenna Feb 2011 A1
20110049769 Duchoslav et al. Mar 2011 A1
20110054429 Lademann et al. Mar 2011 A1
20110056638 Rosset Mar 2011 A1
20110059669 He et al. Mar 2011 A1
20110064928 Bonneh Mar 2011 A1
20110065573 McEneany et al. Mar 2011 A1
20110065871 Nagano et al. Mar 2011 A1
20110067369 Chung et al. Mar 2011 A1
20110068507 Warren et al. Mar 2011 A1
20110074060 Angadjivand et al. Mar 2011 A1
20110076250 Belenkaya et al. Mar 2011 A1
20110084028 Stanfel et al. Apr 2011 A1
20110091761 Miller et al. Apr 2011 A1
20110094515 Duffy Apr 2011 A1
20110104493 Barnholtz et al. May 2011 A1
20110114274 Takano et al. May 2011 A1
20110117176 Klun et al. May 2011 A1
20110117353 Henshaw et al. May 2011 A1
20110117439 Yamada et al. May 2011 A1
20110123584 Seidling et al. May 2011 A1
20110124769 Moen et al. May 2011 A1
20110124835 DeWeijer et al. May 2011 A1
20110129510 Liebmann et al. Jun 2011 A1
20110130063 Matsubayashi et al. Jun 2011 A1
20110142900 Ohta et al. Jun 2011 A1
20110143110 Tsuchiya et al. Jun 2011 A1
20110147299 Stanfel et al. Jun 2011 A1
20110171535 Ohinshi et al. Jul 2011 A1
20110171890 Nakayama et al. Jul 2011 A1
20120015577 Rudman et al. Jan 2012 A1
Foreign Referenced Citations (150)
Number Date Country
1290517 Oct 1991 CA
0340763 Nov 1989 EP
0610894 Aug 1994 EP
0610897 Aug 1994 EP
0830466 Mar 1998 EP
0836656 Apr 1998 EP
0859073 Aug 1998 EP
0880909 Dec 1998 EP
0 666 344 Sep 1999 EP
1161576 Dec 2001 EP
1 243 675 Sep 2002 EP
0 645 480 Nov 2002 EP
0 961 847 Dec 2002 EP
1359632 Apr 2003 EP
0 935 682 Sep 2003 EP
1 416 077 May 2004 EP
0 905 292 Oct 2004 EP
1538686 Jun 2005 EP
1 550 746 Jul 2005 EP
1 322 802 Aug 2005 EP
1 314 808 Jan 2006 EP
1252219 Aug 2006 EP
1 325 184 Sep 2006 EP
1 715 089 Oct 2006 EP
1 319 095 Nov 2006 EP
1 731 634 Dec 2006 EP
1 149 195 Jan 2007 EP
1 412 567 Jan 2007 EP
1 404 905 Apr 2007 EP
0 842 310 Jan 2008 EP
1 894 609 Mar 2008 EP
1 903 134 Mar 2008 EP
1 938 883 Jul 2008 EP
2082082 Jul 2009 EP
1 516 079 Dec 2009 EP
2 135 984 Dec 2009 EP
1 224 900 Jun 2010 EP
2 243 872 Oct 2010 EP
2283796 Feb 2011 EP
2287374 Feb 2011 EP
1 620 506 Mar 2011 EP
0847263 Mar 2011 EP
2292309 Mar 2011 EP
1474555 Apr 2011 EP
2308579 Apr 2011 EP
2311542 Apr 2011 EP
2311543 Apr 2011 EP
2654674 May 1991 FR
1073640 Jun 1967 GB
52-066719 Jun 1977 JP
58-83046 May 1983 JP
58174625 Oct 1983 JP
58-220818 Dec 1983 JP
61-047822 Mar 1986 JP
61-296120 Dec 1986 JP
62-078213 Apr 1987 JP
63-159523 Jul 1988 JP
S63-227898 Sep 1988 JP
1162825 Jun 1989 JP
1-229899 Sep 1989 JP
1-272820 Oct 1989 JP
1-289838 Nov 1989 JP
02-026920 Jan 1990 JP
2-210092 Aug 1990 JP
3-16378 Mar 1991 JP
3-180587 Aug 1991 JP
04-057918 Feb 1992 JP
04-327209 Nov 1992 JP
4327209 Nov 1992 JP
5-18334 Mar 1993 JP
05-263316 Oct 1993 JP
1993-263316 Oct 1993 JP
5321106 Dec 1993 JP
6-002221 Jan 1994 JP
6-25396 Feb 1994 JP
9-77963 Mar 1997 JP
9-100397 Apr 1997 JP
9-249742 Sep 1997 JP
09-291472 Nov 1997 JP
09-310230 Dec 1997 JP
2000-95850 Apr 2000 JP
3131100 Jan 2001 JP
31131100 Jan 2001 JP
2001-123335 May 2001 JP
2003-253555 Sep 2003 JP
2004-137319 May 2004 JP
2004-137418 May 2004 JP
2004137418 May 2004 JP
2005-002510 Jan 2005 JP
2005-154450 Jun 2005 JP
2006233365 Sep 2006 JP
2010255173 Nov 2010 JP
4648815 Mar 2011 JP
2001-0044145 Jun 2001 KR
531939 Nov 2005 KR
2011-031744 Mar 2011 KR
2011-031746 Mar 2011 KR
2414950 Mar 2011 RU
2414960 Mar 2011 RU
230212 Apr 2005 TW
WO 9307197 Apr 1993 WO
WO 9424218 Oct 1994 WO
WO 9503172 Feb 1995 WO
WO 9947621 Sep 1999 WO
WO 9948668 Sep 1999 WO
WO 0166666 Sep 2001 WO
WO 02060497 Aug 2002 WO
WO 03069038 Aug 2003 WO
WO 2004067818 Aug 2004 WO
WO 2004099314 Nov 2004 WO
WO 2004113598 Dec 2004 WO
WO 2005066403 Jul 2005 WO
WO 2005103354 Nov 2005 WO
WO 2005103357 Nov 2005 WO
WO 2006001739 Jan 2006 WO
WO 2006052732 May 2006 WO
WO 2006098851 Sep 2006 WO
WO 2006107695 Oct 2006 WO
WO 2007089423 Aug 2007 WO
WO 2007112443 Oct 2007 WO
WO 2008028134 Mar 2008 WO
WO 2008085332 Jul 2008 WO
WO 2009024836 Feb 2009 WO
WO 2009051283 Apr 2009 WO
WO 2009076401 Jun 2009 WO
WO 2009088564 Jul 2009 WO
WO 2009140381 Nov 2009 WO
WO 2009152349 Dec 2009 WO
WO 2010114820 Oct 2010 WO
WO 2010117612 Oct 2010 WO
WO 2010125239 Nov 2010 WO
WO 2010140853 Dec 2010 WO
WO 2010146240 Dec 2010 WO
WO 2011015709 Feb 2011 WO
WO 2011018459 Feb 2011 WO
WO 2011008481 Mar 2011 WO
WO 2011027732 Mar 2011 WO
WO 2011028661 Mar 2011 WO
WO 2011034523 Mar 2011 WO
WO 2011047966 Apr 2011 WO
WO 2011049831 Apr 2011 WO
WO 2011049927 Apr 2011 WO
WO 2011052173 May 2011 WO
WO 2011054932 May 2011 WO
WO 2011062761 May 2011 WO
WO 2011063372 May 2011 WO
WO 2011066224 Jun 2011 WO
WO 2011070233 Jun 2011 WO
2011104427 Sep 2011 WO
2011157892 Dec 2011 WO
Non-Patent Literature Citations (178)
Entry
New copending U.S. Appl. No. 13/053,615, filed Mar. 22, 2011, Rakesh Kumar Gupta et al.
USPTO Notice of Allowance dated Apr. 4, 2011 for copending U.S. Appl. No. 12/199,304.
USPTO Office Action dated Mar. 18, 2011 for copending U.S. Appl. No. 11/648,953.
USPTO Office Action dated Apr. 6, 2011 for copending U.S. Appl. No. 12/975,487.
USPTO Office Action dated Apr. 4, 2011 for copending U.S. Appl. No. 12/981,960.
USPTO Office Action dated Apr. 6, 2011 for copending U.S. Appl. No. 12/975,482.
USPTO Office Action dated Jun. 7, 2011 for copending U.S. Appl. No. 12/982,001.
USPTO Office Action dated Jun. 9, 2011 for copending U.S. Appl. No. 12/975,459.
USPTO Office Action dated May 27, 2011 for copending U.S. Appl. No. 12/975,452.
USPTO Office Action dated Jun. 23, 2011 for copending U.S. Appl. No. 12/966,487.
USPTO Office Action dated Jun. 23, 2011 for copending U.S. Appl. No. 12/966,502.
USPTO Office Action dated Jun 23, 2011 for copending U.S. Appl. No. 12/975,443.
Office Action with Mail Date of Jan. 25, 2008 for related U.S. Appl. No. 11/343,955.
PCT International Search Report dated Feb. 4, 2008 for International Application No. PCT/US2007/001082.
U.S. Appl. No. 11/204,868, filed Aug. 16, 2005, William Alston Haile, et al.; now published as U.S. 2005-0282008 referenced above.
U.S. Appl. No. 11/343,955, filed Jan. 31, 2006, Rakesh Kumar Gupta, et al.; now published as 2007-0179275 referenced above.
U.S. Appl. No. 11/344,320, filed Jan. 31, 2006, Rakesh Kumar Gupta, et al.; now published as U.S. 2006-0194047 referenced above.
U.S. Appl. No. 11/648,953, filed Jan. 3, 2007, Rakesh Kumar Gupta, et al.; now published as U.S. 2008-0160859 referenced above.
U.S. Appl. No. 08/550,042, filed Oct. 30, 1995, Michael C. Cook.
Office Action with Mail Date of Oct. 10, 2008 for related U.S. Appl. No. 11/343,955.
PCT International Search Report dated Nov. 6, 2008 for International Application No. PCT/US2007/025661.
PCT International Search Report dated Jul. 26, 2007 for International Application No. PCT/US2007/001083.
Office Action with Mail Date of Mar. 30, 2009 for related U.S. Appl. No. 11/204,868.
Office Action with Mail Date of Mar. 26, 2009 for related U.S. Appl. No. 11/344,320.
Notice of Allowance; Date Mailed Mar. 9, 2009; for U.S. Appl. No. 11/343,955.
U.S. Appl. No. 61/172,257, filed Apr. 24, 2009, Rakesh Kumar Gupta, et al.
PCT International Search Report dated Jul. 3, 2009 for International Application No. PCT/US2009/001717.
USPTO Notice of Allowance dated Nov. 9, 2009 for copending U.S. Appl. No. 11/648,955.
USPTO Office Action dated Dec. 24, 2009 for copending U.S. Appl. No. 11/344,320.
USPTO Office Action dated Dec. 22, 2009 for copending U.S. Appl. No. 11/204,868.
USPTO Notice of Allowance dated Jun. 9, 2010 for copending U.S. Appl. No. 11/344,320.
USPTO Notice of Allowance dated Jun. 9, 2010 for copending U.S. Appl. No. 11/204,868.
USPTO Office Action dated Aug. 6, 2010 for copending U.S. Appl. No. 11/648,953.
USPTO Office Action dated Dec. 21, 2004 for U.S. Appl. No. 10/850,548.
USPTO Notice of Allowance dated Jun. 8, 2005 for U.S. Appl. No. 10/850,548.
PCT International Search Report dated Feb. 7, 2005 for International Application No. PCT/US2004/018682.
Copending U.S. Appl. No. 12/765,461, filed Apr. 22, 2010, Rakesh Kumar Gupta, et al.
Smook, G.A., “Handbook for Pulp and Paper Technologist”, Angus Wilde Publications, 2nd Ed., 1992, pp. 194-195, 211-212.
USPTO Notice of Allowance dated Aug. 7, 2009 for U.S. Appl. No. 11/343,955.
PCT International Search Report dated Dec. 30, 2009 for International Application No. PCT/US2007/025770.
Ke Qinfei, et al., “Non-woven Science”, Donghau University Press, Sep. 2004, Catalog, p. 115-132 (unavailable).
USPTO Office Action dated Jan. 25, 2008 for U.S. Appl. No. 11/343,955.
USPTO Notice of Allowance dated Nov. 9, 2009 for U.S. Appl. No. 11/648,955.
USPTO Office Action dated Sep. 27, 2010 for U.S. Appl. No. 12/199,304.
USPTO Notice of Allowance dated Sep. 30, 2010 for U.S. Appl. No. 11/344,320.
USPTO Notice of Allowance dated Oct. 14, 2010 for U.S. Appl. No. 11/204,868.
Copending U.S. Appl. No. 12/909,574, filed Oct. 21, 2010, Rakesh Kumar Gupta, et al.
Copending U.S. Appl. No. 12/966,483, filed Dec. 13, 2010, William Alston Haile, et al.
Copending U.S. Appl. No. 12/966,487, filed Dec. 13, 2010, William Alston Haile, et al.
Copending U.S. Appl. No. 12/966,494, filed Dec. 13, 2010, William Alston Haile, et al.
Copending U.S. Appl. No. 12/966,502, filed Dec. 13, 2010, William Alston Haile, et al.
Copending U.S. Appl. No. 12/966,507, filed Dec. 13, 2010, William Alston Haile, et al.
Copending U.S. Appl. No. 12/966,512, filed Dec. 13, 2010, William Alston Haile, et al.
Copending U.S. Appl. No. 12/966,518, filed Dec. 13, 2010, William Alston Haile, et al.
Copending U.S. Appl. No. 12/975,443, filed Dec. 22, 2010, Rakesh Kumar Gupta, et al.
Copending U.S. Appl. No. 12/975,447, filed Dec. 22, 2010, Rakesh Kumar Gupta, et al.
Copending U.S. Appl. No. 12/975,450, filed Dec. 22, 2010, Rakesh Kumar Gupta, et al.
Copending U.S. Appl. No. 12/975,452, filed Dec. 22, 2010, Rakesh Kumar Gupta, et al.
Copending U.S. Appl. No. 12/975,456, filed Dec. 22, 2010, Rakesh Kumar Gupta, et al.
Copending U.S. Appl. No. 12/975,459, filed Dec. 22, 2010, Rakesh Kumar Gupta, et al.
Copending U.S. Appl. No. 12/975,463, filed Dec. 22, 2010, Rakesh Kumar Gupta, et al.
Copending U.S. Appl. No. 12/975,482, filed Dec. 22, 2010, Rakesh Kumar Gupta, et al.
Copending U.S. Appl. No. 12/975,484, filed Dec. 22, 2010, Rakesh Kumar Gupta, et al.
Coons, R., “Eastman Chemical Core Focus Delivers Value,” Chemical Week, Aug. 15/22, 2011, pp. 19-22.
USPTO Office Action dated Sep. 15, 2011 for copending U.S. Appl. No. 11/648,953.
USPTO Office Action dated Sep. 8, 2011 for copending U.S. Appl. No. 12/966,494.
USPTO Office Action dated Sep. 26, 2011 for copending U.S. Appl. No. 12/966,507.
USPTO Office Action dated Sep. 1, 2011 for copending U.S. Appl. No. 12/975,450.
USPTO Office Action dated Aug. 24, 2011 for copending U.S. Appl. No. 12/975,456.
USPTO Office Action dated Sep. 27, 2011 for copending U.S. Appl. No. 12/975,463.
USPTO Office Action dated Jan. 25, 2012 for copending U.S. Appl. No. 12/981,982.
USPTO Notice of Allowance dated Jan. 9, 2012 for copending U.S. Appl. No. 12/975,482.
New copending provisional U.S. Appl. No. 13/352,362, filed Jan. 18, 2012.
USPTO Notice of Allowance dated Feb. 7, 2012 for copending U.S. Appl. No. 12/975,459.
USPTO Notice of Allowance dated Jul. 18, 2011 for copending U.S. Appl. No. 12/199,304.
USPTO Office Action dated Aug. 10, 2011 for copending U.S. Appl. No. 12/966,512.
USPTO Office Action dated Nov. 10, 2011 for copending U.S. Appl. No. 12/981,950.
USPTO Notice of Allowance dated Dec. 23, 2011 for copending U.S. Appl. No. 12/975,452.
USPTO Notice of Allowance dated Dec. 8, 2011 for copending U.S. Appl. No. 12/981,960.
USPTO Notice of Allowance dated Dec. 13, 2011 for copending U.S. Appl. No. 12/966,487.
USPTO Notice of Allowance dated Dec. 12, 2011 for copending U.S. Appl. No. 12/966,502.
USPTO Notice of Allowance dated Dec. 9, 2011 for copending U.S. Appl. No. 12/966,512.
USPTO Office Action dated Nov. 10, 2011 for copending U.S. Appl. No. 12/975,484.
New copending U.S. Appl. No. 13/273,692, filed Oct. 14, 2011, Rakesh Kumar Gupta et al.
New copending U.S. Appl. No. 13/273,648, filed Oct. 14, 2011, Rakesh Kumar Gupta et al.
New copending U.S. Appl. No. 13/273,710, filed Oct. 14, 2011, Rakesh Kumar Gupta et al.
New copending U.S. Appl. No. 13/273,720, filed Oct. 14, 2011, Rakesh Kumar Gupta et al.
New copending U.S. Appl. No. 13/273,929, filed Oct. 14, 2011, Rakesh Kumar Gupta et al.
New copending U.S. Appl. No. 13/273,937, filed Oct. 14, 2011, Rakesh Kumar Gupta et al.
New copending U.S. Appl. No. 13/273,727, filed Oct. 14, 2011, Rakesh Kumar Gupta et al.
New copending U.S. Appl. No. 13/273,737, filed Oct. 14, 2011, Rakesh Kumar Gupta et al.
New copending U.S. Appl. No. 13/273,745, filed Oct. 14, 2011, Rakesh Kumar Gupta et al.
New copending U.S. Appl. No. 13/273,749, filed Oct. 14, 2011, Rakesh Kumar Gupta et al.
USPTO Office Action dated Aug. 14, 2012 for U.S. Appl. No. 12/199,304.
USPTO Notice of Allowance dated Jul. 27, 2012 for U.S. Appl. No. 12/981,982.
USPTO Notice of Allowance dated Jul. 19, 2012 for U.S. Appl. No. 12/981,950.
USPTO Notice of Allowance dated Aug. 10, 2012 for U.S. Appl. No. 12/975,487.
USPTO Notice of Allowance dated Jul. 31, 2012 for U.S. Appl. No. 12/975,456.
Office Action with Mail Date of Dec. 22, 2009 for copending U.S. Appl. No. 11/204,868.
Office Action with Mail Date of Mar. 2, 2012 for copending U.S. Appl. No. 12/966,518.
Office Action with Mail Date of Nov. 10, 2011 for copending U.S. Appl. No. 12/975,447.
USPTO Notice of Allowance dated Feb. 21, 2012 for copending U.S. Appl. No. 12/975,450.
USPTO Notice of Allowance dated Feb. 17, 2012 for copending U.S. Appl. No. 12/982,001.
USPTO Notice of Allowance dated Feb. 23, 2012 for copending U.S. Appl. No. 13/053,615.
U.S. Appl. No. 11/648,955, filed Jan. 3, 2007, Rakesh Kumar Gupta, et al.
PCT International Search Report dated Feb. 4, 2008 for International Application No. PCT/US2007/025770.
Database WPI, Week 200450, Thomson Scientific, London, GB; AN 2004/520211 XP002639794 & JP 20041137418A May 13, 2004 -abstract-.
USPTO Office Action dated Mar. 2, 2012 for copending U.S. Appl. No. 12/966,518.
USPTO Notice of Allowance dated Apr. 13, 2012 for copending U.S. Appl. No. 12/966,487.
UsPTO Office Action dated Apr. 19, 2012 for copending U.S. Appl. No. 12/975,456.
USPTO Notice of Allowance dated Apr. 18, 2012 for copending U.S. Appl. No. 12/966,494.
USPTO Notice of Allowance dated Apr. 18, 2012 for copending U.S. Appl. No. 12/975,484.
USPTO Office Action dated Apr. 19, 2012 for copending U.S. Appl. No. 12/975,463.
USPTO Office Action dated Mar. 16, 2012 for copending U.S. Appl. No. 12/966,483.
USPTO Notice of Allowance dated Apr. 2, 2012 for copending U.S. Appl. No. 12/966,502.
USPTO Notice of Allowance dated Mar. 21, 2012 for copending U.S. Appl. No. 12/966,512.
USPTO Notice of Allowance dated Apr. 2, 2012 for copending U.S. Appl. No. 12/975,452.
USPTO Notice of Allowance dated Mar. 15, 2012 for copending U.S. Appl. No. 12/981,960.
USPTO Office Action dated Apr. 23, 2012 for copending U.S. Appl. No. 12/966,507.
USPTO Office Action dated May 3, 2012 for copending U.S. Appl. No. 12/765,461.
USPTO Office Action dated May 21, 2012 for copending U.S. Appl. No. 12/981,982.
USPTO Office Action dated May 10, 2012 for copending U.S. Appl. No. 12/966,521.
USPTO Notice of Allowance dated Jan. 3, 2012 for copending U.S. Appl. No. 12/975,487.
Provisional U.S. Appl. No. 61/405,306, filed Oct. 21, 2010.
Provisional U.S. Appl. No. 61/405,312, filed Oct. 21, 2010.
Investigation of the utility of islands-in-the-stream bicomponent fiber technology in the spunbound process. Fedorova, Dec. 2006, pp. 22-23 & 74, retrieved from the internet on Mar. 20, 2012 <URL: http://repository.lib.ncsu.edu/ir/bitstream/1840.16/5145/1/etd.pdf>, 85200W002 ISR.
Keith, James M., “Dispersions of Synthetic Fibers in Wet-Lay Nonwovens”, MiniFIBERS, Inc., originally published in the Tappi Journal, vol. 77, No. 6, Jun. 1994, 85200W003 ISR.
USPTO Office Action dated Jan. 30, 2012 for copending U.S. Appl. No. 12/978,443.
USPTO Office Action dated Aug. 31, 2011 for copending U.S. Appl. No. 13/053,615.
USPTO Notice of Allowance dated Jun. 4, 2012 for copending U.S. Appl. No. 12/981,960.
USPTO Office Action dated Jun. 7, 2012 for copending U.S. Appl. No. 12/966,487.
USPTO Notice of Allowance dated Jun. 11, 2012 for copending U.S. Appl. No. 12/966,512.
USPTO Notice of Allowance dated Jun. 13, 2012 for copending U.S. Appl. No. 12/966,502.
USPTO Notice of Allowance dated Jun. 29, 2012 for copending U.S. Appl. No. 12/981,950.
USPTO Notice of Allowance dated Jul. 3, 2012 for copending U.S. Appl. No. 12/974,452.
USPTO Notice of Allowance dated Jul. 6, 2012 for copending U.S. Appl. No. 12/975,456.
New copending U.S. Appl. No. 13/433,854, filed Mar. 29, 2012, Clark et al.
New copending U.S. Appl. No. 13/433,812, filed Mar. 29, 2012, Clark et al.
USPTO Notice of Allowance dated Jul. 27, 2012 for copending U.S. Appl. No. 12/981,982.
Investigation of the utility of islands-in-the-stream bicomponent fiber technology in the spunbound process. Fedorova, Dec. 2006 (retrieved on Mar. 20, 2012 from internet) pp. 22-23, 74 <URL: http://repository.lib.ncsu.edu/ir/bitstream/1840.16/5145/1/etd.pdf>.
“Choosing the Proper Short Cut Fiber”, technical data sheet, MiniFibers, Inc., [online] pp. 1-2, 2006, [retrieved on Feb. 15, 2006], Retrieved from the Inernet: <URL: htts://www.minifibers.com/Literature/choosing—fiber.htm>.
Keith, James M., “Dispersions fo Synthetic Fibers in Wet-Lay Nonwovens”. MiniFIBERS, Inc., originally published in the Tappi Journal, vol. 77, No. 6, Jun. 1994, entire document.
Database WPI Thomson Scientific, London, GB AN2004/520211 XP002639794 & JP 2004/137418 Dated May 13, 2004—abstract.
USPTO Office Action dated Jul. 5, 2012 for copending U.S. Appl. No. 12/966,507.
USPTO Office Action dated Oct. 4, 2012 for copending U.S. Appl. No. 13/273,745.
USPTO Office Action dated Aug. 27, 2012 for copending U.S. Appl. No. 12/975,443.
USPTO Office Action dated Aug. 28, 2012 for copending U.S. Appl. No. 12/975,447.
USPTO Notice of Allowance dated Oct. 11, 2012 for copending U.S. Appl. No. 12/975,487.
USPTO Notice of Allowance dated Oct. 22, 2012 for copending U.S. Appl. No. 12/966,518.
USPTO Notice of Allowance dated Nov. 2, 2012 for copending U.S. Appl. No. 12/966,507.
USPTO Office Action dated Nov. 2, 2012 for copending U.S. Appl. No. 13/273,692.
USPTO Notice of Allowance dated Dec. 10, 2012 for copending U.S. Appl. No. 12/966,521.
New co-pending U.S. Appl. No. 13/687,466, filed Nov. 28, 2012.
New co-pending U.S. Appl. No. 13/687,472, filed Nov. 28, 2012.
New co-pending U.S. Appl. No. 13/687,478, filed Nov. 28, 2012.
New co-pending U.S. Appl. No. 13/687,493, filed Nov. 28, 2012.
New co-pending U.S. Appl. No. 13/687,505, filed Nov. 28, 2012.
USPTO Office Action dated Dec. 4, 2012 for copending U.S. Appl. No. 13/273,749.
PCT International Search Report dated Feb. 28, 2012 for Application No. PCT/US2011/056990.
PCT International Search Report dated Feb. 28, 2012 for Application No. PCT/US2011/056994.
PCT International Search Report dated Feb. 14, 2012 for Application No. PCT/US2011/056989.
PCT International Search Report dated Feb. 28, 2012 for Application No. PCT/US2011/056995.
PCT International Search Report dated Feb. 28, 2012 for Application No. PCT/US2011/056991.
PCT International Search Report dated Feb. 28, 2012 for Application No. PCT/US2011/057002.
Provisional U.S. Appl. No. 61/405,306, filed Oct. 21, 2010, Rakesh Kumar Gupta, et al.
Provisional U.S. Appl. No. 61/405,312, filed Oct. 21, 2010, Rakesh Kumar Gupta, et al.
Provisional U.S. Appl. No. 61/588,744, filed Nov. 11, 2011, Clark, et al.
Provisional U.S. Appl. No. 61/592,854, filed Jan. 31, 2012, Parker, et al.
Provisional U.S. Appl. No. 61/592,867, filed Jan. 31, 2010, Parker, et al.
Provisional U.S. Appl. No. 61/592,876, filed Jan. 31, 2010, Parker, et al.
Provisional U.S. Appl. No. 61/592,917, filed Jan. 31, 2010, Parker, et al.
Provisional U.S. Appl. No. 61/592,974, filed Jan. 31, 2010, Parker, et al.
USPTO Notice of Allowance dated Jan. 8, 2013 for copending U.S. Appl. No. 12/966,483.
USPTO Notice of Allowance dated Jan. 10, 2013 for copending U.S. Appl. No. 12/975,447.
USPTO Notice of Allowance dated Jan. 15, 2013 for copending U.S. Appl. No. 12/975,463.
PCT International Search Report dated Jan. 23, 2013 for Application No. PCT/US2012/064272.
USPTO Office Action dated Nov. 20, 2012 for copending U.S. Appl. No. 13/273,710.
USPTO Office Action dated Nov. 26, 2012 for copending U.S. Appl. No. 13/273,648.
Related Publications (1)
Number Date Country
20120058163 A1 Mar 2012 US
Divisions (1)
Number Date Country
Parent 10850548 May 2004 US
Child 11204868 US
Continuations (1)
Number Date Country
Parent 11204868 Aug 2005 US
Child 12966521 US
Continuation in Parts (1)
Number Date Country
Parent 10465698 Jun 2003 US
Child 10850548 US