Water soluble biogum compositions and hydrosols prepared therefrom

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to novel compositions of matter comprised of a water soluble biogum, to process for the formulation thereof, and to the utilization of such compositions in the preparation of various hydrosols therefrom. More especially, this invention relates to compositions of matter adapted for enhanced, complete and effective dissolution in an aqueous medium, comprised of a biogum of a class of heteropolysaccharides of microbial origin, and more particularly comprised of a Xanthan gum.
By "biogum" or "heteropolysaccharide of microbial origin", there is intended an exocellular linear polymer of high molecular weight, in excess of one million, obtained by the fermentation of a carbohydrate by the action of bacteria of the genus Xanthomonas or Arthrobacter, or of fungi of the genus Sclerotium.
And "Xanthan gum" is intended to connote a polysaccharide produced by the fermentation of a carbohydrate with bacteria of the genus Xanthomonas.
Xanthan gum is a heteropolysaccharide having a molecular weight in excess of 10.sup.6. It contains D-glucose, D-mannose and D-glucuronate in the molar ratios of 2.8/2.0/2.0. It is partially acetylated with approximately 4.7% of acetyl radicals. It additionally contains approximately 3% of pyruvate radicals attached to a single lateral chain of the D-glucopyranosyl matrix as a ketal.
Finally, the term "sol" is intended to connote a colloidal solution of the biogum.
2. Description of the Prior Art
Certain of the biogums, by virtue of their viscosity and rheology, are useful as thickening agents for aqueous systems in numerous fields of application. Thus, Xanthan gum, for example, has to date been employed in fields as varied as construction, paints, textiles, cosmetics, petroleum exploitation, paper, the food industry, water treatment, phytosanitation, etc.
For many applications, it is necessary to convert the biogum to the form of an aqueous solution thereof. However, it is a disadvantage of most of the water soluble gums that they are quite difficult to solubilize. In attempting the very rapid hydration thereof, the particles or grains in contact with water are surrounded with a thin gelatinized film and they agglomerate. These agglomerates or floccules, surrounded by partially swollen polymers on the surface thereof, disintegrate and dissolve only with difficulty.
It has been proposed to improve the dispersibility and solubility of Xanthan gum by chemical reaction with glyoxal (French Patent No. 2,371,462).
This prior art process, however, requires a special treatment of the gum. Thus, serious need exists in this art for improved means to facilitate the dissolution of the otherwise difficultly dissolved/dispersed biogums.
SUMMARY OF THE INVENTION
Accordingly, a major object of the present invention is the provision of improved means for accelerating the dispersion of biogums in water and to increase the rate of dissolution thereof and thereby increase the speed of obtainment of high viscosity sols therefrom, by compounding certain additives therewith, while at the same time preserving the rheological properties of the biogum.
Another object of the invention is the provision of the subject biogums in a readily manipulated powder form, which dissolves well and swells rapidly in water.
Yet another object of the invention is to provide for the aforesaid desiderata by presenting the biogum in the form of powdery compositions having the highest content of the active biogum substance.
Briefly, the present invention features compositions of matter comprised of water soluble biogums, which compositions are adapted to facilitate dispersion and dissolution of the biogum component by having incorporated therein, or also being comprised of, an additive adapted to introduce a certain content of water thereto, or "water donor", or an additive adapted to itself sorb and retain water from an external aqueous environment.
DETAILED DESCRIPTION OF THE INVENTION
More particularly according to this invention, the subject biogums are produced by fermenting a carbohydrate by the action of bacteria of the genus Xanthomonas or Arthrobacter, or by fungi belonging to the genus Sclerotium.
Representative species of the bacteria or fungi that may be used for the production of these biogum heterosaccharides are, for example: Xanthomonas begoniae, Xanthomonas campestris, Xanthomonas carotea, Xanthomonas hederae, Xanthomonas incanae, Xanthomonas malvacearum, Xanthamonas papavericola, Xanthomonas phaseoli, Xanthomonas pisi, Xanthomonas vasculorum, Xanthomonas vesicatoria, Xanthomonas vitians, Xanthomonas pelargonii, Arthrobacter stabilis, Arthrobacter viscosus, Sclerotium glucanicum, Sclerotium rolfsii, and the like.
The species particularly suitable for the aforesaid type of fermentation are Xanthomonas begoniae, Xanthomonas campestris, Xanthomonas incanae and Xanthomonas pisi.
The species Xanthomonas campestris is especially suitable for the production of the subject biogums.
And it is of course possible to ferment a very wide variety of carbohydrates with the microorganisms belonging to the aforenoted genera in order to produce the heteropolysaccharide biogums useful in the compositions of the invention. Exemplary carbohydrates that may be employed include glucose, sucrose, fructose, maltose, lactose, soluble starch, corn starch, potato starch, and the like. The fermentation of the carbohydrate is typically effected in an aqueous medium containing up to 60 g/l glucide. It is also known that the fermentation medium may additionally comprise a source of phosphorus, a source of magnesium which is an enzyme activator, and a source of nitrogen which usually consists of "distillery solubles" (U.S. Pat. No. 3,000,790), bran or whole grain cereals, such as sorghum, soy beans or corn (U.S. Pat. No. 3,271,267), "corn steep" (U.S. Pat. No. 3,355,447) or inorganic nitrogen compounds, such as ammonium nitrate (U.S. Pat. No. 3,391,060) or ammonium phosphate (French Application No. 76/05933).
It too may be advantageous, prior to use, to subject the fermented mash to heating at a temperature ranging from 80.degree. to 130.degree. C. for from approximately 10 min to approximately one hour.
The heteropolysaccharide is separated from the fermenting mash and is used in the powder form. The separation of the heteropolysaccharide from the mash, possibly preheated as above-indicated, may be effected by conventional methods, for example, by precipitating it by addition to said mash of a lower alcohol, such as methanol, ethanol, isopropanol, tertiary butanol or acetone, or a mixture of such precipitating agents. Once precipitated, the heteropolysaccharide is separated, washed with the liquid of precipitation, and then dried and ground.
The heteropolysaccharide may also be subjected to subsequent purification operations; for this purpose, the known methods of the prior art may be used. Same consist, for example, of exposing the fermented mash, or the aqueous gel reconstituted from the heteropolysaccharide extracted from the mash, to centrifuging or filtration using diatomaceous earth, to the action of enzymes of protease type (French Pat. No. 2,264,077), or to sodium hydroxide (U.S. Pat. No. 3,729,460).
Preferably, that Xanthan gum produced by the fermentation of a carbohydrate with a pure culture of Xanthomonas campestris, is used consistent herewith; said biogum being extracted with isopropanol, and then dried and ground.
The water donor component of the subject compositions, or material providing the required fraction of water, is comprised of either bound water, or sorbed water, or water of crystallization. The first category of materials includes hydrated silica and alumina, either alone or in admixture, in a natural or synthetic form.
Thus, finely precipitated silica, in the form of fine particles having a large surface area, may be used. More particularly, silica particles having a BET surface ranging from 200 to 400 m.sup.2 /g are employed, [the BET surface is determined by the method of Brunauer-Emmett-Teller, described in Journal of the American Chemical Society, 60, page 309 (February 1938)]. The ultimate particle size of the silica varies from 200 to 800 .ANG..
Further, hydrated silica gels are also suitable for use in the invention, in particular the following three principal types of gels: gels having a BET surface of 750-800 m.sup.2 /g, a pore volume of 0.37-0.40 cm.sup.3 /g, and an average particle diameter of 22-26 .ANG.; gels having a BET surface of 300-350 m.sup.2 /g, a pore volume of 0.9-1.1 cm.sup.3 /g, and an average particle diameter of 120-160 .ANG.; and gels having a BET surface of 100-200 m.sup.2 /g, a pore volume of 1.4-2.0 cm.sup.3 /g, and an average particle diameter of 180-220 .ANG..
Also useful consistent herewith are the dehydrated silica gels having a BET surface of 10 to 500 m.sup.2 /g and a pore volume of 0.5 to 1.1 cm.sup.3 /g, with an average pore diameter ranging from 30 to 3,000 .ANG., preferably 600 to 3,000 .ANG.. An autoclave treatment, described in French Pat. No. 2,093,176, enables providing the silica with the surface desired.
The water donor may also be an alumina hydrate in either of two states of hydration: Al.sub.2 O.sub.3.3H.sub.2 O and Al.sub.2 O.sub.3.H.sub.2 O. Same may be employed in their natural form: hydrargillite or gibbsite, bayerite, nordstrandite, boehmite, diaspore; or in their synthetic form. Dried alumina gels of the boehmite type, having a surface of 200 to 400 m.sup.2 /g and pore diameters of 50 to 100 .ANG., or various commercial products, in particular the .alpha.-trihydrate obtained via the Bayer process and having spheroidal particles with dimensions of 20 to 150 microns, too may be used.
All of the aforesaid compounds are products per se known to the art and are described, for example, in the Kirk-Othmar encyclopedia, Encyclopedia Of Chemical Technology, Volume 2.
Also useful are the hydrated silica aluminates in the form of argillas, or natural or synthetic zeolites.
Exemplary of the argillas suitable for use according to this invention, those belonging to the following groups are representative:
(i) Kaolin type: kaolinite, dickite, nakrite, anauxite, halloysite, endelitte;
(ii) Serpentine type: chrysolite, amesite, cronstedite, chamosite, garnierite;
(iii) Montmorillonite type: montmorillonite (bentonite), beidellite, nontronite, hectorite, saponite, sauconite;
(iv) Vermiculite or chlorite type; and
(v) Attapulgite or sepiolite.
Representative natural zeolites are analcime, harmotome, phillipsite, gismondine, laumontite, erionite, offretite, levynite, faujasite, chabazite, gmelinite, natrolite, scolecite, mesolite, thomsonite, edingtonite, mordenite, ferrierite, epistilbite, heulandite, clinoptilolite, stilbite, brewsterite. Preferably, faujasite or mordenite is utilized.
Exemplary of the synthetic zeolites, the following commercial zeolites are representative: zeolites of type A, X, Y, L and those reproducing the structure of mordenite, chabazite and erionite.
The zeolites X and Y typically have a BET surface of 800 m.sup.2 /g and a pore volume, respectively, of 0.36 cm.sup.3 /g 0.34 cm.sup.3 /g.
The zeolites of type A, particularly of type 4A, have a BET surface of less than 10 m.sup.2 /g and a pore volume of 0.30 cm.sup.3 /g.
For a detailed description of hydrated silica aluminates, reference is made to the literature: for example, for the argillas, to Kirk-Othmar, Encyclopedia Of Chemical Technology, Volume 5, and for the natural and synthetic zeolites, to D. W. Breck, Zeolite Molecular Sieves, A. Wiley-Interscience Publications (1974).
Also intended as water donors or materials incorporating water into the subject compositions are the hydrates of various inorganic or organic metal salts, in particular the alkali or alkaline earth metal salts.
More specifically, hydrates of the following salts or compounds, used either alone or in admixture or combination, may be used: carbonates, halides, nitrates, phosphates, silicates, sulfates, as well as the acetates, citrates, lactates, laurates and tartrates of sodium, potassium, calcium, magnesium, and the like.
As specific examples of the foregoing, the following are representative:
(1) Sodium acetate trihydrate: NaC.sub.2 H.sub.3 O.sub.2.3H.sub.2 O
(2) Sodium carbonate heptahydrate: Na.sub.2 CO.sub.3.7H.sub.2 O
(3) Sodium citrate pentahydrate: Na.sub.3 C.sub.6 H.sub.5 O.sub.7.5.5H.sub.2 O
(4) Sodium orthophosphate dodecahydrate: Na.sub.3 PO.sub.4.12H.sub.2 O
(5) Magnesium and sodium tartrate decahydrate: Na.sub.2 Mg(C.sub.4 H.sub.4 O.sub.6).sub.2.10H.sub.2 O
(6) Sodium sulfate heptahydrate: Na.sub.2 SO.sub.4.7H.sub.2 O
(7) Sodium sulfate decahydrate: Na.sub.2 SO.sub.4.10H.sub.2 O
(8) Potassium and magnesium chloride hexahydrate: KCl.MgCl.sub.2.6H.sub.2 O
(9) Potassium and magnesium sulfate hexahydrate: K.sub.2 SO.sub.4.MgSO.sub.4.6H.sub.2 O
(10) Calcium acetate dihydrate: Ca(C.sub.2 H.sub.3 O.sub.2).sub.2. 2H.sub.2 O
(11) Calcium carbonate hexahydrate: CaCO.sub.3.6H.sub.2 O
(12) Calcium chloride hexahydrate: CaCl.sub.2.6H.sub.2 O
(13) Calcium citrate tetrahydrate: Ca.sub.3 (C.sub.6 H.sub.5 O.sub.7).sub.2.4H.sub.2 O
(14) Calcium lactate pentahydrate: Ca(C.sub.3 H.sub.5 O.sub.3).sub.2.5H.sub.2 O
(15) Calcium nitrate trihydrate: Ca(NO.sub.3).sub.2. 3H.sub.2 O
(16) Calcium nitrate tetrahydrate: Ca(NO.sub.3).sub.2.4H.sub.2 O
(17) Calcium sulfate dihydrate: CaSO.sub.4.2H.sub.2 O
(18) Calcium tartrate tetrahydrate: CaC.sub.4 H.sub.4 O.sub.6.4H.sub.2 O
(19) Magnesium acetate tetrahydrate: Mg(C.sub.2 H.sub.3 O.sub.3).sub.2.4H.sub.2 O
(20) Magnesium chloride hexahydrate: MgCl.sub.2.6H.sub.2 O
(21) Magnesium carbonate pentahydrate: MgCO.sub.3.5H.sub.2 O
(22) Magnesium lactate trihydrate: Mg(C.sub.3 H.sub.5 O.sub.3).sub.2.3H.sub.2 O
(23) Magnesium nitrate hexahydrate: Mg(NO.sub.3).sub.2.6H.sub.2 O
(24) Magnesium orthophosphate octahydrate: Mg.sub.3 (PO.sub.4).sub.2.8H.sub.2 O
(25) Magnesium sulfate heptahydrate: MgSO.sub.4.7H.sub.2 O
(26) Magnesium tartrate pentahydrate: MgC.sub.4 H.sub.4 O.sub.6.5H.sub.2 O
(27) Sodium carbonate decahydrate: Na.sub.2 CO.sub.3.10H.sub.2 O
From among all of those water donors above-outlined, finely divided silicas, capable of adsorbing 2 to 3 times their weight in water, are preferably selected.
It too has now surprisingly been found that the compositions of the invention improve the dissolution of the water soluble biogum to a degree increasing with the original degree of difficulty of dissolution of the biogum.
It has also been determined that typically for the best results to be obtained consistent herewith, a third additive is included, such as a surfactant of the anionic and/or nonionic type.
A preferred embodiment of this invention is thus defined by a composition of matter comprising a water soluble biogum having enhanced properties of dissolution, the same including, in addition to the water soluble biogum, a material incorporating water into the composition, or water donor, or material adapted to sorb and retain water and an anionic and/or nonionic surfactant.
For a description of the surfactants intended hereby, reference is made, for example, to Kirk-Othmar, Encyclopedia Of Chemical Technology, Volume 19, or to the different volumes in the series, Surfactant Sciences Series, Marcel Dekker, Inc.; Vol. 1: Nonionic Surfactants, by Martin J. Schick; Vol. 7: Anionic Surfactants, by Warner M. Linfield; or the work by McCutcheons: Detergents and Emulsifiers, International and North American Edition.
As examples of the anionic surface active agents that may be used, the following are representative:
(i) soaps of alkali metals, such as the sodium or potassium salts of saturated or unsaturated fatty acids having 8 to 24 carbon atoms, preferably having 14 to 20 carbons, or aminocarboxylic acid derivatives, such as sodium N-lauryl sarconisate, sodium N-acylsarconisate, and the like;
(ii) alkali sulfonates such as the alkyl sulfonates, aryl sulfonates or alkylaryl sulfonates; in particular alkyl sulfonates, such as, for example, the diesters of sulfosuccinic acid, such as sodium diethylhexylsulfosuccinate, sodium dioctylsulfosuccinate, alkylbenzenesulfonates of the formula R.sub.1 --C.sub.6 H.sub.4 SO.sub.3 M.sub.1 wherein the radical R.sub.1 is a linear or branched chain alkyl radical containing 8 to 13 carbon atoms, such as, for example, a nonyl, dodecyl or tridecyl radical and M.sub.1 represents a sodium atom, a potassium atom, an ammonium radical, diethanolamine or triethanolamine; alkylnaphthalenesulfonates of the formula (R).sub.no C.sub.10 H.sub.7-no SO.sub.3 M.sub.1 wherein no is a number ranging from 1 to 3 and the radical R is a linear or branched chain alkyl radical containing 1 to 4 carbon atoms, such as, for example, a methyl, isopropyl or isobutyl radical and M.sub.1 is as above-defined; other sulfonates may also be employed, such as N-acyl, N-alkyltaurates of the formula R.sub.2 --CO--N(R.sub.2 ')--CH.sub.1 --CH.sub.2 --SO.sub.3 Na wherein R.sub.2 is an alkyl radical having 11 to 18 carbon atoms and R.sub.2 ' is a methyl or ethyl radical, such as, for example, sodium N-oleoyl-N-methyltaurate or N-palmitoyl-N-methyltaurate; olefin sulfonates resulting from the sulfonation of the linear olefin fractions, C.sub.14 to C.sub.18 ;
(iii) sulfates and sulfate products: among the alkyl sulfates having the formula R.sub.3 OSO.sub.3 M.sub.1, representative are those wherein the R.sub.3 radical is a lauryl, cetyl or myristyl radical and M.sub.1 is as above-defined; natural sulfate oils and fats; the disodium salt of sulfated oleic acid; polyoxyethylene sulfate fatty alcohols of the formula R.sub.4 (O--CH.sub.2 --CH.sub.2).sub.n.sbsb.1 OSO.sub.3 M.sub.1 wherein R.sub.4 is an alkyl radical containing 6 to 16 carbon atoms, such as, for example, a myristyl radical or a linear or branched chain alkyl radical, such as, for example, a hexyl, octyl, decyl or dodecyl radical, n.sub.1 is the number of mols of ethylene oxide and varies from 1 to 4 and M.sub.1 is as above-defined; polyoxyethylene alkylphenol sulfates having the formula R.sub.5 --C.sub.6 H.sub.4 (O--CH.sub.2 --CH.sub.2).sub.n.sbsb.2 OSO.sub.3 M.sub.1, wherein R.sub.5 is a linear or branched chain alkyl radical containing 8 to 13 carbon atoms, such as, for example, an octyl, nonyl or dodecyl radical, n.sub.2 is the number of mols of ethylene oxide and varies from 1 to 6 and M.sub.1 is as above-defined;
(iv) alkaline phosphates: the mono- and diesters of orthophosphoric acid or one of its salts which may be represented, for the alkyl phosphates, by the formula (R.sub.6 O)PO(OM.sub.2).sub.2 and, for the dialkyl phosphates, by the formula (R.sub.6 O).sub.2 PO(OM.sub.2) wherein R.sub.6 is a linear or branched chain alkyl radical having 6 to 12 carbon atoms and M.sub.2 represents a hydrogen atom, or a sodium or potassium atom; as an example of the radical R.sub.6, n-hexyl, n-octyl, n-ethylhexyl, dimethylhexyl, n-decyl, dimethyloctyl, trimethylheptyl and trimethylnonyl are noted; the mono- or diesters of orthophosphoric acid, or salt thereof, polyoxyethyleneated, which may be represented, for the polyoxyethylene alkyl phosphates, by the formula: ##STR1## and, for the dialkyl polyoxyethylene phosphates, by the formula: ##STR2## wherein R.sub.7 represents a linear or branched chain alkyl radical having 6 to 12 carbon atoms, a phenyl radical, an alkylphenyl radical with the alkyl chain having from 8 to 12 carbon atoms, n.sub.3 is the number of mols of ethylene oxide and varies from 2 to 8, and M.sub.2 is as above-defined; as examples of the radical R.sub.7, hexyl, octyl, decyl, dodecyl and nonylphenyl are representative.
Exemplary nonionic surfactants are the compounds obtained by condensation of an alkylene oxide with an organic compound, which may be aliphatic or alkylaromatic. Representative nonionic surfactants are:
(i) polyoxyethylene alkylphenols, for example, the products of the condensation of 5 to 25 mols of ethylene oxide per mol of alkylphenol, the alkyl radical of which being straight or branched chain and containing from 6 to 12 carbon atoms; in particular, nonylphenol condensed with approximately 10 to 30 mols of ethylene oxide per mol of phenol, dinonylphenol condensed with 15 mols of ethylene oxide per mol of phenol and dodecylphenol condensed with 12 mols of ethylene oxide per mol of phenol, are representative;
(ii) aliphatic polyoxyethylene alcohols resulting from the condensation of 5 to 30 mols of ethylene oxide with linear or branched chain fatty alcohols containing from 8 to 22 carbon atoms: for example, the product of condensation of approximately 15 mols of ethylene oxide with 1 mol of tridecanol or coprah alcohol; myristyl alcohol condensed with 10 mols of ethylene oxide;
(iii) fatty amides, such as, for example, the diethanolamide of fatty acids, or polyoxyethyleneated fatty acids, such as lauric acid or coconut oil;
(iv) polyoxyethylene and polyoxypropylene derivatives; illustrative of this type of surfactant are the well known products marketed under the trademark "PLURONICS". Same are obtained by the sequential addition of propylene oxide and ethylene oxide to a reactive hydrogen compound with a low molecular weight, such as, for example, propylene glycol.
In order to facilely incorporate the surfactant into the compositions of the invention, it is introduced in a solid, preferably powder form.
The surfactants are in the solid and, more frequently, in the liquid state. In the case of a liquid surfactant, it must first be deposited onto a powder support capable of sorbing and desorbing the liquid and which is chemically inert, insoluble or soluble. It may also be sorbed directly onto the powder consisting of the water donor, with water optionally being added thereto.
Preferably, a solid surfactant such as sodium alkylpropylnaphthalene sulfonate, in particular sodium diisopropylnaphthalene sulfonate, is utilized.
The proportions of the various, advantageously three components in the subject biogum compositions, are preferably as follows:
The amount of water in the compositions according to the invention, expressed as the ratio by weight of biogum/water, may vary over wide limits, from 6.5 to 1, preferably 2.5 to 1.
The lower limit is not critical. However, it is preferred that this ratio does not exceed 4.
The amount of water donor is defined as the ratio by weight of the water donor to water; it preferably ranges from 0.3 to 0.6, while it nonetheless may be selected within a larger range, from 0.3 to 2.6.
The amount of the surfactant employed, defined as the ratio of the weight of the surfactant to the total weight of the composition of the invention, may vary from 0 to 0.10. The upper limit is not critical, but there is no advantage in attaining weight ratios higher than 0.25. Preferably, the amount of surfactant is selected such that said ratio ranges from 0.03 to 0.07.
Examples of the subject compositions comprised of a water soluble biogum are as follows:
(1) 30 to 70% by weight water soluble biogum;
(2) 7 to 40% by weight of water donor;
(3) 0 to 10% by weight of an anionic and/or a nonionic surfactant; and
(4) 15 to 37% by weight of water.
Preferred compositions are the following:
(1) 50 to 60% by weight water soluble biogum;
(2) 8 to 15% by weight of water donor;
(3) 3 to 7% by weight of an anionic and/or nonionic surfactant; and
(4) 24 to 36% by weight of water.
Concerning the preparation of the compositions according to the invention, it varies slightly depending on whether or not the water component of any given composition is externally added or comprises water of crystallization, and depending on whether or not the surfactant is in the solid or liquid form.
The process for the preparation of the compositions according to the invention comprises mixing, in the dry state, the water donor, onto which water may be adsorbed, with the biogum and optionally adding thereto the anionic and/or nonionic surfactant.
The first operation, which features the impregnation of the water donor with water, entails the following materials: finely divided silica, dehydrated silica gels, alumina hydrates and silica aluminate hydrates. Progressively, under agitation, water is added to the water donor. This stage is omitted, if, as the water donor, hydrated silica gels or the hydrates of inorganic or organic salts are employed.
The water donor is in the form of a dry powder, even if it is impregnated with water, as aforesaid.
Subsequently, its admixture with the water soluble biogum is effected in a powder mixer of known type: free-falling, drum type mixer, vertical or horizontal screw mixers, horizontal Lodige type mixer, or the like.
The introduction of the surfactant, if it is a solid, is effected into the mixture of the water donor and the biogum.
If the surfactant is present in the form of a liquid, it is generally adsorbed onto the water donor, simultaneously with or successively to the adsorption of water, whereupon it is admixed with the biogum.
After all of the components are introduced, the mixing is continued. The duration of the operation is a function of the apparatus used and is easily determined by those skilled in the art, such that a homogeneous mixture is obtained.
The process of the invention provides compositions in the form of a powder having excellent storage stability.
Also according to the invention, sols are prepared from the aforementioned compositions of matter.
The preparation of said sols is effected simply by adding the powdered composition to the aqueous medium under agitation, by means of conventional agitator devices (anchor agitation, screw or turbine agitation, etc.).
The introduction of the composition of the invention into the water may take place rapidly, in a single fraction, without difficulty. It does not require any special precautions.
The quantity of the composition introduced is such that, typically, the concentration of the water soluble biogum in the sol varies from 0.2 to 2% by weight.
Agitation is then maintained until a constant viscosity results; usually, the duration of agitation ranges from 10 to 30 min.
By virtue of the formulation of a water soluble biogum in the form of the compositions of the invention, marked improvement in the dissolution of the biogum, together with an increase in the speed at which the viscosity of the resultant sol attains a maximum value, both ensue, especially when the biogum is dissolved under conditions of mild agitation. By way of example, the viscosity of a sol comprising 0.5% by weight Xanthan gum in city water having a hardness of 25.degree. HT (or 100 mg/l Ca.sup.++ ions) measured at 23.degree. C. with a Brookfield Model LVT viscosimeter, at a velocity of 10 rpm using a No. 2 plunger, was compared with the viscosity of a sol having the same concentration in Xanthan gum, but prepared from a composition according to the invention containing:
(1) 60% by weight Xanthan gum;
(2) 8.75% by weight of a precipitated silica having a BET surface of 250 m.sup.2 /g;
(3) 5% by weight of sodium diisopropylnaphthalenesulfonate; and
(4) 26.25% by weight of water.
With the composition according to the invention, the maximum viscosity of the sol, namely, 1,800 mPa.multidot.s, was attained after only about 15 min, while the viscosity of the sol of the Xanthan gum alone was only 600 mPa.multidot.s after 15 min, and 1,300 mPa.multidot.s after 30 min, with the maximum viscosity not being attained until after at least one hour.
It will be seen that the sols obtained utilizing the compositions of the invention are perfectly stable under conventional storage conditions; compare the examples to follow.

In order to further illustrate the present invention and the advantages thereof, the following specific examples are given, it being understood that same are intended only as illustrative and in nowise limitative.
In said examples to follow, the heteropolysaccharide biogum employed was the Xanthan gum marketed by Societe Rhone-Poulenc under the commercial designation of Rhodopol 23, and having the following specifications:
______________________________________(i) Appearance Cream colored powder(ii) Apparent density, g/cm.sup.3 0.8(iii) Active material 90%(iv) Ash 10%(v) Moisture content 10%(vi) pH (1% sol in distilled 7% water)(vii) Brookfield LVT 30 M viscosity 2,200-3,000 cps Needle No. 4(viii) Particle size: Particles <75.mu. <30% >297.mu. <2%______________________________________
Also in the following examples,those operating conditions set forth immediately below were utilized in each example for the formulation of the compositions according to the invention and for the preparation of the sols therefrom, except as otherwise stated.
The procedure employed for the formulation of the subject compositions was as follows:
(i) Water was sorbed, if necessary, onto the water donor, in the amount indicated. For this purpose, the water was slowly poured under mild agitation into a beaker containing said water donor;
(ii) The water soluble Xanthan biogum was then added to the water impregnated water donor, and same were then intimately admixed;
(iii) Finally, the solid surfactant was added thereto; and
(iv) The resulting composition was homogenized for one hour in a powder mixer.
The conditions for the preparation of the sols were as follows; in each experiment, 400 g of sol were prepared:
(i) Into a beaker equipped with a frame-type agitator rotating at a velocity of 100 rpm, 400 g water were introduced; said water being city or tap water having a hardness of 25.degree. HT (100 mg/l Ca.sup.++ ions);
(ii) The powdered composition was rapidly poured therein in the desired amount, with the extent of the addition being less than 30 sec; and
(iii) The agitation was maintained until a constant viscosity resulted.
It should be noted that the solution test was made more difficult by reason of the mild conditions of agitation, thereby making it possible to observe the improvement in dispersibility; higher degrees of agitation would not be beneficial.
The agitator employed was a frame blade placed in the solution such that the upper part thereof was flush with the surface of the water, thereby aiding the wetting of the surface of the powder poured onto the water.
The following examples illustrate the different compositions of the invention, either with or without surfactant. The properties of the sols obtained with the compositions of the invention are compared with those of sols containing only the water soluble Xanthan biogum.
In all of the examples to follow, the percentages are expressed by weight.
EXAMPLES 1 and 2
(1) Preparation of compositions based upon Xanthan gum
The following compositions were formulated using Xanthan gum, a light precipitated silica as the water donor and the anionic surfactant, sodium diisopropylnaphthalene sulfonate (Example 1), optionally with a nonionic surfactant (Example 2) being added, the latter consisting of a nonylphenol condensed with 10 mols of ethylene oxide.
The characteristics and proportions of the various components of said compositions were as follows:
______________________________________ Composition 1 Composition 2______________________________________Xanthan gum (Rhodopol 23 33.3% 20%Precipitated silica (Tixosil 38A) 22.2% 30%Sodium diisopropylnaphtha- 4.5% 3%lenesulfonate (Supragil WP)Nonylphenol with 10 E.O. -- 20%(Cemulsol NP 10)City water 40% 27%______________________________________
Tixosil 38A is a precipitated silica having a BET surface of 250 m.sup.2 /g and a pore volume, of those pores varying in size from 400 .ANG. to 2.5 .mu., of 1.80 cm.sup.3 /g of silica, and a moisture content at 105.degree. C. of less than 7%.
Supragil WP is sodium diisopropylnaphthalenesulfonate, an anionic surfactant in the solid state. More precisely, it has the formula of (C.sub.3 H.sub.7).sub.no C.sub.10 H.sub.7-no SO.sub.3 Na with no=1.8.
Cemulsol NP 10 is a nonylphenol condensed with 10 mols of ethylene oxide; it is aliquid, nonionic surfactant.
The preparation of the subject compositions was carried out under the aforedescribed conditions, except that the liquid surfactant was adsorbed onto the silica under the same conditions as the water, prior to the addition of the Xanthan gum.
(2) Preparation of the sols
The sols also were prepared under the aforedescribed conditions, with the following concentrations by weight of commercial Xanthan gum, i.e., at a moisture content of about 10%: 0.2%; 0.3%; 0.5%; 1%.
A series of control experiments was also carried out wherein only the Xanthan gum was utilized.
The operating conditions for the preparation of the sols were those above-outlined, except that the speed of agitation was 400 rpm, instead of 100 rpm.
(3) Study of the sols
(a) Viscosity measurements:
The viscosity of the sols prepared from the compositions of the invention and from the Xanthan gum alone was a function of the concentration of the biopolymer therein; it was determined for concentrations of 0.2%, 0.3%, 0.5% and 1% by weight of the Xanthan gum.
The viscosity measurements were taken at 23.degree. C. with the aid of a Brookfield Model RV viscosimeter, and a velocity of 10 rpm, with No. 2 plungers for the concentrations 0.2%, 0.3% and 0.5% and a No. 3 plunger for the 1% concentration.
Measurements were recorded after 5, 10, 30 and 45 min of agitation, after a quiescent period of 24 hours.
The results obtained for the Compositions 1 and 2 of Examples 1 and 2 and for the Xanthan gum of Experiment A are respectively reported in Tables I and II. The appearance of the product sols is also reported.
TABLE I__________________________________________________________________________Measurements of viscosities in mPa.s (BROOKFIELD Model RV Viscosimeter -10 rpm - Plungers Nos. 2 and 3)Appearance of the solutionsREFERENCES COMPOSITION 1 COMPOSITION 2__________________________________________________________________________Concentration in Xanthan gum 0.2% 0.3% 0.5% 1% 0.2% 0.3% 0.5% 1%Duration of agitation 5 minutes 170 685 1840 5690 15 95 1165 726010 minutes 295 770 1905 5740 205 845 2240 710030 minutes 310 775 1930 5950 360 820 2070 718045 minutes 320 775 1950 5960 380 830 2020 6720After a quiescent period of 325 750 1970 6000 340 800 2090 660024 hoursObservations after 5 minutes Good dispersion; presence of a Very good dispersion; suspension of few, small floccules. fine, white particles.Observations after 10 minutes Still some very small floccules. Formation of a light foam.Observations after 30 minutes Homogeneous sol; no silica Formation of a light foam. visible in suspension.__________________________________________________________________________
TABLE II__________________________________________________________________________Measurements of viscosities in mPa.s (BROOKFIELD Model RV Viscosimeter -10 rpm - Plungers Nos. 2 and 3) Appearance of the solutionsREFERENCE XANTHAN GUM__________________________________________________________________________Concentration in Xanthan gum 0.2% 0.3% 0.5% 1%Duration of agitation 5 minutes not not not not measurable measurable measurable measurable10 minutes 145 400 1300 331030 minutes 300 650 1890 540045 minutes 300 680 1870 5500After a quiescent period of 290 670 1825 546024 hoursObservation after 5 minutes Heterogeneous mixture of water and coarse floccules or agglomerates.Observation after 10 minutes Onset of coarse, opalescent floccules.Observation after 30 minutes Still some floccules; homogeneous medium__________________________________________________________________________
A comparative analysis of Tables I and II evidences the following:
(i) With Composition 1, in any concentration but less than 0.2%, maximum viscosity is attained as a practical matter in 5 minutes, while in the case of the Xanthan gum alone, it was necessary to wait 30 minutes.
The dispersion of the subject composition was good and only a few, rare floccules appeared when the powder was added rapidly, but same disappeared rather quickly.
(ii) With Composition 2, about 10 minutes were required to obtain total swelling; which is still abundantly favorable with respect to the Xanthan gum alone.
The dispersion was excellent, but a suspension of fine white particles was observed, because of the higher silica content of this formula. Consequently, when such a composition is selected for use, care must be taken that the suspension does not interfere with the intended end application.
Under the same conditions, the Xanthan gum sol was, after 5 minutes, a heterogeneous mixture filled with agglomerates and practically without viscosity; it was necessary to wait 30 minutes in order to obtain a nearly homogeneous medium which had attained its ultimate viscosity.
The comparison of the sols of these two compositions with that of Xanthan gum after 24 hours at rest or quiescence, i.e., at equilibrium, demonstrated that the two compositions yield, at an equal concentration in Xanthan gum, slightly higher viscosities:
(1) Composition 1: +8 to 12%
(2) Composition 2: +15 to 20%
Up to 10%, it is considered that one is within the limits of accuracy and reproducibility of the measurements. Thereafter, it may be assumed that the filler, which is important especially in the case of Composition 2, contributes to a slight increase in viscosity.
(b) Comparison of rheological behavior:
The plotting of rheogram curves evidenced the rheological behavior of the sols obtained from Compositions 1 and 2, and enabled verification that with this formulation the rheological behavior of Xanthan gum was not modified.
The rheograms were plotted with the aid of a Rheomat 30 rheometer after 24 hours.
These curves enabled calculation of critical stress at the threshold of flow, and viscosities at different velocity gradients.
Tables III and IV report the entirety of the test
TABLE III__________________________________________________________________________Measurements of critical stress at the threshold of flow in Pa and ofviscositiesin mPa.s (RHEOMAT 30 viscosimeter) at two velocity gradientsREFERENCES COMPOSITION 1 COMPOSITION 2__________________________________________________________________________Concentration in Xanthan gum 0.2% 0.3% 0.5% 1% 0.2% 0.3% 0.5% 1%Threshold stress in Pa 0.25 1.2 3.3 12.4 0.3 1.0 3.8 13.6Viscosity in mPa.s at 428 950 2315 7030 428 860 2570 70702.78 s.sup.-1Viscosity in mPa.s at 15 25 45 115 15 25 48 120278 s.sup.-1__________________________________________________________________________
TABLE IV______________________________________Measurements of critical stress at the threshold of flow in Pa andof viscosities in mPa.s (RHEOMAT 30 viscosimeter) at twovelocity gradientsREFERENCE XANTHAN GUM______________________________________Xanthan gum concentration 0.2% 0.3% 0.5% 1%Threshold stress in Pa 0.2 0.7 3.2 10.7Viscosity in mPa.s at 2.78 s.sup.-1 364 730 2315 6260Viscosity in mPa.s at 278 s.sup.-1 15 23 45 103______________________________________
A comparison of the rheograms for the two compositions and for the Xanthan gum alone (Tables III and IV) demonstrated that:
(i) The subject compositions had a flow threshold (.delta.) of the same order of magnitude as that of the Xanthan gum and were well adapted for rapid, effective dispersion/dissolution;
(ii) At low shearing, 2.78 s.sup.-1, and at equal concentrations, the compositions yield a slightly higher viscosity;
(iii) At a high viscosity gradient, 278 s.sup.-1, and at equal concentrations, the compositions always yield solutions slightly higher in viscosity; and
(iv) The presence of a filler in Compositions 1 and 2 does not impart thixotropy to the product solutions.
In conclusion, the overall results demonstrated that Xanthan gum formulated into the compositions of the invention was unchanged as regards its rheological properties, and the dissolution thereof in aqueous media was clearly markedly enhanced.
EXAMPLES 3 to 6.
In the following examples, a higher proportion of Xanthan gum was used in the compositions of the invention.
(1) Preparation of compositions based upon Xanthan gum
Compositions containing Xanthan gum, a precipitated silica and sodium diisopropylnaphthalene sulfonate and water, were prepared in the following proportions:
______________________________________ COM- COM- COM- COM- POSI- POSI- POSI- POSI- TION TION TION TION 3 4 5 6______________________________________Xanthan gum (Rhodopol 23) 40% 50% 60% 70%Precipitated silica 18.35% 15% 11.65% 8.35%(Tixosil 38A)Sodium diisopropyl- 5% 5% 5% 5%naphthalene sulfonate(Supragil WP)Water 36.65% 30% 23.35% 16.65%______________________________________
The Xanthan gum content varied from 40 to 70%, the silica/water ratio was constant at 0.5 and the amount of sodium diisopropylnaphthalenesulfonate was maintained at 5%.
The characteristics of the product compositions were as set forth in Examples 1 and 2.
(2) Preparation of the sols
For each experiment, 400 g of a sol having a constant Xanthan gum content of 0.5% were prepared.
(3) Viscosity measurements
The viscosities of the sols prepared from Compositions 3, 4, 5 and 6 were measured at 23.degree. C. after 5, 10, 15, 20, 30 and 60 minutes, with a Brookfield Model RV viscosimeter at a velocity of 10 rpm and with a No. 2 plunger.
The values obtained are reported in Table V.
With the same amount of Xanthan gum concentration, dissolution and increase in viscosity were, respectively:
(a) the easiest and most rapid for Composition 1 (Example 1); and
(b) the most difficult and slowest for the Xanthan gum alone.
The four compositions investigated had an intermediate behavior, with the best and the closest to Composition 1 being Composition 3, then 4, 5 and finally 6, which approaches Xanthan gum alone, but, in all cases, the compositions according to the invention afforded improved results.
TABLE V______________________________________Measurements of viscosities in mPa.s (BROOKFIELD ModelRV Viscosimeter - 10 rpm - No. 2 Plunger) of 0.5% sols COM- COM- COM- COM- POSI- POSI- POSI- POSI- XAN- TION TION TION TION THANREFERENCES 3 4 5 6 GUM______________________________________Duration ofAgitation 5 minutes 1740 1424 1164 780 not measur- able10 minutes 1960 1668 1540 1130 19515 minutes 2000 1848 1780 1380 56520 minutes 1960 1910 1924 1640 105030 minutes 1970 1930 1920 1730 132560 minutes 2010 1950 1940 1790 1460______________________________________
EXAMPLES 7 to 14
The following examples illustrate the effects of varying the Xanthan gum/water ratio which result regardless of the amount of silica present.
(1) Preparation of compositions based upon Xanthan gum
Eight new compositions were prepared following that general procedure above-described, i.e., the Compositions 7 to 14:
__________________________________________________________________________ COMP. 7 COMP. 8 COMP. 9 COMP. 10 COMP. 11 COMP. 12 COMP. 13 COMP.__________________________________________________________________________ 14Xanthan gum 50 60 50 50 40 50 60 60(Rhodopol 23)Precipitated silica 11.25 8.75 15 30 39.45 25.55 11.65 7.75(Tixosil 38A)Sodium diisopropyl- 5 5 5 5 5 5 5 5naphthalene sulfonate(Supragil WP)Water 33.75 26.25 15 15 15.55 19.45 23.35 27.25__________________________________________________________________________
(2) Preparation of the sols
Sols containing said Compositions 7 to 14 were prepared in quantities such that the concentration of Xanthan gum therein was constant and equal to 0.5%.
(3) Viscosity measurements
The viscosity of sols prepared from the Compositions 7 to 14 was measured after 5, 10, 15, 30 and 60 minutes, with a Brookfield Model RV viscosimeter at a velocity of 10 rpm and with a No. 2 plunger.
The results obtained are reported in Table VI; those obtained with the Compositions 3 to 6 are repeated:
TABLE VI__________________________________________________________________________Measurements of viscosities in mPa.s (BROOKFIELD Model RV Viscosimeter -10 rpm - Plunger No. 2)of 0.5% sols__________________________________________________________________________REFERENCES COMP. 3 COMP. 4 COMP. 5 COMP. 6 COMP. 7 COMP. 8 COMP. 9__________________________________________________________________________% of Xanthan gum in 40 50 60 70 50 60 50compositionXanthan gum/water ratio 1.1 1.7 2.6 4.2 1.5 2.3 3.3Silica/water 0.5 0.5 0.5 0.5 0.33 0.33 1Duration of agitation 5 minutes 1740 1424 1164 780 1600 1424 95010 minutes 1960 1668 1540 1130 1904 1720 142015 minutes 2000 1848 1780 1380 1920 1848 171220 minutes 1960 1910 1924 1640 1980 1870 182030 minutes 1970 1930 1920 1730 1980 1870 186060 minutes 2010 1950 1940 1790 2000 1904 1884__________________________________________________________________________REFERENCES COMP. 10 COMP. 11 COMP. 12 COMP. 13 COMP. 14 Xanthan gum__________________________________________________________________________% of Xanthan gum in 50 40 50 60 60 100compositionXanthan gum/water 3.3 2.6 2.6 2.6 2.2 --ratioSilica/water 2 2.5 1.3 0.5 0.28 --Duration of agitation 5 minutes 724 1020 1020 1232 1408 not measurable10 minutes 1200 1428 1410 1668 1792 19515 minutes 1540 1736 1750 1870 1860 56520 minutes 1844 1930 1930 1960 1940 105030 minutes 1896 1980 1984 1960 1924 132560 minutes 1988 2024 2024 2000 1960 1460__________________________________________________________________________
After 5 minutes of agitation, it was determined that the compositions in which the quantity of water was the greatest for the same amount of Xanthan gum, solubilized the easiest and provided the highest viscosity.
It will be appreciated that when the Xanthan gum/water ratio varied from 3.3 to 2.3, the increase in viscosity was very large after 5 minutes of agitation, from 700 mPa.multidot.s to 1400 mPa.multidot.s; a gain of 100%.
Below a ratio of 2.5, the increase was clearly less and became negligible after 20 minutes.
To formulate a composition having the highest possible content in Xanthan gum and the maximum of water, it is necessary to introduce a minimum amount of silica, and thus much water and but little silica. In fact, the maximum amount of water that it has been possible to sorb onto the silica was three times its weight in water, if the appearance of the final product as a dry, flowable powder without agglomerates, was to be preserved.
With a silica/water ratio of 0.28, the powder was too moist, formed agglomerates and there was no enhancement in dispersion and the rate of dissolution.
(4) Stability studies
The stability of the "powder" compositions and of the sols prepared therefrom was examined during extended storage periods.
(a) Stability of "powder" compositions:
The compositions were maintained at an ambient temperature of 23.degree. C. in polyethylene bottles.
The aforedescribed compositions 4 to 8 were tested.
After a storage time of 24 hours, 20 days (Composition 8), 30 days (Composition 4) and 60 days, sols containing 0.5% of the Compositions 4 and 8 were prepared.
The viscosity obtained was measured 30 minutes after the preparation of the sols, with a Brookfield, Model RV viscosimeter, at a velocity of 10 rpm and with a No. 2 plunger.
The following results were obtained; storage durations are expressed in hours (h) and days (j).
______________________________________REFERENCES COMPOSITION 4 COMPOSITION 8______________________________________Duration of 24 h 30 j 60 j 24 h 20 j 60 jstorageViscosity in 2000 1930 1910 1870 1890 1910mPa.s______________________________________
It was noted that the appearance of the compositions remains unchanged and same retained their effectiveness even after two months of storage.
(b) Stability of sols:
From the Compositions 7 and 8, sols were prepared in the usual manner and were maintained in closed containers, in a room maintained at 23.degree. C.
The viscosity was measured after storage periods of 1 hour, 20 days and 56 days under the conditions described under (a).
The following results were obtained; storage periods are expressed in hours (h) and days (j).
______________________________________REFERENCES COMPOSITION 7 COMPOSITION 8______________________________________Duration of 1 h 20 j 56 j 1 h 20 j 56 jstorageViscosity in 2000 1960 1920 1870 1920 1860mPa.s______________________________________
The stability of the sols was very good, the more so since no preservative had been added; no odor or moisture was detected after 56 days of storage.
EXAMPLES 15 to 18
The following examples demonstrate the effects of the proportions of surfactant in the compositions according to the invention.
(1) Preparation of compositions based upon Xanthan gum
Compositions 15-18 containing Xanthan gum, a precipitated silica, water and the surfactant, sodium diisopropylnaphthalene sulfonate, in increasing amounts, were prepared as follows:
______________________________________ COM- COM- COM- COM- POSI- POSI- POSI- POSI- TION TION TION TION 15 16 17 18______________________________________Xanthan gum (Rhodopol 23) 62.5 64 62 60Precipitated silica (Tixosil 38A) 9.38 8.75 8.75 8.75Sodium diisopropylnaphthalene 0 1 3 5sulfonate (Supragil WP)Water 28.12 26.25 26.25 26.25______________________________________
The content in sodium diisopropylnaphthalene sulfonate varied from 0 to 5%.
The silica and water were present in the constant ratio of 0.33.
The contents in Xanthan gum and the mixture of silica and water were determined in a manner such that the gum/water ratio was equal to, or close as possible to 2.2.
The compositions were formulated according to the general technique above-described.
(2) Preparation of the sols
Subsequently, the sols were prepared from the Compositions 15 to 18 in quantities such that the concentration in Xanthan gum therein was constant and equal to 0.5%.
(3) Viscosity measurements
The viscosity of the sols prepared from the Compositions 15 to 18 was measured after 5, 10, 15, 20 and 30 minutes with a Brookfield, Model RV viscosimeter at a velocity of rpm and with a No. 2 plunger.
The results obtained are reported in Table VII.
TABLE VII__________________________________________________________________________Measurements of viscosities in mPa.s (BROOKFIELD Model RV Viscosimeter -10 rpm - No. 2 plungerof 0.5% solsREFERENCES COMPOSITION 15 COMPOSITION 16 COMPOSITION 17 COMPOSITION Xanthan__________________________________________________________________________ gum% Of sodium diisopropyl- 0 1 3 5 0naphthalene sulfonate inthe compositionDuration of agitation 5 minutes 1040 1200 1580 1600 not measurable10 minutes 1420 1540 1980 2000 19515 minutes 1680 1820 1990 2000 56520 minutes 1900 1900 1990 2000 105030 minutes 1920 1920 1990 2000 1325__________________________________________________________________________
It will be appreciated that it is preferred to use sodium diisopropylnaphthalene sulfonate, because it improved viscosity. The presence of a surfactant was thus desirable. There is no advantage in employing an excess of sodium diisopropylnaphthalene sulfonate, as an amount of 3% appears to be sufficient to rapidly obtain the maximum viscosity.
EXAMPLES 19 to 21
The following examples illustrate the use of other surfactants.
(1) Preparation of compositions based upon Xanthan gum
The compositions of the preceding examples were prepared using sodium diisopropylnaphthalene sulfonate (Supragil WP) as the surfactant, which is a powder product having a low wetting strength of 4.1 g/l at 20.degree. C., determined by the standard method NFT 73 406 (French National Standard).
Hereinafter, the following liquid surfactants were used:
(i) an Alfol 10-12, 7 O.E., 5 O.P.: i.e., a mixture of linear primary alcohols having 10 and 12 carbon atoms and condensed with 7 mols of ethylene oxide and 5 mols of propylene oxide (Cemulsol FM 33)=a nonionic surfactant with a wetting strength of 0.70 g/l; and
(ii) sodium dioctylsulfosuccinate (Celanol DOS 63) in solution in isopropanol: a liquid anionic surfactant having a strong wetting strength of 0.30 g/l.
The formulation of compositions of the invention was effected by taking into consideration the wetting strength of the surfactant in the determination of its concentration.
______________________________________ COMPO- COMPO- COMPO- SITION 19 SITION 20 SITION 21______________________________________Xanthan gum 60 56.7 62(Rhodopol 23)Precipitated silica 10.75 12.05 8.75(Tixosil 37A)Alfol 10-12, 7 O.E., 3 55 O.P. (CemulsolFM 33)Sodium dioctylsulfo- 2succinate (CelanolDOS 65)Isopropanol 1Water 26.25 26.25 26.25______________________________________
The compositions were formulated as aforesaid, except that the liquid surfactant was sorbed onto the silica under the same conditions as the water, prior to the addition of the Xanthan gum.
(2) Preparation of the sols
The sols were prepared from the Compositions 19 to 21 in quantities such that the concentration therein of the Xanthan gum was constant and equal to 0.5%.
(3) Viscosity measurements
The viscosity of sols prepared from the subject compositions was measured after 5, 10, 15, 20, 30 and 60 minutes with a Brookfield Model RV viscosimeter at a velocity of 10 rpm and with a No. 2 plunger.
The results obtained are reported in Table VIII; for comparison, the results obtained with sodium diisopropylnaphthalene sulfonate in Examples 17 and 18 were repeated.
The compositions tested with the surfactants having good wetting strength yield results better than those obtained in their absence, but they remain clearly below those obtained with sodium diisopropylnaphthalene sulfonate.
TABLE VIII__________________________________________________________________________Measurements of viscosities in mPa.s (BROOKFIELD Model RV Viscosimeter -10 rpm -No. 2 plunger) of 0.5% solsREFERENCES COMP. 17 COMP. 18 COMP. 19 COMP. 20 COMP. 21 Xanthan gum__________________________________________________________________________% Surfactant in the 3 5 3 5 2 0compositionDuration of agitation 5 minutes 1580 1620 1240 1360 1120 not measurable10 minutes 2000 1980 1600 1740 1460 19515 minutes 1980 1980 1840 1880 1640 56520 minutes 1980 2000 1980 1940 1860 105030 minutes 2000 2000 1980 1960 1900 132560 minutes 2000 2000 2000 1980 1980 1460__________________________________________________________________________
EXAMPLES 22 to 30
The following examples illustrate the use of other materials incorporating water into the subject compositions.
(1) Preparation of compositions based upon Xanthan gum
All of the compositions prepared with the different materials (except with the hydrated silica gels) included:
(i) 60% Xanthan gum (Rhodopol 23);
(ii) 17.5% of water donor;
(iii) 5% sodium diisopropylnaphthalene sulfonate (Supragil WP); and
(iv) 17.5% water
When the water donor was a hydrated silica gel, the composition had the following formulation:
(i) 60% Xanthan gum (Rhodopol 23);
(ii) 35% hydrated silica gel; and
(iii) 5% sodium diisopropylnaphthalene sulfonate (Supragil WP).
Hereinafter, at least one example of each category of the water donor materials is given:
(a) Hydrated silica gel (A) containing 68% water and having a BET surface of 600 m.sup.2 /g;
(b) Hydrated silica gel (B) containing 86% water and having a BET surface of 600 m.sup.2 /g;
(c) Dehydrated silica gel having a BET surface of 380 m.sup.2 /g and a pore volume of 1 cm.sup.3 /g (Spherosil);
(d) Alumina hydrate (C) having a BET surface of approximately 300 to 350 m.sup.2 /g, a pore volume of 0.7 to 0.8 cm.sup.3 /g and an average particle diameter of 10.mu. (Alumina SCP 350);
(e) Alumina hydrate (D) having a BET surface of 200 m.sup.2 /g, a pore volume of 0.6 cm.sup.3 /g and an average particle diameter of 15.mu. (Alumina Condea);
(f) Hydrargillite SH 5: natural alumina hydrate having a BET surface of 5 m.sup.2 /g;
(g) Attapulgite: argilla from Senegal;
(h) Bentonite having an average particle of 1 to 5.mu.; and
(i) Zeolite 4A: synthetic zeolite of sodium type, having a BET surface of 3 to 4 m.sup.2 /g, a pore volume of 0.2 cm.sup.3 /g and an average particle diameter of 4.mu. (zeolite 4A SLD No. 9).
These compositions according to the invention were also prepared as described above.
(2) Preparation of the sols
Sols were prepared from the Compositions 22 to 30 in quantities such that the concentration of Xanthan gum therein was constant, and equal to 0.5%.
(3) Viscosity measurements
The viscosity of the sols prepared from the Compositions 22 to 30 was measured after 5, 10, 15, 20 and 30 minutes, with a Brookfield Model RV viscosimeter at 10 rpm and with a plunger No. 2.
The results obtained are reported in Table IX.
Without being as efficient as the finely precipitated silica (Tixosil 38), the "other" water donors tested enhanced, to varying degrees, the development of viscosity due to the Xanthan gum.
TABLE IX__________________________________________________________________________Measurements of viscosities in mPa.s (BROOKFIELD Model RV viscosimeter -10 rpm - No. 2 plunger)of 0.5% sols__________________________________________________________________________REFERENCES COMPOSITION 22 COMPOSITION 23 COMPOSITION 24 COMPOSITION 25 COMPOSITION__________________________________________________________________________ 26Nature of water donor Hydrated silica Hydrated silica Dehydrated Alumina hydrate Alumina hydrate gel (A) gel (B) silica gel (C) (D) (Spherosil)Duration of agitation 5 minutes 540 1160 720 160 22010 minutes 1180 1600 1300 540 72015 minutes 1800 1800 1640 1020 122020 minutes 1920 1900 1850 1480 166030 minutes 1900 1960 1920 1620 1820__________________________________________________________________________REFERENCES COMPOSITION 27 COMPOSITION 28 COMPOSITION 29 COMPOSITION Xanthan__________________________________________________________________________ gumNature of water donor Hydrargillite Attapulgite Bentonite Zeolite 4A noneDuration of agitation 5 minutes 140 860 350 390 not measurable10 minutes 450 1360 940 790 19515 minutes 780 1640 1210 1120 56520 minutes 1120 1810 1440 1520 105030 minutes 1720 1900 1760 1850 1325__________________________________________________________________________
EXAMPLES 31 to 39
The following examples demonstrate the use of hydrated salts as the water donors.
(1) Preparation of compositions based upon Xanthan gum
All of the compositions prepared were formulated as follows:
(i) 60% Xanthan gum (Rhodopol 23);
(ii) 35% of a hydrated salt; and
(iii) 5% of sodium diisopropylnaphthalene sulfonate (Supragil WP).
The following salts were used:
(a) Sodium sulfate decahydrate: Na.sub.2 SO.sub.4.10H.sub.2 O;
(b) Sodium carbonate decahydrate: Na.sub.2 CO.sub.3.10H.sub.2 O;
(c) Sodium phosphate dodecahydrate: Na.sub.3 PO.sub.4.12H.sub.2 O;
(d) Sodium acetate trihydrate: NaC.sub.2 H.sub.3 O.sub.2.3H.sub.2 O;
(e) Sodium citrate pentahydrate: Na.sub.3 C.sub.6 H.sub.5 O.sub.7.5.5H.sub.2 O;
(f) Calcium chloride hexahydrate: CaCl.sub.2.6H.sub.2 O;
(g) Calcium lactate pentahydrate: Ca(C.sub.3 H.sub.5 O.sub.3).sub.2.5H.sub.2 O;
(h) Magnesium chloride hexahydrate: MgCl.sub.2.6H.sub.2 O; and
(i) Magnesium nitrate hexahydrate: Mg(NO.sub.3).sub.2.6H.sub.2 O
These compositions according to the invention were prepared as above-described, except that the stage of water impregnation was eliminated.
(2) Preparation of sols
Sols were prepared from the Compositions 31 to 39 in quantities such that the concentration of Xanthan gum therein was constant and equal to 0.5%.
(3) Viscosity measurements
The viscosity of the sols prepared from the Compositions 31 to 39 was measured after 5, 10, 15, 20 and 30 minutes, with a Brookfield Model RV viscosimeter at 10 rpm and with a No. 2 plunger.
The results obtained are reported in Table X; the Xanthan gum/water and salt/water ratios are by weight.
TABLE X__________________________________________________________________________Measurements of viscosities in mPa.s (BROOKFIELD Model RV viscosimeter -10 rpm - No. 2 plunger)of 0.5% sols__________________________________________________________________________REFERENCES COMPOSITION 31 COMPOSITION 32 COMPOSITION 33 COMPOSITION 34 COMPOSITION__________________________________________________________________________ 35Nature of water donor Na.sub.2 SO.sub.4.10H.sub. 2 O Na.sub.2 CO.sub.3.10H.sub. 2 O Na.sub.3 PO.sub.4.12H.sub. NaC.sub.2 H.sub.3 O.sub.2 .3H.sub. 2 O Na.sub.3 C.sub.6 H.sub.5 O.sub.7 .5.H.sub. 2 OXanthan gum/water 3.1 2.8 3.0 4.3 6.25Salt/water 0.8 0.6 0.75 1.5 2.6Duration of agitation 5 minutes 820 780 640 740 74010 minutes 1240 1100 1020 1540 140015 minutes 1440 1220 1200 1660 156020 minutes 1550 1300 1320 1700 168030 minutes 1700 1480 1500 1800 1760__________________________________________________________________________REFERENCES COMPOSITION 36 COMPOSITION 37 COMPOSITION 38 COMPOSITION Xanthan__________________________________________________________________________ gumNature of water donor CaCl.sub.2 .6H.sub.2 O Ca(C.sub.3 H.sub.5 O.sub.3).sub.2.5H.sub.2 O MgCl.sub.2.6H.sub.2 O Mg(NO.sub. 3).sub.2.6H.sub.2 O --Xanthan gum/water 3.6 5.9 3.2 4.2 --Salt/water 1.0 2.4 0.9 1.4Duration of agitation 5 minutes 200 680 260 500 010 minutes 960 1260 820 1160 24015 minutes 1370 1540 1160 1540 67020 minutes 1600 1660 1380 1700 100030 minutes 1740 1800 1460 1840 1350__________________________________________________________________________
All of the hydrated salts tested resulted in a clear improvement in the rate of dissolution and swelling, with respect to Xanthan gum alone.
The following conclusions are thus reached from the examples:
(i) The combination of Xanthan gum with a water donor improved the rate of dissolution of Xanthan gum and the speed of attainment of maximum viscosity;
(ii) The addition of a surfactant further improved the speed of development of maximum viscosity;
(iii) The preferred composition was the following:
(a) 60% Xanthan gum;
(b) 8.75% finely precipitated silica;
(c) 5% sodium diisopropylnaphthalene sulfonate; and
(d) 26.25% water.
The FIGURE of Drawing illustrates the variation in viscosity of the respective sols, measured at 10 rpm as a function of duration of agitation:
(i) With the preferred composition of the invention (Curve 1);
(ii) With the same composition, but without the surfactant (Curve 2); and
(iii) With Xanthan gum alone (Curve 3).
In these three cases, the concentration of the Xanthan gum was constant and equal to 0.5%. The superiority of the results obtained with the compositions of the invention is thus confirmed.
While the invention has been described in terms of various preferred embodiments, the skilled artisan will appreciate that various modifications, substitutions, omissions, and changes may be made without departing from the spirit thereof. Accordingly, it is intended that the scope of the present invention be limited solely by the scope of the following claims.

Number	Name	Date
3228855	Cadmus et al.	Jan 1966
3578499	Crotty et al.	May 1971
3640826	Lang et al.	Feb 1972
3655579	Crotty et al.	Apr 1972
3801502	Hitzman	Apr 1974
4299790	Greenberg	Nov 1981
4357260	Sandford et al.	Jan 1982

Water soluble biogum compositions and hydrosols prepared therefrom

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

CROSS-REFERENCE TO RELATED APPLICATIONS

US Referenced Citations (7)

Continuations (1)