Water soluble polymer binder for lithium ion battery

Abstract

An electrode for a rechargeable lithium ion battery includes an electro-active material, a (polystyrenebutadiene rubber)-poly (acrylonitrile-co-acrylamide) polymer, and a conductive additive. A battery using the inventive electrode is also disclosed.

Description

FIELD OF INVENTION

The present invention relates to a water soluble polymer binder for use in a rechargeable lithium ion battery and the battery in which the binder is used.

BACKGROUND

Rechargeable batteries use polymer binders to bind the active particulate material together and adhere this particulate material to the current collector in the fabrication of battery electrodes. The binder is generally comprised of one or more polymers. The binders commonly used in commercial li-ion batteries are polyvinyledene fluoride (PVDF), ethylene-propylene and a diene (EPDM). These polymers are generally insoluble in water and, thus are dissolved in an organic solvent such as N-methyl pyrrolidone (NMP). The organic solvent additionally serves as a dispersion medium for the active materials. Some disadvantages of using organic solvents are that they have relatively high cost, can possess negative environmental impacts, and pose disposal issues. Further, PVDF is highly unstable and tends to break down at high temperatures.

Known water soluble binders, such as carboxy methyl cellulose (CMC), require a thickening agent to control the viscosity of the binder. Further, they exhibit only marginal adhesion capability. Polytetrafluoroethylene (PTFE) based water soluble binders also exhibit poor adhesion and do not exhibit good cycle life. Further, other known binders undergo hydrolysis under acid or basic conditions. To avoid the hydrolysis and to improve the dispersion, adhesion to the current collector, in a water-based blending process, the pH must therefore be tightly controlled.

Accordingly, there is a need for a water soluble polymer binder in rechargeable lithium batteries. This water soluble binder should exhibit stability throughout a wide pH range, which results in greater ease in preparing slurry for electrode fabrication.

SUMMARY

Briefly, the present invention provides an electrode comprising an electro-active material, a (polystyrenebutadiene rubber)-poly (acrylonitrile-co-acrylamide) polymer; and a conductive additive.

The present invention also provides a battery comprising a positive electrode mix comprising a positive electrode active material and a water soluble binder comprising a (polystyrenebutadiene rubber)-poly (acrylonitrile-co-acrylamide) polymer. A negative electrode mix comprises a negative electrode active material and a water soluble binder comprising a (polystyrenebutadiene rubber)-poly (acrylonitrile-co-acrylamide) polymer. The battery further comprises an electrolyte.

Further, the present invention provides a battery comprising a positive electrode comprising a positive active material selected from the group consisting of LiNiCoAlO₂, LiMn₂O₄, LiNi_yCo_xM_zO, where M═Mn, Al, Sn, In, Ga or Ti and 0.15<x<0.5, 0.5<y<0.8 and 0<z<0.15, Li[Li_(1−2y)/3Ni_yMn_(2−y)/3]O₂, Li[Li_(1−y)/3Co_yMn_(2−2y)/3]O₂ and Li[Ni_yCo_1−2yMn_y]O₂ where x=(2−y)/3 and 0<y<0.5, LiNiCoO₂.MnO₂, lithium rich compounds Li_1+y(Ni_1/3Co_1/3Mn_1/3)_1−yO₂, where y=(x/(2+x) and x=0-0.33, and xLi₂MnO₃(1−x)Li(NiCoMn)O₂ and Li_(1+y)(Ni_0.5Co_0.2Mn_0.3)_1−yO₂, where y=(x/(2+x) and x=0-0.33, and LiMPO₄, where M is one or more of the first row transition-metal cations selected from the group consisting of V, Cr, Mn, Fe, Co, Ni, and combinations thereof, a water soluble binder comprising a (polystyrenebutadiene rubber)-poly (acrylonitrile-co-acrylamide) polymer, and a conductive additive selected from the group consisting of carbon black, acetylene black, graphite, and combinations thereof. A negative electrode comprises a negative active material selected from the group consisting of graphite, hard carbon, silicon, silicon alloy, tin, tin alloy, and lithium titanate. The negative electrode further comprises a water soluble binder comprising the (polystyrenebutadiene rubber)-poly (acrylonitrile-co-acrylamide) polymer and the conductive additive. The battery also includes an electrolyte comprised of lithium salt in cyclic and linear carbonates or other solvents used in the Li-ion battery electrolyte

BRIEF DESCRIPTION OF THE DRAWINGS

The foregoing summary, as well as the following detailed description of the invention, will be better understood when read in conjunction with the appended drawings. For the purpose of illustrating the invention, there is shown in the drawing certain embodiments of the present invention. It should be understood, however, that the invention is not limited to the precise arrangements shown. In the drawings:

FIG. 1 is a schematic view of a battery formed in a jellyroll configuration according to an exemplary embodiment of the present invention;

FIG. 1A is a schematic view of the battery of FIG. 1 with the electrolyte;

FIG. 2 is a cross-sectional representation of a prismatic electrochemical cell according to an exemplary embodiment of the present invention; and

FIG. 3 is a schematic representation of a positive electrode, a separator and a negative electrode-bi-cell configuration of the exemplary embodiment illustrated in FIG. 1.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

In describing the embodiments of the invention illustrated in the drawings, specific terminology will be used for the sake of clarity. However, the invention is not intended to be limited to the specific terms so selected, it being understood that each specific term includes all technical equivalents operating in similar manner to accomplish similar purpose. It is understood that the drawings are not drawn exactly to scale.

The following describes particular embodiments of the present invention. It should be understood, however, that the invention is not limited to the embodiments detailed herein. Generally, the following disclosure refers to lithium ion batteries and a water soluble binder for use in lithium ion batteries.

Referring to FIGS. 1 and 1A, a rechargeable lithium ion battery 100 according to an exemplary embodiment of the present invention includes a positive electrode 112 formed from a positive electrode mix 110, a negative electrode 122 formed from a negative electrode mix 120, and an electrolyte 130. While FIG. 1 illustrates battery 100 formed in a “jellyroll” configuration, those skilled in the art will recognize that other formations, such as, for example, a prismatic configuration, which is illustrated in FIG. 2, may also be used within the teaching of the present invention.

Positive electrode mix 110 includes a positive electrode active material selected from the group consisting of LiNiCoAlO₂, LiMn₂O₄, LiNi_yCo_xM_zO, where M═Mn, Al, Sn, In, Ga or Ti and 0.15<x<0.5, 0.5<y<0.8 and 0<z<0.15, Li[Li_(1−2y)/3Ni_yMn_(2−y)/3]O₂, Li[Li_(1−y)/3Co_yMn_(2−2y)/3]O₂ and Li[Ni_yCo_1−2yMn_y]O₂ where x=(2−y)/3 and 0<y<0.5, LiNiCoO₂.MnO₂, lithium rich compounds Li_i+y(Ni_1/3Co_1/3Mn_1/3)_1−yO₂, where y=(x/(2+x) and x=0-0.33, and xLi₂MnO₃(1−x)Li(NiCoMn)O₂ and Li_(1+y)(Ni_0.5Co_0.2Mn_0.3)_1−yO₂, where y=(x/(2+x) and x=0-0.33, and LiMPO₄, where M is one or more of the first row transition-metal cations selected from the group consisting of V, Cr, Mn, Fe, Co, Ni, and combinations thereof. In an exemplary embodiment, the positive electrode active material is between about 80 and about 90 percent (by weight) of the positive electrode mix 110.

Positive electrode mix 110 may further include a conductive additive or additives selected from the group consisting of carbon black, acetylene black, graphite and combinations thereof. In an exemplary embodiment, the conductive additive material is between about 0 and about 20 percent (by weight) of the positive electrode mix 110.

Positive electrode mix 110 also includes a water soluble polymer comprising a copolymer of (polystyrenebutadiene rubber)-poly (acrylonitrile-co-acrylamide), and water. The binder is mixed with the positive electrode active material, the conductive additive, and water to form a slurry.

Polystyrenebutadiene rubber is less susceptible than other water soluble binders to hydrolysis under acidic or basic conditions (i.e., pH less than 5 or greater than 10). It has been found that the combination of poly (acrylonitrile-co-acrylamide) into the polystyrenebutadiene rubber, forming a four-monomer-based copolymer, results in a water soluble binder with even more stability than polystyrenebutadiene rubber over a broader pH range. This attribute makes slurry preparation easier than when using prior art water soluble binders because the pH of the slurry does not have to be as tightly controlled throughout the blending process as it had in prior art slurries.

An exemplary (polystyrenebutadiene rubber)-poly (acrylonitrile-co-acrylamide) polymer has the chemical formula:

where a, b, m, and n are each greater than zero and are percentages that add up to 100 percent (or “1”). In an exemplary embodiment, a=b=m=n=0.25. In another exemplary embodiment, a>b and m>n. In an exemplary embodiment, a=0.3, b=0.2, m=0.333, and n=0.167.

In an exemplary embodiment, the mole ratio of styrene units to butadiene units (a:b) is between about 0.5:1.5 and about 1.5:0.5 and the mole ratio of acrylonitrile units to acrylamide units (m:n) is between about 0.5:1.5 and about 1.5:0.5. Further, an exemplary mole ratio of polystyrenebutadiene units to (acrylonitrile-co-acrylamide) units (a+b):(c+d) is between about 0.25:0.75 and about 0.75:0.25.

In an exemplary embodiment, an average molecular weight of the polymer is between about 10,000 and 1,000,000 and in another exemplary embodiment, the average molecular weight of the polymer is between about 100,000 and 200,000.

In an exemplary embodiment, the water soluble binder is between about 1 and about 10 percent (by weight) of positive electrode mix 110.

The water soluble binder is used to make the slurry in the absence of a thickening agent or any external reagent to control its viscosity. An exemplary binder has a viscosity ranging between about 3,000 centipoise and about 50,000 centipoise. The water soluble binder is also provided in the absence of a wetting agent or any other additives to improve the active material and conductive additive dispersion.

The slurry is coated on an aluminum current collector or a carbon coated aluminum current collector to form positive electrode 112. The slurry pH can range between about 7 and about 11.7 without significant reaction with the current collector.

Negative electrode mix 120 comprises a negative electrode active additive or additives material selected from the group consisting of graphite, hard carbon, silicon, silicon alloy, tin, tin alloy, and lithium titanate. In an exemplary embodiment, the negative electrode active material is between about 80 and about 95 percent (by weight) of the negative electrode mix 120.

Negative electrode mix 120 may further include a conductive additive selected from the group consisting of carbon black, acetylene black, graphite and combinations thereof. In an exemplary embodiment, the conductive additive material is between about 0 and about 20 percent (by weight) of the negative electrode mix 120.

Negative electrode mix 120 further comprises the water soluble binder as described above with respect to the positive electrode mix 110. In an exemplary embodiment, the water soluble binder is between about 1 and about 10 percent (by weight) of the negative electrode mix 120. The binder is mixed with the negative electrode active material, the conductive additive, and water to form a slurry. The slurry is coated on a copper current collector to form negative electrode 122.

An exemplary electrolyte 130 may be comprised of lithium salts such as LiBF₄, LiPF₆, LiBOB, LiTFSI or LiFSI or mixtures thereof in cyclic and linear carbonates or other solvent combinations

To form battery 100, after positive electrode 112 and negative electrode 122 are formed, positive electrode 112 and negative electrode 122 are each then compressed or calendared for specific thickness. Electrodes 112, 122 are stacked as shown in FIG. 3, with separator 140 between each positive electrode 112 and negative electrode 122. The stack is dried in a vacuum oven until the moisture is below 2000 ppm, and most preferably below 200 ppm. The electrode may also be dried separately and stacked inside the dry room. The electrode stack may be inserted into a polyethylene or polypropylene cell housing 150, shown in FIG. 2, and filled with electrolyte 130, forming battery 100. Battery 100 is then charged and discharged to complete the forming process.

EXAMPLES

The following examples are given purely as an illustration and should not be interpreted as constituting any kind of limitation to the invention.

The preparation of the binder was by water-phase precipitation polymerization. K₂S₂O₈—Na₂S₂O₅ was used as the initiator system in the presence of Fe²⁺. A round-bottom flask was charged with a solution of 0.225 g (0.8 mmol) potassium persulfate, 0.105 g (0.6 mmol) sodium metabisulfite, and 1 ppm ferrous sulfate in 150 mL of deionized water. A solution of 18.44 g (0.177 mol) styrene, 9.58 g (0.177 mol) butadiene, 9.40 g (0.177 mol) acrylonitrile, and 12.59 g (0.177 mol) acrylamide in 150 mL of deionized water was added to the reaction mixture while being mixed with an overhead stirrer. The reaction was conducted under a nitrogen atmosphere for 2 hours in a water bath controlled at 50° C. The polymer was then filtered and washed with deionized water to remove the unreacted monomers and initiator. The yield was about 53 percent.

The positive active material mix is prepared by mixing between about 10 and about 90 weight percent of active material, between about 0 and about 20 weight percent of conductive additive and between about 1 and about 10 weight percent of the binder polymer disclosed above, and water ranging between 20 to 80 weight percent. High pH is a major problem in the positive active materials, which contains mostly cobalt and nickel or combinations thereof with other transition metals. To control the pH of the positive active material slurry, diluted polymeric acid is added to the slurry very slowly until the pH of the slurry was between about 7 and about 11.7, and most preferably between about 7 and about 10. The reduced pH of the slurry helps to improve the dispersion and the reaction with the current collector is suppressed. Some examples of this carboxylic acid are: Polylactic acid (PLA), Polyacrylic acid, Polysuccinic acid, poly maleic acid and anhydride, poly furoic (pyromucic acid), poly fumaric acid, poly sorbic acid, poly linoleic acid, poly linolenic acid, poly glutamic acid, poly methacrylic acid, poly licanic acid, poly glycolic acid, poly aspartic acid, Poly amic acid, poly formic acid, poly acetic acid, poly propoionic acid, poly butyric acid, poly sebacic acid, and copolymers thereof. The list of polymer acid examples may be equally applied to any other exemplary embodiment(s) of this specification as suitable, and is not exclusive.

The negative active mix is prepared by mixing between about 10 and about 95 weight percent active material, between about 0 and about 20 weight percent of conductive additive and between about 1 and about 10 weight percent of the binder polymer disclosed above. The negative electrode slurry pH is between about 7 and about 10. pH control for the negative active mix is not necessary. The electrolyte in the exemplary embodiment was lithium salt in cyclic and linear carbonates.

The cells were built as described in FIGS. 1-3. The cells were then filled with electrolyte 130.

While the principles of the invention have been described above in connection with preferred embodiments, it is to be clearly understood that this description is made only by way of example and not as a limitation of the scope of the invention.

Claims

1. A battery comprising: a positive electrode mix comprising: a positive electrode active material; anda water soluble binder comprising a (polystyrenebutadiene rubber)-poly (acrylonitrile-co-acrylamide) polymer; anda negative electrode mix comprising: a negative electrode active material; anda water soluble binder comprising a (polystyrenebutadiene rubber)-poly (acrylonitrile-co-acrylamide) polymer; andan electrolyte.

2. The battery according to claim 1, wherein the positive electrode active material comprises between about 80 and about 95 percent (by weight) of the positive electrode mix.

3. The battery according to claim 2, wherein the conductive additive material comprises between about 1 and about 20 percent (by weight) of the positive electrode mix.

4. The battery according to claim 3, wherein the water soluble binder comprises between about 1 and about 10 percent (by weight) of the positive electrode mix.

5. The battery according to claim 1, wherein the negative electrode active material comprises between about 80 and about 95 percent (by weight) of the negative electrode mix.

6. The battery according to claim 5, wherein the conductive additive material comprises between about 0 and about 20 percent (by weight) of the negative electrode mix.

7. The battery according to claim 6, wherein the water soluble binder comprises between about 1 and about 10 percent (by weight) of the negative electrode mix.

8. The battery according to claim 1, wherein the water soluble binder is provided in the absence of a thickening agent.

9. The battery according to claim 1, wherein the water soluble binder is provided in the absence of a wetting agent.

10. The battery according to claim 1, wherein each of the positive electrode mix and the negative electrode mix further comprises a conductive additive.

11. A battery comprising: a positive electrode comprising: a positive active material selected from the group consisting of LiNiCoAlO2, LiMn2O4, LiNiyCoxMzO, where M═Mn, Al, Sn, In, Ga or Ti and 0.15<x<0.5, 0.5<y<0.8 and 0<z<0.15, Li[Li(1−2y)/3NiyMn(2−y)/3]O2, Li[Li(1−y)/3CoyMn(2−2y)/3]O2 and Li[NiyCo1−2yMny]O2 where x=(2−y)/3 and 0<y<0.5, LiNiCoO2.MnO2, lithium rich compounds Li1+y(Ni1/3Co1/3Mn1/3)1−yO2, where y=(x/(2+x) and x=0-0.33, and xLi2MnO3(1−x)Li(NiCoMn)O2 and Li(1+y)(Ni0.5Co0.2Mn0.3)1−yO2, where y=(x/(2+x) and x=0-0.33, and LiMPO4, where M is one or more of the first row transition-metal cations selected from the group consisting of V, Cr, Mn, Fe, Co, Ni, and combinations thereof;a water soluble binder comprising a (polystyrenebutadiene rubber)-poly (acrylonitrile-co-acrylamide) polymer; anda conductive additive selected from the group consisting of carbon black, acetylene black, graphite, and combinations thereof;a negative electrode comprising: a negative active material selected from the group consisting of graphite, hard carbon, silicon, silicon alloy, tin, tin alloy, and lithium titanate;a water soluble binder comprising the (polystyrenebutadiene rubber)-poly (acrylonitrile-co-acrylamide) polymer; andthe conductive additive; andan electrolyte comprised of lithium salt in cyclic and linear carbonates.

12. The battery according to claim 11, wherein a mole ratio of acrylonitrile units to acrylamide units is between about 3:1 and about 1:1.

13. The battery according to claim 11, wherein a mole ratio of styrene units to butadiene units is between about 0.5:1.5 and about 1.5:0.5.

14. The battery according to claim 11, wherein an average molecular weight of the polymer is between about 10,000 and 1,000,000.

15. The battery according to claim 14, wherein the average molecular weight of the polymer is between about 100,000 and 200,000.

16. The battery according to claim 11, wherein the water soluble binder is provided in the absence of a thickening agent.