WATERPROOFING MEMBRANE SYSTEM AND METHOD

Abstract

A waterproofing membrane system for waterproofing a concrete substrate includes a first layer comprising a thermoplastic elastomeric waterproof material using advanced polymerization and squeeze technology. The second layer comprises a carrier sheet that comprises a fabric. The third layer comprises an adhesive to provide bonding of the first layer with a concrete substrate upon contact. In addition, the third layer may reduce migration of water and vapor traveling between the first layer and the concrete substrate. In some examples, the waterproofing membrane system also includes a fourth layer to provide mechanical protection and ease of handling for the first layer, the second layer, and the third layer. In some examples, the first layer comprises a thermoplastic polyolefin (TPO), the fabric comprises polypropylene or polyethylene, the adhesive comprises a C5 petroleum resin, and the fourth layer is a protective coating comprising quartz sand (SiO2) having a reflectivity of 4.5%.

Description

TECHNICAL FIELD

This patent application relates generally to a waterproofing membrane system and method, and more specifically, to systems and methods for waterproofing a concrete substrate and other related waterproofing applications.

BACKGROUND

Laminate sheets are typically used for waterproofing concrete. These laminate sheets, however, are normally applied to a concrete substrate that has already been formed, such as a building foundation. As a result, such laminate sheets are applied on a cured concrete surface. In other concrete applications, laminate sheets can also be applied to concrete that is freshly-poured, or on surfaces that are not yet cured.

Conventional laminate sheets offer limited waterproofing capabilities when applied to either cured or non-cured concrete substrates. The integrity of a waterproofing membrane system is generally based on materials, size, dimensions, and arrangement of various layers. In many cases, conventional laminate sheets do not form an adequate water barrier or are cumbersome to use and install, which also results in poor waterproofing. In addition, conventional laminate sheets lack durability in extreme weather conditions and typically cannot accommodate heavy foot traffic or other physical wear.

As a result, a more robust waterproofing membrane system and method may be imperative to overcome the shortcomings of conventional systems and methods.

BRIEF DESCRIPTION OF DRAWINGS

Features of the present disclosure are illustrated by way of example and not limited in the following Figure(s), in which like numerals indicate like elements, in which:

FIG. 1 illustrates a cross-section of a waterproofing membrane system, according to an example;

FIG. 2 illustrates a cross-section of a waterproofing membrane system, according to another example; and

FIGS. 3A-3C illustrate cross-sections of various waterproofing membrane systems, according to an example.

DETAILED DESCRIPTION

For simplicity and illustrative purposes, the present disclosure is described by referring mainly to examples and embodiments thereof. In the following description, numerous specific details are set forth in order to provide a thorough understanding of the present disclosure. It will be readily apparent, however, that the present disclosure may be practiced without limitation to these specific details. In other instances, some methods and structures readily understood by one of ordinary skill in the art have not been described in detail so as not to unnecessarily obscure the present disclosure. As used herein, the terms “a” and “an” are intended to denote at least one of a particular element, the term “includes” means includes but not limited to, the term “including” means including but not limited to, and the term “based on” means based at least in part on.

As described above, conventional laminate sheets offer limited waterproofing capabilities when applied to either cured or non-cured concrete substrates. They lack durability and cannot accommodate heavy physical wear or extreme conditions. Use and installation of conventional laminate sheets are also cumbersome. In many cases, conventional laminate sheets do not provide an adequate water barrier for which they are created.

FIG. 1 illustrates a cross-section of a waterproofing membrane system 100, according to an example. As shown, the waterproofing membrane system 100 may include various layers. For example, the waterproofing membrane system 100 may have a first layer 102, a second layer 104, a third layer 106, and a fourth layer 108.

The first layer 102 may be a membrane layer. The membrane layer may be made of a thermoplastic elastomeric waterproof material using advanced polymerization together with squeeze technology having high tensile strength and resistant to oxidation and puncture. For example, the membrane may include a thermoplastic polyolefin (TPO). In another example, the membrane may include other various materials, such as elastomer (POE) plastic, EVA plastic, plasticizer, antioxidant, etc.

The second layer 104 may be a carrier sheet. In an example, the carrier sheet may include a fabric made of polypropylene. In some examples, the carrier sheet may be made of 100% polypropylene. Alternatively, the carrier sheet may be made of a fabric that includes a mix of polypropylene and polyethylene.

The third layer 106 may be an adhesive layer. In an example, the adhesive layer may be made of C5 petroleum resin. The adhesive layer may provide bonding of the membrane and concrete upon contact, as well as reduce migration of water and vapor traveling between these two materials.

The fourth layer 108 may be a protective coating. In an example, the protective coating may be made of quartz sand (SiO2) or other similar material(s). In some examples, the protective coating may have a reflectivity of 4.5%. Depending on application or purpose, the reflectivity may be greater than, equal to, or lesser than 4.5%. The protective coating may also provide mechanical protection for the membrane, carrier sheet, and/or adhesive layer as well, so that the surface of the membrane or other layers, for example, may be more easily handled. This may be especially important in transportation, storage, and application the waterproofing membrane on a concrete substrate.

FIG. 2 illustrates a cross-section of a waterproofing membrane system 200, according to another example. As shown, the waterproofing membrane system 200 may be similar to waterproofing membrane system 100 of FIG. 1 and include various layers. In the waterproofing membrane system 200 of FIG. 2, however, there may be only three total layers. The waterproofing membrane system 200 may have a first layer 203, a second layer 206, and a third layer 208. The second layer 206 may be an adhesive layer similar to that of the third layer 106 of FIG. 1, and the third layer 208 may be a protective coating similar to that of the fourth layer 108 of FIG. 1. The first layer 203 may be a carrier sheet that incorporates a membrane-like features. In effect, the first layer 203 may be an integrated version of the first layer 102 and the second layer 104 of FIG. 1.

Other various examples or variations may also be provided. For example, the layers of FIGS. 1 and 2 may be interchangeable, substituted, and/or arranged in an order different than what is shown.

FIGS. 3A-3C illustrate cross-sections of various waterproofing membrane systems, according to an example. FIG. 3A may depict a waterproofing membrane system that includes a single sheet 303. Sheet 303 may be the waterproof membrane system 100 of FIG. 1 or the waterproof membrane system 200 of FIG. 2. Here, sheet 303 may be a homoegenous waterproofing membrane system that does not include any other layer or component. Advantages of a homogeneous waterproofing membrane system is its relatively lightweight nature, making it easier to transport, store, and install.

FIG. 3B may depict a waterproofing membrane system that includes sheet 303 and a backing sheet 305. In an example, the backing sheet 305 may be a woven or a non-woven material. The backing sheet 305 may help with strength, durability of the waterproofing membrane system, or may help with use and installation of the waterproofing membrane system. It may also help protect the waterproofing membrane during transportation, storage, and application. Other various advantages may be apparent.

FIG. 3C may depict a waterproofing membrane system that includes two sheets 303 with a reinforcement sheet 307 therebetween. In an example, reinforcement sheet 307 may be a woven or a non-woven material. reinforcement sheet 307 may help with strength, durability of the waterproofing membrane system, or may help with use and installation of the waterproofing membrane system. It may also help protect the waterproofing membrane during transportation, storage, and application. Other various advantages may be apparent.

In an example, the waterproofing membrane system and method may follow the specifications outlined below in TABLE 1.

TABLE 1
	INDEX
ITEM	H	L (Fleece back)	P
The resin thickness of Middle fabric,	—
mm≥
Maximum tension, N/cm≥	—	200	250
Tension strength, Mpa≥	12	—	—
Maximum tension elongation, %≥	—	—	15
Fracture elongation, %≥	500	250	—
Heat treatment size change rate %≤	2	1	0.5
Low temperature bend	−40° C. No crack
Water tightness	0.3 Mpa, 2 h, No seepage
Attack resistance	0.5 kg m, No seepage
Static charge resistance	—	—	20 kg, No
			seepage
Seam strip strength, N/mm≥	4.0 or	3.0
	Membranes
	break
Right-angle tear strength, N/mm≥	60	—	—
Trapezoid tear strength N≥	—	250	450
Bibulous	After soaking≤	4.0
rate
(70° C.	Air-cure later≥	−0.4
168 h), %
Heat aging	Time	672	h
(115° C.)	Appearance	No
		blister, flaw, delamination, coherence, hole
	Tensile strength	—	90	90
	retention, %≥
	Elongation rate of	90	—	—
	keeping, %≥
	Low-temperature bend	−40° C., No crack
Chemistry	Appearance	No
		blister, flaw, delamination, coherence, hole
	Tensile strength	—	90	90
	retention, %≥
	Elongation rate of	90	—	—
	keeping, %≥
	Low-temperature bending	−40° C., No crack
Artificial	Time	1500	h
weather	Appearance	No
accelerated		blister, flaw, delamination, coherence, hole
aging	Tensile strength	—	90	90
	retention %≥
	Elongation rate of	90	—	—
	keeping %≥
	Low temperature bend	−40° C., No crack

In another example, the waterproofing membrane system and method may follow the specifications outlined below in TABLE 2 and TABLE 3.

TABLE 2
	Dimensions (Nominal)	TPO Waterproofing Membrane System
	Thickness	0.046	in. (1.2 mm)
	Roll size	6 ft. 6 in. × 65 ft. 7 in. (2 m × 20 m)
	Roll area	430	ft2 (40 m2)
	Roll weight	132	lbs (60 kg)
	Minimum side/end laps	3	in. (75 mm)

TABLE 3
		TPO Waterproofing
	Property	Membrane System
	Color	White
	Thickness	0.046	in. (1.2 mm)
	Lateral water migration resistance	Pass at 180 ft (55 m)
	Low temperature flexibility	−40° C. no leaking
	Resistance to hydrostatic head	180	ft (55 m)
	Elongation	612%
	Tensile strength, film	2262	psi (15.6 MPa)
	Crack cyclin at −9.4° F.	Unaffected, Pass
	(−23° C.), 100 cycles
	Puncture resistance	184	lbs (820N)
	Peel adhesion to concrete	4	lbs/in. (700N/m)
	Lap peel adhesian at 72° F. (22° C.)	6.85	lbs/in. (120N/m)
	Lap peel adhesian at 40° F. (4° C.)	5	lbs/in. (900N/m)
	Permeance to water vapor	0/35 MPa × 2 h = 0.7 ng
	transmission

Furthermore, in some examples, weathering between −40° C. through 110° C. may not affect the waterproofing membrane system. The waterproofing membrane system may be environmentally friendly as well, and may not include chlorine and other hazardous materials. The waterproofing membrane system may also be extremely durable and have an effective life of up to 50 years. The waterproofing membrane system may include crack resistance. This waterproofing membrane system may be suitable for the construction of exposed or non-exposed roof waterproof layer. It may also be easy to shape along any surface area to provide waterproofing. In additional to concrete application, the waterproofing membrane system described herein may also be used on light steel roof, not only to reduce the weight of roofing, and excellent saving materials, waterproof and anti-condensation, suit for large industrial plants, public buildings. Other various waterproofing applications may be provided as well, such as for drinking water reservoirs, toilets, basements, tunnels, grain depots, subways, reservoirs, commercial, public, residential applications, etc.

What has been described and illustrated herein are examples of the disclosure along with some variations. The terms, descriptions, and figures used herein are set forth by way of illustration only and are not meant as limitations. Many variations are possible within the scope of the disclosure, which is intended to be defined by the following claims-and their equivalents-in which all terms are meant in their broadest reasonable sense unless otherwise indicated.

Claims

1. A method for forming a unitary waterproofing membrane system, comprising: providing a first waterproof membrane sheet;providing a reinforcement sheet on top of the first waterproof membrane sheet; andproviding a second waterproof membrane sheet on top of the reinforcement sheet,wherein the reinforcement sheet is to secure the first waterproof membrane sheet to the second waterproof membrane sheet, andwherein each of the first and second waterproof membrane sheets is formed by: providing a first layer segment comprising a carrier sheet incorporated with a thermoplastic elastomeric waterproof material,providing a second layer segment on the first layer segment, wherein the second layer segment comprises an adhesive, andproviding a third layer segment on the second layer segment, wherein the third layer segment comprises a protective coating.

2. The method of claim 1, wherein all of edges of the reinforcement sheet, the first waterproof membrane sheet, and the second waterproof membrane sheet are coincident with each other.

3. The method of claim 1, wherein the protective coating of the third layer segment of each of the first and second waterproof membrane sheets comprises quartz sand (SiO2).

4. The method of claim 1, wherein the unitary waterproofing membrane system withstands weather temperature between −40° C. through 110° C.

5. The method of claim 1, wherein the thermoplastic elastomeric waterproof material of the first layer segment of each of the first and second waterproof membrane sheets comprises thermoplastic polyolefin (TPO).

6. The method of claim 1, wherein the carrier sheet of the first layer segment of each of the first and second waterproof membrane sheets comprises a fabric made of polypropylene.

7. The method of claim 1, wherein the adhesive of the second layer segment of each of the first and second waterproof membrane sheets comprises C5 petroleum resin.

8. The method of claim 1, wherein the protective coating of the third layer segment of each of the first and second waterproof membrane sheets comprises a predetermined percentage of reflectivity.

9. A method for forming a unitary waterproofing membrane system, comprising: providing a first waterproof membrane sheet;providing a reinforcement sheet on top of the first waterproof membrane sheet; andproviding a second waterproof membrane sheet on top of the reinforcement sheet,wherein the reinforcement sheet is to secure the first waterproof membrane sheet to the second waterproof membrane sheet, andwherein the first waterproof membrane sheet is formed by: providing a first layer segment comprising a thermoplastic elastomeric waterproof material,providing a second layer segment on the first layer segment, wherein the second layer segment comprises an adhesive, andproviding a third layer segment on the second layer segment, wherein the third layer segment comprises a protective coating.

10. The method of claim 9, wherein all of edges of the reinforcement sheet, the first waterproof membrane sheet, and the second waterproof membrane sheet are coincident with each other.

11. The method of claim 9, wherein the protective coating of the third layer segment of each of the first and second waterproof membrane sheets comprises quartz sand (SiO2).

12. The method of claim 9, wherein the unitary waterproofing membrane system withstands weather temperature between −40° C. through 110° C.

13. The method of claim 9, wherein the thermoplastic elastomeric waterproof material of the first layer segment of each of the first and second waterproof membrane sheets comprises thermoplastic polyolefin (TPO).

14. The method of claim 9, wherein the carrier sheet of the first layer segment of each of the first and second waterproof membrane sheets comprises a fabric made of polypropylene.

15. The method of claim 9, wherein the adhesive of the second layer segment of each of the first and second waterproof membrane sheets comprises C5 petroleum resin.

16. The method of claim 9, wherein the protective coating of the third layer segment of each of the first and second waterproof membrane sheets comprises a predetermined percentage of reflectivity.