Patent Application
20050111808
The present invention relates generally to the field of waveguides. In particular, the present invention relates to compositions suitable for use in forming flexible optical waveguides. The invention further relates to methods of forming flexible optical waveguides. As well, the invention relates to flexible optical waveguides and to electronic devices that include a flexible optical waveguide.
Signal transmission using pulse sequences of light is becoming increasingly important in high-speed communications. For example, optical integrated circuits (OICs) are gaining importance for high bandwidth optical interconnects. As a result, the integration of optical components such as waveguides, filters, optical interconnects, lenses, diffraction gratings, and the like, is becoming increasingly important. Optical waveguides are typically constructed by surrounding a core material with a clad layer. Optical radiation propagates in the core material because the clad layer has a lower index of refraction than the core material. Waveguides may be used individually or as an array supported on a substrate. The waveguides often perform a passive function on the optical radiation. For example, splitters divide an optical signal in one waveguide into two or more waveguides; couplers add an optical signal from two or more waveguides into a smaller number of waveguides; and wavelength division multiplexing (“WDM”) structures separate an input optical signal into spectrally discrete output signals, each of which couples to separate waveguides, usually by employing either phase array designs or gratings. Spectral filters, polarizers, and isolators may be incorporated into the waveguide. As well, waveguides may alternatively contain active functionality, wherein the input signal is altered by interaction with a second optical or electrical signal. Exemplary active functionality includes amplification and switching such as with electro-optic, thermo-optic or acousto-optic devices.
Waveguide substrates include, for example silicon wafers and circuit backplanes for use in server devices. The ability to handle waveguides without crack defects in the core and/or cladding materials is desirable. The cracking property generally is a result of brittleness in the coating material. Many organic polymer-based waveguides such as polyimides are flexible, but have other drawbacks such as moisture absorption, high losses and expense. Silicon-based systems, which address various shortcomings of organic polymer systems, are generally brittle resulting in crack defects as a result of handling.
Photoimageable waveguide cores have been proposed wherein portions of the coating are dissolved in an organic solvent to generate the desired structures. This technique has the drawback of using organic solvents that are difficult to dispose of, waste treat and/or contain in a closed environment. It is therefore desirable to have the option of using aqueous developers to create waveguide structures from photoimageable coatings.
Hybrid silicon-carbon polymer systems have been proposed which address brittleness in interlayer dielectric coatings, especially for pore generating compositions, for microcircuit applications. (See, e.g., Chandross et al, U.S. Pat. No. 6,251,486). These systems are typically coated, cured and reactive ion etched using standard lithographic procedures to create desired structures. This technique is not intended for and would not be useful with aqueous based development.
There is thus a need in the art for compositions suitable for use in manufacturing optical waveguides, which compositions provide beneficial flexibility characteristics while also being developable in an aqueous developer solution. As well, there is a need in the art for waveguides formed from these compositions, for methods of forming such waveguides, and for electronic devices that include such waveguides.
One aspect of the invention provides compositions suitable for use in manufacturing flexible optical waveguides. The compositions include a polymer, having: units of the formula (R1SiO1.5) and (R22SiO), wherein R1 and R2 are the same or different, and are substituted and/or unsubstituted organic groups, and wherein the (R22SiO) units are present in an amount of 14 wt % or more based on the polymer; and a plurality of functional end and/or internal groups; and a component for altering the solubility of the composition upon activation. The solubility of the composition in a dried state is alterable upon activation of the component such that the composition is developable in an aqueous developer solution.
In a second aspect of the invention, a flexible optical waveguide is provided. The waveguide has a core and a clad, wherein the core and/or the clad are formed from a composition that includes a polymer having units of the formula (R1SiO1.5) and (R22SiO), wherein R1 and R2 are the same or different, and are substituted or unsubstituted organic groups, and wherein the (R22SiO) units are present in an amount of 14 wt % or more based on polymer; and a plurality of functional end and/or internal groups; and a component for altering the solubility of the composition upon activation. The solubility of the composition in a dried state is alterable upon activation of the component such that the composition is developable in an aqueous developer solution.
In a third aspect of the invention, provided is an electronic device that comprises a flexible optical waveguide as described above.
In a fourth aspect of the invention, methods of forming a flexible optical waveguide are provided. The methods involve: (a) forming a layer over a substrate from a composition that includes: a polymer, having: polymerized units of the formula (R1SiO1.5) and (R22SiO), wherein R1 and R2 are the same or different and are substituted or unsubstituted organic groups, and wherein the (R22SiO) units are present in an amount of 14 wt % or more; and a plurality of functional end or internal groups; and a component for altering the solubility of the composition upon activation, wherein the solubility of the composition in a dried state is alterable upon activation of the component such that the composition is developable in an aqueous developer solution; and (b) activating at least a portion of the layer, wherein the layer is a core or a clad layer.
The present invention will be discussed with reference to the following drawings, in which like reference numerals denote like features, and in which:
The present invention provides compositions suitable for use in forming flexible optical waveguides. Unless otherwise specified, amounts for components of the composition are given in weight % based on the composition absent any solvent. As used herein, the term “polymer” includes oligomers, dimers, trimers, tetramers and the like, and encompasses homopolymers and higher order polymers, i.e., polymers formed from two or more different monomer units and heteropolymers. The term “alkyl” refers to linear, branched and cycloalkyl groups, which are substituted or unsubstituted and can include heteroatoms in or on the chain. The term “aromatic” refers to aromatic groups, which are substituted or unsubstituted and can include heterocycles. The terms “a” and “an” mean “one or more”.
The term “in a dried state” means a composition containing 10 wt % or less of a solvent, based on the entire composition. The term “wherein the solubility of the composition in a dried state is alterable” means that the solubility of the composition is alterable for any (not necessarily every) solvent content in the range of 10 wt % or less.
The term “developable in an aqueous developer solution” means that, in the case of a negative-working material, the composition, when (i) coated to a thickness of 8 μm in a dried state on a silicon wafer, and (ii) then placed in a 2N NaOH developer solution, a 2N KOH developer solution or a 2N TMAH developer solution, or a 1N solution thereof, or a 0.7N solution thereof, or even a 0.26N solution thereof at a temperature of from 70 to 180° F. (21 to 82.2° C.) with either static or spray developing at 40 psi impinging spray and is completely dissolved within ten minutes, or within two minutes, or even within one minute, or even within 30 seconds.
The term “flexible” or “flexibility” as it relates to the described optical waveguides refers to the ability of the compositions in the dried state to be coated onto copper foil and bent around a conical Mandrel bar without cracking or crazing. The specifics of the conical Mandrel test are well know in the coatings industry as exemplified by ASTM D522-93a (Reapproved 2001).
The compositions include a polymer that has polymerized units of the formula (R1SiO1.5) and (R22SiO), wherein R1 and R2 are the same or different, and are substituted or unsubstituted organic groups, and a plurality of functional end and/or internal groups. The compositions further include a component for altering the solubility of the composition upon activation. The solubility of the composition in a dried state is alterable upon activation of the component such that the composition is developable in an aqueous developer solution.
The silicon-containing polymers useful in the present invention include, for example, siloxanes, silsesquioxanes, and caged siloxanes and combinations thereof. The silicon-containing polymer may be present in the composition in an amount of from 1 to 99.5 wt %, for example from 60 to 98.5 wt %. Exemplary organic groups for R1 and R2 include substituted and unsubstituted alkyl, aryl and heterocyclic groups. The alkyl groups can be straight chain, branched or cyclic having, for example, from 1 to 20 carbon atoms, and typically have from 1 to 20 carbon atoms, such as methyl, ethyl, propyl, isopropyl, t-butyl, t-amyl, octyl, decyl, dodecyl, cetyl, stearyl, cyclohexyl, and 2-ethylhexyl. The alkyl groups can be substituted with heteroatoms in and/or on the alkyl chain, for example, or can be non-aromatic cyclic groups such as cyclopentyl, cyclohexyl, norbonyl, adamantly, piperidinyl, tetrahydrofuranyl and tetrahydrothiophenyl groups. Exemplary aryl groups include those having from 6 to 20 carbon atoms, for example, from 6 to 15 carbon atoms, such as phenyl, tolyl, benzyl, 1-naphthyl, 2-naphthyl and 2-phenanthryl, and can be substituted with heteroatoms. Heterocyclic groups can be aromatic, for example, thiophene, pyridine, pyrimidine, pyrrole, phosphole, arsole, and furane.
Typical for R1 and R2 are substituted and unsubstituted methyl, ethyl, propyl, cyclopentyl, cyclohexyl, benzyl, phenyl, adamantyl groups, and combinations thereof It is believed that inclusion of the R22SiO component in the polymer imparts a higher level of flexibility than the polymer without it. The R1SiO1.5 units are typically present in the polymer in an amount of from 1 to 86 wt %, for example, from 15 to 80 wt % or from 25 to 60 wt %, or from 25 to 50 wt %, based on the polymer. The R22SiO polymerized units are typically present in the polymer in an amount of 14 wt % or more, for example, from 14 to 99 wt % or from 14 to 60 wt %, or from 14 to 50 wt %, based on the polymer.
The silicon-containing polymer can take the form of a copolymer or higher order polymer, either random- or block-type. The polymer can include, for example, one or more additional silicon-containing unit, with the proportions for each unit ranging from 1 to 85 wt %, for example, from 15 to 80 wt % or from 25 to 60 wt %, or from 25 to 50 wt %, based on the polymer. The additional units can, for example, be represented as siloxanes, silsesquioxanes, cage siloxanes and/or combinations thereof. For example, the polymer can further include polymerized units of the formula (R3SiO1.5), wherein R3 is a substituted or unsubstituted organic group as described above with respect to R1. One of R1 and R3 can, for example, be chosen from substituted or unsubstituted alkyl groups, and the other of R1 and R3 chosen from substituted or unsubstituted aryl groups.
The polymer can be, for example, an alkyl silicon-containing polymer such as a polymer containing methyl silsesquioxane units and dimethylsiloxane units; an aryl silicon-containing polymer such as a polymer containing phenyl silsesquioxane units and ditolyl siloxane units or an aralkyl silicon-containing polymer such as a polymer containing methyl and phenyl silsesquioxane units and diphenyl siloxane units.
As described above, the side chain groups of the polymer can be optionally substituted. “Substituted” means that one or more hydrogen atoms on the side chain groups is replaced by another substituent group, for example, deuterium, halogen such as fluorine, bromine, and chlorine, (C1-C6)alkyl, (C1-C6)haloalkyl, (C1-C10)alkoxy, (C1-C10)alkylcarbonyl, (C1-C10)alkoxycarbonyl, (C1-C10)alkylcarbonyloxy, alkylamine, alkylsulfur containing materials, and the like. The silicon-containing polymers may contain a wide range of repeating units, either random or block. The silicon polymer units useful in the present invention may have, for example, from 5 to 150 repeating units, typically from about 10 to 35 repeating units; and the siloxane units useful in the present invention may have for example from 5 to 150 repeating units, typically from about 7 to 25 repeating units. Thus, the silicon-containing polymer may vary widely in molecular weight. Typically, the polymers have a weight average molecular weight (Mw) of from about 500 to 15,000, more typically from about 1000 to 10,000, even more typically from about 1000 to 5000. It has been found that the dissolution rate of the compositions in accordance with the invention in an aqueous developer decreases with an increase in the molecular weight Mw and number average molecular weight, Mn.
The silicon-containing polymers further include two or more functional end and/or internal groups that allow condensation polymerization to occur. Such end and/or internal groups can be, for example, hydroxy, alkoxy such as ethoxy, propoxy, isopropoxy, carboxyester, amino, amido, epoxy, imino, carboxyacid, anhydride, olefinic, acrylic, acetal, orthoester, vinyl ether, and combinations thereof. Of these, hydroxy groups are typical. The functional end and/or internal content in the polymer is present from about 0.5 to 35 wt % based on the polymer, for example from about 1 to 10 wt %, or from about 2 to 5 wt %.
The described polymer materials can be prepared by known methods with readily available starting materials. For example, a 42.5:42.5:15 methyl-phenyl-dimethyl silicon containing copolymer can be synthesized by condensation reaction of 42.5 wt % methyl-triethoxy-silane, 42.5 wt % phenyl-triethoxy-silane, and 15 wt % dimethyl-diethoxysilane. An active component is also present in the composition to allow the composition to be alterable in its solubility in aqueous developer. In the case of a negative working material, it is thought that the active component catalyzes coupling of exposed portions of the silicon-containing polymer composition, rendering the coupled portions insoluble in an aqueous developer. A wide variety of active components may be used in the present invention, including, but not limited to, photoacid generators, photobase generators, thermal acid generators and thermal base generators. Of these, photoacid and thermal acid generators, components generating an acid upon activation, are typical.
The photoacid generators useful in the present invention can be any compound or compounds which generate acid upon exposure to light. Suitable photoacid generators are known and include, but are not limited to, halogenated triazines, onium salts, sulfonated esters, substituted hydroxyimides, substituted hydroxylimines, azides, naphthoquinones such as diazonaphthoquinones, diazo compounds, and combinations thereof.
Particularly useful halogenated triazines include, for example, halogenated alkyl triazines such as the trihalomethyl-s-triazines. The s-triazine compounds are condensation reaction products of certain methyl-trihalomethyl-s-triazines and certain aldehydes or aldehyde derivatives. Such s-triazine compounds may be prepared according to the procedures disclosed in U.S. Pat. No. 3,954,475 and Wakabayashi et al., Bulletin of the Chemical Society of Japan, 42, 2924-30 (1969). Other triazine type photoacid generators useful in the present invention are disclosed, for example, in U.S. Pat. No. 5,366,846.
Onium salts with weakly nucleophilic anions are particularly suitable for use as photoacid generators in the present invention. Examples of such anions are the halogen complex anions of divalent to heptavalent metals or non-metals, for example, antimony, tin, iron, bismuth, aluminum, gallium, indium, titanium, zirconium, scandium, chromium, hafnium, copper, boron, phosphorus and arsenic. Examples of suitable onium salts include, but are not limited to, diazonium salts such as diaryl-diazonium salts and onium salts of group VA and B, IIA and B and I of the Periodic Table, for example, halonium salts such as iodonium salts, quaternary ammonium, phosphonium and arsonium salts, sulfonium salts such as aromatic sulfonium salts, sulfoxonium salts or selenium salts. Examples of suitable onium salts are disclosed, for example, in U.S. Pat. Nos. 4,442,197; 4,603,101; and 4,624,912. Sulfonium salts such as triphenylsulfonium hexafluorophosphate and mixtures thereof are preferred.
The sulfonated esters useful as photoacid generators in the present invention include, for example, sulfonyloxy ketones. Suitable sulfonated esters include, but are not limited to, benzoin tosylate, t-butylphenyl alpha-(p-toluenesulfonyloxy)-acetate, 2,6-dinitrobenzyl tosylate, and t-butyl alpha-(p-toluenesulfonyloxy)-acetate. Such sulfonated esters are disclosed, for example, in the Journal of Photopolymer Science and Technology, vol. 4, No. 3,337-340 (1991).
Substituted hydroxyimides which can be used include, for example, n-trifluoromethylsulfonyloxy-2,3-diphenylmaleimide and 2-trifluoromethylbenzenesulfonyloxy-2,3-diphenylmaleimide. Suitable substituted hydroxylimines include, for example, 2-(-nitrilo-2-methylbenzylidene)-(5-hydroxyiminobutylsulfonyl)-thiophene. Azides useful in the present invention include, for example, 2,6-(4-azidobenzylidene)cyclohexanone. Naphthoquinones can include, for example, 2,1-diazonaphthoquinone-4-sulfonate ester of 2,3,4-trihydroxybenzophenone. Among the diazo compounds, 1,7-bis(4-chlorosulonyl phenyl)-4-diazo-3,5-heptanedione can be used.
Photobase generators useful in the present invention can be any compound or compounds which liberate base upon exposure to light. Suitable photobase generators include, but are not limited to, benzyl carbamates, benzoin carbamates, O-carbamoylhydroxyamines, O-carbamoyloximes, aromatic sulfonamides, alpha-lactams, N-(2-allylethenyl)amides, arylazide compounds, N-arylformamides, 4-(ortho-nitrophenyl)dihydropyridines, and combinations thereof.
Thermal acid generators useful in the present invention can be any compound or compounds which generate an acid on heat activation. The heat can be supplied by indirect methods such as convection heating or by direct heating methods such as laser heating techniques.
Suitable thermal acid generators are known and include, but are not limited to, halogenated triazines, ammonium salts of acids, onium salts, sulfonated esters, substituted hydroxyimides, substituted hydroxylimines, azides, naphthoquinones such as diazonaphthoquinones, diazo compounds, and combinations thereof.
The amount of active component useful in the present invention, in the case of a negative working material, is any amount sufficient to catalyze coupling of the silicon-containing polymer upon exposure to actinic radiation or heat to render the coupled portion insoluble in an aqueous developer. The active component is typically present in the composition in an amount of from 0.01 to 25 wt %, for example, from 0.05 to 12 wt %.
One or more additional flexibility enhancing ingredients can optionally be included in the compositions of the invention to further enhance the flexibility of the formed coatings or other products formed from the compositions. Suitable flexibilizer materials include, for example, polysiloxanes and plasticizers such as long chain alkyds and dibasic esters. Typically, the flexibilizer has two or more groups in its chain that are capable of coupling with the silicon-containing polymer. Such groups include, for example, hydroxy, alkoxy, carboxyester, amino, amido, epoxy, imino, carboxyacid, anhydride, olefinic, acrylic, acetal, orthoester, vinyl ether, and combinations thereof. Plasticizing ingredients may be used to further improve the flexibility to the desired level. Exemplary polysiloxane flexibilizer materials include polysiloxanes terminated with functional groups such as silanol-terminated polydiphenylsiloxanes and silanol-terminated polydimethylsiloxanes, typically in which the endgroups consist only of functional groups. The additional flexibility enhancing agent is typically present in the composition in an amount of less than 30 wt %, for example, less than 20 wt %.
Other additives may optionally be present in the compositions of the invention including, but are not limited to, surface leveling agents, wetting agents, antifoam agents, adhesion promoters, thixotropic agents, and the like. Such additives are well known in the art for coating compositions. The use of surface leveling agents, for example silicone-base oils such as S
The compositions of the invention can optionally contain one or more organic cross-linking agents. Cross-linking agents include, for example, materials which link up components of the composition in a three-dimensional manner. Aromatic or aliphatic cross-linking agents that react with the silicon-containing polymer are suitable for use in the present invention. Such organic cross-linking agents will cure to form a polymerized network with the silicon-containing polymer, and reduce solubility in a developer solution. Such organic cross-linking agents may be monomers or polymers. It will be appreciated by those skilled in the art that combinations of cross-linking agents may be used successfully in the present invention.
Suitable organic cross-linking agents useful in the present invention include, but are not limited to: amine containing compounds, epoxy containing materials, compounds containing at least two vinyl ether groups, allyl substituted aromatic compounds, and combinations thereof. Typical cross-linking agents include amine containing compounds and epoxy containing materials.
The amine containing compounds useful as cross-linking agents in the present invention include, but are not limited to: melamine monomers, melamine polymers, alkylolmethyl melamines, benzoguanamine resins, benzoguanamine-formaldehyde resins, urea-formaldehyde resins, glycoluril-formaldehyde resins, and combinations thereof.
It will be appreciated by those skilled in the art that suitable organic cross-linker concentrations will vary with factors such as cross-linker reactivity and specific application of the composition. When used, the cross-linking agent(s) is typically present in the composition in an amount of from 0.1 to 50 wt %, for example, from 0.5 to 25 wt % or from 1 to 20 wt %.
The present compositions can optionally contain one or more solvents. Such solvents aid in formulating the present compositions and in coating the present compositions on a substrate. A wide variety of solvents may be used. Suitable solvents include, but are not limited to, glycol ethers, such as ethylene glycol monomethyl ether, propylene glycol monomethyl ether, dipropylene glycol monomethyl ether; esters such as methyl cellosolve acetate, ethyl cellosolve acetate, propylene glycol monomethyl ether acetate, dipropylene glycol monomethyl ether acetate, dibasic esters, carbonates such as propylene carbonate, γ-butyrolactone, esters such as ethyl lactate, n-amyl acetate and n-butyl acetate, alcohols such as n-propanol, iso-propanol, ketones such as cyclohexanone, methyl isobutyl ketone, diisobutyl ketone and 2-heptanone, lactones such as γ-butyrolactone and γ-caprolactone, ethers such as diphenyl ether and anisole, hydrocarbons such as mesitylene, toluene and xylene, and heterocyclic compounds such as N-methyl-2-pyrrolidone, N,N′-dimethylpropyleneurea, or mixtures thereof.
The compositions of the present invention can be prepared by combining, in admixture, the silicon-containing polymer, the catalytic component, and other optional components in any order.
The present compositions are particularly suitable for use in the manufacture of flexible optical waveguides. Optical waveguides can be used in forming opto-electrical devices including, but not limited to, splitters, couplers, spectral filters, polarizers, isolators, multiplexers such as wavelength division multiplexing structures, amplifiers, attenuators, switches, and the like or, on a larger scale, in electronic devices such as printed wiring boards, integrated circuits, interconnects, and the like. The present photodefinable compositions are also particularly useful in manufacturing display devices including lenses as well as optical elements such as mirrors, prisms and connectors. As used herein, the term electronic device is intended to encompass opto-electronic devices, for example, those described above, as well as the aforementioned larger scale devices that include an opto-electronic device.
The waveguides of the present invention may be manufactured as individual waveguides or as an array of waveguides. A method of preparing a waveguide using the inventive composition involves: (a) forming a layer over a substrate from a composition as described above, and (b) activating at least a portion of the layer, wherein the layer is a clad and/or a core layer. The compositions of the current invention are suitable for use in forming waveguide clad and/or core structures. For purposes of example only, a method of forming a flexible optical waveguide having clad and core structures formed from the inventive compositions will be described. A waveguide is formed by depositing core and first and second cladding layers. The clad of the final structure has a lower index of refraction as compared to the core. Particularly useful waveguides include a core having an index of refraction of from 1.4 to 1.7 and a cladding having an index of refraction of from 1.3 to 1.69.
With reference to
A first cladding layer 4 can be formed on the substrate surface 2. The first cladding layer 4 (as well as the other waveguide layers to be described) may be formed from the compositions of the invention, by any technique including, but not limited to, screen printing, curtain coating, roller coating, slot coating, spin coating, flood coating, electrostatic spray, spray coating, or dip coating. When the compositions and constructs of the present invention are spray coated, a heated spray gun may optionally be used. The viscosity of the composition may be adjusted to meet the requirements for each method of application by viscosity modifiers, thixotropic agents, fillers and the like. The first cladding layer is deposited to a thickness in the dried state of from about 1 to 100 μm, for example, from about 10 to 50 μm.
The first cladding layer 4 can be cured, for example, thermally or photolytically depending on the type of active component in the first cladding composition. The thermal curing temperature is from 90° C. to 300° C., for example from 90° C. to 220° C. Such curing typically occurs over a period of from five seconds to one hour. Such curing may be affected by heating the substrate in an oven or on a hot plate. Alternatively the waveguide clad can be flood exposed, for example, with 1 to 2 Joules/cm2 of actinic radiation followed by the thermal cure from 90° C. to 300° C., for example from 90° C. to 220° C.
A core layer 6 is formed on the first clad layer formed from the composition of the invention. The core layer is coated to a thickness of from about 1 to 100 μm, for example, from about 8 to 60 μm. The coated substrate is then soft cured, such as by baking, to remove solvent in the coating. Such curing may take place at various temperatures, depending upon the particular solvent chosen. Suitable temperatures are any that are sufficient to substantially remove any solvent present. The soft curing may be at any temperature from room temperature (25° C.) to 300° C. depending, for example, on the substrate and the thermal budget. Such curing can occur, for example, over a period of from 5 seconds to 60 minutes in an oven or on a hot plate.
After curing, the layer of the present composition can then be imaged by exposure to actinic radiation. Such methods include, for example, contact imaging, projection imaging, and laser direct write imaging, including laser direct write imaging by multiphoton absorption. Multiphoton absorption can, if desired, be used to form 3-dimensional structures within the layer. The exposure pattern, as defined, for example, by mask 8 in
The unexposed areas may be removed, such as by contact with a suitable developer, leaving only the exposed areas remaining on the substrate, thus forming core structures 6′ in
Such development may be at a variety of temperatures such as from room temperature to about 65° C., for example from 21 to 49° C. Development time with aggressive agitation can be within ten minutes, for example, within five minutes, within two minutes, within one minute, or within 30 seconds. Development can take place, for example, in a static development chamber or on a conveyorized platform upon which developer is sprayed. Spray pressures can range from 5 to 40 psi, for example, from 10 to 25 psi.
Following development, the present waveguides may undergo a final cure step. The curing can, for example, include a flood exposure, for example, with 1 to 2 Joules/cm2 of actinic radiation. Additionally, or alternatively, the waveguides may be heated at a temperature of from about 130° to 300° C. in air or an inert atmosphere such as nitrogen or argon. Next, a second cladding layer 10 can be formed as described above over the first cladding layer 4 and core structure 6′. The second cladding layer may be the same or different from the first cladding layer. The second cladding layer can be thermally activated and/or photo activated to provide a waveguide structure as described above with respect to the first clad layer. The second cladding layer is typically deposited to a thickness of from about 1 to 100 μm, for example, from about 10 to 50 μm.
Optical waveguides of the present invention possess excellent transparencies at a variety of wavelengths. Thus, the present optical waveguides may be used at, for example, 600 to 1700 nm. It will be appreciated that the present optical waveguides may be advantageously used at other wavelengths. Thus, the present optical waveguides are particularly suited for use in data communications and telecommunications applications.
The following examples are intended to illustrate further various aspects of the present invention, but are not intended to limit the scope of the invention in any aspect. The wt % as used in the examples are based on full compositions including solvent.
32.67 wt % propylene glycol monomethyl ether acetate, 61.1 wt % phenyl-methyl-silsesquioxane (50:50 wt % based on polymer), 0.11 wt % diphenylnaphthylsulfonium tosylate, 6.06 wt % tetramethylolmethyl glycoluril and 0.06 wt % Dow S
32.67 wt % propylene glycol monomethyl ether acetate, 61.1 wt % phenyl-methyl-dimethyl silsesquioxane (42.5:42.5:15 wt % based on polymer), 0.11 wt % diphenylnaphthylsulfonium tosylate, 6.06 wt % tetramethylolmethyl glycoluril and 0.06 wt % Dow S
Example 1 was repeated, but the coating thickness obtained after spin-coating was 60 μm. No cracking of the waveguide was found.
50 wt % propylene glycol monomethyl ether acetate, 49 wt % phenyl-dimethyl silsesquioxane (50:50 wt % based on polymer), 0.99 wt % triphenylsulfonium hexafluorophosphate, and 0.01 wt % Dow S
45 wt % propylene glycol monomethyl ether acetate, 50 wt % of phenyl-methyl-dimethyl-silsesquioxane (40:40:20 wt % based on polymer), 4.95 wt % benzoin tosylate, and 0.05 wt % Dow S
37 wt % propylene glycol monomethyl ether acetate, 57.99 wt % methyl-diphenyl silsesquioxane (50:50 wt % based on polymer), 5 wt % triphenylsulfonium trifluoromethylsulphonate, and 0.01 wt % Dow S
Clad (1) Layer
A first cladding layer composition is formed by combining in admixture of 50 wt % propylene glycol monomethyl ether acetate, 44.99 wt % phenyl-methyl-dimethylsilsesquioxane (37.5:47.2:15 wt % based on polymer), 5 wt % triphenylsulfonium trifluoromethylsulphate and 0.01 wt % Dow S
Core
The first cladding layer is coated with the core composition of Example 1 and patterned and cure as described in Example 1.
Clad (2) Layer
A second cladding layer composition is formed over the patterned core and first cladding layer using the same composition (but with reduced solvent to increase the solids to 69 wt %) and procedures used in forming the first cladding layer, except the thickness of the second cladding layer after the soft-bake is 25 μm. It is expected that flexible optical waveguides are formed.
Clad (1) Layer
A first cladding layer composition is formed by combining in admixture 39 wt % propylene glycol monomethyl ether acetate, 56 wt % phenyl-methyl-dimethylsilsesquioxane (40:40:20 wt % based on polymer), 4.99 wt % of amine blocked dodecylphenylsulphate, and 0.01 wt % Dow S
Core
The first cladding layer is coated with the core composition of Example 2 and is patterned and cured as described in Example 2
Clad (2) Layer
A second cladding layer composition is formed over the patterned core and first cladding layer using the same composition (but with reduced solvent to increase the solids to 69 wt %) and procedures used in forming the first cladding layer, except the thickness of the second cladding layer after the soft-bake is 60 μm. It is expected that flexible optical waveguides are formed.
Clad (1) Layer
A first cladding layer composition is formed by combining in admixture of 50 wt % propylene glycol monomethyl ether acetate, 44.99 wt % phenyl-methyl-dimethylsilsesquioxane (42.5:42.5:15 wt % based on polymer), 5 wt % triphenylsulfonium trifluoromethylsulphate and 0.01 wt % Dow S
Core
The first cladding layer is coated with the core composition of Example 3 and patterned and cure as described in Example 3.
Clad (2) Layer
A second cladding layer composition is formed over the patterned core and first cladding layer using the same composition (but with reduced solvent to increase the solids to 65 wt %) and procedures used in forming the first cladding layer, except the spin-coating speed is 1250 rpm and the thickness of the second cladding layer after the soft-bake is 12 μm. It is expected that flexible optical waveguides are formed.
Clad (1) Layer
A first cladding layer composition is formed by combining in admixture 39 wt % propylene glycol monomethyl ether acetate, 56 wt % phenyl-methyl-dimethylsilsesquioxane (40:40:20 wt % based on polymer), 4.99 wt % of amine blocked dodecylphenylsulphate, and 0.01 wt % Dow S
Core
The first cladding layer is coated with the core composition of Example 4 and is patterned and cured as described in Example 4.
Clad (2) Layer
A second cladding layer composition is formed over the patterned core and first cladding layer using the same composition (but with reduced solvent to increase the solids to 69 wt %) and procedures used in forming the first cladding layer, except the thickness of the second cladding layer after the soft-bake is 60 μm. It is expected that flexible optical waveguides are formed.
While the invention has been described in detail with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made, and equivalents employed, without departing from the scope of the claims.
This application claims the benefit under 35 U.S.C. § 119(e) of U.S. Provisional Application No. 60/525,010, filed Nov. 25, 2003, the entire contents of which are incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| 60525010 | Nov 2003 | US |