Claims
- 1. In a sintered ceramic product consisting essentially of
- (a) from about 40 to about 98 percent silicon nitride,
- (b) from about 2 to about 60 percent of silicides of at least one metal selected from the group consisting of iron, nickel and cobalt, and
- (c) up to about 20 percent of at least one oxide, nitride or silicate of an element selected from IUPAC group 2, 3, 4, 13 or the lanthanide series, all percentages being by weight based on the total weight of the product,
- the improvement comprising an alpha-to-beta ratio of silicon nitride in the sintered ceramic product that falls within area A of FIG. 1 and a content of high metal-content silicides in the sintered ceramic product that is at least 50% by weight of the silicides present.
- 2. The sintered product of claim 1 wherein up to 50% by weight of the silicon nitride is replaced by at least one refractory carbide, nitride other than silicon nitride, or boride.
- 3. In a process for preparing a sintered ceramic product comprising
- (1) intimately mixing a powder mixture consisting essentially of
- (a) from about 50 to about 98 percent silicon nitride,
- (b) from about 1 to about 50 percent of at least one metal selected from the group consisting of iron, nickel and cobalt, or an oxide or alloy thereof, and
- (c) from 0.02 to about 20 percent of at least one oxide, nitride or silicate of an element selected from IUPAC group 2, 3, 4, 13 or the lanthanide series, all percentages being by weight based on the total weight of the powder mixture,
- (2) reacting the components of the powder mixture by heating to a temperature of 1300.degree.-1700.degree. C. in a non-oxidizing atmosphere until component 1(b) is completely converted to its corresponding silicides, and
- (3) maintaining the powder mixture at a temperature of 1300.degree.-1700.degree. C. in the non-oxidizing atmosphere until the composition formed in (2) densifies,
- the improvement comprising reacting the components of the powder mixture until the alpha-to-beta ratio of silicon nitride in the sintered ceramic product falls within area A of FIG. 1 and at least 50% by weight of the silicides in the sintered ceramic product are high metal-content silicides.
- 4. The process of claim 3 wherein the heating of the powder mixture is carried out at a pressure of at least 500 psi.
- 5. The process of claim 4 wherein the pressure is 2000-6000 psi.
- 6. The process of claim 3 wherein the non-oxidizing atmosphere is a nitrogen atmosphere.
- 7. The process of claim 3 wherein up to 50% by weight of the silicon nitride is replaced by at least one refractory carbide, nitride other than silicon nitride, or boride.
- 8. The process of claim 3 wherein the powder mixture comprises 50-93% by weight of silicon nitride, 5-25% by weight of at least one metal selected from the group consisting of iron, nickel and cobalt, 1-10% by weight of at least one oxide of IUPAC group 3 elements or the lanthanide series, and 1-5% by weight of aluminum oxide.
- 9. The process of claim 8 wherein fully stabilized zirconium oxide, partially stabilized zirconium oxide or hafnium oxide is substituted for all or part of the oxide of IUPAC group 3 elements or the lanthanide series.
- 10. The process of claim 3 wherein the powder mixture comprises 50-93% by weight of silicon nitride, 5-25% by weight of at least one metal selected from the group consisting of iron, nickel and cobalt, 1-10% by weight of at least one oxide of IUPAC group 2 elements, and 1-5% by weight of aluminum oxide.
- 11. The process of claim 10 wherein fully stabilized zirconium oxide or hafnium oxide is substituted for all or part of the oxide of IUPAC group 2 elements.
- 12. A wear resistant cutting tool prepared from the sintered ceramic product of claim 1.
- 13. A wear resistant cutting tool prepared from the sintered ceramic product of claim 2.
Parent Case Info
This application is a continuation-in-part of Ser. No. 07/336,397 filed Apr. 11, 1989 now U.S. Pat. No. 5,023,214.
US Referenced Citations (5)
Number |
Name |
Date |
Kind |
3409417 |
Vatis |
Nov 1968 |
|
4093687 |
Greskovich et al. |
Jun 1978 |
|
4124402 |
Greskovich et al. |
Nov 1978 |
|
4332909 |
Nishida et al. |
Jun 1982 |
|
4407971 |
Kamatsu et al. |
Oct 1983 |
|
Foreign Referenced Citations (8)
Number |
Date |
Country |
262654 |
Apr 1981 |
EPX |
71997 |
Feb 1983 |
EPX |
57-200266 |
Aug 1982 |
JPX |
64269 |
Apr 1983 |
JPX |
58-64269 |
Apr 1983 |
JPX |
144058 |
Aug 1983 |
JPX |
176109 |
Oct 1983 |
JPX |
477379 |
Oct 1969 |
CHX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
336397 |
Apr 1989 |
|