One aspect is a feedthrough for a medical implantable device including a ferrule having a metal that is configured to be welded to a case of the implantable device. The ferrule substantially surrounds an insulator and shares an interface therewith, the insulator having a glass or ceramic material. Conductive elements are formed through the insulator providing an electrically conductive path through the insulator. There is no braze or solder at the interface between the ferrule and the insulator and that there is no braze or solder adjacent the conductive elements.
Description
BACKGROUND

One aspect relates to a feedthrough device for an implantable medical device. Feedthroughs establish an electrical connection between a hermetically sealed interior and an exterior of the medical device. Known implantable therapeutic devices include cardiac pacemakers or defibrillators, which usually include a hermetically sealed metal housing, which is provided with a connection body, also called header, on one side. Said connection body includes a connection socket for connecting electrode leads. In this context, the connection socket includes electrical contacts that serve to electrically connect electrode leads to the control electronics in the interior of the housing of the implantable therapeutic device—also called implantable device. An essential prerequisite for an electrical bushing of this type is hermetic sealing with respect to the surroundings.


Accordingly, it needs to be made sure that the conducting wires that are introduced into an insulation element and via which the electrical signals proceed, are introduced into the insulation element without any gaps. In this context, it has proven to be disadvantageous that the conducting wires in general are made of a metal and need to be introduced into a ceramic insulation element. In order to ensure long-lasting connection between the two elements, the internal surface of the bore hole in the insulation element must be metallized for soldering the conducting wires into them. Said metallization inside the bore hole in the insulation element has proven to be difficult to apply. Homogeneous metallization of the internal surface of the bore hole in the insulation element can be ensured only by means of expensive procedures. Alternatively or in addition to, brazing may be used to connect the wires to the insulation element. Both metallization and brazing, however, can lead to leaks over time.


For these and other reasons there is a need for the present invention.





BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings are included to provide a further understanding of embodiments and are incorporated in and constitute a part of this specification. The drawings illustrate embodiments and together with the description serve to explain principles of embodiments. Other embodiments and many of the intended advantages of embodiments will be readily appreciated as they become better understood by reference to the following detailed description. The elements of the drawings are not necessarily to scale relative to each other. Like reference numerals designate corresponding similar parts.



FIGS. 1A and 1B illustrate a feedthrough device in accordance with the prior art.



FIG. 2 illustrates a cross-sectional view of a feedthrough assembly in an implantable medical device in accordance with one embodiment.



FIGS. 3A and 3B respectively illustrate cross-sectional and plan views of a feedthrough assembly in accordance with one embodiment.



FIG. 4 illustrates a feedthrough assembly and method of forming in accordance with one embodiment.



FIG. 5 illustrates a flow diagram of a method of forming a feedthrough assembly in accordance with one embodiment.



FIG. 6 illustrates a cross-sectional view of a feedthrough assembly in an implantable medical device in accordance with one embodiment.



FIG. 7 illustrates a cross-sectional view of a feedthrough assembly in an implantable medical device in accordance with one embodiment.





DETAILED DESCRIPTION

In the following Detailed Description, reference is made to the accompanying drawings, which form a part hereof, and in which is shown by way of illustration specific embodiments in which the invention may be practiced. In this regard, directional terminology, such as “top,” “bottom,” “front,” “back,” “leading,” “trailing,” etc., is used with reference to the orientation of the Figure(s) being described. Because components of embodiments can be positioned in a number of different orientations, the directional terminology is used for purposes of illustration and is in no way limiting. It is to be understood that other embodiments may be utilized and structural or logical changes may be made without departing from the scope of the present invention. The following detailed description, therefore, is not to be taken in a limiting sense, and the scope of the present invention is defined by the appended claims.


It is to be understood that the features of the various exemplary embodiments described herein may be combined with each other, unless specifically noted otherwise.


In accordance with one embodiment, a method of coupling an insulator to a surrounding ferrule in an implantable medical device is provided. An insulator is provided having a plurality of conducting elements extending therethrough. The insulator is placed with conducting elements within a ferrule having a frame-like shape surrounding the insulator along an interface. The insulator is heated with a first laser until raising the temperature of insulator to a first temperature level. The ferrule is welded to the insulator along the interface with a second laser once the insulator has reached the first temperature.


Normally, the energy level required to weld the ferrule to the insulator along the interface is so fast and locally restricted that the ceramic of the insulator would normally crack. Because the first laser first gradually raises the temperature of the ceramic insulator before the weld, however, the thermal shock of the welding is minimized.


In one embodiment, the temperature of the insulator is maintained with the first laser while the second laser welds the insulator to the ferrule. This can continue to maintain the reduction in thermal shock during welding to further minimize any cracking. In one embodiment, the first laser is controlled to scan the entire surface of the insulator.


In one embodiment, the conducting elements are provided in the insulator such that they do not extend past a surface of the insulator. As such, the first laser is able to scan the entire surface of the insulator without interference from the conducting elements.


In one embodiment, the insulator is provided free of braze such that the first laser is able to scan the entire surface of the insulator without melting any braze. As such, the hermeticity of feedthrough is not compromised by melting of braze.


In one embodiment, the first laser is a CO2 laser configured to scan the insulator and bring its temperature up into the range of 1,300 to 1,600 degrees centigrade. In one embodiment, the first laser is controlled to ramp the temperature of the insulator from room temperature to between 1,300 and 1,600 degrees Centigrade at a rate of 100-150 degrees Centigrade per second. In one embodiment, the first laser is controlled to ramp down the temperature of the insulator at a rate of 100-150 degrees Centigrade per second until the temperature reaches 300 degrees Centigrade. Controlling the temperature in these ways can help prevent cracking the insulator material.


In one embodiment, the ferrule is provided with an inner edge that is tapered, wherein the insulator has an outer edge that is also tapered to match the inner edge of the ferrule, which can provide advantages in holding the ferrule relative to the insulator during welding.


In one embodiment, a feedthrough for a medical implantable device includes a ferrule comprising a metal that is configured to be welded to a case of the implantable device. An insulator is substantially surrounded by the ferrule and shares an interface therewith. The insulator comprises a glass or ceramic material. Conductive elements are formed through the insulator providing an electrically conductive path through the insulator. There is no braze or solder at the interface between the ferrule and the insulator and there is no braze or solder adjacent the conductive elements. With no braze or solder at the interfaces, there is reduced risk of leak and the hermiticity of the feedthrough is preserved.


In one embodiment, the ferrule comprises one of a group comprising niobium, titanium, titanium alloy, molybdenum, cobalt, zirconium, chromium and platinum, the insulator comprises aluminum oxide and the conductive elements comprise a cermet. These materials allow the avoidance of any brazing to secure hermetic seals in the feedthrough.


In one embodiment, the ferrule is configured with an inner edge that is tapered and the insulator is configured with an outer edge that is tapered to match the inner edge of the ferrule. In one embodiment, the taper of the respective edges of the ferrule and the insulator are tapered at an angle of 5 to 15 degrees relative to a line running perpendicular to a top surface of the feedthrough. The taper angle of the edges of the insulator and the ferrule at the interface allows the insulator to seat easily in the ferrule before the two are welded together along the interface. The taper angle of the outer edges of the insulator against the corresponding inner edges of the ferrule prevents relative movement of the ferrule and the insulator during assembly and welding.


In one embodiment, the distance between the ferrule and the insulator along the interface is no larger than 25 microns. Keeping the gap at the interface less than 25 microns minimized cracking of the insulator during welding.


In one embodiment, a method of welding an insulator in an implantable medical device in provided. An insulator is provided having a plurality of conducting elements extending therethrough. The insulator with conducting elements is placed within a metallic case surrounding the insulator at an interface. The insulator is heated with a first laser until raising the temperature of insulator to a first temperature level. The case is welded to the insulator with a second laser once the insulator has reached the first temperature.



FIGS. 1A and 1B illustrate respective perspective and sectional views of feedthrough device 10, such as for an implantable medical device, in accordance with the prior art. Feedthrough device 10 includes ferrule 12, insulator 14 and feedthrough pins 16. Ferrule 12 is a frame-like structure with an internal opening into which insulator 14 is formed and through which feedthrough pins 16 extend. Insulator 14 facilitates feedthrough pins 16 extending through the frame-like structure of ferrule 12 in a non-conductive manner.


Ferrule 12 is configured to fit into an opening of a case for an implantable medical device and such that it can be tightly secured thereto in order to ensure a hermetic seal with respect to an internal space of the medical device. Feedthrough pins 16 extend from within the internal space of the case of the medical device to outside the device, thereby providing electrical connection from the inside to the outside, while maintaining a hermetic seal. Flanges 22 can be provided on ferrule 12 to further aid in securing feedthrough device 10 to the opening of the case of the implantable medical device and ensuring its hermetic seal.


Typically, insulator 14 is a ceramic or glass material, while ferrule 12 is metallic. Ferrule 12 is metallic so that it can be readily welded to a metallic case of the implantable medical device. In order for the ceramic material of insulator 14 to be coupled to the metallic material of ferrule 12, insulator 14 is typically “metalized” with metalized coating 20. Alternatively, a metallic braze is used to secure ceramic material of insulator 14 to the metallic material of ferrule 12. Similarly, braze 18 is used to couple the ceramic material of insulator 14 to feedthrough pins 16, which are metallic conductors.


Use of braze 18 to secure insulator 14 to feedthrough pins 16 and to secure insulator 14 to ferrule 12, and/or the need for metalized coating 20 to secure insulator 14 to ferrule 12 creates extra processing steps and adds to the complication and expense of manufacturing feedthrough device 10. Such braze 18 and metallization 20 can also lead to leaks and failure of a hermitic seal for feedthrough device 10.



FIG. 2 illustrates implantable medical device 100 in accordance with one embodiment. Implantable medical device 100 includes feedthrough assembly 102 and case 104. Feedthrough assembly 102 includes ferrule 110, insulator 112 and conducting elements 114. In one embodiment, ferrule 110 is a frame-like structure into which insulator 112 and conducting elements 114 are formed. In one embodiment, feedthrough assembly 102 is welded to case 104 such that an interior 120 of case 104 is hermetically sealed relative to its exterior 122.


In the exemplary embodiment according to FIG. 1, ferrule 110 is configured to be essentially frame-shaped and secured to case 104 thereby defining an internal space 120 and an external space 122. Ferrule 110 can be of a variety of shapes, for example, it can be a disc-shaped, round, an oval or a polygonal, in one embodiment a rectangular or square, cross-section in a sectional plane perpendicular to the drawing plane in FIG. 1. However, other cross-sections are also feasible as a general rule. The disc of ferrule 110 can be arranged, fully in the external space 122, in the internal space 120, or straddling the two as illustrated in FIG. 1.


In one embodiment, ferrule 110 of feedthrough assembly 102 is a metallic material, as is case 104, such that feedthrough assembly 102 is readily weldable to case 104. In one embodiment, conducting elements 114 are of an electrically conductive material such that they provide a conductive path from internal space 120 to external space 122 of case 104. Insulator 112 is of a non-electrically conductive material such that there is no conductive connection between ferrule 110 and conducting elements 114. All of the interfaces between insulator 112 and conducting elements 114 and between insulator 112 and ferrule must be sealed in such a way that a hermetic seal is maintained between internal space 120 and external space 122 of case 104. In one embodiment, all of these interfaces are so sealed without the use of braze or solder, as will be more fully explained below.



FIG. 3A illustrate a cross sectional view of feedthrough assembly 102 in accordance with one embodiment. FIG. 3B illustrates feedthrough assembly 102 viewed from a “lower” side relative to how it is depicted in FIG. 3A. In one embodiment, feedthrough assembly 102 is assembled by forming insulator 112 and conducting elements 114 in a first process. In one embodiment, insulator 112 is a ceramic material, such as aluminum oxide (Al2O3), and conducting elements 114 are a cermet material.


In the context of one embodiment, the terms, “cermet” or “cermet-containing,” shall refer to all composite materials made of ceramic materials in a metallic matrix (binding agent). These are characterized by their particularly high hardness and wear resistance. The “cermets” and/or “cermet-containing” substances are cutting materials that are related to hard metals, but contain no tungsten carbide hard metal and are produced by powder metallurgical means. A sintering process for cermets and/or the cermet-containing elements proceeds just like with homogeneous powders with the exception that the metal is compacted more strongly at the same pressuring force as compared to the ceramic material. The cermet-containing bearing element has a higher thermal shock and oxidation resistance than sintered hard metals. In most cases, the ceramic components of the cermet are aluminum oxide (Al2O3) and zirconium dioxide (ZrO2), whereas niobium, molybdenum, titanium, cobalt, zirconium, chromium and platinum are conceivable as metallic components.


The ceramic of insulator 112 can be, for example, a multi-layer ceramic sheet into which a plurality of vias is introduced. The cermet of conducting elements 114 is then introduced into the vias. In one embodiment, both materials are introduced in a green state, and as such, the combination is fired together. Accordingly, the joining of the insulator 112 and conducting elements 114 forms a hermetic seal therebetween without the use of braze or solder.


In accordance with one embodiment, insulator 112 is secured to ferrule 110 to form a hermetic seal therebetween, also without the use of braze of solder. In order to secure insulator 112 to ferrule 110, they are laser welded together. In one embodiment, a two-part laser welding process is used. In one embodiment, a first laser is scanned across insulator 112 in order to heat up the ceramic. Once an appropriate level of heat is reached, a second laser is used to perform a weld to join the insulator 112 to ferrule 110. In one embodiment, a first laser is used to scan both insulator 112 and ferrule 110 both before and after welding with a second laser.



FIG. 4 illustrates feedthrough assembly 102 in accordance with one embodiment. In one embodiment, ferrule 110 is joined to insulator 112 along interface 130 using a laser weld. In order to prepare interface 130 for a laser weld, a first laser 140 scans insulator 112 in order to raise the temperature of insulator 112. In one embodiment, first laser 140 is a CO2 laser that is configured to scan over the ceramic material of insulator 112 in order to raise the temperature of the ceramic. In one embodiment, first laser 140 scans over insulator 112 to bring its temperature up into the range of 1,300 to 1,600 degrees centigrade.


Once this temperature range is achieved, a second laser 150 is used to weld along interface 130 between ferrule 110 and insulator 112. In one embodiment, second laser 150 is a YAG or fiber laser, which welds ferrule 110 to insulator 112 while first laser 140 maintains the temperature of insulator 112. Because second laser 150 produces a fast and locally restricted energy along interface 130, it would normally crack a material like ceramic of insulator 112. Accordingly, using first laser 140 to first raise the temperature of the ceramic of insulator 112 before application of the localized energy of second laser 150 minimizes the thermal shock of the welding by second laser 150.


In one embodiment, ferrule 110 is a material that is selected to have a coefficient of thermal expansion that is similar to that of the material of insulator 112. In one embodiment, insulator 112 is aluminum oxide (Al2O3) and ferrule 110 is niobium. Because aluminum oxide (Al2O3) has a coefficient of thermal expansion of 8.5×10−6/C and niobium has a coefficient of thermal expansion of 8.7×10−6/C, both materials will shrink a very similar amount after the heat of first and second lasers 140 and 150 is removed, such that there will be very little stress or cracking at the weld along interface 130. As such, the hermitic seal that is established by welding ferrule 110 to case 104 will not leak.


In one embodiment, a material selected for insulator 112 will have a coefficient of thermal expansion (CTE) that is within 25 percent of the CTE of the material selected for ferrule 110. In one embodiment, the CTE of the materials are kept similar, or within 25 percent of each other, such that the helium leak rate for implantable medical device 100, once feedthrough assembly 102 is secured to case 104, is less than 3.0 E-09 Atm cc/sec.


In other embodiments, other metals with similar coefficients of thermal expansion can be used for ferrule 110 in conjunction with an aluminum oxide (Al2O3) insulator 112. For example, zirconium (ZrO2) having a CTE of 8.6×10−6/C, titanium (grade 2) having a CTE of 10.1×10−6/C, and titanium −45 niobium (grade 36) having a CTE of 10.6×10−6/C may also be used in some embodiments.


In one embodiment, first laser 140 is controlled to focus its energy on insulator 112 and also onto ferrule 110. Heating both the ceramic of insulator 112 and the metal of ferrule 110 before the weld can improve the quality of the weld. In one embodiment, it is also important that first laser 140 continues to maintain the heated temperature of insulator 112 while second laser 150 performs the weld at interface 130.


In one embodiment, ferrule 110 is particularly configured for heating with first laser 140 before welding with second laser 150. As illustrated in FIGS. 1A and 1B, a feedthrough device 10 having feedthrough pins 16 extending through insulator 14 will is not readily heated by a laser. Because feedthrough pins 16 extend well beyond the surface of insulator 14, they will tend to interfere with a laser that needs to scan the entire surface of the insulator in order to heat it up sufficiently before welding with another laser.


In addition, feedthrough device 10 also requires braze 18 to seal feedthrough pins 16 relative to insulator 14. As such, even if a laser were able to somehow navigate around feedthrough pins 16 to scan the entire surface of insulator 14, braze 18 would likely re-flow from the heat caused by the laser. Typically, braze 18 is a metal such as gold, and its melting point is below the temperature to which first laser 140 will heat the insulator and adjacent material, such as braze 18. This would very likely compromise the seal between feedthrough pins 16 and insulator 14 and potentially cause leaking.


As previously indicated, feedthrough assembly 102 in accordance with one embodiment includes conducting elements 114 that are introduced into vias within insulator 112. In some embodiments, conducting elements 114 may be configured to extend beyond the top and bottom surfaces of insulator 112, and in other embodiments, conducting elements can be configured to be flush with one or both surfaces. As illustrated in FIG. 3A, for example, conducting elements 114 are configured to be flush or aligned with both top and bottom surfaces of insulator 112. In this configuration, first laser 140 is able to readily scan the entire surface of insulator 112 without inference from anything projecting from the surface. Furthermore, because conducting elements 114 and insulator 112 are sealed with a co-sintering process such that no braze is used, scanning first laser 140 over the surface of insulator 112 will not cause problems in re-flowing braze.


In one embodiment, the distance between ferrule 110 and insulator 112 along interface 130 is controlled such that the structures are snugly fitted before being welded by second laser 150. If a significant gap exists between ferrule 110 and insulator 112, some cracking can occur during the welding process. In one embodiment, the distance between ferrule 110 and insulator 112 at any location along interface 130 is no larger than 25 microns. As such, when the two materials are welded, cracking of insulator 112 is minimized.



FIG. 5 is a flow diagram illustrating a process 200 of making a feedthrough assembly in accordance with one embodiment. In a first step 210, conductive elements are introduced into an insulator. In one embodiment, the conductive elements are either formed to be flush with the surfaces of the insulator or are milled or ground to be flush. At step 220, the conductive elements and insulator are placed in a frame-like ferrule. The insulator and ferrule are immediately adjacent each other forming an interface.


At step 230, a first laser is scanned over the entire surface of the insulator in order to bring up the temperature of the insulator. In one embodiment, the insulator is heated from room temperature to between 1,300 and 1,600 degrees Centigrade. In one embodiment, the first laser is controlled to ramp the temperature from room temperature to between 1,300 and 1,600 degrees Centigrade at a rate of 100-150 degrees Centigrade per second. In one embodiment, heating at this rate will not cause the insulator material to fracture or crack. In one embodiment, while the first laser is directed to scan the entire surface of the insulator, and in one embodiment is directed so as to additionally scan the ferrule that surrounds the insulator.


At step 240, a second laser is used to weld the ferrule to the insulator along the interface therebetween. In one embodiment, the first laser continues to scan the insulator, while the second laser welds the ferrule to the insulator, in order to maintain the temperature on the insulator. In one embodiment, the first laser continues to maintain the temperature of the insulator between 1,300 and 1,600 degrees Centigrade while the second laser welds the ferrule to the insulator. In one embodiment, once the entire interface is welded, the first laser is controlled to allow the temperature to ramp down at a controlled rate. In one embodiment, the first laser is controlled to ramp down the temperature at a rate of 100-150 degrees Centigrade per second until the temperature reaches 300 degrees Centigrade. Then, the first laser can be turned off or can be controlled to continue ramping down until the temperature reaches room temperature.



FIG. 6 illustrates implantable medical device 300 in accordance with one embodiment. Implantable medical device 300 includes feedthrough assembly 302 and case 304. Feedthrough assembly 302 includes ferrule 310, insulator 312 and conducting elements 314. In one embodiment, ferrule 310 is a frame-like structure into which insulator 312 and conducting elements 314 are formed. In one embodiment, feedthrough assembly 302 is welded to case 304 such that an interior 320 of case 304 is hermetically sealed relative to its exterior 322.


In one embodiment, ferrule 310 has an inner edge that is tapered and insulator 312 has an outer edge that is also tapered to match the inner edge of ferrule 310 at interface 330. In one embodiment, the edges at interface 330 are tapered at a taper angle α relative to a line running perpendicular to the top surface of feedthrough assembly 302. In one embodiment, taper angle α is between 5 and 15 degrees. In one embodiment, the taper angle α of the edges of insulator 312 and ferrule 310 at interface 330 allows insulator 312 to seat easily in ferrule 310 before the two are welded together along interface 330. The taper angle α of the outer edges of insulator 312 against the corresponding inner edges of ferrule 310 prevents relative movement of ferrule 310 and insulator 312 during assembly and welding.


In one embodiment, once insulator 312 is seated against ferrule 310, insulator 312 is heated with a first laser as described above with prior embodiments. After a temperature range is reached, a second laser is directed at the interface 330 between ferrule 310 and insulator 312 such that ferrule 310 is welded to insulator 312, similar to that described above with respect to feedthrough assembly 102.



FIG. 7 illustrates implantable medical device 400 in accordance with one embodiment. Implantable medical device 400 includes feedthrough assembly 402 and case 404. Feedthrough assembly 402 includes insulator 412 and conducting elements 414. As is evident from a comparison of FIG. 7 to FIG. 6 or FIG. 2, feedthrough assembly 402 does not include a ferrule such that insulator 412 is welded directly to case 404 such that an interior 420 of case 404 is hermetically sealed relative to its exterior 422.


In one embodiment, feedthrough assembly 402 includes insulator 412 with an outer edge that is tapered and case 404 has an inner edge that is also tapered to match the outer edge of insulator 412. Once feedthrough assembly 402 is placed in an opening of case 404, insulator 412 is heating with a first laser as described above with prior embodiments. After a temperature range is reached, a second laser is directed at the interface between case 404 and insulator 412 such that case 404 is welded to feedthrough assembly 402. Since case 404 is typically metallic, such as consisting of titanium, the second laser welds the metallic case to the insulator 412 similarly to that described above for how the ferrule and insulator are welded together.


Attaching feedthrough assembly 402 directly to case 404 without the need of a ferrule simplifies the assembly process and steps, reduces parts and material, and reduces overall time and cost.


Although specific embodiments have been illustrated and described herein, it will be appreciated by those of ordinary skill in the art that a variety of alternate and/or equivalent implementations may be substituted for the specific embodiments shown and described without departing from the scope of the present invention. This application is intended to cover any adaptations or variations of the specific embodiments discussed herein. Therefore, it is intended that this invention be limited only by the claims and the equivalents thereof.

Claims
  • 1. A feedthrough for a medical implantable device comprising: a ferrule comprising a metal that is configured to be welded to a case of the implantable device;an insulator at least partially surrounded by the ferrule and sharing an interface therewith,the insulator comprising a glass or ceramic material that is characterized by the absence of any material that will flow when heated to a temperature between 1,300 and 1,600 degrees C. at the interface between the insulator and case;conductive elements formed through the insulator providing an electrically conductive path through the insulator;characterized in that there is no braze or solder at the interface between the ferrule and the insulator and that there is no braze or solder adjacent the conductive elements; andwherein the ferrule is configured with an inner edge that is tapered and the insulator is configured with an outer edge that is tapered to match the inner edge of the ferule,the taper of each at an angle of 5 to 15 degrees relative to a line running perpendicular to a top surface of the feedthrough.
  • 2. The feedthrough of claim 1, wherein the ferrule comprises one of a group comprising niobium, titanium, titanium alloy, molybdenum, cobalt, zirconium, chromium and platinum and the insulator comprises aluminum oxide.
  • 3. The feedthrough of claim 1, wherein the conductive elements comprise a cermet.
  • 4. The feedthrough of claim 3, wherein the conducting elements comprising cermet are provided in the insulator such that they do not extend past a surface of the insulator.
  • 5. The feedthrough of claim 1, wherein the distance between the ferrule and the insulator along the interface is no larger than 25 microns.
  • 6. The feedthrough of claim 1, wherein the conductive elements, the insulator, the ferrule and any interface between them are free of braze and solder or other material that will flow when heated to a temperature between 1,300 and 1,600 degrees C.
CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional of U.S. patent application Ser. No. 14/991,329, entitled “WELDED FEEDTHROUGH”, having a filing date of Jan. 8, 2016, which is a divisional of U.S. patent application Ser. No. 13/804,888, entitled “LASER WELDING A FEEDTHROUGH,” having a filing date of Mar. 14, 2013, now U.S. Pat. No. 9,478,959, both of which are incorporated herein by reference.

US Referenced Citations (176)
Number Name Date Kind
3979187 Scherer Sep 1976 A
4152540 Duncan et al. May 1979 A
4217137 Kraska et al. Aug 1980 A
4315054 Sack et al. Feb 1982 A
4352951 Kyle Oct 1982 A
4354964 Hing et al. Oct 1982 A
4362792 Bowsky et al. Dec 1982 A
4456786 Kyle Jun 1984 A
4488673 Hopper, Jr. Dec 1984 A
4602956 Partlow et al. Jul 1986 A
4678868 Kraska et al. Jul 1987 A
4737601 Gartzke Apr 1988 A
4774953 Foote Oct 1988 A
4782209 Caers et al. Nov 1988 A
4816621 Huebner et al. Mar 1989 A
4991582 Byers et al. Feb 1991 A
4992910 Evans Feb 1991 A
5043535 Lin Aug 1991 A
5046262 Kerbaugh Sep 1991 A
5245999 Dahlberg et al. Sep 1993 A
5272283 Kuzma Dec 1993 A
5306891 Fleming et al. Apr 1994 A
5333095 Stevenson et al. Jul 1994 A
5407119 Churchill et al. Apr 1995 A
5408066 Trapani et al. Apr 1995 A
5513793 Malmgren May 1996 A
5515604 Horine et al. May 1996 A
5654106 Purnell et al. Aug 1997 A
5683435 Truex et al. Nov 1997 A
5693580 Brow Dec 1997 A
5738270 Malmgren Apr 1998 A
5750926 Schulman et al. May 1998 A
5769874 Dahlberg Jun 1998 A
5782891 Hassler et al. Jul 1998 A
5796019 Lupton et al. Aug 1998 A
5821011 Taylor et al. Oct 1998 A
5851222 Taylor et al. Dec 1998 A
5855711 Araki et al. Jan 1999 A
5861714 Wei et al. Jan 1999 A
5866851 Taylor et al. Feb 1999 A
5870272 Seifried et al. Feb 1999 A
5905627 Brendel et al. May 1999 A
6093476 Horiuchi et al. Jul 2000 A
6232004 Lasater May 2001 B1
6284080 Haq et al. Sep 2001 B1
6414835 Wolf et al. Jul 2002 B1
6579492 Wehler Jun 2003 B2
6586675 Bealka et al. Jul 2003 B1
6643903 Stevenson et al. Nov 2003 B2
6660116 Wolf et al. Dec 2003 B2
6999818 Stevenson et al. Feb 2006 B2
7035076 Stevenson Apr 2006 B1
7035077 Brendel Apr 2006 B2
7038900 Stevenson et al. May 2006 B2
7068491 Burdon et al. Jun 2006 B1
7107099 O'Phelan et al. Sep 2006 B1
7136273 Stevenson et al. Nov 2006 B2
7145076 Knappen et al. Dec 2006 B2
7174219 Wahlstrand et al. Feb 2007 B2
7174223 Dalton et al. Feb 2007 B2
7222419 Horng et al. May 2007 B2
7260434 Lim et al. Aug 2007 B1
7274963 Spadgenske Sep 2007 B2
7437817 Zhang et al. Oct 2008 B2
7480988 Ok et al. Jan 2009 B2
7502217 Zhao et al. Mar 2009 B2
7561917 Wegrzyn, III et al. Jul 2009 B2
7564674 Frysz et al. Jul 2009 B2
7569452 Fu et al. Aug 2009 B2
7630768 Coffed et al. Dec 2009 B1
7668597 Engmark et al. Feb 2010 B2
7706124 Zhao et al. Apr 2010 B2
7720538 Janzig et al. May 2010 B2
7736191 Sochor Jun 2010 B1
7742817 Malinowski et al. Jun 2010 B2
7747321 Fischbach et al. Jun 2010 B2
7761165 He et al. Jul 2010 B1
7765005 Stevenson Jul 2010 B2
7794256 Sochor Sep 2010 B1
7818876 Suaning Oct 2010 B2
7901761 Jiang et al. Mar 2011 B1
7930032 Teske et al. Apr 2011 B2
7970474 Starke Jun 2011 B2
7989080 Greenberg et al. Aug 2011 B2
8000804 Wessendorf et al. Aug 2011 B1
8065009 Biggs Nov 2011 B2
8131369 Taylor et al. Mar 2012 B2
8131376 Faraji et al. Mar 2012 B1
8155743 Rundle et al. Apr 2012 B2
8163397 Ok et al. Apr 2012 B2
8179658 Brendel et al. May 2012 B2
8189333 Foster May 2012 B2
8288654 Taylor et al. Oct 2012 B2
8346362 Kinney et al. Jan 2013 B2
8355785 Hammond et al. Jan 2013 B1
8391983 Lim Mar 2013 B2
8494635 Troetzschel et al. Jul 2013 B2
8497435 Nagata et al. Jul 2013 B2
8528201 Troetzschel et al. Sep 2013 B2
8552311 Koester et al. Oct 2013 B2
8656736 Terao Feb 2014 B2
8659870 Brendel et al. Feb 2014 B2
8742268 Reisinger et al. Jun 2014 B2
8755887 Troetzschel et al. Jun 2014 B2
8825162 Reisinger Sep 2014 B2
8886320 Troetzschel et al. Nov 2014 B2
8894914 Pavlovic Nov 2014 B2
8929987 Troetzschel et al. Jan 2015 B2
9478959 Markham et al. Oct 2016 B2
20010013756 Mori et al. Aug 2001 A1
20010018012 Harmand et al. Aug 2001 A1
20010034966 Golubkov et al. Nov 2001 A1
20010041227 Hislop Nov 2001 A1
20020139556 Ok et al. Oct 2002 A1
20020166739 Naerheim Nov 2002 A1
20030109903 Berrang et al. Jun 2003 A1
20040023101 Jacobson et al. Feb 2004 A1
20040116976 Spadgenske Jun 2004 A1
20040128016 Stewart Jul 2004 A1
20060025866 Serafin, Jr. et al. Feb 2006 A1
20060247714 Taylor et al. Nov 2006 A1
20060259093 Stevenson et al. Nov 2006 A1
20070041164 Greenberg et al. Feb 2007 A1
20070150020 Hokanson Jun 2007 A1
20070183118 Fu et al. Aug 2007 A1
20070217121 Fu et al. Sep 2007 A1
20070276389 Franke et al. Nov 2007 A1
20080060834 Eck et al. Mar 2008 A1
20080071313 Stevenson et al. Mar 2008 A1
20080119906 Starke May 2008 A1
20080203917 Maya Aug 2008 A1
20080269831 Erickson Oct 2008 A1
20090192578 Biggs Jul 2009 A1
20090281586 Lim Nov 2009 A1
20100023086 Lim Jan 2010 A1
20100109966 Mateychuk et al. May 2010 A1
20100121438 Jarvik May 2010 A1
20100241206 Truex et al. Sep 2010 A1
20100258342 Parker Oct 2010 A1
20100258540 Tamura et al. Oct 2010 A1
20110032658 Iyer Feb 2011 A1
20110034965 Troetzschel et al. Feb 2011 A1
20110034966 Troetzschel et al. Feb 2011 A1
20110048770 Reiterer et al. Mar 2011 A1
20110094768 Davis et al. Apr 2011 A1
20110106228 Reiterer et al. May 2011 A1
20110108320 Lakner May 2011 A1
20110186349 Troetzschel Aug 2011 A1
20110190885 Troetzschel et al. Aug 2011 A1
20110232961 Teske Sep 2011 A1
20110232962 Teske Sep 2011 A1
20120006576 Barry et al. Jan 2012 A1
20120127627 Brendel et al. May 2012 A1
20120193117 Specht et al. Aug 2012 A1
20120193118 Kempf et al. Aug 2012 A1
20120193119 Kempf et al. Aug 2012 A1
20120193125 Pavlovic et al. Aug 2012 A1
20120193141 Reisinger et al. Aug 2012 A1
20120194981 Kempf et al. Aug 2012 A1
20120197326 Pavlovic Aug 2012 A1
20120197327 Specht Aug 2012 A1
20120197335 Reisinger Aug 2012 A1
20120197368 Reisinger Aug 2012 A1
20120200011 Pavlovic Aug 2012 A1
20120203294 Troetzschel Aug 2012 A1
20120209100 De Beeck et al. Aug 2012 A1
20130035733 Breyen et al. Feb 2013 A1
20130060312 Iyer et al. Mar 2013 A1
20130184797 Tang et al. Jul 2013 A1
20130299233 Troetzschel et al. Nov 2013 A1
20140008121 Troetzschel et al. Jan 2014 A1
20140144014 Troetzschel et al. May 2014 A1
20140262493 Markham et al. Sep 2014 A1
20140262494 Reisinger et al. Sep 2014 A1
20140368298 Reisinger Dec 2014 A1
20160126712 Markham et al. May 2016 A1
Foreign Referenced Citations (24)
Number Date Country
102614588 Aug 2012 CN
102872529 Jan 2013 CN
69729719 Jul 2005 DE
102006054249 May 2008 DE
102008021064 Oct 2009 DE
102009035971 Feb 2011 DE
102009035972 Apr 2011 DE
102010006837 Aug 2011 DE
102010006838 Aug 2011 DE
102010006689 Sep 2011 DE
102010006690 Sep 2011 DE
102011119125 May 2013 DE
0877400 Nov 1998 EP
0916364 May 1999 EP
1685874 Aug 2006 EP
1754511 Feb 2007 EP
2398026 Dec 2011 EP
1148760 Jun 1989 JP
2133378 May 1990 JP
03073450 Sep 2003 WO
2004110555 Dec 2004 WO
2008103166 Aug 2008 WO
2010091435 Aug 2010 WO
2013075797 May 2013 WO
Non-Patent Literature Citations (9)
Entry
Hussain, et al., “Electrical conductivity of an insulator matrix (alumina) and conductor particle (molybdenum) composites”, Journal of the European Ceramic Society, vol. 23, Issue 2, Feb. 2003, pp. 315-321.
Gil et al., “Grain Growth Kinetics of Pure Titanium,” Scripta Metallurgica et Materialia, vol. 33, No. 8, pp. 1361-1366 (Oct. 15, 1995).
Exner, Horst et al., “Laser Joining of Ceramics in Liquid Phase,” pp. 1-8 (Nov. 8, 2011).
International Search Report and the Written Opinion for International Application No. PCT/US2014/026011 dated Nov. 5, 2014 (13 pages).
Restriction Requirement for U.S. Appl. No. 13/804,888 dated Oct. 30, 2015 (7 pgs.).
Office Action for U.S. Appl. No. 13/804,888 dated Mar. 18, 2016 (35 pgs.).
Notice of Allowance for U.S. Appl. No. 13/804,888 dated Jul. 26, 2016 (9 pgs.).
Office Action for U.S. Appl. No. 14/991,329 dated Jul. 26, 2018 (12 pgs).
Notice of Allowance for U.S. Appl. No. 14/991,329 dated Jun. 5, 2019 (12 pgs.).
Related Publications (1)
Number Date Country
20190356122 A1 Nov 2019 US
Divisions (2)
Number Date Country
Parent 14991329 Jan 2016 US
Child 16527793 US
Parent 13804888 Mar 2013 US
Child 14991329 US