Patent Application
20230302570
This application is based on and claims the benefit of priority from Chinese Patent Application No. CN202210298257.4, filed on 24 Mar. 2022, the content of which is incorporated herein by reference.
The present invention relates to a welded product and a method of producing a welded product.
A conventional process for producing a welded product includes arc-welding multiple steel members in shielding gas using a welding wire. In this process, slag is formed on the weld surface through the reaction between oxygen in the active gas component of the shielding gas and elements in the steel members and the welding wire, such as Si and Mn.
The welded product is then subjected to electrodeposition coating for improving its corrosion resistance, in which, however, the slag cannot easily be coated by the electrodeposition.
Patent Document 1 discloses a solid wire consisting of C: 0.03 to 0.15% by mass, Si: more than 0 to 0.29% by mass, Mn: 0.5 to 2.8% by mass, Ti: 0.10 to 0.30% by mass, Al: 0.003 to 0.30% by mass, Sn: 0.02 to 0.40% by mass, P: more than 0 to 0.015% by mass, S: more than 0 to 0.030% by mass, B: 0 to 0.0100% by mass, Cr: 0 to 1.5% by mass, Ni: 0 to 3.0% by mass, Mo: 0 to 1.0% by mass, Nb: 0 to 0.3% by mass, V: 0 to 0.3% by mass, Cu: 0 to 0.50% by mass, and a balance of iron and unavoidable impurities.
Patent Document 1: Japanese Unexamined Patent Application, Publication No. 2021-3717
There is, however, a need to improve the ability of slag to be coated by electrodeposition.
It is an object of the present invention to provide a welded product containing slag having a higher ability to be coated by electrodeposition.
An aspect of the present invention is directed to a welded product including: multiple steel members; and one or two or more welds with which the multiple steel members are welded together, at least one of the welds having a surface containing slag, the slag having a Si content of 14% by mass or less and having a mass ratio of Si to Mn of 0.25 or less.
The steel members may have a Si content of 0.72% by mass or less.
The slag may have a dendrite structure.
The slag may have a thickness of 50 μm or less.
Another aspect of the present invention is directed to a method of producing the welded product defined above, the method including subjecting multiple base steel materials to arc welding in a shielding gas.
The shielding gas may have a volume ratio of active gas to inert gas of 5/95 or more and 14/86 or less.
The present invention provides a welded product containing slag having a higher ability to be coated by electrodeposition.
Hereinafter, embodiments of the present invention will be described.
The welded product according to an embodiment of the present invention includes: multiple steel members; and one or two or more welds with which the multiple steel members are welded together, in which at least one of the welds has a surface containing slag. The welded product may include any number of steel members welded together.
The content of Si in the slag is 14% by mass or less and preferably 10% by mass or less. The slag with a Si content of more than 14% by mass will have a reduced ability to be coated by electrodeposition. In this regard, the content of Si in the slag is typically, but not limited to, 0% by mass or more.
The mass ratio of Si to Mn in the slag is 0.25 or less and preferably 0.15 or less. The slag with a mass ratio of Si to Mn of more than 0.25 will have a reduced ability to be coated by electrodeposition and thus will make it less easy to perform coating film formation on the weld.
The content of Si in the steel members is preferably 0.72% by mass or less and more preferably 0.10% by mass or less. The steel members with a Si content of 0.72% by mass or less can produce slag with a reduced Si content, which will have an improved ability to be coated by electrodeposition and make it possible to effectively perform coating film formation on the weld. In this regard, the content of Si in the steel members is typically, but not limited to, 0.005% by mass or more.
The content of C in the steel members is typically, but not limited to, 0.03% by mass or more and 0.10% by mass or less.
The content of Mn in the steel members is typically, but not limited to, 1.00% by mass or more and 2.00% by mass or less.
The content of P in the steel members is typically, but not limited to, 0.001% by mass or more and 0.02% by mass or less.
The content of S in the steel members is typically, but not limited to, 0.001% by mass or more and 0.010% by mass or less.
The multiple steel members may have the same composition or different compositions.
The slag preferably has a dendrite structure. The dendrite structure allows the slag to have an improved ability to be coated by electrodeposition. This is probably attributable to the presence of Si-rich and Mn-rich phases on the order of nanometers. In this regard, the mass ratio of Si to Mn in the Si-rich phase is, for example, 0.13 or more and 0.31 or less. The mass ratio of Si to Mn in the Mn-rich phase is, for example, 0.01 or more and 0.07 or less. The Mn-rich phase has a higher ability to be coated by electrodeposition and can be formed homogeneously on the order of micrometers. Thus, the Mn-rich phase makes it possible to perform coating film formation homogeneously and effectively on the weld.
The thickness of the slag may be defined as the shortest distance between the top of the slag and the steel member which forms an electrically conductive path. In this case, the thickness of the slag is preferably 50 μm or less and more preferably 30 μm or less. The slag with a thickness of 50 μm or less will have an improved ability to be coated by electrodeposition and make it possible to effectively perform coating film formation on the weld. In this regard, the thickness of the slag is typically, but not limited to, 10 μm or more.
The welded product according to an embodiment of the present invention may be produced by a process including subjecting multiple base steel materials to arc welding in a shielding gas. In this process, a welding wire may be used if necessary.
The composition of the base steel materials to be arc-welded is the same as that of the steel members of the welded product according to an embodiment of the present invention.
The volume ratio of active gas to inert gas in the shielding gas is preferably 5/95 or more and 14/86 or less and more preferably 5/95 or more and 10/90 or less. The shielding gas with a volume ratio of active gas to inert gas of 5/95 or more can make the weld penetration depth lager and reduce the occurrence of defects, such as blowholes and pits. The shielding gas with a volume ratio of active gas to inert gas of 14/86 or less can reduce the production or thickness of slag.
Examples of the active gas include, but are not limited to, carbon dioxide (CO2) and oxygen (O2). Examples of the inert gas include, but are not limited to, argon (Ar) and helium (He).
The content of Si in the welding wire is preferably 0.09% by mass or less and more preferably 0.05% by mass or less. The welding wire with a Si content of 0.09% by mass or less can produce slag having a reduced Si content and having an improved ability to be coated by electrodeposition. In this regard, the content of Si in the welding wire is typically, but not limited to, 0.005% by mass or more.
The content of C in the welding wire is typically, but not limited to, 0.02% by mass or more and 0.15% by mass or less.
The content of Mn in the welding wire is typically, but not limited to, 1.40% by mass or more and 2.10% by mass or less.
The content of P in the welding wire is typically, but not limited to, 0.001% by mass or more and 0.02% by mass or less.
The content of S in the welding wire is typically, but not limited to, 0.001% by mass or more and 0.02% by mass or less.
The embodiments of the present invention described above are not intended to limit the present invention and may be altered or modified as appropriate without departing from the gist of the present invention.
Hereinafter, the present invention will be described with reference to examples, which are not intended to limit the present invention.
In a MAG (metal active gas) pulse welding machine, 440 MPa-grade plated steel sheets of 2.0 mm in thickness (base steel materials) were arc-welded in a shielding gas using a welding wire. As a result, a welded product was obtained having the steel members welded together with a weld. Using this process, lap fillet welding, T-joint welding, and flare joint welding were performed with different pulse currents and different arc voltages.
The welding wire included 0.07% by mass of C, 0.05% by mass of Si, 1.6% by mass of Mn, 0.0015% by mass of P, 0.006% by mass of S, 0.2% by mass of Ti, 0.2% by mass of Cu, and a balance of iron and unavoidable impurities. The 440 MPa-grade plated steel sheets included 0.06% by mass of C, 0.1% by mass of Si, 1.2% by mass of Mn, 0.01% by mass of P, 0.02% by mass of S, and a balance of iron and unavoidable impurities. The shielding gas had a volume ratio of CO2 to Ar of 10/90.
The slag present at the surface of the weld was subjected to elemental analysis using a field emission scanning electron microscope (FE-SEM). Specifically, carbon was vapor-deposited on the weld, and then the slag was subjected to elemental analysis by energy dispersive X-ray spectroscopy (EDS) under the conditions shown below.
However, O and C were excluded from the detection target elements in order to eliminate the influence of vapor deposition, contamination, and other factors.
The surface of the welded product was degreased with an alkaline degreaser, Fine Cleaner L4460 (manufactured by Nihon Parkerizing Co., Ltd.), and then thoroughly washed with water. Subsequently, the surface of the welded product was subjected to chemical conversion treatment with a zinc-based surface conditioner, Prepalene X (manufactured by Nihon Parkerizing Co., Ltd.), and a zinc phosphate chemical conversion agent for base coating, Palbond L3020 (manufactured by Nihon Parkerizing Co., Ltd.), and then thoroughly washed with water. Subsequently, the surface of the welded product was subjected to cationic electrodeposition coating with electrodeposition paint, ED6551G (manufactured by PPG Industries), in such a way that an electrodeposited coating with a thickness of 25 μm was formed. Subsequently, the coating was washed with water and then baked at 170° C. for 20 minutes. The ability of the slag to be coated by the electrodeposition was then visually evaluated. The criteria for evaluating the ability of the slag to be coated by the electrodeposition were as follows. OK: It was evaluated as “OK” when the coating film formed by the cationic electrodeposition coating covered the entire surface of the slag. NG: It was evaluated as “NG” when the coating film formed by the cationic electrodeposition coating partially covered the surface of the slag.
Hereinafter, cases where the slag has a Si content of at most 14% by mass and a mass ratio of Si to Mn of at most 0.25 will be called examples, and the other cases will be called comparative examples.