Patent Application
20100084388
The invention pertains to welding electrodes, and more particularly to flux-cored electrodes.
Flux-cored electrodes may be manufactured using a process that employs feeder rod, known as “green rod.” In one process, the green rod is formed into a u-shaped channel, filled with the desired welding flux, mechanically deformed to create a sheath surrounding the flux, and then drawn through a series of dies to the desired final electrode diameter. In another process, the “green rod” may be replaced by steel strip which forms approximately the same depth u-shaped channel prior to filling. Among the difficulties that result from manufacturing flux-cored electrodes in this manner is that portions of the powdered flux spill from the relatively shallow channel during filling and subsequent forming operations.
Another known difficulty that results from manufacturing electrodes in this manner is that the sheath may break in the reducing dies if drawn to too great of a reduction in cross-sectional area. Typically, the amount of reduction in cross-sectional area is calculated to correspond to a predetermined sheath diameter. It is known in the art that reducing the cross-sectional area of the sheath by greater than approximately 60% results in such breakage. Once the sheath is broken in the drawing die, it becomes necessary to weld the sheath back together so that drawing process may continue. Usually, the process continues for a short period until the sheath breaks again at another location. The unpredictable, yet frequent, nature of this breakage has until now resulted in those in the art not attempting to reduce the cross-sectional area of sheaths by greater than 60% using a drawing process. It is believed that increasing the initial cross-sectional area of the sheath and drawing to a pre-determined hardness using drawing equipment having the requisite horsepower may alleviate such breakage problems.
In another aspect of flux-cored electrodes, it is known that the tip of the electrode must be sufficiently clean for a welding arc to be struck between the workpiece and the electrode. As a result of prior welding activity, the tip of the electrode may be covered with slag or other contamination. Thus, the tip must be cut or broken off by the welder prior to striking an arc. Traditional flux-cored electrodes are too soft to be broken or snapped off by hand; the electrode merely deforms without breaking when bent by a welder. Therefore, welders carry and use wire cutters to create a “clean” tip. Periodically, a welder may stop welding to inspect the quality of the weld or simply because of muscle fatigue. After each stoppage, a welder must then pull out wire cutters to produce the necessary “clean” tip before welding can be commenced, thereby adding additional steps to the welding process and decreasing the efficiency of the welder.
In one embodiment a welding electrode includes a sheath formed from a strip of metal having first and second edges. The sheath has an initial cross-sectional area and a second as-drawn cross-sectional area, and a core is received within the sheath. The second cross-sectional area is at least an 80% reduction of the initial cross-sectional area.
Referring now to the drawings wherein the showings are for purposes of illustrating embodiments of the invention only and not for purposes of limiting the same,
In one embodiment, the first and second edges 22, 24 may be substantially parallel. In another embodiment, the metal strip may have an initial thickness of 0.04 inches and an initial width of 1.05 inches. In still another embodiment, the metal strip may comprise steel, aluminum, or any other metal or metal alloy with suitable mechanical properties such that the metal may be formed into a sheath. As the sheath 20 is formed from the metal strip, the metal strip may first be formed into a channel by applying forces using forming equipment known in the art.
Once the metal strip has been formed into a channel, the core composition 30 may be deposited into the channel. As the core composition 30 may be a powdered material, the core composition 30 may be fed by a powder feeder, as known in the art, into the channel. In one embodiment, the core composition 30 may include at least one gas generating compound, whereby the generated gas may shield the weld pool from the ambient environment during the welding operation. In another embodiment, the core composition 30 may include at least one alloying metal which may be used to facilitate forming a weld metal with a desired composition. It is also contemplated that the core composition 30 may include a composition including at least one of at least one gas generating compound and at least one alloying agent.
Once the core composition 30 has been deposited into the channel, the sheath 20 may be formed by applying forces to the both the first edge 22 and the second edge 24 of the metal strip, thereby enclosing the core composition 30 within the sheath 20. In one embodiment, the first edge 22 and second edge 24 may be formed such that the first edge 22 overlaps the second edge 24, forming what may be known as a “lap seam.”
In another embodiment shown in
Referring again to
As the sheath 20 is subjected to the drawing process, the hardness of the sheath may increase due to a phenomenon known as work hardening. Work hardening is the phenomenon whereby a ductile metal becomes harder and stronger as it is plastically deformed due to an increase in the dislocation density of the metal. In one embodiment, the hardness of the sheath 20 may be increased to a hardness that is sufficient such that the electrode 10 may be snapped into two pieces. For example, the tip of the electrode may be grasped between a welder's fingers, by pliers, or by some other grasping implement and subjected to a sudden increase in force, whereby the electrode 10 may be snapped into at least two pieces. In another embodiment, the hardness of the sheath 20 may be at least 200 Vickers 500 g microhardness, as measured by a standard Vickers microhardness testing device with a 500 g load.
In a further embodiment of the subject invention, a welding electrode 10 may be manufactured from a metal strip having an initial hardness and including first and second edges 22, 24. The strip of metal may be formed into a concave channel, and the channel may be filled with a powdered composition 30. Subsequently, the channel may be formed to create a sheath 20 enclosing the powdered composition 30. Means for work hardening the sheath 20 may then be provided. Such means for work hardening may include a forming die, a reducing die or series of said dies in combination. The means for work hardening the sheath may then be employed to work harden the sheath 20. The processes of forming the strip into a concave channel, further forming the strip to create a sheath, and work hardening the sheath may increase the hardness of the sheath to a final hardness such that the sheath may be snapped into at least two pieces.
The invention has been described herein with reference to the disclosed embodiments. Obviously, modifications and alterations will occur to others upon a reading and understanding of this specification. It is intended to include all such modifications and alterations insofar as they come within the scope of the appended claims or the equivalence thereof.