The present disclosure relates to a welding method and system.
Welding is a process that joins materials, usually metals, by causing coalescence. This is often done by melting the workpieces to form a pool of molten material (the weld pool) that cools to become a strong joint, with pressure sometimes used in conjunction with heat, or by itself, to produce the weld. As a non-limiting example, a laser beam may be applied between two metal workpieces, generating heat within the workpieces. The workpieces are wholly or partly made of a base material, such as steel. A molten pool is created where the temperature is greater than the melting point of the base materials subjected to heat. Sometimes, a filler material is added to change the composition of the welds. Next, the weld pool cools and becomes a weld joint.
Many different energy sources can be used for welding, including laser, electric arc, electron beam, etc. During welding, energy is applied to at least two workpieces using a suitable energy source in order to generate heat at an interference between the two workpieces. As a non-limiting example, during laser welding, the laser welding head directs energy to a target location at an interference between the two workpieces. As a result, the base material of the workpieces at the target location melts (sometimes along with the filler material), thereby forming a weld pool. The area of the base material around the weld pool, which is not melted, is also affected by the heat generated by the energy applied with the welding head and is therefore referred to as the heat-affected zone (HAZ). The heat in the HAZ can change the microstructure of the base material, thereby changing the mechanical properties of the base material at the HAZ. The HAZ thus refers to an area of the base material that is not melted and has had its microstructure and properties altered by welding. In most cases the effect of welding on HAZ can be detrimental—depending on the base materials and the heat input of the welding process. For example, HAZ of high strength steels is often softened after welding. As a consequence, the hardness of the base material at the HAZ decreases in relation to the hardness of the base material. The extent and magnitude of softening depends primarily on the base material, and the amount and concentration of heat input by the welding thermal process. It is therefore useful to control the thermal process at the HAZ in order to minimize HAZ softening.
A welding method has been developed to minimize HAZ softening by increased cooling speed in HAZ with an external cooling unit compared to the normal welding conditions. The normal welding conditions are referred to that where welds are naturally cooled to room temperature. In an embodiment, the welding method includes the following steps: (a) determining, via a control module, martensite tempering temperature the temperature of martensite tempering (i.e., the martensite tempering temperature), which is one main reason for HAZ based, at least in part, on the chemical composition and microstructure of the base material (e.g. metail) of the first and second workpieces; (b) applying sufficient energy to the workpieces to melt the workpieces at a target location, thereby creating a weld pool; (c) determining, via the control module, a target temperature and cooling range of a coolant based, at least in part, on the martensite tempering temperature and HAZ width; and (d) cooling the workpieces such that the temperature of the workpieces at the HAZs does not reach the martensite tempering temperature in order to minimize softening at the HAZs. Each HAZ is an area of the workpieces around the weld pool subjected to heat stemming from the energy applied to the workpieces at the target location. The term “martensite tempering temperature” refers to the temperature in which tempered martensite is formed in the base material.
The present disclosure also relates to a welding system for minimizing HAZ softening. In an embodiment, the welding system includes an energy source configured to supply energy and a welding head coupled to the energy source. The welding head is configured to direct sufficient energy to at least two workpieces to melt the workpieces at a target location in order to create a weld pool. The welding system further includes a control module programmed to execute the following instructions: (a) determine a martensite tempering temperature of the workpieces based, at least in part, on the chemical composition and microstructure of the base material; and (b) determine a target temperature and cooling range of a coolant based, at least in part, on the martensite tempering temperature and HAZ width. The welding system further includes a cooling system configured to carry the coolant ith the suitable cooling extent and magnitude to cool the workpieces such that a temperature of the workpieces at the HAZs does not reach the martensite tempering temperature in order to minimize softening at HAZs, such that the martensite tempering temperature and its holding time at HAZs of the workpiece are reduced and shortened by enhanced cooling rate from the external strengthening cooling.
The above features and advantages and other features and advantages of the present invention are readily apparent from the following detailed description of the best modes for carrying out the invention when taken in connection with the accompanying drawings.
Referring now to the drawings, wherein the like numerals indicate corresponding parts throughout the several views,
With continued reference to
The welding system 100 further includes a welding head 104 and a robot control unit 106 for controlling the movement and operation of the welding head 104 in relation to the first and second workpieces 10, 12. The robot control unit 106 may be a computer numerical control (CNC) unit capable of controlling the movement and location of the welding head 104. To do so, the robot control unit 106 is mechanically coupled to the welding head 104 and in electronic communication with the control module 102. The robot control unit 106 can therefore receive input (i.e., instructions) from the control module 102 and can then stop or move the welding head 104 relative to the first and second workpieces 10, 12.
In addition to the robot control unit 106, the welding system 100 includes an energy source 108 configured to supply energy E (e.g., such as a gas flame, an electric arc, a laser, an electron beam, friction, or ultrasound). The energy source 108 is coupled to the welding head 104, and the welding head 104 can direct the energy E (e.g., gas flame, an electric arc, a laser, an electron beam, friction, or ultrasound) from the energy source 108 toward the first and second workpieces 10, 12. The robot control unit 106 is in electronic communication with the energy source 108 and can therefore activate or deactivate the energy source 108. Upon activation, the welding head 104 directs energy E from the energy source 108 to the first and second workpieces 10, 12. Upon deactivation, the welding head 104 stops directing energy E from the energy source 108 to the first and second workpieces 10, 12.
The welding system 100 further includes a data acquisition unit 112 and at least one temperature sensor 110 capable of detecting the temperature of the first and second workpieces 10, 12 and generating a temperature signal S indicative of the temperature of the first and second workpieces 10, 12 at and near the target location T. The temperature sensor 110 is in electronic communication with the data acquisition unit 112 and may be a pyrometer, a thermal camera, or a combination thereof. The temperature sensor 110 can also be a contact-type temperature sensor like thermocouple. The data acquisition unit 112 receives input (e.g., temperature signal S) from the temperature sensor 110 and stores data indicative of the temperature of the first and second workpieces 10, 12. Accordingly, the data acquisition unit 112 includes memory capable of storing data received from the temperature sensor 110. The control module 102 is in electronic communication with the data acquisition unit 112 and can receive data relative to the workpieces temperature from the data acquisition unit 112.
The welding system 100 can be used to weld the first and second workpieces 10, 12 together. To do so, the robot control unit 106 activates the energy source 108 once the welding head 104 has reached a target location T at an interference between the first and second workpieces 10, 12. Upon activation, the energy source 108 supplies energy E to the welding head 104, and the welding head 104 directs the energy E to the target location T, which is at an interference between the first and second workpieces 10, 12. The welding head 104 should supply sufficient energy E to the first and second workpieces 10, 12 to melt the base material of the first and second workpieces 10, 12 at the target location T. In order words, the energy E applied by the welding head 104 should be sufficient to generate enough heat to melt the base material of the first and second workpieces 10, 12 at the target location T. A filler material may be added into the molten pool (e.g., a location at an interference between the first and second workpieces 10, 12). The term “weld pool” refers to a pool of melted base material and may include melted filler material. The weld pool W then cools to form a weld 14 (
With continued reference to
In order to minimize HAZ softening, the HAZs are cooled during or after the welding process. Also, cooling of the workpieces 10, 12 prior to welding reduces the HAZ softening. To do so, a cooling system 114 may be used to cool the HAZs during, after, or prior to the welding process. The cooling system 114 may be external or part of the welding system 100. Regardless, the cooling system 114 is in electronic communication with the control module 102 and includes a cooling controller 116 and passageways 120 for conveying a coolant C, such as water. The passageways 120 may be tubes, such as cooper tubes, or any other apparatus suitable to convey coolant C. The passageways 120 (e.g., cooper tubes) may be disposed adjacent the first and second workpieces 10, 12 such that coolant C flowing through the passageways 120 can cool the first and second workpieces 10, 12. The cooling controller 116 is fluidly coupled to a coolant source 118 and can therefore receive coolant C from the coolant source 118. For example, the coolant C may be any type of fluid (e.g., liquid or gas) and, therefore, the cooling controller 116 can receive a cold liquid (e.g., cold water) or a cold gas (e.g., chiller gas). In other words, the coolant source 118 is in fluid communication (e.g., liquid or gaseous communication) with the cooling system 114. The coolant source 118 contains coolant (e.g., water). The cooling controller 116 can control the temperature of the coolant C (i.e., the coolant or target temperature). To do so, the cooling controller 116 may include a cooling device 122, such as a chiller. The cooling device 122 removes heat from the coolant C, and the cooling controller 116 can supply coolant C to the passageways 120 at a controlled temperature. The cooling controller 116 can also control the flow rate of the coolant C (i.e., the coolant flow rate) delivered to the passageways 120. To do so, the cooling controller 116 may include at least one control valve 124 configured to control the flow rate of the coolant C. In addition to the flow rate, the cooling controller 116 can control the location of the cooling by, for example, allowing coolant C to flow through some of (but not all) the passageways 120. To do so, the cooling controller 116 may include additional valves (not shown) capable of controlling the flow of coolant C through the passageways 120.
The welding method 200 begins at step 202. Step 202 entails determining a chemical composition of the first and second workpieces 10, 12. In particular, step 202 entails determining the chemical composition of the base material forming the first and second workpieces 10, 12. The first and second workpieces 10, 12 may have the same or different chemical compositions. The chemical composition of the first and second workpieces 10, 12 may be supplied by the vendor of the first and second workpieces 10, 12 and may already be stored in the memory of the control module 102 in, for example, a lookup table. In addition, chemical composition of the workpieces 10, 12 can also be determined by the other methods such as non-limiting methods of X-Ray Fluorescence(XRF) and DES. Accordingly, the control module 102 may determine the chemical composition of the first and second workpieces 10, 12 by retrieving the information from its memory.
The welding method 200 then proceeds to step 204. Step 204 entails determining, via the control module 102, the martensite tempering temperature of the first and second workpieces 10, 12 based, at least in part, on the chemical composition and microstructure of the first and second workpieces 10. 12. In particular, step 204 entails calculating, via the control module 102, the martensite tempering temperature of the base material forming the first and second workpieces 10, 12.
Next, the welding method 200 proceeds to step 206. Step 206 entails applying sufficient energy E to the first and second workpieces 10, 12 to melt the first and second workpieces 10, 12 at the target location T, thereby creating the weld pool W. As discussed above, the target location T is at an interference between the first and second workpieces 10, 12. Energy E (e.g., laser) may be applied to the first and second workpieces 10, 12 using the welding head 104, robot control unit 106, and energy source 108 as discussed above. Therefore, step 206 may also include positioning the welding head 104 at an interference between the first and second workpieces 10, 12 over the target location T and then activating the energy source 108 using the robot control unit 106 to apply energy E to the first and second workpieces 10, 12 at the target location T. Step 206 may further include adding a filler material to the base material at the target location T once the base material has reached its melting point. In other words, step 206 may include adding a filler material to the weld pool. Step 206 may be part of a fusion welding process. As non-limiting examples, the fusion welding process may be arc welding (e.g., tungsten inert gas (TIG) welding, plasma welding, gas tungsten arc welding (GTAW)), laser welding, resistance spot welding, solid state welding (e.g., friction stir welding), ultrasonic welding, or combination thereof, such as a hybrid laser-arc welding.
Next, the welding method 200 continues to step 208. Step 208 entails determining, via the control module 102, the temperature of the first and second workpieces 10, 12 (i.e., the measured temperature) in order to identify the locations of the heat-affected zones (HAZs) in the base material of the first and second workpieces 10, 12. To do so, the temperature sensor 110 may detect the temperature of the first and second workpieces 10, 12 at and around the target location T (
Then, the welding method 200 continues to step 210. Step 210 entails determining, via the control module 102, the cooling parameters suitable to cool the first and second workpieces 10, 12 until the temperature of the first and second workpieces at the HAZs is controlled below the martensite tempering temperature determined in step 204. Thus, step 210 entails determining, via the control module 102, the cooling parameters for the HAZs based, at least in part, on the martensite tempering temperature. The cooling parameters may include, but are not limited to, the target temperature and target flow rate of the coolant C flowing through the passageways 120 as well as the cooling location in the first and second workpieces 10, 12. The target temperature of the coolant C is also referred to as the coolant temperature, and the flow rate of the coolant C flowing through the passageways 120 is referred to as the coolant flow rate. Accordingly, step 210 includes determining, via the control module 102, the coolant temperature based, at least in part, on the martensite tempering temperature determined in step 204 and HAZ width. The “HAZ width” refers to the width of the HAZ. In addition, step 210 includes determining, via the control module 102, the coolant flow rate based, at least in part, on the martensite tempering temperature determined in step 204. Furthermore, step 210 includes determining, via the control module 102, the cooling location in the first and second workpieces 10, 12 based, at least in part, on the location of the HAZs identified in step 208. In the present disclosure, the “cooling location” refers to the areas in the first and second workpieces 10, 12 that should be cooled in order to minimize HAZ softening. The cooling parameters may also include a cooling range. The term “cooling range” means the difference in temperature between the cooling C entering the passageways 120 and the coolant C leaving the passageways 120. Step 210 also include determining the cooling range.
Next, the welding method 200 proceeds to step 212. Step 212 entails cooling the first and second workpieces 10, 12 (using the cooling system 114) such that the temperature of the first and second workpieces 10, 12 at the HAZs is controlled below the martensite tempering temperature in order to minimize softening at the HAZs. As discussed above, each HAZ is an area of the first and second workpieces 10, 12 around the weld pool W subjected to heat stemming from the energy E applied to the first and second workpieces 10, 12 at the target location T. To cool the first and second workpieces 10, 12, the cooling system 114 delivers coolant C (e.g., cold water) through the passageways 120 in order to cool the HAZs of the first and second workpieces 10, 12. In particular, the cooling system 114 supplies coolant C to the passageways 120 at the coolant temperature and coolant flow rate determined in step 210. Also, the cooling system 114 is configured to carry the coolant C and deliver the coolant C to the passageways 120 located adjacent to the cooling location determined in step 210. Accordingly, the cooling system 114 can cool mainly around the HAZs of the first and second workpieces 10, 12. It is also contemplated that the cooling system may cool only the HAZs of the first and second workpieces 10, 12. Step 212 (i.e., cooling) and step 206 (i.e., applying energy E) may be conducted simultaneously. Also, the step 212 (i.e., cooling) may be conducted before or after step 206 (i.e., applying energy E).
While the best modes for carrying out the invention have been described in detail, those familiar with the art to which this invention relates will recognize various alternative designs and embodiments for practicing the invention within the scope of the appended claims.