(1) Field of the Invention
The present invention relates to welding two metal work-pieces together and relates in particular, but not exclusively, to welding together two relatively thick work-pieces made from metal alloys that have been prepared for use in the manufacture of aircraft components.
(2) Description of Related Art
When manufacturing aircraft components it is sometimes necessary or desirable to weld together thick work-pieces for example solid blocks of aluminium alloy having a thickness of 50 mm or greater. The alloy will typically be an aluminium alloy that has been treated so that it has certain mechanical properties necessary for the alloy to be suitable for use in the manufacture of aircraft components. As a result, the microstructure of the alloy is formed of relatively coarse elongate grains that are generally oriented parallel to each other. Welding blocks of aluminium of such a thickness is generally performed by means of a fusion welding process such as an electron beam (EB) welding process. It is common when joining blocks of aluminium in this way for cracks to form (for example micro-cracks) in or near the region of the weld. Such cracks weaken the welded component particularly under fatigue loading.
It is an object of the present invention to produce a method of welding two work-pieces together that eliminates or reduces the formation of cracks during the welding process as compared to the known prior art method described above.
According to the present invention there is provided a method of welding together two metal work-pieces, the method including the following steps:
It has been found that the treating of the metal in the region of the weld joint to be formed mitigates the problems associated with the formation of cracks. It has been observed that the formation of at least some cracks in the methods of the prior art tends to occur in the work-piece near the interface between the alloy and the weld, in regions where there has been partial liquefaction of the alloy due to the heat generated when welding. Such cracks are often referred to as liquation cracks and commonly occur at the boundary between adjacent grains in the alloy. It is thought that such cracks result from the formation of grain boundary liquid (at temperatures below the melting point of the grains of the alloy), which, being unable to support the tensile stresses that are developed as a result of the temperature changes during and after welding, leads to cracks forming along the grain boundary.
The average maximum dimension of the grains in the work-piece outside the region that has been subjected to said surface treatment is preferably at least five times greater than the average maximum dimension of the grains in the work-piece inside the region. Alternatively or additionally, the method is performed such that there is at least one cross-section in which the difference between the grain size number of the material in the work-piece outside the region that has been subjected to said surface treatment and the grain size number of the material in the work-piece inside the region is greater than or equal to 4. The grain size number, G, of a material is defined by the equation n=2G-1, where n=the number of grains per square inch at 100× magnification (i.e. the number of grains in an area of 0.0645 mm2).
The preparation of the work-pieces may, if necessary, include a step of treating or machining the surface treated regions of each work-piece to produce a surface on one work-piece that can be fusion welded to a corresponding surface on the other work-piece. The regions subjected to said surface treatment may for example be skimmed to produce substantially flat surfaces. The skimming of the work-pieces may for example be performed by a milling machine. The skimming may typically remove a layer of material from a face of the work-piece that, had the work-piece not been subjected to said surface treatment, would have been about 0.5 mm thick. The depth of material removed during skimming will of course depend on the amount of material that needs to be removed in order to provide a flat surface, which will of course depend on the surface treatment employed.
The surface treatment of the metal is preferably performed within a region that encompasses the region that will liquefy during the fusion welding process. The region that will liquefy may for example at the lowest be about 2 mm, and may be as high as 5 mm (or even higher depending on the fusion welding method employed), to either side of the weld joint. In the case where the depth of liquefaction during fusion welding is 2 mm to either side of the joint, the surface treating of the metal beforehand must extend beyond that depth, for example to a depth of at least 5 mm. In the case where the surface of the work-piece is skimmed between the steps of surface treatment and fusion welding, then the depth of the material that has been subjected to said surface treatment will of course be reduced. The surface treatment may be conducted to a depth of at least 10 mm. The surface treatment may be conducted to a depth of less than 100 mm. The surface treatment may for example be conducted to a depth of between 5 mm and 40 mm and more preferably to a depth of between 10 mm and 30 mm. It will of course be understood that the surface treatment is referred to as such only because the treatment is effected near the surface of the work-piece and that the term is not limited to treatments where the treatment affects only the surface properties of the work-piece.
It will be appreciated that, depending on the depth to which the metal is subjected to said surface treatment, the fusion welding process may generate a heat affected zone (i.e. a zone in which the mechanical properties of the metal/alloy, such as for example hardness, are altered by the heat generated during welding) that extends beyond the boundary of the metal that has been subjected to said surface treatment.
The surface treatment is preferably so performed that the temperature of the metal does not reach the melting temperature of the metal work-piece. Advantageously, the surface treatment is performed such that the temperature of the metal does not exceed the eutectic phase melting temperature. Preferably, the surface treatment is performed such that the temperature of the metal does not exceed the liquation temperature of the metal in the grain boundaries.
Advantageously, the performance of the surface treatment causes plasticization of the metal, but preferably causes substantially no liquefaction or fluidization. Preferably, the surface treatment causes substantially no melting of the metal.
Advantageously, the surface treatment is performed by means of a friction stir welding process. Such a process is described in U.S. Pat. No. 5,460,317 (Thomas et al), U.S. Pat. No. 5,813,592 (Midling et al), WO 93/10935 (The Welding Institute), and WO 95/26254 (Norsk Hydro A. S.), the specifications of which are hereby fully incorporated herein by reference thereto. The friction stir welding process may be in the form of a process as described in any of those references. It will be understood that the term “friction stir welding” encompasses any method of welding in which a probe of material harder than the work-piece material is caused to move relative to the work-piece to generate frictional heat causing the work-piece in the region of the probe to become plasticised, the probe effectively entering the work-piece. The probe is conventionally caused to rotate about the probe axis and to move along the work-piece along the length of the weld to be formed.
The fusion welding process is conveniently performed by means of an electron beam welding process. Other fusion welding processes could be utilised but, of the methods currently available, electron beam welding is preferred because of the depth of weld achievable at relatively low weld widths.
The work-pieces may be made from low-density alloys. For example, the density of the metal is preferably less than 5,000 Kgm−3, more preferably less than 4,000 Kgm−3, and yet more preferably less than 3,000 Kgm−3. The work-pieces are preferably made from lightweight alloys. The work-pieces may be made from aluminium alloys. The work-pieces may be made from cold-worked metal. The cold-worked metal may for example have been subjected to a rolling process. The method is of particular application in the case where the work-pieces are suitable for use in the manufacture of an aircraft or aerospace component. For example, the metal may be any conventional or suitable alloy used in the aerospace industry, such as 2000 series, 6000 series, 7000 series aluminium alloys, or aluminium-lithium alloys. Such alloys have in the past been viewed as being difficult to weld together satisfactorily, especially where the depth of the joint to be welded is greater than or equal to about 50 mm. Such alloys may be difficult to weld satisfactorily due to one or more of several factors including a) the complexity of the alloying system, b) the particular heat treatment(s) to which the alloy has previously been subjected, c) the mechanical/chemical structure/composition of the material, d) the particular arrangement of different phases in the alloy or of precipitates formed in the alloy and/or e) the size and/or orientation of the grains of the alloy material.
The two work-pieces may, but need not be, of the same type of material. The method of the present invention is for example advantageously able to be used to weld together different metals or alloys. For example, the method of the present invention could be utilised when manufacturing a component, one part of which being required to have one set of mechanical/physical properties and another part of the component being required to have a different set of mechanical/physical properties.
The method may of course be performed to weld together one or more other work-pieces, possibly welding the multiplicity of work-pieces together simultaneously or possibly welding the multiplicity of work-pieces together in series (sequentially).
The work-pieces may be in the form of blocks of material. The blocks of material after having been welded together may for example be machined into a component. The present invention thus also provides a method of manufacturing a component, for example an aircraft component, wherein the component is machined from a block of metal, the block of metal having been made from two or more work-pieces welded together in accordance with the method according to the present invention as described above. The block or blocks may conveniently, but not necessarily, be cuboid in shape. The size and shape of the work-pieces to be welded together may be, and possibly need only be, limited by the limitations of the fusion welding process employed. For example, it is possible to weld with a 120 kW (120 kV operating at up to 1000 mA) electron beam welding apparatus to depths of up to 450 mm. With such an apparatus it would be possible to weld together two work-pieces having a thickness of 450 mm by means of a single pass electron beam weld. If a dual pass (i.e. one welding pass on each side of the joint to be welded) electron beam weld process is utilised, the thickness of work-pieces able to be joined could be as high as 900 mm. Greater thicknesses of material could be welded together with more powerful fusion welding equipment. Whilst a dual pass electron beam welding process is possible, a single pass process is preferred, because of the potential difficulties in ensuring a high quality weld joint in the region where the two electron beam welds interface.
It will be appreciated that the work-pieces may be trimmed and/or machined after performance of the method of the present invention and that therefore the integrity of the weld joint in the regions of the work-piece that are subsequently removed is not important. There may also be other regions where the integrity of the joint between the work-pieces is not important for other reasons. For example, the work-pieces once joined might be machined into a component that in use is subjected to forces/stresses such that the strength of weld joint required varies across the joint. In such cases, the portions of the respective work-pieces being welded together in accordance with the present invention may actually be contained within larger regions that have been subjected to a surface treatment, or similarly prepared.
According to another aspect of the invention there is provided a method of manufacturing an aircraft component including the following steps:
According to a further aspect of the invention there is provided a method of welding together two metal work-pieces, the work-pieces being made from a lightweight alloy suitable for use in the manufacture of an aircraft component, the method including the following steps:
The invention further provides a component comprising a weld joint joining one part of the component to an adjacent part of the component, the component in the region of the joint comprising a portion, that has been fusion welded, sandwiched between two portions that have each been friction stir welded. The component may be in the form of an aerospace component, an aircraft component or any other similar component.
It will be appreciated that features described with reference to one aspect of the invention may be incorporated into other aspects of the invention. For example, the component, for example an aircraft component, according to the present invention may be made by means of the method of the present invention.
It will be appreciated that a component formed by means of the present invention may require further processing before assembly. The component may therefore, in certain circumstances, be considered as an intermediate, requiring further processing before being considered as a finished article. For example, the component may require further machining, treating, assembly with other parts, or any other such processes. It will therefore be understood that the term component is used herein both to cover the case where the component is in a state ready for final assembly and the case where the component is at an earlier stage in the component's manufacture.
According to a preferred aspect of the invention there is also provided a method of welding together two work-pieces, the method including the following steps:
Embodiments of the present invention will now be described by way of example only with reference to the accompanying drawings, of which:
a illustrates schematically the welding together of two metal plates according to a first embodiment of the invention;
b shows a portion of one of the plates shown in
c shows a cross-section of the portion of the plate shown in
a shows a cross-section of the final welded joint formed by means of the first embodiment;
b to 2f show magnified portions of
g shows a portion of
The first embodiment of the invention relates to an experiment in which two rolled plates were welded together. The rolled plates 1 before being joined are illustrated schematically in
The microstructure of the respective sides 2 of the plates 1 to be joined was modified using a friction stir welding process. The tool used in friction stir welding process had a 30 mm shoulder diameter and a pin having a length of 12.05 mm. The pin used has a cross-section that tapers (the cross-section becomes progressively smaller) along its length, the angle of the taper being 10 degrees, from a diameter of 14 mm at its widest at the top of the pin (immediately beneath the shoulder). Ten overlapping bead-on-plate weld runs were performed in the LT (Long Transverse) direction on the side 2 of each plate 1 using the following welding parameters: tool rotation=190 rpm, welding speed=150 mm/min and vertical force (i.e. down the length of the tool)=61 kN. To avoid material overheating during the welding process, on completion of each weld run (each bead-on-plate weld) the plate was allowed to cool to room temperature before the next weld run was commenced.
After the friction stir welding step was completed, the top surfaces of the welds were skimmed, thereby removing about 1.0-1.5 mm of material from the sides 2 to be welded together, thereby forming a smooth flat surface. Both plates were also machined to trim their thickness (in the ST direction) so that the surface of the side 2 of the plate 1 to be welded was 100 mm thick, the entire surface on that side 2 thus having been affected by the friction stir welding process (thereby providing a fine grain structure).
The two plates 1 were assembled in a vacuum chamber with the use of tack welds to form a 100 mm thick (in the ST direction) butt joint running in the LT direction. Run-in and run-out plates were positioned either side of the butt joint and the joint was backed by a backing plate. Electron beam welding was then performed horizontally in the LT direction with a vertical beam and using the following welding parameters: accelerating voltage=60 kV, beam current=450 mA, focus current=610 mA, welding speed=240 mm/min, vacuum in the chamber=2×10−4 torr, beam oscillation=1.2 mm diameter circle and an oscillation frequency=800 Hz.
The welded joint so produced is shown in
The average width of the electron beam weld is about 5 mm. The average width of regions A-D-A combined is about 20 mm. The width of the heat affected zone of the electron beam weld is very approximately 30 mm.
b shows a region of
c shows a region of
d shows a region of
e shows a region of
f shows a region of
a to 2g illustrate that the present embodiment may be utilised to produce high quality welds, without liquation cracking, on alloys where it has generally been considered difficult, if not impossible, to form welds on joints having any substantial thickness. The limit on the thickness of the joint of the present invention will probably be determined by the limit of the thickness to which the fusion welding (in this embodiment, electron beam welding) can be effected satisfactorily.
By way of comparison,
According to a third embodiment, shown in
It will, of course, be appreciated that various modifications may be made to the above-described embodiments without departing from the spirit of the present invention. For example, components (such as for example a wing rib or a section of the wing skin) other than a wing spar could be machined from the billets of aluminium once welded together. Rather than electron beam welding, other fusion welding processes could be employed, such as laser welding. The invention has application in relation to alloys other than Aluminium alloys including for example Magnesium alloys. Other modifications will, of course, be apparent to the person skilled in the art.
| Number | Date | Country | Kind |
|---|---|---|---|
| 0225518 | Nov 2002 | GB | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/GB03/04646 | 10/28/2003 | WO | 00 | 4/29/2005 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2004/039527 | 5/13/2004 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4503314 | Kakami et al. | Mar 1985 | A |
| 4830265 | Kennedy et al. | May 1989 | A |
| 5211910 | Pickens et al. | May 1993 | A |
| 5460317 | Thomas et al. | Oct 1995 | A |
| 5720824 | Bronson et al. | Feb 1998 | A |
| 5813592 | Midling et al. | Sep 1998 | A |
| 6045028 | Martin et al. | Apr 2000 | A |
| 6050475 | Kinton et al. | Apr 2000 | A |
| 6051325 | Talwar et al. | Apr 2000 | A |
| 6098808 | Matsuda et al. | Aug 2000 | A |
| 6168067 | Waldron et al. | Jan 2001 | B1 |
| 6219916 | Walker et al. | Apr 2001 | B1 |
| 6227430 | Rosen et al. | May 2001 | B1 |
| 6398883 | Forrest et al. | Jun 2002 | B1 |
| 6659330 | Ezumi et al. | Dec 2003 | B2 |
| 6712916 | Mishra et al. | Mar 2004 | B2 |
| 6726085 | Litwinski et al. | Apr 2004 | B2 |
| 6742697 | McTernan et al. | Jun 2004 | B2 |
| 6777106 | Catteau et al. | Aug 2004 | B2 |
| 6799708 | von Strombeck et al. | Oct 2004 | B2 |
| 7122761 | Ditzel et al. | Oct 2006 | B2 |
| 20020158109 | Gendoh et al. | Oct 2002 | A1 |
| 20030218052 | Litwinski | Nov 2003 | A2 |
| Number | Date | Country |
|---|---|---|
| 199 57 136 | Feb 2001 | DE |
| 0 615 480 | Sep 1994 | EP |
| 0 810 054 | Dec 1997 | EP |
| 0 810 055 | Dec 1997 | EP |
| 1 162 283 | Dec 2001 | EP |
| 52 131943 | Nov 1977 | JP |
| 57181775 | Nov 1982 | JP |
| 2001150155 | May 2001 | JP |
| 2001-234308 | Aug 2001 | JP |
| 2002-249860 | Sep 2002 | JP |
| WO 9310935 | Jun 1993 | WO |
| WO9310935 | Jun 1993 | WO |
| WO 9526254 | Oct 1995 | WO |
| WO 0183153 | Nov 2001 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20060013645 A1 | Jan 2006 | US |