Patent Grant
9076592
Wet capacitors are increasingly being used in the design of circuits due to their volumetric efficiency, reliability, and process compatibility. Wet capacitors typically have a larger capacitance per unit volume than certain other types of capacitors, making them valuable in high-current, high power and low-frequency electrical circuits. One type of wet capacitor that has been developed is a wet electrolytic capacitor that includes a valve metal anode, a cathode, and a liquid electrolyte. The unit cell voltage in this type of capacitor is generally higher due to the formation of a dielectric metal oxide film over the anode surface. Wet electrolytic capacitors containing a dielectric from a valve metal tend to offer a good combination of high capacitance with low leakage current. Another type of wet capacitor is a wet symmetric capacitor in which the anode and cathode are similar in terms of structure and composition. The unit cell voltage in this type of capacitor is generally low due to the inevitable decomposition of the electrolyte at high voltage. Whether electrolytic or symmetric, however, the cathodes of wet capacitors have typically included a metal substrate and a conductive coating that provides protection from the liquid electrolyte. Capacitance of the conductive coating is measured through either a faradic current, e.g., electrochemical process or non-faradic mechanism (e.g., double layer formation). Conventional coatings include activated carbon, metal oxides (e.g., niobium dioxide), and the like. Unfortunately, however, the coatings are expensive and can become easily detached under certain conditions.
As such, a need remains for a wet electrolytic capacitor that possesses good thermal, mechanical robustness and electrical performance.
In accordance with one embodiment of the present invention, a wet electrolytic capacitor is disclosed that comprises an anode, cathode, and fluid working electrolyte in communication with the anode and cathode. The anode comprises a sintered porous anode body that is coated with a dielectric. The cathode comprises a metal substrate over which is disposed a conductive polymer coating. The conductive polymer coating is formed by anodic electrochemical polymerization of a microemulsion, and the microemulsion comprises a precursor monomer, nonionic surfactant, sulfonic acid, and solvent.
In accordance with another embodiment of the present invention, a wet electrolytic capacitor is disclosed that comprises an anode, fluid working electrolyte, and a generally cylindrical metal casing within which the anode and fluid electrolyte are positioned. The anode contains a generally cylindrical, sintered porous anode body that is coated with a dielectric, and contains tantalum. The anode further comprises an anode lead wire that extends from the proximal end of the anode in the longitudinal direction. A conductive polymer coating is disposed on the metal casing so that the coating is in communication with the fluid electrolyte. The conductive polymer coating is formed by anodic electrochemical polymerization of a microemulsion, the microemulsion comprising a precursor monomer, nonionic surfactant, sulfonic acid, and solvent.
In accordance with yet another embodiment of the present invention, a method for forming a cathode of a wet capacitor is disclosed that comprises applying a microemulsion to a metal substrate, wherein the microemulsion comprises a precursor monomer, nonionic surfactant, sulfonic acid, and solvent; placing an electrode in contact with the metal substrate; and supplying a current feed to the electrode to induce electrolysis and oxidative polymerization of the precursor monomer, thereby forming a conductive polymer coating.
Other features and aspects of the present invention are set forth in greater detail below.
A full and enabling disclosure of the present invention, including the best mode thereof, directed to one of ordinary skill in the art, is set forth more particularly in the remainder of the specification, which makes reference to the appended figures in which:
Repeat use of reference characters in the present specification and drawings is intended to represent same or analogous features or elements of the invention.
It is to be understood by one of ordinary skill in the art that the present discussion is a description of exemplary embodiments only, and is not intended as limiting the broader aspects of the present invention, which broader aspects are embodied in the exemplary construction.
The present invention generally relates to a wet electrolytic capacitor that contains an anodically oxidized porous anode body, a cathode containing a metal substrate coated with a conductive coating, and a working electrolyte that wets the dielectric on the anode. The degree of surface contact between the conductive coating and the surface of the metal substrate is enhanced in the present invention by selectively controlling the manner in which the conductive coating is formed. More particularly, the conductive coating is formed through anodic electrochemical polymerization (“electro-polymerization”) of a microemulsion on the surface of the metal substrate. The microemulsion is a thermodynamically stable, isotropic liquid mixture that contains a precursor monomer, sulfonic acid, nonionic surfactant, and solvent. Through selective control of the components of the microemulsion, the present inventors have discovered that a variety of benefits can be achieved. For example, the pH level of the microemulsion may be kept at a relatively neutral level to minimize the extent that the monomer will undergo premature polymerization under acidic conditions, thereby extending the operational lifetime of the microemulsion. This may be accomplished through the use of a surfactant that is nonionic, rather than ionic, and by selectively controlling the relative concentration of the ionic sulfonic acid component relative to other nonionic components of the microemulsion. The present inventors have also discovered that the nature of the microemulsion can allow it to substantially uniformly cover the surface of the substrate, and when polymerized, also facilitate the growth of oligomeric chains immediately adjacent to the surface of the metal substrate and within the pits, which can increase robustness and mechanical stability.
Various embodiments of the present invention will now be described in more detail.
I. Cathode
A. Metal Substrate
The substrate may be include a metal, such as tantalum, niobium, aluminum, nickel, hafnium, titanium, copper, silver, steel (e.g., stainless), alloys thereof (e.g., electrically conductive oxides), composites thereof (e.g., metal coated with electrically conductive oxide), and so forth. Titanium and tantalum, as well as alloys thereof, are particularly suitable for use in the present invention. The geometric configuration of the substrate may generally vary as is well known to those skilled in the art, such as in the form of a container, can, foil, sheet, screen, mesh, etc. In one embodiment, for example, the metal substrate forms a casing having a generally cylindrical shape. It should be understood, however, that any geometric configuration may be employed in the present invention, such as D-shaped, rectangular, triangular, prismatic, etc. The casing may optionally include a lid that covers the anode and electrolyte, which may be formed from the same or different material than the casing.
If desired, the substrate may be roughened to increase its surface area and increase the degree to which the conductive polymer may be able to adhere thereto. In one embodiment, for example, the surface is chemically etched, such as by applying a solution of a corrosive substance (e.g., hydrochloric acid) to the surface. The surface may also be electrochemically etched, such as by applying a voltage to a solution of the corrosive substance so that it undergoes electrolysis. The voltage may be raised to a sufficiently high level to initiate “sparking” at the surface of the substrate, which is believed to create high local surface temperatures sufficient that etches away the substrate. This technique is described in more detail in U.S. Patent Application Publication No. 2010/0142124 to Dreissig, et al. In addition to chemical or electrochemical roughening techniques, mechanical roughening may also be employed. In one embodiment, for instance, the surface of the metal substrate may be abrasive blasted by propelling a stream of abrasive media (e.g., sand) against at least a portion of a surface thereof.
B. Microemulsion
The microemulsion employed for anodic electrochemical polymerization generally contains a solvent that serves as a continuous phase within which the precursor monomer is dispersed. Any of a variety of different solvents may be employed in the microemulsion, such as alcohols, glycols, water, etc. In one particular embodiment, the microemulsion is aqueous in nature. Regardless, solvents (e.g., water) may constitute from about 50 wt. % to about 99 wt. %, in some embodiments from about 70 wt. % to about 98 wt. % and in some embodiments, from about 80 wt. % to about 95 wt. %. The remaining components of the microemulsion (e.g., precursor monomers, nonionic surfactants, and sulfonic acids) may likewise constitute from about 1 wt. % to about 50 wt. %, in some embodiments from about 2 wt. % to about 30 wt. % and in some embodiments, from about 5 wt. % to about 20 wt. % of the microemulsion.
i. Precursor Monomer
Any of a variety of precursor monomers may be employed in the microemulsion that are capable of being polymerized to form a conductive polymer. Specific examples of such monomers include, for instance, pyrroles (e.g., pyrrole, alkylpyrroles, etc.), thiophenes (e.g., 3,4-ethylenedioxythiophene), anilines (e.g., alkylanilines, such as methylaniline, and alkoxyanilines, such as methoxyaniline), as well as derivatives and combinations thereof. A single monomer may be employed to form a homopolymer, or two or more monomers may be employed to form a copolymer. In one particular embodiment, for example, a thiophene derivative monomer may be employed that has the following general structure:
wherein,
T is O or S;
D is an optionally substituted C1 to C5 alkylene radical (e.g., methylene, ethylene, n-propylene, n-butylene, n-pentylene, etc.);
R7 is independently selected from a linear or branched, optionally substituted C1 to C18 alkyl radical (e.g., methyl, ethyl, n- or iso-propyl, n-, iso-, sec- or tert-butyl, n-pentyl, 1-methylbutyl, 2-methylbutyl, 3-methylbutyl, 1-ethylpropyl, 1,1-dimethylpropyl, 1,2-dimethylpropyl, 2,2-dimethylpropyl, n-hexyl, n-heptyl, n-octyl, 2-ethylhexyl, n-nonyl, n-decyl, n-undecyl, n-dodecyl, n-tridecyl, n-tetradecyl, n-hexadecyl, n-octadecyl, etc.); optionally substituted C5 to C12 cycloalkyl radical (e.g., cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl cyclodecyl, etc.); optionally substituted C6 to C14 aryl radical (e.g., phenyl, naphthyl, etc.); optionally substituted C7 to C18 aralkyl radical (e.g., benzyl, o-, m-, p-tolyl, 2,3-, 2,4-, 2,5-, 2-6, 3-4-, 3,5-xylyl, mesityl, etc.); optionally substituted C1 to C4 hydroxyalkyl radical, or hydroxyl radical; and
q is an integer from 0 to 8, in some embodiments, from 0 to 2, and in one embodiment, 0. It should be understood that the R7 group(s) may be bonded to one or more of the carbon atoms of the ring system.
Examples of substituents for the radicals “D” or “R7” include, for instance, hydroxyl, alkyl, cycloalkyl, aryl, aralkyl, alkoxy, halogen, ether, thioether, disulphide, sulfoxide, sulfone, sulfonate, amino, aldehyde, keto, carboxylic acid ester, carboxylic acid, carbonate, carboxylate, cyano, alkylsilane and alkoxysilane groups, carboxylamide groups, and so forth. Particularly suitable thiophene monomers are those in which “D” is an optionally substituted C2 to C3 alkylene radical. For instance, optionally substituted 3,4-alkylenedioxythiophenes may be employed that have the general structure:
wherein, R7 and q are as defined above. In one particular embodiment, “q” is 0 such that the monomer is 3,4-ethylenedioxythiophene. One commercially suitable example of 3,4-ethylenedioxthiophene is available from Heraeus Clevios under the designation Clevios™ M. Of course, as noted above, derivatives of 3,4-ethylenedioxythiophene may also be employed. The derivatives may be made up of identical or different monomer units and used in pure form and in a mixture with one another and/or with the monomers. For instance, suitable derivatives of 3,4-ethylenedioxythiophene include those having the following general structure:
where,
y is from 1 to 10, in some embodiments from 1 to 5, in some embodiments, from 1 to 3, and in some embodiments, from 1 to 2 (e.g., 2); and
R is a linear or branched, optionally substituted C1 to C18 alkyl radical (e.g., methyl, ethyl, n- or iso-propyl, n-, iso-, sec- or tert-butyl, n-pentyl, 1-methylbutyl, 2-methylbutyl, 3-methylbutyl, 1-ethylpropyl, 1,1-dimethylpropyl, 1,2-dimethylpropyl, 2,2-dimethylpropyl, n-hexyl, n-heptyl, n-octyl, 2-ethylhexyl, n-nonyl, n-decyl, n-undecyl, n-dodecyl, n-tridecyl, n-tetradecyl, n-hexadecyl, n-octadecyl, etc.); optionally substituted C5 to C12 cycloalkyl radical (e.g., cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl cyclodecyl, etc.); optionally substituted C6 to C14 aryl radical (e.g., phenyl, naphthyl, etc.); optionally substituted C7 to C18 aralkyl radical (e.g., benzyl, o-, m-, p-tolyl, 2,3-, 2,4-, 2,5-, 2-6, 3-4-, 3,5-xylyl, mesityl, etc.); optionally substituted C1 to C4 hydroxyalkyl radical; hydroxyl radical; or a combination thereof. Examples of substituents for the radicals “R” include, for instance, hydroxyl, alkyl, cycloalkyl, aryl, aralkyl, alkoxy, halogen, ether, thioether, disulphide, sulfoxide, sulfone, sulfonate, amino, aldehyde, keto, carboxylic acid ester, carboxylic acid, carbonate, carboxylate, cyano, alkylsilane and alkoxysilane groups, carboxylamide groups, and so forth. Particular examples of such polymers include hydroxyethylated poly(3,4-ethylenedioxythiophene) (y is 2 and R is OH) and hydroxymethylated poly(3,4-ethylenedioxthiophene) (y is 1 and R is OH). It should be understood that other “R” group(s) may also be bonded to one or more other the carbon atoms of the ring system.
Suitable pyrrole monomers may likewise include those having the following general structure:
wherein,
R1 is independently selected from hydrogen, alkyl, alkenyl, alkoxy, alkanoyl, alkythio, aryloxy, alkylthioalkyl, alkylaryl, arylalkyl, amino, alkylamino, dialkylamino, aryl, alkylsulfinyl, alkoxyalkyl, alkylsulfonyl, arylthio, arylsulfinyl, alkoxycarbonyl, arylsulfonyl, acrylic acid, phosphoric acid, phosphonic acid, halogen, nitro, cyano, hydroxyl, epoxy, silane, siloxane, alcohol, benzyl, carboxylate, ether, amidosulfonate, ether carboxylate, ether sulfonate, ester sulfonate, and urethane; or both R1 groups together may form an alkylene or alkenylene chain completing a 3, 4, 5, 6, or 7-membered aromatic or alicyclic ring, which ring may optionally include one or more divalent nitrogen, sulfur or oxygen atoms; and
R2 is hydrogen, alkyl, alkenyl, aryl, alkanoyl, alkylthioalkyl, alkylaryl, arylalkyl, amino, epoxy, silane, siloxane, alcohol, benzyl, carboxylate, ether, ether carboxylate, ether sulfonate, ester sulfonate, and urethane. In one particular embodiment, both R1 and R2 are hydrogen. Other suitable pyrroles may include 3-alkylpyrroles, such as 3-hexylpyrrole; 3,4-dialkylpyrroles, such as 3,4-dihexylpyrrole; 3-alkoxypyrroles, such as 3-methoxypyrrole; and 3,4-dialkoxypyrroles, such as 3,4-dimethoxypyrrole.
The total concentration of monomers employed in the microemulsion may vary, but is typically from about 0.1 wt. % to about 15 wt. %, in some embodiments from about 0.4 wt. % to about 10 wt. %, and in some embodiments, from about 0.5 wt. % to about 5 wt. % by weight of the microemulsion.
ii. Nonionic Surfactant
A nonionic surfactant is also employed in the microemulsion. The presence of nonionic micelles leads to an increase in the solubility, forming a microscopically homogenous distribution of these micelles and in some cases a solution of the precursor monomer. Nonionic surfactants typically have a hydrophobic base, such as a long chain alkyl group or an alkylated aryl group, and a hydrophilic chain containing a certain number (e.g., 1 to about 30) of ethoxy and/or propoxy moieties. Although not necessarily require, nonionic surfactants having a certain hydrophilic/lipophilic balance (“HLB”) value may help improve the stability of the microemulsion. The HLB index is well known in the art and is a scale that measures the balance between the hydrophilic and lipophilic solution tendencies of a compound with lower numbers representing highly lipophilic tendencies and the higher numbers representing highly hydrophilic tendencies. In some embodiments of the present invention, the HLB value of the nonionic surfactant is from about 5 to about 20, in some embodiments from about 10 to about 19 and in some embodiments, from about 11 to about 18. If desired, two or more surfactants may be employed that have HLB values either below or above the desired value, but together have an average HLB value within the desired range.
Suitable nonionic surfactants may include, for instance, polyoxyethylene chains as hydrophilic groups, polyglycerol fatty acid esters, polyglycerol fatty alcohol ethers, sucrose fatty acid esters, and hydrocarbyl polyglycosides. In one embodiment, the nonionic surfactant includes polyoxyethylene chains as hydrophilic groups and is selected from the group of polyoxyethylene fatty acid esters, polyoxyethylene fatty alcohol ethers, polyoxyethylene sorbitol anhydride fatty acid esters, polyoxyethylene glycerol mono fatty acid esters, polyoxyethylene hydrogenated castor oil and polyoxyethylene hydrogenated castor oil mono fatty acid esters, etc., as well as combinations thereof. Particularly suitable are polyoxyethylene fatty alcohol ethers in which the fatty alcohol forming the polyoxyethylene fatty alcohol ether is saturated or unsaturated, and has 8 to 22 carbon atoms (e.g., 8 to 14), and the polyoxyethylene structure moiety contains on average 4 to 60 ethylene oxide repeating units (e.g., 4 to 12). Examples of such surfactants include polyoxyethylene octyl ethers (e.g., polyoxyethylene-5 octyl ether), polyoxyethylene decyl ethers, polyoxyethylene lauryl ethers (e.g., polyoxyethylene-8 lauryl ether or polyoxyethylene-10-lauryl ether), polyoxyethylene myristyl ethers, polyoxyethylene palmityl ethers, polyoxyethylene isostearyl ethers, polyoxyethylene stearyl ethers, polyoxyethylene oleyl ethers, polyoxyethylene behenyl ethers, etc.
Regardless of its particular form, the nonionic surfactant can facilitate the formation of a microemulsion of precursor monomer droplets. Without intending to be limited by theory, it is believed that such droplets can result in the formation of very small polymer units on the surface of the cathode substrate during anodic electrochemical polymerization. Such smaller polymer units can, in turn, result in a coating that is substantially uniform with excellent surface coverage. The droplets may, for instance, have an average diameter of about 5 micrometers or less, in some embodiments about 4 micrometers or less, in some embodiments from about 10 nanometers to about 2 micrometers, and in some embodiments, from about 20 nanometers to about 1 micrometer. The term “diameter” can refer to the “hydrodynamic equivalent diameter” of a particle as determined using known techniques, such as photon correlation spectroscopy, dynamic light scattering, quasi-elastic light scattering, etc. These methods are generally based on the correlation of particle size with diffusion properties of particles obtained from Brownian motion measurements. Brownian motion is the random movement of the particles due to bombardment by the solvent molecules that surround the particles. The larger the particle, the more slowly the Brownian motion will be. Velocity is defined by the translational diffusion coefficient. The measured particle size value thus relates to how the particle moves within a liquid and is termed the “hydrodynamic diameter.” Various particle size analyzers may be employed to measure the diameter in this manner. One particular example is a Cordouan VASCO 3 Particle Size Analyzer.
To help achieve the desired improvement in the surface coverage of the precursor monomer, it is also generally desired that the concentration of the nonionic surfactant is selectively controlled within a certain range relative to the precursor monomer. For example, the ratio of the weight of nonionic surfactants to the weight of precursor monomers within the microemulsion may be from about 0.5 to about 1.5, in some embodiments from about 0.6 to about 1.4, and in some embodiments, from about 0.8 to about 1.2. Nonionic surfactants may, for instance, constitute from about 0.2 wt. % to about 10 wt. %, in some embodiments from about 0.5 wt. % to about 8 wt. %, and in some embodiments, from about 1 wt. % to about 5 wt. % of the microemulsion.
iii. Sulfonic Acid
The microemulsion of the present invention also contains a sulfonic acid that can act as a secondary dopant to provide excess charge to the conductive polymer and stabilize its conductivity. Such acids may, for example, result in a microemulsion that has an electrical conductivity of from about 1 to about 100 milliSiemens per centimeter (“mS/cm”), in some embodiments from about 5 to about 60 mS/cm, and in some embodiments, from about 15 to about 50 mS/cm, determined at a temperature of 23° C. using any known electric conductivity meter (e.g., Oakton Con Series 11). The nature of the sulfonic acid, as wells as its relative concentration, may also be selectively controlled so that the pH level of the microemulsion remains relatively neutral as noted above, such as within a range of from about 5.0 to about 8.5, in some embodiments from about 5.5 to about 8.0, and in some embodiments, from about 6.0 to about 7.5. For example, the ratio of the weight of sulfonic acids to the weight of precursor monomers within the microemulsion is from about 0.2 to about 1.2, in some embodiments from about 0.4 to about 1.1, and in some embodiments, from about 0.6 to about 1.0. Likewise, the ratio of the weight of sulfonic acids to the weight of nonionic surfactants within the microemulsion is from about 0.2 to about 1.2, in some embodiments from about 0.3 to about 0.9, and in some embodiments, from about 0.4 to about 0.8.
The sulfonic acid is typically a low molecular weight organic-based monosulfonic acid, disulfonic acid, or trisulfonic acid. Specific examples of such acids include, for instance, alkylsulfonic acids (e.g., 2-acrylamide-2-methylpropanesulfonic acid, etc.); arylene sulfonic acids, such as benzenesulfonic acids (e.g., phenolsulfonic acid, styrenesulfonic acid, p-toluenesulfonic acid, dodecylbenzenesulfonic acid, etc.) and naphthalenesulfonic acids (e.g., 1-naphthalenesulfonic acid, 2-naphthalenesulfonic acid, 1,3-naphthalenedisulfonic acid, 1,3,6-naphthalenetrisulfonic acid, 6-ethyl-1-naphthalenesulfonic acid, etc.); anthraquinonesulfonic acids (e.g., anthraquinone-1-sulfonic acid, anthraquinone-2-sulfonic acid, anthraquinone-2,6-disulfonic acid, 2-methylanthraquinone-6-sulfonic acid, etc.); camphorsulfonic acids, as well as derivatives and mixtures thereof. Arylene sulfonic acids are particularly suitable for use in the microemulsion, such as 1-naphthalenesulfonic acid, 2-naphthalenesulfonic acid, and/or p-toluenesulfonic acid.
It should be understood that the term “sulfonic acid” as used herein also encompass salts of acids, such as those noted above, which can dissociate in an aqueous solution, such as sodium salts, lithium salts, potassium salts, etc. In one embodiment, for example, the sulfonic acid may be a sodium or potassium salt of 1-naphthalenesulfonic acid, 2-naphthalenesulfonic acid, and/or p-toluenesulfonic acid.
iv. Other Components
In addition to the components noted above, the microemulsion may also contain various other additives. For example, a defoaming agent may be employed in certain embodiments to reduce the degree of foam produced by the nonionic surfactant during the anodic electrochemical polymerization. Suitable defoaming agents may include, for instance, oils, esters, ethers, glycols, polysiloxanes, long chain oxygenated hydrocarbons (e.g., C6 to C12 alcohols), etc., as well as mixtures thereof. Particularly suitable defoaming agents are long chain oxygenated hydrocarbons, such as octanol, decanol and polyethylene glycols. When employed, such defoaming agents may constitute from about 0.01 wt. % to about 5 wt. %, in some embodiments from about 0.05 wt. % to about 4 wt. %, and in some embodiments, from about 0.1 wt. % to about 2 wt. % of the microemulsion. Besides defoaming agents, a wide variety of other additives may also be employed in the microemulsion. Nevertheless, one particular benefit of the present invention is that the microemulsion, and the resulting conductive polymer coating, can be generally free of iron ions (e.g., Fe2+ or Fe3+ ions) that are often employed in the oxidative catalysts (e.g., iron(III)-p-toluene sulfonate or iron(III)-o-toluene sulfonate) used during chemical polymerization of conductive polymers, which can lead to dielectric degradation at the high voltages often employed during the use of the wet capacitor. For instance, the microemulsion typically contains less than about 0.5 wt. %, in some embodiments, less than about 0.1 wt. %, and in some embodiments, less than about 0.05 wt. % (e.g., 0 wt. %) of such iron-based oxidative catalysts.
B. Anodic Electrochemical Polymerization
To apply the microemulsion to the metal substrate, any of a variety of suitable application techniques may be employed, such as screen-printing, dipping, electrophoretic coating, spraying, etc. Regardless of how it is applied, the monomer within the microemulsion is anodically electrochemically-polymerized to form a conductive polymer coating on the surface of the metal substrate. In one embodiment, for example, the metal substrate is dipped into a bath containing the microemulsion of the present invention. A pair of electrodes may be disposed within the bath for electrolysis. One electrode may be connected to the positive terminal of a power source and also in contact with the metal substrate. The other electrode may be connected to the negative terminal of the power source and an additional inert metal. During operation, the power source supplies a current feed to the electrodes in the electrochemical cell, thereby inducing electrolysis of the electrolyte and oxidative polymerization of the monomer in the microemulsion, or solution, onto the metal substrate. Anodic electrochemical polymerization is generally performed at ambient temperature to ensure that the microemulsion does not phase separate. For example, the microemulsion may be kept at a temperature of from about 15° C. to about 80° C., in some embodiments from about 20° C. to about 75° C., and in some embodiments, from about 25° C. to about 50° C. The amount of time in which the metal substrate is in contact with the microemulsion during anodic electrochemical polymerization may vary. For example, the metal substrate may be dipped into such a solution for a period of time ranging from about 10 seconds to about 10 minutes.
If desired, multiple polymerization steps may be repeated until the desired thickness of the coating is achieved. In such cases, the additional layer(s) may be polymerized using the technique and microemulsion of the present invention, or using other methods, such as chemical polymerization. The additional layer(s) (e.g., chemically polymerized layer) may be disposed directly on the metal substrate or over the electro-polymerized layer. Regardless, the total target thickness of the coating may generally vary depending on the desired properties of the capacitor. Typically, the resulting conductive polymer coating has a thickness of from about 0.2 micrometers (“μm”) to about 50 μm, in some embodiments from about 0.5 μm to about 20 μm, and in some embodiments, from about 1 μm to about 5 μm. It should be understood that the thickness of the coating is not necessarily the same at all locations on the substrate. Nevertheless, the average thickness of the coating on the substrate generally falls within the ranges noted above.
The resulting conductive polymer coating includes conductive polymer(s) that are typically π-conjugated chains of aromatic heterocyclic units and have increased electrical conductivity after oxidation. Because the conductive polymer is generally semi-crystalline or amorphous, it can dissipate and/or absorb the heat associated with the high voltage. This in turn prevents fluid electrolyte phase transitions (from liquid to gas) at the interface. The conductive polymer will somewhat swell through absorption of some volume of fluid electrolyte. Examples of such π-conjugated conductive polymers that can be formed in accordance with the present invention include polyheterocycles (e.g., polypyrroles, polythiophenes, polyanilines, etc.), polyacetylenes, poly-p-phenylenes, polyphenolates, and so forth. In one particular embodiment, the substituted polythiophene has the following general structure:
wherein,
T, D, R7, and q are defined above; and
n is from 1 to 2,000, in some embodiments from 2 to 500, and in some embodiments, from 4 to 350. Particularly suitable thiophene polymers are those in which “D” is an optionally substituted C2 to C3 alkylene radical. For instance, the polymer may be optionally substituted poly(3,4-ethylenedioxythiophene), which has the following general structure:
II. Anode
The anode may include a sintered porous body formed from a valve metal composition. The valve metal composition may contain a valve metal (i.e., metal that is capable of oxidation) or valve metal-based compound, such as tantalum, niobium, aluminum, hafnium, titanium, alloys thereof, oxides thereof, nitrides thereof, and so forth. For example, the valve metal composition may contain an electrically conductive oxide of niobium, such as niobium oxide having an atomic ratio of niobium to oxygen of 1:1.0±1.0, in some embodiments 1:1.0±0.3, in some embodiments 1:1.0±0.1, and in some embodiments, 1:1.0±0.05. The niobium oxide may be NbO0.7, NbO1.0, NbO1.1, and NbO2. Examples of such valve metal oxides are described in U.S. Pat. No. 6,322,912 to Fife; U.S. Pat. No. 6,391,275 to Fife et al.; U.S. Pat. No. 6,416,730 to Fife et al.; U.S. Pat. No. 6,527,937 to Fife; U.S. Pat. No. 6,576,099 to Kimmel, et al.; U.S. Pat. No. 6,592,740 to Fife, et al.; and U.S. Pat. No. 6,639,787 to Kimmel, et al.; and U.S. Pat. No. 7,220,397 to Kimmel, et al., as well as U.S. Patent Application Publication Nos. 2005/0019581 to Schnitter; 2005/0103638 to Schnitter, et al.; 2005/0013765 to Thomas, et al., all of which are incorporated herein in their entirety by reference thereto for all purposes.
To form the anode, a powder of the valve metal composition is generally employed. The powder may contain particles any of a variety of shapes, such as nodular, angular, flake, etc., as well as mixtures thereof. Particularly suitable powders are tantalum powders available from Cabot Corp. (e.g., C255 flake powder, TU4D flake/nodular powder, etc.) and H. C. Starck (e.g., NH175 nodular powder). In certain cases, the powder may have a low specific charge to optimize the ability to grow a thick dielectric layer that is capable of withstanding high operational voltages. That is, the powder may have a specific charge of less than about 20,000 microFarads*Volts per gram (“μF*V/g”), in some embodiments about 1,000 μF*V/g to about 20,000 μF*V/g, and in some embodiments, from about 2,000 to about 15,000 μF*V/g. However, powders having a relatively high specific charge can also be employed. For example, such high specific charge powders may have a specific charge of from about 20,000 to about 450,000 μF*V/g, in some embodiments from about 30,000 to about 350,000 μF*V/g or more, in some embodiments from about 40,000 to about 300,000 μF*V/g, and in some embodiments, from about 50,000 to about 200,000 μF*V/g.
The powder may be formed using techniques known to those skilled in the art. A precursor tantalum powder, for instance, may be formed by reducing a tantalum salt (e.g., potassium fluotantalate (K2TaF7), sodium fluotantalate (Na2TaF7), tantalum pentachloride (TaCl5), etc.) with a reducing agent (e.g., hydrogen, sodium, potassium, magnesium, calcium, etc.). Such powders may be agglomerated, such as through one or multiple heat treatment steps in an inert or reducing atmosphere. The powder may also be subjected to various other optional techniques as is known in the art, such as milling, deoxidation, leaching, doping, etc.
The powder may also be mixed with a binder and/or lubricant to ensure that the particles adequately adhere to each other when pressed to form the anode body. Suitable binders may include, for instance, poly(vinyl butyral); poly(vinyl acetate); poly(vinyl alcohol); poly(vinyl pyrrolidone); cellulosic polymers, such as carboxymethylcellulose, methyl cellulose, ethyl cellulose, hydroxyethyl cellulose, and methylhydroxyethyl cellulose; atactic polypropylene, polyethylene; polyethylene glycol (e.g., Carbowax from Dow Chemical Co.); polystyrene, poly(butadiene/styrene); polyamides, polyimides, and polyacrylamides, high molecular weight polyethers; copolymers of ethylene oxide and propylene oxide; fluoropolymers, such as polytetrafluoroethylene, polyvinylidene fluoride, and fluoro-olefin copolymers; acrylic polymers, such as sodium polyacrylate, poly(lower alkyl acrylates), poly(lower alkyl methacrylates) and copolymers of lower alkyl acrylates and methacrylates; and fatty acids and waxes, such as stearic and other soapy fatty acids, vegetable wax, microwaxes (purified paraffins), etc. The binder may be dissolved and dispersed in a solvent. Exemplary solvents may include water, alcohols, and so forth. When utilized, the percentage of binders and/or lubricants may vary from about 0.1% to about 8% by weight of the total mass. It should be understood, however, that binders and/or lubricants are not necessarily required in the present invention.
The resulting powder may be compacted to form a pellet using a powder press device. For example, a press mold may be employed that is a single station compaction press containing a die and one or multiple punches. Alternatively, anvil-type compaction press molds may be used that use only a die and single lower punch. Single station compaction press molds are available in several basic types, such as cam, toggle/knuckle and eccentric/crank presses with varying capabilities, such as single action, double action, floating die, movable platen, opposed ram, screw, impact, hot pressing, coining or sizing. The powder may be compacted around an anode lead (e.g., tantalum wire). It should be further appreciated that the anode lead may alternatively be attached (e.g., welded) to the anode body subsequent to pressing and/or sintering of the anode body.
After compaction, any binder/lubricant may be removed using a variety of different techniques. In certain embodiments, for example, the pellet is heated under vacuum pressure at a certain temperature (e.g., from about 150° C. to about 500° C.) for several minutes to drive off the binder/lubricant. The pellet may also be washed with a liquid solution (e.g., aqueous solution) to help assist in the removal of the binder/lubricant, such as described in U.S. Pat. No. 6,197,252 to Bishop, et al., which is incorporated herein in its entirety by reference thereto for all purposes.
Once formed, the anode body may then be sintered. The temperature, atmosphere, and time of the sintering may depend on a variety of factors, such as the type of anode, the size of the anode, etc. Typically, sintering occurs at a temperature of from about from about 800° C. to about 1900° C., in some embodiments from about 1000° C. to about 1500° C., and in some embodiments, from about 1100° C. to about 1400° C., for a time of from about 5 minutes to about 100 minutes, and in some embodiments, from about 30 minutes to about 60 minutes. If desired, sintering may occur in an atmosphere that limits the transfer of oxygen atoms to the anode. For example, sintering may occur in a reducing atmosphere, such as in a vacuum, inert gas, hydrogen, etc. The reducing atmosphere may be at a pressure of from about 10 Torr to about 2000 Torr, in some embodiments from about 100 Torr to about 1000 Torr, and in some embodiments, from about 100 Torr to about 930 Torr. Mixtures of hydrogen and other gases (e.g., argon or nitrogen) may also be employed.
Referring to
In certain embodiments, at least one longitudinally extending channel is recessed into the anode body. Such channels may be formed during pressing as would be known to those skilled in the art. For example, the press mold may contain one or more longitudinal indentations that correspond to the desired shape of the channels. In this manner, the powder is compressed around the indentations so that when removed from the mold, the resulting anode body contains longitudinal channels at those areas where the longitudinal indentations were located in the mold.
The channels may have a relatively high aspect ratio (length divided by width), such as about 2 or more, in some embodiments about 5 or more, in some embodiments from about 10 to about 200, in some embodiments from about 15 to about 150, in some embodiments from about 20 to about 100, and in some embodiments, from about 30 to about 60. Such channels can significantly increase the outer surface area of the anode, which may enhance the degree to which the anode can dissipate heat and increase the likelihood that the anodizing electrolyte will pass into the pores of the anode body during anodic oxidation. Referring again to
At least a portion of the channels 28 may have a relatively high aspect ratio (length divided by width). The length “L1” (
The extent to which the channels are recessed into the anode body may be selectively controlled to achieve a balance between increased surface and integrity of the anode structure. That is, if the depth of the channels is too great, it may be difficult to press the anode into a physically strong structure. Likewise, if the depth is too small, the desired benefits may not be achieved. Thus, in most embodiments, the channels are recessed so that they extend in a direction that is from about 2% to about 60%, in some embodiments from about 5% to about 50%, and in some embodiments, from about 10% to about 45% of the thickness of the anode body in the same direction. Referring again to
Of course, the depth of each of the channels need not be the same. Referring to
Typically, the anode also contains an anode lead wire that helps connect the anode to the terminations of the resulting capacitor. The lead wire may be formed from any electrically conductive material, such as tantalum, niobium, nickel, aluminum, hafnium, titanium, etc., as well as oxides and/or nitrides of thereof. Although not necessarily required, it is often desired that the lead wire extend in the same longitudinal direction as the channels. In the embodiment of
Regardless of whether channels are present, the porous anode body may be anodically oxidized (“anodized”) so that a dielectric layer is formed over and/or within the anode body. For example, a tantalum (Ta) anode body may be anodized to tantalum pentoxide (Ta2O5). Typically, anodization is performed by initially applying a solution to the anode body, such as by dipping anode body into the electrolyte. A solvent is generally employed, such as water (e.g., deionized water). To enhance ionic conductivity, a compound may be employed that is capable of dissociating in the solvent to form ions. Examples of such compounds include, for instance, acids, such as described below with respect to the electrolyte. For example, an acid (e.g., phosphoric acid) may constitute from about 0.01 wt. % to about 5 wt. %, in some embodiments from about 0.05 wt. % to about 0.8 wt. %, and in some embodiments, from about 0.1 wt. % to about 0.5 wt. % of the anodizing solution. If desired, blends of acids may also be employed.
A current is passed through the anodizing solution to form the dielectric layer. The value of the formation voltage manages the thickness of the dielectric layer. For example, the power supply may be initially set up at a galvanostatic mode until the required voltage is reached. Thereafter, the power supply may be switched to a potentiostatic mode to ensure that the desired dielectric thickness is formed over the entire surface of the anode. Of course, other known methods may also be employed, such as pulse or step potentiostatic methods. The voltage at which anodic oxidation occurs typically ranges from about 4 to about 250 V, and in some embodiments, from about 9 to about 200 V, and in some embodiments, from about 20 to about 150 V. During oxidation, the anodizing solution can be kept at an elevated temperature, such as about 30° C. or more, in some embodiments from about 40° C. to about 200° C., and in some embodiments, from about 50° C. to about 100° C. Anodic oxidation can also be done at ambient temperature or lower. The resulting dielectric layer may be formed on a surface of the anode and within its pores.
III. Working Electrolyte
The working electrolyte is a fluid that may be impregnated within the anode, or it may be added to the capacitor at a later stage of production. The fluid electrolyte generally uniformly wets the dielectric. Various suitable electrolytes are described in U.S. Pat. Nos. 5,369,547 and 6,594,140 to Evans, et al. Typically, the electrolyte is ionically conductive in that has an electrical conductivity of from about 0.1 to about 20 Siemens per centimeter (“S/cm”), in some embodiments from about 0.2 to about 10 S/cm, and in some embodiments, from about 0.5 to about 5 S/cm, determined at a temperature of about 23° C. using any known electric conductivity meter (e.g., Oakton Con Series 11). Within the ranges noted above, it is believed that the ionic conductivity of the electrolyte allows the electric field to extend into the electrolyte to a length (Debye length) sufficient to result in significant charge separation. This extends the potential energy of the dielectric to the electrolyte so that the resulting capacitor is able to store even more potential energy than predicted by the thickness of the dielectric. In other words, the capacitor may be charged to a voltage that exceeds the formation voltage of the dielectric. The ratio of the voltage to which the capacitor can be charged to the formation voltage may, for instance, be from about 1.0 to 2.0, in some embodiments from about 1.1 to about 1.8, and in some embodiments, from about 1.2 to about 1.6. As an example, the voltage to which the capacitor is charged may be from about 200 to about 350 V, in some embodiments from about 220 to about 320 V, and in some embodiments, from about 250 to about 300V.
The fluid electrolyte is generally in the form of a liquid, such as a solution (e.g., aqueous or non-aqueous), microemulsion, gel, etc. For example, the electrolyte may be an aqueous solution of an acid (e.g., sulfuric acid, phosphoric acid, or nitric acid), base (e.g., potassium hydroxide), or salt (e.g., ammonium salt, such as a nitrate), as well any other suitable electrolyte known in the art, such as a salt dissolved in an organic solvent (e.g., ammonium salt dissolved in a glycol-based solution). Various other electrolytes are described in U.S. Pat. Nos. 5,369,547 and 6,594,140 to Evans, et al.
The desired ionic conductivity may be achieved by selecting ionic compound(s) (e.g., acids, bases, salts, and so forth) within certain concentration ranges. In one particular embodiment, salts of weak organic acids may be effective in achieving the desired conductivity of the electrolyte. The cation of the salt may include monatomic cations, such as alkali metals (e.g., Li+, Na+, K+, Rb+, or Cs+), alkaline earth metals (e.g., Be2+, Mg2+, Ca2+, Sr2+ or Ba2+), transition metals (e.g., Ag+, Fe2+, Fe3+, etc.), as well as polyatomic cations, such as NH4+. The monovalent ammonium (NH4+), sodium (K+), and lithium (Li+) are particularly suitable cations for use in the present invention. The organic acid used to form the anion of the salt is “weak” in the sense that it typically has a first acid dissociation constant (pKa1) of about 0 to about 11, in some embodiments about 1 to about 10, and in some embodiments, from about 2 to about 10, determined at about 23° C. Any suitable weak organic acids may be used in the present invention, such as carboxylic acids, such as acrylic acid, methacrylic acid, malonic acid, succinic acid, salicylic acid, sulfosalicylic acid, adipic acid, maleic acid, malic acid, oleic acid, gallic acid, tartaric acid (e.g., dextotartaric acid, mesotartaric acid, etc.), citric acid, formic acid, acetic acid, glycolic acid, oxalic acid, propionic acid, phthalic acid, isophthalic acid, glutaric acid, glucosic acid, lactic acid, aspartic acid, glutaminic acid, itaconic acid, trifluoroacetic acid, barbituric acid, cinnamic acid, benzoic acid, 4-hydroxybenzoic acid, aminobenzoic acid, etc.; blends thereof, and so forth. Polyprotic acids (e.g., diprotic, triprotic, etc.) are particularly desirable for use in forming the salt, such as adipic acid (pKa1 of 4.43 and pKa2 of 5.41), α-tartaric acid (pKa1 of 2.98 and pKa2 of 4.34), meso-tartaric acid (pKa1 of 3.22 and pKa2 of 4.82), oxalic acid (pKa1 of 1.23 and pKa2 of 4.19), lactic acid (pKa1 of 3.13, pKa2 of 4.76, and pKa3 of 6.40), etc.
While the actual amounts may vary depending on the particular salt employed, its solubility in the solvent(s) used in the electrolyte, and the presence of other components, such weak organic acid salts are typically present in the electrolyte in an amount of from about 0.1 to about 25 wt. %, in some embodiments from about 0.2 to about 20 wt. %, in some embodiments from about 0.3 to about 15 wt. %, and in some embodiments, from about 0.5 to about 5 wt. %.
The electrolyte is typically aqueous in that it contains an aqueous solvent, such as water (e.g., deionized water). For example, water (e.g., deionized water) may constitute from about 20 wt. % to about 95 wt. %, in some embodiments from about 30 wt. % to about 90 wt. %, and in some embodiments, from about 40 wt. % to about 85 wt. % of the electrolyte. A secondary solvent may also be employed to form a solvent mixture. Suitable secondary solvents may include, for instance, glycols (e.g., ethylene glycol, propylene glycol, butylene glycol, triethylene glycol, hexylene glycol, polyethylene glycols, ethoxydiglycol, dipropyleneglycol, etc.); glycol ethers (e.g., methyl glycol ether, ethyl glycol ether, isopropyl glycol ether, etc.); alcohols (e.g., methanol, ethanol, n-propanol, iso-propanol, and butanol); ketones (e.g., acetone, methyl ethyl ketone, and methyl isobutyl ketone); esters (e.g., ethyl acetate, butyl acetate, diethylene glycol ether acetate, methoxypropyl acetate, ethylene carbonate, propylene carbonate, etc.); amides (e.g., dimethylformamide, dimethylacetamide, dimethylcaprylic/capric fatty acid amide and N-alkylpyrrolidones); sulfoxides or sulfones (e.g., dimethyl sulfoxide (DMSO) and sulfolane); and so forth. Such solvent mixtures typically contain water in an amount from about 40 wt. % to about 80 wt. %, in some embodiments from about 50 wt. % to about 75 wt. %, and in some embodiments, from about 55 wt. % to about 70 wt. % and secondary solvent(s) in an amount from about 20 wt. % to about 60 wt. %, in some embodiments from about 25 wt. % to about 50 wt. %, and in some embodiments, from about 30 wt. % to about 45 wt. %. The secondary solvent(s) may, for example, constitute from about 5 wt. % to about 45 wt. %, in some embodiments from about 10 wt. % to about 40 wt. %, and in some embodiments, from about 15 wt. % to about 35 wt. % of the electrolyte.
If desired, the electrolyte may be relatively neutral and have a pH of from about 4.5 to about 7.0, in some embodiments from about 5.0 to about 6.5, and in some embodiments, from about 5.5 to about 6.0. One or more pH adjusters (e.g., acids, bases, etc.) may be employed to help achieve the desired pH. In one embodiment, an acid is employed to lower the pH to the desired range. Suitable acids include, for instance, organic acids such as described above; inorganic acids, such as hydrochloric acid, nitric acid, sulfuric acid, phosphoric acid, polyphosphoric acid, boric acid, boronic acid, etc.; and mixtures thereof. Although the total concentration of pH adjusters may vary, they are typically present in an amount of from about 0.01 wt. % to about 10 wt. %, in some embodiments from about 0.05 wt. % to about 5 wt. %, and in some embodiments, from about 0.1 wt. % to about 2 wt. % of the electrolyte.
The electrolyte may also contain other components that help improve the electrical performance of the capacitor. For instance, a depolarizer may be employed in the electrolyte to help inhibit the evolution of hydrogen gas at the cathode of the electrolytic capacitor, which could otherwise cause the capacitor to bulge and eventually fail. When employed, the depolarizer normally constitutes from about 1 to about 500 parts per million (“ppm”), in some embodiments from about 10 to about 200 ppm, and in some embodiments, from about 20 to about 150 ppm of the electrolyte. Suitable depolarizers may include nitroaromatic compounds, such as 2-nitrophenol, 3-nitrophenol, 4-nitrophenol, 2-nitrobenzonic acid, 3-nitrobenzonic acid, 4-nitrobenzonic acid, 2-nitroace tophenone, 3-nitroacetophenone, 4-nitroacetophenone, 2-nitroanisole, 3-nitroanisole, 4-nitroanisole, 2-nitrobenzaldehyde, 3-nitrobenzaldehyde, 4-nitrobenzaldehyde, 2-nitrobenzyl alcohol, 3-nitrobenzyl alcohol, 4-nitrobenzyl alcohol, 2-nitrophthalic acid, 3-nitrophthalic acid, 4-nitrophthalic acid, and so forth. Particularly suitable nitroaromatic depolarizers for use in the present invention are nitrobenzoic acids, anhydrides or salts thereof, substituted with one or more alkyl groups (e.g., methyl, ethyl, propyl, butyl, etc). Specific examples of such alkyl-substituted nitrobenzoic compounds include, for instance, 2-methyl-3-nitrobenzoic acid; 2-methyl-6-nitrobenzoic acid; 3-methyl-2-nitrobenzoic acid; 3-methyl-4-nitrobenzoic acid; 3-methyl-6-nitrobenzoic acid; 4-methyl-3-nitro benzoic acid; anhydrides or salts thereof; and so forth.
The particular manner in which the components are incorporated into the capacitor is not critical and may be accomplished using a variety of techniques. Referring to
A seal 23 (e.g., glass-to-metal) may also be employed that connects and seals the anode 20 to the cathode 43. An electrically insulating bushing 89 (e.g., polytetrafluoroethylene (“PTFE”)) and/or support 91 may also be employed to help stabilize the anode 20 and lead 42 and maintain the desired spacing within the capacitor. If desired, a separator (not shown) may also be positioned between the cathode 43 and anode 20 to prevent direct contact between the anode and cathode. Examples of suitable materials for this purpose include, for instance, porous polymer materials (e.g., polypropylene, polyethylene, polycarbonate, etc.), porous inorganic materials (e.g., fiberglass mats, porous glass paper, etc.), ion exchange resin materials, etc. Particular examples include ionic perfluoronated sulfonic acid polymer membranes (e.g., Nafion™ from the E.I. DuPont de Nemeours & Co.), sulphonated fluorocarbon polymer membranes, polybenzimidazole (PBI) membranes, and polyether ether ketone (PEEK) membranes. To optimize the volumetric efficiency of the capacitor, it is generally desired that the separator has a relatively small thickness. For example, the thickness of the separator, when employed, typically ranges from about 5 to about 250 micrometers, in some embodiments from about 10 to about 150 micrometers, and in some embodiments, from about 15 to about 100 micrometers.
The lid or casing may define an internal orifice through which extends a conductive tube 56 that is generally hollow and of a size and shape sufficient to accommodate an anode lead. The conductive tube 56 is typically formed from a metal, such as tantalum, niobium, aluminum, nickel, hafnium, titanium, copper, silver, steel (e.g., stainless), alloys thereof (e.g., electrically conductive oxides), composites thereof (e.g., metal coated with electrically conductive oxide), and so forth. During and/or after assembly and sealing (e.g., welding), the electrolyte may be introduced into the casing through a fill-port. Filling may be accomplished by placing the capacitor in a vacuum chamber so that the fill-port extends into a reservoir of the electrolyte. When the chamber is evacuated, pressure is reduced inside the capacitor. When the vacuum is released, pressure inside the capacitor re-equilibrates, and the electrolyte is drawn through the fill-port into the capacitor.
Regardless of its particular configuration, the capacitor of the present invention may exhibit excellent electrical properties. For example, the capacitor may exhibit a high volumetric efficiency, such as from about 50,000 μF*V/cm3 to about 300,000 μF*V/cm3, in some embodiments from about 60,000 μF*V/cm3 to about 200,000 μF*V/cm3, and in some embodiments, from about 80,000 μF*V/cm3 to about 150,000 μF*V/cm3, determined at a frequency of 120 Hz and at room temperature (e.g., 25° C.). Volumetric efficiency is determined by multiplying the formation voltage of a part by its capacitance, and then dividing by the product by the volume of the part. For example, a formation voltage may be 175 volts for a part having a capacitance of 520 μF, which results in a product of 91,000 μF*V. If the part occupies a volume of about 0.8 cm3, this results in a volumetric efficiency of about 113,750 μF*V/cm3.
The capacitor may also exhibit a high stored energy that enables it suitable for use in high pulse applications. Energy is generally determined according to the equation E=½*CV2, where C is the capacitance in farads (F) and V is the working voltage of capacitor in volts (V). The capacitance may, for instance, be measured using a capacitance meter (e.g., Keithley 3330 Precision LCZ meter with Kelvin Leads, 2 volts bias and 1 volt signal) at operating frequencies of from 10 to 120 Hz (e.g., 120 Hz) and a temperature of about 23° C. For example, the capacitor may exhibit a stored energy of about 2.0 joules per cubic centimeter (J/cm3) or more, in some embodiments about 3.0 J/cm3, in some embodiments from about 3.5 J/cm3 to about 10.0 J/cm3, and in some embodiments, from about 4.0 to about 8.0 J/cm3. The capacitance may likewise be about 1 milliFarad per square centimeter (“mF/cm2”) or more, in some embodiments about 2 mF/cm2 or more, in some embodiments from about 5 to about 50 mF/cm2, and in some embodiments, from about 8 to about 20 mF/cm2. The capacitor may also exhibit a relatively high “breakdown voltage” (voltage at which the capacitor fails), such as about 180 volts or more, in some embodiments about 200 volts or more, and in some embodiments, from about 210 volts to about 260 volts.
The equivalent series resistance (“ESR”)—the extent that the capacitor acts like a resistor when charging and discharging in an electronic circuit—may also be less than about 15,000 milliohms, in some embodiments less than about 10,000 milliohms, in some embodiments less than about 5,000 milliohms, and in some embodiments, from about 1 to about 4,500 milliohms, measured with a 2-volt bias and 1-volt signal at a frequency of 120 Hz. In addition, the leakage current, which generally refers to the current flowing from one conductor to an adjacent conductor through an insulator, can be maintained at relatively low levels. For example, the numerical value of the normalized leakage current of a capacitor of the present invention is, in some embodiments, less than about 1 μA/μF*V, in some embodiments less than about 0.5 μA/μF*V, and in some embodiments, less than about 0.1 μA/μF*V, where μA is microamps and μF*V is the product of the rated capacitance and the rated voltage. Leakage current may be measured using a leakage test meter (e.g., MC 190 Leakage test, Mantracourt Electronics LTD, UK) at a temperature of about 23° C. and at a certain rated voltage after a charging time of from about 60 to about 300 seconds. Such ESR and normalized leakage current values may even be maintained after aging for a substantial amount of time at high temperatures. For example, the values may be maintained for about 100 hours or more, in some embodiments from about 300 hours to about 2500 hours, and in some embodiments, from about 400 hours to about 1500 hours (e.g., 500 hours, 600 hours, 700 hours, 800 hours, 900 hours, 1000 hours, 1100 hours, or 1200 hours) at temperatures ranging from about 100° C. to about 250° C., and, in some embodiments from about 100° C. to about 200° C. (e.g., 100° C., 125° C., 150° C., 175° C., or 200° C.).
The electrolytic capacitor of the present invention may be used in various applications, including but not limited to medical devices, such as implantable defibrillators, pacemakers, cardioverters, neural stimulators, drug administering devices, etc.; automotive applications; military applications, such as RADAR systems; consumer electronics, such as radios, televisions, etc.; and so forth. In one embodiment, for example, the capacitor may be employed in an implantable medical device configured to provide a therapeutic high voltage (e.g., between approximately 500 volts and approximately 850 volts, or, desirably, between approximately 600 Volts and approximately 900 volts) treatment for a patient. The device may contain a container or housing that is hermetically sealed and biologically inert. One or more leads are electrically coupled between the device and the patient's heart via a vein. Cardiac electrodes are provided to sense cardiac activity and/or provide a voltage to the heart. At least a portion of the leads (e.g., an end portion of the leads) may be provided adjacent or in contact with one or more of a ventricle and an atrium of the heart. The device may also contain a capacitor bank that typically contains two or more capacitors connected in series and coupled to a battery that is internal or external to the device and supplies energy to the capacitor bank. Due in part to high conductivity, the capacitor of the present invention can achieve excellent electrical properties and thus be suitable for use in the capacitor bank of the implantable medical device.
The present invention may be better understood by reference to the following examples.
The following materials were employed in the examples.
EDT=3,4-ethylenedioxythiophene (Hereaus);
TSA=p-toluene sulfonic acid, sodium salt; and
POE-10-LE=polyoxyethylene-10-lauryl ether (or decaethylene glycol monodecyl ether).
Equivalent Series Resistance (ESR)
Equivalence series resistance may be measured using a Keithley 3330 Precision LCZ meter with Kelvin Leads 2.2 volt DC bias and a 0.5 volt peak to peak sinusoidal signal. The operating frequency was 120 Hz and the temperature was 23° C.±2° C.
Capacitance
The capacitance was measured using a Keithley 3330 Precision LCZ meter with Kelvin Leads with 2.2 volt DC bias and a 0.5 volt peak to peak sinusoidal signal. The operating frequency was 120 Hz and the temperature was 23° C.±2° C.
Leakage Current:
Leakage current (“DCL”) was measured using a leakage test set that measures leakage current at a temperature of was 23° C.±2° C. and at the rated voltage after a minimum of 60 seconds.
Seven (7) cylindrical tantalum cans were sandblasted with a JetStreem Blaster II (SCM System, Inc.) for about 20 seconds. The samples were then degreased in water in an ultrasonic bath and dried at a temperature of 85° C. for 5 minutes. An amount of 18.78 g of decaethylene glycol monododecyl ether was added to 80 mL of 40° C. deionized water in a 100 mL flask. The mixture was stirred until all solute was dissolved and the solution was allowed to cool to room temperature. An amount of 1.94 g of sodium p-toluenesulfonate was then added and the mixture was stirred again until all solute was completely dissolved. A monomer of 3,4-ethylenedioxythiophene in the amount of 4.26 g was added and the flask was gently agitated to achieve a thermodynamic reaction. Finally, 20 mL of room temperature deionized water was added to form a microemulsion. Each of the aforementioned cans was filled with the microemulsion and placed in a copper receptacle connecting the can to the positive pole of a power supply. A Pt wire was electrically connected to the negative pole of the power supply and inserted into the can and microemulsion. Electro-polymerization was performed for about 30 minutes using a constant current setting of 5 mA to form a structure of poly(3,4-ethylenedioxythiophene. The cans were then rinsed in methanol to remove reaction by-products and dried at 85° C. for 5 minutes,
Pressed and sintered cylindrical Ta anodes of 560 μF/125V rating were impregnated with a 5.0 M aqueous solution of sulfuric acid (specific gravity of 1.26 g/cm3). The capacitors were then assembled via conventional wet Ta capacitor practices. The finished wet capacitors were tested for electrical performance (i.e., leakage current, ESR, and capacitance). The measurements were conducted at was 23° C.±2° C. The results are set forth below.
These and other modifications and variations of the present invention may be practiced by those of ordinary skill in the art, without departing from the spirit and scope of the present invention. In addition, it should be understood that aspects of the various embodiments may be interchanged both in whole or in part. Furthermore, those of ordinary skill in the art will appreciate that the foregoing description is by way of example only, and is not intended to limit the invention so further described in such appended claims.
The present application claims priority to U.S. Provisional Application Ser. No. 61/611,717, filed on Mar. 16, 2012, which is incorporated herein in its entirety by reference thereto.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4864472 | Yoshimura et al. | Sep 1989 | A |
| 4943892 | Tsuchiya et al. | Jul 1990 | A |
| 5019949 | Ikeda et al. | May 1991 | A |
| 5071521 | Kojima et al. | Dec 1991 | A |
| 5117332 | Kudoh et al. | May 1992 | A |
| 5119274 | Kinuta et al. | Jun 1992 | A |
| 5187649 | Kudoh et al. | Feb 1993 | A |
| 5187650 | Kudoh et al. | Feb 1993 | A |
| 5236627 | Hannecart et al. | Aug 1993 | A |
| 5284723 | Hannecart et al. | Feb 1994 | A |
| 5369547 | Evans | Nov 1994 | A |
| 5424907 | Kojima et al. | Jun 1995 | A |
| 5754394 | Evans et al. | May 1998 | A |
| 6088218 | Hamada et al. | Jul 2000 | A |
| 6134099 | Igaki et al. | Oct 2000 | A |
| 6168639 | Taketani et al. | Jan 2001 | B1 |
| 6224639 | Hamada et al. | May 2001 | B1 |
| 6239965 | Shiraishi et al. | May 2001 | B1 |
| 6313979 | Taketani et al. | Nov 2001 | B1 |
| 6324050 | Kobatake et al. | Nov 2001 | B1 |
| 6361572 | Igaki et al. | Mar 2002 | B1 |
| 6409777 | Kobatake et al. | Jun 2002 | B2 |
| 6426866 | Shoji et al. | Jul 2002 | B2 |
| 6462936 | Fujimoto et al. | Oct 2002 | B1 |
| 6594140 | Evans et al. | Jul 2003 | B1 |
| 6614063 | Hayashi et al. | Sep 2003 | B2 |
| 6671168 | Yoshida et al. | Dec 2003 | B2 |
| 6733545 | Shoji et al. | May 2004 | B2 |
| 6842328 | Schott et al. | Jan 2005 | B2 |
| 6853540 | Kudoh et al. | Feb 2005 | B2 |
| 6885547 | Nitta et al. | Apr 2005 | B2 |
| 7002790 | Hossick-Schott et al. | Feb 2006 | B2 |
| 7079377 | Schott et al. | Jul 2006 | B2 |
| 7125764 | Taketani et al. | Oct 2006 | B2 |
| 7157326 | Suda et al. | Jan 2007 | B2 |
| 7180728 | Kobayashi | Feb 2007 | B2 |
| 7224576 | Hossick-Schott | May 2007 | B2 |
| 7248461 | Takagi et al. | Jul 2007 | B2 |
| 7256982 | Lessner et al. | Aug 2007 | B2 |
| 7262954 | Iida et al. | Aug 2007 | B1 |
| 7374585 | Yoshimitsu et al. | May 2008 | B2 |
| 7479166 | Ito | Jan 2009 | B2 |
| 7499260 | Schott et al. | Mar 2009 | B2 |
| 7515396 | Biler | Apr 2009 | B2 |
| 7667954 | Lessner et al. | Feb 2010 | B2 |
| 7687102 | Hossick-Schott et al. | Mar 2010 | B2 |
| 7729103 | Kato et al. | Jun 2010 | B2 |
| 7742281 | Goto et al. | Jun 2010 | B2 |
| 7760490 | Takatani et al. | Jul 2010 | B2 |
| 7785741 | Viavattine | Aug 2010 | B2 |
| 7800887 | Iida et al. | Sep 2010 | B2 |
| 7821772 | Kobayashi et al. | Oct 2010 | B2 |
| 7842104 | Yoshimitsu | Nov 2010 | B2 |
| 7876549 | Umemoto et al. | Jan 2011 | B2 |
| 8027151 | Kikuchi et al. | Sep 2011 | B2 |
| 8035953 | Nemoto et al. | Oct 2011 | B2 |
| 8050014 | Iwasa et al. | Nov 2011 | B2 |
| 8057553 | Iwasa et al. | Nov 2011 | B2 |
| 8083920 | Yoshimitsu | Dec 2011 | B2 |
| 8279585 | Dreissig et al. | Oct 2012 | B2 |
| 8339769 | Schott et al. | Dec 2012 | B2 |
| 8405958 | Takahashi et al. | Mar 2013 | B2 |
| 20090002923 | Kobayashi et al. | Jan 2009 | A1 |
| 20090052119 | Ota et al. | Feb 2009 | A1 |
| 20090086413 | Takatani et al. | Apr 2009 | A1 |
| 20090231782 | Fujita et al. | Sep 2009 | A1 |
| 20090242415 | Yoshimitsu | Oct 2009 | A1 |
| 20100079928 | Harada et al. | Apr 2010 | A1 |
| 20100107386 | Furukawa et al. | May 2010 | A1 |
| 20100127205 | Yoshimitsu | May 2010 | A1 |
| 20100136222 | Furukawa et al. | Jun 2010 | A1 |
| 20100157510 | Miyachi et al. | Jun 2010 | A1 |
| 20100172068 | Yoshimitsu | Jul 2010 | A1 |
| 20100182736 | Miyachi et al. | Jul 2010 | A1 |
| 20100193745 | Harada et al. | Aug 2010 | A1 |
| 20100232090 | Harada et al. | Sep 2010 | A1 |
| 20100254071 | Nishimura | Oct 2010 | A1 |
| 20100271757 | Ishikawa et al. | Oct 2010 | A1 |
| 20100302714 | Kobayaykawa et al. | Dec 2010 | A1 |
| 20110031441 | Hsu et al. | Feb 2011 | A1 |
| 20110051319 | Ishikawa et al. | Mar 2011 | A1 |
| 20110051321 | Yamaguchi et al. | Mar 2011 | A1 |
| 20110122545 | Yoshimitsu | May 2011 | A1 |
| 20110188173 | Ota et al. | Aug 2011 | A1 |
| 20110205690 | Komatsu et al. | Aug 2011 | A1 |
| 20110211295 | Ueda et al. | Sep 2011 | A1 |
| 20110232056 | Hayashi et al. | Sep 2011 | A1 |
| 20110233450 | Nobuta et al. | Sep 2011 | A1 |
| 20130242465 | Weaver et al. | Sep 2013 | A1 |
| 20130242468 | Pinwill et al. | Sep 2013 | A1 |
| Number | Date | Country |
|---|---|---|
| 2 327 743 | Jun 2011 | EP |
| Entry |
|---|
| Article—Rudge et al., “Conducting Polymers as Active Materials in Electrochemical Capacitors,” Journal of Power Sources, vol. 47, 1994, pp. 89-107 (38 pages). |
| Paper—Aldissi et al., “Conducting Polymers in Ultracapacitor Applications,” Presented at Conference Proceedings at ANTEC '98, Atlanta, Georgia, Apr. 26-Apr. 30, 1998, 6 pages. |
| Paper—Evans, David A., “High Energy Density Electrolytic-Electrochemical Hybrid Capacitor,” Presented at 14th Capacitor and Resistor Technology Symposium , Mar. 22, 1994, and in CARTS' 1994 Proceedings. |
| Search Report for GB1304127.2 dated Aug. 6, 2013, 3 pages. |
| Biler et al., U.S. Appl. No. 13/783,634, filed Mar. 4, 2013, Wet Capacitor Cathode Containing a Conductive Copolymer. |
| Weaver et al., U.S. Appl. No. 13/783,656, filed Mar. 4, 2013, Wet Capacitor Cathode Containing a Conductive Coating Formed Anodic Electrochemical Polymerization of a Colloidal Suspension. |
| Martin Biler, U.S. Appl. No. 13/783,755, filed Mar. 4, 2013, Wet Capacitor Cathode Containing an Akyl-Substituted Poly(3,4-Ethylenedioxythiophene). |
| Article—Tsakova et al., “Anodic polymerization of 3,4-ethylenedioxythiophene from aqueous microemulsions,” Electrochimica Acta, vol. 46, Issue 5, 2000, pp. 759-768. |
| Article—Wang et al., “Electrochemical supercapacitor electrode material based on poly(3,4-ethylenedioxythiophene)/polypyrrole composite,” Journal of Power Sources, vol. 163, Issue 2, 2007, pp. 1120-1125. |
| Abstract of Presentation—Midler, “Microemulsions as drug delivery systems,” Mar. 3, 2003, 2 pages, http://www.vetcontact.com/. |
| Article—Harrison, “Microemulsion technology for surfactants,” Speciality Chemicals Magazine, Nov. 2004, pp. 32-36, www.specchemonline.com. |
| Book—Behler et al., Reactions and Synthesis in Surfactant Systems, Chapter 1: Industrial Surfactant Syntheses, 2001, 44 pages. |
| Article—Wang, “Research progress on a novel conductive polymer—poly(3,4-ethylenedioxythiophene) (PEDOT),” Journal of Physics: Conference Series, vol. 152, Issue 1, 2009, pp. 012023. |
| Abstract of Article—Choi et al., “Poly(3,4-ethylenedioxythiophene) nanoparticles prepared in aqueous DBSA solutions,” Synthetic Metals, vol. 141, Issue 3, 2004, pp. 293-299. |
| Article—Naoi et al., “Simultaneous electrochemical formulation of Al2O3/polypyrrole layers (I): effect of electrolyte anion in formation process,” Electrochimica Acta, vol. 45, Issue 20, 2000, pp. 3413-3421. |
| Article—Naoi et al., “Simultaneous Formation of Separate Conducting and Insulating Layers on Aluminum Electrode by Electrolysis,” Electrochemical and Solid-State Letters, vol. 1, Issue 1, 1998, pp. 34-36. |
| Abstract of Presentation—Winkels et al., “Electropolymerization of Thiophene Derivatives and Composite Materials from Microemulsions,” 2001 Joint International Meeting—the 200th Meeting of The Electrochemical Society, Inc. and the 52nd Annual Meeting of the International Society of Electrochemistry—San Francisco, California, 2001, 1 page. |
| Related Application Form. |
| Number | Date | Country | |
|---|---|---|---|
| 20130242466 A1 | Sep 2013 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61611717 | Mar 2012 | US |