Patent Grant
9216406
The present invention relates to the field of catalysts. More specifically, the present invention relates to a method of producing a catalyst.
Wet chemistry can be used to put small platinum particles on a ceramic surface in order to create a catalyst. However, when the catalyst is heated up and used, the platinum particles are not sufficiently bonded to the ceramic surface. As a result, they are mobile, allowing them to move around and find other platinum particles. Upon the platinum particles' discovery of each other, they agglomerate into bigger platinum particles.
For example, even if prior art processes start with ½ nanometer platinum particles, by the time the aging test has been performed (equivalent to 10 years on a car), the platinum particles have agglomerated to become 16 nanometer particles.
This agglomeration of platinum particles results in a massive reduction in catalytic surface area. As a result, the performance of the catalyst significantly decreases.
The present invention employs a pinning agent to securely bond catalytic material to a core nano-particle. The pinning agent securely anchors the catalytic material to the core nano-particle, thereby minimizing or eliminating the mobility and agglomeration of the catalytic material. As a result, the present invention is able to provide a minimally-aging or even a non-aging catalyst that substantially maintains the extremely small size of the catalytic particles on each core nano-particle, thereby maximizing the catalytic surface area.
In one aspect of the present invention, a nano-particle is comprises an interior region and an exterior surface. The interior region comprises a mixed-metal oxide, wherein the mixed-metal oxide comprises aluminum oxide and palladium. The exterior surface comprises pure metallic palladium.
In some embodiments, the palladium in the interior region extends to and is bonded with the pure metallic palladium at the exterior surface. In some embodiments, the nano particle comprises a diameter of approximately 10 nanometers or less.
In some embodiments, the mixed-metal oxide forms a center core of the nano-particle. In some embodiments, the mixed-metal oxide consists only of aluminum oxide and palladium.
In some embodiments, the mixed-metal oxide forms a monolayer that surrounds a center core of the nano-particle. In some embodiments, the center core comprises silica.
In another aspect of the present invention, a method of forming nano-particles comprises: loading a quantity of aluminum oxide material and a quantity of palladium material into a plasma gun in a desired ratio; vaporizing the quantity of aluminum oxide material and the quantity of palladium material using the plasma gun, thereby forming a vapor cloud comprising vaporized aluminum oxide and vaporized palladium; and quenching the vapor cloud, thereby condensing the vaporized aluminum oxide and the vaporized palladium into nano-particles. Each nano-particle comprises an interior region and an exterior surface. The interior region comprises a mixed-metal oxide that includes aluminum oxide and palladium, and the exterior surface comprises pure metallic palladium.
In some embodiments, the step of vaporizing the quantity of aluminum oxide material and the quantity of palladium material comprises: flowing a working gas into a reactor of the plasma gun; delivering energy to the working gas, thereby forming a plasma stream; and flowing the quantity of aluminum oxide material and the quantity of palladium material into the plasma stream.
In some embodiments, the palladium in the interior region extends to and is bonded with the pure metallic palladium at the exterior surface. In some embodiments, the nano-particles have an average grain size of approximately 10 nanometers or less.
In some embodiments, the mixed-metal oxide forms a center core of the nano-particle. In some embodiments, the mixed-metal oxide consists only of aluminum oxide and palladium.
In yet another aspect of the present invention, a method of forming nano-particles comprises: providing a quantity of aluminum material and a quantity of palladium material in a desired ratio; and forming a plurality of nano-particles from the quantity of aluminum material and the quantity of palladium material using a wet chemistry process. Each formed nano-particle comprises an interior region and an exterior surface. The interior region comprises a mixed-metal oxide that includes aluminum oxide and palladium, and the exterior surface comprises pure metallic palladium.
In some embodiments, the aluminum material is a salt or an organic compound, the palladium material is a salt, and the wet chemistry process comprises forming the mixed-metal oxide from the aluminum material and the palladium material via a chemical reaction. In some embodiments, the mixed-metal oxide forms a center core of each nano-particle, and the mixed-metal oxide consists only of aluminum oxide and palladium.
In some embodiments, the step of forming the plurality of nano-particles using a wet chemistry process comprises forming a monolayer around a center core of each nano-particle, the monolayer comprising the mixed-metal oxide. In some embodiments, the center core of each nano-particle comprises silica.
In some embodiments, the palladium in the interior region extends to and is bonded with the pure metallic palladium at the exterior surface. In some embodiments, the nano-particles have an average grain size of approximately 10 nanometers or less.
In yet another aspect of the present invention, a catalytic carrier nano-particle comprises a carrier nano-particle comprising an interior region and an exterior surface. The interior region comprises a mixed-metal oxide that includes aluminum oxide and palladium, and the exterior surface comprises pure metallic palladium. A catalytic nano-particle is bonded to the pure metallic palladium at the exterior surface. The catalytic nano-particle is platinum.
In some embodiments, the palladium in the interior region extends to and is bonded with the pure metallic palladium at the exterior surface. In some embodiments, the carrier nano-particle comprises a diameter of approximately 10 nanometers or less.
In some embodiments, the mixed-metal oxide forms a center core of the carrier nano-particle. In some embodiments, the mixed-metal oxide consists only of aluminum oxide and palladium.
In some embodiments, the mixed-metal oxide forms a monolayer that surrounds a center core of the carrier nano-particle. The nano-particle of claim 26, wherein the center core comprises silica.
In yet another aspect of the present invention, a method of forming nano-particles comprises: loading a quantity of aluminum oxide material, a quantity of palladium material, and a quantity of platinum material into a plasma gun in a desired ratio; vaporizing the quantity of aluminum oxide material, the quantity of palladium material, and the quantity of platinum material using the plasma gun, thereby forming a vapor cloud comprising vaporized aluminum oxide, vaporized palladium, and vaporized platinum; and quenching the vapor cloud, thereby condensing the vaporized aluminum oxide, the vaporized palladium, and the vaporized platinum into carrier nano-particles. Each carrier nano-particle comprises an interior region and an exterior surface. The interior region comprises a mixed-metal oxide that includes aluminum oxide and palladium, the exterior surface comprises a pure metallic palladium, and a platinum nano-particle is bonded to the pure metallic palladium at the exterior surface.
In some embodiments, the step of vaporizing the quantity of aluminum oxide material, the quantity of palladium material, and the quantity of platinum material comprises: flowing a working gas into a reactor of the plasma gun; delivering energy to the working gas, thereby forming a plasma stream; and flowing the quantity of aluminum oxide material, the quantity of palladium material, and the quantity of platinum material into the plasma stream.
In some embodiments, the palladium in the interior region extends to and is bonded with the pure metallic palladium at the exterior surface. In some embodiments, the carrier nano-particles have an average grain size of approximately 10 nanometers or less.
In some embodiments, the mixed-metal oxide forms a center core of the carrier nano-particle. In some embodiments, the mixed-metal oxide consists only of aluminum oxide and palladium.
In yet another aspect of the present invention, a method of forming nano-particles comprises: providing a quantity of aluminum material, a quantity of palladium material, and a quantity of platinum material in a desired ratio; and forming a plurality of carrier nano-particles from the quantity of aluminum material, the quantity of palladium material, and the quantity of platinum material using a wet chemistry process. Each carrier nano-particle comprises an interior region and an exterior surface. The interior region comprises a mixed-metal oxide that includes aluminum oxide and palladium, the exterior surface comprises a pure metallic palladium, and a platinum nano-particle is bonded to the pure metallic palladium at the exterior surface.
In some embodiments, the aluminum material is a salt or an organic compound, the palladium material is a salt, and the wet chemistry process comprises forming the mixed-metal oxide from the aluminum material and the palladium material via a chemical reaction, and forming a carrier particle suspension comprising a plurality of aluminum-palladium carrier particles. Each aluminum-palladium carrier particle comprises an interior region and an exterior surface. The interior region comprises the mixed-metal oxide that includes aluminum oxide and palladium, and the exterior surface comprises pure metallic palladium. In some embodiments, the wet chemistry process further comprises mixing a platinum solution with the carrier particle suspension, and bonding platinum nano-particles formed from the platinum solution to the pure metallic palladium on the aluminum-palladium carrier particles. In some embodiments, the platinum solution is a platinum nitrate solution or a platinum chloride solution.
In some embodiments, the aluminum material is a salt or an organic compound, the palladium material is a salt, and the wet chemistry process comprises forming the mixed-metal oxide from the aluminum material and the palladium material via a chemical reaction, forming a monolayer of the mixed-metal oxide around a center core of each carrier nano-particle, and forming a suspension of the carrier nano-particles. The center core comprises a different chemical composition from the monolayer, and each monolayer comprises an interior region and an exterior surface. The interior region comprises the mixed-metal oxide that includes aluminum oxide and palladium, and the exterior surface comprises pure metallic palladium. In some embodiments, the wet chemistry process further comprises mixing a platinum solution with the suspension of nano-particles, and bonding platinum nano-particles formed from the platinum solution to the pure metallic palladium on the carrier nano-particles. In some embodiments, the platinum solution is a platinum nitrate solution or a platinum chloride solution. In some embodiments, the center core of each carrier nano-particle comprises silica.
In some embodiments, the palladium in the interior region extends to and is bonded with the pure metallic palladium-platinum alloy at the exterior surface. In some embodiments, the carrier nano-particles have an average grain size of approximately 10 nanometers or less.
In yet another aspect of the present invention, a method of forming nano-particles comprises: forming a plurality of aluminum-palladium carrier particles using a plasma gun, wherein each aluminum-palladium carrier particle comprises an interior region and an exterior surface, the interior region comprising a mixed-metal oxide that includes aluminum oxide and palladium, and the exterior surface comprising pure metallic palladium; and affixing a platinum nano-particle to the pure metallic palladium on each of the aluminum-palladium carrier particles using a wet chemistry process.
In some embodiments, forming the plurality of aluminum-palladium carrier particles using the plasma gun comprises: loading a quantity of aluminum oxide material and a quantity of palladium material into the plasma gun in a desired ratio; vaporizing the quantity of aluminum oxide material and the quantity of palladium material using the plasma gun, thereby forming a vapor cloud comprising vaporized aluminum oxide and vaporized palladium; and quenching the vapor cloud, thereby condensing the vaporized aluminum oxide and the vaporized palladium into carrier nano-particles. Each carrier nano-particle comprises an interior region and an exterior surface. The interior region comprises a mixed-metal oxide that includes aluminum oxide and palladium, and the exterior surface comprises pure metallic palladium.
In some embodiments, the step of vaporizing the quantity of aluminum oxide material and the quantity of palladium material comprises flowing a working gas into a reactor of the plasma gun, delivering energy to the working gas, thereby forming a plasma stream, and flowing the quantity of aluminum oxide material and the quantity of palladium material into the plasma stream. In some embodiments, the palladium in the interior region extends to and is bonded with the pure metallic palladium at the exterior surface. In some embodiments, the aluminum-palladium carrier particles have an average grain size of approximately 10 nanometers or less.
In some embodiments, the mixed-metal oxide forms a center core of each aluminum-palladium carrier particle. In some embodiments, the mixed-metal oxide consists only of aluminum oxide and palladium.
In some embodiments, the wet chemistry process comprises mixing a platinum solution with the aluminum-palladium carrier particles, and bonding platinum nano-particles formed from the platinum solution to the pure metallic palladium on the aluminum-palladium carrier particles. In some embodiments, the platinum solution is a platinum nitrate solution or a platinum chloride solution.
In some embodiments, the palladium in the interior region extends to and is bonded with the pure metallic palladium at the exterior surface. In some embodiments, the aluminum-palladium carrier particles have an average grain size of approximately 10 nanometers or less.
In yet another aspect of the present invention, a catalyst comprises a support structure, and a plurality of carrier nano-particles bonded to the support structure. Each carrier nano-particle comprises an interior region and an exterior surface. The interior region comprises a mixed-metal oxide, and the exterior surface comprises a pure metal. A catalytic particle is bonded with the pure metal at the exterior surface.
In some embodiments, the support structure is a porous ceramic material, and the plurality of carrier nano-particles are disposed within the pores of the ceramic material. In some embodiments, the mixed-metal oxide comprises aluminum oxide and palladium. In some embodiments, the pure metal is palladium. In some embodiments, the mixed-metal oxide in the interior region extends to and is bonded with the pure metal at the exterior surface. In some embodiments, the carrier nano-particles have an average grain size of approximately 10 nanometers or less.
In some embodiments, the mixed-metal oxide forms a center core of each carrier nano-particle. In some embodiments, the mixed-metal oxide consists only of aluminum oxide and palladium.
In some embodiments, the mixed-metal oxide forms a monolayer that surrounds a center core of each carrier nano-particle. In some embodiments, the center core comprises silica.
In some embodiments, the exterior surface comprises a pure metal alloy. In some embodiments, the catalytic particle is platinum. In some embodiments, the catalyst is a non-aging catalyst.
In yet another aspect of the present invention, a method of forming a catalyst comprises: providing a support structure; providing a plurality of carrier nano-particles, wherein each carrier nano-particle comprises an interior region and an exterior surface, the interior region comprising a mixed-metal oxide, and the exterior surface comprising a pure metal, wherein a catalytic particle is bonded with the pure metal at the exterior surface; and bonding the plurality of carrier nano-particles to the support structure.
In some embodiments, the support structure is a porous ceramic material, and the plurality of carrier nano-particles are disposed within the pores of the ceramic material. In some embodiments, the mixed-metal oxide includes aluminum oxide and palladium, and the pure metal comprises pure metallic palladium. In some embodiments, the catalytic particle is platinum. In some embodiments, the palladium in the interior region extends to and is bonded with the pure metallic palladium at the exterior surface. In some embodiments, the carrier nano-particles have an average grain size of approximately 10 nanometers or less.
In some embodiments, the mixed-metal oxide forms a center core of the carrier nano-particle. In some embodiments, the mixed-metal oxide consists only of aluminum oxide and palladium.
In some embodiments, the step of providing a plurality of carrier nano-particles comprises: loading a quantity of a first material, a quantity of a second material, and a quantity of a third material into a plasma gun in a desired ratio; vaporizing the quantity of the first material, the quantity of the second material, and the quantity of the third material using the plasma gun, thereby forming a vapor cloud comprising vaporized first material, vaporized second material, and vaporized third material; and quenching the vapor cloud, thereby condensing the vaporized first material, the vaporized second material, and the vaporized third material into carrier nano-particles. Each carrier nano-particle comprises the interior region and the exterior surface. In some embodiments, the step of vaporizing the quantity of the first material, the quantity of the second material, and the quantity of the third material comprises flowing a working gas into a reactor of the plasma gun, delivering energy to the working gas, thereby forming a plasma stream, and flowing the quantity of the first material, the quantity of the second material, and the quantity of the third material into the plasma stream.
In some embodiments, the step of providing a plurality of carrier nano-particles comprises: providing a quantity of a first material, a quantity of a second material, and a quantity of third material in a desired ratio; and forming the plurality of carrier nano-particles from the quantity of the first material, the quantity of the second material, and the quantity of the third material using a wet chemistry process. In some embodiments, the mixed-metal oxide comprises the first material and the second material, the exterior surface comprises the second material, and the catalytic particle comprises the third material. In some embodiments, the wet chemistry process comprises forming the mixed-metal oxide from the first material and the second material via a chemical reaction, and forming a carrier particle suspension comprising a plurality of carrier particles. Each carrier particle comprises the interior region and the exterior surface, the mixed-metal oxide of the interior region comprising the first material and the second material, and the pure metal at the exterior surface comprising the second material.
In some embodiments, the first material is an aluminum material, and the second material is a palladium material. In some embodiments, the aluminum material is a salt or an organic compound, and the palladium material is a salt.
In some embodiments, the wet chemistry process further comprises mixing a catalytic solution with the carrier particle suspension, and bonding catalytic nano-particles formed from the catalytic solution to the pure metal on the carrier particles. In some embodiments, the catalytic solution is a platinum solution and the catalytic nano-particles are platinum nano-particles. In some embodiments, the platinum solution is a platinum nitrate solution or a platinum chloride solution.
In some embodiments, forming the mixed-metal oxide comprises forming a monolayer around a center core of each carrier particle. The center core comprises a different chemical composition from the monolayer, and each monolayer comprises the interior region and the exterior surface. In some embodiments, the mixed-metal oxide includes aluminum oxide and palladium, and the pure metal at the exterior surface comprises palladium. In some embodiments, the wet chemistry process further comprises mixing a catalytic solution with the carrier particle suspension, and bonding catalytic nano-particles formed from the catalytic solution to the pure metal on the carrier particles. In some embodiments, the catalytic solution is a platinum solution and the catalytic nano-particles are platinum nano-particles. In some embodiments, the platinum solution is a platinum nitrate solution or a platinum chloride solution. In some embodiments, the center core of each carrier nano-particle comprises silica.
In some embodiments, the step of providing the plurality of carrier nano-particles comprises: forming a plurality of carrier particles using a plasma gun, wherein each carrier particle comprises the interior region and the exterior surface; and affixing a catalytic nano-particle to the pure metal on each of the carrier particles using a wet chemistry process. In some embodiments, the step of forming the plurality of carrier particles using the plasma gun comprises: loading a quantity of a first material and a quantity of a second material into the plasma gun in a desired ratio; vaporizing the quantity of the first material and the quantity of the second material using the plasma gun, thereby forming a vapor cloud comprising vaporized first material and vaporized second material; and quenching the vapor cloud, thereby condensing the vaporized first material and the vaporized second material into the carrier particles. In some embodiments, the step of vaporizing the quantity of first material and the quantity of second material comprises: flowing a working gas into a reactor of the plasma gun; delivering energy to the working gas, thereby forming a plasma stream; and flowing the quantity of first material and the quantity of second material into the plasma stream. In some embodiments, the step of affixing a catalytic nano-particle to the pure metal using a wet chemistry process comprises mixing a catalytic solution with the core particles, and bonding catalytic nano-particles formed from the catalytic solution to the pure metal on the carrier particles. In some embodiments, the catalytic solution is a platinum solution and the catalytic nano-particles are platinum nano-particles. In some embodiments, the platinum solution is a platinum nitrate solution or a platinum chloride solution. In some embodiments, bonding the plurality of carrier nano-particles to the support structure comprises performing a calcining process.
In yet another aspect of the present invention, a nano-particle comprises an interior region comprising a mixed-metal oxide, and an exterior surface comprising a pure metal.
In some embodiments, the mixed-metal oxide comprises aluminum oxide and palladium. In some embodiments, the pure metal is palladium. In some embodiments, the mixed-metal oxide in the interior region extends to and is bonded with the pure metal at the exterior surface. In some embodiments, the nano-particle comprises a diameter of approximately 10 nanometers or less.
In some embodiments, the mixed-metal oxide forms a center core of the nano-particle. In some embodiments, the mixed-metal oxide consists only of aluminum oxide and palladium.
In some embodiments, the mixed-metal oxide forms a monolayer that surrounds a center core of the nano-particle. In some embodiments, the center core comprises silica. In some embodiments, the exterior surface comprises a pure metal alloy. In some embodiments, the pure metal alloy is a palladium-platinum alloy.
In yet another aspect of the present invention, a method of forming nano-particles comprises providing a quantity of a first material and a quantity of a second material, and forming a plurality of nano-particles from the quantity of the first material and the quantity of the second material. Each nano-particle comprises an interior region and an exterior surface. The interior region comprises a mixed-metal oxide, and the exterior surface comprises a pure metal.
In some embodiments, the mixed-metal oxide comprises the first material and the second material, and the pure metal comprises the second material. In some embodiments, the mixed-metal oxide comprises aluminum oxide and palladium, and the pure metal comprises palladium. In some embodiments, the mixed-metal oxide comprises aluminum oxide and palladium, and the pure metal comprises a palladium-platinum alloy.
In some embodiments, the step of forming the plurality of nano-particles comprises: loading the quantity of the first material and the quantity of the second material into a plasma gun in a desired ratio; vaporizing the quantity of the first material and the quantity of the second material using the plasma gun, thereby forming a vapor cloud comprising vaporized first material and vaporized second material; and quenching the vapor cloud, thereby condensing the vaporized first material and the vaporized second material into nano-particles, wherein each nano-particle comprises the interior region and the exterior surface. In some embodiments, the step of vaporizing the quantity of the first material and the quantity of the second material comprises: flowing a working gas into a reactor of the plasma gun; delivering energy to the working gas, thereby forming a plasma stream; and flowing the quantity of the first material and the quantity of the second material into the plasma stream. In some embodiments, the mixed-metal oxide comprises the first material and the second material, and the pure metal comprises the second material. In some embodiments, the first material is an aluminum material and the second material is a palladium material.
In some embodiments, the step of forming the plurality of nano-particles comprises performing a wet chemistry process with the quantity of first material and the quantity of second material. In some embodiments, the wet chemistry process comprises forming the mixed-metal oxide from the first material and the second material via a chemical reaction. In some embodiments, the first material comprises an aluminum material, and the second material comprises a palladium material. In some embodiments, the aluminum material is a salt or an organic compound, and the palladium material is a salt. In some embodiments, the mixed-metal oxide forms a center core of each nano-particle, and the mixed-metal oxide consists only of aluminum oxide and palladium. In some embodiments, the wet chemistry process comprises forming a monolayer around a center core of each nano-particle. The monolayer comprises the mixed-metal oxide. In some embodiments, the center core of each nano-particle comprises silica.
In some embodiments, the mixed-metal oxide in the interior region extends to and is bonded with the pure metal at the exterior surface. In some embodiments, the nano-particles have an average grain size of approximately 10 nanometers or less.
In yet another aspect of the present invention, a nano-particle comprises an interior region comprising a mixed-metal oxide, an exterior surface comprising a pure metal, and a catalytic particle affixed to the pure metal. The catalytic particle has a chemical composition different from the pure metal and the mixed-metal oxide.
In some embodiments, the mixed-metal oxide comprises a first material and a second material, the pure metal comprises the second material, and the catalytic particle comprises a third material. In some embodiments, the mixed-metal oxide forms a monolayer that surrounds a center core of the nano-particle. In some embodiments, the center core comprises silica.
In some embodiments, the mixed-metal oxide comprises aluminum-oxide and a metallic pinning agent that does not comprise platinum, the pure metal comprises the metallic pinning agent, and the catalytic particle comprises platinum. In some embodiments, the metallic pinning agent comprises copper, molybdenum, or cobalt. In some embodiments, the catalytic particle comprises a metal alloy. In some embodiments, the metal alloy is a palladium-platinum alloy. In some embodiments, the metallic pinning agent comprises copper, molybdenum, or cobalt, and the catalytic particle comprises a palladium-platinum alloy.
In some embodiments, the mixed-metal oxide in the interior region extends to and is bonded with the pure metal at the exterior surface. In some embodiments, the nano particle comprises a diameter of approximately 10 nanometers or less.
In some embodiments, the catalytic particle is a nano-particle. In some embodiments, the catalytic particle comprises a diameter of approximately 1 nanometer or less. In some embodiments, the catalytic particle comprises a diameter of approximately ½ nanometer.
In yet another aspect of the present invention, a method of forming a nano-particle comprising: providing a carrier nano-particle, wherein the carrier nano-particle comprises an interior region and an exterior surface, the interior region comprising a mixed-metal oxide, and the exterior surface comprising a pure metal; and affixing a catalytic particle to the pure metal, wherein the catalytic particle has a chemical composition different from the pure metal and the mixed-metal oxide.
In some embodiments, the mixed-metal oxide is formed from a first material and a second material, the pure metal is formed from the second material, and the catalytic particle is formed from a third material. In some embodiments, the mixed-metal oxide forms a monolayer that surrounds a center core of the carrier nano-particle. In some embodiments, the center core comprises silica.
In some embodiments, the mixed-metal oxide comprises aluminum-oxide and a metallic pinning agent that does not comprise platinum, the pure metal comprises the metallic pinning agent, and the catalytic particle comprises platinum. In some embodiments, the metallic pinning agent comprises copper, molybdenum, or cobalt. In some embodiments, the catalytic particle comprises a metal alloy. In some embodiments, the metal alloy is a palladium-platinum alloy. In some embodiments, the metallic pinning agent comprises copper, molybdenum, or cobalt, and the catalytic particle comprises a palladium-platinum alloy.
In some embodiments, the mixed-metal oxide in the interior region extends to and is bonded with the pure metal at the exterior surface. In some embodiments, the carrier nano-particle comprises a diameter of approximately 10 nanometers or less.
In some embodiments, the catalytic particle is a nano-particle. In some embodiments, the catalytic particle comprises a diameter of approximately 1 nanometer or less. In some embodiments, the catalytic particle comprises a diameter of approximately ½ nanometer.
In some embodiments, the steps of providing the carrier nano-particle and affixing the catalytic particle to the pure metal are performed using a plasma gun. In some embodiments, the steps of providing the carrier nano-particle and affixing the catalytic particle to the pure metal are performed using a wet chemistry process.
In some embodiments, providing the carrier nano-particle comprises loading a quantity of a first material and a quantity of a second material into a plasma gun in a desired ratio, vaporizing the quantity of the first material and the quantity of the second material, thereby forming a vapor cloud comprising vaporized first material and vaporized second material, and quenching the vapor cloud, thereby condensing the vaporized first material and the vaporized second material into the carrier nano-particle. The carrier nano-particle comprises the interior region and the exterior surface. In some embodiments, the step of vaporizing the quantity of the first material and the quantity of the second material comprises flowing a working gas into a reactor of the plasma gun, delivering energy to the working gas, thereby forming a plasma stream, and flowing the quantity of the first material and the quantity of the second material into the plasma stream. In some embodiments, the step of affixing the catalytic particle to the pure metal is performed using a wet chemistry process. In some embodiments, the wet chemistry process comprises mixing a catalytic solution with the carrier nano-particle, and bonding a catalytic particle formed from the catalytic solution to the pure metal on the carrier nano-particle. In some embodiments, the catalytic solution is a platinum solution and the catalytic particle is a platinum nano-particle. In some embodiments, the platinum solution is a platinum nitrate solution or a platinum chloride solution.
In yet another aspect of the present invention, a method of forming catalytic nano-particles comprises: providing a plurality of carrier nano-particles, wherein each carrier nano-particle comprises an interior region and an exterior surface, the interior region comprising a mixed-metal oxide, and the exterior surface comprising a pure metal; and affixing a catalytic nano-particle to the pure metal on each carrier nano-particle.
In some embodiments, the step of affixing the catalytic nano-particle to the pure metal is performed using a plasma gun. In some embodiments, the step of affixing the catalytic nano-particle to the pure metal comprises: loading the plurality of nano-particles and a quantity of catalytic material into a plasma gun in a desired ratio, vaporizing the quantity of catalytic material, thereby forming a vapor cloud comprising vaporized catalytic material, and quenching the vapor cloud, thereby condensing the vaporized catalytic material into catalytic nano-particles that are bonded to the pure metal on the carrier nano-particles.
In some embodiments, the plurality of carrier nano-particles has an average grain size of approximately 10 nanometers or less. In some embodiments, each catalytic nano particle comprises a diameter of approximately 1 nanometer or less. In some embodiments, each catalytic nano-particle comprises a diameter of approximately ½ nanometer.
In some embodiments, the step of affixing the catalytic nano-particle to the pure metal is performed using a wet chemistry process. In some embodiments, the step of affixing a catalytic nano-particle to the pure metal using a wet chemistry process comprises mixing a catalytic solution with the plurality of carrier nano-particles, and bonding catalytic nano-particles formed from the catalytic solution to the pure metal on the plurality of carrier nano-particles. In some embodiments, the catalytic solution is a platinum solution and the catalytic nano-particles are platinum nano-particles. In some embodiments, the platinum solution is a platinum nitrate solution or a platinum chloride solution.
The following description is presented to enable one of ordinary skill in the art to make and use the invention and is provided in the context of a patent application and its requirements. Various modifications to the described embodiments will be readily apparent to those skilled in the art and the generic principles herein may be applied to other embodiments. Thus, the present invention is not intended to be limited to the embodiment shown but is to be accorded the widest scope consistent with the principles and features described herein.
This disclosure provides several embodiments of the present invention. It is contemplated that any features from any embodiment can be combined with any features from any other embodiment. In this fashion, hybrid configurations of the illustrated and describer embodiments are well within the scope of the present invention.
This disclosure refers to both particles and powders. These two terms are equivalent, except for the caveat that a singular “powder” refers to a collection of particles. The present invention may apply to a wide variety of powders and particles. Powders that fall within the scope of the present invention may include, but are not limited to, any of the following: (a) nano-structured powders (nano-powders), having an average grain size less than 250 nanometers and an aspect ratio between one and one million; (b) submicron powders, having an average grain size less than 1 micron and an aspect ratio between one and one million; (c) ultra-fine powders, having an average grain size less than 100 microns and an aspect ratio between one and one million; and (d) fine powders, having an average grain size less than 500 microns and an aspect ratio between one and one million.
Various aspects of the disclosure may be described through the use of flowcharts. Often, a single instance of an aspect of the present disclosure may be shown. As is appreciated by those of ordinary skill in the art, however, the protocols, processes, and procedures described herein may be repeated continuously or as often as necessary to satisfy the needs described herein. Additionally, it is contemplated that certain method steps of the invention can be performed in alternative sequences to those disclosed in the flowcharts. Accordingly, the scope of the claims should not be limited to any specific order of method steps unless the order is explicitly required by the language of the claims.
The interior region is the region between the center of the carrier particle and the exterior surface 115. This interior region comprises a mixed-metal oxide 110. In some embodiments, the mixed-metal oxide 110 comprises aluminum oxide along with an accompanying metal. In some embodiments, this accompanying metal is palladium. Other accompanying metals that have been found to be suitable are copper, molybdenum, and cobalt. It is contemplated that other oxides and other metals may be used as well.
The exterior surface comprises one or more pure metal regions 120 consisting of pure metal. Metals that have been found to be suitable for these pure metal regions include palladium, copper, molybdenum, and cobalt. However, it is contemplated that other metals may be used as well. For the purposes of this disclosure, the terms “pure metal” and “pure metallic” should be interpreted to mean that the regions consist only of metal and are characterized by the absence of any other type of material. For example, the pure metal regions 120 may comprise a metal or a metal-metal alloy, but they may not comprise any ceramic material. The purpose of these purely metal regions 120 is to provide exposed regions at the exterior surface 115 of the carrier nano-particle 100 to which catalytic nano-particles 130 will have a strong attraction.
The catalytic nano-particles 130 are bonded, or otherwise affixed, to these pure metal regions 120. In some embodiments, these catalytic nano-particles 130 comprise or consist of platinum. In some embodiments, these catalytic nano-particles 130 comprise or consist of a platinum alloy, such as a platinum-palladium alloy. However, it is contemplated that other catalytic materials may be used as well. In some embodiments, the catalytic nano-particles 130 have an average grain size of approximately 1 nanometer or less. In some embodiments, the catalytic nano-particles 130 have an average grain size of approximately ½ nanometer. However, it is contemplated that other sizes are within the scope of the present invention. Although
The pure metal regions 120 are bonded to the mixed-metal oxide 110 and act as pinning agents to securely affix the catalytic nano-particles 130 to the carrier nano-particle 100, thereby reducing or eliminating the mobility of the catalytic nano-particles 130 and preventing their agglomeration.
The interior region is the region between the center of the carrier particle and the exterior surface 215. This interior region comprises a mixed-metal oxide 210. In some embodiments, the mixed-metal oxide 210 comprises aluminum oxide along with an accompanying metal. In some embodiments, this accompanying metal is palladium. Other accompanying metals that have been found to be suitable are copper, molybdenum, and cobalt. It is contemplated that other oxides and other metals may be used as well.
The embodiment of
Similar to the exterior surface of carrier nano-particle 100, the exterior surface of carrier nano-particle 200 comprises one or more pure metal regions 220 consisting of pure metal. Metals that have been found to be suitable for these pure metal regions include palladium, copper, molybdenum, and cobalt. However, it is contemplated that other metals may be used as well. For the purposes of this disclosure, the terms “pure metal” and “pure metallic” should be interpreted to mean that the regions consist only of metal and are characterized by the absence of any other type of material. For example, the pure metal regions 220 may comprise a metal or a metal-metal alloy, but they may not comprise any ceramic material. The purpose of these purely metal regions 220 is to provide exposed regions at the exterior surface 215 of the carrier nano-particle 200 to which catalytic nano-particles 230 will have a strong attraction.
As discussed above with respect to the embodiment of
As previously discussed with respect to the embodiment of
Whether it is with respect to the embodiments of
Whether it is with respect to the embodiments of
In some embodiments, the mixed-metal oxide 210 can be anything between a partial monolayer and multiple monolayers. In some embodiments, pure metal regions 220 can be anything between a metal atom partially bonded to oxygen atoms in the matrix, with at least one bonding site to anchor a metal particle, and a metal atom cluster with one or more atoms incorporated in the mixed-metal oxide and one or more pure metal atoms available to alloy with a metallic catalysis particle (e.g., a platinum nano-particle).
It is contemplated that a variety of different methods can be employed to impregnate the catalyst supports 310A, 310B with the catalyst carrier nano particles 330A, 330B. In some embodiments, a liquid dispersion of the catalyst carrier nano-particles is applied to the catalyst support. The catalyst support is allowed to dry and/or a drying process is performed on the catalyst support. As the liquid in the dispersion evaporates, the catalyst carrier nano-particles settle onto the surface of the support and/or into the pores within the support. When the impregnated catalyst support dries, electrostatic interactions and other forces between the catalyst carrier nano-particles and the catalyst support effectuate some adhesion. Advantageously, such forces cause the nano-particles to stick onto the surfaces and pores of the support.
In some embodiments, a calcining step is performed to form oxide-oxide bonds between the nano-particles and the catalyst support, exposing them to heat, pressure, or a combination thereof. The calcining temperature is generally from 350 to 1000 degrees centigrade, and the pressure is on the order of ambient atmosphere to several atmospheres. For optimum oxide-oxide bonds, a portion of the catalytic carrier nano-particles is chosen to correspond to the material of which the catalyst support is comprised. By way of example, if a portion of the catalyst carrier nano-particles comprises alumina, then the catalyst support preferably comprises alumina, although dissimilar oxides are also contemplated. Due to the physical and chemical bond between the catalyst support and the nano-particles, islands of nano-particles that are bonded, fixed or otherwise pinned to the surfaces of the catalyst support will not migrate and coalesce during catalytic conversion. The surface area for catalysis remains high, and therefore the catalytic activity remains high. In effect, operations such as fine chemical plants and oil refineries will not be required to stop operations and swap out ineffective catalyst supports with fresh catalyst supports with the same frequency as existing processes, thereby increasing throughput at the plants and refineries and reducing their overall cost of operation.
At step 410, a plurality of carrier nano-particles is formed. Each carrier nano-particle comprises an interior region and an exterior surface. The interior region comprises a mixed-metal oxide, while the exterior surface comprises a pure metal. The carrier nano-particles can comprise any of the elements discussed above with respect to
At step 420, at least one catalytic particle is bonded to each of the carrier nano-particles, thereby forming catalytic carrier nano-particles. The catalytic particle is bonded to the pure metal at the exterior surface of the carrier particle. The catalytic particle can comprise any of the elements discussed above with respect to
At step 430, the plurality of carrier nano-particles are bonded to a support structure. One example of such a support structure is a porous ceramic material. However, it is contemplated that other types of support structures can be employed. The support structure can comprise any of the elements discussed above with respect to
At step 510, a first material, a second material, and a third material are loaded into a plasma gun in a desired ratio. In some embodiments, the first material is an aluminum oxide material, the second material is a palladium material, and the third material is a platinum material. However, it is contemplated that other materials can be used in addition or as an alternative to these materials.
At step 520, the first material, the second material, and the third material are vaporized using the plasma gun, thereby forming a vapor cloud that comprises vaporized first material, vaporized second material, and vaporized third material.
At step 530, the vapor cloud is quenched, thereby condensing the vaporized material into carrier nano-particles with catalytic nano-material bonded to the carrier nano-particles. Each nano-particle comprises an interior region and an exterior surface. The interior region comprises a mixed-metal oxide. The exterior surface comprises a pure metal. The catalytic nano-material is bonded to the pure metal at the exterior surface.
It is contemplated that the present invention can employ a variety of different types of plasma gun systems to vaporize and quench the loaded material into nano-particles. In a preferred embodiment, the nano-particles are substantially uniform in size. The nano-particles can be formed by introducing micron-sized material into a plasma process, such as described and claimed in the co-owned application Ser. No. 11/110,341 , filed Apr. 19, 2005 (now abandoned), and titled “High Throughput Discovery of Materials Through Vapor Phase Synthesis,” and the co-owned and co-pending application Ser. No. 12/151,935 , filed May 8, 2008 , and titled “Highly Turbulent Quench Chamber,” both of which are hereby incorporated by reference as if set forth herein.
Generally, the chamber 730 operates as a reactor, producing an output comprising particles within a gas stream. Production includes the basic steps of combination, reaction, and conditioning as described later herein. The system combines precursor material supplied from the precursor supply device 710 and working gas supplied from the working gas supply device 720 within the energy delivery zone of the chamber 730.
In some embodiments, the precursor material comprises a powdered substance. In some embodiments, the precursor material is micron-sized. In some embodiments, the precursor material comprises an average grain diameter of 500-600 nanometers. In some embodiments, the precursor material comprises an average grain diameter of one micrometer. In some embodiments, the precursor material comprises an average grain diameter greater than or equal to 5 microns.
The system energizes the working gas in the chamber 730 using energy from the energy supply system 725, thereby forming a plasma. The plasma is applied to the precursor material within the chamber 730 to form an energized, reactive mixture. This mixture comprises one or more materials in at least one of a plurality of phases, which may include vapor, gas, and plasma. The reactive mixture flows from the plasma production and reactor chamber 730 into the quench chamber 745 through an injection port 740.
The quench chamber 745 preferably comprises a substantially cylindrical surface 750, a frusto-conical surface 755, and an annular surface 760 connecting the injection port 740 with the cylindrical surface 750. The frusto-conical surface 760 narrows to meet the outlet 765. The plasma production and reactor chamber 730 includes an extended portion at the end of which the injection port 740 is disposed. This extended portion shortens the distance between the injection port 740 and the outlet 765, reducing the volume of region in which the reactive mixture and the conditioning fluid will mix, referred to as the quench region. In a preferred embodiment, the injection port 740 is arranged coaxially with the outlet 765. The center of the injection port is positioned a first distance d1 from the outlet 765. The perimeter of the injection port is positioned a second distance d2 from a portion of the frusto-conical surface 755. The injection port 740 and the frusto-conical surface 755 form the aforementioned quench region therebetween. The space between the perimeter of the injection port 740 and the frusto-conical surface 755 forms a gap therebetween that acts as a channel for supplying conditioning fluid into the quench region. The frusto-conical surface 755 acts as a funneling surface, channeling fluid through the gap and into the quench region.
While the reactive mixture flows into the quench chamber 745, the ports 790 supply conditioning fluid into the quench chamber 745. The conditioning fluid then moves along the frusto-conical surface 755, through the gap between the injection port 740 and the frusto-conical surface 755, and into the quench region. In some embodiments, the controlled atmosphere system 770 is configured to control the volume flow rate or mass flow rate of the conditioning fluid supplied to the quench region.
As the reactive mixture moves out of the injection port 740, it expands and mixes with the conditioning fluid. Preferably, the angle at which the conditioning fluid is supplied produces a high degree of turbulence and promotes mixing with the reactive mixture. This turbulence can depend on many parameters. In a preferred embodiment, one or more of these parameters is adjustable to control the level of turbulence. These factors include the flow rates of the conditioning fluid, the temperature of the frusto-conical surface 755, the angle of the frusto-conical surface 755 (which affects the angle at which the conditioning fluid is supplied into the quench region), and the size of the quench region. For example, the relative positioning of the frusto-conical surface 755 and the injection port 740 is adjustable, which can be used to adjust the volume of quench region. These adjustments can be made in a variety of different ways, using a variety of different mechanisms, including, but not limited to, automated means and manual means.
During a brief period immediately after entering the quench chamber 745, particle formation occurs. The degree to which the particles agglomerate depends on the rate of cooling. The cooling rate depends on the turbulence of the flow within the quench region. Preferably, the system is adjusted to form a highly turbulent flow, and to form very dispersed particles. For example, in preferred embodiments, the turbidity of the flow within the quench region is such that the flow has a Reynolds Number of at least 1000.
Still referring to
Substantial heat is emitted, mostly in the form of radiation, from the reactive mixture following its entry into the quench chamber 745. The quench chamber 745 is designed to dissipate this heat efficiently. The surfaces of the quench chamber 745 are preferably exposed to a cooling system (not shown). In a preferred embodiment, the cooling system is configured to control a temperature of the frusto-conical surface 755.
Following injection into the quench region, cooling, and particle formation, the mixture flows from the quench chamber 745 through the outlet port 765. Suction generated by a generator 795 moves the mixture and conditioning fluid from the quench region into the conduit 792. From the outlet port 765, the mixture flows along the conduit 792, toward the suction generator 795. Preferably, the particles are removed from the mixture by a collection or sampling system (not shown) prior to encountering the suction generator 795.
Still referring to
The angle of the frusto-conical surface affects the angle at which the conditioning fluid is supplied into the quench region, which can affect the level of turbulence in the quench region. The conditioning fluid preferably flows into the quench region along a plurality of momentum vectors. The greater the degree of the angle between the momentum vectors, the higher the level of turbulence that will be produced. In a preferred embodiment, the high turbulent quench chamber comprises a frusto-conical surface that is configured to funnel at least two conditioning fluid momentum vectors into the quench region such that there is at least a 90 degree angle between the two momentum vectors. It is contemplated that other angle degree thresholds may be applied as well. For example, attention may also be paid to the angle formed between at least one of the conditioning fluid momentum vectors and the momentum vector of the reactive mixture. In one embodiment of a highly turbulent quench chamber, a reactive mixture inlet is configured to supply the reactive mixture into the quench region along a first momentum vector, the frusto-conical surface is configured to supply the conditioning fluid to the quench region along a second momentum vector, and the second momentum vector has an oblique angle greater than 20 degrees relative to the first momentum vector.
The size of the quench region also affects the level of turbulence in the quench region. The smaller the quench region, the higher the level of turbulence that will be produced. The size of the quench region can be reduced by reducing the distance between the center of the injection port 740 and the outlet 765.
The high turbulence produced by the embodiments of the present invention decreases the period during which particles formed can agglomerate with one another, thereby producing particles of more uniform size, and in some instances, producing smaller-sized particles. Both of these features lead to particles with increased dispersibility and increased ratio of surface area to volume. While the plasma process described above is extremely advantageous in producing the nano-particles, it is contemplated that the nano-particles can be produced in other ways as well.
At step 610, a first material and a second material are loaded into a plasma gun in a desired ratio. In some embodiments, the first material is an aluminum oxide material and the second material is a palladium material. However, it is contemplated that other materials can be used in addition or as an alternative to these materials.
At step 620, the first material and the second material are vaporized using the plasma gun, thereby forming a vapor cloud that comprises vaporized first material and vaporized second material.
At step 630, the vapor cloud is quenched, thereby condensing the vaporized first material and vaporized second material into carrier nano-particles. Each carrier nano-particle comprises an interior region and an exterior surface. The interior region comprises a mixed-metal oxide. The exterior surface comprises a pure metal.
At step 640, the carrier nano-particles and a third material are loaded into a plasma gun in a desired ratio. In some embodiments, the third material is a platinum material. However, it is contemplated that other materials can be used in addition or as an alternative to a platinum material.
At step 650, the third material is vaporized using the plasma gun, thereby forming a vapor cloud that comprises vaporized third material.
At step 660, the carrier nano-particles are mixed with the vaporized third material in the vapor cloud.
At step 670, the vapor cloud is quenched, thereby condensing the vaporized third material into catalytic nano-particles and bonding them to the pure metal at the exterior surface of the carrier nano-particles.
As discussed above, it is contemplated that the present invention can employ a variety of different types of plasma gun systems to vaporize and quench the loaded material into nano-particles. The nano-particles can be formed by introducing micron-sized material into a plasma process, such as described and claimed in the co-owned and co-pending application Ser. No. 12/152,111, filed May 9, 2008, and titled “Powder Coating System and Method Including Gun Extension,” which is hereby incorporated by reference as if set forth herein.
The motive gas supply chamber 810 is fluidly coupled to a motive gas supply system 815, which is configured to supply a motive gas. Preferably, the motive gas is an inert gas, such as argon. Furthermore, the chamber 810 preferably include airtight inlets and outlets configured to permit conduits to pass through to supply the plasma production chamber 820 and coating chamber 830. The motive gas supply chamber 810 can include airtight couplings that permit these conduits to pass through while preventing leakage either into or out of the chambers. Furthermore, output from the coating chamber 830 can flow into the cooling conduit 870, which can also passes through a wall of the motive gas supply chamber 810. Preferably, the cooling conduit 870 also exits the motive gas supply chamber through an airtight coupling.
The plasma production chamber 820 preferably includes several types of inputs for receiving power, gas, and target materials. Inputs are provided to the chamber 820 by a variety of supply systems through means described below. Functional aspects of these supply systems are also described below.
Various input conduits fluidly couple the plasma gas supply mixer 840 with a first gas supply vessel 842 and a second gas supply vessel 844. The plasma gas supply system 840 includes an outlet fluidly coupled with an inlet of the plasma production chamber 820. The gas supply system 840 and the production chamber 820 are coupled by a conduit that passes through the motive gas supply chamber 810. Preferably, but not shown in the figure, an overall system controller provides control signals to the plasma gas supply system 840.
The power supply system 825 is also coupled to the plasma production chamber 820 through conduits that pass through the motive gas supply chamber 810. Preferably, but not shown in the figure, an overall system controller provides control signals to the power supply system 825.
The coater supply system 852 houses precursor material and includes an externally controllable delivery system fluidly coupled to a materials inlet of the plasma production chamber 820. The supply system 852 is coupled with the production chamber 820 by a conduit that passes through the motive gas supply chamber 810. Preferably, but not shown in the figure, an overall system controller provides control signals to the supply system 852.
Preferably, the conduits that run between the plasma gas supply system 840 and the production chamber 820, the coater supply system 852 and the plasma production chamber 820, and the power supply system 825 and the plasma production chamber 820, all enter the motive gas supply chamber 810 through air-tight seals. In some embodiments, the conduits of the various supply systems all have dedicated airtight entrances to the motive gas supply chamber 810. In some embodiments, a single airtight entrance accommodates multiple conduits.
The coating chamber 830 preferably includes inlets for motive gas, coater material-plasma mixture, and coatee material, as well as an outlet to provide an output to the cooling conduit 870. The inlets for motive gas couple the motive gas supply chamber 810 to the interior of the coating chamber 830. Preferably, these inlets are channels of adjustable size that directly coupled the two chambers, yet permit for controlled flow from the supply chamber 810 into the coating chamber 830.
Coatee material is stored within the coatee material supply system 854, which preferably sits outside the motive gas supply chamber 810. A conduit passes from the supply system 854 through the motive gas supply chamber 810 and also through a wall of the coating chamber 830. The coatee material supply system 854 includes a controllable delivery system that provides coatee material to the conduit. Preferably, the conduit enters both chambers though airtight seals. The conduit terminates within the coating chamber at a selected location. Preferably, the location of the terminus is selected based on parameters of operation. Also preferably, but not shown, an overall system controller is configured to supply control signals to the supply system 854.
The cooling conduit 870 connects the coating chamber 830 with the sampling system 880. The conduit 870 exits the motive gas supply chamber 810 through airtight means. The cooling conduit 870 includes a first section 872, a second section 874, third section 876, and fourth section 878. The sections are joined by gas input couplings that contain gas input features. The first section 872 is joined to the second section 874 by the gas input coupling 862. In turn, the second section 874 is joined to the third section 876 by the gas input coupling 864. The gas input coupling 866 joins the third section 876 to the fourth section 878.
In the illustrated embodiment, no gas is shown being supplied to the gas input couplings 862, 864, 866 for input into the cooling conduit 870. However, gas can be supplied through one or more of the gas input couplings.
The sampling system 880 is fluidly coupled between the cooling conduit 870 and the motive pump 890. The sampling system 880 is configured to receive output from the cooling conduit 870, sample material having appropriate characteristics from the output, and permit remains of the output to flow to the motive pump 890, which is fluidly coupled through a conduit to the sampling system 880.
During operation, the supply systems 840, 852, and 825 provide plasma gas, coater material, and power, respectively, to the plasma production chamber 820. Power from the delivery system 825 is used to energize gas from the supply system 840 to produce a plasma within the production chamber 820. The coater material supply system 852 provides coater material in metered amounts into the plasma production chamber 820, exposing the coater material to plasma formed therein.
The overall control system (not shown) sends signals to the plasma gas supply system 840, coater material supply system 852, and power supply system 825 to set operational parameters. The plasma gas supply system 840 determines the ratio of mixing for the first and second gasses to produce plasma gas, as well as the rate at which the plasma gas feeds into the plasma production chamber 820. In a preferred embodiment, the first gas is hydrogen and the second gas is an inert gas, such as argon. The coater material supply system 852 determines the rate at which the coater material is supplied into the plasma production chamber 820. The power supply system 825 determines the voltage and amperage at which power is supplied to the plasma production chamber. In combination, these parameters determine the characteristics of the plasma produced within the plasma production chamber 820, as well as the characteristics of the plasma-coatee material mixture also produced within the chamber 820. Furthermore, although the coater supply system is described as providing only a single coater material into the plasma production chamber 820 at a single location, in some embodiments of the present invention, the coater supply system 852 supplies a plurality of materials into the plasma production chamber 820 at one or more locations.
The motive gas supply chamber 810 receives motive gas, typically an inert gas such as argon, from a preferably dedicated motive gas supply system 815. The motive gas supply chamber 810 provides an airtight enclosure around the plasma production chamber 820 and coating chamber 830. The motive gas supply system 815 preferably maintains a pressure within the motive gas supply chamber 810 that slightly exceeds the ambient pressure of the environment in which the system 800 is housed, regardless of any variation in suction force generated by the motive pump 890.
The coating chamber 830 receives a coater material and plasma mixture from the plasma production chamber 820. The coating chamber 830 also receives motive gas through input features. Preferably, these input features provide for an adjustable flow rate of motive gas into the coating chamber 830. Motive gas flow is preferably motivated by the motive pump 890 by pulling a negative pressure on the conduit 870, motivating mass flow through the outlet of the coating chamber 870. However, the flow rate of the motive gas into the coating chamber 830 is preferably controlled by the overall control system.
Furthermore, the coatee material supply system 854 provides a metered stream of coater material through the coatee material conduit to the conduit's terminus location within the coating chamber 830. The rate at which coatee material is provided into the chamber 830 preferably is determined by the overall control system. Furthermore, although the terminus of the coatee material supply conduit is shown to deposit material only at one location within the coating chamber 830, in some embodiments of the present invention, the terminus deposits coatee material at a plurality of locations within the conduit (e.g., in an annular configuration surrounding output of the plasma production chamber 820).
Preferably, coating chamber 830 is shaped and the operational parameters of the apparatus 800 are controlled so that the coater material and plasma mixture enters the coating chamber and reaches a maximum enthalpy shortly thereafter. Most preferably, this maximum of enthalpy occurs within a defined region of the coating chamber 830, with the average enthalpy of the mixture falling as it moves away from that region with its minimum (within the coating chamber 830) coming at the outlet to the cooling conduit 870. For example, as illustrated in
Furthermore, in certain embodiments of the present invention, the coating chamber 830 is shaped and the operational parameters of the apparatus 800 are chosen so that the coater material begins to condense from the coater material and gas mixture within a defined region of the coating chamber 830. For example, in
The cooling conduit 870 receives the coated particle and gas mixture from the coating chamber 830. Preferably, the mixture is pulled into the cooling conduit by the motive pump 890. However, in some embodiments, a motive pump or other system within the sampling system 880 provides some motive force to pull the mixture. Of course, to some extent, pressure provided by the plasma production chamber 820 and the motive gas supply 815 motivate the movement of the mixture into the cooling conduit 870.
In some embodiments, the cooling conduit 870 is equipped with an active cooling system. In some embodiments, a gas is supplied into the gas input couplings 862, 864, or 866. In some of these embodiments, the gas is a cooling and entraining gas. In some of these embodiments, the gas is a passivating gas configured to reduce the reactivity of the condensed particles within the mixture.
As mentioned above, the sampling system 880 preferably permits the motive pump 890 to provide a motive force therethrough. However, in some embodiments the sampling system 880 provides additional motive force. In some embodiments the sampling system 880 supplants the motive force provided by the motive pump 890 and provides a substitute motive force to the cooling conduit 870.
It is contemplated that the sampling system 880 can be configured in a variety of ways. In one embodiment, the sampling system 880 comprises a sampling structure, at least one filled aperture formed in the sampling structure, and at least one unfilled aperture formed in the sampling structure. Each filled aperture is configured to collect particles from the mixture stream, such as by using a filter. The sampling structure is configured to be adjusted between a pass-through configuration and a collection configuration. The pass-through configuration comprises an unfilled aperture being fluidly aligned with a conduit, such as conduit 870, thereby allowing the unfilled aperture to receive the mixture stream from the conduit and the mixture stream to flow through the sampling structure without substantially altering the particle content of the mixture stream. The collection configuration comprises a filled aperture being fluidly aligned with the conduit, thereby allowing the filled aperture to receive the mixture stream and collect particles while the mixture stream is being flown through the filled aperture.
It is contemplated that the sampling structure can be adjusted between the pass-through configuration and the collection configuration in a variety of ways. In one embodiment, the sampling structure is a disk-shaped structure including an annular array of apertures, wherein the annular array comprises a plurality of the filled apertures and a plurality of the unfilled apertures. The sampling structure is rotatably mounted to a base, wherein rotational movement of the sampling structure results in the adjustment of the sampling structure between the pass-through configuration and the collection configuration. In another embodiment, the sampling structure is a rectangular-shaped structure including a linear array of apertures, wherein the linear array comprises a plurality of the filled apertures and a plurality of the unfilled apertures. The sampling structure is slideably mounted to a base, wherein sliding of the sampling structure results in the adjustment of the sampling structure between the pass-through configuration and the collection configuration.
It is contemplated that the particles of the present invention can be formed and bonded using wet chemistry methods in addition or as an alternative to the use of a plasma-based system. Such methods include, but are not limited to, the methods described in the following references, which are hereby incorporated by reference as if set forth herein: Adschiri et al., “Hydrothermal synthesis of metal oxide nanoparticles at supercritical conditions” (Journal of Nanoparticle Research 3: 227-235, 2001); Kratohvil et al., “Preparation and properties of coated, uniform, inorganic colloidal particles: I. Aluminum (hydrous) oxide on hematile, chromia, and titania” (Advanced Ceramics Materials 2:4, 1987); Matijevic, “Monodispersed Metal (Hydrous) Oxides—A Fascinating Field of Colloid Science” (Acc. Chem. Res. 14, 22-29, 1981); Lakshmi et al., “Sol-Gel Template Synthesis of Semiconductor Oxide Micro- and Nanostructures” (Chem. Mater. 9, 2544-2550, 1997); Carnes et al., “Synthesis, Characterization, and Adsorption Studies of Nanocrystalline Aluminum Oxide and a Biometallic Nanocrystalline Aluminum Oxide/Magnesium Oxide” (Chem. Mater. 14, 2922-2929, 2002); Zhu et al., “y-Alumina Nanofibers Prepared from Aluminum Hydrate with Poly(ethylene oxide) Surfactant” (Chem. Mater. 14, 2086-2093, 2002); Alexander et al., “PROCESS FOR MODIFYING THE PROPERTIES OF A SILICA SOL AND PRODUCT THEREOF” (U.S. Pat. No. 2,892,797, Issued Jun. 30, 1959); Alexander et al., “AQUASOLS OF POSITIVELY-CHARGED COATED SILICA PARTICLES AND THEIR PRODUCTION” (U.S. Pat. No. 3,007,878, Issued Nov. 7, 1961); Moore, Jr., “STABLE POSITIVELY CHARGED ALUMINA COATED SILICA SOLS AND THEIR PREPARATION BY POST-NEUTRALIZATION” (U.S. Pat. No. 3,719,607, Issued Mar. 6, 1973); Moore, Jr., “STABLE POSITIVELY CHARGED ALUMINA COATED SILICA SOLS” (U.S. Pat. No. 3,745,126, Issued Jul. 10, 1973); and Kovarik, “METAL OXIDE SOLS” (U.S. Pat. No. 3,864,142, Issued Feb. 4, 1975).
At step 910, a first material and a second material are provided in a desired ratio. In some embodiments, the first material is an aluminum material and the second material is a palladium material. In some embodiments, the aluminum material is a salt or an organic compound, and the palladium material is a salt. However, it is contemplated that other materials can be used in addition or as an alternative to these materials.
At step 920, a plurality of carrier nano-particles are formed from the first material and the second material via a chemical reaction using a wet chemistry process. Each carrier nano-particle comprises an interior region and an exterior surface, the interior region comprises a mixed-metal oxide. The exterior surface comprises a pure metal. In some embodiments, the center core of each carrier nano-particle comprises silica.
At step 930, a suspension of the carrier nano-particles is formed and mixed with a catalytic solution (a solution comprising particles having catalytic properties). In some embodiments, the catalytic solution is a platinum solution. In some embodiments, the platinum solution is a platinum nitrate solution or a platinum chloride solution. However, it is contemplated that other types of catalytic solutions can be used.
At step 940, the catalytic solution reacts with the carrier nano-particles, thereby pinning catalytic nano-particles to the pure metal at the exterior surface of the carrier nano-particles. For example, in one embodiment, platinum ions from the catalytic solution react with the oxide surface of the carrier nano-particles, resulting in discreet platinum atoms ending up on the surface of the carrier nano-particles. These atoms can diffuse over the oxide surface and agglomerate with other platinum atoms to form platinum nano-particles. When a platinum nano-particle reaches a palladium atom cluster bonded in the oxide surface, the platinum cluster alloys with the palladium cluster, thereby pinning the platinum cluster. In some embodiments, the carrier nano-particles have an average grain size of approximately 10 nanometers or less. In some embodiments, the catalytic nano-particles have an average grain size of approximately 1 nanometer or less. In some embodiments, the catalytic nano-particles have an average grain size of approximately ½ nanometer. However, it is contemplated that other sizes are within the scope of the present invention.
At step 1010, a first material and a second material are loaded into a plasma gun in a desired ratio. In some embodiments, the first material is an aluminum oxide material and the second material is a palladium material. However, it is contemplated that other materials can be used in addition or as an alternative to these materials.
At step 1020, the first material and the second material are vaporized using the plasma gun, thereby forming a vapor cloud that comprises vaporized first material and vaporized second material.
At step 1030, the vapor cloud is quenched, thereby condensing the vaporized first material and vaporized second material into carrier nano-particles. Each carrier nano-particle comprises an interior region and an exterior surface. The interior region comprises a mixed-metal oxide. The exterior surface comprises a pure metal. One objective of the present invention is to mix an easily oxidizable and reducible metal into a carrier oxide (e.g., aluminum oxide, ceria, zirconia, silica, etc.). The idea is that the metal (e.g., Pd, Cu, Zn, Cr, Ni, etc.) gets incorporated into the oxide matrix. However, by making this an oxygen deficient environment, such as by adding H2 into the carrier gas, some of the metal is in its non-oxidized state on the surface of the particle. One method that can be used is to form mixed-metal oxide nano-particles, and then expose them to a reducing environment, such as H2 at temperature or a H2 plasma, and partially reduce the metal-oxide on the surface. The carrier-oxide would not easily reduce in this environment. However, the oxidation state of the metal buried below the surface of the mixed metal oxide is not crucial. The result is a mixed-metal oxide particle with metal atoms on the surface that are not fully oxidized. These metal atoms form the anchor for the metallic catalysis particles added later, such as described in steps 930 and 940 of
At step 1040, the carrier nano-particles are mixed with a catalytic solution. In some embodiments, the catalytic solution is a platinum solution. In some embodiments, the platinum solution is a platinum nitrate solution or a platinum chloride solution. However, it is contemplated that other types of catalytic solutions can be used.
At step 1050, the catalytic solution reacts with the carrier nano-particles, thereby pinning catalytic nano-particles to the pure metal at the exterior surface of the carrier nano-particles. For example, in one embodiment, platinum ions from the catalytic solution react with the oxide surface of the carrier nano-particles, resulting in discreet platinum atoms ending up on the surface of the carrier nano-particles. These atoms can diffuse over the oxide surface and agglomerate with other platinum atoms to form platinum nano-particles. When a platinum nano-particle reaches a palladium atom cluster bonded in the oxide surface, the platinum cluster alloys with the palladium cluster, thereby pinning the platinum cluster. In some embodiments, the carrier nano-particles have an average grain size of approximately 10 nanometers or less. In some embodiments, the catalytic nano-particles have an average grain size of approximately 1 nanometer or less. In some embodiments, the catalytic nano-particles have an average grain size of approximately ½ nanometer. However, it is contemplated that other sizes are within the scope of the present invention.
The present invention has been described in terms of specific embodiments incorporating details to facilitate the understanding of principles of construction and operation of the invention. Such reference herein to specific embodiments and details thereof is not intended to limit the scope of the claims appended hereto. It will be readily apparent to one skilled in the art that other various modifications may be made in the embodiment chosen for illustration without departing from the spirit and scope of the invention as defined by the claims.
This application is a continuation of U.S. patent application Ser. No. 13/033,514 , filed Feb. 23, 2011 , now U.S. Pat. No. 8,669,202 issued Mar. 11, 2014.
| Number | Name | Date | Kind |
|---|---|---|---|
| 2021936 | Johnstone | Nov 1935 | A |
| 2284554 | Beyerstedt | May 1942 | A |
| 2419042 | Todd | Apr 1947 | A |
| 2519531 | Worn | Aug 1950 | A |
| 2562753 | Trost | Jul 1951 | A |
| 2689780 | Rice | Sep 1954 | A |
| 3001402 | Koblin | Sep 1961 | A |
| 3042511 | Reding, Jr. | Jul 1962 | A |
| 3067025 | Chisholm | Dec 1962 | A |
| 3145287 | Rotolico et al. | Aug 1964 | A |
| 3178121 | Wallace, Jr. | Apr 1965 | A |
| 3179782 | Matvay | Apr 1965 | A |
| 3181947 | Vordahl | May 1965 | A |
| 3235700 | Mondain-Monval et al. | Feb 1966 | A |
| 3313908 | Unger et al. | Apr 1967 | A |
| 3387110 | Wendler et al. | Jun 1968 | A |
| 3401465 | Larwill | Sep 1968 | A |
| 3450926 | Kiernan | Jun 1969 | A |
| 3457788 | Miyajima | Jul 1969 | A |
| 3520656 | Yates et al. | Jul 1970 | A |
| 3537513 | Austin | Nov 1970 | A |
| 3552653 | Inoue | Jan 1971 | A |
| 3617358 | Dittrich | Nov 1971 | A |
| 3667111 | Chartet | Jun 1972 | A |
| 3741001 | Fletcher et al. | Jun 1973 | A |
| 3752172 | Cohen et al. | Aug 1973 | A |
| 3761360 | Auvil et al. | Sep 1973 | A |
| 3774442 | Gustaysson | Nov 1973 | A |
| 3804034 | Stiglich, Jr. | Apr 1974 | A |
| 3830756 | Sanchez et al. | Aug 1974 | A |
| 3857744 | Moss | Dec 1974 | A |
| 3871448 | Vann et al. | Mar 1975 | A |
| 3892882 | Guest et al. | Jul 1975 | A |
| 3914573 | Muehlberger | Oct 1975 | A |
| 3959094 | Steinberg | May 1976 | A |
| 3959420 | Geddes et al. | May 1976 | A |
| 3969482 | Teller | Jul 1976 | A |
| 4008620 | Narato et al. | Feb 1977 | A |
| 4018388 | Andrews | Apr 1977 | A |
| 4021021 | Hall et al. | May 1977 | A |
| 4127760 | Meyer et al. | Nov 1978 | A |
| 4139497 | Castor et al. | Feb 1979 | A |
| 4146654 | Guyonnet | Mar 1979 | A |
| 4157316 | Thompson et al. | Jun 1979 | A |
| 4171288 | Keith et al. | Oct 1979 | A |
| 4174298 | Antos | Nov 1979 | A |
| 4189925 | Long | Feb 1980 | A |
| 4227928 | Wang | Oct 1980 | A |
| 4248387 | Andrews | Feb 1981 | A |
| 4253917 | Wang | Mar 1981 | A |
| 4260649 | Dension et al. | Apr 1981 | A |
| 4284609 | deVries | Aug 1981 | A |
| 4315874 | Ushida et al. | Feb 1982 | A |
| 4326492 | Leibrand, Sr. et al. | Apr 1982 | A |
| 4344779 | Isserlis | Aug 1982 | A |
| 4369167 | Weir | Jan 1983 | A |
| 4388274 | Rourke et al. | Jun 1983 | A |
| 4419331 | Montalvo | Dec 1983 | A |
| 4431750 | McGinnis et al. | Feb 1984 | A |
| 4436075 | Campbell et al. | Mar 1984 | A |
| 4440733 | Lawson et al. | Apr 1984 | A |
| 4458138 | Adrian et al. | Jul 1984 | A |
| 4459327 | Wang | Jul 1984 | A |
| 4505945 | Dubust et al. | Mar 1985 | A |
| 4506136 | Smyth et al. | Mar 1985 | A |
| 4513149 | Gray et al. | Apr 1985 | A |
| 4523981 | Ang et al. | Jun 1985 | A |
| 4545872 | Sammells et al. | Oct 1985 | A |
| RE32244 | Andersen | Sep 1986 | E |
| 4609441 | Frese, Jr. et al. | Sep 1986 | A |
| 4610857 | Ogawa et al. | Sep 1986 | A |
| 4616779 | Serrano et al. | Oct 1986 | A |
| 4723589 | Iyer et al. | Feb 1988 | A |
| 4731517 | Cheney | Mar 1988 | A |
| 4751021 | Mollon et al. | Jun 1988 | A |
| 4764283 | Ashbrook et al. | Aug 1988 | A |
| 4765805 | Wahl et al. | Aug 1988 | A |
| 4780591 | Bernecki et al. | Oct 1988 | A |
| 4824624 | Palicka et al. | Apr 1989 | A |
| 4836084 | Vogelesang et al. | Jun 1989 | A |
| 4855505 | Koll | Aug 1989 | A |
| 4866240 | Webber | Sep 1989 | A |
| 4877937 | Müller | Oct 1989 | A |
| 4885038 | Anderson et al. | Dec 1989 | A |
| 4921586 | Molter | May 1990 | A |
| 4970364 | Müller | Nov 1990 | A |
| 4982050 | Gammie et al. | Jan 1991 | A |
| 4983555 | Roy et al. | Jan 1991 | A |
| 4987033 | Abkowitz et al. | Jan 1991 | A |
| 5006163 | Benn et al. | Apr 1991 | A |
| 5015863 | Takeshima et al. | May 1991 | A |
| 5041713 | Weidman | Aug 1991 | A |
| 5043548 | Whitney et al. | Aug 1991 | A |
| 5070064 | Hsu et al. | Dec 1991 | A |
| 5073193 | Chaklader et al. | Dec 1991 | A |
| 5133190 | Abdelmalek | Jul 1992 | A |
| 5151296 | Tokunaga | Sep 1992 | A |
| 5157007 | Domesle et al. | Oct 1992 | A |
| 5187140 | Thorsteinson et al. | Feb 1993 | A |
| 5192130 | Endo et al. | Mar 1993 | A |
| 5217746 | Lenling et al. | Jun 1993 | A |
| 5225656 | Frind | Jul 1993 | A |
| 5230844 | Macaire et al. | Jul 1993 | A |
| 5233153 | Coats | Aug 1993 | A |
| 5269848 | Nakagawa | Dec 1993 | A |
| 5294242 | Zurecki et al. | Mar 1994 | A |
| 5330945 | Beckmeyer et al. | Jul 1994 | A |
| 5338716 | Triplett et al. | Aug 1994 | A |
| 5369241 | Taylor et al. | Nov 1994 | A |
| 5371049 | Moffett et al. | Dec 1994 | A |
| 5372629 | Anderson et al. | Dec 1994 | A |
| 5392797 | Welch | Feb 1995 | A |
| 5436080 | Inoue et al. | Jul 1995 | A |
| 5439865 | Abe et al. | Aug 1995 | A |
| 5442153 | Marantz et al. | Aug 1995 | A |
| 5452854 | Keller | Sep 1995 | A |
| 5460701 | Parker et al. | Oct 1995 | A |
| 5464458 | Yamamoto | Nov 1995 | A |
| 5485941 | Guyomard et al. | Jan 1996 | A |
| 5486675 | Taylor et al. | Jan 1996 | A |
| 5534149 | Birkenbeil et al. | Jul 1996 | A |
| 5534270 | De Castro | Jul 1996 | A |
| 5543173 | Horn, Jr. et al. | Aug 1996 | A |
| 5553507 | Basch et al. | Sep 1996 | A |
| 5558771 | Hagen et al. | Sep 1996 | A |
| 5562966 | Clarke et al. | Oct 1996 | A |
| 5582807 | Liao et al. | Dec 1996 | A |
| 5596973 | Grice | Jan 1997 | A |
| 5611896 | Swanepoel et al. | Mar 1997 | A |
| 5630322 | Heilmann et al. | May 1997 | A |
| 5652304 | Calderon et al. | Jul 1997 | A |
| 5714644 | Irgang et al. | Feb 1998 | A |
| 5723027 | Serole | Mar 1998 | A |
| 5723187 | Popoola et al. | Mar 1998 | A |
| 5726414 | Kitahashi et al. | Mar 1998 | A |
| 5733662 | Bogachek | Mar 1998 | A |
| 5749938 | Coombs | May 1998 | A |
| 5776359 | Schultz et al. | Jul 1998 | A |
| 5788738 | Pirzada et al. | Aug 1998 | A |
| 5804155 | Farrauto et al. | Sep 1998 | A |
| 5811187 | Anderson et al. | Sep 1998 | A |
| 5837959 | Muehlberger et al. | Nov 1998 | A |
| 5851507 | Pirzada et al. | Dec 1998 | A |
| 5853815 | Muehlberger | Dec 1998 | A |
| 5858470 | Bernecki et al. | Jan 1999 | A |
| 5884473 | Noda et al. | Mar 1999 | A |
| 5905000 | Yadav et al. | May 1999 | A |
| 5928806 | Olah et al. | Jul 1999 | A |
| 5935293 | Detering et al. | Aug 1999 | A |
| 5973289 | Read et al. | Oct 1999 | A |
| 5989648 | Phillips | Nov 1999 | A |
| 5993967 | Brotzman, Jr. et al. | Nov 1999 | A |
| 5993988 | Ohara et al. | Nov 1999 | A |
| 6004620 | Camm | Dec 1999 | A |
| 6012647 | Ruta et al. | Jan 2000 | A |
| 6033781 | Brotzman, Jr. et al. | Mar 2000 | A |
| 6045765 | Nakatsuji et al. | Apr 2000 | A |
| 6059853 | Coombs | May 2000 | A |
| 6066587 | Kurokawa et al. | May 2000 | A |
| 6084197 | Fusaro, Jr. | Jul 2000 | A |
| 6093306 | Hanrahan et al. | Jul 2000 | A |
| 6093378 | Deeba et al. | Jul 2000 | A |
| 6102106 | Manning et al. | Aug 2000 | A |
| 6117376 | Merkel | Sep 2000 | A |
| 6140539 | Sander et al. | Oct 2000 | A |
| 6168694 | Huang et al. | Jan 2001 | B1 |
| 6190627 | Hoke et al. | Feb 2001 | B1 |
| 6213049 | Yang | Apr 2001 | B1 |
| 6214195 | Yadav et al. | Apr 2001 | B1 |
| 6228904 | Yadav et al. | May 2001 | B1 |
| 6254940 | Pratsinis et al. | Jul 2001 | B1 |
| 6261484 | Phillips et al. | Jul 2001 | B1 |
| 6267864 | Yadav et al. | Jul 2001 | B1 |
| 6322756 | Arno et al. | Nov 2001 | B1 |
| 6342465 | Klein et al. | Jan 2002 | B1 |
| 6344271 | Yadav et al. | Feb 2002 | B1 |
| 6362449 | Hadidi et al. | Mar 2002 | B1 |
| 6379419 | Celik et al. | Apr 2002 | B1 |
| 6387560 | Yadav et al. | May 2002 | B1 |
| 6395214 | Kear et al. | May 2002 | B1 |
| 6398843 | Tarrant | Jun 2002 | B1 |
| 6399030 | Nolan | Jun 2002 | B1 |
| 6409851 | Sethuram et al. | Jun 2002 | B1 |
| 6413781 | Geis et al. | Jul 2002 | B1 |
| 6416818 | Aikens et al. | Jul 2002 | B1 |
| RE37853 | Detering et al. | Sep 2002 | E |
| 6444009 | Liu et al. | Sep 2002 | B1 |
| 6475951 | Domesle et al. | Nov 2002 | B1 |
| 6488904 | Cox et al. | Dec 2002 | B1 |
| 6491423 | Skibo et al. | Dec 2002 | B1 |
| 6506995 | Fusaro, Jr. et al. | Jan 2003 | B1 |
| 6517800 | Cheng et al. | Feb 2003 | B1 |
| 6524662 | Jang et al. | Feb 2003 | B2 |
| 6531704 | Yadav et al. | Mar 2003 | B2 |
| 6548445 | Buysch et al. | Apr 2003 | B1 |
| 6554609 | Yadav et al. | Apr 2003 | B2 |
| 6562304 | Mizrahi | May 2003 | B1 |
| 6562495 | Yadav et al. | May 2003 | B2 |
| 6569393 | Hoke et al. | May 2003 | B1 |
| 6569397 | Yadav et al. | May 2003 | B1 |
| 6569518 | Yadav et al. | May 2003 | B2 |
| 6572672 | Yadav et al. | Jun 2003 | B2 |
| 6579446 | Teran et al. | Jun 2003 | B1 |
| 6596187 | Coll et al. | Jul 2003 | B2 |
| 6603038 | Hagemeyer et al. | Aug 2003 | B1 |
| 6607821 | Yadav et al. | Aug 2003 | B2 |
| 6610355 | Yadav et al. | Aug 2003 | B2 |
| 6623559 | Huang | Sep 2003 | B2 |
| 6635357 | Moxson et al. | Oct 2003 | B2 |
| 6641775 | Vigliotti et al. | Nov 2003 | B2 |
| 6652822 | Phillips et al. | Nov 2003 | B2 |
| 6652967 | Yadav et al. | Nov 2003 | B2 |
| 6669823 | Sarkas et al. | Dec 2003 | B1 |
| 6682002 | Kyotani | Jan 2004 | B2 |
| 6689192 | Phillips et al. | Feb 2004 | B1 |
| 6699398 | Kim | Mar 2004 | B1 |
| 6706097 | Zomes | Mar 2004 | B2 |
| 6706660 | Park | Mar 2004 | B2 |
| 6710207 | Bogan, Jr. et al. | Mar 2004 | B2 |
| 6713176 | Yadav et al. | Mar 2004 | B2 |
| 6716525 | Yadav et al. | Apr 2004 | B1 |
| 6744006 | Johnson et al. | Jun 2004 | B2 |
| 6746791 | Yadav et al. | Jun 2004 | B2 |
| 6772584 | Chun et al. | Aug 2004 | B2 |
| 6786950 | Yadav et al. | Sep 2004 | B2 |
| 6813931 | Yadav et al. | Nov 2004 | B2 |
| 6817388 | Tsangaris et al. | Nov 2004 | B2 |
| 6832735 | Yadav et al. | Dec 2004 | B2 |
| 6838072 | Kong et al. | Jan 2005 | B1 |
| 6841509 | Hwang et al. | Jan 2005 | B1 |
| 6855410 | Buckley | Feb 2005 | B2 |
| 6855426 | Yadav | Feb 2005 | B2 |
| 6855749 | Yadav et al. | Feb 2005 | B1 |
| 6858170 | Van Thillo et al. | Feb 2005 | B2 |
| 6886545 | Holm | May 2005 | B1 |
| 6891319 | Dean et al. | May 2005 | B2 |
| 6896958 | Cayton et al. | May 2005 | B1 |
| 6902699 | Fritzemeier et al. | Jun 2005 | B2 |
| 6916872 | Yadav et al. | Jul 2005 | B2 |
| 6919065 | Zhou et al. | Jul 2005 | B2 |
| 6919527 | Boulos et al. | Jul 2005 | B2 |
| 6933331 | Yadav et al. | Aug 2005 | B2 |
| 6972115 | Ballard | Dec 2005 | B1 |
| 6986877 | Takikawa et al. | Jan 2006 | B2 |
| 6994837 | Boulos et al. | Feb 2006 | B2 |
| 7007872 | Yadav et al. | Mar 2006 | B2 |
| 7022305 | Drumm et al. | Apr 2006 | B2 |
| 7052777 | Brotzman, Jr. et al. | May 2006 | B2 |
| 7073559 | O'Larey et al. | Jul 2006 | B2 |
| 7074364 | Jähn et al. | Jul 2006 | B2 |
| 7081267 | Yadav | Jul 2006 | B2 |
| 7101819 | Rosenflanz et al. | Sep 2006 | B2 |
| 7147544 | Rosenflanz | Dec 2006 | B2 |
| 7147894 | Zhou et al. | Dec 2006 | B2 |
| 7166198 | Van Der Walt et al. | Jan 2007 | B2 |
| 7166663 | Cayton et al. | Jan 2007 | B2 |
| 7172649 | Conrad et al. | Feb 2007 | B2 |
| 7172790 | Koulik et al. | Feb 2007 | B2 |
| 7178747 | Yadav et al. | Feb 2007 | B2 |
| 7208126 | Musick et al. | Apr 2007 | B2 |
| 7211236 | Stark et al. | May 2007 | B2 |
| 7217407 | Zhang | May 2007 | B2 |
| 7220398 | Sutorik et al. | May 2007 | B2 |
| 7255498 | Bush et al. | Aug 2007 | B2 |
| 7265076 | Taguchi et al. | Sep 2007 | B2 |
| 7282167 | Carpenter | Oct 2007 | B2 |
| 7307195 | Polverejan et al. | Dec 2007 | B2 |
| 7323655 | Kim | Jan 2008 | B2 |
| 7384447 | Kodas et al. | Jun 2008 | B2 |
| 7402899 | Whiting et al. | Jul 2008 | B1 |
| 7417008 | Richards et al. | Aug 2008 | B2 |
| 7494527 | Jurewicz et al. | Feb 2009 | B2 |
| 7507495 | Wang et al. | Mar 2009 | B2 |
| 7517826 | Fujdala et al. | Apr 2009 | B2 |
| 7534738 | Fujdala et al. | May 2009 | B2 |
| 7541012 | Yeung et al. | Jun 2009 | B2 |
| 7541310 | Espinoza et al. | Jun 2009 | B2 |
| 7557324 | Nylen et al. | Jul 2009 | B2 |
| 7572315 | Boulos et al. | Aug 2009 | B2 |
| 7576029 | Saito et al. | Aug 2009 | B2 |
| 7576031 | Beutel et al. | Aug 2009 | B2 |
| 7604843 | Robinson et al. | Oct 2009 | B1 |
| 7611686 | Alekseeva et al. | Nov 2009 | B2 |
| 7615097 | McKeclutie et al. | Nov 2009 | B2 |
| 7618919 | Shimazu et al. | Nov 2009 | B2 |
| 7622693 | Foret | Nov 2009 | B2 |
| 7632775 | Zhou et al. | Dec 2009 | B2 |
| 7635218 | Lott | Dec 2009 | B1 |
| 7674744 | Shiratori et al. | Mar 2010 | B2 |
| 7678419 | Kevwitch et al. | Mar 2010 | B2 |
| 7704369 | Olah et al. | Apr 2010 | B2 |
| 7709411 | Zhou et al. | May 2010 | B2 |
| 7709414 | Fujdala et al. | May 2010 | B2 |
| 7745367 | Fujdala et al. | Jun 2010 | B2 |
| 7750265 | Belashchenko et al. | Jul 2010 | B2 |
| 7759279 | Shiratori et al. | Jul 2010 | B2 |
| 7759281 | Kezuka et al. | Jul 2010 | B2 |
| 7803210 | Sekine et al. | Sep 2010 | B2 |
| 7842515 | Zou et al. | Nov 2010 | B2 |
| 7851405 | Wakamatsu et al. | Dec 2010 | B2 |
| 7874239 | Howland | Jan 2011 | B2 |
| 7875573 | Beutel et al. | Jan 2011 | B2 |
| 7897127 | Layman et al. | Mar 2011 | B2 |
| 7902104 | Kalck et al. | Mar 2011 | B2 |
| 7905942 | Layman | Mar 2011 | B1 |
| 7935655 | Tolmachev | May 2011 | B2 |
| 8003020 | Jankowiak et al. | Aug 2011 | B2 |
| 8051724 | Layman et al. | Nov 2011 | B1 |
| 8076258 | Biberger | Dec 2011 | B1 |
| 8080494 | Yasuda et al. | Dec 2011 | B2 |
| 8089495 | Keller | Jan 2012 | B2 |
| 8129654 | Lee et al. | Mar 2012 | B2 |
| 8142619 | Layman et al. | Mar 2012 | B2 |
| 8168561 | Virkar | May 2012 | B2 |
| 8173572 | Feaviour | May 2012 | B2 |
| 8211392 | Grubert et al. | Jul 2012 | B2 |
| 8258070 | Fujdala et al. | Sep 2012 | B2 |
| 8278240 | Tange et al. | Oct 2012 | B2 |
| 8294060 | Mohanty et al. | Oct 2012 | B2 |
| 8309489 | Roldan Cuenya et al. | Nov 2012 | B2 |
| 8349761 | Xia et al. | Jan 2013 | B2 |
| 8404611 | Nakamura et al. | Mar 2013 | B2 |
| 8524631 | Biberger | Sep 2013 | B2 |
| 8557727 | Yin et al. | Oct 2013 | B2 |
| 8574408 | Layman | Nov 2013 | B2 |
| 8574520 | Koplin et al. | Nov 2013 | B2 |
| 8652992 | Yin et al. | Feb 2014 | B2 |
| 8669202 | van den Hoek et al. | Mar 2014 | B2 |
| 8679433 | Yin et al. | Mar 2014 | B2 |
| 20010004009 | MacKelvie | Jun 2001 | A1 |
| 20010042802 | Youds | Nov 2001 | A1 |
| 20010055554 | Hoke et al. | Dec 2001 | A1 |
| 20020018815 | Sievers et al. | Feb 2002 | A1 |
| 20020068026 | Murrell et al. | Jun 2002 | A1 |
| 20020071800 | Hoke et al. | Jun 2002 | A1 |
| 20020079620 | DuBuis et al. | Jun 2002 | A1 |
| 20020100751 | Carr | Aug 2002 | A1 |
| 20020102674 | Anderson | Aug 2002 | A1 |
| 20020131914 | Sung | Sep 2002 | A1 |
| 20020143417 | Ito et al. | Oct 2002 | A1 |
| 20020168466 | Tapphorn et al. | Nov 2002 | A1 |
| 20020182735 | Kibby et al. | Dec 2002 | A1 |
| 20020183191 | Faber et al. | Dec 2002 | A1 |
| 20020192129 | Shamouilian et al. | Dec 2002 | A1 |
| 20030036786 | Duren et al. | Feb 2003 | A1 |
| 20030042232 | Shimazu | Mar 2003 | A1 |
| 20030047617 | Shanmugham et al. | Mar 2003 | A1 |
| 20030066800 | Saim et al. | Apr 2003 | A1 |
| 20030085663 | Horsky | May 2003 | A1 |
| 20030102099 | Yadav et al. | Jun 2003 | A1 |
| 20030108459 | Wu et al. | Jun 2003 | A1 |
| 20030110931 | Aghajanian et al. | Jun 2003 | A1 |
| 20030129098 | Endo et al. | Jul 2003 | A1 |
| 20030139288 | Cai et al. | Jul 2003 | A1 |
| 20030143153 | Boulos et al. | Jul 2003 | A1 |
| 20030172772 | Sethuram et al. | Sep 2003 | A1 |
| 20030223546 | McGregor et al. | Dec 2003 | A1 |
| 20040009118 | Phillips et al. | Jan 2004 | A1 |
| 20040023302 | Archibald et al. | Feb 2004 | A1 |
| 20040023453 | Xu et al. | Feb 2004 | A1 |
| 20040077494 | LaBarge et al. | Apr 2004 | A1 |
| 20040103751 | Joseph et al. | Jun 2004 | A1 |
| 20040109523 | Singh et al. | Jun 2004 | A1 |
| 20040119064 | Narayan et al. | Jun 2004 | A1 |
| 20040127586 | Jin et al. | Jul 2004 | A1 |
| 20040129222 | Nylen et al. | Jul 2004 | A1 |
| 20040166036 | Chen et al. | Aug 2004 | A1 |
| 20040167009 | Kuntz et al. | Aug 2004 | A1 |
| 20040176246 | Shirk et al. | Sep 2004 | A1 |
| 20040208805 | Fincke et al. | Oct 2004 | A1 |
| 20040213998 | Hearley et al. | Oct 2004 | A1 |
| 20040235657 | Xiao et al. | Nov 2004 | A1 |
| 20040238345 | Koulik et al. | Dec 2004 | A1 |
| 20040251017 | Pillion et al. | Dec 2004 | A1 |
| 20040251241 | Blutke et al. | Dec 2004 | A1 |
| 20050000321 | O'Larey et al. | Jan 2005 | A1 |
| 20050000950 | Schroder et al. | Jan 2005 | A1 |
| 20050058797 | Sen et al. | Mar 2005 | A1 |
| 20050066805 | Park et al. | Mar 2005 | A1 |
| 20050070431 | Alvin et al. | Mar 2005 | A1 |
| 20050077034 | King | Apr 2005 | A1 |
| 20050097988 | Kodas et al. | May 2005 | A1 |
| 20050106865 | Chung et al. | May 2005 | A1 |
| 20050133121 | Subramanian et al. | Jun 2005 | A1 |
| 20050153069 | Tapphorn et al. | Jul 2005 | A1 |
| 20050163673 | Johnson et al. | Jul 2005 | A1 |
| 20050199739 | Kuroda et al. | Sep 2005 | A1 |
| 20050211018 | Jurewicz et al. | Sep 2005 | A1 |
| 20050220695 | Abatzoglou et al. | Oct 2005 | A1 |
| 20050227864 | Sutorik et al. | Oct 2005 | A1 |
| 20050233380 | Pesiri et al. | Oct 2005 | A1 |
| 20050240069 | Polverejan et al. | Oct 2005 | A1 |
| 20050258766 | Kim | Nov 2005 | A1 |
| 20050274646 | Lawson et al. | Dec 2005 | A1 |
| 20050275143 | Toth | Dec 2005 | A1 |
| 20060043651 | Yamamoto et al. | Mar 2006 | A1 |
| 20060051505 | Kortshagen et al. | Mar 2006 | A1 |
| 20060068989 | Ninomiya et al. | Mar 2006 | A1 |
| 20060094595 | Labarge | May 2006 | A1 |
| 20060096393 | Pesiri | May 2006 | A1 |
| 20060105910 | Zhou et al. | May 2006 | A1 |
| 20060108332 | Belashchenko | May 2006 | A1 |
| 20060153728 | Schoenung et al. | Jul 2006 | A1 |
| 20060153765 | Pham-Huu et al. | Jul 2006 | A1 |
| 20060159596 | De La Veaux et al. | Jul 2006 | A1 |
| 20060166809 | Malek et al. | Jul 2006 | A1 |
| 20060211569 | Dang et al. | Sep 2006 | A1 |
| 20060213326 | Gollob et al. | Sep 2006 | A1 |
| 20060222780 | Gurevich et al. | Oct 2006 | A1 |
| 20060231525 | Asakawa et al. | Oct 2006 | A1 |
| 20070020167 | Han et al. | Jan 2007 | A1 |
| 20070044513 | Kear et al. | Mar 2007 | A1 |
| 20070048206 | Hung et al. | Mar 2007 | A1 |
| 20070049484 | Kear et al. | Mar 2007 | A1 |
| 20070063364 | Hsiao et al. | Mar 2007 | A1 |
| 20070084308 | Nakamura et al. | Apr 2007 | A1 |
| 20070084834 | Hanus et al. | Apr 2007 | A1 |
| 20070087934 | Martens et al. | Apr 2007 | A1 |
| 20070092768 | Lee et al. | Apr 2007 | A1 |
| 20070153390 | Nakamura et al. | Jul 2007 | A1 |
| 20070161506 | Saito et al. | Jul 2007 | A1 |
| 20070163385 | Takahashi et al. | Jul 2007 | A1 |
| 20070172721 | Pak et al. | Jul 2007 | A1 |
| 20070173403 | Koike et al. | Jul 2007 | A1 |
| 20070178673 | Gole et al. | Aug 2007 | A1 |
| 20070221404 | Das et al. | Sep 2007 | A1 |
| 20070253874 | Foret | Nov 2007 | A1 |
| 20070266825 | Ripley et al. | Nov 2007 | A1 |
| 20070292321 | Plischke et al. | Dec 2007 | A1 |
| 20080006954 | Yubuta et al. | Jan 2008 | A1 |
| 20080026041 | Tepper et al. | Jan 2008 | A1 |
| 20080031806 | Gavenonis et al. | Feb 2008 | A1 |
| 20080038578 | Li | Feb 2008 | A1 |
| 20080045405 | Beutel et al. | Feb 2008 | A1 |
| 20080047261 | Han et al. | Feb 2008 | A1 |
| 20080057212 | Dorier et al. | Mar 2008 | A1 |
| 20080064769 | Sato et al. | Mar 2008 | A1 |
| 20080104735 | Howland | May 2008 | A1 |
| 20080105083 | Nakamura et al. | May 2008 | A1 |
| 20080116178 | Weidman | May 2008 | A1 |
| 20080125308 | Fujdala et al. | May 2008 | A1 |
| 20080125313 | Fujdala et al. | May 2008 | A1 |
| 20080138651 | Doi et al. | Jun 2008 | A1 |
| 20080175936 | Tokita et al. | Jul 2008 | A1 |
| 20080187714 | Wakamatsu et al. | Aug 2008 | A1 |
| 20080206562 | Stucky et al. | Aug 2008 | A1 |
| 20080207858 | Kowaleski et al. | Aug 2008 | A1 |
| 20080248704 | Mathis et al. | Oct 2008 | A1 |
| 20080274344 | Vieth et al. | Nov 2008 | A1 |
| 20080277092 | Layman et al. | Nov 2008 | A1 |
| 20080277264 | Sprague | Nov 2008 | A1 |
| 20080277266 | Layman | Nov 2008 | A1 |
| 20080277267 | Biberger | Nov 2008 | A1 |
| 20080277268 | Layman | Nov 2008 | A1 |
| 20080277269 | Layman et al. | Nov 2008 | A1 |
| 20080277270 | Biberger et al. | Nov 2008 | A1 |
| 20080277271 | Layman | Nov 2008 | A1 |
| 20080280049 | Kevwitch et al. | Nov 2008 | A1 |
| 20080280751 | Harutyunyan et al. | Nov 2008 | A1 |
| 20080280756 | Biberger | Nov 2008 | A1 |
| 20080283411 | Eastman et al. | Nov 2008 | A1 |
| 20080283498 | Yamazaki | Nov 2008 | A1 |
| 20080307960 | Hendrickson et al. | Dec 2008 | A1 |
| 20090010801 | Murphy et al. | Jan 2009 | A1 |
| 20090018008 | Jankowiak et al. | Jan 2009 | A1 |
| 20090054230 | Veeraraghavan et al. | Feb 2009 | A1 |
| 20090081092 | Yang et al. | Mar 2009 | A1 |
| 20090088585 | Schammel et al. | Apr 2009 | A1 |
| 20090092887 | McGrath et al. | Apr 2009 | A1 |
| 20090098402 | Kang et al. | Apr 2009 | A1 |
| 20090114568 | Trevino et al. | May 2009 | A1 |
| 20090162991 | Beneyton et al. | Jun 2009 | A1 |
| 20090168506 | Han et al. | Jul 2009 | A1 |
| 20090170242 | Lin et al. | Jul 2009 | A1 |
| 20090181474 | Nagai | Jul 2009 | A1 |
| 20090200180 | Capote et al. | Aug 2009 | A1 |
| 20090208367 | Calio et al. | Aug 2009 | A1 |
| 20090209408 | Kitamura et al. | Aug 2009 | A1 |
| 20090223410 | Jun et al. | Sep 2009 | A1 |
| 20090253037 | Park et al. | Oct 2009 | A1 |
| 20090274897 | Kaner et al. | Nov 2009 | A1 |
| 20090274903 | Addiego | Nov 2009 | A1 |
| 20090286899 | Hofmann et al. | Nov 2009 | A1 |
| 20090320449 | Beutel et al. | Dec 2009 | A1 |
| 20090324468 | Golden et al. | Dec 2009 | A1 |
| 20100050868 | Kuznicki et al. | Mar 2010 | A1 |
| 20100089002 | Merkel | Apr 2010 | A1 |
| 20100092358 | Koegel et al. | Apr 2010 | A1 |
| 20100124514 | Chelluri et al. | May 2010 | A1 |
| 20100166629 | Deeba | Jul 2010 | A1 |
| 20100180581 | Grubert et al. | Jul 2010 | A1 |
| 20100180582 | Mueller-Stach et al. | Jul 2010 | A1 |
| 20100186375 | Kazi et al. | Jul 2010 | A1 |
| 20100240525 | Golden et al. | Sep 2010 | A1 |
| 20100275781 | Tsangaris | Nov 2010 | A1 |
| 20100323118 | Mohanty et al. | Dec 2010 | A1 |
| 20110006463 | Layman | Jan 2011 | A1 |
| 20110030346 | Neubauer et al. | Feb 2011 | A1 |
| 20110049045 | Hurt et al. | Mar 2011 | A1 |
| 20110052467 | Chase et al. | Mar 2011 | A1 |
| 20110143041 | Layman et al. | Jun 2011 | A1 |
| 20110143915 | Yin et al. | Jun 2011 | A1 |
| 20110143916 | Leamon | Jun 2011 | A1 |
| 20110143926 | Yin et al. | Jun 2011 | A1 |
| 20110143930 | Yin et al. | Jun 2011 | A1 |
| 20110143933 | Yin et al. | Jun 2011 | A1 |
| 20110144382 | Yin et al. | Jun 2011 | A1 |
| 20110152550 | Grey et al. | Jun 2011 | A1 |
| 20110158871 | Arnold et al. | Jun 2011 | A1 |
| 20110174604 | Duesel et al. | Jul 2011 | A1 |
| 20110243808 | Fossey et al. | Oct 2011 | A1 |
| 20110245073 | Oljaca et al. | Oct 2011 | A1 |
| 20110247336 | Farsad et al. | Oct 2011 | A9 |
| 20110305612 | Müller-Stach et al. | Dec 2011 | A1 |
| 20120023909 | Lambert et al. | Feb 2012 | A1 |
| 20120045373 | Biberger | Feb 2012 | A1 |
| 20120063963 | Watanabe et al. | Mar 2012 | A1 |
| 20120097033 | Arnold et al. | Apr 2012 | A1 |
| 20120122660 | Andersen et al. | May 2012 | A1 |
| 20120124974 | Li et al. | May 2012 | A1 |
| 20120171098 | Hung et al. | Jul 2012 | A1 |
| 20120214666 | van den Hoek et al. | Aug 2012 | A1 |
| 20120263633 | Koplin et al. | Oct 2012 | A1 |
| 20120308467 | Carpenter et al. | Dec 2012 | A1 |
| 20120313269 | Kear et al. | Dec 2012 | A1 |
| 20130034472 | Cantrell et al. | Feb 2013 | A1 |
| 20130079216 | Biberger et al. | Mar 2013 | A1 |
| 20130125970 | Ko et al. | May 2013 | A1 |
| 20130213018 | Yin et al. | Aug 2013 | A1 |
| 20130280528 | Biberger | Oct 2013 | A1 |
| 20130281288 | Biberger et al. | Oct 2013 | A1 |
| 20130294989 | Koch et al. | Nov 2013 | A1 |
| 20130316896 | Biberger | Nov 2013 | A1 |
| 20130331257 | Barcikowski et al. | Dec 2013 | A1 |
| 20130345047 | Biberger et al. | Dec 2013 | A1 |
| 20140018230 | Yin et al. | Jan 2014 | A1 |
| 20140120355 | Biberger | May 2014 | A1 |
| 20140128245 | Yin et al. | May 2014 | A1 |
| 20140140909 | Qi et al. | May 2014 | A1 |
| 20140148331 | Biberger et al. | May 2014 | A1 |
| 20140161693 | Brown et al. | Jun 2014 | A1 |
| 20140209451 | Biberger et al. | Jul 2014 | A1 |
| 20140228201 | Mendoza Gómez et al. | Aug 2014 | A1 |
| 20140243187 | Yin et al. | Aug 2014 | A1 |
| 20140252270 | Lehman, Jr. | Sep 2014 | A1 |
| 20140263190 | Biberger et al. | Sep 2014 | A1 |
| 20140318318 | Layman et al. | Oct 2014 | A1 |
| 20140338519 | Biberger | Nov 2014 | A1 |
| Number | Date | Country |
|---|---|---|
| 101301610 | Nov 2008 | CN |
| 34 45 273 | Jun 1986 | DE |
| 0 347 386 | Dec 1989 | EP |
| 0 385 742 | Sep 1990 | EP |
| 1 134 302 | Sep 2001 | EP |
| 1 256 378 | Nov 2002 | EP |
| 1 619 168 | Jan 2006 | EP |
| 1 790 612 | May 2007 | EP |
| 1 955 765 | Aug 2008 | EP |
| 1 307 941 | Feb 1973 | GB |
| 49-31571 | Mar 1974 | JP |
| 56-146804 | Nov 1981 | JP |
| 61-086815 | May 1986 | JP |
| 62-102827 | May 1987 | JP |
| 63-214342 | Sep 1988 | JP |
| 1-164795 | Jun 1989 | JP |
| 2-6339 | Jan 1990 | JP |
| 3-226509 | Oct 1991 | JP |
| 5-193909 | Aug 1993 | JP |
| 05-228361 | Sep 1993 | JP |
| 05-324094 | Dec 1993 | JP |
| 6-93309 | Apr 1994 | JP |
| 6-135797 | May 1994 | JP |
| 6-172820 | Jun 1994 | JP |
| 6-272012 | Sep 1994 | JP |
| H6-065772 | Sep 1994 | JP |
| 07-031873 | Feb 1995 | JP |
| 7-138020 | May 1995 | JP |
| 7-207381 | Aug 1995 | JP |
| 07-256116 | Oct 1995 | JP |
| 8-158033 | Jun 1996 | JP |
| 8-215576 | Aug 1996 | JP |
| 8-217420 | Aug 1996 | JP |
| 9-141087 | Jun 1997 | JP |
| 10-130810 | May 1998 | JP |
| 10-249198 | Sep 1998 | JP |
| 11-502760 | Mar 1999 | JP |
| 2000-220978 | Aug 2000 | JP |
| 2002-88486 | Mar 2002 | JP |
| 2002-241812 | Aug 2002 | JP |
| 2002-336688 | Nov 2002 | JP |
| 2003-126694 | May 2003 | JP |
| 2004-233007 | Aug 2004 | JP |
| 2004-249206 | Sep 2004 | JP |
| 2004-290730 | Oct 2004 | JP |
| 2005-503250 | Feb 2005 | JP |
| 2005-122621 | May 2005 | JP |
| 2005-218937 | Aug 2005 | JP |
| 2005-342615 | Dec 2005 | JP |
| 2006-001779 | Jan 2006 | JP |
| 2006-508885 | Mar 2006 | JP |
| 2006-87965 | Apr 2006 | JP |
| 2006-247446 | Sep 2006 | JP |
| 2006-260385 | Sep 2006 | JP |
| 2006-326554 | Dec 2006 | JP |
| 2007-29859 | Feb 2007 | JP |
| 2007-44585 | Feb 2007 | JP |
| 2007-46162 | Feb 2007 | JP |
| 2007-138287 | Jun 2007 | JP |
| 2007-203129 | Aug 2007 | JP |
| 493241 | Mar 1976 | SU |
| 200611449 | Apr 2006 | TW |
| 201023207 | Jun 2010 | TW |
| WO-9628577 | Sep 1996 | WO |
| WO-0072965 | Dec 2000 | WO |
| WO-02092503 | Nov 2002 | WO |
| WO-03094195 | Nov 2003 | WO |
| WO-2004052778 | Jun 2004 | WO |
| WO-2005063390 | Jul 2005 | WO |
| WO 2006079213 | Aug 2006 | WO |
| WO-2006096205 | Sep 2006 | WO |
| WO-2007144447 | Dec 2007 | WO |
| WO-2008092478 | Aug 2008 | WO |
| WO-2008130451 | Oct 2008 | WO |
| WO-2008130451 | Oct 2008 | WO |
| WO-2009017479 | Feb 2009 | WO |
| WO-2011081833 | Jul 2011 | WO |
| WO-2012028695 | Mar 2012 | WO |
| WO-2013028575 | Feb 2013 | WO |
| WO-2013093597 | Jun 2013 | WO |
| WO-2013151557 | Oct 2013 | WO |
| Entry |
|---|
| Babin, A. et al. (1985). “Solvents Used in the Arts,” Center for Safety in the Arts: 16 pages. |
| Bateman, J. E. et al. (Dec. 17, 1998). “Alkylation of Porous Silicon by Direct Reaction with Alkenes and Alkynes,” Angew. Chem Int. Ed. 37(19):2683-2685. |
| Carrot, G. et al. (Sep. 17, 2002). “Surface-Initiated Ring-Opening Polymerization: A Versatile Method for Nanoparticle Ordering,” Macromolecules 35(22):8400-8404. |
| Chaim, R. et al. (2009). “Densification of Nanocrystalline Y2O3 Ceramic Powder by Spark Plasma Sintering,” Journal of European Ceramic Society 29: 91-98. |
| Chen, H.-S. et al. (Jul. 3, 2001). “On the Photoluminescence of Si Nanoparticles,” Mater. Phys. Mech. 4:62-66. |
| Chen, W.-J. et al. (Mar. 18, 2008). “Functional Fe3O4/TiO2 Core/Shell Magnetic Nanoparticles as Photokilling Agents for Pathogenic Bacteria,” Small 4(4): 485-491. |
| Das, N. et al. (2001). “Influence of the Metal Function in the “One-Pot” Synthesis of 4-Methyl-2-Pentanone (Methyl Isobutyl Ketone) from Acetone Over Palladium Supported on Mg(Al)O Mixed Oxides Catalysts,” Catalysis Letters 71(3-4): 181-185. |
| Faber, K. T. et al. (Sep. 1988). “Toughening by Stress-Induced Microcracking in Two-Phase Ceramics,” Journal of the American Ceramic Society 71: C-399-C401. |
| Fauchais, P. et al. (Jun. 1989). “La Projection Par Plasma: Une Revue,” Ann. Phys. Fr. 14(3):261-310. |
| Fauchais, P. et al. (Jan. 1993). “Les Dépôts Par Plasma Thermique ” Revue Générale De L'Electricité, RGE, Paris, France, No. 2, pp. 7-12 (in French). |
| Fauchais, P. et al. (Jan. 1996). “Plasma Spray: Study of the Coating Generation,” Ceramics International 22(4):295-303. |
| Fojtik, A. et al. (Apr. 29, 1994). “Luminescent Colloidal Silicon Particles,”Chemical Physics Letters 221 :363-367. |
| Fojtik, A. (Jan. 13, 2006). “Surface Chemistry of Luminescent Colloidal Silicon Nanoparticles,” J. Phys. Chem. B. 110(5):1994-1998. |
| Gangeri, M. et al. (2009). “Fe and Pt Carbon Nanotubes for the Electrocatalytic Conversion of Carbon Dioxide to Oxygenates,” Catalysis Today 143: 57-63. |
| Gutsch, A. et al. (2002). “Gas-Phase Production of Nanoparticles,” Kona No. 20, pp. 24-37. |
| Han, B. Q. et al. (Jan. 2004). “Deformation Mechanisms and Ductility of Nanostructured Al Alloys”, Mat. Res. Soc. Symp. Proc. 821:P9.1.1-P9.1.6. |
| Heberlein, J. (2002). “New Approaches in Thermal Plasma Technology”, Pure Appl. Chem. 74(3):327-335. |
| Hua, F. et al. (Mar. 2006). “Organically Capped Silicon Nanoparticles With Blue Photoluminescence Prepared by Hydrosilylation Followed by Oxidation,” Langmuir 22(9):4363-4370. |
| Ji, Y. et al. (Nov. 2002) “Processing and Mechanical Properties of Al2O3—5 vol.% Cr Nanocomposites,” Journal of the European Ceramic Society 22(12):1927-1936. |
| Jouet, R. J. et al. (Jan. 25, 2005). “Surface Passivation of Bare Aluminum Nanoparticles Using Perfluoroalkyl Carboxylic Acids,” Chem. Mater.17(11):2987-2996. |
| Kenvin, J. C. et al. (1992). “Supported Catalysts Prepared from Mononuclear Copper Complexes: Catalytic Properties”, J. Catalysis 135:81-91. |
| Konrad, H. et al. (1996). “Nanostructured Cu—Bi Alloys Prepared by Co-Evaporation in a Continuous Gas Flow,” NanoStructured Materials 7(6):605-610. |
| Kim, N. Y. et al. (Mar. 5, 1997). “Thermal Derivatization of Porous Silicon with Alcohols,” J. Am. Chem. Soc. 119(9):2297-2298. |
| Kwon, Y.-S. et al. (Apr. 30, 2003). “Passivation Process for Superfine Aluminum Powders Obtained by Electrical Explosion of Wires,” Applied Surface Science 211:57-67. |
| Lakis, R. E. et al. (1995). “Alumina-Supported Pt—Rh Catalysts: I. Microstructural Characterization,” Journal of Catalysis 154: 261-275. |
| Langner, A. et al. (Aug. 25, 2005). “Controlled Silicon Surface Functionalization by Alkene Hydrosilylation,” J. Am. Chem. Soc. 127(37):12798-12799. |
| Li, D. et al. (Apr. 9, 2005). “Environmentally Responsive “Hairy” Nanoparticles: Mixed Homopolymer Brushes on Silica Nanoparticles Synthesized by Living Radical Polymerization Techniques,” J. Am. Chem. Soc. 127(7):6248-6256. |
| Li, X. et al. (May 25, 2004). “Surface Functionalization of Silicon Nanoparticles Produced by Laser-Driven Pyrolysis of Silane Followed by HF-HNO3 Etching,” Langmuir 20(11):4720-4727. |
| Liao, Y.-C. et al. (Jun. 27, 2006). “Self-Assembly of Organic Monolayers on Aerosolized Silicon Nanoparticles,” J.Am. Chem. Soc. 128(28):9061-9065. |
| Liu, S.-M. et al. (Jan. 13, 2006). “Enhanced Photoluminescence from Si Nano-Organosols by Functionalization With Alkenes And Their Size Evolution,” Chem. Mater. 18(3):637-642. |
| Luo, J. et al. (2008). “Core/Shell Nanoparticles as Electrocatalysts for Fuel Cell Reactions,” Advanced Materials 20: 4342-4347. |
| Mignard, D. et al. (2003). “Methanol Synthesis from Flue-Gas CO2 and Renewable Electricity: A Feasibility Study,” International Journal of Hydrogen Energy 28: 455-464. |
| Mühlenweg, H. et al. (2004). “Gas-Phase Reactions—Open Up New Roads to Nanoproducts,” Degussa ScienceNewsletter No. 08, pp. 12-16. |
| Nagai, Y. et al. (Jul. 3, 2006). “Sintering Inhibition Mechanism of Platinum Supported on Ceria-Based Oxide and Pt—Oxide-Support Interaction,” J. Catalysis 242:103-109. |
| NASA (2009). “Enthalpy,” Article located at http://www.grc.nasa.gov/WWW/K-12/airplane/enthalpy.htrnl, published by National Aeronautics and Space Administration on Nov. 23, 2009, 1 page. |
| Neiner, D. (Aug. 5, 2006). “Low-Temperature Solution Route to Macroscopic Amounts of Hydrogen Terminated Silicon Nanoparticles,” J. Am. Chem. Soc. 128:11016-11017. |
| Netzer, L. et al. (1983). “A New Approach to Construction of Artificial Monolayer Assemblies,” J. Am. Chem. Soc. 105(3):674-676. |
| Park, H.-Y. et al. (May 30, 2007). “Fabrication of Magnetic Core@Shell Fe Oxide@Au Nanoparticles for Interfacial Bioactivity and Bio-Separation,” Langmuir 23: 9050-9056. |
| Park, N.-G. et al. (Feb. 17, 2004). “Morphological and Photoelectrochemical Characterization of Core-Shell Nanoparticle Films for Dye-Sensitized Solar Cells: Zn—O Type Shell on SnO2 and TiO2 Cores,” Langmuir 20: 4246-4253. |
| “Plasma Spray and Wire Flame Spray Product Group,” located at http://www.processmaterials.com/spray.html, published by Process Materials, Inc., last accessed Aug. 5, 2013, 2 pages. |
| “Platinum Group Metals: Annual Review 1996” (Oct. 1997). Engineering and Mining Journal, p. 63. |
| Rahaman, R. A. et al. (1995). “Synthesis of Powders,” in Ceramic Processing and Sintering. Marcel Decker, Inc., New York, pp. 71-77. |
| Sailor, M. J. (1997). “Surface Chemistry of Luminescent Silicon Nanocrystallites,” Adv. Mater. 9(10):783-793. |
| Schimpf, S. et al. (2002). “Supported Gold Nanoparticles: In-Depth Catalyst Characterization and Application in Hydrogenation and Oxidation Reactions,” Catalysis Today 2592: 1-16. |
| Stiles, A. B. (Jan. 1, 1987). “Manufacture of Carbon-Supported Metal Catalysts,” in Catalyst Supports and Supported Catalysts, Butterworth Publishers, MA, pp. 125-132. |
| Subramanian, S. et al. (1991). “Structure and Activity of Composite Oxide Supported Platinum—Iridium Catalysts,” Applied Catalysts 74: 65-81. |
| Tao, Y.-T. (May 1993). “Structural Comparison of Self-Assembled Monolayers of n-Alkanoic Acids on the surfaces of Silver, Copper, and Aluminum,” J. Am. Chem. Soc. 115(10):4350-4358. |
| Ünal, N. et al. (Nov. 2011). “Influence of WC Particles on the Microstructural and Mechanical Properties of 3 mol% Y2O3 Stabilized ZrO2 Matrix Composites Produced by Hot Pressing,” Journal of the European Ceramic Society (31)13: 2267-2275. |
| Viswanathan, V. et al. (2006). “Challenges and Advances in Nanocomposite Processing Techniques,” Materials Science and Engineering R 54: 121-285. |
| Vardelle, A. et al. (1996). “Coating Generation: Vaporization of Particles in Plasma Spraying and Splat Formation,” Universite de Limoges, 123 Avenue A. Thomas 87000, Limoges, France, Pure & Appl. Chem. 68(5):1093-1099. |
| Vardelle, M. et al. (Jun. 1991). “Experimental Investigation of Powder Vaporization in Thermal Plasma Jets,” Plasma Chemistry and Plasma Processing 11(2):185-201. |
| Yoshida, T. (1994). “The Future of Thermal Plasma Processing for Coating”, Pure & Appl. Chem. 66(6):1223-1230. |
| Zou, J. et al. (Jun. 4, 2004). “Solution Synthesis of Ultrastable Luminescent Siloxane-Coated Silicon Nanoparticles,” Nano Letters 4(7):1181-1186. |
| Non-Final Office Action mailed Mar. 7, 2014, for U.S. Appl. No. 12/968,253, filed Dec. 14, 2010, for Biberger, 15 pages. |
| International Search Report mailed Dec. 20, 2012, for PCT Patent Application No. PCT/US2012/025966, filed Feb. 21, 2012, published on Aug. 30, 2012, as WO-2012/115977; 3 pages. |
| Written Opinion mailed on Dec. 20, 2012, for PCT Patent Application No. PCT/US2012/025966, filed Feb. 21, 2012, published on Aug. 30, 2012, as WO-2012/115977; 4 pages. |
| International Preliminary Report on Patentability dated Aug. 27, 2013, for PCT Patent Application No. PCT/US2012/025966, filed Feb. 21, 2012, published on Aug. 30, 2012, as WO-2012/115977; 5 pages. |
| U.S. Appl. No. 13/291,983, filed Nov. 8, 2011, for Layman et al. |
| U.S. Appl. No. 12/152,084, filed May 9, 2008, for Biberger. |
| U.S. Appl. No. 13/028,693, filed Feb. 16, 2011, for Biberger. |
| U.S. Appl. No. 12/943,909, filed Nov. 10, 2010, for Layman. |
| U.S. Appl. No. 12/152,111, filed May 9, 2008, for Biberger et al. |
| U.S. Appl. No. 12/151,830, filed May 8, 2008, for Biberger et al. |
| U.S. Appl. No. 12/968,248, filed Dec. 14, 2010, for Biberger. |
| U.S. Appl. No. 12/968,245, filed Dec. 14, 2010, for Biberger. |
| U.S. Appl. No. 12/968,241, filed Dec. 14, 2010, for Biberger. |
| U.S. Appl. No. 12/968,239, filed Dec. 14, 2010, for Biberger. |
| U.S. Appl. No. 12/969,128, filed Dec. 15, 2010, for Biberger. |
| U.S. Appl. No. 12/962,463, filed Dec. 7, 2010, for Leaman. |
| U.S. Appl. No. 12/961,030, filed Dec. 6, 2010, for Lehman. |
| U.S. Appl. No. 12/961,108, filed Dec. 6, 2010, for Lehman. |
| U.S. Appl. No. 12/961,200, filed Dec. 6, 2010, for Lehman. |
| U.S. Appl. No. 12/968,253, filed Dec. 14, 2010, for Biberger. |
| U.S. Appl. No. 12/968,235, filed Dec. 14, 2010, for Biberger. |
| U.S. Appl. No. 12/969,306, filed Dec. 15, 2010, for Lehman et al. |
| U.S. Appl. No. 12/969,447, filed Dec. 15, 2010, for Biberger et al. |
| U.S. Appl. No. 12/969,087, filed Dec. 15, 2010, for Biberger. |
| U.S. Appl. No. 12/962,533, filed Dec. 7, 2010, for Yin et al. |
| U.S. Appl. No. 12/962,523, filed Dec. 7, 2010, for Yin et al. |
| U.S. Appl. No. 12/001,643, filed Dec. 11, 2007, for Biberger et al. |
| U.S. Appl. No. 12/474,081, filed May 28, 2009, for Biberger et al. |
| U.S. Appl. No. 12/001,602, filed Dec. 11, 2007, for Biberger et al. |
| U.S. Appl. No. 12/001,644, filed Dec. 11, 2007, for Biberger et al. |
| U.S. Appl. No. 12/969,457, filed Nov. 15, 2010, for Leamon et al. |
| U.S. Appl. No. 12/969,503, filed Nov. 15, 2010, for Leamon et al. |
| U.S. Appl. No. 12/954,813, filed Nov. 26, 2010, for Biberger. |
| U.S. Appl. No. 12/954,822, filed Nov. 26, 2010, for Biberger. |
| Ahmad, K. et al. (2008). “Hybrid Nanocomposites: A New Route Towards Tougher Alumina Ceramics,” Composites Science and Technology 68: 1321-1327. |
| Chau, J. K. H. et al. (2005). “Microwave Plasma Synthesis of Silver Nanopowders,” Materials Letters 59: 905-908. |
| Date, A. R. et al. (1987). “The Potential of Fire Assay and Inductively Coupled Plasama Source Mass Spectrometry for the Determination of Platinum Group Elements in Geological Materials,” Analyst 112: 1217-1222. |
| Ihlein, G. et al.(1998). “Ordered Porous Materials as Media for the Organization of Matter on the Nanoscale,” Applied Organometallic Chemistry 12: 305-314. |
| Lamouroux, E. et al. (2007). “Identification of Key Parameters for the Selective Growth of Single or Double Wall Carbon Nanotubes on FeMo/Al2O3 CVD Catalysts,” Applied Catalysts A: General 323: 162-173. |
| Martinez-Hansen, V. et al. (2009). “Development of Aligned Carbon Nanotubes Layers Over Stainless Steel Mesh Monoliths,” Catalysis Today 1475: 571-575. |
| Panchula, M. L. et al. (2003). “Nanocrystalline Aluminum Nitride: I, Vapor-Phase Synthesis in a Forced-Flow Reactor,” Journal of the American Ceramic Society 86(7): 1114-1120. |
| Wan, J. et al. (2005). “Spark Plasma Sintering of Silicon Nitride/Silicon Carbide Nanocomposites with Reduced Additive Amounts,” Scripta Materialia 53: 663-667. |
| Number | Date | Country | |
|---|---|---|---|
| 20140249021 A1 | Sep 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13033514 | Feb 2011 | US |
| Child | 14175894 | US |