Patent Grant
10290430
High voltage electrolytic capacitors are often employed in implantable medical devices. These capacitors are required to have a high energy density because it is desirable to minimize the overall size of the implanted device. This is particularly true of an implantable cardioverter defibrillator (“ICD”), also referred to as an implantable defibrillator, because the high voltage capacitors used to deliver the defibrillation pulse can occupy as much as one third of the ICD volume. ICDs typically use two to four electrolytic capacitors in series to achieve the desired high voltage for shock delivery. Typically, metal foils (e.g., aluminum foil) are used in the electrolytic capacitor due to their small size. Because the electrostatic capacitance of the capacitor is proportional to its electrode area, the surface of the metallic foil may be, prior to the formation of the dielectric film, roughened or subjected to a chemical conversion to increase its effective area. This step of roughening the surface of the metallic foil is called etching. Etching is normally carried out either by the method (chemical etching) of conducting immersion into a solution of hydrochloric acid or by the method (electrochemical etching) of carrying out electrolysis in an aqueous solution of hydrochloric acid. The capacitance of the electrolytic capacitor is determined by the extent of roughing (the surface area) of the anode foil and the thickness and the dielectric constant of the oxide film.
Due to the limited surface area that may be provided by etching metallic foils, attempts have also been made to employ porous sintered pellets in wet electrolytic capacitors—i.e., “wet tantalum” capacitors. A tantalum pellet, for instance, may be formed by compressing a powder under high pressure and sintering at high temperature to form a sponge-like structure, which is very strong and dense but also highly porous. As a result of the high voltages encountered in medical devices, however, low specific charge powders must generally be employed. Namely, if the specific charge is too high, relatively thin sinter necks tend to form between adjacent particles, which can cause the dielectric layer in the vicinity of these necks to fail at high voltages.
As such, a need currently exists for an improved wet electrolytic capacitor for use in implantable medical devices, such as defibrillators.
In accordance with one embodiment of the present invention, a wet electrolytic capacitor is disclosed that comprises a planar anode, cathode, and fluidic working electrolyte in communication with the anode and cathode. The anode comprises an anodically oxidized pellet formed from a pressed and sintered valve metal powder. The valve metal powder is formed by reacting an oxide of a valve metal compound with a reducing agent that contains a metal having an oxidation state of 2 or more. The cathode comprises a metal substrate coated with a conductive coating.
In accordance with another embodiment of the present invention, a wet electrolytic capacitor is disclosed that comprises a planar anode, cathode, and fluidic working electrolyte in communication with the anode and cathode. The anode comprises an anodically oxidized pellet formed from a pressed and sintered tantalum powder. The powder is nodular or angular and has a specific charge of about 15,000 μF*V/g or more. The cathode comprises a metal substrate coated with a conductive coating.
In accordance with yet another embodiment of the present invention, a method for forming a wet electrolytic capacitor is disclosed that comprises pressing a tantalum powder into the form of a pellet, wherein the powder is formed by reacting tantalum pentoxide with a reducing agent that contains magnesium, calcium, strontium, barium, cesium, aluminum, or a combination thereof; sintering the pellet; anodically oxidizing the sintered pellet to form a dielectric layer that overlies the anode; and positioning the anode and a fluidic working electrolyte within a casing.
Other features and aspects of the present invention are set forth in greater detail below.
A full and enabling disclosure of the present invention, including the best mode thereof, directed to one of ordinary skill in the art, is set forth more particularly in the remainder of the specification, which makes reference to the appended figures in which:
Repeat use of references characters in the present specification and drawings is intended to represent same or analogous features or elements of the invention.
It is to be understood by one of ordinary skill in the art that the present discussion is a description of exemplary embodiments only, and is not intended as limiting the broader aspects of the present invention, which broader aspects are embodied in the exemplary construction.
Generally speaking, the present invention is directed to a wet electrolytic capacitor that contains a cathode, fluidic working electrolyte, and planar anode formed from an anodically oxidized sintered porous pellet. The pellet may be formed from a pressed valve metal powder, which in turn, is formed by reacting an oxide of a valve metal compound (e.g., tantalum pentoxide) with a reducing agent that contains a metal having an oxidation state of 2 or more. Examples of such metals may include, for instance, alkaline earth metals (e.g., magnesium, calcium, strontium, barium, cesium, etc.), aluminum, and so forth. Through the use of such a powder, the present inventors have discovered that higher capacitance levels can be achieved than previously thought possible for the high voltage capacitors employed in implantable medical devices.
Various embodiments of the present invention will now be described in more detail.
I. Anode
The anode is formed from a valve metal powder that contains a valve metal (i.e., metal that is capable of oxidation) or valve metal-based compound, such as tantalum, niobium, aluminum, hafnium, titanium, alloys thereof, oxides thereof, nitrides thereof, and so forth. For example, the valve metal powder may contain an electrically conductive oxide of niobium, such as niobium oxide having an atomic ratio of niobium to oxygen of 1:1.0±1.0, in some embodiments 1:1.0±0.3, in some embodiments 1:1.0±0.1, and in some embodiments, 1:1.0±0.05. The niobium oxide may be NbO0.7, NbO1.0, NbO1.1, and NbO2.
As noted above, the valve metal powder may be formed by reacting an oxide of a valve metal compound with a reducing agent that contains a metal having a relatively high oxidation state (e.g., magnesium). The valve metal oxide is typically a tantalum and/or niobium oxide capable of being reduced, such as Ta2Ox (x≤5) (e.g., Ta2O5) or Nb2Ox (x≤5) (e.g., Nb2O5). The reducing agent may be provided in a gaseous, liquid, or solid state, and may also be in the form of the metal, as well as alloys or salts thereof. In one embodiment, for instance, a halide salt (e.g., chloride, fluoride, etc.) may be employed. If desired, other components may also be added before, during, or after the reaction, such as dopants, alkali metals, etc. The reduction of the oxide is typically carried out at a temperature of from about 400° C. to about 1200° C., and in some embodiments, from about 600° C. to about 1000° C., for about 20 to about 300 minutes. Heating may be carried out in a reactor under an inert atmosphere (e.g., argon or nitrogen atmosphere) so that a molten bath is formed. Suitable reactors may include, for instance, vertical tube furnaces, rotary kilns, fluid bed furnaces, multiple hearth furnaces, self-propagation high-temperature synthesis reactors, etc. The reactor may be maintained under inert gas until that the mass in the reaction vessel is cooled to ambient temperature. Additional details of such a reduction reaction may be described in U.S. Patent Publication Nos. 2003/0110890 to He, et al. and 2004/0163491 to Shekhter, et al.
After the reduction, the product may be cooled, crushed, and washed to remove excess impurities or reactants. The washing solution may include, for instance, a mineral acid and water. If desired, the powder may be subjected to additional treatment to remove any tantalates/niobates (e.g., magnesium tantalate) that may have formed during the reaction. In one embodiment, for instance, one technique for removing the tantalates/niobates involves heating the powder under vacuum at a temperature of from about 1100° C. to about 1400° C. for about 15 minutes to about 6 hours. Likewise, another technique for removing the tantalates/niobates involves heating the powder at a temperature of from about 800° C. to about 1300° C. in the presence of a getter material, such as magnesium, calcium and/or aluminum, for about 15 minutes to about 6 hours. Such techniques may be described in more detail in U.S. Pat. No. 7,431,751 to Shekhter, et al. Although not required, the powder may be subjected to additional refining steps as is known in the art, such as doping, deoxidizing, etc.
Regardless of the particular steps employed, the resulting powder has a variety of beneficial properties. The powder may, for example, be a free-flowing, finely divided powder that contains primary particles having a three-dimensional shape, such as a nodular or angular shape. Such particles are not generally flat and thus have a relatively low “aspect ratio”, which is the average diameter or width of the particles divided by the average thickness (“D/T”). For example, the aspect ratio of the particles may be about 4 or less, in some embodiments about 3 or less, and in some embodiments, from about 1 to about 2. The powder may also have a relatively high specific surface area, such as about 1 square meter per gram (“m2/g”) or more, in some embodiments about 2 m2/g or more, and in some embodiments, from about 4 to about 30 m2/g. The term “specific surface area” generally refers to surface area as determined by the physical gas adsorption (B.E.T.) method of Bruanauer, Emmet, and Teller, Journal of American Chemical Society, Vol. 60, 1938, p. 309, with nitrogen as the adsorption gas. The test may be conducted with a MONOSORB® Specific Surface Area Analyzer available from QUANTACHROME Corporation, Syosset, N.Y., which measures the quantity of adsorbate nitrogen gas adsorbed on a solid surface by sensing the change in thermal conductivity of a flowing mixture of adsorbate and inert carrier gas (e.g., helium).
The primary particles of the powder may also have a median size (D50) of from about 5 to about 1000 nanometers, and in some embodiments, from about 10 to about 500 nanometers, such as using a laser particle size distribution analyzer made by BECKMAN COULTER Corporation (e.g., LS-230), optionally after subjecting the particles to an ultrasonic wave vibration of 70 seconds. Due to its high surface area and low particle size, the powder may have a high specific charge, such as greater than about 15,000 microFarads*Volts per gram (“μF*V/g”), in some embodiments from about 18,000 to about 80,000 μF*V/g, and in some embodiments, from about 20,000 to about 45,000 μF*V/g. As is known in the art, the specific charge may be determined by multiplying capacitance by the anodizing voltage employed, and then dividing this product by the weight of the anodized electrode body. Despite the use of such high specific charge powders with three-dimensional particles, the present inventors have nevertheless discovered that the ability to achieve high voltages can be achieved through the manner in which the powder is formed. More particularly, it is believed that the particular reduction process employed can achieve “sinter necks” between adjacent agglomerated particles that are relatively large in size. Sinter necks are the small cross-sectional area of the electrical path within the metal structure. Typically, the sinter necks have a size of about 200 nanometers or more, in some embodiments about 250 nanometers or more, and in some embodiments, from about 300 to about 800 nanometers. Because the necks are relatively large in size, the dielectric layer in the vicinity of the neck is more likely not to fail at high forming voltages.
The powder (as well as the anode) may also have a relatively low alkali metal, carbon, and oxygen content. For example, the powder may have no more than about 50 ppm carbon or alkali metals, and in some embodiments, no more than about 10 ppm carbon or alkali metals. Likewise, the powder may have no more than about 0.15 ppm/μC/g oxygen, and in some embodiments, no more than about 0.10 ppm/μC/g oxygen. Oxygen content may be measured by LECO Oxygen Analyzer and includes oxygen in natural oxide on the tantalum surface and bulk oxygen in the tantalum particles. Bulk oxygen content is controlled by period of crystalline lattice of tantalum, which is increasing linearly with increasing oxygen content in tantalum until the solubility limit is achieved. This method was described in “Critical Oxygen Content In Porous Anodes Of Solid Tantalum Capacitors”, Pozdeev-Freeman et al., Journal of Materials Science: Materials In Electronics 9, (1998) 309-311 wherein X-ray diffraction analysis (XRDA) was employed to measure period of crystalline lattice of tantalum. Oxygen in sintered tantalum anodes may be limited to thin natural surface oxide, while the bulk of tantalum is practically free of oxygen.
To facilitate the construction of the anode, certain additional components may also be included in the powder. For example, the powder may be optionally mixed with a binder and/or lubricant to ensure that the particles adequately adhere to each other when compacted or pressed to form the pellet. Suitable binders may include, for instance, poly(vinyl butyral); poly(vinyl acetate); poly(vinyl alcohol); poly(vinyl pyrollidone); cellulosic polymers, such as carboxymethylcellulose, methyl cellulose, ethyl cellulose, hydroxyethyl cellulose, and methylhydroxyethyl cellulose; atactic polypropylene, polyethylene; polyethylene glycol (e.g., Carbowax from Dow Chemical Co.); polystyrene, poly(butadiene/styrene); polyamides, polyimides, and polyacrylamides, high molecular weight polyethers; copolymers of ethylene oxide and propylene oxide; fluoropolymers, such as polytetrafluoroethylene, polyvinylidene fluoride, and fluoro-olefin copolymers; acrylic polymers, such as sodium polyacrylate, poly(lower alkyl acrylates), poly(lower alkyl methacrylates) and copolymers of lower alkyl acrylates and methacrylates; and fatty acids and waxes, such as stearic and other soapy fatty acids, vegetable wax, microwaxes (purified paraffins), etc. The binder may be dissolved and dispersed in a solvent. Exemplary solvents may include water, alcohols, and so forth. When utilized, the percentage of binders and/or lubricants may vary from about 0.1% to about 8% by weight of the total mass. It should be understood, however, that binders and/or lubricants are not necessarily required in the present invention.
The resulting powder may be compacted to form a pellet using any conventional powder press device. For example, a press mold may be employed that is a single station compaction press containing a die and one or multiple punches. Alternatively, anvil-type compaction press molds may be used that use only a die and single lower punch. Single station compaction press molds are available in several basic types, such as cam, toggle/knuckle and eccentric/crank presses with varying capabilities, such as single action, double action, floating die, movable platen, opposed ram, screw, impact, hot pressing, coining or sizing. The powder may be compacted around an anode lead wire. The wire may be formed from any electrically conductive material, such as tantalum, niobium, aluminum, hafnium, titanium, etc., as well as electrically conductive oxides and/or nitrides of thereof.
Any binder/lubricant may be removed after pressing by heating the pellet under vacuum at a certain temperature (e.g., from about 150° C. to about 500° C.) for several minutes. Alternatively, the binder/lubricant may also be removed by contacting the pellet with an aqueous solution, such as described in U.S. Pat. No. 6,197,252 to Bishop, et al. Thereafter, the pellet is sintered to form a porous, integral mass. The pellet is typically sintered at a temperature of from about 800° C. to about 2000° C., in some embodiments from about 1200° C. to about 1800° C., and in some embodiments, from about 1500° C. to about 1700° C., for a time of from about 5 minutes to about 100 minutes, and in some embodiments, from about 8 minutes to about 15 minutes. This may occur in one or more steps. If desired, sintering may occur in an atmosphere that limits the transfer of oxygen atoms to the anode. For example, sintering may occur in a reducing atmosphere, such as in a vacuum, inert gas, hydrogen, etc. The reducing atmosphere may be at a pressure of from about 10 Torr to about 2000 Torr, in some embodiments from about 100 Torr to about 1000 Torr, and in some embodiments, from about 100 Torr to about 930 Torr. Mixtures of hydrogen and other gases (e.g., argon or nitrogen) may also be employed.
Upon sintering, the pellet shrinks due to the growth of metallurgical bonds between the particles. Because shrinkage generally increases the density of the pellet, lower press densities (“green”) may be employed to still achieve the desired target density. For example, the target density of the pellet after sintering is typically from about 5 to about 8 grams per cubic centimeter. As a result of the shrinking phenomenon, however, the pellet need not be pressed to such high densities, but may instead be pressed to densities of less than about 6.0 grams per cubic centimeter, and in some embodiments, from about 4.5 to about 5.5 grams per cubic centimeter. Among other things, the ability to employ lower green densities may provide significant cost savings and increase processing efficiency.
Due to the thin nature of the planar anode, it is sometimes desirable to control the manner in which the anode wire is inserted to limit the extent that stresses applied during manufacturing will cause the wire to pull out of the anode. For example, in one embodiment, at least a portion of the wire within the anode is bent at an angle relative to the longitudinal axis of the wire. This “bend” reduces the ease to which the wire can be pulled out in the longitudinal direction after the anode is pressed and sintered. Referring to
In addition to its geometric configuration, the extent to which the anode wire is inserted into the anode may also be controlled to help minimize the likelihood of withdrawal during manufacturing. That is, the wire is less likely to be pulled out of the anode the farther it is inserted. Of course, too great of a wire insertion can alter the uniformity of the press density, which can impact the resulting electrical performance of the anode. In this regard, the present inventors have discovered that the ratio of the length of the anode in which the wire is inserted to the entire length of the anode is typically from about 0.1 to about 0.6, and in some embodiments, from about 0.2 to about 0.5. In
The thickness of the planar anode is generally small to improve the electrical performance and volumetric efficiency of the resulting capacitor. In
The anode also contains a dielectric formed by anodically oxidizing (“anodizing”) the sintered anode so that a dielectric layer is formed over and/or within the anode. For example, a tantalum (Ta) anode may be anodized to tantalum pentoxide (Ta2O5). Typically, anodization is performed by initially applying a solution to the anode, such as by dipping anode into the electrolyte. Aqueous solvents (e.g., water) and/or non-aqueous solvents (e.g., ethylene glycol) may be employed. To enhance conductivity, a compound may be employed that is capable of dissociating in the solvent to form ions. Examples of such compounds include, for instance, acids, such as described below with respect to the electrolyte. For example, an acid (e.g., phosphoric acid) may constitute from about 0.01 wt. % to about 5 wt. %, in some embodiments from about 0.05 wt. % to about 0.8 wt. %, and in some embodiments, from about 0.1 wt. % to about 0.5 wt. % of the anodizing solution. If desired, blends of acids may also be employed.
A current is passed through the anodizing solution to form the dielectric layer. The value of the formation voltage manages the thickness of the dielectric layer. For example, the power supply may be initially set up at a galvanostatic mode until the required voltage is reached. Thereafter, the power supply may be switched to a potentiostatic mode to ensure that the desired dielectric thickness is formed over the entire surface of the anode. Of course, other known methods may also be employed, such as pulse or step potentiostatic methods. The voltage at which anodic oxidation occurs is typically high to achieve a capacitor capable of operating at a high voltage range. That is, the voltage is typically from about 100 volts to about 300 volts, in some embodiments from about 170 volts to about 280 volts, and in some embodiments, from about 200 volts to about 250 volts. The temperature of the anodizing solution may range from about 10° C. to about 200° C., in some embodiments from about 20° C. to about 150° C., and in some embodiments, from about 30° C. to about 90° C. The resulting dielectric layer may be formed on a surface of the anode and within its pores. When employed, the specific nature of the powder may allow the resulting anode to achieve a high specific charge even at the high formation voltages often employed in the present invention.
II. Working Electrolyte
The working electrolyte may be in electrical communication with the cathode and anode. The electrolyte is a fluid that may be impregnated within the anode, or it may be added to the capacitor at a later stage of production. The fluid electrolyte generally uniformly wets the dielectric on the anode. Various suitable electrolytes are described in U.S. Pat. Nos. 5,369,547 and 6,594,140 to Evans, et al. Typically, the electrolyte is ionically conductive in that has an electrical conductivity of from about 0.1 to about 20 Siemens per centimeter (“S/cm”), in some embodiments from about 0.2 to about 15 S/cm, and in some embodiments, from about 0.5 to about 10 S/cm, determined at a temperature of about 23° C. using any known electric conductivity meter (e.g., Oakton Con Series 11). The fluid electrolyte is generally in the form of a liquid, such as a solution (e.g., aqueous or non-aqueous), colloidal suspension, gel, etc. For example, the electrolyte may be an aqueous solution of an acid (e.g., sulfuric acid, phosphoric acid, or nitric acid), base (e.g., potassium hydroxide), or salt (e.g., ammonium salt, such as a nitrate), as well any other suitable electrolyte known in the art, such as a salt dissolved in an organic solvent (e.g., ammonium salt dissolved in a glycol-based solution). Various other electrolytes are described in U.S. Pat. Nos. 5,369,547 and 6,594,140 to Evans, et al.
The desired ionic conductivity may be achieved by selecting ionic compound(s) (e.g., acids, bases, salts, and so forth) within certain concentration ranges. In one particular embodiment, salts of weak organic acids may be effective in achieving the desired conductivity of the electrolyte. The cation of the salt may include monatomic cations, such as alkali metals (e.g., Li+, Na+, K+, Rb+, or Cs+), alkaline earth metals (e.g., Be2+, Mg2+, Ca2+, Sr2+ or Ba2+), transition metals (e.g., Ag+, Fe2+, Fe3+, etc.), as well as polyatomic cations, such as NH4+. The monovalent ammonium (NH4+), sodium (K+), and lithium (Li+) are particularly suitable cations for use in the present invention. The organic acid used to form the anion of the salt may be “weak” in the sense that it typically has a first acid dissociation constant (pKa1) of about 0 to about 11, in some embodiments about 1 to about 10, and in some embodiments, from about 2 to about 10, determined at about 23° C. Any suitable weak organic acids may be used in the present invention, such as carboxylic acids, such as acrylic acid, methacrylic acid, malonic acid, succinic acid, salicylic acid, sulfosalicylic acid, adipic acid, maleic acid, malic acid, oleic acid, gallic acid, tartaric acid (e.g., dextotartaric acid, mesotartaric acid, etc.), citric acid, formic acid, acetic acid, glycolic acid, oxalic acid, propionic acid, phthalic acid, isophthalic acid, glutaric acid, gluconic acid, lactic acid, aspartic acid, glutaminic acid, itaconic acid, trifluoroacetic acid, barbituric acid, cinnamic acid, benzoic acid, 4-hydroxybenzoic acid, aminobenzoic acid, etc.; blends thereof, and so forth. Polyprotic acids (e.g., diprotic, triprotic, etc.) are particularly desirable for use in forming the salt, such as adipic acid (pKa1 of 4.43 and pKa2 of 5.41), α-tartaric acid (pKa1 of 2.98 and pKa2 of 4.34), meso-tartaric acid (pKa1 of 3.22 and pKa2 of 4.82), oxalic acid (pKa1 of 1.23 and pKa2 of 4.19), lactic acid (pKa1 of 3.13, pKa2 of 4.76, and pKa3 of 6.40), etc.
While the actual amounts may vary depending on the particular salt employed, its solubility in the solvent(s) used in the electrolyte, and the presence of other components, such weak organic acid salts are typically present in the electrolyte in an amount of from about 0.1 to about 25 wt. %, in some embodiments from about 0.2 to about 20 wt. %, in some embodiments from about 0.3 to about 15 wt. %, and in some embodiments, from about 0.5 to about 5 wt. %.
The electrolyte is typically aqueous in that it contains an aqueous solvent, such as water (e.g., deionized water). For example, water (e.g., deionized water) may constitute from about 20 wt. % to about 95 wt. %, in some embodiments from about 30 wt. % to about 90 wt. %, and in some embodiments, from about 40 wt. % to about 85 wt. % of the electrolyte. A secondary solvent may also be employed to form a solvent mixture. Suitable secondary solvents may include, for instance, glycols (e.g., ethylene glycol, propylene glycol, butylene glycol, triethylene glycol, hexylene glycol, polyethylene glycols, ethoxydiglycol, dipropyleneglycol, etc.); glycol ethers (e.g., methyl glycol ether, ethyl glycol ether, isopropyl glycol ether, etc.); alcohols (e.g., methanol, ethanol, n-propanol, iso-propanol, and butanol); ketones (e.g., acetone, methyl ethyl ketone, and methyl isobutyl ketone); esters (e.g., ethyl acetate, butyl acetate, diethylene glycol ether acetate, methoxypropyl acetate, ethylene carbonate, propylene carbonate, etc.); amides (e.g., dimethylformamide, dimethylacetamide, dimethylcaprylic/capric fatty acid amide and N-alkylpyrrolidones); sulfoxides or sulfones (e.g., dimethyl sulfoxide (DMSO) and sulfolane); and so forth. Such solvent mixtures typically contain water in an amount from about 40 wt. % to about 80 wt. %, in some embodiments from about 50 wt. % to about 75 wt. %, and in some embodiments, from about 55 wt. % to about 70 wt. % and secondary solvent(s) in an amount from about 20 wt. % to about 60 wt. %, in some embodiments from about 25 wt. % to about 50 wt. %, and in some embodiments, from about 30 wt. % to about 45 wt. %. The secondary solvent(s) may, for example, constitute from about 5 wt. % to about 45 wt. %, in some embodiments from about 10 wt. % to about 40 wt. %, and in some embodiments, from about 15 wt. % to about 35 wt. % of the electrolyte.
If desired, the electrolyte may be relatively neutral and have a pH of from about 4.5 to about 8.0, in some embodiments from about 5.0 to about 7.5, and in some embodiments, from about 5.5 to about 7.0. One or more pH adjusters (e.g., acids, bases, etc.) may be employed to help achieve the desired pH. In one embodiment, an acid is employed to lower the pH to the desired range. Suitable acids include, for instance, organic acids such as described above; inorganic acids, such as hydrochloric acid, nitric acid, sulfuric acid, phosphoric acid, polyphosphoric acid, boric acid, boronic acid, etc.; and mixtures thereof. Although the total concentration of pH adjusters may vary, they are typically present in an amount of from about 0.01 wt. % to about 10 wt. %, in some embodiments from about 0.05 wt. % to about 5 wt. %, and in some embodiments, from about 0.1 wt. % to about 2 wt. % of the electrolyte.
The electrolyte may also contain other components that help improve the electrical performance of the capacitor. For instance, a depolarizer may be employed in the electrolyte to help inhibit the evolution of hydrogen gas at the cathode of the electrolytic capacitor, which could otherwise cause the capacitor to bulge and eventually fail. When employed, the depolarizer normally constitutes from about 1 to about 500 parts per million (“ppm”), in some embodiments from about 10 to about 200 ppm, and in some embodiments, from about 20 to about 150 ppm of the electrolyte. Suitable depolarizers may include nitroaromatic compounds, such as 2-nitrophenol, 3-nitrophenol, 4-nitrophenol, 2-nitrobenzonic acid, 3-nitrobenzonic acid, 4-nitrobenzonic acid, 2-nitroace tophenone, 3-nitroacetophenone, 4-nitroacetophenone, 2-nitroanisole, 3-nitroanisole, 4-nitroanisole, 2-nitrobenzaldehyde, 3-nitrobenzaldehyde, 4-nitrobenzaldehyde, 2-nitrobenzyl alcohol, 3-nitrobenzyl alcohol, 4-nitrobenzyl alcohol, 2-nitrophthalic acid, 3-nitrophthalic acid, 4-nitrophthalic acid, and so forth. Particularly suitable nitroaromatic depolarizers for use in the present invention are nitrobenzoic acids, anhydrides or salts thereof, substituted with one or more alkyl groups (e.g., methyl, ethyl, propyl, butyl, etc.). Specific examples of such alkyl-substituted nitrobenzoic compounds include, for instance, 2-methyl-3-nitrobenzoic acid; 2-methyl-6-nitrobenzoic acid; 3-methyl-2-nitrobenzoic acid; 3-methyl-4-nitrobenzoic acid; 3-methyl-6-nitrobenzoic acid; 4-methyl-3-nitrobenzoic acid; anhydrides or salts thereof; and so forth.
III. Cathode
A. Metal Substrate
The cathode typically contains a metal substrate, which may also optionally serve as a casing for the capacitor. The substrate may be formed from a variety of different metals, such as tantalum, niobium, aluminum, nickel, hafnium, titanium, copper, silver, steel (e.g., stainless), alloys thereof, composites thereof (e.g., metal coated with electrically conductive oxide), and so forth. The geometric configuration of the substrate may generally vary as is well known to those skilled in the art, such as in the form of a foil, sheet, screen, container, can, etc. The metal substrate may form the all or a portion of casing for the capacitor, or it may simply be applied to the casing. Regardless, the substrate may have a variety of shapes, such as generally cylindrical, D-shaped, rectangular, triangular, prismatic, etc. If desired, a surface of the substrate may be roughened to increase its surface area and increase the degree to which a material may be able to adhere thereto. In one embodiment, for example, a surface of the substrate is chemically etched, such as by applying a solution of a corrosive substance (e.g., hydrochloric acid) to the surface. Mechanical roughening may also be employed. For instance, a surface of the substrate may be abrasive blasted by propelling a stream of abrasive media (e.g., sand) against at least a portion of a surface thereof.
B. Conductive Coating
A conductive coating may also be disposed on a surface of the metal substrate (e.g., interior surface) to serve as an electrochemically active material for the capacitor. Any number of layers may be employed in the coating. The materials employed in the coating may vary. For example, the conductive coating may contain a noble metal (e.g., ruthenium, rhodium, palladium, silver, osmium, iridium, platinum, gold, etc.), an oxide (e.g., ruthenium oxide), carbonaceous materials, conductive polymers, etc. In one embodiment, for example, the coating may include conductive polymer(s) that are typically π-conjugated and have electrical conductivity after oxidation or reduction. Examples of such π-conjugated conductive polymers include, for instance, polyheterocycles (e.g., polypyrroles, polythiophenes, polyanilines, etc.), polyacetylenes, poly-p-phenylenes, polyphenolates, and so forth. Substituted polythiophenes are particularly suitable for use as conductive polymer in that they have particularly good mechanical robustness and electrical performance. In one particular embodiment, the substituted polythiophene has the following general structure:
wherein,
T is O or S;
D is an optionally substituted C1 to C5 alkylene radical (e.g., methylene, ethylene, n-propylene, n-butylene, n-pentylene, etc.);
R7 is a linear or branched, optionally substituted C1 to C18 alkyl radical (e.g., methyl, ethyl, n- or iso-propyl, n-, iso-, sec- or tert-butyl, n-pentyl, 1-methylbutyl, 2-methylbutyl, 3-methylbutyl, 1-ethylpropyl, 1,1-dimethylpropyl, 1,2-dimethylpropyl, 2,2-dimethylpropyl, n-hexyl, n-heptyl, n-octyl, 2-ethylhexyl, n-nonyl, n-decyl, n-undecyl, n-dodecyl, n-tridecyl, n-tetradecyl, n-hexadecyl, n-octadecyl, etc.); optionally substituted C5 to C12 cycloalkyl radical (e.g., cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl cyclodecyl, etc.); optionally substituted C6 to C14 aryl radical (e.g., phenyl, naphthyl, etc.); optionally substituted C7 to C18 aralkyl radical (e.g., benzyl, o-, m-, p-tolyl, 2,3-, 2,4-, 2,5-, 2-6, 3-4-, 3,5-xylyl, mesityl, etc.); optionally substituted C1 to C4 hydroxyalkyl radical, or hydroxyl radical; and
q is an integer from 0 to 8, in some embodiments, from 0 to 2, and in one embodiment, 0; and
n is from 2 to 5,000, in some embodiments from 4 to 2,000, and in some embodiments, from 5 to 1,000. Example of substituents for the radicals “D” or “R7” include, for instance, alkyl, cycloalkyl, aryl, aralkyl, alkoxy, halogen, ether, thioether, disulphide, sulfoxide, sulfone, sulfonate, amino, aldehyde, keto, carboxylic acid ester, carboxylic acid, carbonate, carboxylate, cyano, alkylsilane and alkoxysilane groups, carboxylamide groups, and so forth.
Particularly suitable thiophene polymers are those in which “D” is an optionally substituted C2 to C3 alkylene radical. For instance, the polymer may be optionally substituted poly(3,4-ethylenedioxythiophene), which has the following general structure:
Methods for forming conductive polymers, such as described above, are well known in the art. For instance, U.S. Pat. No. 6,987,663 to Merker, et al. describes various techniques for forming substituted polythiophenes from a monomeric precursor. The monomeric precursor may, for instance, have the following structure:
wherein,
T, D, R7, and q are defined above. Particularly suitable thiophene monomers are those in which “D” is an optionally substituted C2 to C3 alkylene radical. For instance, optionally substituted 3,4-alkylenedioxythiophenes may be employed that have the general structure:
wherein, R7 and q are as defined above. In one particular embodiment, “q” is 0. One commercially suitable example of 3,4-ethylenedioxthiophene is available from Heraeus Clevios under the designation Clevios™ M. Other suitable monomers are also described in U.S. Pat. No. 5,111,327 to Blohm, et al. and U.S. Pat. No. 6,635,729 to Groenendaal, et al. Derivatives of these monomers may also be employed that are, for example, dimers or trimers of the above monomers. Higher molecular derivatives, i.e., tetramers, pentamers, etc. of the monomers are suitable for use in the present invention. The derivatives may be made up of identical or different monomer units and used in pure form and in a mixture with one another and/or with the monomers. Oxidized or reduced forms of these precursors may also be employed.
The thiophene monomers may be chemically polymerized in the presence of an oxidative catalyst. The oxidative catalyst typically includes a transition metal cation, such as iron(III), copper(II), chromium(VI), cerium(IV), manganese(IV), manganese(VII), ruthenium(III) cations, etc. A dopant may also be employed to provide excess charge to the conductive polymer and stabilize the conductivity of the polymer. The dopant typically includes an inorganic or organic anion, such as an ion of a sulfonic acid. In certain embodiments, the oxidative catalyst employed in the precursor solution has both a catalytic and doping functionality in that it includes a cation (e.g., transition metal) and anion (e.g., sulfonic acid). For example, the oxidative catalyst may be a transition metal salt that includes iron(III) cations, such as iron(III) halides (e.g., FeCl3) or iron(III) salts of other inorganic acids, such as Fe(ClO4)3 or Fe2(SO4)3 and the iron(III) salts of organic acids and inorganic acids comprising organic radicals. Examples of iron (III) salts of inorganic acids with organic radicals include, for instance, iron(III) salts of sulfuric acid monoesters of C1 to C20 alkanols (e.g., iron(III) salt of lauryl sulfate). Likewise, examples of iron(III) salts of organic acids include, for instance, iron(III) salts of C1 to C20 alkane sulfonic acids (e.g., methane, ethane, propane, butane, or dodecane sulfonic acid); iron (III) salts of aliphatic perfluorosulfonic acids (e.g., trifluoromethane sulfonic acid, perfluorobutane sulfonic acid, or perfluorooctane sulfonic acid); iron (III) salts of aliphatic C1 to C20 carboxylic acids (e.g., 2-ethylhexylcarboxylic acid); iron (III) salts of aliphatic perfluorocarboxylic acids (e.g., trifluoroacetic acid or perfluorooctane acid); iron (III) salts of aromatic sulfonic acids optionally substituted by C1 to C20 alkyl groups (e.g., benzene sulfonic acid, o-toluene sulfonic acid, p-toluene sulfonic acid, or dodecylbenzene sulfonic acid); iron (III) salts of cycloalkane sulfonic acids (e.g., camphor sulfonic acid); and so forth. Mixtures of these above-mentioned iron(III) salts may also be used. Iron(III)-p-toluene sulfonate, iron(III)-o-toluene sulfonate, and mixtures thereof, are particularly suitable. One commercially suitable example of iron(III)-p-toluene sulfonate is available from Heraeus Clevios under the designation Clevios™ C.
Various methods may be utilized to form the conductive layer. In one embodiment, the oxidative catalyst and monomer are applied, either sequentially or together, such that the polymerization reaction occurs in situ on the substrate. Suitable application techniques may include screen-printing, dipping, electrophoretic coating, and spraying, may be used to form a conductive polymer coating. As an example, a monomer may initially be mixed with the oxidative catalyst to form a precursor solution. Once the mixture is formed, it may be applied to the metal substrate and then allowed to polymerize so that the conductive layer is formed. Alternatively, the oxidative catalyst and monomer may be applied sequentially. In one embodiment, for example, the oxidative catalyst is dissolved in an organic solvent (e.g., butanol) and then applied as a dipping solution. The substrate may then be dried to remove the solvent therefrom. Thereafter, the substrate may be dipped into a solution containing the monomer. Polymerization is typically performed at temperatures of from about −10° C. to about 250° C., and in some embodiments, from about 0° C. to about 200° C., depending on the oxidizing agent used and desired reaction time. Suitable polymerization techniques, such as described above, may be described in more detail in U.S. Publication No. 2008/232037 to Biler.
While chemical polymerization techniques may be employed in certain embodiments, it is often desired to minimize the use of oxidative catalysts in the capacitor as such materials can often lead to the formation of iron radicals (e.g., Fe2+ or Fe3+ ions). These radicals can, in turn, lead to dielectric degradation at the high voltages often employed during the use of the wet capacitor. Thus, anodic electrochemical polymerization techniques may be employed in certain embodiments to form the conductive polymer. Such techniques generally employ a colloidal suspension that is generally free of iron-based oxidative catalysts. For instance, the colloidal suspension typically contains less than about 0.5 wt. %, in some embodiments, less than about 0.1 wt. %, and in some embodiments, less than about 0.05 wt. % (e.g., 0 wt. %) of such iron-based oxidative catalysts.
The colloidal suspension may be in the form of a macroemulsion, microemulsion, solution, etc. depending on the particular nature of the components of the suspension. Regardless, the suspension generally contains a solvent that serves as a continuous phase within which the precursor monomer is dispersed. Any of a variety of different solvents may be employed in the colloidal suspension, such as alcohols, glycols, water, etc. In one particular embodiment, the colloidal suspension is aqueous in nature. If desired, other additives may also be employed in the suspension to facilitate polymerization, such as surfactants (e.g., nonionic, anionic, or cationic surfactants), dopants (e.g., sulfonic acids), defoaming agents, and so forth. Solvents (e.g., water) may constitute from about 50 wt. % to about 99 wt. %, in some embodiments from about 70 wt. % to about 98 wt. % and in some embodiments, from about 80 wt. % to about 95 wt. %. The remaining components of the colloidal suspension (e.g., precursor monomers, surfactants, and sulfonic acids) may likewise constitute from about 1 wt. % to about 50 wt. %, in some embodiments from about 2 wt. % to about 30 wt. % and in some embodiments, from about 5 wt. % to about 20 wt. % of the colloidal suspension.
To apply the colloidal suspension, any of a variety of suitable application techniques may be employed, such as screen-printing, dipping, electrophoretic coating, spraying, etc. Regardless of how it is applied, the monomer within the colloidal suspension may be anodically electrochemically-polymerized to form the conductive polymer layer. In one embodiment, for example, the metal substrate is dipped into a bath containing the colloidal suspension of the present invention. A pair of electrodes may be disposed within the bath for electrolysis. One electrode may be connected to the positive terminal of a power source and also in contact with the metal substrate. The other electrode may be connected to the negative terminal of the power source and an additional inert metal. During operation, the power source supplies a current feed to the electrodes in the electrochemical cell, thereby inducing electrolysis of the electrolyte and oxidative polymerization of the monomer in the colloidal suspension, or solution, onto the metal substrate. Anodic electrochemical polymerization is generally performed at ambient temperature to ensure that the colloidal suspension does not phase separate. For example, the colloidal suspension may be kept at a temperature of from about 15° C. to about 80° C., in some embodiments from about 20° C. to about 75° C., and in some embodiments, from about 25° C. to about 50° C. The amount of time in which the metal substrate is in contact with the colloidal suspension during anodic electrochemical polymerization may vary. For example, the metal substrate may be dipped into such a solution for a period of time ranging from about 10 seconds to about 10 minutes.
Multiple polymerization steps may be repeated until the desired thickness of the coating is achieved. In one embodiment, for example, a chemically polymerized layer may be formed directly over the noble metal layer and an electrochemical polymerized layer may be disposed thereover, or vice versa. Regardless, the total target thickness of the conductive polymer layer(s) may generally vary depending on the desired properties of the capacitor. Typically, the resulting conductive polymer layer(s) have a thickness of from about 0.2 micrometers (“μm”) to about 50 μm, in some embodiments from about 0.5 μm to about 20 μm, and in some embodiments, from about 1 μm to about 5 μm. It should be understood that the thickness of the layers are not necessarily the same at all locations on the substrate. Nevertheless, the average thickness on the substrate generally falls within the ranges noted above.
The particular manner in which the components are incorporated into the capacitor is not critical and may be accomplished using a variety of techniques. In most embodiments, however, the anode is positioned within a casing. Referring to
Although not shown, one or more separators may be employed between the anode and cathode (e.g., between the anode 200 and the first casing member 14, between the anode 200 and the second casing member 16, or between the anode and both casing members) that help insulate the anode and conductive polymer-coated cathode from each other. Examples of suitable materials for this purpose include, for instance, porous polymer materials (e.g., polypropylene, polyethylene, etc.), porous inorganic materials (e.g., fiberglass mats, porous glass paper, etc.), ion exchange resin materials, etc. Particular examples include ionic perfluoronated sulfonic acid polymer membranes (e.g., Nafion™ from the E.I. DuPont de Nemeours & Co.), sulphonated fluorocarbon polymer membranes, polybenzimidazole (PBI) membranes, and polyether ether ketone (PEEK) membranes. Although preventing direct contact between the anode and cathode, the separator permits ionic current flow of the electrolyte to the electrodes.
A feedthrough 30 (
Regardless of its particular configuration, the capacitor of the present invention may exhibit excellent electrical properties. For example, the capacitor may exhibit a high volumetric efficiency, such as from about 50,000 μF*V/cm3 to about 300,000 μF*V/cm3, in some embodiments from about 60,000 μF*V/cm3 to about 200,000 μF*V/cm3, and in some embodiments, from about 80,000 μF*V/cm3 to about 150,000 μF*V/cm3, determined at a frequency of 120 Hz and at room temperature (e.g., 25° C.). Volumetric efficiency is determined by multiplying the formation voltage of a part by its capacitance, and then dividing by the product by the volume of the part. For example, a formation voltage may be 175 volts for a part having a capacitance of 520 μF, which results in a product of 91,000 μF*V. If the part occupies a volume of about 0.8 cm3, this results in a volumetric efficiency of about 113,750 μF*V/cm3.
The capacitor may also exhibit a high energy density that enables it suitable for use in high pulse applications. Energy density is generally determined according to the equation E=½*CV2, where C is the capacitance in farads (F) and V is the working voltage of capacitor in volts (V). The capacitance may, for instance, be measured using a capacitance meter (e.g., Keithley 3330 Precision LCZ meter with Kelvin Leads, 2 volts bias and 1 volt signal) at operating frequencies of from 10 to 120 Hz (e.g., 120 Hz) and a temperature of 25° C. For example, the capacitor may exhibit an energy density of about 2.0 joules per cubic centimeter (J/cm3) or more, in some embodiments about 3.0 J/cm3, in some embodiments from about 3.5 J/cm3 to about 10.0 J/cm3, and in some embodiments, from about 4.0 to about 8.0 J/cm3. The capacitance may likewise be about 1 milliFarad per square centimeter (“mF/cm2”) or more, in some embodiments about 2 mF/cm2 or more, in some embodiments from about 5 to about 50 mF/cm2, and in some embodiments, from about 8 to about 20 mF/cm2. The capacitor may also exhibit a relatively high “breakdown voltage” (voltage at which the capacitor fails), such as about 180 volts or more, in some embodiments about 200 volts or more, and in some embodiments, from about 210 volts to about 260 volts.
The equivalent series resistance (“ESR”)—the extent that the capacitor acts like a resistor when charging and discharging in an electronic circuit—may also be less than about 15,000 milliohms, in some embodiments less than about 10,000 milliohms, in some embodiments less than about 5,000 milliohms, and in some embodiments, from about 1 to about 4,500 milliohms, measured with a 2-volt bias and 1-volt signal at a frequency of 120 Hz. In addition, the leakage current, which generally refers to the current flowing from one conductor to an adjacent conductor through an insulator, can be maintained at relatively low levels. For example, the numerical value of the normalized leakage current of a capacitor of the present invention is, in some embodiments, less than about 1 μA/μF*V, in some embodiments less than about 0.5 μA/μF*V, and in some embodiments, less than about 0.1 μA/μF*V, where μA is microamps and μF*V is the product of the capacitance and the rated voltage. Leakage current may be measured using a leakage test meter (e.g., MC 190 Leakage test, Mantracourt Electronics LTD, UK) at a temperature of 25° C. and at a certain rated voltage after a charging time of from about 60 to about 300 seconds. Such ESR and normalized leakage current values may even be maintained after aging for a substantial amount of time at high temperatures. For example, the values may be maintained for about 100 hours or more, in some embodiments from about 300 hours to about 2500 hours, and in some embodiments, from about 400 hours to about 1500 hours (e.g., 500 hours, 600 hours, 700 hours, 800 hours, 900 hours, 1000 hours, 1100 hours, or 1200 hours) at temperatures ranging from about 100° C. to about 250° C., and, in some embodiments from about 100° C. to about 200° C. (e.g., 100° C., 125° C., 150° C., 175° C., or 200° C.).
The electrolytic capacitor of the present invention may be used in various applications, including but not limited to implantable medical devices, such as implantable defibrillators, pacemakers, cardioverters, neural stimulators, drug administering devices, etc. In one embodiment, for example, the capacitor may be employed in an implantable medical device configured to provide a therapeutic high voltage (e.g., between approximately 500 volts and approximately 850 volts, or, desirably, between approximately 600 Volts and approximately 900 volts) treatment for a patient. The device may contain a container or housing that is hermetically sealed and biologically inert. One or more leads are electrically coupled between the device and the patient's heart via a vein. Cardiac electrodes are provided to sense cardiac activity and/or provide a voltage to the heart. At least a portion of the leads (e.g., an end portion of the leads) may be provided adjacent or in contact with one or more of a ventricle and an atrium of the heart. The device may also contain a capacitor bank that typically contains two or more capacitors connected in series and coupled to a battery that is internal or external to the device and supplies energy to the capacitor bank. Due in part to high conductivity, the capacitor of the present invention can achieve excellent electrical properties and thus be suitable for use in the capacitor bank of the implantable medical device.
The present invention may be better understood by reference to the following example.
Capacitance (“CAP”), equivalent series resistance (“ESR”) and leakage current (“DCL”) were tested in an aqueous neutral electrolyte at a temperature of 37° C.±0.5° C.
Capacitance (“CAP”)
Capacitance may be measured using a Keithley 3330 Precision LCZ meter with Kelvin Leads with 2.2 volt DC bias and a 0.5 volt peak to peak sinusoidal signal. The operating frequency may be 120 Hz.
Equivalent Series Resistance (“ESR”)
Equivalence series resistance may be measured using a Keithley 3330 Precision LCZ meter with Kelvin Leads 2.2 volt DC bias and a 0.5 volt peak to peak sinusoidal signal. The operating frequency may be 120 Hz.
Leakage Current (“DCL”)
Leakage current may be determined by charging to 250V for 300 seconds without any resistor in series.
Anodes were formed from a nodular, magnesium-reduced tantalum powder (H.C. Starck) and flake tantalum powder (Global Advanced Metals). Samples of each powder type were pressed to 5.3 g/cm3 density using 4% of stearic acid lubricant. After delubrication, samples of each powder were then vacuum sintered at 1400° C. for 10 minutes in a hanging crucible. Upon sintering, the pellets were anodized in a solution containing 50% glycol/water with phosphoric acid at a temperature of 85° C. and a conductivity of 1 mS/cm. The formation current density was 45 mA/g for each sample. Anodization voltage of 220 volts was tested. The resulting anodes had a D-shape in which the length was about 32 millimeters, the width was about 23 millimeters, and the thickness was about 2 millimeters. The anodes were then joined together with two cathodes prepared from Pd/PEDT coated titanium sheets (0.1 mm thick) separated with two plastic meshes (0.2 mm thick). The resulting capacitors were then tested as described above. The results are set forth below.
As shown, the nodular powder was able to achieve a comparatively high capacitance and lower DCL. Using the capacitance values obtained and assuming an operating voltage, energy density (E=0.5*CV2) indicated the nodular powder also had a significantly higher energy density.
These and other modifications and variations of the present invention may be practiced by those of ordinary skill in the art, without departing from the spirit and scope of the present invention. In addition, it should be understood that aspects of the various embodiments may be interchanged both in whole or in part. Furthermore, those of ordinary skill in the art will appreciate that the foregoing description is by way of example only, and is not intended to limit the invention so further described in such appended claims.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5111327 | Blohm et al. | May 1992 | A |
| 5369547 | Evans | Nov 1994 | A |
| 5560761 | Naito | Oct 1996 | A |
| 5716511 | Melody et al. | Feb 1998 | A |
| 5808857 | Stevens | Sep 1998 | A |
| 5922215 | Pless et al. | Jul 1999 | A |
| 5930109 | Fishler | Jul 1999 | A |
| 5968210 | Strange et al. | Oct 1999 | A |
| 5983472 | Fayram et al. | Nov 1999 | A |
| 6094339 | Evans | Jul 2000 | A |
| 6162345 | Kinard et al. | Dec 2000 | A |
| 6193779 | Reichert et al. | Feb 2001 | B1 |
| 6197252 | Bishop et al. | Mar 2001 | B1 |
| 6231993 | Stephenson et al. | May 2001 | B1 |
| 6238456 | Wolf et al. | May 2001 | B1 |
| 6238810 | Strange et al. | May 2001 | B1 |
| 6246569 | Strange et al. | Jun 2001 | B1 |
| 6249423 | O'Phelan et al. | Jun 2001 | B1 |
| 6261434 | Melody et al. | Jul 2001 | B1 |
| 6267861 | Kinard et al. | Jul 2001 | B1 |
| 6346185 | Kinard et al. | Feb 2002 | B1 |
| 6377442 | Strange et al. | Apr 2002 | B1 |
| 6421226 | O'Phelan et al. | Jul 2002 | B1 |
| 6426864 | O'Phelan et al. | Jul 2002 | B1 |
| 6556863 | O'Phelan et al. | Apr 2003 | B1 |
| 6594140 | Evans et al. | Jul 2003 | B1 |
| 6635729 | Groenendaal et al. | Oct 2003 | B1 |
| 6659283 | Muffoletto et al. | Dec 2003 | B1 |
| 6786951 | He et al. | Sep 2004 | B2 |
| 6802951 | Hossick-Schott | Oct 2004 | B2 |
| 6802954 | Hemphill et al. | Oct 2004 | B1 |
| 6815306 | Strange et al. | Nov 2004 | B1 |
| 6858126 | Hemphill et al. | Feb 2005 | B1 |
| 6914769 | Welsch et al. | Jul 2005 | B2 |
| 6965510 | Liu et al. | Nov 2005 | B1 |
| 6987663 | Merker et al. | Jan 2006 | B2 |
| 7043300 | O'Phelan et al. | May 2006 | B2 |
| 7090762 | Tripp et al. | Aug 2006 | B2 |
| 7150767 | Schneider et al. | Dec 2006 | B1 |
| 7150776 | Shekhter et al. | Dec 2006 | B2 |
| 7196899 | Feger et al. | Mar 2007 | B1 |
| 7244279 | Seitz et al. | Jul 2007 | B2 |
| 7248462 | Melody et al. | Jul 2007 | B2 |
| 7271994 | Stemen et al. | Sep 2007 | B2 |
| 7286336 | Liu et al. | Oct 2007 | B2 |
| 7341705 | Schnitter | Mar 2008 | B2 |
| 7342774 | Hossick-Schott et al. | Mar 2008 | B2 |
| 7381396 | Thomas et al. | Jun 2008 | B2 |
| 7385802 | Ribble et al. | Jun 2008 | B1 |
| 7419926 | Schnitter et al. | Sep 2008 | B2 |
| 7431751 | Shekhter et al. | Oct 2008 | B2 |
| 7445646 | Strange et al. | Nov 2008 | B1 |
| 7483260 | Ziarniak et al. | Jan 2009 | B2 |
| 7515396 | Biler | Apr 2009 | B2 |
| 7531010 | Feger et al. | May 2009 | B1 |
| 7544218 | Norton et al. | Jun 2009 | B2 |
| 7558051 | O'Phelan et al. | Jul 2009 | B2 |
| 7678175 | Shekhter et al. | Mar 2010 | B2 |
| 7678259 | Melody et al. | Mar 2010 | B2 |
| 7684171 | Rorvick et al. | Mar 2010 | B2 |
| 7715174 | Beauvais et al. | May 2010 | B1 |
| 7727372 | Liu et al. | Jun 2010 | B2 |
| 7731893 | Freeman et al. | Jun 2010 | B2 |
| 7824463 | Haas | Nov 2010 | B2 |
| 7837743 | Gaffney et al. | Nov 2010 | B2 |
| 7846217 | Poplett | Dec 2010 | B2 |
| 7879217 | Goad et al. | Feb 2011 | B2 |
| 7898794 | Haas et al. | Mar 2011 | B2 |
| 8038866 | Jiang et al. | Oct 2011 | B2 |
| 8206600 | Ribble | Jun 2012 | B2 |
| 8298478 | Hintz | Oct 2012 | B2 |
| 8313621 | Goad et al. | Nov 2012 | B2 |
| 8514547 | Galvagni et al. | Aug 2013 | B2 |
| 8619408 | Sherwood et al. | Dec 2013 | B2 |
| 8687347 | Bates et al. | Apr 2014 | B2 |
| 9076592 | Masheder et al. | Jul 2015 | B2 |
| 20050013765 | Thomas et al. | Jan 2005 | A1 |
| 20050019581 | Schnitter | Jan 2005 | A1 |
| 20050103638 | Schnitter et al. | May 2005 | A1 |
| 20060091020 | Hossick-Schott et al. | May 2006 | A1 |
| 20090244811 | Pascenko | Oct 2009 | A1 |
| 20100318140 | Hintz et al. | Dec 2010 | A1 |
| 20120179217 | Bates et al. | Jul 2012 | A1 |
| 20130141841 | Dreissig | Jun 2013 | A1 |
| 20130242466 | Masheder et al. | Sep 2013 | A1 |
| 20140218843 | Evans | Aug 2014 | A1 |
| 20140268497 | Weaver et al. | Sep 2014 | A1 |
| 20140268499 | O'Phelan et al. | Sep 2014 | A1 |
| 20160064150 | Haas | Mar 2016 | A1 |
| Number | Date | Country |
|---|---|---|
| 1308566 | Aug 2001 | CN |
| WO 0067936 | Nov 2000 | WO |
| Entry |
|---|
| Haas et al., “Recent Advances in the Development and Processing of Tantalum and Niobium Capacitor Powders,” lecture held during the meeting “CARTS International” from Mar. 31-Apr. 3, 2014, in the Biltmore Hotel, Santa Clara, California, USA, published in the conference transcript on pp. 327-343. |
| Data Sheet for “NH 175 Capacitor Grade Tantalum Powder” from H.C. Starck, Sep. 7, 2012, 4 pages. |
| Observations by third parties according to German Patents Act Section 43 (3), Nov. 21, 2016, 23 pages. |
| Third-Party Comments on Patent Application FR 3 029 226 dated Feb. 20, 2017, 13 pages. |
| French Preliminary Search dated Oct. 25, 2017, 4 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20160148757 A1 | May 2016 | US |