Wet-End Manufacturing Process for Bitumen-Impregnated Fiberboard

Abstract
A process for manufacturing fiberboard by preparing a fiber slurry mixture including containing cellulose fibers and water then atomizing a liquid bituminous material, such as asphalt. The liquid bituminous material is atomized by mixing it with a pressurized gas, such as compressed air, forming a mist comprising droplets of bituminous material having a diameter between 20 microns and 50 microns. A water spray solidifies the bituminous material droplets thereby forming bituminous particles which fall into the fiber slurry within the spray chamber. From there the slurry is sheared, dewatered, and dried, forming a finished fiberboard.
Description
BACKGROUND OF THE INVENTION

The present disclosure relates to a process for manufacturing fiber expansion joints. In particular, the present disclosure relates to a method for introducing fine particles of bituminous material, such as asphalt, into a slurry fiber mixture for formation into boards used in fiber expansion joint applications. Although the term “asphalt” is used throughout the present disclosure, it should be understood that any bituminous material, including tars and pitches, may be employed and still remain within the scope of the present disclosure.


Asphalt impregnated expansion joints are used in connection with concrete structures to relieve stresses created by thermal expansion and contraction of the concrete and prevent failure of the concrete caused by changes in ambient temperature. Typical applications for asphalt impregnated fiber expansion joints include sidewalks, driveways, floor slabs, streets, highways, airport runways, and similar applications. Because such concrete expansion joints are installed in applications exposed to the weather, it is desirable that water absorption be limited to prevent degradation of the expansion joint. It is also desirable that concrete expansion joints have strength and resiliency. Therefore, asphalt impregnated fiberboard expansion joints are required to meet or exceed the requirements of ASTM Standard Specification D 1751-04.


ASTM D 1751-04 requires that an expansion joint for concrete paving and structural applications have specified material characteristics, including that 35% weight of the finished fiberboard shall be asphalt uniformly distributed throughout the board. Additionally, the stress required to compress a test specimen of a fiber expansion joint to 50% of its original thickness must not be less than 100 psi nor greater than 750 psi. When a fiber expansion joint is compressed to 50% of its original thickness having three of its edges restrained, the amount of extrusion of the free edge cannot exceed 0.25 inch. A fiber expansion joint that has been compressed to 50% of its original thickness must recover at least 70% of its thickness within 10 minutes after the applied load is released. A fiber expansion joint must not have a density less than 19 lb./cu. ft. A fiber expansion joint test specimen with four square-cut edges, when submerged horizontally under 1 inch of water at 70 degrees F. may not absorb more than 15 volume % in 24 hours for a nominal volume of ½ inch and no more than 20 volume % for all other thicknesses.


Fiber expansion joints have been made by saturating fiberboard in an asphalt/solvent solution, allowing the asphalt solvent mixture to be absorbed into the fibers, and allowing the solvent to evaporate. Fiber expansion joints have also been made by adding solid asphalt particles into a slurry of fibers. The asphalt particles are dispersed in the fiber slurry by mechanical mixing, and the slurry is dewatered, pressed into a board and dried.


BRIEF SUMMARY OF THE INVENTION

The present disclosure relates to a process for manufacturing fiberboard including the steps of preparing a fiber slurry mixture by adding a material containing cellulose fibers to water and agitating the fiber slurry mixture and transferring the fiber slurry mixture to a spray chamber. Then a bituminous material, such as asphalt, is heated to a temperature between 300 and 440 degrees F., wherein the bituminous material is in a liquid state. The liquid bituminous material is atomized within the spray chamber by mixing it with a pressurized gas, such as compressed air, forming a mist comprising droplets of bituminous material having a diameter between 20 microns and 50 microns. A water spray solidifies the bituminous material droplets thereby forming bituminous particles which fall into the fiber slurry within the spray chamber. From there the slurry is sheared, dewatered, and dried, forming a finished fiberboard.


The present disclosure also relates to a process for atomizing a bituminous material, such as asphalt, to produce solid particles ranging in size from 20 microns to 50 microns. A bituminous material is heated to a temperature between 300 and 450 degrees F., wherein the bituminous material is in a liquid state. The liquid bituminous material is atomized by mixing the liquid bituminous material with a gas, such as compressed air, by passing each through a nozzle. The gas is supplied at a pressure between 10 psi and 50 psi, but preferably between 20 psi and 40 psi and a temperature between 200 degrees F. and 300 degrees F. Mixing the liquid bituminous material and the compressed gas produces a mist of bituminous droplets having a diameter between 20 microns and 50 microns. A water spray having a temperature between 40 degrees F. and 60 degrees F., but preferably between 45 degrees F. and 55 degrees F. is applied to the bituminous mist, solidifying the bituminous material droplets and thereby forming bituminous particles having a diameter between 20 microns and 50 microns.





BRIEF DESCRIPTION OF SEVERAL VIEWS OF THE DRAWINGS

The present disclosure will be described hereafter with reference to the attached drawings which are given as a non-limiting example only, in which:



FIG. 1 is a schematic representation of the process of the present disclosure;



FIG. 2 is a schematic representation of the spray tank of the present disclosure;



FIG. 3 is a section view of an asphalt spray nozzle;



FIG. 4 is an end view of the nozzle shown in FIG. 3.





DETAILED DESCRIPTION OF THE INVENTION

The process for manufacturing an asphalt-impregnated fiberboard of the present disclosure introduces fine asphalt particles into a fiber slurry by atomizing molten asphalt and spray cooling the atomized asphalt. The asphalt particles may then be added directly to the fiber slurry or stored for later use.


Referring now to FIG. 1, a fiber slurry is prepared in a pulper 10 by adding material containing cellulose fibers, such as wood pulp, sugar cane, switch grass, straw, recycled paper pulp, or other cellulose containing organic material to water. A mixer 12, agitates the fiber slurry, maintaining the fibers in suspension. The fiber slurry is transferred to a pulp chest 14 where it is held while awaiting further processing, depending on production parameters. Depending on the application, a pump 16 may be used to transfer the fiber slurry from the pulper 10 to the pulp chest 14. Alternatively, the fiber slurry may be transferred by gravity into the pulp chest 14.


Asphalt is heated in a tank 20 to a temperature between 300 and 440 degrees F. At this temperature, the asphalt is in a liquid phase and flows freely. From the tank 20, a pump 22 transfers the molten asphalt through a filter to remove any impurities such as solids or coking that may have formed during the heating process. A heater 26 is provided to further heat the molten asphalt to a temperature between 400 and 450 degrees F. The heater 26 also provides heat to the piping carrying the molten asphalt to the spray chamber 30.


In an exemplary embodiment, the heater 26 is a shell and tube heat exchanger having hot mineral oil on the shell side and the molten asphalt on the tube side. The heater maintains mineral oil at a temperature of approximately 600 degrees F. The mineral oil is circulated within the shell side of the heater, transferring heat to the molten asphalt as it passes through the tube side of the heater. The asphalt transfer piping 28 is constructed of double lumen pipe, wherein the heated oil circulates through an outer lumen to maintain the temperature of the molten asphalt as it is flows through an inner lumen as it is transferred from the asphalt tank to the spray chamber.


Referring now to FIG. 2, the spray chamber 30 includes a housing 32, enclosing an atomization head 34. The atomization head 34 includes a plurality of asphalt nozzles 36. Each nozzle is connected to the asphalt piping 28. In an exemplary embodiment, a pump 38 is connected in-line with each nozzle 36 for metering the flow of asphalt. Each nozzle 36 is also connected to a pressurized air manifold 40.


An air compressor, 42 supplies a source of compressed air which is dried and heated to a temperature between 200 degrees F. and 300 degrees F. The dried compressed air is provided to each nozzle 36 through a solenoid valve 44. The solenoid valve 44 allows the compressed air to be applied to only those nozzles 36 in use providing bitumen to the slurry in the spray chamber 30. The compressed air may be provided at a pressure between 10 psi and 50 psi. In an exemplary embodiment, the compressed air is provided at a pressure of between approximately 20 psi and 40 psi. It has been found that moist air causes the molten asphalt to solidify prematurely, resulting in clogging of the nozzles. It is therefore desirable that the compressed air be passed through a suitable commercially available air dryer before it is introduced into the process.


Referring to FIGS. 3 and 4, each nozzle 36 includes a body 46 having a liquid passage 48, through which molten asphalt flows, surrounded by a plurality of gas passages 50, which provide pressurized air as shown in FIGS. 3 and 4. The liquid passage 48 and the gas passages 50 discharge into an atomization chamber 52. The liquid passage 48 may be located along the longitudinal axis of the nozzle body 46 and gas passages 50 symmetrically disposed about liquid passage 48. Such a nozzle design is shown in U.S. Pat. No. 6,997,405 which is herein incorporated by reference. The atomization chamber 52 is configured to combine the molten asphalt and the pressurized air to produce an asphalt mist 54. The atomization chamber 52 includes a conical wall 53 having an angle φ which may be varied depending on the desired atomization pattern. In an exemplary embodiment of the present disclosure, the atomization chamber 54 has a wall angle φ of 45 degrees, which produces a conical spray pattern having a vertex angle of 45 degrees. The atomized asphalt mist 54 is discharged from atomization chamber 54 as liquid asphalt droplets having a diameter of approximately 20 to 50 microns. The size of the asphalt droplets may be varied by adjusting the air pressure. Generally, higher air pressure produces atomized asphalt having a smaller particle size.


The spray chamber 30 shown in FIG. 2 depicts five spray nozzles for clarity. However, in an exemplary embodiment of the present disclosure, the spray chamber 30 includes a spray head 34 having twelve spray nozzles 36. Each spray nozzle is designed for an asphalt flow rate of 1 gal/min. Having solenoid valves controlling the asphalt flow to individual nozzles allows for varying the asphalt flow rate depending on the desired production rate and/or asphalt concentration for the finished product. For example, the amount of asphalt added to the fiber slurry may be adjusted from about 1 gal/min, with a single solenoid valve open at a minimum production rate to about 12 gal/min at high production rates. Also, the number of nozzles in operation may be driven as a function of the desired asphalt content in a finished product.


The spray chamber 30 also includes a plurality of water spray heads 56 arranged proximate to the discharge of the asphalt nozzles 36. The water spray heads 56 are connected to a supply of chilled water maintained at a temperature of approximately 40 degrees F. to 60 degrees F. In an exemplary embodiment of the present disclosure, the chilled water is provided at a temperature between 45 degrees F. and 55 degrees F. The spray heads 56 are configured to direct a water mist towards the atomized asphalt discharge at a spray angle θ of approximately 45 degrees downward. The chilled water mist solidifies the molten droplets of the atomized asphalt mist, forming solid asphalt particles having a size of 20 to 50 microns.


A pulp supply line 58 connects the pulp chest 14 to the spray chamber 30. A slurry feed pump 60 is provided in the pulp supply line 58 to transfer the fibrous material slurry from the pulp chest 14 to the spray chamber 30. The slurry feed pump 60 may be of variable speed and connected to a control system (not shown) to accommodate variable production throughput.


The fibrous material slurry is pumped into the spray chamber 30 to a predetermined level 62. As the molten asphalt mist 54 is cooled and the asphalt droplets solidify, fine asphalt particles drop into the fibrous material slurry in the bottom of the spray chamber 30. One or more mechanical mixers 64 agitate the fibrous material slurry, maintaining a homogeneous mixture of fibers and asphalt particles.


The slurry in the spray chamber 30 should contain about 8% weight to about 10% weight fiber or solid content. The slurry should also contain about 10% weight to about 30% weight asphalt.


A discharge pump 66 is connected to the outlet of the spray chamber 30 and directs the slurry to the next step in the process. The discharge pump 66 may be coordinated with the fibrous slurry feed pump 60 to maintain a predetermined slurry level and dwell time within the spray chamber 30.


From the spray chamber 30, the slurry is transferred to a refiner 68 where the slurry is sheared by a series of mixing plates. The mixing plates are mounted on a shaft and rotate relative to each other. As the slurry flows through the refiner, it passes between the mixing plates, shearing the slurry and in the process shredding the fibrous material. The shredding of the cellulose fibers forms a large amount of surface area for interaction with and dispersion of the asphalt particles, allowing for even distribution of the asphalt particles throughout the fibers.


Additional ingredients may be added to the slurry including waxes, starches, alum, and other fillers and agents. These additional ingredients and fillers may be added at any point in the process prior to dewatering where they will become intermixed with the other components, as is known in the art. For example a wax, such as paraffin, may be added to the slurry in a concentration of about 1.0% weight to about 2.5% weight; starch may be added in a concentration of about in a concentration of about 1.0% weight to about 3.0% weight; and aluminum sulfate may be added in a concentration of about 1.0% weight to about 2.0% weight.


In an alternative embodiment of the present disclosure, a dye may be added to the slurry before drying. The dye serves to color the fibrous material to produce an evenly colored finished fiberboard improving the aesthetic appearance of the fiberboard. The addition of a dye, also serves to regulate the pH of the slurry. The dye should have a pH of about 6 to about 8. It has been discovered that a slurry having a pH of approximately 6.8 has been found to promote better adhesion of the asphalt particles to the cellulose fibers, and thus improved distribution of asphalt throughout the finished fiberboard. The dye may be a generally commercially available water-based dye. Alternatively, a solvent based dye may be used. However, a solvent-based dye contains volatile compounds which may be harmful to the environment and which may present the risk of fire or explosion when subjected to heat while drying.


A slurry transfer pump 70 pumps the slurry mixture from the refiner 68 to a ready chest 72 where it is held for dewatering. Another transfer pump 74 pumps the slurry from the ready chest 72 to a Fourdrinier-type press 76 as is commonly known in the art, where the slurry is dewatered and formed into a wet fiber mat.


After the dewatered wet mat leaves the Fourdrinier press 76, the mat passes through a shear 78 where it is cut before being fed into a dryer 80. The mat is dried for approximately 1-3 hours depending on its physical characteristics. The finished fiberboard preferably should have about 10% weight to about 40% weight total asphalt content and less than about 3% total moisture content. After being dried, the fiberboard may pass through a second shear 82 again be cut to a commercially desirable size. The finished fiberboard may then be stacked 84 for further processing or for shipment.


Alternatively, an additional coating of asphalt or other petroleum fluid may be applied to the outer surface of the fiberboard to provide additional resistance to moisture penetration. A coater 86 applies by roller the additional coating to the major surfaces of the fiberboard. For example, a commercially available hot melt double-sided roller coater manufactured by the Black Bros. Co. may be used. Fluids such as flux oil or fuel oil, in addition to asphalt, have been found to resist water penetration into the finished fiberboard.


Although ASTM D 1751-04 specifies that the finished fiber board have an asphalt content of at least 35.0% weight, a number of tests were preformed on fiber boards manufactured by the process of the present disclosure, varying the % weight of asphalt. For example, an asphalt-impregnated fiberboard manufactured by the process of the present disclosure containing 15% weight asphalt was tested according to ASTM Method D 545. The results are summarized in Table 1 below:









TABLE 1







asphalt content 15% weight











Property
Test Results
ASTM 1751-04















Compression (psi)
150
Pass



Extrusion (in.)
0.30
Fail



Recovery (%)
65
Fail



Density (lb./cu. Ft.)
20
Pass



Water absorption
24
Fail










A second test was performed on a fiberboard containing 25% weight asphalt content. The results are summarized in Table 2 below:









TABLE 2







asphalt content 25% weight











Property
Test Results
ASTM 1751-04















Compression (psi)
350
Pass



Extrusion (in.)
0.25
Pass



Recovery (%)
75
Pass



Density (lb./cu. Ft.)
21
Pass



Water absorption
19
Fail



(volume %)










A third test was performed on a fiberboard containing 35% weight asphalt content. The results are summarized in Table 3 below:









TABLE 3







asphalt content 35% weight











Property
Test Results
ASTM 1751-04















Compression (psi)
540
Pass



Extrusion (in.)
0.15
Pass



Recovery (%)
78
Pass



Density (lb./cu. Ft.)
22
Pass



Water absorption
12
Pass



(volume %)












The process of the present disclosure allows introduction of very fine asphalt particles into the fibrous slurry mix. It has been discovered that small asphalt particle size allows for better dispersion of the asphalt throughout the fibers and increased bonding between asphalt and fiber. Thus a fiberboard may be produced exhibiting improved characteristics over asphalt-impregnated fiberboards produced by methods presently known in the art.


While this disclosure has been described as having exemplary embodiments, this application is intended to cover any variations, uses, or adaptations using the general principles set forth herein. It is envisioned that those skilled in the art may devise various modifications and equivalents without departing from the spirit and scope of the disclosure as recited in the following claims. Further, this application is intended to cover such departures from the present disclosure as come within the known or customary practice within the art to which it pertains.

Claims
  • 1. A process for manufacturing fiber board comprising the steps of: preparing a fiber slurry mixture by adding a material containing cellulose fibers to water and agitating the fiber slurry mixture;transferring the fiber slurry mixture to a spray chamber;heating a bituminous material to a temperature between 300 and 440 degrees F., wherein the bituminous material is in a liquid state;atomizing the liquid bituminous material within the spray chamber by mixing the liquid bituminous material with a pressurized gas, forming a mist comprising droplets of bituminous material having a diameter between 20 microns and 50 microns;solidifying the bituminous material droplets by spraying water into the mist thereby forming bituminous particles which fall into the fiber slurry within the spray chamber;shearing the slurry containing cellulose fibers and bituminous particles;dewatering the slurry containing cellulose fibers and bituminous particles, leaving a wet mat containing fibers and bituminous material;drying the wet mat thereby forming a fiber board; andoptionally, further including the step of applying a coating to both major sides of the dried fiberboard.
  • 2. The process of claim 1, wherein after heating the bituminous material, including the additional step of heating the bituminous material to a temperature between 400 and 450 degrees F.
  • 3. The process of claim 2 wherein the additional step of further heating the bituminous material is performed in a heat exchanger, wherein mineral oil heated to a temperature of approximately 600 degrees F. is circulated about the heat exchanger as the bituminous material passes through the heat exchanger.
  • 4. The process of claim 1 wherein the bituminous material is atomized by mixing with a gas, optionally compressed air, which may be heated to a temperature between 200 degrees F. and 300 degrees F., wherein the gas has a pressure of between approximately 10 psi and 50 psi; alternatively, wherein the gas has a pressure of between approximately 20 psi and 40 psi.
  • 5. The process of claim 1 wherein the material containing cellulose fibers is selected from the group consisting of wood pulp, sugar cane, switch grass, straw, and recycled paper pulp.
  • 6. The process of claim 1 wherein the solid content of the slurry is less than about 10% weight but greater than about 8% weight.
  • 7. The process of claim 1 wherein the asphalt content of the slurry is less than about 30% weight but greater than about 10% weight.
  • 8. The process of claim 1 further including the step of adding a wax to the slurry wherein the wax content is greater than about 1.0% weight but less than about 2.5% weight; optionally, further including the step of adding a starch to the slurry wherein the starch content is greater than about 1.0% weight but less than about 3.0% weight; optionally, further including the step of adding aluminum sulphate to the slurry wherein the aluminum sulfate content is greater than about 1.0% weight but less than about 2.0% weight; optionally, further including the step of adding a solvent-based or water-based dye to the slurry wherein the dye content is greater than about 0.001% weight of the slurry but less than about 2.0% weight of the slurry.
  • 9. The process of claim 8 wherein the dye has a pH between about 6 and about 8.
  • 10. The process of claim 1 wherein the coating is selected from the group consisting of asphalt, flux oil, and fuel oil.
  • 11. The process of claim 10 wherein the total content of the coating is between about 1% and about 10% weight of the fiber board.
  • 12. The process of claim 1 wherein the total bitumen content of the fiberboard is between about 10% and 40% by weight.
  • 13. A process for producing bituminous particles by atomizing a molten bituminous material comprising the steps of: heating a bituminous material to a temperature such that the bituminous material is in a liquid state;passing the liquid bituminous material through a nozzle, the nozzle having a liquid passage and a plurality of gas passages, and an atomization chamber, wherein the liquid bituminous material and a pressurized gas provided through the plurality of gas passages are mixed together within the atomization chamber forming a mist of liquid bitumen droplets;solidifying the liquid bitumen droplets by spraying with water;wherein the bituminous material is heated to a temperature between 300 and 440 degrees F.; andwherein the bituminous material is atomized by mixing with a gas having a pressure of between approximately 10 psi and 50 psi; alternatively, wherein the bituminous material is atomized by mixing with a gas having a pressure of between approximately 20 psi and 40 psi.
  • 14. The process of claim 13 further including the step of additionally heating the bituminous material to a temperature of between 400 to 450 degrees F.
  • 15. The process of claim 13 wherein the pressurized gas is compressed air.
  • 16. The process of claim 15 wherein the compressed air is heated to a temperature between 200 degrees F. and 300 degrees F.
  • 17. A process for manufacturing fiber board comprising the steps of: preparing a fiber slurry mixture by adding a material containing cellulose fibers to water and agitating the fiber slurry mixture,the material containing cellulose fibers being selected from the group consisting of wood pulp, sugar cane, switch grass, straw, and recycled paper pulp, and wherein the solid content of the slurry is less than about 10% weight but greater than about 8% weight;heating a bituminous material to a temperature between 300 and 450 degrees F., wherein the bituminous material is in a liquid state;atomizing the liquid bituminous material within the spray chamber by mixing the liquid bituminous material with a gas,wherein the gas is supplied at a pressure between 20 psi and 40 psi, andwherein the gas is supplied at a temperature between 200 degrees F. and 300 degrees F.,producing a mist comprising droplets of bituminous material having a diameter between 20 microns and 50 microns;solidifying the bituminous material droplets by spraying water into the mist,the water having a temperature between 45 degrees F. and 55 degrees F., thereby forming bituminous particles having a diameter between 20 microns and 50 microns which fall into the fiber slurry within the spray chamber, wherein the asphalt content of the slurry is less than about 30% weight but greater than about 10% weight;shearing the slurry containing cellulose fibers and bituminous particles;dewatering the slurry containing cellulose fibers and bituminous particles, leaving a wet mat containing fibers and bituminous material; anddrying the wet mat thereby forming a fiber board, the finished fiber board having a total bitumen content between about 10% and 40% by weight.
  • 18. The process of claim 17 wherein the gas is compressed air.
  • 19. A process for producing bituminous particles from a molten bituminous material comprising the steps of: heating a bituminous material to a temperature such that the bituminous material is in a liquid state;passing the liquid bituminous material through a liquid passage for receiving an adjustable flow of liquid bituminous material thereby forming liquid bitumen droplets; andallowing the liquid bitumen droplets to enter a slurry and solidify in the slurry, wherein the slurry comprises a material containing cellulose fibers and water.
  • 20. The process of claim 19 wherein the liquid passage is disposed within a nozzle, the nozzle including a plurality of gas passages configured to allow flow of a pressurized gas and further comprising the step of mixing the flow of liquid bituminous material with the flow of pressurized gas to form a mist of liquid bitumen droplets; and wherein the bituminous material is atomized by mixing with the pressurized gas having a pressure of between approximately 10 psi and 50 psi; alternatively, wherein the bituminous material is atomized by mixing with the pressurized gas having a pressure of between approximately 20 psi and 40 psi.
  • 21. The process of claim 20 wherein the pressurized gas is compressed air that is optionally heated to a temperature between 200 degrees F. and 300 degrees F.
  • 22. The process of claim 19 wherein the bituminous material is heated to a temperature between 300 and 440 degrees F.
  • 23. The process of claim 22 further including the step of additionally heating the bituminous material to a temperature of between 400 to 450 degrees F.
  • 24. The process of claim 19 wherein the material containing cellulose fibers is selected from the group consisting of wood pulp, sugar cane, switch grass, straw, and recycled paper pulp, and wherein the solid content of the slurry is less than about 10% weight.
  • 25. The process of claim 19 wherein the bituminous material content of the slurry is less than about 35% weight of total solids but greater than about 10% weight of total solids.
RELATED APPLICATIONS

This application claims priority to, and is a continuation of, co-pending U.S. application Ser. No. 13/526,177, having a filing date of Jun. 18, 2012, which is a continuation of U.S. application Ser. No. 13/248,758, having a filing date of Sep. 29, 2011, now U.S. Pat. No. 8,241,463, which is a continuation of U.S. patent application Ser. No. 12/881,721, having a filing date of Sep. 14, 2010, now U.S. Pat. No. 8,038,845, which is a divisional of U.S. patent application Ser. No. 12/200,993, having a filing date of Aug. 29, 2008, now U.S. Pat. No. 7,815,772, all of which are incorporated herein by reference in their entireties.

Divisions (1)
Number Date Country
Parent 12200993 Aug 2008 US
Child 12881721 US
Continuations (3)
Number Date Country
Parent 13526177 Jun 2012 US
Child 13772942 US
Parent 13248758 Sep 2011 US
Child 13526177 US
Parent 12881721 Sep 2010 US
Child 13248758 US