Embodiments of the present invention are directed to white light emitting devices; in particular, although not exclusively, to white light emitting devices comprising multiple photoluminescence materials. More particularly, although not exclusively, embodiments concern white light emitting devices comprising first and second solid-state light emitters, LEDs, covered by first and second photoluminescence materials.
White light emitting LEDs (“white LEDs”) include one or more photoluminescence materials (typically inorganic phosphor materials), which absorb a portion of the excitation light (typically blue or red) emitted by the LED and re-emit light of a different color (wavelength). The portion of the excitation light generated by the LED that is not absorbed by the photoluminescence material combined with the light emitted by the photoluminescence material provides light which appears to the eye as being white in color. Due to their long operating life expectancy (>50,000 hours) and high luminous efficacy (100 lumens per watt and higher), white LEDs are rapidly replacing conventional fluorescent, compact fluorescent and incandescent lamps.
One form of white light emitting devices is Chip on Board (COB) in which multiple LED Chips (Dies) are located on a substrate before one or more photoluminescence materials is disposed thereon. Typically, a COB white LED comprises blue LED Chips which are covered by a mixture of red and green/yellow photoluminescence materials. However, COB white LEDs can suffer from low luminous efficacy.
Some white light emitting LEDs comprise red LED Chips that do not include phosphor/photoluminescence materials. More particularly, the red LED Chips do not involve wavelength conversion to generate red light. While white light emitting LEDs comprising red LED Chips are considered to be relatively efficient compared with other forms, they can suffer from poor thermal stability; that is, they can exhibit poor color stability with changes in temperature; due to blue and red LED chips having different thermal characteristics.
The present invention intends to address and/or overcome the limitations discussed above by presenting new designs and methods not hitherto contemplated nor possible by known constructions. More particularly, there is a need for a white light emitting device that exhibits improved luminous efficacy and thermal stability.
According to an aspect of the present invention, there is provided a white light emitting device comprising: first and second LEDs operable to generate excitation light having a dominant wavelength in a range from 440 nm to 480 nm and mounted on a substrate; a first photoluminescence material which generates light having a peak emission wavelength in a range from 500 nm to 590 nm; and a second photoluminescence material which generates light having a peak emission wavelength in a range from 600 nm to 650 nm, wherein the first LED is covered by the first photoluminescence material, and the second LED is covered by the first and second photoluminescence materials. It may be that the first LED is covered by the first photoluminescence material only, and the second LED is covered by both the first and second photoluminescence materials.
The provision of a white light emitting device formed in accordance with the invention that comprises a combination of a first and second photoluminescence material exhibits improved luminous efficacy and thermal stability compared with known constructions. More particularly, the arrangement in which the first LED is covered by the first photoluminescence material, and the second LED is covered by the first and second photoluminescence materials converts the blue light into red light more effectively. That is the majority of the blue excitation light from the second LED is converted by the second photoluminescence material to light having a peak emission wavelength in a range from 600 nm to 650 nm, that is red light. White light is thus generated from the combination of the unconverted blue excitation light from the first and second LEDs, the light having a peak emission wavelength in a range from 500 nm to 590 nm generated by the first photoluminescence material, and the light having a peak emission wavelength in a range from 600 nm to 650 nm generated by the second photoluminescence material.
It may be that the first photoluminescence material covers the light emitting faces of the first LED. More particularly, the first photoluminescence material may cover the faces opposite and adjacent the substrate on which the first LED is mounted. This may improve the uniformity of light emission from the first LED, for example.
The first and second photoluminescence materials may cover the light emitting faces of the second LED. More particularly, the first and second photoluminescence materials may cover the faces opposite and adjacent the substrate on which the second LED is mounted. This may improve the uniformity of light emission from the second LED, for example. This may also improve luminous efficacy since more of the blue excitation light will be exposed to the first and second photoluminescence materials leading to improved levels of converted light having a peak emission wavelength ranging from 500 nm to 590 nm and from 600 nm to 650 nm.
The first photoluminescence material may be directly in contact with the first LED. This may improve luminous efficacy since more of the blue excitation light will be exposed to the first photoluminescence material leading to improved levels of converted light having a peak emission wavelength ranging from 500 nm to 590 nm.
In some embodiments, the first photoluminescence material may be located remotely to the first and second LEDs. It may be that another material is located between the first photoluminescence material and the first and second LEDs, for instance. This enables the white light emitting device of the present invention to be more versatile with regard to the different types of photoluminescence materials or other materials that it includes.
The first photoluminescence material may be in the form of a component. This may allow retro-fitting of such a component so that the white light emitting device can be assembled and disassembled more easily. It may also allow simple replacement of the component having the first photoluminescence material with a different first photoluminescence material to achieve a desired color temperature or luminous efficacy for instance.
The second photoluminescence material may be directly in contact with the second LED. This may improve luminous efficacy since the second photoluminescence material will be exposed to more of the blue excitation light leading to improved levels of converted light having a peak emission wavelength ranging from 600 nm to 650 nm.
The first photoluminescence material may generate light having a peak emission wavelength in a range from 520 nm to 530 nm.
The second photoluminescence material may generate light having a peak emission wavelength in a range from 620 nm to 635 nm.
It may be that the first photoluminescence material comprises a first phosphor material and/or the second photoluminescence material comprises a second phosphor material.
The first photoluminescence/phosphor material may be excitable to generate white light having a correlated color temperature of 5000K to 6500K. Similarly, the second photoluminescence/phosphor material may be excitable to, in combination with the first phosphor material, generate white light having a correlated color temperature of 2700K to 3500K. In this way, the white light emitting device may be color tunable.
The first phosphor material may comprise at least one selected from a garnet (YAG) phosphor of general composition Y3-x(Al1-yGay)5O2:Cex; (Y,Ba)3-x(Al1-yGay)5O12:Cex; a LuAG phosphor of general composition Lu3-x(Al1-yMy)5O12:Cex where M=Mg, Ca, Sr, Ba, Ga; an orthosilicate phosphor of general composition A2SiO4:Eu where A=Mg, Ca, Sr, Ba, (Sr1-xBax)2SiO4:Eu; and or an oxynitride phosphor of general composition MxSi12-(m+n)Alm+nOnN16-n:Eu where M=Mg, Ca and/or Sr.
The second phosphor material may comprise at least one selected from a nitride (CASN) phosphor of general composition (Ca1-xSrx)AlSiN3:Eu; a nitride (2:5:8) phosphor of general composition Ba2-xSrxSi5N8:Eu; MSe1-xSx:Eu where M=Mg, Ca, Sr, Ba, Zn; CaSe1-xSx:Eu, (Sr1-xMx)yEuzSiO5 where M=Ba, Mg, Ca, Zn; a complex fluoride phosphor of general composition K2SiF6:Mn4+; and K2TiF6:Mn4+.
It may be that the first photoluminescence material comprises a first quantum dot material and/or the second photoluminescence material comprises a second quantum dot material. A quantum dot (QD) is a portion of matter (e.g. semiconductor) whose excitons are confined in all three spatial dimensions that may be excited by radiation energy to emit light of a particular wavelength or range of wavelengths. QDs can comprise different materials, for example cadmium selenide (CdSe). The color of light generated by a QD is enabled by the quantum confinement effect associated with the nano-crystal structure of the QD. The energy level of each QD relates directly to the physical size of the QD. For example, the larger QDs, such as red QDs, can absorb and emit photons having a relatively lower energy (i.e. a relatively longer wavelength). On the other hand, green QDs, which are smaller in size can absorb and emit photons of a relatively higher energy (shorter wavelength). Examples of suitable QDs can include: CdZnSeS (cadmium zinc selenium sulfide), CdxZn1-x Se (cadmium zinc selenide), CdSexS1-x (cadmim selenium sulfide), CdTe (cadmium telluride), CdTexS1-x (cadmium tellurium sulfide), InP (indium phosphide), InxGa1-xP (indium gallium phosphide), InAs (indium arsenide), CuInS2 (copper indium sulfide), CuInSe2 (copper indium selenide), CuInSxSe2-x (copper indium sulfur selenide), Cu InxGa1-x S2 (copper indium gallium sulfide), CuInxGa1-xSe2 (copper indium gallium selenide), CuInxAl1-x Se2 (copper indium aluminum selenide), CuGaS2 (copper gallium sulfide) and CuInS2xZnS1-x (copper indium selenium zinc selenide). The optical properties of the core nano-crystals in one material can be altered by growing an epitaxial-type shell of another material. Depending on the requirements, the core/shell nano-crystals can have a single shell or multiple shells. The shell materials can be chosen based on the band gap engineering. For example, the shell materials can have a band gap larger than the core materials so that the shell of the nano-crystals can separate the surface of the optically active core from its surrounding medium. In the case of the cadmium-based QDs, e.g. CdSe QDs, the core/shell quantum dots can be synthesized using the formula of CdSe/ZnS, CdSe/CdS, CdSe/ZnSe, CdSe/CdS/ZnS, or CdSe/ZnSe/ZnS. Similarly, for CuInS2 quantum dots, the core/shell nanocrystals can be synthesized using the formula of CuInS2/ZnS, CuInS2/CdS, CuInS2/CuGaS2, CuInS2/CuGaS2/ZnS and so on.
The white light emitting device may comprise a plurality of first and second LEDs. For instance, the plurality of first and second LEDs may be in the form of symmetrical arrays. Symmetrical arrays may improve the uniformity of light emission by the white light emitting device. More particularly, the plurality of first and second LEDs may be configured such that their arrays are symmetrically/evenly distributed.
The plurality of first and second LEDs may be in the form of asymmetrical arrays. Despite this, the white light emitting device exhibits improved luminous efficacy and does not suffer from reduced uniformity by way of the configuration of the first LED being covered by the first photoluminescence material, and the second LED being covered by the first and second photoluminescence materials.
Since the first and second LEDS each comprise blue LEDs, the first and second LEDs may comprise the same drive current, which provides a simplified and robust system leading to improved efficacy.
The white light emitting device may comprise a first string having first and second LEDs in a ratio of 0:1 to 1:0, and a second string having first and second LEDs in a ratio of 0:1 to 1:0. and wherein the same voltage is applied to the first and second strings—compared with red LEDs which have different drive characteristics.
Advantageously, the same power may be applied to the first and second strings, thereby providing a simplified and robust system. This is because the present invention may utilize all blue LEDs (including phosphor coated red for instance). For example, with a known device comprising traditional blue and red LEDs, it becomes necessary to provide different power to the strings based on the different drive characteristics blue and red LEDs and thus depending on the number of red LEDs within a string. Since all the LEDs according to the present invention have the same thermal characteristics—the system produces a more stable color output with changes in temperature compared with known constructions.
The power applied to the first and second strings may be independently controllable. The white light emitting device may thus be color tunable.
The first and/or second LEDs may be in the form of a flip chip, vertical chip or lateral chip.
The white light emitting device may comprise a diffusing layer. The diffusing layer may improve the color uniformity, particularly color over angle, of light emission by the white light emitting device.
The diffusing layer may be in direct contact with the first photoluminescence material. It may be that the diffusing layer comprises a light transmissive material and light scattering particles. Enhanced color uniformity is particularly advantageous when the device is used in large beam optics. Moreover, the amount of photoluminescence material used may also be reduced thereby providing a more cost-effective manner of manufacturing the white light emitting device. This is because the diffusing layer comprising light scattering particles increases the probability that a photon will result in the generation of photoluminescence light by directing light back into the first or second photoluminescence materials. Thus, the amount of photoluminescence material required to generate a given color temperature of light can be reduced since more of the blue excitation light is converted to photoluminescence light owing to the diffusing layer.
In embodiments, the substrate comprises a circuit board. For example, the substrate may comprise a ceramic substrate or metal core printed circuit board.
In embodiments, the white light emitting device described herein may be a tunable white light emitting device.
According to another aspect, the present invention encompasses a method of manufacturing a white light emitting device, comprising the steps of: providing first and second LEDs operable to generate excitation light having a dominant wavelength in a range from 440 nm to 480 nm; providing a first photoluminescence material which generates light having a peak emission wavelength in a range from 500 nm to 590 nm; providing a second photoluminescence material which generates light having a peak emission wavelength in a range from 600 nm to 650 nm; disposing the second photoluminescence material over the second LED; and disposing the first photoluminescence material over the first and second LEDs.
The method may comprise having a plurality of first and second LEDs.
The method may comprise the step of disposing a diffusing layer over the first photoluminescence material.
In another aspect, the present invention envisages a white light emitting device comprising: a first LED operable to generate excitation light having a dominant wavelength in a range from 440 nm to 480 nm; a first photoluminescence material which generates light having a peak emission wavelength in a range from 500 nm to 590 nm; and a photoluminescence converted LED operable to generate light having a peak emission wavelength in a range from 600 nm to 650 nm, said photoluminescence converted LED comprising a second LED operable to generate excitation light and a second photoluminescence material that covers the light emitting faces of the second LED; and wherein the first photoluminescence material covers the first LED and the photoluminescence converted LED.
According to another aspect, the present invention comprehends a white light emitting device comprising: a first LED operable to generate excitation light having a dominant wavelength in a range from 440 nm to 480 nm; a first photoluminescence material which generates light having a peak emission wavelength in a range from 500 nm to 590 nm; and a photoluminescence converted LED operable to generate light having a peak emission wavelength in a range from 600 nm to 650 nm, said photoluminescence converted LED comprising a second LED operable to generate excitation light having a dominant wavelength in a range from 440 nm to 480 nm and a second photoluminescence material which generates light having a peak emission wavelength in a range from 600 nm to 650 nm and covers the light emitting faces of the LED; and wherein the first photoluminescence material covers the first LED and the photoluminescence converted LED.
The phosphor converted LED may generate light with a peak emission wavelength in a range from 600 nm to 650 nm.
These and other aspects and features of the present invention will become apparent to those ordinarily skilled in the art upon review of the following description of specific embodiments of the invention in conjunction with the accompanying figures, wherein:
Embodiments of the present invention will now be described in detail with reference to the drawings, which are provided as illustrative examples of the invention so as to enable those skilled in the art to practice the invention. Notably, the figures and examples below are not meant to limit the scope of the present invention to a single embodiment, but other embodiments are possible by way of interchange of some or all of the described or illustrated elements. Moreover, where certain elements of the present invention can be partially or fully implemented using known components, only those portions of such known components that are necessary for an understanding of the present invention will be described, and detailed descriptions of other portions of such known components will be omitted so as not to obscure the invention. In the present specification, an embodiment showing a singular component should not be considered limiting; rather, the invention is intended to encompass other embodiments including a plurality of the same component, and vice-versa, unless explicitly stated otherwise herein. Moreover, applicants do not intend for any term in the specification or claims to be ascribed an uncommon or special meaning unless explicitly set forth as such. Further, the present invention encompasses present and future known equivalents to the known components referred to herein by way of illustration. Throughout this specification like reference numerals are used to denote like parts.
A known white light emitting device 10 will now be described with reference to
The known white light emitting device 10 comprises LEDs dies 12 disposed on a substrate 14, and a photoluminescence material mixture 16 disposed over LEDs dies 12.
More particularly,
Typically, the photoluminescence material mixture 16 comprises a homogenous mixture of cerium-activated yellow garnet (YAG) phosphor having a general composition Y3(Al,Ga)5O2:Ce and a europium-activated red-emitting nitride (CASN) phosphor having a general composition CaAlSiN3:Eu2+. Blue excitation light from the blue LED dies 12 is converted to yellow and red light by the Y3(Al,Ga)5O12:Ce and CaAlSiN3:Eu2+ phosphors respectively. The combination of the yellow, red and unconverted blue light generates white light.
The photoluminescence material mixture 16 is deposited onto the circular substrate 14 inside the wall 18 and completely covers the blue LED dies 12. The known light emitting device 10 can suffer from low luminous efficacy.
Some white light emitting LEDs comprise red LED dies that do not include phosphor/photoluminescence materials. More particularly, the red LED dies do not involve wavelength conversion to generate red light. While white light emitting LEDs comprising red LED dies are considered to be relatively efficient compared with other forms, they suffer from poor thermal stability; that is, they can exhibit poor color stability with changes in temperature.
Referring now to
The white light emitting device 210 comprises first LED dies (InGaN—indium gallium nitride dies) 212a and second LED dies (InGaN—indium gallium nitride dies) 212b disposed on a substrate 214, and a first photoluminescence material 216a and a second photoluminescence material 216b.
More particularly,
The first photoluminescence material 216a comprises a cerium-activated yellow garnet (YAG) phosphor having a general composition Y3(Al,Ga)5O12:Ce dispersed in silicone. The first photoluminescence material 216a generates light having a peak emission wavelength in a range from 500 nm to 590 nm. The first photoluminescence material 216a is excitable to generate, in combination with unconverted blue excitation light, white light having a correlated color temperature of 5000K to 6500K (“cool white”).
The second photoluminescence material 216b can comprise a europium-activated red-emitting nitride (CASN) phosphor having a general composition CaAlSiN3:Eu2 dispersed in silicone. The second photoluminescence material 216b generates light having a peak emission wavelength in a range from 600 nm to 650 nm. The second photoluminescence material 216b is excitable to generate, in combination with unconverted blue excitation light and photoluminescence generated light by the first photoluminescence material, white light having a correlated color temperature of 2700K to 3500K (“warm white”).
In this embodiment, the second LEDs 212b are coated with the second photoluminescence material 216b. The second LEDs are individually coated. The coating may be in the form of chip scale packaging (CSP) or each individual second LED 212b may be coated by another suitable method involving depositing the second photoluminescence material 216b thereon.
Following the positioning of the first LEDs 212a, which are uncoated, and second LEDs 212b, which are coated with the second photoluminescence material 216b, on the circular substrate 214—the first photoluminescence material 216a is deposited on the first LEDs 212a and second LEDs 212b inside the wall 218. As best seen in
Blue excitation light from the first LEDs 212a is converted to yellow light by the Y3(Al,Ga)5O12:Ce phosphor in the first photoluminescence material 216a. The majority, if not all, of the blue excitation light from the second LEDs 212b is converted to red light by the CaAlSiN3:Eu2+ phosphor in the second photoluminescence material 216b. Any unconverted blue excitation light from the second LEDs 212b is converted to yellow light by the Y3(Al,Ga)5O12:Ce phosphor in the first photoluminescence material 216a. The combination of the yellow, red and unconverted blue light generates white light.
As seen in
Similarly, the first and second photoluminescence materials 216a, 216b cover the light emitting faces 220d, 220e, 220f of the second LEDs 212b. The second photoluminescence material 216b is directly in contact with the second LEDs 212b, and the first photoluminescence material 216a overlays the second photoluminescence material 216b. In this embodiment, therefore, the blue excitation light emitted from the second LEDs 212b traverses the second photoluminescence material 216b before reaching the first photoluminescence material 216a. The second photoluminescence material 216b covers the light emitting faces 220e opposite the circular substrate 214 on which the second LEDs 212b are mounted; and the second photoluminescence material 216b covers the light emitting faces 220d, 220f adjacent the circular substrate 214 on which the second LEDs 212b are mounted. This can improve the uniformity of light emission from the second LEDs 212b. This also improves luminous efficacy since more of the blue excitation light will be incident on the second photoluminescence material 216b leading to improved levels of converted light having a peak emission wavelength ranging from 600 nm to 650 nm.
The provision of the white light emitting device 210 formed in accordance with the invention exhibits improved luminous efficacy and thermal stability compared with known constructions. More particularly, the arrangement in which the first LEDs 212a are covered by the first photoluminescence material 216a, and the second LEDs 212b are covered by the first and second photoluminescence materials 216a, 216b converts the blue excitation light into red light more effectively. It may be that in some embodiments the majority of the blue excitation light from the second LEDs 212b is converted to light having a peak emission wavelength in a range from 600 nm to 650 nm by the second photoluminescence materials 216b. White light is thus generated from the combination of the unconverted blue excitation light from the first and second LEDs 212a, 212b, the light having a peak emission wavelength in a range from 500 nm to 590 nm generated by the first photoluminescence material 216a, and the light having a peak emission wavelength in a range from 600 nm to 650 nm generated by the second photoluminescence material 216b.
Optionally, the white light emitting device 210 may comprise a diffusing layer (not shown). The diffusing layer may improve the color uniformity of light emission by the white light emitting device 210. The diffusing layer may be in direct contact with the first photoluminescence material 216a. It may be that the diffusing layer comprises a light transmissive material and light scattering particles. Enhanced color uniformity is particularly advantageous when the device is used in large beam optics. Moreover, the amount of photoluminescence material used may also be reduced thereby providing a more cost-effective manner of manufacturing the white light emitting device 210. This is because the diffusing layer comprising light scattering particles increases the probability that a photon will result in the generation of photoluminescence light by directing blue excitation light back into the first or second photoluminescence materials 216a, 216b. Thus, the amount of photoluminescence material required to generate a given color temperature of light can be reduced since more of the blue excitation light is converted to photoluminescence light owing to the diffusing layer.
Referring now to
The flip-chip second LED 312b comprises an InGaN (indium gallium nitride) die 322 coated with a second photoluminescence material 316b. The InGaN (indium gallium nitride) die 322 is operable to generate excitation light having a dominant wavelength in a range from 440 nm to 480 nm. The second photoluminescence material 316b is operable to generate light having a peak emission wavelength in a range from 600 nm to 650 nm. The die 322 comprises an n-electrode 324a and a p-electrode 324b at its base 326. The n-electrode 324a and a p-electrode 324b are connected to two corresponding bonding pads 328a, 328b. In turn, bonding pad 328a is seated on a contact pad 330a, while the other bonding pad 328b is seated on a contact pad 330b. The contact pads 330a, 330b are mounted on a planar substrate 314.
Referring to
The lateral-chip second LED 412b comprises an InGaN (indium gallium nitride) die 422 coated with a second photoluminescence material 416b on its upper 436b and all side surfaces 436a, 436c The die 422 is seated on bonding pad 428. The die 422 is operable to generate excitation light having a dominant wavelength in a range from 440 nm to 480 nm. The second photoluminescence material 416b is operable to generate light having a peak emission wavelength in a range from 600 nm to 650 nm. The die 422 comprises an n-electrode 424a and a p-electrode 424b on opposing ends of its upper surface 436b. Bond wires 438a, 438b connect the n-electrode 424a and the p-electrode 424b to corresponding contact pads 430a, 430b which are mounted on a planar substrate 414.
Referring to
The vertical-chip second LED 512b comprises an InGaN (indium gallium nitride) die 522 coated with a second photoluminescence material 516b on its upper surface 536b only. More particularly, the side surfaces 536a, 536c are not coated with the second photoluminescence material 516b since the vertical chip emits light from its upper surface only. The die 522 is operable to generate excitation light having a dominant wavelength in a range from 440 nm to 480 nm. The second photoluminescence material 516b is operable to generate light having a peak emission wavelength in a range from 600 nm to 650 nm. The die 522 comprises an n-electrode 524a on one end of its upper surface 536b. A bond wire 538a connects the n-electrode 524a to a corresponding contact pad 530a which is mounted on a planar substrate 514. The die 522 comprises a p-electrode 424b at its base 526 which is seated on bonding pad 528. In turn, bonding pad 328 is seated on a contact pad 530b which is mounted on a planar substrate 314.
Referring now to
Referring now to
Experimental
Referring to
Experiments 1 and 2 were conducted together with a Control Experiment. The composition of the phosphor layers used in these experiments is shown in Tables 1 and 2.
In Experiment 1, there was provided a white light emitting device which comprised 24 blue LEDs disposed on a circular substrate (COB). A red phosphor layer having the composition of Table 1 was dispensed over 12 of the 24 blue LEDs thereby coating their light emitting faces entirely with the red phosphor layer. A yellow and green phosphor (mixture) layer having the composition of Table 2 was then dispensed over the circular substrate thereby covering the 12 red-phosphor-coated LEDs and the 12 non-coated LEDs.
In Experiment 2, there was provided a white light emitting device which comprised 24 blue LEDs disposed on a circular substrate (COB). A red phosphor layer having the composition of Table 1 was dispensed over all 24 blue LEDs thereby coating their light emitting faces entirely with the red phosphor layer. A yellow and green phosphor (mixture) layer having the composition of Table 2 was then dispensed over the circular substrate thereby covering all the 24 red-phosphor-coated LEDs.
In the Control Experiment, there was provided a white light emitting device which comprised 24 blue LEDs disposed on a circular substrate (COB). A yellow and green phosphor (mixture) layer having the composition of Table 2 was dispensed over the circular substrate thereby covering all the 24 blue LEDs. The blue LEDs were not coated with a red phosphor layer.
5%
The results of Experiments 1 and 2 and the Control Experiment are shown in Table 3 below. All values in Table 3 are average values.
The current used in all Experiments was 349.9 mA. The efficacy of Experiments 1 and 2 is based on the normalized forward voltage (Vf) value of 17.17 of the Control Experiment. A true comparison of the Control Experiment, Experiment 1 and Experiment 2 is thus achieved.
A comparison of the Efficacy between the Control Experiment (154.01 lm/W) and Experiment 1 (155.02 lm/W) shows an improvement of 1.01 lm/W equating to approximately 0.66%. This demonstrates that by covering half of the blue LEDs with the red phosphor layer and then all the blue LEDs with a yellow/green phosphor mixture layer, a superior efficacy is achieved—that is approximately 0.66% better than known constructions (Control Experiment) which is a significant improvement and advantage.
A comparison of the Efficacy between the Control Experiment (154.01 lm/W) and Experiment 2 (155.94 lm/W) shows an improvement of 1.93 lm/W equating to approximately 1.25%. This demonstrates that by covering all of the blue LEDs with the red phosphor layer and then all the blue LEDs with a yellow/green phosphor mixture layer, a superior efficacy is achieved—that is approximately 1.25% better than known constructions (Control Experiment) which is a significant improvement and advantage.
It will be appreciated that the present invention is not restricted to the specific embodiments described and that variations can be made that are within the scope of the invention.
It will be understood that the following clauses form part of the disclosure of the invention defined herein. More particularly, the invention herein may be defined by the combination of the features of the clauses as detailed below, and said clauses may be utilized to amend the combination of the features within the claims of this application.