This application claims the priority of Chinese patent application No. 201910356846.1 entitled “White Light Emitting Device, Light Bar and Light Apparatus”, filed on Apr. 29, 2019, which is incorporated in its entirety herein by reference.
The present disclosure relates to a technical field of light-emitting devices, and in particular to a white light emitting device capable of emitting light having a spectrum similar to the spectrum of sunlight, and a light bar and a light apparatus using the light emitting device.
As people's requirements for light quality increase, more and more application scenarios increase higher requirements for light colors of light-emitting devices. However, there is no uniform evaluation standard for sunlight-like products on the market. To make their spectra as close to the solar spectra as possible, some products known as sunlight-like products would output high-intensity spectral energy at wavelengths in the range of 440 nm-460 nm, even exceeding the range of a blue light hazard radiation curve; meanwhile, they have significant absence at wavelengths in the range of 460 nm-480 nm, making the spectrum discontinuous. These existing products can only have good degree of similarity in a wavelength range of 500 nm-620 nm with the sunlight, so they cannot actually become sunlight-like products.
A white light emitting device is provided in the present technical solution. It is analyzed that a degree of similarity of a spectrum of the white light emitting device and a spectrum of sunlight are high, and the white light emitting device maintains the degree of similarity of above 90% in a visible light range (430 nm-650 nm) to prevent the problem of blue light glare.
The present disclosure is achieved through the following technical solutions.
A white light emitting device, wherein a relative spectrum of the white light emitting device is ϕ(λ), and a relative spectrum of a black body radiation with a corresponding color temperature is S(λ), an area normalization is performed on ϕ(λ) and S(λ) to convert an equal energy spectrum ϕ′(λ) of the white light emitting device and an equal energy spectrum S′(λ) of the black body radiation with the corresponding color temperature, and then a degree of similarity R of the equal energy spectrum of the white light emitting device and the equal energy spectrum of the black body radiation satisfies the following formula:
wherein
S′ (λ)=S (λ) /k1
k1=Σ430650S (λ)
Φ′ (λ)=Φ (λ) /k2
k2=Σ430650Φ (A)
R≥85% when λi is 380 nm and λn is 680 nm.
In some embodiments, R≥90% when λi is 430 nm and λn is 650 nm, and more preferably, R≥95%.
In some embodiments, R≥80% when λi is 465 nm and λn is 495 nm.
In some embodiments, the white light of the light emitting device is achieved by combining a blue chip, whose main emission peak is in the range of 380 nm-430 nm, with phosphors. The phosphors have a scheme consisting of three kinds of phosphors or a scheme consisting of four kinds of phosphors. For example, the phosphors are composed of a blue phosphor (having a main emission peak of 430 nm-500 nm and a full width at half maximum (FWHM) of 20 nm-100 nm), a green phosphor (having a main emission peak of 480 nm-550 nm and a FWHM of 20 nm-80 nm) and a red phosphor (having a main emission peak of 600 nm-700 nm and a FWHM of 80 nm-120 nm); or composed of a blue phosphor (having a main emission peak of 430 nm-500 nm and a FWHM of 20 nm-100 nm), a green phosphor (having a main emission peak of 480 nm-550 nm and a FWHM of 20 nm-80 nm), a yellow phosphor (having a main emission peak of 540 nm-600 nm and a FWHM of 60 nm-120 nm) and a red phosphor (having a main emission peak of 600 nm-700 nm and a FWHM of 80 nm-120 nm). Wherein the blue phosphor can be aluminate, chlorophosphate or silicate, specifically including BaMgAl10O17:Eu2+, BaAl12O9:Eu2+, Sr5(PO4)3Cl:Eu2+, Ba5(PO4)3Cl:Eu2+, RbNa3(Li3SiO4)4:Eu2+ or MgSr3Si2O8:Eu2+; the green phosphor can be oxynitride, silicate or aluminate, specifically including SiAlON:Eu2+, BaSiON2:Eu2+, Ba2SiO4:Eu2+ or LuAG; the yellow phosphor can be aluminate, silicate or nitride, specifically including Ga-YAG, Sr2SiO4:Eu2+, (BaSr)2SiO4:Eu2+ or La3Si6N11:Ce3+; the red phosphor can be nitride, sulfide or fluoride, specifically including CaAlSiN3:Eu2+, (Ca1-xSrx)AlSiN3:Eu2+, Ca2Si5N8:Eu2+, Sr2Si5N8:Eu2+, Ba2Si5N8:Eu2+, CaS:Eu2+ or MgGeF6:Mn4+.
A light bar includes at least one white light emitting device as provided above, and a substrate for mounting and fixing the white light emitting device.
The white light emitting device or the light bar provided above can be mounted in a housing of a light apparatus and connected with other necessary circuit elements to form the light apparatus.
A white light emitting device is provided in the present technical solutions. The white light emitting device can maintain the degree of similarity of above 90% in the visible light range (430 nm-650 nm), as well as a low amplitude of fluctuation in spectra and excellent spectral continuity, such that a spectrum of the light apparatus of the disclosure approximates to the spectrum of the sunlight, thereby providing a user with good lighting effects and performing indoor activities with illumination resembling an outdoor environment.
Hereinafter, the present disclosure will be further described in detail through specific implementations in conjunction with the accompany drawings. However, a person skilled in the art would understand that the following embodiments are only used to illustrate the present disclosure and should not be regarded as limiting the scope of the present disclosure. If a specific technique or condition is not indicated in the embodiments, the technique or condition shall be considered as a technique or condition described in literature in the field or in accordance with a product specification. Reagents or instruments used without an indication of a manufacturer are all conventional products that are commercially available.
A white light emitting device is provided in the present disclosure. A relative spectrum of the white light emitting device is ϕ(λ), and a relative spectrum of a black body radiation with the corresponding color temperature is S(λ). An area normalization is performed on ϕ(λ) and S(λ) to convert an equal energy spectrum ϕ′(λ) of the white light emitting device and an equal energy spectrum S′(λ) of the black body radiation with the corresponding color temperature. A degree of similarity R of the equal energy spectrum of the white light emitting device and the equal energy spectrum of the black body radiation satisfy the following formula:
wherein
S′ (λ)=S (λ) /k1
k1=Σ430650S (λ)
Φ′ (λ)=Φ (λ) /k2
k2=Σ430650Φ (λ)
R≥85% when λi is 380 nm and λn is 680 nm.
In some embodiments, R≥90% when λi is 430 nm and λn is 650 nm, and more preferably, R≥95%.
In some embodiments, R≥80% when λi is 465 nm and λn is 495 nm.
In some embodiments, the white light of the light emitting device is achieved by combining a blue chip, whose main emission peak is in the range of 380 nm-430 nm, with phosphors. The phosphors have a scheme consisting of three kinds of phosphors or a scheme consisting of four kinds of phosphors. The phosphors are composed of a blue phosphor (having a main emission peak of 430 nm-500 nm and a FWHM of 20 nm-100 nm), a green phosphor (having a main emission peak of 480 nm-550 nm and a FWHM of 20 nm-80 nm) and a red phosphor (having a main emission peak of 600 nm-700 nm and a FWHM of 80 nm-120 nm); or composed of a blue phosphor (having a main emission peak of 430 nm-500 nm and a FWHM of 20 nm-100 nm), a green phosphor (having a main emission peak of 480 nm-550 nm and a FWHM of 20 nm-80 nm), a yellow phosphor (having a main emission peak of 540 nm-600 nm and a FWHM of 60 nm-120 nm) and a red phosphor (having a main emission peak of 600 nm-700 nm and a FWHM of 80 nm-120 nm). wherein the blue phosphor is aluminate, chlorophosphate or silicate, specifically including BaMgAl10O17:Eu2+, BaAl12O9:Eu2+, Sr5(PO4)3Cl:Eu2+, Ba5(PO4)3Cl:Eu2+, RbNa3(Li3SiO4)4:Eu2+ or MgSr3Si2O8:Eu2+; the green phosphor is oxynitride, silicate or aluminate, specifically including SiAlON:Eu2+, BaSiON2:Eu2+, Ba2SiO4:Eu2+ or LuAG; the yellow phosphor is aluminate, silicate or nitride, specifically including Ga-YAG, Sr2SiO4:Eu2+, (BaSr)2SiO4:Eu2+ or La3Si6N11:Ce3+; the red phosphor is nitride, sulfide or fluoride, specifically including CaAlSiN3:Eu2+, (Ca1-xSrx)AlSiN3:Eu2+, Ca2Si5N8:Eu2+, Sr2Si5N8:Eu2+, Ba2Si5N8:Eu2+, CaS:Eu2+ or MgGeF6:Mn4+.
A light bar includes at least one white light emitting device as provided above, and a substrate for mounting and fixing the white light emitting device.
The white light emitting device or the light bar provided above can be mounted in a housing of a light apparatus and connected with other necessary circuit elements to form the light apparatus.
The white light emitting device emits the light when the phosphors are excited by an ultraviolet chip, wherein the phosphors are calculated in parts by weight and is a mixture of 55%-85% BaMgAl10O17:Eu2+, 2%-15% SiAlON:Eu2+, and 10%-35% (Ca1-xSrx)AlSiN3:Eu2+.
The detailed proportions are as shown in Table 1.
The white light emitting device is prepared according to the proportions shown in Embodiment 1. The relative spectrum ϕ(λ) of the white light emitting device and the relative spectrum S(λ) of the black body radiation with the corresponding color temperature are shown in
In combination with measured data, when λi is 380 nm and λn is 680 nm, R=87.9%; and, when λi is 430 nm and λn is 650 nm, R=93.8%. Meanwhile, a characteristic region of 465 nm-495 nm (that is, when λi is 465 nm and λn is 495 nm) can be converted to R=86.5%, which proves that the spectrum of the white light emitting device at wavelengths of 460 nm-500 nm is relatively continuous, approximating to an effect of natural light.
The white light emitting devices made with the proportions shown in Embodiment 2, Embodiment 3, and Embodiment 4 have a lighting effect similar to that of Embodiment 1. The relative spectrum ϕ(λ) of the product of each embodiment is measured separately, and in combination with the degree of similarity formula, meets the product requirements: when λi is 380 nm and λn is 680 nm, R≥85%; when λi is 430 nm and λn is 650 nm, R≥90%; and, when λi is 465 nm and λn is 495 nm, R≥80%.
The white light emitting device emits light when the phosphors are excited by an ultraviolet chip. The phosphors are calculated in parts by weight and is a mixture of 55%-85% M5(PO4)3Cl:Eu2+(M=Sr,Ba), 5%-20% Ba2SiO4:Eu2+, 2%-15% Ga-YAG and 2%-10% M2Si5N8:Eu2+(M=Ca,Sr,Ba). The detailed proportions are as shown in Table 2.
The white light emitting device is prepared according to the proportions shown in Embodiment 5. A contrast diagram of the relative spectrum ϕ(λ) of the white light emitting device and the relative spectrum S(λ) of the black body radiation with the corresponding color temperature is as shown in
In combination with the measured data, when λi is 380 nm and λn is 680 nm, R=87.8%; and, when λi is 430 nm and λn is 650 nm, R=93.8%. Meanwhile, a characteristic region of 465 nm-495 nm (that is, when λi is 465 nm and λn is 495 nm) can be converted to R=83.7%, which proves that the spectrum of the white light emitting device at the wavelengths of 460 nm-500 nm is relatively continuous, approximating to an effect of natural light.
The white light emitting devices made with the proportions shown in Embodiment 6, Embodiment 7, and Embodiment 8 have a lighting effect similar to that of Embodiment 5. The relative spectrum ϕ(λ) of the product of each embodiment is measured separately, and in combination with the degree of similarity formula, meets the product requirements: when λi is 380 nm and λn is 680 nm, R≥85%; when λi is 430 nm and λn is 650 nm, R≥90%; and, when λi is 465 nm and λn is 495 nm, R≥80%.
The white light emitting device emits light when the phosphors are excited by an ultraviolet chip. The phosphors are calculated in parts by weight and is a mixture of 55%-70% RbNa3(Li3SiO4)4:Eu2+, 5%-20% Ba2SiO4:Eu2+, 2%-15% La3Si6N11:Ce3+ and 2%-10% CaS:Eu2+. The detailed proportions are as shown in Table 3.
The white light emitting device is prepared according to the proportions shown in Embodiment 9. A contrast diagram of the relative spectrum ϕ(λ) of the white light emitting device and the relative spectrum S(λ) of the black body radiation with the corresponding color temperature is as shown in
In combination with the measured data, when λi is 380 nm and λn is 680 nm, R=86.9%; and, when λi is 430 nm and λn is 650 nm, R=95.0%. Meanwhile, a characteristic region of 465 nm-495 nm (that is, when λi is 465 nm and λn is 495 nm) can be converted to R=93.0%, which proves that the spectrum of the white light emitting device at the wavelengths of 460 nm-500 nm approximates to the spectrum of natural light.
The white light emitting devices prepared with the proportions shown in Embodiment 10, Embodiment 11, and Embodiment 12 have a lighting effect similar to that of Embodiment 9. The relative spectrum ϕ(λ) of the product of each embodiment is measured separately, and in combination with the degree of similarity formula, meets the product requirements: when λi is 380 nm and λn is 680 nm, R≥85%; when λi is 430 nm and λn is 650 nm, R≥90%; and, when λi is 465 nm and λn is 495 nm, R≥80%.
Number | Date | Country | Kind |
---|---|---|---|
201910356846.1 | Apr 2019 | CN | national |
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/CN2019/124920 | 12/12/2019 | WO | 00 |