20180298877
The present invention relates to a wind-turbine rotor blade and to a method for producing a wind-turbine rotor blade.
Rotor blades of wind-turbines are typically produced from fiber-composite materials such as GRPs or CRPs, for example. Here, for example, two half-shells can be produced and then adhesively bonded to one another or fastened to one another in some other way. The half-shells can be produced, for example, in a vacuum injection-molding process or infusion process.
In principle, in the field of the rotor blade technology of wind turbines, particular stability requirements are placed on the hub-side end pieces of rotor blades since these are responsible for the introduction of force from the rotor blade into a hub of the wind turbine. Particularly high static and dynamic loads can occur here.
WO 2014/072120 A1 shows a method for producing semifinished products for wind-turbine rotor blades. The semifinished product is produced by winding a resin-impregnated laid scrim.
The following documents have been mentioned as prior art by the German Patent and Trademark Office in the priority-establishing German patent application: DE 10 2010 019 666 A1, DE 29 21 152 C2, WO 2014/072120 A1, DE 10 2010 002 432 A1 and DE 1 045 810 A.
Provided is an improved wind-turbine rotor blade and also an improved method for producing a wind-turbine rotor blade.
Provided is a wind-turbine rotor blade having a rotor blade portion which comprises a rotor blade inner portion with a first end having a plurality of fastening units for fastening to a hub of a wind turbine and a second end having a flange for fastening further portions of the wind-turbine rotor blade. The inner blade portion is produced from polymer concrete.
According to a further aspect of the present invention, the rotor blade portion has a plurality of resin-impregnated fiber-composite laid scrims or rovings which are wound around the inner rotor blade portion.
According to a further aspect of the present invention, the inner rotor blade portion has at least one spar cap which is wound in by means of the fiber-composite laid scrims.
According to a further aspect of the present invention, the inner rotor blade portion is designed to be hollow on the inside and has a corrugated inner contour.
Provided is a method for producing a wind-turbine rotor blade. A rotor blade portion is produced from polymer concrete. This rotor blade portion produced from polymer concrete is used as a winding mandrel and resin-impregnated fiber-composite laid scrims are wound around the winding mandrel.
The invention is concerned with the idea of producing at least parts of the rotor blade by winding. A winding mandrel required for this purpose can be produced from polymer concrete and the winding mandrel can constitute part of the finished wind-turbine rotor blade. The winding mandrel thus remains in the wind-turbine rotor blade. There is thus no need for a hitherto required demolding of a hitherto used separable steel mandrel. Furthermore, the weight of the rotor blade can be reduced. The use of polymer concrete improves the recyclability of the rotor blade.
The winding mandrel can be cast or spun from polymer concrete. It is optionally possible here for a flange with prefabricated threaded inserts or for complete metal flanges to be concomitantly cast in or spun in. Subsequent machining can thus be completely or partly dispensed with. In addition thereto, further threaded connection inserts, such as, for example, for rear edge segments, can be concomitantly cast in.
The use of a polymer concrete component as a winding mandrel can lead to a reduction in the costs and in the production times.
Further refinements of the invention form the subject matter of the subclaims.
Advantage and exemplary embodiments of the invention will be explained in more detail below with reference to the drawing, in which
The inner rotor blade portion 210 is produced from polymer concrete. The main constituent part of the polymer concrete can constitute a mixture of dried sand of different grain size and/or finely ground or pulverulent quartz and a binding synthetic resin. It is furthermore possible for relatively large stones, for example based on granite, also to be provided in the polymer concrete. The strength properties of the polymer concrete can be selected by admixing short fibers of glass or carbon. Here, good packing and compaction of the fillers should be achieved.
According to one aspect of the present invention, the polymer concrete can be produced from 50% coarse sand (equivalent diameter 0.63 to 2 mm), 15% medium sand (equivalent diameter 0.2-0.63 mm), 10% quartz powder (equivalent diameter 0.063 to 0.2 mm), 5% short fiber (glass fiber), fiber length about 20 to 30 mm (filament diameter including the size, about 19 μm) and 20% (resin/curing agent mixture) synthetic resin, for example an epoxy resin-based two-component resin system or thermoplastic resin systems or curing agents. Other percentage distributions are also possible.
An inner rotor blade portion 210 can be produced from these constituent parts. This inner rotor blade portion can be used as a winding core or winding mandrel during the production of a rotor blade of a wind turbine. This winding core or winding mandrel can perform a number of structural tasks (such as, for example, an anti-buckling support) during the operation of the rotor blade. The winding mandrel thus remains in the rotor blade of the wind turbine.
According to one aspect of the present invention, flanges 211, 212 can be provided at the ends of the inner rotor portion 210. These flanges can be cast in the polymer concrete.
To produce a rotor blade of a wind turbine according to the invention, an inner rotor blade portion of polymer concrete is thus used as a winding mandrel. This occurs by casting or spinning a polymer concrete, and the thus produced portion is used as a winding mandrel and fiber-composite laid scrims or rovings can be impregnated in resin and then wound around the winding mandrel in order to produce a semifinished product which becomes part of a rotor blade.
It is possible, for example, for flanges and rotor blade connections also to be directly concomitantly wound in.
Polymer concrete is advantageous in terms of the high chemical resistance, the sealing tightness, the aging resistance, the damping properties and its dynamic strength.
Mechanical finishing is reduced by using an inner rotor blade portion as a winding core composed of polymer concrete with already incorporated flanges. Furthermore, fillers which are more favorable can be allowed. Moreover, a weight reduction is also possible through a more efficient material use.
The inner rotor blade portion can be produced from polymer concrete. This can be cast under vibration or spun (spun concrete). The rotor blade portion remains in the rotor blade after the production of the rotor blade and can optionally serve as an anti-buckling support. Furthermore, the rotor blade portion can be used as a winding mandrel.
According to one aspect of the present invention, the inner surfaces can be designed to be smooth, have ribs or be designed to be corrugated over the circumference and in the longitudinal direction.
According to one aspect of the present invention, the rotor bade portion has prefabricated flanges consisting of steel, GRP or CRP, steel inserts or metallic threaded sleeves. Particularly during the production of the inner rotor blade portion, these can be concomitantly cast in or concomitantly spun in.
According to a further aspect of the present invention, it is possible for main or auxiliary spar caps (suction side, pressure side, front side and end edge) to be concomitantly wound in on the inside or outside. For example, depressions can be concomitantly cast in or provided in the contour of the inner rotor blade portion. The provision of the depressions in the outer contour of the inner rotor blade portion allows components to be inserted or applied by adhesive bonding such that a smooth outer contour is present for winding reinforcing material.