This application is a national phase of PCT application No. PCT/JP2019/019629, filed on 17 May 2019, which claims priority from Japanese patent application No. 2018-099503, filed on 24 May 2018, all of which are incorporated herein by reference.
A technique disclosed by this specification relates to a wire connection structure and a wire connection method.
There is known a wire connection structure in which cores of a plurality of wires are bonded. A method for bundling and twisting cores of a plurality of wires and bonding the cores by ultrasonic welding (see Patent Document 1) is, for example, known as a core bonding method.
Patent Document 1: JP 2005-322544A
With the bonding method as described above, in the case of bonding two types of wires different in core material, bonding strength is not sufficient and problems such as the peeling of a bonded part may occur. Thus, there has been a demand for improvement.
A wire connection structure disclosed by this specification is provided with one or more first wires each including a first core and a first insulation coating covering the first core and having a first core exposed portion formed by partially exposing the first core from the first insulation coating, one or more second wires each including a second core made of a material different from that of the first core and a second insulation coating covering the second core and having a second core exposed portion formed by partially exposing the second core from the second insulation coating, and a bonded portion formed by welding the first core exposed portion(s) and the second core exposed portion(s), wherein a total cross-sectional area of the second core(s) is equal to or less than ⅓ of the sum of total cross-sectional areas of the first core(s) and the second core(s), the bonded portion has two pairs of outer surfaces extending along an extending direction of the first and second wires and facing each other and a distance between one pair of the outer surfaces, out of the two pairs of outer surfaces, is longer than a distance between another pair of the outer surfaces, and the second core exposed portion(s) is/are arranged adjacent to one outer surface, out of the one pair of outer surfaces, in the bonded portions.
Further, a wire connection method disclosed by this specification is a method for connecting one or more first wires each including a first core and a first insulation coating covering the first core and one or more second wires each including a second core made of a material different from that of the first core and a second insulation coating covering the second core, a total cross-sectional area of the second core(s) being equal to or less than ⅓ of the sum of total cross-sectional areas of the first core(s) and the second core(s), the method including an exposing step of stripping the first insulation coating and the second insulation coating in parts of each first wire and each second core to expose the first core and the second core, and a welding step of ultrasonically welding parts of the first core(s) and the second core(s) exposed in the exposing step to form a bonded portion by an ultrasonic welding machine including a welding horn and a receiving jig, wherein, in the welding step, welding is performed with the first core(s) held in contact with the receiving jig and the second core(s) held in contact with the welding horn, and a distance between a first contact surface in contact with the receiving jig and a second contact surface in contact with the welding horn is longer than a distance between one pair of outer surfaces different from the first and second contact surfaces in the bonded portion.
According to the wire connection structure and the wire connection method disclosed by this specification, it is possible to suppress the peeling of a bonded part.
A wire connection structure disclosed by this specification is provided with one or more first wires each including a first core and a first insulation coating covering the first core and having a first core exposed portion formed by partially exposing the first core from the first insulation coating, one or more second wires each including a second core made of a material different from that of the first core and a second insulation coating covering the second core and having a second core exposed portion formed by partially exposing the second core from the second insulation coating, and a bonded portion formed by welding the first core exposed portion(s) and the second core exposed portion(s), wherein a total cross-sectional area of the second core(s) is equal to or less than ⅓ of the sum of total cross-sectional areas of the first core(s) and the second core(s), the bonded portion has two pairs of outer surfaces extending along an extending direction of the first and second wires and facing each other and a distance between one pair of the outer surfaces, out of the two pairs of outer surfaces, is longer than a distance between another pair of the outer surfaces, and the second core exposed portion(s) is/are arranged adjacent to one outer surface, out of the one pair of outer surfaces, in the bonded portions.
Further, a wire connection method disclosed by this specification is a method for connecting one or more first wires each including a first core and a first insulation coating covering the first core and one or more second wires each including a second core made of a material different from that of the first core and a second insulation coating covering the second core, a total cross-sectional area of the second core(s) being equal to or less than ⅓ of the sum of total cross-sectional areas of the first core(s) and the second core(s), the method including an exposing step of stripping the first insulation coating and the second insulation coating in parts of each first wire and each second core to expose the first core and the second core, and a welding step of ultrasonically welding parts of the first core(s) and the second core(s) exposed in the exposing step to form a bonded portion by an ultrasonic welding machine including a welding horn and a receiving jig, wherein, in the welding step, welding is performed with the first core(s) held in contact with the receiving jig and the second core(s) held in contact with the welding horn, and a distance between a first contact surface in contact with the receiving jig and a second contact surface in contact with the welding horn is longer than a distance between one pair of outer surfaces different from the first and second contact surfaces in the bonded portion.
In the wire connection structure and the wire connection method disclosed by this specification, the “total cross-sectional area of the first core(s)” is a cross-sectional area of one first core provided in one first wire if there is one first wire, and is a total of cross-sectional areas of a plurality of first cores provided in a plurality of first wires if there are the plurality of first wires. Similarly, the “total cross-sectional area of the second core(s)” is a cross-sectional area of one second core provided in one second wire if there is one second wire, and is a total of cross-sectional areas of a plurality of second cores provided in a plurality of second wires if there are the plurality of second wires.
Further, in the wire connection structure disclosed by this specification, “the second core exposed portion(s) is/are arranged adjacent to one outer surface, out of the one pair of outer surfaces, in the bonded portions” means that one second core exposed portion provided in one second wire is arranged adjacent to the one outer surface if there is one second wire, and means that a bundle of a plurality of the second core exposed portions provided in a plurality of the second wires is arranged adjacent to the one outer surface if there are the plurality of second wires.
Further, in the wire connection method disclosed by this specification, “the first core(s) held in contact with the receiving jig” means that one first core provided in one first wire is in contact with the receiving jig if there is one first wire, and means that a bundle of a plurality of the first cores provided in a plurality of the first wires is in contact with the receiving jig if there are the plurality of first wires. Similarly, “the second core(s) held in contact with the welding horn” means that one second core provided in one second wire is in contact with the welding horn if there is one first wire, and means that a bundle of a plurality of the second cores provided in a plurality of the second wires is in contact with the welding horn if there are the plurality of second wires.
According to the above configuration, the second core exposed portion(s) is/are arranged adjacent to the one outer surface, out of the one pair of outer surfaces of the bonded portion. Here, since the distance between the one pair of outer surfaces, out of the two pairs of outer surfaces, is longer than the distance between the other pair of outer surfaces in the bonded portion, a width of each of the one pair of outer surfaces is shorter than a width of each of the other pair of outer surfaces. If the second core exposed portion(s) having a smaller total cross-sectional area is/are arranged adjacent to either one of the other pair of outer surfaces (outer surfaces having a wider width), the arrangement of the second core exposed portion(s) changes at every welding and a variation of welding strength becomes larger. In contrast, by arranging the second core exposed portion(s) having a smaller total cross-sectional area adjacent to either one of the one pair of outer surfaces (outer surfaces having a narrower width), the variation of welding strength can be reduced and the peeling of a bonded part can be suppressed.
In the above configuration, either one(s) of the first core(s) and the second core(s) may be made of aluminum or aluminum alloy. Further, the other(s) of the first core(s) and the second core(s) may be made of copper or copper alloy.
In the above configuration, the bonded portion may include a first layer constituted by the first core exposed portion(s) and a second layer adjacent to the first layer and constituted by the second core exposed portion(s).
Here, “the first layer constituted by the first core exposed portion(s)” means that the first layer is constituted by one first core exposed portion provided in one first wire if there is one first wire, and means that the first layer is constituted by a bundle of a plurality of the first core exposed portions provided in a plurality of first wires if there are the plurality of first wires. Similarly, “the second layer constituted by the second core exposed portion(s)” means that the second layer is constituted by one second core exposed portion provided in one second wire if there is one second wire, and means that the second layer is constituted by a bundle of a plurality of the second core exposed portions provided in a plurality of second wires if there are the plurality of second wires.
As just described, if a part constituted by the first core exposed portion(s) and a part constituted by the second core exposed portion(s) are divided into two layers in the bonded portion, the variation of welding strength can be further suppressed and the peeling of the bonded part can be suppressed as compared to the case where the part constituted by the first core exposed portion(s) and the part constituted by the second core exposed portion(s) are not completely divided into two layers.
A specific example of the technique disclosed by this specification is described below with reference to the drawings. Note that the present invention is not limited to these illustrations and is intended to be represented by claims and include all changes in the scope of claims and in the meaning and scope of equivalents.
An embodiment is described with reference to
As shown in
As shown in
In this embodiment, a total cross-sectional area A2 of the second cores 11B (a total of cross-sectional areas of the second cores 11B of the plurality of second wires 10B) is smaller than a total cross-sectional area A1 of the first cores 11A (a total of cross-sectional areas of the first cores 11A of the plurality of first wires 10A). More specifically, the total cross-sectional area A2 of the second cores 11B is equal to or less than ⅓ of the sum (A1+A2) of the total cross-sectional areas of the first cores 11A and the second cores 11B.
A plurality of the first core exposed portions 11AE and a plurality of the second core exposed portions 11BE are welded in a bundled state by ultrasonic welding.
As shown in
An example of a method for manufacturing the harness 1 having the above configuration by connecting the plurality of first wires 10A and the plurality of second wires 10B is described below.
First, the first insulation coating 12A is stripped to expose the first core 11A in the end part of each of the plurality of first wires 10A. The second insulation coating 12B is similarly stripped to expose the second core 11B in the end part also for each of the plurality of second wires 10B (exposing step).
Subsequently, parts where the first and second cores 11A, 11B are exposed in the exposing step (first core exposed portions 11AE, second core exposed portions 11BE) are bundled and bonded by ultrasonic welding (bonding step). As shown in
Subsequently, as shown in
In this welding step, the first core exposed portions 11AE are in contact with the anvil 31 and the second core exposed portions 11BE are in contact with the welding horn 32. Further, in the formed bonded portion 20, the distance H between the lower surface Ud (equivalent to a first contact surface) in contact with the anvil 31 and the upper surface Up (equivalent to a second contact surface) in contact with the welding horn 32 is longer than the distance W between the right and left side surfaces R, L.
As described above, the harness 1 of this embodiment is provided with the first wires 10A each including the first core 11A made of aluminum or aluminum alloy and the first insulation coating 12A covering the first core 11A and having the first core exposed portion 11AE formed by partially exposing the first core 11A from the first insulation coating 12A, the second wires 10B each including the second core 11B made of copper or copper alloy and the second insulation coating 12B covering the second core 11B and having the second core exposed portion 11BE formed by partially exposing the second core 11B from the second insulation coating 12B, and the bonded portion 20 obtained by welding the first core exposed portions 11AE and the second core exposed portions 11BE. The total cross-sectional area A2 of the second cores 11B is equal to or less than ⅓ of the sum of the total cross-sectional areas of the first cores 11A and the second cores 11B. The bonded portion 20 has the two pairs of outer surfaces extending along the extending direction of the first and second wires 10A, 10B and facing each other, the distance H between the one pair of outer surfaces (upper surface Up and lower surface Ud), out of the two pairs of outer surfaces, is longer than the distance W between the other pair of outer surfaces (right side surface R and left side surface L), and the second core exposed portions 11BE are arranged adjacent to the upper surface Up in the bonded portion 20.
Further, the wire connection method of this embodiment is a method for connecting the first wires 10A each including the first core 11A made of aluminum or aluminum alloy and the first insulation coating 12A covering the first core 11A and the second wires 10B each including the second core 11B made of copper or copper alloy and the second insulation coating 12B covering the second core 11B, the total cross-sectional area A2 of the second cores 11B is equal to or less than ⅓ of the sum (A1+A2) of the total cross-sectional areas of the first cores 11A and the second cores 11B, and the method includes the exposing step of stripping the first and second insulation coatings 12A, 12B in the end parts of the respective first and second wires 10A, 10B to expose the first and second cores 11A, 11B, and the welding step of ultrasonically welding the parts of the first and second cores 11A, 11B exposed in the exposing step (first and second core exposed portions 11AE, 11BE) to form the bonded portion 20 by the ultrasonic welding machine 30 including the welding horn 32 and the anvil 31. In the welding step, welding is performed with the first cores 11AB held in contact with the anvil 31 and the second cores 11B held in contact with the welding horn 32. In the bonded portion 20, the distance H between the lower surface Ud in contact with the anvil 31 and the upper surface Up in contact with the welding horn 32 is longer than the distance W between the pair of outer surfaces (right and left side surfaces R, L) different from the upper and lower surfaces Ud, Up.
According to the above configuration, the second core exposed portions 11BE are arranged adjacent to the upper surface Up of the bonded portion 20. Here, since the distance H between the one pair of outer surfaces (upper and lower surfaces Up, Ud), out of the two pairs of outer surfaces, is longer than the distance W between the other pair of outer surfaces (right and left side surfaces R, L) in the bonded portion 20, a width of the upper and lower surfaces Up, Ud (distance between the right and left ends of
Such an arrangement of the second core exposed portions 11BE is effective when a difference between the total cross-sectional area A1 of the first cores 11A and the total cross-sectional area A2 of the second cores 11B is large, and particularly effective when the total cross-sectional area A2 of the second cores 11B is equal to or less than ⅓ of the sum (A1+A2) of the total cross-sectional areas of the first cores 11A and the second cores 11B.
Further, the bonded portion 20 includes the first layer 21 constituted by the first core exposed portions 11AE and the second layer 22 adjacent to the first layer 21 and constituted by the second core exposed portions 11BE. If a part constituted by the first core exposed portions 11AE and a part constituted by the second core exposed portions 11BE are divided into two layers in the bonded portion 20 in this way, the variation of welding strength can be further suppressed and the peeling of the bonded part can be suppressed.
<First Modification>
As in the embodiment, a harness 40 of a first modification includes a part (bonded portion 41) obtained by welding the first core exposed portions 11AE and the second core exposed portions 11BE. As in the embodiment, the distance H between the one pair of outer surfaces (upper and lower surfaces Up, Ud) extending along the extending direction of the wires 10A, 10B and facing each other is longer than the distance W between the other pair of outer surfaces (right and left side surfaces R, L) extending along the extending direction of the wires 10A, 10B and facing each other in the bonded portion 41.
As shown in
In this modification, the first and second bonded portions 42, 43 are not completely divided into two layers in the bonded portion 41 unlike in the embodiment. However, since the second bonded portion 43 is arranged adjacent to the upper surface Up having a narrower width, a certain effect of reducing the variation of welding strength and suppressing the peeling of a bonded part is obtained.
<Second Modification>
As shown in
In manufacturing the harness 50 of this modification, ultrasonic welding may be performed under welding conditions suitable for the welding of copper in the bonding step. However, since a welding temperature of copper is higher than that of aluminum, molten aluminum may adhere to the welding horn 32. Accordingly, the bonding step is preferably performed in two stages as follows.
First, in a first bonding step, only first core exposed portions 52AE are bundled and bonded by ultrasonic welding to first form a first layer 54. At this time, welding may be performed under conditions in conformity with the material of the first cores 52A (conditions suitable for the welding of copper).
Subsequently, in a second bonding step, the first layer 54 formed in the first bonding step is placed on the anvil 31. Subsequently, second core exposed portions 52BE are arranged on the first layer 54 (on the side of the welding horn 32). Then, ultrasonic welding is performed to bond the second core exposed portions 52BE on the first layer 54 and form a second layer 55, whereby a bonded portion 53 is completed. At this time, welding may be performed under conditions in conformity with the material of the second cores 52B (conditions suitable for the welding of aluminum).
Since the other configuration is the same as in the embodiment, components similar to those of the embodiment are denoted by the same reference signs and not described.
<Other Modifications>
Although the plurality of first wires 10A and the plurality of second wires 10B are provided in the above embodiment, one first wire and/or one second wire may be provided. Further, the first and second wires may have different core thicknesses (core cross-sectional areas), the plurality of first wires may include wires having different core thicknesses (core cross-sectional areas), or the plurality of second wires may include wires having different core thicknesses (core cross-sectional areas).
[Used Machines, Used Materials]
A “Schunk Mimic 4” produced by Schunk GmbH & Co. KG was used as an ultrasonic welding machine. A “horizontal tensile testing machine: MS-6” produced by Sunmec Co., Ltd. was used as a tensile testing machine.
A wire size was indicated by a cross-sectional area (mm2: sq) of a core (stranded wire).
[Test Method]
1) Fabrication of Test Bodies
Wires shown in Table 1 were respectively cut to a length of 100 mm and insulation coatings of 10 mm on tips are removed to expose cores.
Subsequently, using the ultrasonic welding machine, an exposed part of a copper core was welded under conditions recommended for copper by the ultrasonic welding machine. Subsequently, exposed parts of aluminum cores and the previously fabricated copper core exposed portion solidified by ultrasonic welding were welded to obtain a test body. At this time, the core of the copper wire (core having a smaller total cross-sectional area) was arranged on the side of a welding horn. A width (equivalent to the distance W of the above embodiment) and a height (equivalent to the distance H) of a bonded part are shown in Table 1.
The obtained test bodies were subjected to a tear strength test.
2) Tear Strength Test
Using the tensile testing machine, one copper wire 60 was pulled at 100 mm/min and a maximum load until a bonded part was torn was measured with other wires 61 fixed by a fixing tool 62 as shown in
Using wires shown in Table 2, test bodies were fabricated as in Test Example 1 and a tear strength test was conducted. A result is shown in Table 2.
Using wires shown in Table 3, test bodies were fabricated as in Test Example 1 and a tear strength test was conducted. A result is shown in Table 3.
Using wires shown in Table 4, test bodies were fabricated as in Test Example 1 and a tear strength test was conducted. A result is shown in Table 4.
Using wires shown in Table 5, test bodies were fabricated. A core of an aluminum wire (core having a smaller total cross-sectional area) was arranged on the welding horn side under conditions recommended for copper by the welding machine. Other fabrication conditions were the same as in Test Example 1.
A tear strength test was conducted as in Test Example 1 for the obtained test bodies. A result is shown in Table 5.
Using wires shown in Table 6, test bodies were fabricated as in Test Example 1 and a tear strength test was conducted. A result is shown in Table 6.
[Result]
As shown in Table 1, in Test Example 1, a high tear strength was exhibited both in the case of pulling the copper wire and in the case of pulling the aluminum wires and it was found that two types of the cores were firmly bonded in the bonded part. The same holds true for the other test examples.
| Number | Date | Country | Kind |
|---|---|---|---|
| JP2018-099503 | May 2018 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2019/019629 | 5/17/2019 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2019/225492 | 11/28/2019 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 8931685 | Kataoka | Jan 2015 | B2 |
| 9505083 | Ruhl | Nov 2016 | B2 |
| 20040134062 | Jonli | Jul 2004 | A1 |
| 20120318554 | Koto | Dec 2012 | A1 |
| Number | Date | Country |
|---|---|---|
| 2005-322544 | Nov 2005 | JP |
| 2007-185706 | Jul 2007 | JP |
| 2011-014438 | Jan 2011 | JP |
| 2013-235671 | Nov 2013 | JP |
| 2013-242991 | Dec 2013 | JP |
| 2017-126520 | Jul 2017 | JP |
| 2017-168400 | Sep 2017 | JP |
| Entry |
|---|
| International Search Report dated Jun. 18, 2019 for WO 2019/225492 A1 (4 pages). |
| Number | Date | Country | |
|---|---|---|---|
| 20210184376 A1 | Jun 2021 | US |