Patent Application
20090293674
This invention relates to wire for refining molten metal with additives, such as metallic material and/or minerals, and an associated method of manufacturing such wire.
This application is a National Phase Application filed pursuant to 35 U.S.C. § 371 claiming priority to PCT/GB2006/079832 A1, entitled “WIRE FOR REFINING MOLTEN METAL AND ASSOCIATED METHOD OF MANUFACTURE,” filed on Aug. 3, 2006, which is a Patent Cooperation Treaty Application of United Kingdom Patent Application No. GB 0501775.1, entitled “WIRE FOR REFINING MOLTEN METAL AND ASSOCIATED METHOD OF MANUFACTURE,” filed on Jan. 28, 2005.
Prior to casting a molten metal, such as molten steel, refining wires can be injected into the molten metal vessels such as a ladle, pot or continuous casting tundish, to provide the metal with improved characteristics. The purpose of the refining wire is to inject refining materials, such as metals and/or minerals, encapsulated in the sheath of the wire into the molten metal in accurate quantities and in a controller manner, when the refining materials display either a high affinity to oxygen, or a low melting and/or vapor point, or a high vapor pressure, or a low solubility or law density compared to the molten metal, or a combination of these factors. In this regard, it is important to achieve a high percentage of recovery of the refining material defined as the ratio of the injected material quantity remaining into the molten metal divided by the total material quantity injected.
In a known method manufacturing a refining wire, a steel strip is rolled to form a U-shaped section that is filled with refining material in powered form. The two longitudinal edges of the U-shaped strip section, which have been pre-folded to that effect, are then hooked together. In this manner, a refining wire is formed with the steel sheath encapsulating a core of refining material.
Another method of manufacturing a refining wire is the same as above with the exception that the refining material is introduced into the U-shaped section as a solid extruded wire.
Refining wires produced by these known methods usually have a sheath thickness in the range of 0.2 mm to 0.6 mm due to the manufacturing and product constraints. As a result, the wire can be deformed easily by the high pressure of the feeder pinch rolls used to inject the wire through a guide tube into the molten metal vessel, thereby requiring guide tubes with comparatively large inner diameters which are detrimental to guiding the refining wire accurately into the vessel.
Sometimes also, the refining wire is not sufficiently rigid to penetrate a solidified surface of slag floating on the surface of the molten metal, such as molten steel, in the vessel.
Further, the hook-type closure for the steel sheath of the wires discussed above does not allow for the deep rolling or drawing of such wires down to much smaller diameters, in which case, the core can include excessive and undesirable amounts of air which, during the refining process, is detrimental to the quality fo the molten metal as well as the recovery of the core material. Moreover, the refining material can interact with the components of the air or other materials, such as moisture or oxidizing agents, thus reducing the shelf life of the wire.
It is an object of the present invention to provide a refining wire that overcomes, or at least substantially reduces, the disadvantages associated with the known refining wires discussed above.
It is another object of the invention to provide a refining wire and associate method of manufacture, with a sheath thickness which is larger than those of the known refining wires discussed above, resulting in improved manufacturing techniques for refining molten metals, particularly molten steel.
Accordingly, a first aspect of the invention provides a molten metal refining wire comprising a metal sheath encapsulating a core of refining material, wherein the core is sealed within the sheath in a fluid-tight manner.
Preferably, the wire has been deep rolled or drawn to a smaller diameter.
The sheath may be made of any suitable metallic material. However, when the refining wire is used for refining molten steel, the sheath is preferably a low carbon, low silicon steel.
The encapsulated core of refining material may, again, be any suitable material for refining molten metal, for example molten steel, such materials including, inter alia, pure calcium or calcium, aluminum or nickel metal or any combination thereof, a calcium-silicon alloy (CaSi), a ferro-titanium alloy (FeTi), a ferro-boron alloy (FeB), or any combination thereof.
A second aspect of the invention resides in a method of manufacturing a molten metal refining wire comprising a metallic sheath encapsulating a core of refining material, wherein the core is encapsulated within the sheath in a fluid-tight manner.
A third aspect of the invention resides in a method of manufacturing a molten metal refining wire comprising a metallic sheath encapsulating a core of refining material, the method comprising forming a metal strip into a sheath with the refining material encapsulated therein, and sealing together, preferably by welding, the longitudinal edges of the so-formed sheath in a fluid-tight manner.
In either aspect of the inventive method defined above, the sheath may again be made of any suitable metallic material but when the refining wire is used for refining molten steel, the sheath is preferable a low carbon- low silicon steel.
Also, the edges of the sheath are preferably butt welded together.
The encapsulated core of refining material may, again, be any suitable material for refining molten metal, for example molten steel, such materials including, inter alia, pure calcium or calcium, aluminum or nickel metal or any combination thereof, a calcium-silicon alloy (CaSi), a ferro-titanium alloy (FeTi), a ferro-boron alloy (FeB), or any combination thereof.
Thus, because the refining wire sheath is sealed, such as welded, preferably butt welded, to encapsulate the refining material of the core in a fluid-tight manner, sheath thicknesses of up to 2.0 mm can achieved, as opposed to a maximum sheath thickness of 0.6 mm for the previously known refining wires.
In order to reduce oxygen, air or other deleterious gases remaining in the sheath of the so-formed wire, the wire can be deep rolled or drawn to a smaller diameter, thereby expelling such gases from the wire, without detriment to the integrity thereof, whilst also tending to the close the sheath around the core more tightly. In this manner, core refining material apparent density ratios over 95% of the theoretical solid core equivalent, can be achieved.
Further and due to the thicker sheaths, damage to the wire, which might otherwise occur with the known refining wires through the high-pressure of the pinch rolls thrusting the wire through the guide tubes into the molten metal vessel, is diminished, while the wire, particularly when having higher sheath thicknesses, is sufficiently rigid to the penetrate the solidified surface of the slag floating on the surface of the molten metal in the vessel.
Further, the wire does not tend to melt high in the vessels before reaching the bottom thereof, as do the known refining wires, thereby releasing the refining material under high static pressure, far away from the oxygen present in the slag and atmosphere above, and increasing the floatation time of law density refining materials, these all being favorable factors for achieving a high recover.
A forth aspect of the invention provides a method of refining molten metal, comprising injecting into molten metal a refining wire in accordance with the first aspect of the invention or a wire manufactured in accordance with the second or third aspect of the invention defined above.
In order that the invention may be more fully understood, a refining wire in accordance therewith will now be described by way of example and by way of comparison with a prior art refining wire, in accordance with the accompanying Examples and drawings in which:
Referring firstly to the prior art refining wire, as indicated generally at 1 in
As discussed above, due tot the bulkiness of the hook-type closure and because that closure is not properly sealed, that is to say, it is not fluid-tight, deep rolling or drawing of the wire 1 is not possible and, also, air can be present within the refining material 4. This undesirable oxygen is detrimental to the quality of the molten steel as the refining wire 1 is injected hereinto, as well as to the recovery of the core material 4.
Referring now to the
In contrast to the prior art refining wire 1 discussed above in relation to
Also, any air, oxygen or other gas present in the sheath 12 can be reduced by expelling it from the sheath interior if the wire 11 is deep rolled or drawn down in diameter. This also tends to close the sheath 12 more tightly around the core 14.
The following Examples are provided to illustrate the compositions and dimensions of preferred molten steel refining wires in accordance with the invention, where the steel from which the sheath is made is SAE 1006 steel or its equivalent, the core material is powered pure calcium powder and the outside diameter of each wire is 9.0 mm.
Deep rolling or drawing of the wires may be necessary to provide smaller diameter wires, in dependence upon operating conditions of the refining process, while also tending to the close the sheaths more tightly around the wire cores.
Thus, it can be seen that the invention provides refining wires which improve metal refining techniques, in that, inter alia, they reduce impurities being injected into molten metals, while retaining their overall integrity, particularly during their being fed to the molten metal vessel and their penetration into the molten metal through the slag floating on the molten metal surface.
Also because the sheaths are sealed and have regular, continuous, generally smooth circumferences, they can be readily deep rolled or drawn into smaller diameters without detriment tot heir integrity, while also expelling air, oxygen or any other undesirable gas from the sheath interiors.
Further, deep rolling or drawing of the refining wires to smaller diameters can provide for a core material keeping an apparent density compression ratio of over 95% of the theoretical solid core equivalent.
| Number | Date | Country | Kind |
|---|---|---|---|
| 0501775.1 | Jan 2005 | GB | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/GB06/79832 | 8/3/2006 | WO | 00 | 6/17/2009 |