The present invention is directed to a wire-in-channel type superconductive conductor of the type which is used in superconducting magnets, such as are commonly found in magnetic resonance imaging machines, particle accelerators, etc., and methods of producing such wire-in-channel type superconductive conductors.
In wire-in-channel superconductive conductors, a superconducting wire is soldered into a normally-conductive channel of a corresponding dimension.
Such wire-in-channel superconductive conductors have been found effective in achieving long continuous lengths, and in providing a superconductive conductor which is suitable for persistent magnets. Wire-in-channel superconductive conductors of this type are typically insulated by a polyester braid 24.
The known copper channel wire-in-channel type superconductive conductor 10 is designed to provide a high copper-to-superconductor ratio, for stability, without the necessity of processing all of the copper with the superconductor. As a result, the cost of production is significantly reduced as compared to methods of production which require processing all of the copper with the superconductor.
Because of the large quantity of material used in the conductive channel in many applications, it is desirable to reduce the weight of the channel 20 and also to make it more pliable for ease in magnet fabrication. Aluminum is an excellent substitute material for the usual copper, being less costly, more pliable and lighter in weight; however, the use of aluminum as a direct substitute for copper presents several manufacturing difficulties such as quality of solder bond, soldering temperature and compatibility of fluxes as well as the flexibility of the completed wire-in-channel conductor. Accordingly, aluminum has not been used as a direct substitute for the copper material normally used for the channel 20 shown in
Japanese patent application JP04071112A describes an arrangement in which an aluminum channel 20 is formed, and at least the interior of the groove 22 is coated in copper by a process such as electroplating, dipping or vapour deposition. The superconducting wire is then soldered 18 onto the copper coating within the groove 22, the resulting composite material then being subjected to a drawing process.
The present invention provides alternative and improved methods for producing a copper-clad aluminum conductive channel and a superconducting wire in copper-clad aluminum channel conductor using this channel.
The present invention also provides a wire-in-channel superconductive conductor wherein the conductive channel is fabricated from an electrically conductive metal or alloy core with at least one layer of a metallic cladding comprising a layer of a high strength alloy; and an outer layer of copper.
The above, and further, objects, characteristics and advantages of the present invention will become more apparent from consideration of the following description of certain embodiments thereof, in conjunction with the accompanying drawings, wherein:
According to the present invention, a copper-clad aluminum conductive channel for use in producing a superconducting wire in copper-clad-aluminum channel, is produced from an aluminum wire 30 coated with a metallurgically bonded copper layer 32 such as shown in
Rather than forming an aluminum channel section which is then at least partially coated with copper by a process such as electroplating, dipping or vapour deposition, the present invention provides a cost-effective and efficient method for producing copper-clad aluminum channel section suitable for use in producing composite wire-in-channel superconductive conductor, using commercially-available copper clad aluminum wire, such as illustrated in cross-section in
The cost of commercially available electrical grade copper clad aluminum wire is lower in price per unit length than solid copper. It is also lighter in weight because of the lighter weight of aluminum. A 10% copper clad aluminum wire is 2.8 times as long as a similar wire consisting of an equal weight of copper.
By employing such a composite wire in place of solid copper, such as is used for the channel 20 in conventional wire-in-channel superconductor, manufacturing costs are reduced, the weight of the final conductor is reduced and no change is required in the production process.
By employing such a composite wire, a much simpler manufacturing method may be employed as compared to depositing a copper coating onto at least part of the surface of an aluminum channel, as described by the prior art.
By applying conventional wire drawing and shaping techniques to the copper-clad aluminum wire represented in
In an example of a manufacturing process according to an aspect of the present invention, a circular cross-section copper clad aluminum wire, commercially available and fabricated by known industrial manufacturing process, is processed using wire drawing and shaping techniques, conventional in themselves, into a grooved channel, approximately rectangular in profile (
The copper clad aluminum wire described is much softer than solid copper wire, which extrapolates to a higher production speed in forming the channel and far less die wear, both of which lower the cost of forming the channel 40 as compared to a corresponding method employing solid copper wire to form the channel 20.
The grooved channel 40 and a 0.813 mm diameter superconductive wire 12 are then passed together through a solder bath where the superconductive wire 12 is pressed into the groove 42 in the copper clad aluminum channel 40. The composite superconductive conductor thus formed may then be passed through a die within the solder bath to press the superconductive wire 12 into the groove 42. The die may also serve to draw the conductor to a final cross-section, and in doing so may deform the channel 40 to more securely retain the superconductive wire 12, as illustrated in
The specific heat capacity of the copper clad channel is less than that of the conventional solid copper channel, which results in higher speeds in the soldering process. A controlling parameter in setting the production line speed is the rate that the channel can be heated to the soldering temperature, and since it takes less energy to heat the copper clad aluminum channel to the soldering temperature, as compared to a conventional copper channel, the production line speed can be proportionally increased, as compared to a similar method employing a solid copper channel.
The resulting structure may be quenched at the exit from the solder bath, or allowed to cool naturally, to solidify the solder and bond the structure together.
The method of forming a composite superconducting conductor having a superconducting wire 12 soldered 18 into a groove 42 in a copper 32 clad aluminum 30 channel according to the invention does not require steps such as electroplating, dipping or vapour deposition, as required by the prior art, resulting in a simplified and less costly manufacturing method, in turn resulting in greater reliability and reduced cost of the finished product.
While copper clad aluminum wire is available commercially, and the formation of the copper-clad aluminum wire does not form part of the present invention, it may be noted that several methods for forming the composite copper clad aluminum wire are available. Some of these are listed below and the choice again depends on the application. If required, copper-clad aluminum wire may be produced in-situ for use according to the present invention by any of the following processes.
The method employed according to the present invention for converting a copper-clad aluminum wire into a copper-clad channel 40 profile is simpler and more industrially acceptable than the copper coating of an aluminum channel suggested by the prior art.
The aluminum 30 used to form the channel can be replaced by any suitable aluminum alloy, or indeed any other suitable alloy. The choice will depend on the application. In one case, electrical conductivity may dictate the choice, while in other cases the mechanical strength may be the dominant criterion. Although commercially available copper clad aluminum wire has been described, the invention is not limited to this single configuration. By incorporating a multiple layer structure, a reinforced channel conductor can be obtained. For example, a wire 30 comprising aluminum or other electrically conductive alloy core encased within a layer of high strength alloy 33 such as steel, with an outer layer 32 of copper, may be used, as shown in
Alternatively, or in addition, to the use of a layer of high-strength alloy within the wire used to form the channel, an elongate high-strength member such as a wire or strip 35 (the alternative arrangement is shown schematically in
The step of soldering the superconducting wire into the copper clad aluminum profile to form the composite conductor may be performed using any suitable soft solder including but not limited to alloys of Pb, Cu, Sb, Sn and Zn. One particular solder which may be used comprises Sn-5% Sb by weight.
The aluminum used in the copper clad aluminum wire should preferably be high purity aluminum, electrical grade aluminum or high strength aluminum.
The copper used in the copper clad aluminum wire should preferably be high conductivity copper such as 1100 (OFHC) grade copper.
The copper used in the copper clad aluminum wire may be an alloyed copper for improved strength.
It may be found advantageous to apply a tinning layer over at least part of the outer copper layer 32 of the channel, particularly the surface in and near the groove 42 which will receive and be soldered to the superconducting wire. Such tinning layers are known to assist soldering. A tinning layer may be of tin, or any suitable solder. Once the channel 40 and the superconductive wire 12 have been soldered 18 together, the whole outer surface of the resultant wire-in-channel superconductor will most likely be tinned.
In further embodiments of the present invention, an elongate member of a material of high specific heat capacity can be incorporated into the composite conductor before, during or after the solder bonding of the superconducting wire to the channel profile, to improve thermal stability. Such material can be treated to accept solder by extrusion, electroplating or co-drawing, etc.
The foregoing disclosure has been set forth merely to illustrate the invention and is not intended to be limiting. Since modifications of the disclosed embodiments incorporating the spirit and substance of the invention may occur to persons skilled in the art, the invention should be construed to include everything within the scope of the appended claims and equivalents thereof.
Number | Date | Country | Kind |
---|---|---|---|
0622755.7 | Nov 2006 | GB | national |
This is a U.S. National Stage Application under 35 U.SC. §371 pursuant to International Application No. PCT/GB2007/050395, filed Jul. 11, 2007, and claims priority of U.S. Provisional Application No. 60/830,694, filed Jul. 14, 2006, and British Application No. GB 0622755.7, filed Nov. 15, 2006, the entire disclosure of which is herein expressly incorporated by reference.
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/GB2007/050395 | 7/11/2007 | WO | 00 | 2/2/2009 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO2008/007141 | 1/17/2008 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
1384448 | Gilbert et al. | Jul 1921 | A |
3501581 | Edwards | Mar 1970 | A |
3551976 | Zentgraf et al. | Jan 1971 | A |
3570118 | Reynolds et al. | Mar 1971 | A |
3699647 | Bidault et al. | Oct 1972 | A |
4079187 | Fillunger et al. | Mar 1978 | A |
4490578 | Suzuki et al. | Dec 1984 | A |
4751614 | Mehnert | Jun 1988 | A |
4857675 | Marancik et al. | Aug 1989 | A |
4954479 | Dubots et al. | Sep 1990 | A |
4994633 | Puhn | Feb 1991 | A |
5266416 | Inoue et al. | Nov 1993 | A |
5620798 | Huang et al. | Apr 1997 | A |
6508001 | Adrian | Jan 2003 | B2 |
Number | Date | Country |
---|---|---|
0 500 101 | Aug 1992 | EP |
59224007 | Dec 1984 | JP |
4-71112 | Mar 1992 | JP |
WO 2006035065 | Apr 2006 | WO |
Number | Date | Country | |
---|---|---|---|
20090194316 A1 | Aug 2009 | US |
Number | Date | Country | |
---|---|---|---|
60830694 | Jul 2006 | US |