Patent Grant
11929215
The present invention is related to a solid electrolytic capacitor comprising a pressed powder anode and an anode wire extending therefrom. More specifically, the present invention is related to a process for improving the connection between the anode wire and anode thereby allowing for the use of powders with a higher charge density per gram (CV/g).
There is an ever increasing demand for electronics with higher capability, lower cost, and better durability. This demand, at the electronics level, places a burden on the component manufacturers to provide more functionality and, often, this increased functionality is required in the same, or less, volume of the electronics. With regards to capacitors this has led to the constant desire to provide higher volumetric efficiency or capacitance per volume of capacitor.
Solid electrolytic capacitors comprising a pressed powder anode with a wire extending therefrom, for connectivity, are well known in the art. The anode wire is in electrical contact with the anode. The anode wire is typically attached to the anode in one of two ways. In one method common to the art the wire is inserted into the anode powder and secured in the powder during the pressing operation. In a second method the anode wire is welded to the anode after pressing. In each case the anode is sintered and, in the case of a welded wire, prior to anode wire attachment.
The ever constant desire for increased volumetric efficiency has lead to the development of anode powders with increasing CV/g. Unfortunately, these new powders have proven to be very difficult to utilize since the particles necessary to achieve the high CV/g fail to form an adequate bond to the anode wire during the pressing and sintering steps. As the CV/g increases, and the anode size decreases, the problem of inadequate bonding to the anode wire is exasperated. This is a particular problem when deoxygenation sintering is utilized as described in commonly assigned U.S. Pat. No. 8,349,030 to Hussey et al. which is incorporated herein by reference. The deoxygenation further erodes the bond between the anode and anode wire often leading to complete dissociation of the two.
One option is to sinter the anode to a higher degree thereby improving the bond strength between the anode wire and anode. The increased sintering temperatures are believed to form more adequate necks between the particles of the powder to gain sufficient wire to anode mechanical strength. Unfortunately, increased sintering reduces the surface area of the anode metal in the anode and thus the CV/g, and ultimately decreasing the capacitance of the resulting capacitor, which eliminates the advantages offered by the more expensive higher charge powder.
Welding the wire to the formed anode is one approach to addressing this problem. In the welding process a broad welding nugget forms inside and outside of the anode edge. One problem with the welded wire is the requirement for double sintering. The first sintering is before the welding to provide mechanical strength to the anode and the second sintering is after the welding to clean the welding nugget. In addition, the use of welded wires on high charge powders and double sintering is problematic due to the oversaturation of the powder particles with oxygen and precipitation of the crystalline oxide.
There is currently no suitable way to utilize the high charge powders to their fullest extent due to the ineffective adhesion between the anode powder and anode wire. Provided herein is an improved method of forming the connection between the anode and anode wire resulting in an improved capacitor.
It is an object of the invention to provide an improved capacitor comprising an improved connection between the anode and anode wire.
A particular feature of the invention is the ability to utilize high charge capacity anode powders without degradation of the charge capacity due to excess sintering otherwise required to secure the anode wire thereto.
A particular advantage of the instant invention is the ability to utilize high CV/g powders and to process the high CV/g powders in a deoxygenation sintering process which is typically not suitable due to failure of the bond between the anode wire and pressed powder of the anode.
These and other embodiments, as will be realized, are provided in a method for forming an anode wherein the method comprises:
inserting an anode wire in an anode powder with a first portion of the anode wire extending from the anode powder;
pressing a portion of the anode powder to form a bulk region having a first density; and
pressing a second portion of the anode powder with the anode wire in the second portion to form a high density region with a second density wherein the pressing of the second portion is sufficient to distort the anode wire in the second portion.
Yet another embodiment is provided in a capacitor comprising an anode. The anode comprises a pressed anode powder comprising a bulk density region with a first density and a high density region with a second density wherein the second density is higher than the first density region. An anode wire extends into the high density region wherein the anode wire is distorted in the high density region.
Yet another embodiment is provided in a method for forming a capacitor anode. The method comprises:
inserting an anode wire in an anode powder with a first portion of said anode wire extending from the anode powder;
pressing a portion of the anode powder to form a pressed powder anode comprising a face of egress and a terminal end wherein the pressing comprises forming a bulk region having a first density and a high density portion having a second density with the anode wire in the high density portion wherein the pressing of the high density portion is sufficient to distort the anode wire in the second portion; and
wherein the high density portion extends to the terminal end.
Yet another embodiment is provided in q method for forming a capacitor anode. The method comprises:
inserting an anode wire in an anode powder with a first portion of the anode wire extending from the anode powder wherein the anode wire is conical;
pressing a portion of the anode powder to form a pressed powder anode comprising a face of egress and a terminal end wherein the pressing comprises forming a bulk region having a first density and a high density portion having a second density with the anode wire in the high density portion wherein the pressing of the high density portion is sufficient to distort said anode wire in said second portion.
Yet another embodiment is provided in a capacitor comprising an anode. The anode comprises a pressed anode powder comprising a bulk density region with a first density and a high density region with a second density wherein the second density is higher than the first density and the high density region extends to a terminal end. An anode wire extends into the high density region at a face of egress wherein the anode wire comprises a distorted portion in the high density region.
Yet another embodiment is provided in a capacitor comprising an anode. The anode comprises a pressed anode powder comprising a bulk density region with a first density and a high density region with a second density wherein the second density is higher than the first density and the high density region extends to a terminal end. An anode wire extends into the high density region at a face of egress wherein the anode wire comprises a distorted portion in the high density region and the anode wire is conical.
The present invention is related to an improved method for connecting an anode wire to an anode and an improved capacitor formed thereby.
The connection between the anode wire, which is preferably tantalum, and the pressed powder forming the anode connection is a particular concern with high charge powders and small anodes. High charge powders have higher volumetric shrinkage and lose surface area faster than lower charge powders at comparable sinter temperatures. Thus, to utilize the high surface area of the high charge powder, lower sinter temperatures are needed. Lower sinter temperatures result in a limited number of contact points and prevent robust connection. By increasing the density of powder in the immediate vicinity of the wire the connection strength is significantly improved.
The present invention solves the aforementioned problem by compressing the powder in the vicinity of the anode wire to the extent necessary to physically distort a portion of the Ta wire during the powder pressing process. Increasing the pressure of the press to the extent necessary to distort the anode wire forms a strong bond between the anode wire and pressed powder thereby allowing for the use of high CV/g powders and/or smaller anode sizes. The increased mechanical strength also allows for sintering at the optimum temperature, with preservation of the high internal surface area, without degradation of the bond between the anode wire and pressed powder anode.
Yet another advantage of the invention is the ability to decrease the length of the anode wire extending into the anode body in an embodiment thereby increasing the amount of anode powder within the same volume of anode. Reducing the amount of wire inside the anode also reduces the cost of the wire. Increasing the amount of powder in the porous anode body is especially an advantage in small size anodes.
Yet another advantage of the invention is the ability to improve the coverage of conductive polymer on the pressed anode. The conductive polymer functions as the cathode in the capacitor.
The anode powder is pressed, with the anode wire contained therein, by dual density pressing with a low pressure portion, for forming the bulk density of the anode powder, and a high pressure portion in an area containing the wire. The high pressure portion is sufficiently high to cause physical deformation of the, preferably tantalum, wire embedded in the powder as will be more readily understood from further discussions. While not limited thereto a compression ratio of at least 2:1 is sufficient to demonstrate the invention with the advantage exemplified in a significant increase in pull strength. At a compression ratio of 2:1 the high density region is compressed to half the thickness of the bulk density region.
For the purposes of the instant invention a distorted wire is defined as a wire wherein the longest cross-sectional length in the distorted region is at least 10% longer than the equivalent diameter of the wire. More preferably the longest cross-sectional length in the distorted region is at least 15% longer than the average equivalent diameter of the wire and even more preferably the longest cross-sectional length in the distorted region is at least 20% longer than the average equivalent diameter of the wire. Equivalent diameter is the diameter of a circle having the same surface area as a cross-section of the wire taken perpendicular to the long axis.
The low pressure pressing is selected based on the desired bulk density of the anode as well known to those of skill in the art. It is preferable that the high density region have a density which is above that of the bulk density where the high density region has a density which is at least 125% to 200% of the bulk density with the bulk density being the average density of those portions of the anode excluding the high density region and transition. A density in the high density region of at least 150% of the bulk density is preferable. It would be understood to those of skill in the art that the maximum density is the theoretical maximum density of the metal, or about 16.7 g/cc for tantalum. In practice it is not practical to exceed about 90% of the theoretical maximum density.
The invention will be described with reference to the figures forming an integral, non-limiting, component of the invention. Throughout the various figures similar elements will be numbered accordingly.
An embodiment of the invention is illustrated schematically and will be described with reference to
A distorted anode wire is illustrated schematically in isolation view in
An embodiment of the invention is illustrated in and will be described with reference to
An embodiment of the invention is illustrated and will be described with reference to
An embodiment of the invention will be described with reference to
An embodiment of the invention is illustrated in cross-sectional schematic view in
With the present invention the high density area around the flattened wire provides a strong wire-to-powder bond without a need for second sintering and the related change in chemical composition caused thereby. This approach can be used to improve the mechanical and electrical properties of anodes in a broad range of the powder, with virtually any available level of CV/g, whereas application of the welded wire is limited to relatively coarse powders.
It is particularly preferred that the anode be subjected to a deoxidation-sintering process, referred to in the art as deox-sinter or d-sinter, as set forth in U.S. Pat. No. 8,349,030. This is especially beneficial on high charge powder. Without being limited by theory, it is hypothesized that during deoxidation sintering the powder exhibits lower shrinkage, or even expansion, of the powder. With traditional sintering the shrinkage is hypothesized to form a bond with the wire and this bond is not adequately formed in deoxidation sintering as evidenced by the ease with which the wire and anode body are separated. The inability to form strong adhesion between the anode body and the embedded anode lead wire has limited the use of deoxidation sintering to lower charge density powders where the lead wire could be welded to the pre-sintered anodes. In a particularly preferred embodiment deoxidation-sintering can be done in concert with the high density compaction without the typically observed problems associated with poor bonding between the anode wire and pressed anode powder thereby allowing for the use of higher charge density powders and higher volumetric efficiency measured as the capacitance as a function of capacitor volume.
Pull strength is a measurement of the force required, measured by weight, to pull the anode wire from the anode. Pull strengths over 10 kg's can be realized with the instant invention and in some instances the pull strength is sufficiently high that Ta wire breakage occurs before the wire is successfully pulled from the sintered anode body.
The anode preferably comprises a valve metal or conductive oxide of the valve metal with particularly preferred anode materials being selected from aluminum, tantalum and niobium with tantalum being most preferred. The anode has a dielectric thereon, which is preferably an oxide of the anode metal. A cathode is on the dielectric wherein the cathode is preferably chosen from manganese dioxide and conductive polymer. A particularly preferred conductive polymer is 3,4-polyethylene dioxythiophene (PEDT). Dielectric formation and the formation of a cathode from manganese dioxide and conductive polymer is well known to those of skill in the art and further elaboration herein is not necessary.
The anode powder preferably has a charge density of at least 100,000 CV/g, more preferably at least 200,000 CV/g, even more preferably at least 400,000 CV/g and most preferably at least 500,000 CV/g as determined for tantalum. Alternatively, the anode powder is a different valve metal, such as niobium, with an equivalent surface area to tantalum necessary to achieve the charge density.
Deoxidation sintering is accomplished by the use of a reducing agent with a higher oxygen affinity than the valve metal. Preferred reducing agents include alkali metals, alkaline earth metals or aluminum. Calcium, magnesium and aluminum are preferred reducing agents with magnesium being most preferred.
In the process of forming an anode a valve metal powder is pressed into pellets. It is optional, but preferable, to add a lubricant or binder to the powder. A lubricant or binder used during pressing improves the density uniformity through the pellet and prevents die wear-out. An anode lead wire is embedded into the pellet during the pressing. During pressing native oxide which covers the surface of the particles incorporates in the original necks which inhibits subsequent sintering processes.
If a lubricant or binder is used the lubricant or binder is removed by heating in vacuum, or by washing in aqueous detergents. The pressed anodes are deoxidized by reaction with a reducing agent in a deoxidizing furnace at temperatures above the melting point of the reducing agent and typically in the range of 900° C. to 1100° C. These temperatures are much lower than conventional sintering temperatures used for the coarse powders used in high voltage capacitors, which are typically sintered at temperatures in the range 1200° C.-2100° C. depending on the powder CV/g. This first deoxidizing process removes bulk oxygen from the powders preferably from the original necks between the powder particles created at the pressing process. More preferably the pressed pellets are placed in crucibles with Mg chunks or powder and deoxidized by heating above the melting point of magnesium.
In one embodiment, as described in U.S. Pat. No. 7,731,893 B2, the anodes are deoxidized by reducing agent, preferably magnesium, and sintered sequentially. The sealing layer of the reducing agent oxide on the anode surface prevents oxidation in air when anodes are removed from the deoxidizing furnace and placed in a sintering furnace. The layer of reducing agent oxide on the surface is removed preferably by leaching. Leaching can be accomplished in an aqueous mineral acid. A particularly suitable wash solution for removing MgO is a dilute aqueous solution of sulfuric acid and hydrogen peroxide. In other embodiment, described in U.S. Pat. No. 8,349,030 B1, deoxidized and leached anodes undergo sintering in vacuum in a sintering furnace at sintering temperatures equal to, or slightly lower than, conventionally used sintering temperatures. Sintering temperatures are preferably about 1,200° C. to about 1,800° C. and typically about 1500° C. After sintering the lead wire is attached to the sintered anode preferably by welding and the anode is preferably subjected to a second deoxidizing process and a leaching step wherein the oxide of the reducing agent is removed. The second deoxidizing step and leaching step is preferably performed under the same conditions as the first deoxidizing and leaching for manufacturing convenience though different conditions can be used within the scope of conditions suitable for removing the oxide of the reducing agent from the surface.
To form a capacitor the anode is anodized to form a dielectric on the surface wherein the dielectric is preferably an oxide of the valve metal. Anodization is well known in the art and the method of anodizing is not particularly limited herein. Other dielectrics could be incorporated without departing from the scope of the invention but oxides of the anode are widely used in the art.
A cathode layer is formed on the dielectric. The cathode is a conductive layer and may be formed from conductive polymers, such as conductive thiophenes with polyethylenedioxythiophene being exemplary for use in demonstrating the invention. Other cathode layers, such as manganese dioxide which is a conductive semiconductor, are suitable for use in demonstration of the invention. The cathode is formed by coating or in-situ polymerization as well known to those of skill in the art.
It is widely understood that external terminations are difficult to form on the cathode, particularly with a conductive polymeric cathode, and additional layers are typically included to facilitate termination. In particular, carbon layers overcoated with metal layers, such as silver or nickel, are suitable for demonstration of the invention. Carbon layers and metal layers are formed by coating and/or electroplating as well known to those of skill in the art.
The capacitor is typically finished which may include attachment of external anode terminations in electrical contact with the anode wire, external cathode terminations in electrical contact with the cathode, encapsulating in an insulator, testing, packaging and the like.
A vacuum refers to a pressure which is lower than atmospheric pressure. In practice a pressure of no more than 10−4 atm is suitable for demonstration of the teachings herein. Inert gas refers to non-reactive gases or gases which exclude oxidizers such as oxygen. Particularly preferred inert gases include nitrogen, argon, helium and neon. Argon is most preferred. Nitrogen can form nitrides at high sintering temperatures, particularly with tantalum, and is therefore less preferred.
A series of tantalum anodes were prepared in identical fashion using 200,000 CV/g tantalum. The bulk of the anode was pressed to a density of 6.75 g/cc to form monolithic rectangular anode bodies having a size of about 5.20 mm (0.206″) wide, 5.49 mm (0.216″) long and 1.14 mm (0.045″) thick. Throughout the examples, the control samples have no further pressing than used to achieve bulk density. In the inventive samples the powder in the vicinity of the wire was pressed at a compression ratio of about 2:1 or to the degree necessary to distort the 0.381 mm (0.015″) diameter wire in the powder. The result was a pressed powder anode comprising an anode wire therein as represented schematically in
A series of tantalum anodes were prepared in identical fashion using tantalum powder of various charge densities as indicated in Table 2. The bulk of the anode was pressed to a density as reported in Table 2 to form monolithic rectangular anode bodies having a size of about 2.39 mm (0.094″) wide, 1.78 mm (0.070″) long and 0.48 mm (0.019″) thick. In the control samples no further pressing was done. In the inventive samples the powder in the vicinity of the wire was pressed at a compression ratio of about 2:1 or to the degree necessary to distort the 0.300 mm (0.0118″) diameter wire in the powder. A dielectric was formed on the anode at a formation voltage (Vf) as listed in Table 2. The anodes were tested for electrical properties. The control that did not have the powder pressed around the anode, but was deox-sintered, failed due to separation of the anode wire from the anode body and no electrical results could be obtained.
The results presented in Table 2 demonstrate an advantages of the invention which allows for the use of deoxidation sintering while still achieving comparable adhesive strength between the anode body and anode wire. At equivalent formation voltage an improvement in wet leakage (Wet Lkg) can be therefore be realized.
A series of anodes were prepared as in Example 2 using 200,000 CV/g tantalum powder. The powder was pressed to a density of 6.75 g/cc with the high density portion in the vicinity of the wire pressed at a compression ratio of about 2:1. In this example the high pressure was offset from the point of egress as illustrated in
The results presented in Table 3 demonstrate the advantages of the inventive concept and especially the synergism achievable with the high density pressing around the wire and deoxidation sintering. In particular, with a given powder a higher charge can be obtained, at equivalent formation voltage, with lower wet leakage.
A series of anodes were prepared as in Example 2 using tantalum powder with a nominal charge as indicated in Table 4. The anodes were pressed to a density as indicated in Table 4 to either a B-1 case size which was 2.26 mm (0.089″) wide, 1.63 mm (0.064″) long and 1.04 mm (0.041″) thick or a B-2 case size which was 2.13 mm (0.084″) wide, 1.52 mm (0.060″) long and 0.99 mm (0.039″) thick. For the B-1 case size a tantalum wire with a 0.30 mm (0.0118″) diameter was used. For the B-2 case size a tantalum wire with a 0.19 mm (0.0074″) diameter was used. The anodes were vacuum sintered at the temperatures reported in Table 4. The average wire pull strength and average volume shrinkage was determined and reported in Table 4.
Additional results illustrating the advantages of an offset indent, wherein the high density region does not reach the wire egress face, is provide graphically in
A series of anodes were prepared with a tantalum powder have a 200,000 CV/g charge. Each sample was pressed to a density of 6.75 g/cc into a rectangular anode having a size of 3.56 mm (0.140″) wide, 5.08 mm (0.200″) length and 0.813 mm (0.032″) thick around an anode wire with a diameter of 0.381 mm (0.015″). The anodes were deoxidation sintered. The control received no further compression. The inventive sample received multiple high density compressions with a mid-density compression between the high density press regions as illustrated and described relative to
A series of capacitors was formed as a D-case 1.4 rated volt 220 μF capacitors. About half of the capacitors were formed as inventive capacitors comprising an anode as illustrated schematically in
The invention has been described with reference to the preferred embodiments without limit thereto. One of skill in the art would realize additional embodiments and alterations which are not specifically stated herein but are within the scope of the invention as set forth in the claims appended hereto.
The present application is a continuation-in-part of pending U.S. patent application Ser. No. 16/219,355 filed Dec. 13, 2018 which is a divisional application of U.S. patent application Ser. No. 15/872,075 filed Jan. 16, 2018 now U.S. Pat. No. 10,290,429 issued May 14, 2019 which, in turn, claims priority to expired U.S. Provisional Application No. 62/447,123 filed Jan. 17, 2017 all of which are incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4945452 | Sturmer et al. | Jul 1990 | A |
| 5949639 | Maeda et al. | Sep 1999 | A |
| 8349030 | Hussey et al. | Jan 2013 | B1 |
| 10347431 | Tochio | Jul 2019 | B2 |
| 20080037201 | Kuriyama | Feb 2008 | A1 |
| 20090147445 | Kuriyama | Jun 2009 | A1 |
| 20130279078 | Djebara | Oct 2013 | A1 |
| 20140254067 | Myung | Sep 2014 | A1 |
| 20160181022 | Djebara | Jun 2016 | A1 |
| 20160268054 | Petrzilek et al. | Sep 2016 | A1 |
| 20170040118 | Zednicek | Feb 2017 | A1 |
| Number | Date | Country |
|---|---|---|
| S62-116538 | Jul 1987 | JP |
| 1996162373 | Jun 1996 | JP |
| H10-106897 | Apr 1998 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20210375555 A1 | Dec 2021 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62447123 | Jan 2017 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15872075 | Jan 2018 | US |
| Child | 16219355 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16219355 | Dec 2018 | US |
| Child | 17399500 | US |