The present invention relates to the field of sulfur removal and recovery in petroleum production and industry. In particular, the present invention is directed to yolk-shell nanoparticles, the use of the yolk-shell nanoparticles in a method for H2S removal from gas streams, and a corresponding method for H2S removal from gas streams also comprising the regeneration of the yolk-shell nanoparticles.
Acid gases such as hydrogen sulfide (H2S) and carbon dioxide (CO2) along with other impurities often exist in crude oil and natural gas. The diminishing number of the sweet reservoirs worldwide forced many nations towards exploiting heavier and more acidic reservoirs. Since these gases pose severe hazards to both the environment and human health, more technologies to treat them are being developed to remove and recover sulfur species from the gas phase. Those processes are typically given the term H2S removal processes (Y. Al Wahedi, A. I. Torres, S. Al Hashimi, N. I. Dowling, P. Daoutidis, and M. Tsapatsis, “Economic assessment of temperature swing adsorption systems as Claus tail gas clean up units,” Chemical Engineering Science, vol. 126, pp. 186-195, 2015; S. Ibrahim, A. Al Shoaibi, and A. Gupta, “Role of toluene in hydrogen sulfide combustion under Claus condition,” Applied energy, vol. 112, pp. 60-66, 2013).
Commonly, the recovery of sulfur species in petroleum products goes through two stages; a sweetening/desulfurization stage followed by a sulfur recovery stage. In the first stage, H2S and other sulfur species are removed from the petroleum feed either by solvent capture for gases or by hydro-desulfurization for oil (D. M. Wang, “Breakthrough behavior of H2S removal with an iron oxide-based CG-4 adsorbent in a fixed-bed reactor,” 2008). The captured H2S-enriched stream is passed to the sulfur recovery unit. Nowadays, the Claus unit is the most common method used for sulfur recovery, however, it has thermodynamic limitations and leaves around 2 to 5% of the H2S coming in untreated (R. L. Mora, “Sulphur condensation influence in Claus catalyst performance,” Journal of Hazardous Materials, vol. 79, pp. 103-115, 12/1/2000).
The dry adsorption process is an available, feasible and environmental friendly process used for H2S removal (M. Ozekmekci, G. Salkic, and M. F. Fellah, “Use of zeolites for the removal of H2S: A mini-review,” Fuel Processing Technology, vol. 139, pp. 49-60, 11//2015). Various types of adsorbents including metal oxides, zeolites and activated carbon have been tested.
Activated carbons have high adsorption capacities, however, they form fines due to their large micropores. Existing commercial technologies can achieve higher removal of H2S (up to 99.9%) but come at a relatively high capital and operating cost (X. Zhang, G. Dou, Z. Wang, L. Li, Y. Wang, H. Wang, et al., “Selective catalytic oxidation of H2S over iron oxide supported on alumina-intercalated Laponite clay catalysts,” Journal of hazardous materials, vol. 260, pp. 104-111, 2013).
Metal oxides enjoy the attributes of high density and high capacity. The use of metal oxides as adsorbents usually results into the formation of non-regenerable side products that are thermodynamically stable. Moreover, metal oxides lose their activity when subjected to repeated sulfidation and oxidation cycles due to sintering (M. Behl, J. Yeom, Q. Lineberry, P. K. Jain, and M. A. Shannon, “A regenerable oxide-based H2S adsorbent with nanofibrous morphology,” Nature nanotechnology, vol. 7, pp. 810-815, 2012). Sintering refers to the formation of agglomerates from metal oxide crystallites during adsorption and regeneration. Consequently, sintering leads to the formation of bigger crystals of metal oxides, which possess a smaller surface area and less reactive sites. In summary, sintering leads to a loss of adsorbent capacity.
The problem of sintering has been addressed in the past by developing metal-based nanoparticles such as metal oxide/sulfide/sulfate/hydroxides nanoparticles being stabilized, i.e. protected from sintering by a support, e.g. a porous inert oxide material, or, by an encapsulation, e.g. in the form of core-shell nanoparticles, wherein the metal-based nanoparticles are encapsulated by a shell made from a porous inter oxide material. In particular, copper oxide-based adsorbents are known in the art for the removal of sulfur species from gas streams. For example, WO2015/073372 relates to a mesoporous silica support material which is impregnated with copper oxide nanoparticles. The nanoparticles are uniformly distributed throughout the porous silica support and sulfur compounds are adsorbed on the nanoparticles. Supporting metal oxides on mesoporous silica generally addresses the sintering problem. However, supporting metal oxides on mesoporous silica results in low adsorption capacities.
In the past, metal oxides or mixed metal oxides on mesoporous support such as silica-supported copper and zinc oxides were identified to be stable during H2S adsorption-regeneration cycles (B. Elyassi, Y. Al Wahedi, N. Rajabbeigi, P. Kumar, J. S. Jeong, X. Zhang, et al., “A high-performance adsorbent for hydrogen sulfide removal,” Microporous and Mesoporous Materials, vol. 190, pp. 152-155, 2014). However, silica-supported copper and zinc oxides appeared to have low H2S adsorption capacities ranging between 0.16 to 2.5 mmol S/g of adsorbent (B. Elyassi, Y. Al Wahedi, N. Rajabbeigi, P. Kumar, J. S. Jeong, X. Zhang, et al., “A high-performance adsorbent for hydrogen sulfide removal,” Microporous and Mesoporous Materials, vol. 190, pp. 152-155, 2014, Table 1). Consequently, metal oxides or mixed metal oxides on mesoporous supports such as silica-supported copper and zinc oxides require large bed volumes to achieve the required H2S removal causing many practical and environmental issues.
Thus, there is need for improved adsorbents for H2S which have a high H2S adsorption capacity on the one hand and which are stable during regeneration, i.e. loss of H2S adsorption capacity due to sintering is minimized, on the other. Specifically, it is desirable to provide for regenerable adsorbents being highly reactive towards H2S, i.e. having a high loading of metal-based nanoparticles and having pores allowing for high diffusion capability, while side reactions are minimized at the same time. More important, the adsorbents should not undergo sintering at the high temperatures needed for the regeneration of the adsorbents.
However, supporting the nanoparticles by a porous inert oxide material may lead to reduced absorbance capacities, while the shell of core-shell nanoparticles might block some of the active surfaces of the catalysts.
Therefore, it is desirable to provide for nanoparticulate adsorbent materials balancing out reactivity, i.e. activity and selectivity, and stability towards sintering. Thus, it is preferred to provide for metal-based nanoparticles protected by a spherical shell made from an inert oxide material, wherein there is a void space between the shell and the metal-based nanoparticles, allowing for the metal-based nanoparticles to expand and contract during adsorption and regeneration without hindrance or agglomeration.
The present invention relates to yolk-shell nanoparticles having both a high stability towards sintering and high H2S adsorption capacities.
The present invention solves the shortcomings of the prior art by yolk-shell nanoparticles comprising a mesoporous inert oxide material as a shell and as the “yolk” metal-based nanoparticles, such as metal oxide, metal sulfide, metal sulfate, and/or metal hydroxide nanoparticles, wherein the metal-based nanoparticles are contained by said shell and wherein there is a void space between the shell and the metal-based nanoparticles.
In particular, the present invention relates to yolk-shell nanoparticles as adsorbents for H2S, wherein the yolk-shell nanoparticles according to the present invention comprise a mesoporous silica shell and copper-based nanoparticles, such as copper oxide, copper sulfide, copper sulfate, and/or copper hydroxide nanoparticles, wherein the copper-based nanoparticles are contained by said shell and wherein there is a void space between the shell and the copper-based nanoparticles.
In another aspect, the invention relates to a process for producing the yolk-shell nanoparticles according to the present invention comprising the steps of:
In a further aspect, the invention relates to a process for H2S removal from gas streams comprising the steps of:
For a detailed understanding of the present invention, reference should be made to the following detailed description in conjunction with the drawings and embodiments according to the present invention.
In the following, preferred embodiments of the invention are described with reference to the figures, in which:
a+b shows X-Ray powder diffraction patterns of Cu(OH)2 particles as copper-based precursors according to another embodiment of the present invention, wherein the Cu(OH)2 particles were prepared from copper sulfate as copper-based starting material and sodium hydroxide as a base in water at pH=8 in the presence of 200 mg PVP-10, before (a) and after the addition of silica source of TEOS in neutral (A) and alkaline medium(B) as received (b) and after calcination at 450° C. for 2 hours (c).
a+b show TEM Images of CuO/SiO2 SAD-3B (on the top of
a+b show X-Rays diffraction patterns of Cu(OH)2/SiO2 yolk-shell nanoparticles according to another embodiment of the present invention as received from ethanol before (A) and after calcination (B) at 450° C. for 2 hours: (a) SAD-36_1A, (b) SG-16A, (c) SAD-36_2A, (d) SAD-36_4A and (e) SAD-36_3A.
“Nanoparticle” according to the present invention refers to inorganic particulate matter having an average particle size in the nanometers range.
“Yolk-shell nanoparticles” according to the present invention refers to nanoparticulate material comprising metal oxide nanoparticles contained by hollow shells made from a mesoporous inert oxide material. In other words, in yolk-shell nanoparticles there is a void space separating the metal oxide nanoparticles from the mesoporous shell. As it is known in the art, yolk-shell nanoparticles generally have low densities and large surface areas. Moreover, yolk-shell nanoparticles commonly also provide for a high molecular loading capacity in the void space, and also for a tunable void space. Due to these properties, yolk-shell nanoparticles may outperform classical core-shell or hollow nanoparticles. In the art, yolk-shell nanoparticles are known in various fields, such as catalysis, sensors, lithium batteries, biomedical applications, or adsorbents.
Porous materials can be characterized, e.g. by nitrogen adsorption/desorption isotherms at 77 K, e.g. the Brunauer-Emmett-Teller, BET, isotherms or and Barret-Joyner-Halenda, BJH, isotherms. As is known in the art, such analysis allows for determination of surface area (BET isotherms), pore volume and pore size distribution (BJH isotherm) and thus also the “average pore size”. “Average pore size” as used throughout this application refers to the average pore size as determined by nitrogen adsorption/desorption isotherms, specifically the BJH isotherm.
“H2S adsorption capacity” according to the present invention refers to the maximum amount of H2S adsorbed by the yolk-shell nanoparticles. The H2S adsorption capacity may for example be determined from H2S adsorption curves as described in the examples according to this invention. The H2S adsorption capacity may be expressed in the amount of H2S adsorbed per amount of yolk-shell nanoparticles, e.g. in mmol/g, or in the amount of H2S adsorbed per amount of copper oxide nanoparticles, e.g. in mmol/gCuO.
“Stabilized H2S adsorption capacity” according to the present invention refers to an H2S adsorption capacity which does not change more than 10% from one absorption/regeneration cycle to the other, i.e. the H2S adsorption capacity is within the experimental error margin of 10%.
“Reusability” according to the present invention relates to the ability of the same material to be used in multiple repeated cycles of adsorption and regeneration without substantially compromising the H2S-absorbance capacity.
The present invention relates to yolk-shell nanoparticles comprising a mesoporous silica shell and copper-based nanoparticles, such as copper oxide, copper sulfide, copper sulfate, and/or copper hydroxide nanoparticles, wherein the copper-based nanoparticles are contained by said shell and wherein there is a void space between the shell and the copper-based nanoparticles. The void space between the shell and the copper-based nanoparticles allows the particles to expand and contract freely during adsorption and desorption reactions, which in turn leads to a high reactivity of the copper-based nanoparticles.
The copper-based nanoparticles contained by said mesoporous silica shell are actively involved in the adsorption and desorption reactions with the reactants from the gas streams, such as H2S.For example, the adsorption of H2S is a direct chemical reaction between the copper oxide and the H2S, wherein the copper oxide is consumed by the reaction. In particular, copper oxide nanoparticles are highly reactive towards H2S and form copper sulfate. Consequently, the yolk-shell nanoparticles according to the present invention exhibit high H2S adsorption capacities.
The mesoporous silica shell allows reactants to permeate to the inside of the yolk-shell nanoparticles and to contact the copper-based nanoparticles contained by said shell, wherein the chemical reaction between the copper-based nanoparticles and the reactants is largely unaffected by the shell. Further, during regeneration of the yolk-shell nanoparticles, the copper-based nanoparticles contained by the mesoporous silica shell are unable to make contact and agglomerate because of the physical barrier created by the silica shell. The copper-based nanoparticles may thus be regenerated while sintering is kept to a minimum. This allows for reusing the yolk-shell nanoparticles in multiple cycles of adsorption, i.e. H2S-removal from gas streams, and regeneration, i.e. stripping the adsorbed species off the copper-based nanoparticles, without decreasing the adsorption capacity of the yolk-shell nanoparticles. The yolk-shell nanoparticles according to the present invention show higher reusability than other materials known in the art.
In another aspect, the invention relates to a process for producing the yolk-shell nanoparticles according to the present invention comprising the steps of:
As a first step, a copper-based precursor having a low density, such as copper oxide, copper sulfide, copper sulfate, and/or copper hydroxide is provided. A suitable copper-based starting material for the synthesis of the copper-based precursor according to the present invention is selected from the group consisting of copper oxides, copper sulfides, copper sulfates, copper hydroxides, copper acetate, copper acetylacetonate, copper halides and/or any combination thereof. Suitable copper-based starting materials for the synthesis of the copper-based precursor according to the present invention comprise copper salts, such as, for example—but not limited to—, copper actetate, copper sulfate, copper acetylacetonate and/or any combination thereof. The synthesis of the copper-based precursor may be performed either in water or in organic solvents. Suitable organic solvents according to the present invention comprise aliphatic amines selected from the group consisting of trioctyl amine, octyl amine, octadecyl amine, hexadecyl amine, dodecyl amine, oleyl amine and/or any combination thereof. Also, the synthesis of the copper-based precursor may be performed in the presence of a surfactant. Suitable surfactants according to the present invention employed during the provision of the copper-based precursor comprise one or more surfactants selected from the group consisting of cetyltrimethylammonium bromide (CTAB), cetyltrimethylammonium chloride (CTAC), polyvinyl pyrrolidone (PVP), tetradecylsulfonate, tetradecylphosphonic acid (TDPA) and/or any combination thereof. Further, the synthesis of the copper-based precursor may be performed either under air and/or under an atmosphere of an inert gas such as, for example—but not limited to—nitrogen or argon. Reaction temperatures for the synthesis of the copper-based precursor are in the range of 15 to 300° C., e.g. at room temperature, 20 to 30° C., or at elevated temperatures such as 100 to 280° C., 150 to 250° C., 200-280° C. or 100 to 250° C. Also, the synthesis of the copper-based precursor may be performed under neutral to alkaline conditions, i.e. a pH value ranging from 7 to 14, preferably from 8 to 12, more preferably from 9 to 11, and most preferably the pH is 10. Suitable bases comprise, for example—but are not limited to—sodium hydroxide, potassium hydroxide, ammonium hydroxide, and/or any combination thereof.
Second, the mesoporous silica shell is formed around the provided copper-based precursor. Formation of the mesoporous silica shell may be realized via current methods known in the art, such as sol-gel processes. In particular, the mesoporous silica shell is formed via the well-known Stober process which is a hydrolysis-condensation reaction starting from suitable molecular silica precursors such as tetraethyl orthosilicate (TEOS) or tetramethyl orthosilicate (TMOS) and/or any combination thereof. Silica obtained via the Stober process have the advantage that they exhibit monodisperse (uniform) particle sizes. Preferably, the silica is formed in the presence of a surfactant which is removed from the silica reaction product by calcination. Suitable surfactants according to the present invention employed during the formation of the mesoporous silica shell comprise one or more surfactants selected from the group consisting of cetyltrimethylammonium bromide (CTAB), cetyltrimethylammonium chloride (CTAC), polyvinyl pyrrolidone and/or any combination thereof. This allows for the formation of monodisperse silica particles having pores. In dependence on the reaction conditions, such as the solvent, the surfactant, reactant concentrations, catalysts, temperature and/or the pH value, the diameter and volume of the pores may be varied. This allows for control of physical properties such as the surface area.
In a third step, the reaction product obtained by the formation of the silica shell around the copper-based precursor is thermally treated. Thereby, the surfactant is removed from the silica shell and mesopores are formed in the silica shell. In addition, the copper oxide nanoparticles are formed from the copper-based precursor. In particular, thermal treatment is realized by heating the reaction product obtained by the formation of the silica shell around the copper-based precursor to temperatures higher than the decomposition temperature of the surfactant. Thermal treatment of the reaction product obtained by the formation of the silica shell around the copper-based precursor is, for example—but not limited to, performed at temperatures of 400° C. or above, such as 450° C. Moreover, upon thermal treatment the copper-based precursors shrink due to transformation into a denser phase of copper oxide, which leads to a void space between the finally obtained copper oxide nanoparticles and the finally obtained mesoporous silica shell.
Thus, the final product of the synthesis described here are yolk-shell nanoparticles, wherein the copper oxide nanoparticles reside in a hollow sphere inside the mesoporous silica structure wherein a void space between the mesoporous silica shell and the copper oxide nanoparticles is formed. This allows for the copper-oxide nanoparticles to expand and contract within the mesoporous silica shell during adsorption and regeneration, while sintering is prevented concurrently.
In a further aspect, the invention relates to a process for H2S removal from a gas stream comprising the steps of:
The process according to the present invention relates to removal of H2S from a gas stream. According to the present invention, H2S is efficiently removed from a gas stream by adsorption to the yolk-shell nanoparticles according to the present invention.
In particular, adsorbing H2S from a gas stream comprises a direct chemical reaction between H2S from the gas stream and the copper oxide nanoparticles residing in the silica spheres of the yolk-shell nanoparticles, wherein the copper oxide is consumed by the reaction. Copper oxide nanoparticles are highly reactive towards H2S and form copper sulfate. Consequently, the yolk-shell nanoparticles according to the present invention exhibit high H2S adsorption capacities.
Further, regenerating the yolk-shell nanoparticles comprises converting the reaction product of the adsorption process comprising copper-based nanoparticles such as copper sulfate nanoparticles into copper oxide nanoparticles which are again reactive for H2S removal, i.e. the adsorption reaction with H2S. Regeneration of the yolk-shell nanoparticles may comprise stripping the adsorbed species off the copper-based nanoparticles, e.g. via a chemical reaction. Stripping the adsorbed species off the copper-based nanoparticles may involve a chemical reaction with an oxidant, comprised in an oxidant stream. A suitable oxidant stream according to the present invention may comprise an oxidant gas or gas mixture, preferably wherein the oxidant gas or gas mixture comprises oxygen, most preferably wherein the oxidant stream is air. Regenerating the yolk-shell nanoparticles comprises heating the yolk-shell nanoparticles in an oxidant stream to a temperature of at least 500° C., preferably of at least 550° C., more preferably of at least 650° C., even more preferably of at least 700° C. and most preferably of at least 600° C. for 1 hour, preferably for more than 1 hour, more preferably for more than 6 hours, and most preferably for 7 hours. Specifically, the present invention relates to a process for H2S removal from a gas stream comprising both steps (i) and (ii), wherein in step (ii) the yolk-shell nanoparticles are heated in an oxidant stream to a temperature of 600° C. for 7 hours, wherein the oxidant stream is a stream of air.
The void space between the copper-based nanoparticles and the mesoporous silica shells is of great importance for both adsorbing and regenerating the yolk-shell nanoparticles since it allows the copper-based nanoparticles to expand and contract during adsorption and regeneration without hindrance, while sintering is prevented at the same time. This allows for reusing the yolk-shell nanoparticles in multiple cycles of adsorption, i.e. H2S-removal from gas streams, and regeneration, i.e. stripping the adsorbed species off the copper-based nanoparticles, without effectively decreasing the adsorption capacity of the yolk-shell nanoparticles. Thus, the yolk-shell nanoparticles according to the present invention show higher reusability than other materials known in the art.
In the following, embodiments and variations according to the present invention are described in more detail. It is, however, emphasized that the present invention is not limited to these embodiments and variations. It is also mentioned that in the following only individual embodiments of the invention can be described in more detail. The skilled person will realize, however, that the individual features described in relation to these specific embodiments of the adsorbent composition are all as such within the scope of the invention, and that individual features may also be omitted if these seem dispensable in a given case.
The present invention relates to yolk-shell nanoparticles comprising a mesoporous silica shell and copper-based nanoparticles, such as copper oxide, copper sulfide, copper sulfate, and/or copper hydroxide nanoparticles, wherein the copper-based nanoparticles are contained by said shell and wherein there is a void space between the shell and the copper-based nanoparticles. This allows for the copper-oxide nanoparticles to expand and contract within the mesoporous silica shell during adsorption and regeneration, while sintering is prevented concurrently.
In an embodiment according to the invention the yolk-shell nanoparticles comprise copper oxide nanoparticles. In another embodiment according to the invention the yolk-shell nanoparticles comprise copper sulfide nanoparticles. In another embodiment according to the invention the yolk-shell nanoparticles comprise copper sulfate nanoparticles. In another embodiment according to the invention the yolk-shell nanoparticles comprise copper hydroxide nanoparticles. In a preferred embodiment according to the present invention, the yolk-shell nanoparticles comprise copper oxide nanoparticles. Copper oxide nanoparticles are highly reactive towards H2S and form copper sulfate. Consequently, the yolk-shell nanoparticles according to the present invention comprising copper oxide nanoparticles exhibit high H2S adsorption capacities.
In an embodiment according to the present invention, the yolk-shell nanoparticles comprise copper-based nanoparticles having monodisperse particle sizes. In another embodiment according to the invention, the yolk-shell nanoparticles comprise copper-based nanoparticles having a monodisperse particle size from 1 to 50 nm, preferably from 1 to 30 nm, more preferably from 1 to 20 nm, even more preferably from 1 to 15 nm, and/or most preferably from 1 to 8 nm. In a preferred embodiment according to the present invention, the yolk-shell nanoparticles comprise copper-based nanoparticles having a monodisperse particle size from 1 to 15 nm. In an even more preferred embodiment according to the present invention, the yolk-shell nanoparticles comprise copper-based nanoparticles having a monodisperse particle size from 1 to7 nm. This provides for a high surface area and thus a high reactivity in the adsorbing as well as in the regeneration reaction, respectively.
In a further embodiment according to the present invention, the yolk-shell nanoparticles have mesoporous silica wherein the average pore size of the pores within the mesoporous silica shell is in the range from 10 to 40 nm, preferably from 15 to 30 nm, and more preferably from 20 to 25 nm. This provides for diffusion of molecules from the exterior through the silica shell to the CuO crystallites in the inside of the yolk-shell nanoparticles, while movement of CuO crystallites between individual yolk-shell nanoparticles and potential subsequent sintering is prevented.
In another embodiment according to the present invention, the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 25 to 99 w.t.-%, preferably 40 to 99 w.t.-%, more preferably 50 to 99 w.t.-%, even more preferably 60 to 99 w.t.-% and most preferably between 65 to 99 w.t.-%. In a preferred embodiment according to the present invention the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 65 to 99 w.t.-%. This provides for yolk-shell nanoparticles allowing for balancing out reactivity, i.e. activity and selectivity, and stability towards sintering. In other words, this provides for both high H2S adsorption capacities during H2S adsorption from gas streams on the one hand and high stability towards sintering during regeneration at the other at the same time.
In another embodiment according to the present invention, the yolk-shell nanoparticles according to the present invention provide for high H2S adsorption capacities at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm. In a preferred embodiment according to the present invention, the yolk-shell nanoparticles according to the present invention provide for a high H2S adsorption capacitiy at a temperature of 150° C. and an H2S concentration of 100 ppm.
In a further embodiment according to the present invention, the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of at least 2 mmol/g, preferably of at least 4 mmol/g, more preferably of at least 6 mmol/g, even more preferably of at least 8 mmol/g, and most preferably of at least 10 mmol/g.
In yet another embodiment according to the present invention, the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of at least 2 mmol/gCuO, preferably of at least 4 mmol/gCuO, more preferably of at least 6 mmol/gCuO, even more preferably of at least 8 mmol/gCuO, and most preferably of at least 10 mmol/gCuO.
In an embodiment according to the present invention, the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse particle size from 1 to 50 nm, preferably from 1 to 30 nm, more preferably from 1 to 20 nm, even more preferably from 1 to 15 nm, most preferably from 1 to 8 nm, and wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 25 to 99 w.t.-%, preferably 40 to 99 w.t.-%, more preferably 50 to 99 w.t.-%, even more preferably 60 to 99 w.t.-% and most preferably 65 to 99 w.t.-%, and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of at least 2 mmol/gCuO, preferably of at least 4 mmol/gCuO, more preferably of at least 6 mmol/gCuO, even more preferably of at least 8 mmol/gCuO, and most preferably of at least 10 mmol/gCuO, or any combination thereof. In a preferred embodiment according to the present invention, the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse particle size from 1 to 20 nm, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 60 to 99 w.t.-%, and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of least 2 mmol/gCuO. In a more preferred embodiment according to the present invention, the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse particle size from 1 to 15 nm, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 65 to 99 w.t.-%, and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of least 4 mmol/gCuO. In another preferred embodiment according to the present invention, the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse particle size from 1 to 15 nm, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 65 to 99 w.t.-%, and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of least 10 mmol/gCuO.
Another embodiment according to the present invention relates to a process for producing the yolk-shell nanoparticles according to the present invention comprising the steps of:
In an embodiment according to the present invention, the copper-based precursor provided is selected from the group of copper oxides, copper sulfides, copper sulfates, copper hydroxides and any combination thereof. In a preferred embodiment according to the present invention, the copper-based precursor provided is copper oxide. In another preferred embodiment according to the present invention, the copper-based precursor provided is copper sulfide. In an even more preferred embodiment according to the present invention, the copper-based precursor provided is copper hydroxide.
In a further embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction involving a copper-based starting material selected from the group consisting of copper oxides, copper sulfides, copper sulfates, copper hydroxides, copper acetate, copper acetylacetonate, copper halides and/or any combination thereof. In another embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein the chemical reaction is performed in a solvent selected from the group consisting of water, organic solvent such as aliphatic amines selected from the group consisting of trioctyl amine, octyl amine, octadecyl amine, hexadecyl amine, dodecyl amine, oleyl amine and/or any combination thereof. Also, in a further embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein the chemical reaction is performed in the presence of a surfactant selected from the group consisting of cetyltrimethylammonium bromide (CTAB), cetyltrimethylammonium chloride (CTAC), polyvinyl pyrrolidone, tetradecyl sulfonate, tetradecylphosphonic acid (TDPA) and/or any combination thereof. In another embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein the chemical reaction is performed either under air and/or under an atmosphere of an inert gas selected from the group consisting of nitrogen, helium, neon, argon, krypton, xenon, sulfur hexafluoride, carbon dioxide, and/or any combination thereof. In a further embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein the reaction temperature is in the range of 15 to 300° C., preferably at room temperature or in the range of 20 to 30° C., more preferably 100 to 280° C., even more preferably 150 to 250° C., even more preferably 200-280° C. and 100 to 250° C. In another embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein the pH is in the range from 7 to 14, preferably wherein the pH is in the range from 8 to 12, more preferably wherein the pH is in the range from 9 to 11, and most preferably wherein the pH is 10. In a further embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein the base is selected from the group consisting of neutral bases, anionic bases, cationic bases, monoacidic bases, diacidic bases, triacidic bases and/or any combination thereof, preferably the base is selected from the group consisting of sodium hydroxide, potassium hydroxide, ammonium hydroxide, and/or any combination thereof. In a further embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein a second starting-material is provided, preferably wherein the second-starting material is sulfur. The variation of reaction parameters such as starting materials, solvents, surfactant, atmosphere, temperature, pH-value, and choice of a specific base allow for variation of characteristics of the resulting copper-based precursors such as elemental composition, morphology, particle size, and/or any combination thereof.
In a preferred embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein copper sulfate is the copper-based starting material, and wherein the solvent is water, and wherein the base is sodium hydroxide, and wherein the reaction temperature is room temperature, and wherein the reaction medium is alkaline, i.e. the pH is higher than 7. Such reaction conditions allow for the formation of copper-based precursors in the form of crystalline copper oxide nanoparticles, copper hydroxide nanoparticles and/or any combination thereof which allow for efficient H2S adsorption. A pH value below 7 leads to amorphous particles which do not allow for efficient H2S adsorption.
In a more preferred embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein copper sulfate is the copper-based starting material, and wherein the solvent is water, and wherein the base is sodium hydroxide, and wherein the reaction temperature is room temperature, and wherein the pH is in the range of 8 to 12. This allows for the provision of copper-based precursors in the form of copper hydroxide (Cu(OH)2) nanoparticles having particle sizes in the range of 3 to 11 nm. Such a synthesis allows for the formation of copper hydroxide (Cu(OH)2) nanoparticles having particle sizes allowing for efficient H2S adsorption due to a large surface area.
In another more preferred embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein copper sulfate is the copper-based starting material, and wherein the solvent is water, and wherein the base is sodium hydroxide, and wherein the reaction temperature is room temperature, and wherein the pH is 10. This allows for the provision of copper-based precursors in the form of copper hydroxide (Cu(OH)2) nanoparticles having particle sizes in the range of 5 to 8 nm not only allowing for efficient H2S adsorption but also providing for copper hydroxide (Cu(OH)2) nanoparticles being air-stable.
In another more preferred embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein copper sulfate is the copper-based starting material, and wherein the solvent is water, and wherein the base is sodium hydroxide, and wherein the reaction temperature is room temperature, and wherein the pH is in the range of 8 to 12, and wherein a surfactant such as cetyltrimethylammonium bromide (CTAB) or polyvinyl pyrrolidone having an average molecular weight of 10.000 g/mol (PVP-10) is present. This allows for the provision of copper-based precursors in the form of copper hydroxide (Cu(OH)2) nanoparticles allowing for the synthesis of yolk-shell nanoparticles having both a high H2S adsorption capacity and a high reusability.
In another preferred embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein the copper-based starting material is copper acetylacetonate, and wherein the solvent is oleyl amine. In a more preferred embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein the copper-based starting material is copper acetylacetonate, and wherein the solvent is oleyl amine, and wherein the reaction is performed under air at a reaction temperature in the range of 150° C. to 250° C. This allows for providing cuprite (Cu2O) nanoparticles.
In another more preferred embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein the copper-based starting material is copper acetylacetonate, and wherein the solvent is oleyl amine, and wherein in the reaction is performed under an atmosphere of argon at a reaction temperature in the range of 200° C. to 280° C. This allows for providing copper (Cu(O)) nanoparticles.
In another more preferred embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein the copper-based starting material is copper acetylacetonate, and wherein the solvent is oleyl amine, and wherein the reaction is performed under an atmosphere of argon at a reaction temperature in the range of 100° C. to 250° C., and wherein elemental sulfur is added as a second starting material. This allows for providing copper sulfide (CuSx) nanoparticles.
In another more preferred embodiment according to the present invention, providing the copper-based precursor comprises a chemical reaction, wherein copper acetate is the copper-based starting material, and wherein the solvent is trioctyl amine, and wherein tetradecyl sulfonate is used as a surfactant. This allows for providing copper oxide (CuO) nanoparticles having a particle size of 4 nm.
In an embodiment according to the present invention, forming a silica shell around the provided copper-based precursor is performed in water, ethanol, and/or any combination thereof. In a preferred embodiment according to the present invention, forming a silica shell around the provided copper-based precursor is performed in ethanol. This allows for the formation of a uniformly shaped reaction product having a narrow size distribution.
In a further embodiment according to the present invention, forming a silica shell around the provided copper-based precursor is performed by using a molecular silica precursor selected from the group consisting of tetramethyl orthosilicate (TMOS), tetraethyl orthosilicate (TEOS) and/or any combination thereof. In a preferred embodiment, the molecular silica precursor is tetraethylorthosilicate (TEOS). In another embodiment according to the present invention, forming a silica shell around the provided copper-based precursor is performed in the presence of a surfactant selected from the group consisting of cetyltrimethylammonium bromide (CTAB), cetyltrimethylammonium chloride (CTAC) and/or combinations thereof. In a preferred embodiment, the surfactant is cetyltrimethylammonium bromide (CTAB). In a preferred embodiment according to the present invention, forming a silica shell around the provided copper-based precursor is performed in a reaction mixture comprising the provided copper-based precursor, ethanol, tetraethylorthosilicate (TEOS) and cetyltrimethylammonium bromide (CTAB). In a more preferred embodiment according to the present invention, forming a silica shell around the provided copper-based precursor is performed in a reaction mixture comprising copper hydroxide precursor, water, tetraethylorthosilicate (TEOS) and cetyltrimethylammonium bromide (CTAB). The presence of a surfactant during formation of the silica shell around the provided copper-based precursor allows for the formation of mesopores and for the formation of yolk-shell nanoparticles after thermal treatment. Such yolk-shell nanoparticles provide for a high H2S adsorption capacity.
In a more preferred embodiment according to the present invention, forming a silica shell around the provided copper-based precursor is performed in a reaction mixture comprising the provided copper-based precursor, ethanol and tetraethylorthosilicate (TEOS), wherein no surfactant is present. After thermal treatment, this allows for the formation of yolk-shell nanoparticles providing for a high H2S adsorption capacity.
In an even more preferred embodiment according to the present invention, forming a silica shell around the provided copper-based precursor is performed in a reaction mixture comprising the provided copper-based precursor, ethanol and tetraethylorthosilicate (TEOS), wherein no surfactant is present and wherein the concentration of TEOS is low. After thermal treatment, this allows for the formation of yolk-shell nanoparticles providing for a high H2S adsorption capacity and a high reusability.
In a most preferred embodiment according to the present invention, forming a silica shell around the provided copper-based precursor is performed in a reaction mixture comprising the provided copper-based precursor, a mixture of ethanol and water as solvents, tetraethylorthosilicate (TEOS), and ammonium hydroxide as a base, wherein the pH is 9 and wherein no surfactant is present and wherein the concentration of TEOS is low. After thermal treatment, this allows for the formation of yolk-shell nanoparticles providing for a high H2S adsorption capacity and a high reusability.
In another embodiment according to the present invention thermally treating the silica shell comprising the provided copper-based precursor is performed at temperatures of 400° C. or above, such as 450° C. In a further embodiment according to the present invention thermally treating the silica shell comprising the provided copper-based precursor is performed at temperatures of 400° C. or above for 0.5 hour, preferably 1 hour, more preferably for 3 or more hours and most preferably for 2 hours. In a preferred embodiment according to the present invention thermally treating the silica shell comprising the provided copper-based precursor is performed at a temperature of 450° C. In a most preferred embodiment according to the present invention thermally treating the silica shell comprising the provided copper-based precursor is performed at a temperature of 450° C. for 2 hours. By thermally treating the silica shell comprising the provided copper-based precursor a mesoporous silica shell is formed, and the copper oxide nanoparticles are formed from the copper-based precursor, and a void space between the mesoporous silica shell and the copper oxide nanoparticles is formed. This allows for providing yolk-shell nanoparticles balancing out reactivity, i.e. activity and selectivity, and stability towards sintering. In other words, this provides for both high H2S adsorption capacities during H2S adsorption from gas streams on the one hand and high stability towards sintering during regeneration at the other at the same time.
A further embodiment according to the present invention relates to a process for H2S removal from a gas stream comprising the steps of:
Another embodiment according to the present invention relates to a process for H2S removal from a gas stream comprising both steps (i) and (ii), wherein in step (ii) the yolk-shell nanoparticles are heated in an oxidant stream to a temperature of at least 500° C., preferably of at least 550° C., more preferably of at least 650° C., even more preferably of at least 700° C. and most preferably of at least 600° C.
A further embodiment according to the present invention relates to a process for H2S removal from a gas stream comprising both steps (i) and (ii), wherein in step (ii) the yolk-shell nanoparticles are heated in an oxidant stream for 1 hour, preferably for more than 1 hour, more preferably for more than 6 hours, and most preferably for 7 hours.
A preferred embodiment according to the present invention relates to a process for H2S removal from a gas stream comprising both steps (i) and (ii), wherein in step (ii) the yolk-shell nanoparticles are heated in an oxidant stream to a temperature of 600° C. for 7 hours.
A most preferred embodiment according to the present invention relates to a process for H2S removal from a gas stream comprising the steps of:
Another embodiment according to the present invention relates to a process for H2S removal from a gas stream comprising both steps (i) and (ii), wherein in step (ii) the oxidant stream comprises an oxidant gas or gas mixture, preferably wherein the oxidant gas or gas mixture comprises oxygen, most preferably wherein the oxidant stream is air.
An embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise a mesoporous silica shell and copper-based nanoparticles, such as copper oxide, copper sulfide, copper sulfate, and/or copper hydroxide nanoparticles, wherein the copper-based nanoparticles are contained by said shell and wherein there is a void space between the shell and the copper-based nanoparticles.
Another embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper oxide nanoparticles. In another embodiment relating to a process for H2S removal from a gas stream according to the present invention, the yolk-shell nanoparticles comprise copper sulfide nanoparticles. In another embodiment relating to a process for H2S removal from a gas stream according to the present invention, the yolk-shell nanoparticles comprise copper sulfate nanoparticles. In another embodiment relating to a process for H2S removal from a gas stream according to the present invention, the yolk-shell nanoparticles comprise copper hydroxide nanoparticles. In a preferred embodiment relating to a process for H2S removal from a gas stream according to the present invention, the yolk-shell nanoparticles comprise copper oxide nanoparticles. Copper oxide nanoparticles are highly reactive towards H2S and form copper sulfate. Consequently, the process for H2S removal from a gas stream according to the present invention, allows for high H2S adsorption capacities.
A further embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper-based nanoparticles having monodisperse particle sizes. Another embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper-based nanoparticles having a monodisperse particle size from 1 to 50 nm, preferably from 1 to 30 nm, more preferably from 1 to 20 nm, even more preferably from 1 to 15 nm, and/or most preferably from 1 to 8 nm. A preferred embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper-based nanoparticles having a monodisperse particle size from 1 to 15 nm. An even more preferred embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper-based nanoparticles having a monodisperse particle size from 1 to 8 nm. This provides for a high surface area and thus a high reactivity in the adsorbing as well as in the regeneration reaction, respectively.
A further embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 25 to 99 w.t.-%, preferably 40 to 99 w.t.-%, more preferably 50 to 99 w.t.-%, even more preferably 60 to 99 w.t.-% and most preferably 65 to 99 w.t.-%. A preferred embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 65 to 99 w.t.-%. This provides for a process for H2S removal from a gas stream, wherein yolk-shell nanoparticles allow for balancing out reactivity, i.e. activity and selectivity, and stability towards sintering. In other words, this provides for a process for H2S removal from a gas stream, wherein both high H2S adsorption capacities during H2S adsorption from a gas stream on the one hand and high stability towards sintering during regeneration at the other are provided at the same time.
A further embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of at least 2 mmol/g, preferably of at least 4 mmol/g, more preferably of at least 6 mmol/g, even more preferably of at least 8 mmol/g,and most preferably of at least 10 mmol/g.
Yet another embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of at least 2 mmol/gCuO, preferably of at least 4 mmol/gCuO, more preferably of at least 6 mmol/gCuO, even more preferably of at least 8 mmol/gCuO, and most preferably of at least 10 mmol/gCuO.
A further embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse particle size from 1 to 50 nm, preferably from 1 to 30 nm, more preferably from 1 to 20 nm, even more preferably from 1 to 15 nm, most preferably from 1 to 8 nm, and wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 25 to 99 w.t.-%, preferably 40 to 99 w.t.-%, more preferably 50 to 99 w.t.-%, even more preferably 60 to 99 w.t.-% and most preferably 65 to 99 w.t.-%, and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of at least 2 mmol/gCuO, preferably of at least 4 mmol/gCuO, more preferably of at least 6 mmol/gCuO, even more preferably of at least 8 mmol/gCuO, and most preferably of at least 10 mmol/gCuO, or any combination thereof. A preferred embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse particle size from 1 to 20 nm, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 60 to 99 w.t.-%, and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of least 2 mmol/gCuO. A more preferred embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse particle size from 1 to 15 nm, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 65 to 99 w.t.-%, and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of least 4 mmol/gCuO. An even more preferred embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse particle size from 1 to 15 nm, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 65 to 99 w.t.-%, and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of least 8 mmol/gCuO. A most preferred embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse particle size from 1 to 8 nm, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 65 to 99 w.t.-%, and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of least 10 mmol/gCuO.
A further embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein after the regeneration the yolk-shell nanoparticles do not exhibit substantially reduced H2S adsorption capacity in comparison to their original H2S adsorption capacity. Another embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein after the regeneration the yolk-shell nanoparticles exhibit an H2S adsorption capacity which is substantially the same as their original H2S adsorption capacity. Yet another embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein after the regeneration the yolk-shell nanoparticles exhibit H2S adsorption capacity which is in comparison to the original H2S adsorption capacity not reduced more than 75%, preferably not more than 30%, more preferably not more than 20%, even more preferably not more than 10%, and most preferably not more than 5%. A further embodiment according to the present invention relates to a process for H2S removal from a gas stream, wherein after the fifth, preferably after the forth, more preferably after the third, even more preferably after the second, most preferably after the first regeneration a stabilized H2S adsorption capacity that corresponds to at least 35%, preferably 70%, more preferably at least 80%, even more preferably at least 90%, most preferably at least 95% of the initial H2S adsorption capacity is reached.
A further embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream comprising the steps of:
Another embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream comprising both steps (i) and (ii), wherein in step (ii) the yolk-shell nanoparticles are heated in an oxidant stream to a temperature of at least 500° C., preferably of at least 550° C., more preferably of at least 650° C., even more preferably of at least 700° C. and most preferably of at least 600° C.
A further embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream comprising both steps (i) and (ii), wherein in step (ii) the yolk-shell nanoparticles are heated in an oxidant stream for 1 hour, preferably for more than 1 hour, more preferably for more than 6 hours, and most preferably for 7 hours.
A preferred embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream comprising both steps (i) and (ii), wherein in step (ii) the yolk-shell nanoparticles are heated in an oxidant stream to a temperature of 600° C. for 7 hours.
A most preferred embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream comprising the steps of:
Another embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream comprising both steps (i) and (ii), wherein in step (ii) the oxidant stream comprises an oxidant gas or gas mixture, preferably wherein the oxidant gas or gas mixture comprises oxygen, most preferably wherein the oxidant stream is air.
An embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise a mesoporous silica shell and copper-based nanoparticles, such as copper oxide, copper sulfide, copper sulfate, and/or copper hydroxide nanoparticles, wherein the copper-based nanoparticles are contained by said shell and wherein there is a void space between the shell and the copper-based nanoparticles.
Another embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper oxide nanoparticles. In another embodiment relating to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream according to the present invention, the yolk-shell nanoparticles comprise copper sulfide nanoparticles. In another embodiment relating to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream according to the present invention, the yolk-shell nanoparticles comprise copper sulfate nanoparticles. In another embodiment relating to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream according to the present invention, the yolk-shell nanoparticles comprise copper hydroxide nanoparticles. In a preferred embodiment relating to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream according to the present invention, the yolk-shell nanoparticles comprise copper oxide nanoparticles. Copper oxide nanoparticles are highly reactive towards H2S and form copper sulfate. Consequently, the process for H2S removal from a gas stream according to the present invention, allows for high H2S adsorption capacities.
A further embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper-based nanoparticles having monodisperse particle sizes. Another embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper-based nanoparticles having a monodisperse particle size from 1 to 50 nm, preferably from 1 to 30 nm, more preferably from 1 to 20 nm, even more preferably from 1 to 15 nm, and/or most preferably from 1 to 8 nm. A preferred embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper-based nanoparticles having a monodisperse particle size from 1 to 15 nm. An even more preferred embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper-based nanoparticles having a monodisperse particle size from 1 to 8 nm. This provides for a high surface area and thus a high reactivity in the adsorbing as well as in the regeneration reaction, respectively.
A further embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 25 to 99 w.t.-%, preferably 40 to 99 w.t.-%, more preferably 50 to 99 w.t.-%, even more preferably 60 to 99 w.t.-% and most preferably 65 to 99 w.t.-%. A preferred embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 65 to 99 w.t.-%. This provides for a process for H2S removal from a gas stream, wherein yolk-shell nanoparticles allow for balancing out reactivity, i.e. activity and selectivity, and stability towards sintering. In other words, this provides for a process for H2S removal from a gas stream, wherein both high H2S adsorption capacities during H2S adsorption from a gas stream on the one hand and high stability towards sintering during regeneration at the other are provided at the same time.
A further embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of at least 2 mmol/g, preferably of at least 4 mmol/g, more preferably of at least 6 mmol/g, even more preferably of at least 8 mmol/g and most preferably of at least 10 mmol/g.
Yet another embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of at least 2 mmol/gCuO, preferably of at least 4 mmol/gCuO, more preferably of at least 6 mmol/gCuO, even more preferably of at least 8 mmol/gCuO, and most preferably of at least 10 mmol/gCuO.
A further embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse particle size from 1 to 50 nm, preferably from 1 to 30 nm, more preferably from 1 to 20 nm, even more preferably from 1 to 15 nm, most preferably from 1 to 8 nm, and wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 25 to 99 w.t.-%, preferably 40 to 99 w.t.-%, more preferably 50 to 99 w.t.-%, even more preferably 60 to 99 w.t.-% and most preferably 65 to 99 w.t.-%, and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of at least 2 mmol/gCuO, preferably of at least 4 mmol/gCuO, more preferably of at least 6 mmol/gCuO, even more preferably of at least 8 mmol/gCuO, and most preferably of at least 10 mmol/gCuO, or any combination thereof. A preferred embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse particle size from 1 to 20 nm, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 60 to 99 w.t.-% , and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of least 2 mmol/gCuO. A more preferred embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse particle size from 1 to 15 nm, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 65 to 99 w.t.-%, and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of least 4 mmol/gCuO. An even more preferred embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse particle size from 1 to 15 nm, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 65 to 99 w.t.-%, and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of least 8 mmol/gCuO. A most preferred embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse particle size from 1 to 100 nm, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 65 to 99 w.t.-%, and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of least 10 mmol/gCuO.
A further embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein after the regeneration the yolk-shell nanoparticles do not exhibit substantially reduced H2S adsorption capacity in comparison to their original H2S adsorption capacity. Another embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein after the regeneration the yolk-shell nanoparticles exhibit an H2S adsorption capacity which is substantially the same as their original H2S adsorption capacity. Yet another embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein after the regeneration the yolk-shell nanoparticles exhibit an H2S adsorption capacity which is in comparison to the original H2S adsorption capacity not reduced more than 75%, preferably not more than 30%, more preferably not more than 20%, even more preferably not more than 10%, and most preferably not more than 5%. A further embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein after the fifth, preferably after the forth, more preferably after the third, even more preferably after the second, most preferably after the first regeneration a stabilized H2S adsorption capacity that corresponds to at least 35%, preferably 70%, more preferably at least 80%, even more preferably at least 90%, most preferably at least 95% of the initial H2S adsorption capacity is reached.
A more preferred embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse crystallites size from 1 to 15 nm, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 65 to 99 w.t.-%, and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of least 4 mmol/g, and wherein after the regeneration the yolk-shell nanoparticles exhibit an H2S adsorption capacity which is in comparison to the original H2S adsorption capacity not reduced more than 30%.
A more preferred embodiment according to the present invention relates to the use of yolk-shell nanoparticles in a process for H2S removal from a gas stream, wherein the yolk-shell nanoparticles comprise copper oxide nanoparticles having a monodisperse particle size from 1 to 15 nm, wherein the yolk-shell nanoparticles comprise a relative amount by weight of copper-based nanoparticles relative to the total weight of the yolk-shell nanoparticles of 65 to 99 w.t.-%, and wherein the yolk-shell nanoparticles provide for a H2S adsorption capacity per amount of copper oxide nanoparticles comprised by the yolk-shell nanoparticles at temperatures ranging from 25 to 150° C. and H2S concentrations of 1 to 1400 ppm , preferably at a temperature of 150° C. and an H2S concentration of 100 ppm, of least 4 mmol/gCuO, and wherein after the regeneration the yolk-shell nanoparticles exhibit an H2S adsorption capacity which is in comparison to the original H2S adsorption capacity not reduced more than 20%.
Various copper-based precursors such as metallic Cu, copper oxide (Cu2O, CuO) or copper sulfide (CuS) can be prepared in organic solvents such as aliphatic amines (
Copper oxide nanoparticles as copper-based precursors for the synthesis of yolk-shell nanoparticles according to the present invention were prepared by thermal decomposition of copper(I) acetate in trioctylamine (TOA) and tetradecylphosphonic acid (TDPA). The isolated nanoparticles were of spherical shape, and the average size of the nanoparticles was dependent on the concentration of Cu(I) acetate and TPDA, as analyzed by TEM (
Thermal decomposition of copper acetyl acetonate, (Cu(acac)2) as copper-based starting material in oleyl amine at temperatures of 150 to 250° C. in air leads to the formation of cuprite (Cu2O) nanoparticles. Employing an atmosphere of an inert gas such as argon at temperatures of 200 to 280° C. leads to the formation of metallic Cu nanoparticles as copper-based precursors. Copper sulfides (CuSx) as copper-based precursors can be synthesized from copper acetyl acetonate, (Cu(acac)2) as starting material by the addition of elemental sulfur under vigorous stirring in an atmosphere of an inert gas such as argon at temperatures of 100-250° C.
Using trioctyl amine (TOA) as a solvent, the thermally decomposition of copper acetate in the presence of tetradecyl sulfonate leads to the formation of CuO nanoparticles having a particle size of 4nm. CuO nanoparticles having larger particle sizes can be prepared by using higher amounts of precursors and TDPA (
The copper-based precursors from Example 1, i.e. the copper oxide nanoparticles were reacted with tetraethylorthosilicate (TEOS), Si(OEt)4, in the presence of cetyltrimethylammonium bromide (CTAB), where in ethanol was used as solvent. Electron microscopic images of the so obtained reaction product are shown in Fig. 3. As can be seen, the copper-based precursors, i.e. the copper oxide nanoparticles are efficiently encapsulated in hollow spheres of silica.
Yolk-shell nanoparticles according to the present invention were prepared by thermally treating the reaction product provided in Example 2, i.e. calcination of the copper oxide nanoparticles encapsulated in hollow spheres of silica at 450° C. for 5 h. The calcination reaction was also used to simulate the regeneration reaction of the yolk-shell nanoparticles which already underwent the adsorption reaction with H2S. After calcination, the samples were analyzed by diffraction pattern and electron microscopic analysis. The diffraction pattern of the samples before calcination and after calcination is shown in
The morphology of the yolk-shell nanoparticles did not change during calcination, confirming that sintering was effectively prevented.
The copper-based precursors, i.e. the copper oxide nanoparticles as obtained by the synthesis described in Example 1, were subjected to a reaction for formation of the silica shell around the copper-based precursors, wherein said copper-based precursors, i.e. the copper oxide nanoparticles as obtained in Example 1 were reacted with tetraethylorthosilicate (TEOS), Si(OEt)4, in the presence of cetyltrimethylammonium bromide (CTAB). In this case, water was used as solvent instead of ethanol.
Electron microscopic images of the so obtained reaction product are shown in
This was confirmed by diffraction pattern analysis of the reaction product obtained in Example 3 in comparison to the reaction product obtained in Example 2, as shown in
Accordingly, formation of the silica shell around the copper-based precursors is preferably performed in ethanol.
Yolk-shell nanoparticles comprising copper sulfate nanoparticles were prepared by forming the mesoporous silica shell around the copper-based precursors (CuSx nanoparticles) via a reaction employing CTAB and TEOS and subsequent thermal treatment (calcination) at 450° C. for 5 h as described above. The morphology of the resulting yolk-shell nanoparticles comprising copper sulfate nanoparticles was studied by microscopy (
Nanoparticles without silica shell as obtained in Example 1 were subjected to a calcination reaction at 450° C. for 5 h, and the morphology of the samples was subsequently analyzed by means of microscopic analysis (
H2S adsorption was performed in a fixed bed U-shaped quartz reactor. 10 mg of the yolk shell nanoparticles were mixed with 200 mg of quartz particles after sieving, and the mixture was pretreated at 350° C. for five hours under argon to remove any water and organic solvents.
Subsequently, a nitrogen stream comprising 100 ppm H2S was passed through the reactor at 150° C. and at atmospheric pressure, and the respective H2S breakthrough curves at concentrations of 5 ppm H2S were obtained. After the H2S breakthrough, the system was purged with argon to flush out any remaining H2S. Exemplary breakthrough curves are shown for yolk-shell nanoparticles comprising copper oxide nanoparticles, the mesoporous silica shell either obtained in water (
The sulfur capacity of the different samples, as measured by breakthrough analysis, is summarized in table 1. The samples were prepared with different mole-to-mole ratios of copper-based precursors to TEOS.
The H2S adsorption capacity was highest for the sample comprising 1 CuO : 1.8 TEOS, prepared in ethanol, as described above in Example 2. In contrast, nanoparticles without silica shell proved to be significantly inferior to the yolk-shell nanoparticles according to the invention.
Copper oxide precursors were prepared by the thermolytic synthesis route described in Example 1. The copper oxide precursors obtained had a mean particle size of around 4 nm. Those copper oxide precursors were subjected to the formation of the silica shell in ethanol as described in Example 2.
The relative amount of silica was varied by employing different amounts of CTAB and TEOS. Representative TEM images of exemplary yolk-shell nanoparticles with different relative amounts of silica are shown in
These results suggest that a high relative amount by weight of copper-based (CuO) nanoparticles relative to the total weight of the yolk-shell nanoparticles results in a high sulfur capacity.
A) Cu(OH)2 Nanoparticles as Copper-based Precursors were Obtained from CuSO4 as Precursor in Alkaline Aqueous Media (NaOH) Without the Presence of a Surfactant:
Cu(OH)2 nanoparticles as copper-based precursors can be easily prepared in aqueous solutions under alkaline conditions using copper sulfate, specifically cupric sulfate pentahydrate, CuSO4·5H2O, as copper-based starting material and sodium hydroxide, NaOH, as a base. Copper sulfate reacts with sodium hydroxides to produce copper hydroxide and sodium sulfate according to the following equation:
CuSO4+2NaOH→Cu(OH)2(s)+Na2SO4 (Equation 1)
In a typical synthesis 4 mmol CuSO4.5H2O are dissolving in 100 ml de-ionized water (Mixture A) using a mechanical stirrer at room temperature. In a separate beaker an appropriate amount of sodium hydroxide (0.1-4 g NaOH) is dissolved in 50 ml de-ionized water (Mixture B). Subsequently, Mixture B is steadily added to Mixture A and the resulting mixture is mixed vigorously for 10 min, wherein a precipitate forms. The precipitate is separated by centrifugation at 4000 rpm for 10 min, following 2 washes for the removal of byproducts with ethanol and water, separated again by centrifugation at 4000 rpm for 10 min. Following this procedure various Cu-based yolk structures such as CuO, Cu(OH)2 and mixtures thereof, dependent on the pH (7-14) of the reaction mixture were obtained.
In particular, as shown by XRD patterns (
From these experimental data can be concluded that pure Cu(OH)2 nanoparticles as copper-based precursors can be prepared at pH ranging from 8 to 12. The prepared Cu(OH)2 nanoparticles as copper-based precursors varied in size depending on the pH of the reaction mixture. Specifically, the mean crystallite size based on Scherer equation was estimated from the main peak around 17°for Cu(OH)2 nanoparticles: copper-based precursors prepared in alkaline environment with a pH value of 8, 10 and 12 have particle sizes of 3 nm, 6 nm and 11 nm, respectively. It was also found that crystalline CuO nanoparticles (tenorite structure) having particle sizes greater than 11 nm can be prepared at higher pH (>12). CuO nanoparticles prepared at lower pH (≤7) have smaller particles sizes (≤3 nm) and tend to be amorphous. The prepared Cu(OH)2 copper-based precursors prepared at pH=10 are stable against oxidation in air.
B) Cu(OH)2 Nanoparticles were Obtained from CuSO4 as Precursor in Alkaline Aqueous Media (NaOH) in Presence of a Surfactant:
Cu(OH)2 nanoparticles as copper-based precursors can also be prepared in the presence of surfactants such as cetyltrimethyl ammonium bromide (CTAB) or polyvinyl pyrrolidone having an average molecular weight of 10,000 g/mol (PVP-10 (
A silica-shell was formed around the as-prepared Cu(OH)2 nanoparticles as copper-based precursors from Example 9 employing tetraethyl orthosilicate (TEOS), Si(OEt)4. The formation of the silica shell may be carried out with or without the presence of a surfactant (e.g. cetyltrimethylammonium bromide CTAB or polyvinyl pyrrolidone (PVP);
For example, the Cu(OH)2 nanoparticles provided as copper-based precursor were dispersed in deionized water, following the drop wise addition of TEOS (500 μL) as a source of silica in neutral and alkaline environment. From
Based on the above findings, the synthesis of yolk-shell nanoparticles (Cu(OH)2/SiO2) in the presence of cetyl trimethylammonium bromide (CTAB) as surfactant was studied (
The Cu(OH)2 nanoparticles obtained from the synthesis in water (step 1; cf. Example 9) as copper-based precursors were redispersed in 100 ml water in which an additional amount of CTAB as surfactant was disolved, followed by drop wise addition of TEOS (500μL) as silica source by using an electronic pipette (Mixture C). Then, an aqueous solution of 0.2 g NaOH (Mixture D) was mixed with Mixture C and the reaction was left to react for 24 hours under stirring forming a precipitate. The precipitate was then isolated by centrifugation using 4500 rpm for 10 min following 4 washes with water and acetone. The samples were dried in a glass and collected as a powder. In a final step, the as prepared Cu(OH)2 and Cu(OH)2/SiO2 powders were thermally treated (calcined) at a temperature of 450° C. for 2 hours using a heating rate of 2.5°C./min resulting in the removal of the surfactant (CTAB) from the mesopores of the silica shell.
The Cu(OH)2/SiO2 composites prepared without any addition of the CTAB (SAD-6B) have a mean crystallite size of around 4 nm and have, upon thermal treatment, a relative amount by weight of copper-based (CuO) nanoparticles relative to the total weight of the Cu(OH)2/SiO2 composite of 83.8 w.t. % (
When using CTAB as a surfactant in both steps, i.e. step (i) providing the copper-based precursor and step (ii) forming the silica shell, well-defined yolk-shell nanoparticles comprising CuO nanoparticles are obtained upon thermal treatment (samples SAD-3B and SAD-4B).
When tripling (×3) the amount of CTAB (×3) during the formation of the silica shell, the relative amount by weight of silica relative to the total weight of the yolk-shell nanoparticles is 21% w.t. (SAD-4B) in comparison to 6.9% w.t. (SAD-3B). Thus, increasing the amount of CTAB during the development of silica in water by three, leads to the proportionate increase of mesoporous silica. Increasing the amount of CTAB by 2.5 times during step (i) providing the copper-based precursor having a size of 13 nm leads after formation of the silica shell in step (ii) and thermal treatment in step (iii) to the formation of fine chains of yolk-shell nanoparticles comprising CuO nanoparticles having a size of 6 nm (SAD-5B).
Tables 4a and 4b in combination with Table 4c show that the highest relative amounts by weight of silica relative to the total weight of the yolk-shell nanoparticles were achieved when the hydrolysis/condensation reactions of TEOS, step (ii), took place in ethanol in the presence of sodium hydroxide (sample 3; SG-15B). If no sodium hydroxide is employed in ethanol in step (ii), yolk-shell nanoparticles having high relative amounts by weight of copper oxide relative to the total weight of the yolk-shell nanoparticles of 98.8 w.t. % are formed (entry 4; Sample: SG-16B). Due to corresponding small amount of silica (only 1.2 w.t. % SiO2 in the yolk-shell nanoparticles according to entry 4; Sample: SG-16B) the Cu(OH)2 particles after calcination at 450° C./2 h, become larger, possessing crystallite size of around 10.5 nm (instead of 4 nm) during the synthesis of CuO/SiO2 yolk structure.
The yolk-shell nanoparticles obtained in Example 10 were subjected to powder XRD, SEM, and TEM analysis in order to show the effect of the different solvents used in Example 10 on the relative amounts by weight of copper oxide nanoparticles and the mesoporous silica shell. Further, the effect of different solvents on the H2S adsorption capacities of the yolk-shell nanoparticles was analyzed.
The SEM/EDS results show that when ethanol is used as solvent yolk-shell nanoparticles having a higher relative amount by weight of mesoporous silica shell are obtained (49 w.t. % SiO2).
Furthermore, H2S adsorption capacities (at 150° C. and 100 ppm H2S in the gas inlet stream and at a breakthrough concentration of 5 ppm H2S) were measured for yolk-shell nanoparticles having different relative amounts by weight of copper oxide nanoparticles. The copper oxide nanoparticles contained in the hollow mesoporous silica sphere had a mean crystallite size of 4.3 nm in all cases. The variation of the relative amounts by weight of copper oxide nanoparticles (w.t. %) was achieved by using different solvents or mixtures of solvents for the formation of the silica shell as described in Example 10, i.e. (a) water, (b) water/ethanol (1:1) and (c) ethanol (
As Table 5 indicates, increasing the amount of water being present during the formation of the silica shell around the copper-based precursor leads to increased relative amounts by weight of copper-based (CuO) nanoparticles relative to the total weight of the yolk-shell nanoparticles, and thus also leads to higher sulfur capacities.
The H2S adsorption capacity of yolk-shell nanoparticles as in Example 10 (copper hydroxide as copper-based precursor) was measured by breakthrough analysis as described in Example 7 (
The data in Table 4 also suggest that size effects on the sulfur capacities of the yolk-shell nanoparticles outperform effects on the sulfur capacities due to variation of the relative amounts by weight of copper-based (CuO) nanoparticles relative to the total weight of the yolk-shell nanoparticles.
The reusability of yolk-shell nanoparticles according to the present invention, (C), and state-of-the-art copper oxide nanoparticles, (A) and (B), were compared by evaluating the H2S adsorption capacities (at 150° C. and 100 ppm H2S in the gas inlet stream and at a breakthrough concentration of 5 ppm H2S) for several H2S adsorption—regeneration cycles. (A) were thermally treated CuO nanoparticles (no silica shell), (B) were CuO/SiO2 nanoparticles obtained without using any surfactant and (C) were CuO/SiO2 yolk-shell nanoparticles according to the present invention, wherein the copper-based precursor was prepared in water and in the presence of CTAB as a surfactant, and wherein the silica shell was formed around the copper-based precursor in ethanol and water at a pH of 9. The regeneration of the adsorbents (A), (B), and (C) between the H2S adsorption phases was carried out at 600° C. for 7 hours.
The results according to Table 7 suggest that the reusability of yolk-shell nanoparticles according to the present invention, (C) is three to four times increased in comparison to state-of-the-art copper oxide nanoparticles (A) and (B).
Following the synthesis of Cu(OH)2 in water using the triple amount of the surfactant (1200 mg CTAB instead of 400 mg) in slightly lower pH than 10, four more experiments in water were carried out as given in Table 8a and Table 8b.
All samples were thermally treated after step (iii), i.e. heated to 450° C. for 2 hours (calcination). the effect of various parameters on the final CuO/SiO2 yolk-shell nanoparticles was studied, including the concentration of surfactant (CTAB, 1× or 3×), the silica source (0.2 m or 0.5 ml TEOS) as well as the absence or the presence of the base of the hydroxide, including the sodium hydroxide (NaOH) and the ammonium hydroxide (NH4OH).
The H2S adsorption capacities (at 150° C. and wo ppm H2S in the gas inlet stream and at a breakthrough concentration of 5 ppm H2S) and the reusability of yolk-shell nanoparticles according to the present invention and state-of-the-art copper oxide nanoparticles, (A) and (B) were compared, wherein the reaction conditions for the preparation of the copper-based precursor (step (i)) and the reaction conditions for the formation of the silica shell (step (ii)) around the copper-based precursor provided in step 1 were considered. The regeneration of the adsorbents between the H2S adsorption phases was carried out at 600° C. for 7 hours (
From the experimental data provided in Table 9 the following conclusions can be drawn:
Yolk-shell nanoparticles with high relative amounts by weight of copper-based (CuO) nanoparticles relative to the total weight of the yolk-shell nanoparticles of >98 w.t. % have high H2S adsorption capacities. However, yolk-shell nanoparticles with such high relative amounts of CuO are susceptible to sintering during regeneration of the adsorbent. A drop of the initial capacity of more than 80% is observed in the 2nd H2S adsorption cycle after one regeneration step at 600° C. for 7 h. (
Moreover, yolk-shell nanoparticles according to the invention, wherein the copper-based precursor was prepared in water in the presence of a surfactant in the first step, and in the second step the silica shell was formed around the copper-based precursor in ethanol without the presence of a surfactant (Table 9 Sample SAD-36/4B (
In order to evaluate the sorption properties and pore-size distributions, N2 adsorption-desorption curves (
The N2 adsorption-desorption curves for yolk-shell nanoparticles according to the present invention show hysteresis loops and reveal mesoporous silica shells (
As can be seen from the data presented in Table 10, the sample having a relative amount per weight of CuO of 67.2 w.t. % (SAD-36-4B) shows a bimodal pore-size distribution with mean pore diameters of 24.8 nm and 48.7 nm. The sample having a relative amount per weight of CuO of 43 w.t. % (SAD-36-4B) shows a unimodal pore-size distribution with mean pore diameters of 22.4 nm. The pore-size distribution of both samples reveal that the pores of the silica shell are in the mesoporous range. Without wishing to be bound by theory, the yolk-shell nanoparticle's silica shell having pores in the mesoporous range allows diffusion of molecules from the exterior through the silica shell to the CuO crystallites in the inside of the yolk-shell nanoparticles, while movement of CuO crystallites between individual yolk-shell nanoparticles and subsequent sintering is prevented.