Yttrium oxide phosphor mixture and preparation method thereof

Abstract

Fluorescent materials and preparation methods thereof are provided. The fluorescent materials are represented by the general formula: M, Zn1-xAlxO and Y2O3: Re, wherein Re is at least one selected from Eu and Tb, M is at least one selected from Ag, Au, Pt and Pd in the form of nano-particle, and 0<×≦0.05. The said methods include the following steps: step 1, preparing a colloid of Zn1-xAlxO; step 2, preparing a colloid of Y and Re containing the metal element M; step 3, mixing the colloid of Zn1-xAlxO with the colloid of Y and Re, aging and heating treatment to form the fluorescent materials. Compared to the Y2O3 fluorescent materials in the art the present fluorescent materials have higher luminescence efficiency, conductivity, long life and industrial applicability.

Description

FIELD OF THE INVENTION

The present disclosure relates to the field of optoelectronics and illumination techniques, and more particularly relates to an yttrium oxide phosphor mixture and preparation method thereof.

BACKGROUND OF THE INVENTION

With more and more wide development and application of high-quality display illumination devices in work and life, high-efficiency phosphor has become an increasingly important application material. The traditional oxide phosphor exhibits a good stability, however, its luminous efficiency subjected to the low-voltage electron beam is not high enough.

SUMMARY OF THE INVENTION

Accordingly, it is necessary to provide an yttrium oxide phosphor mixture with high luminous efficiency.

In addition, it is necessary to provide a preparation method of the yttrium oxide phosphor mixture with high luminous efficiency.

An yttrium oxide phosphor mixture is represented by the chemical formulae:M, Zn_1-xAl_xO and Y₂ O₃ : Re;

wherein Re is at least one selected from Eu and Tb, M is at least one selected from the group consisting Ag, Au, Pt and Pd in the form of nano-particle, and 0<x≦0.05.

Preferably, the doping concentration of Re in Y₂O₃ is from 0.1% to 10%; the mole ratio of M to the sum of Re and Y is from 0.00002:1 to 0.01:1; the mole ratio of Zn_1-xAl_xO to the sum of Re and Y is from 0.01:1 to 2:1.

A preparation method of an yttrium oxide phosphor mixture comprises the following steps:

S1, preparing a Zn_1-xAl_xO colloid, wherein 0<x≦0.05;

S2, preparing a Y, Re colloid containing metal nano-particle M or ion M; wherein Re is at least one selected from Eu and Tb, M is at least one selected from the group consisting Ag, Au, Pt and Pd; and

S3, mixing the Zn_1-xAl_xO colloid with the Y, Re colloid containing M in water bath with stirring to produce a mixture colloid, aging and heat treating the mixture colloid to obtain the yttrium oxide phosphor mixture.

Preferably, the step S1 comprises: weighing raw materials of zinc salt and aluminum salt, respectively; dissolving with a solvent; adding stabilizing agent to prepare a mixed solution having a total mole concentration of zinc ion and aluminum ion of 0.05 to 0.70 mol/L; stirring the mixed solution in a water bath of 40° C. to 70° C. for 4 to 8 hours to obtain a precursor solution of Zn_1-xAl_xO; placing the precursor solution of Zn_1-xAl_xO in a 60° C. to 90° C. oven and aging for 40 to 60 hours to obtain the Zn_1-xAl_xO colloid.

The zinc salt is selected from at least one of the group consisting of Zn(CH₃COO)₂.2H₂O, Zn(NO₃)₂.6H₂O, ZnCl₂.2H₂O and ZnSO₄.7H₂O; the aluminum salt is selected from at least one of the group consisting of Al(NO₃)₃.9H₂O, AlCl₃.6H₂O and Al₂(SO₄)₃; the solvent is selected from at least one of the group consisting of C₃H₈O₂ and aqueous ethanol solution; and the volume ratio of ethanol to deionized water of the aqueous ethanol solution is in a range of 3:1 to 7:1; the stabilizing agent is selected from at least one of the group consisting of C₂H₇NO, C₄H₁₁NO₂ and C₆H₁₅O₃N.

Preferably, the step S2 comprises: S21, weighing raw materials of Y and Re respectively according to a doping concentration of Re in Y₂O₃ of 0.1% to 10% to prepare a Y, Re solution having a sum ion concentration of 0.1 mol/L to 2.00 mol/L; wherein the Y, Re solution is a Y, Re aqueous solution or an aqueous ethanol solution; S22, measuring the Y, Re solution, adding ethanol, raw material of M, a complexing agent and a surfactant, successively, to prepare a Y, Re alcohol aqueous solution; wherein the ratio of water to alcohol in the Y, Re alcohol aqueous solution is from 1:1 to 9:1, the sum of mole concentration of Y and Re is 0.1 mol/L to 1.0 mol/L, the mole ratio of the complexing agent to the sum of Y and Re is from 1:1 to 5:1, the concentration of the surfactant is 0.05 mol/L to 0.20 mol/L; wherein deionized water can be added to prepare the Y, Re alcohol aqueous solution; S23, stirring the Y, Re alcohol aqueous solution in a water bath of 40° C. to 60° C. for 4 to 6 hours, and placing the Y, Re alcohol aqueous solution in a 60° C. to 90° C. oven and aging for 56 to 90 hours to obtain the Y, Re colloid containing metal nano-particle M or ion M.

Preferably, the raw materials of Y and Re are metal oxides, hydrochloric acid salts, nitrates, or oxalates; the metal oxides are Y₂O₃, Eu₂O₃, Tb₄O₇; the hydrochloric acid salts are YCl₃.7H₂O, EuCl₃, TbCl₃.6H₂O; the nitrates are Y(NO₃)₃.6H₂O, Eu(NO₃)₃.6H₂O, Tb(NO₃)₃.6H₂O; the oxalates are oxalates which can provide Y³⁺, Eu^{3 +}, and Tb³⁺; the raw material of M is Ag, Au, Pt and Pd in the form of nano-particle; the raw material of M is aqueous or alcohol solution of AgNO₃, HAuCl₄, H₂PtCl₆, H₂PdCl₄; the complexing agent is citric acid; the surfactant is selected from at least one of the group consisting of polyethylene glycol 6000, polyethylene glycol 8000, polyethylene glycol 10000 and polyethylene glycol 20000.

Preferably, during the preparation of the Y, Re aqueous solution, if the hydrochloric acid salts or the nitrates are used as the raw materials of Y and/or Re, the raw materials of Y and/or Re are dissolved in a vessel directly. If the metal oxides or the oxalates are used as the raw materials of Y and/or Re, the metal oxides or the oxalates corresponding to the Y, Re are dissolved in a vessel with hydrochloric acid or nitric acid under a condition of 15° C. to 100° C. with stirring.

Preferably, in step S3, the ratio of the sum of molar amount of Zn and Al to the sum of molar amount of Re and Y in the mixture colloid is in a range of 0.01:1 to 2:1; the temperature of water bath is 15° C. to 80° C., the stirring time is 1 to 4 hours; the aging is placing the mixture colloid in a 100° C. to 200° C. oven for 48 to 96 hours; the heat treating is placing the mixture colloid in a crucible at 800° C. to 1300° C. for 0.5 to 6 hours under an air atmosphere or a reducing atmosphere. The reducing atmosphere are powdered carbon or a mixture of nitride (N₂) and hydrogen H₂ where the proportion of hydrogen to nitrogen in the hydrogen-nitrogen atmosphere is 95:5.

Preferably, when the Re in the yttrium oxide phosphor contains Terbium, the reducing atmosphere is used; when the Re contains only Europium, the air atmosphere is used.

Metal nano-particles are added into the yttrium oxide phosphor doped with a rare earth element, and since the metal nano-particles has large surface area, the internal quantum efficiency of the phosphor is improved due to the surface plasmon coupling effect, thereby improving the luminous efficiency of the phosphor.

Meanwhile, the material is oxide phosphor, which has a long work life. By changing the type and ratio of Re, the phosphor can radiate light with different wavelength. The addition of the conductive material of Zn_1-xAl_xO leads to further improvement of conductivity of the phosphor, thus enhancing the emission luminance of the phosphor. The conductivity of the phosphor can be further improved by changing the amount of Zn and Al in Zn_1-xAl_xO.

The preparation method is a simple, low equipment requirement, and has a short preparation period; the method is proved feasible after several practices.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a flowchart of an embodiment of a method for preparing an yttrium oxide phosphor mixture;

FIG. 2 shows a spectrum of the yttrium oxide phosphor mixture prepared according to the present invention and commercial broadband spectrum phosphor under a cathode ray excitation.

DETAILED DESCRIPTION

The surface plasmon (SP) is a type of a wave spreading along the interface between metal and dielectric, and the amplitude exponentially decay as the distance away from the interface increases. When the metal surface structure is changed, the nature, dispersion relation, excitation mode, and coupling effects of surface plasmon polaritons (SPPs) will change significantly. The electromagnetic fields caused by the SPPs, not only can restrain the spread of light waves in the subwavelength structure, but also can generate and manipulate the electromagnetic radiation from the light frequency to the microwave band, thus active manipulation of light propagation is achieved, and to increase the optical density of states of the luminescent materials and enhances spontaneous emission rate. In addition, by using the surface plasmon coupling effect, the internal quantum efficiency of the luminescent material can be greatly improved, thus enhancing the emission intensity of the material.

Accordingly, when preparing the phosphor, metal nano-particle and conductive material can be added, such that the emission intensity of the phosphor can be enhanced via the surface plasmon coupling effect and excellent conductivity. How to effectively integrate surface plasmon effect and excellent conductive properties in the phosphor has been an important research in the field of materials science, optoelectronics and illumination technology.

An yttrium oxide phosphor mixture, which is conductive and integrated with SP effect, is provided. A preparation method of the yttrium oxide phosphor mixture is provided. The phosphor colloidis prepared by sol-gel method, and conductive material and metal nano-particles are added in the phosphor colloid, thus the emission intensity of the phosphor can be enhanced.

An yttrium oxide phosphor mixture, which includes Y₂O₃, rare earth element Re, metal nano-particle M, and Zn_1-xAl_xO, is represented by the chemical formulae:M, Zn_1-xAl_xO and Y₂O₃:Re;

wherein Re is at least one selected from Eu and Tb, M is at least one selected from the group consisting Ag, Au, Pt and Pd in the form of nano-particle, and 0<x≦0.05.

In a preferable embodiment, Re is doped in Y₂O₃, and the doping concentration is from 0.1% to 10%. The mole ratio of M to the sum of Re and Y is from 0.00002:1 to 0.01:1. The mole ratio of Zn_1-xAl_xO to the sum of Re and Y is from 0.01:1 to 2:1. The metal nano-particles are added into the yttrium oxide phosphor doped with Re, thus improving the luminous efficiency of the phosphor, meanwhile, the material is oxide phosphor, which has a long work life. By changing the type and ratio of Re, the phosphor can radiate light with different wavelength. The addition of the conductive material of Zn_1-xAl_xO leads to further improvement of conductivity of the phosphor, thus enhancing the emission luminance of the phosphor. The conductivity of the phosphor can be further improved by changing the amount of Zn and Al in Zn_1-xAl_xO.

An embodiment of a preparation method of the yttrium oxide phosphor mixture is provided with the following technical solutions:

One, selection of the chemical compounds and raw materials:

1. selection of the raw materials in preparation of Zn_1-xAl_xO colloid.

Selection of zinc salt: zinc acetate (Zn(CH₃COO)₂.2H₂O), zinc nitrate (Zn(NO₃)₂.6H₂O), zinc chloride (ZnCl₂.2H₂O), zinc sulfate (ZnSO₄.7H₂O) of analytical grade;

Selection of aluminum salt: aluminum nitrate (Al(NO₃)₃.9H₂O), aluminum chloride (AlCl₃.6H₂O), aluminum sulfate (Al₂(SO₄)₃), .etc of analytical grade;

Selection of stabilizer: monoethanolamine (C₂H₇NO), diethanolamine (C₄H₁₁NO₂), triethanolamine (C₆H₁₅O₃N) of analytical grade;

Selection of solvent: ethylene glycol monomethyl ether (C₃H₈O₂), ethanol solution (a ratio of ethanol to deionized water ranges from (3-7): 1) of analytical grade.

2. selection of the chemical compounds and raw materials in preparation of Y, Re colloid containing metal nano-particle M or ion M:

The raw materials of metal oxide are Y₂O₃, Eu₂O₃, Tb₄O₇;

The raw materials of hydrochloric acid salts are YCl₃.7H₂O, EuCl₃, TbCl₃.6H₂O;

The raw materials of nitrates are Y(NO₃)₃.6H₂O, Eu(NO₃)₃.6H₂O, Tb(NO₃)₃.6H₂O;

The raw materials of oxalates are oxalates which can provide Y³⁺, Eu³⁺, and Tb³⁺;

Analytical grade hydrochloric acid or analytical nitrate (HNO₃: 65%˜68%, concentration: 14.4˜15.2 mol/L; HCl: 36˜37%, concentration: 11.7 mol/L) are used to dissolve oxide and oxalates;

The solvent is deionized water (H₂O) or mixed solution containing anhydrous ethanol (CH₃CH₂OH) and deionized water, where the ratio of ethanol to the deionized water is in a range of (1˜9):1;

The complexing agent is analytical grade citric acid (C₆H₈O₇.H₂O);

The surfactant is selected from at least one of the group consisting of polyethylene glycol 6000, polyethylene glycol 8000, polyethylene glycol 10000 and polyethylene glycol 20000 of analytical grade.

The raw materials of M are nano-particles of Ag, Au, Pt, Pd; or such salts can be dissolved in water or ethanol as AgNO₃, HAuCl₄, H₂PtCl₆, H₂PdCl₄.

Two, the preparation of phosphor

FIG. 1 illustrates a preparation method of the phosphor including the following steps:

S10, preparation of a Zn_{1-xl Alx}O colloid.

Zinc salt and aluminum salt with a certain mass ratio are weighed respectively according to the chemical formula of Zn_1-xAl_xO, where 0<x≦0.05. After the zinc salt and aluminum salt are dissolved with a solvent, stabilizing agent is added to prepare a mixed solution having a total mole concentration of zinc ion and aluminum ion of from 0.05 to 0.70 mol/L. The mixed solution is stirred in a water bath of 40° C. to 70° C. for 4 to 8 hours to obtain a precursor solution, and then the precursor solution is placed in a 60° C. to 90° C. oven and aged for 40 to 60 hours to obtain the Zn_1-xAl_xO colloid.

S20, preparation of Y, Re colloid containing metal element.

Raw materials of Y and Re are weighed respectively according to a doping concentration of Re in Y₂O₃ of 0.1% to 10% to prepare a Y, Re solution having a sum ion concentration of 0.1 mol/L to 2.00 mol/L, where the Y, Re solution is a Y, Re aqueous solution or an aqueous ethanol solution. The Y, Re solution is measured, and ethanol, raw material of M, a complexing agent and a surfactant are added successively, to prepare a Y, Re alcohol aqueous solution, where the ratio of water to alcohol in the Y, Re alcohol aqueous solution is from 1:1 to 9:1, the sum of mole concentration of Y and Re is 0.1 mol/L to 11.0 mol/L, the mole ratio of the complexing agent to the sum of Y and Re is from 1:1 to 5:1, the concentration of the surfactant is 0.05 mol/L to 0.20 mol/L. In a preferable embodiment, when preparing the Y, Re alcohol aqueous solution, deionized water can be added to maintain the alcohol-water ratio in the Y, Re alcohol aqueous solution. The Y, Re alcohol aqueous solution is stirred in a water bath of 40° C. to 60° C. for 4 to 6 hours, and placed in a 60° C. to 90° C. oven and aged for 56 to 90 hours to obtain the Y, Re colloid containing metal element.

When the added raw material of M is metal nano-particle, the metal element in the Y, Re colloid is in a form of nano-particle; when the added raw material of M is metal salt solution, the metal element in the Y, Re colloid is in a form of ion.

During the preparation of the Y, Re aqueous solution, if the hydrochloric acid salts or the nitrates Y(NO₃)₃.6H₂O, Eu(NO₃)₃.6H₂O, Tb(NO₃), YCl₃.7H₂O, EuCl₃, TbCl₃.6H₂O are used as the raw materials, a proper amount of the chemical compounds is weighed and dissolved in a vessel directly with deionized water. If the metal oxides or the oxalates are used as the raw materials, the metal oxides or the oxalates corresponding to the Y, Re are dissolved in a vessel with analytical grade hydrochloric acid or nitric acid under a condition of 15° C. to 100° C. with stirring.

S30, mixing, aging and heat treating of Zn_1-xAl_xO colloid and Y, Re colloid.

The Zn_1-xAl_xO colloid and the Y, Re colloid are mixed while maintaining the ratio of the sum of molar amount of Zn and Al to the sum of molar amount of Re and Yin the mixture colloid being in a range of 0.01:1 to 2:1. The mixture is then stirred in a water bath of 15° C. to 80° C. for 1 to 4 hours to produce a mixture colloid. The mixture colloid is aged in a 100° C. to 200° C. oven for 48 to 96 hours. After drying, the mixture colloid is placed in a crucible at 800° C. to 1300° C. for 0.5 to 6 hours under an air atmosphere or a carbon reducing atmosphere or a hydrogen-nitrogen reducing atmosphere to obtain the yttrium oxide phosphor mixture, where the proportion of hydrogen to nitrogen in the hydrogen-nitrogen atmosphere is 95:5.

In the preferable embodiment, when the Re in the yttrium oxide phosphor contains Terbium, the reducing atmosphere is used; when the Re contains only Europium, the air atmosphere is used. M in ionic state is reduced to a simple substance of nano-particle state during the heat treatment operation. When the Re contains only Europium, the air atmosphere is used, however, it is found that M in ionic state is also reduced to obtain the simple substance of nano-particle state.

FIG. 2 shows a spectrum of the yttrium oxide phosphor mixture prepared according to the present invention and commercial broadband spectrum phosphor under a cathode ray excitation.

The spectrum is obtained using Shimadzu RF5301PC spectrometer under a 5kv voltage test conditions, where a represents a spectra of an Y₂O₃:Re phosphor adding Ag nano-particle and Zn_1-xAl_xO prepared according to Example 1,b represents a spectra of commercial broadband spectrum phosphor. It is calculated by Shimadzu RF5301PC spectrometer software that, the integral area of a is 1.49 times of the integral area of b.

In other words, the luminous efficiency of the Y₂O₃:Re phosphor adding Ag nano-particle and Zn_1-xAl_xO prepared according to Example 1 is significantly improved compared to the commercial broadband spectrum phosphor.

The preparation method of the yttrium oxide phosphor mixture will further be described below mainly with reference to the specific examples.

EXAMPLE 1

2.1292g of Zn(CH₃COO)₂.2H₂O, 0.1125 g of Al(NO₃)₃.9H₂O, and 0.6 ml C₂H₇NO were weighed and placed in a vessel at room temperature. Glycol ether was added to make 50 ml, stirred at a 60° C. water bath for 4 hours to obtain a clear precursor solution of Zn_0.97Al_0.03O. The precursor solution of Zn_0.97Al_0.03O was placed in a 60° C. oven and aged for 70 hours to form an even Zn_0.97Al_0.03O colloid.

37.9180 g of Y(NO₃)₃.6H₂O and 0.4441 g of Eu(NO₃)₃.6H₂O were weighed and dissolved in deionized water at room temperature to prepare a 100 ml of Y, Eu aqueous solution of 1 mol/L with a doping concentration of Eu in Y of 1%. 4 ml of Y, Eu aqueous solution of 1 mol/L were measured, 1 ml of deionized water and 35 ml of anhydrous ethanol were added as solvent, 0.4 ml of AgNO₃ solution of 0.01 mol/L was added, 3.0742 g of citric acid and 5 g of polyethylene glycol 10000 were added, stirred in a 60° C. water bath for 4 hours to obtain a clear precursor solution of Y, Eu colloid. The obtained precursor solution of Y, Eu colloid was placed in a 90° C. oven and aged for 40 hours to form an even Y, Eu colloid.

1ml of resulting Zn_0.97Al_0.03O colloid was added into the Y, Eu colloid, the mixture was stirred at 15° C. for 2 hours, dried in a 100° C. oven for 48 hours, insulated in an 800° C. muffle furnace for 2 hours to obtain Y₂O₃:Eu phosphor doped with Ag nano-particle and Zn_0.97Al_0.03O.

EXAMPLE 2

0.5460g of Zn(CH₃COO)₂.2H₂O, 0.0047g of Al(NO₃)₃.9H₂O, and 0.4ml C₆H₁₅O₃N were weighed and placed in a vessel at room temperature. A mixed solution containing ethanol and water with a volume ratio of 4:1 was added to make 50 ml, stirred at a 40° C. water bath for 5 hours to obtain a clear precursor solution of Zn_0.995Al_0.005O. The precursor solution of Zn_0.995Al_0.005O was placed in a 50° C. oven and aged for 90 hours to form an even Zn_0.995Al_0.005O colloid.

18.7675 g of Y(NO₃)₃.6H₂O and 0.4461 g of Eu(NO₃)₃.6H₂O were weighed and dissolved in deionized water at room temperature to prepare a 100 ml of Y, Eu aqueous solution of 0.5 mol/L with a doping concentration of Eu in Y of 2%. 8 ml of Y, Eu aqueous solution of 0.50 mol/L were measured, 32 ml of anhydrous ethanol were added as solvent, 2.5 ml of Ag nano-particle solution of 0.001 mol/L was added, 7.6856 g of citric acid and 2 g of polyethylene glycol 8000 were added, stirred in a 40° C. water bath for 6 hours to obtain a clear precursor solution of Y, Eu colloid. The obtained precursor solution of Y, Eu colloid was placed in a 90° C. oven and aged for 60 hours to form an even Y, Eu colloid.

0.4ml of resulting Zn_0.995Al_0.005O colloid was added into the Y, Eu colloid, the mixture was stirred in a 50° C. water bath for 2 hours, dried in a 150° C. oven for 96 hours, insulated in a 1300° C. muffle furnace for 0.5 hours to obtain Y₂O₃:Eu phosphor doped with Ag nano-particle and Zn_0.995Al_0.005O.

EXAMPLE 3

3.1937g of Zn(CH₃COO)₂.2H₂O, 0.1688 g of Al(NO₃)₃.9H₂O, and 0.9 ml C₂H₇NO were weighed and placed in a vessel at room temperature. A methoxyethanol was added to make 50 ml, stirred at a 60° C. water bath for 8 hours to obtain a clear precursor solution of Zn_0.97Al_0.03O. The precursor solution of Zn_0.97Al_0.03O was placed in a 60° C. oven and aged for 65 hours to form an even Zn_0.97Al_0.03O colloid.

10.7260 g of Y₂O₃ and 0.8798 g of Eu₂O₃ were weighed and dissolved in 27 ml of hydrochloric acid at 60° C.; deionized water was added to prepare a 100 ml of Y, Eu aqueous solution of 1 mol/L with a doping concentration of Eu in Y of 5%. 8 ml of Y, Eu aqueous solution of 1.00 mol/L were measured, 32 ml of anhydrous ethanol were added as solvent, 1.6 ml of Pt nano-particle solution of 0.001 mol/L was added, 6.1485 g of citric acid and 5 g of polyethylene glycol 6000 were added, stirred in a 60° C. water bath for 4 hours to obtain a clear precursor solution of Y, Eu colloid. The obtained precursor solution of Y, Eu colloid was placed in a 70° C. oven and aged for 60 hours to form an even Y, Eu colloid.

26ml of resulting Zn_0.97Al_0.03O colloid was added into the Y, Eu colloid, the mixture was stirred in a 80° C. water bath for 2 hours, dried in a 100° C. oven for 48 hours, insulated in an 800° C. muffle furnace for 2 hours to obtain Y₂O₃:Eu phosphor doped with Pt nano-particle and Zn_0.97Al_0.03O.

EXAMPLE 4

1.0865g of Zn(CH₃COO)₂.2H₂O, 0.0188g of Al(NO₃)₃.9H₂O, and 0.4 ml C₂H₇NO were weighed and placed in a vessel at room temperature. A mixed solution containing ethanol and water with a volume ratio of 5:1 was added to make 50 ml, stirred at a 50° C. water bath for 6 hours to obtain a clear precursor solution of Zn_0.985Al_0.015O. The precursor solution of Zn_0.985Al_0.015O was placed in a 60° C. oven and aged for 80 hours to form an even Zn_0.985Al_0.015O colloid.

37.9180 g of Y(NO₃)₃.6H₂O and 0.4441 g of Eu(NO₃)₃.6H₂O were weighed and dissolved in deionized water at room temperature to prepare a 100 ml of Y, Eu aqueous solution of 1 mol/L with a doping concentration of Eu in Y of 1%. 20 ml of Y, Eu aqueous solution of 1 mol/L were measured, 20 ml of anhydrous ethanol were added as solvent, 0.4 ml of Pt nano-particle solution of 0.01 mol/L was added, 15.3712 g of citric acid and 5 g of polyethylene glycol 10000 were added, stirred in a 60° C. water bath for 4 hours to obtain a clear precursor solution of Y, Eu colloid. The obtained precursor solution of Y, Eu colloid was placed in an 80° C. oven and aged for 56 hours to form an even Y, Eu colloid.

1ml of resulting Zn_0.985Al_0.015O colloid was added into the Y, Eu colloid, the mixture was stirred in a 60° C. water bath for 2 hours, dried in a 100° C. oven for 48 hours, insulated in an 800° C. muffle furnace for 2 hours to obtain Y₂O₃:Eu phosphor doped with Pd nano-particle and Zn_0.985Al_0.015O.

EXAMPLE 5

2.4810g of ZnC1₂.2H₂O, 0.1448g of AlCl₃.6H₂O, and 1.5 ml C₄H₁₁NO₂ were weighed and placed in a vessel at room temperature. A mixed solution containing ethanol and water with a volume ratio of 3:1 was added to make 50 ml, stirred at a 70° C. water bath for 8 hours to obtain a clear precursor solution of Zn_0.96Al_0.04O. The precursor solution of Zn_0.96Al_0.040 was placed in a 60° C. oven and aged for 70 hours to form an even Zn_0.96Al_0.04O colloid.

76.5254 g of Y(NO₃)₃.6H₂O and 0.0892 g of Eu(NO₃)₃.6H₂O were weighed and dissolved in deionized water to prepare a 100 ml of Y, Eu aqueous solution of 2 mol/L with a doping concentration of Eu of 0.1%. 20 ml of Y, Eu aqueous solution of 2.00 mol/L were measured, 20 ml of anhydrous ethanol were added as solvent, 0.8 ml of Ag nano-particle solution of 0.001 mol/L was added, 7.6856 g of citric acid and 8 g of polyethylene glycol 10000 were added, stirred in a 50° C. water bath for 6 hours to obtain a clear precursor solution of Y, Eu colloid. The obtained precursor solution of Y, Eu colloid was placed in a 60° C. oven and aged for 60 hours to form an even Y, Eu colloid.

6.7ml of resulting Zn_0.96Al_0.04O colloid was added into the Y, Eu colloid, the mixture was stirred in a 80° C. water bath for 4 hours, dried in a 200° C. oven for 50 hours, insulated in a 1000° C. muffle furnace for 3 hours to obtain Y₂O₃:Eu phosphor doped with Ag nano-particle and Zn_0.96Al_0.04O.

EXAMPLE 6

1.0865g of Zn(CH₃COO)₂.2H₂O, 0.0188 g of Al(NO₃)₃.9H₂O, and 0.4 ml C₂H₇NO were weighed and placed in a vessel at room temperature. A mixed solution containing ethanol and water with a volume ratio of 5:1 was added to make 50 ml, stirred at a 50° C. water bath for 6 hours to obtain a clear precursor solution of Zn_0.99 Al_0.01O. The precursor solution of Zn_0.99 Al_0.01O was placed in a 70° C. oven and aged for 80 hours to form an even Zn_0.99Al_0.01O colloid.

37.9180 g of Y(NO₃)₃.6H₂O and 0.4441 g of Eu(NO₃)₃.6H₂O were weighed and dissolved in deionized water at room temperature to prepare a 100 ml of Y, Eu aqueous solution of 1 mol/L with a doping concentration of Eu in Y of 1%. 20 ml of Y, Eu aqueous solution of 1.00 mol/L were measured, 20 ml of anhydrous ethanol were added as solvent, 2 ml of H₂PdCl₄ solution of 0.1 mol/L was added, 15.3712 g of citric acid and 5 g of polyethylene glycol 20000 were added, stirred in a 60° C. water bath for 4 hours to obtain a clear precursor solution of Y, Eu colloid. The obtained precursor solution of Y, Eu colloid was placed in an 80° C. oven and aged for 56 hours to form an even Y, Eu colloid.

1ml of resulting Zn_0.99Al_0.01O colloid was added into the Y, Eu colloid, the mixture was stirred in a 60° C. water bath for 2 hours, dried in a 100° C. oven for 96 hours, insulated in an 800° C. muffle furnace for 6 hours to obtain Y₂O₃:Eu phosphor doped with Pd nano-particle and Zn_0.99Al_0.01O.

EXAMPLE 7

4.2583 g of Zn(CH₃COO)₂.2H₂O, 0.2251 g of Al(NO₃)₃.9H₂O, and 2 ml C₄H₁₁NO₂ were weighed and placed in a vessel at room temperature. A methoxyethanol was added to make 50 ml, was added to make 50 ml, stirred at a 60° C. water bath for 4 hours to obtain a clear precursor solution of Zn_0.97Al_0.03O. The precursor solution of Zn_0.97Al_0.03O was placed in a 60° C. oven and aged for 78 hours to form an even Zn_0.97Al_0.03O colloid.

37.5350 g of Y(NO₃)₃.6H₂O and 0.9061 g of Tb(NO₃)₃.6H₂O were weighed and dissolved in deionized water at room temperature to prepare a 100 ml of Y, Tb aqueous solution of 1 mol/L with a doping concentration of Tb in Y of 2%. 12 ml of Y, Tb aqueous solution of 1.00 mol/L were measured, 28 ml of anhydrous ethanol were added as solvent, 0.6 ml of Au nano-particle solution of 0.001 mol/L was added, 9.2227 g of citric acid and 5 g of polyethylene glycol 10000 were added, stirred in a 60° C. water bath for 4 hours to obtain a clear precursor solution of Y, Tb colloid. The obtained precursor solution of Y, Tb colloid was placed in a 90° C. oven and aged for 56 hours to form an even Y, Tb colloid.

15 ml of resulting Zn_0.97Al_0.03O colloid was added into the Y, Tb colloid, the mixture was stirred in a 60° C. water bath for 2 hours, dried in a 100° C. oven for 96 hours, insulated in a 1000° C. muffle furnace for 2 hours in a carbon reducing atmosphere to obtain Y₂O₃:Tb phosphor doped with Au nano-particle and Zn_0.97Al_0.03O.

EXAMPLE 8

7.2984 g of Zn(CH₃COO)₂.2H₂O, 0.6565 g of Al(NO₃)₃.9H₂O, and 6 ml C₂H₇NO were weighed and placed in a vessel at room temperature. A mixed solution containing ethanol and water with a volume ratio of 6:1 was added to make 50ml, stirred at a 70° C. water bath for 5 hours to obtain a clear precursor solution of Zn_0.95Al_0.05O. The precursor solution of Zn_0.95Al_0.05O was placed in a 60° C. oven and aged for 85 hours to form an even Zn_0.95Al_0.05O colloid.

31.1728 g of YCl₃ and 1.1198 g of TbCl₃.6H₂O were weighed and dissolved in deionized water at room temperature to prepare a 100 ml of Y, Tb aqueous solution of 1 mol/L with a doping concentration of Eu in Y of 3%. 4 ml of Y, Tb aqueous solution of 1.00 mol/L were measured, 36 ml of anhydrous ethanol were added as solvent, 0.4 ml of H₂PtCl₆ solution of 0. 1 mol/L was added, 6.2125 g of citric acid and 5 g of polyethylene glycol 10000 were added, stirred in a 60° C. water bath for 5 hours to obtain a clear precursor solution of Y, Tb colloid. The obtained precursor solution of Y, Tb colloid was placed in a 60° C. oven and aged for 60 hours to form an even Y, Tb colloid.

4 ml of resulting Zn_0.95Al_0.05O colloid was added into the Y, Tb colloid, the mixture was stirred in a 70° C. water bath for 4 hours, dried in a 180° C. oven for 60 hours, insulated in a 1000° C. muffle furnace under a hydrogen-nitrogen reducing atmosphere for 3 hours to obtain Y₂O₃:Tb phosphor doped with Pt nano-particle and Zn_0.95Al_0.05O.

EXAMPLE 9

2.9452 g of Zn(NO₃)₂.6H₂O, 0.0241 g of AlCl₃.6H₂O, and 0.6ml C₂H₇NO were weighed and placed in a vessel at room temperature. A methoxyethanol was added to make 50 ml, stirred at a 60° C. water bath for 7 hours to obtain a clear precursor solution of Zn_0.99Al_0.01O. The precursor solution of Zn_0.99Al_0.01O was placed in a 60° C. oven and aged for 56 hours to form an even Zn_0.99Al_0.01O colloid.

28.6899 g of oxalate yttrium and 1.7201 g of oxalic acid europium were weighed and dissolved in 20 ml of nitrate at 15° C. with stirring; deionized water was added to prepare a 100 ml of Y, Eu aqueous solution of 1 mol/L with a doping concentration of Eu of 5%. 20 ml of Y, Eu aqueous solution of 1.00 mol/L were measured, 20 ml of anhydrous ethanol were added as solvent, 0.2 ml of HAuCl₄ solution of 0.1 mol/L was added, 7.6856 g of citric acid and 5 g of polyethylene glycol 10000 were added, stirred in a 60° C. water bath for 4 hours to obtain a clear precursor solution of Y, Eu colloid. The obtained precursor solution of Y, Eu colloid was placed in a 60° C. oven and aged for 60 hours to form an even Y, Eu colloid.

5 ml of resulting Zn_0.99Al_0.01O colloid was added into the Y, Eu colloid, the mixture was stirred in an 80° C. water bath for 2 hours, dried in a 100° C. oven for 56 hours, insulated in an 800° C. muffle furnace for 2 hours to obtain Y₂O₃:Eu phosphor doped with Au nano-particle and Zn_0.99Al_0.01O.

EXAMPLE 10

9.8596 g of ZnSO4.7H₂O, 0.2395g of Al₂(SO₄)₃, and 4.7 ml C₆H₁₅O₃N were weighed and placed in a vessel at room temperature. A methoxyethanol was added to make 50 ml, stirred at a 60° C. water bath for 5 hours to obtain a clear precursor solution of Zn_0.98Al_0.02O. The precursor solution of Zn_0.98Al_0.02O was placed in a 60° C. oven and aged for 60 hours to form an even Zn_0.98Al_0.02O colloid.

11.0647 g of Y₂O₃ and 0.3739 g of Tb₄O₇ were weighed and dissolved in 27 ml of hydrochloric acid at 100° C. with stirring; deionized water was added to prepare a 100 ml of Y, Tb aqueous solution of 1 mol/L with a doping concentration of Tb of 2%. 15 ml of Y, Tb aqueous solution of 1.00 mol/L were measured, 25 ml of anhydrous ethanol were added as solvent, 0.75 ml of HAuCl₄ solution of 0.01 mol/L was added, 5.7642 g of citric acid and 5 g of polyethylene glycol 10000 were added, stirred in a 50° C. water bath for 5 hours to obtain a clear precursor solution of Y, Tb colloid. The obtained precursor solution of Y, Tb colloid was placed in a 90° C. oven and aged for 60 hours to form an even Y, Tb colloid.

10 ml of resulting Zn_0.98A1_0.02O colloid was added into the Y, Tb colloid, the mixture was stirred in a 60° C. water bath for 2 hours, dried in a 130° C. oven for 59 hours, insulated in a 1100° C. muffle furnace under a hydrogen-nitrogen reducing atmosphere for 2 hours to obtain Y₂O₃:Tb phosphor doped with Au nano-particle and Zn_0.98Al_0.02O.

EXAMPLE 11

2.1292 g of Zn(CH₃COO)₂.2H₂O, 0.1125 g of Al(NO₃)₃.9H₂O, and 0.6 ml C₂H₇NO were weighed and placed in a vessel at room temperature. A methoxyethanol was added to make 50 ml, was added to make 50 ml, stirred at a 60° C. water bath for 4 hours to obtain a clear precursor solution of Zn_0.97Al_0.03O. The precursor solution of Zn_0.97Al_0.03O was placed in a 60° C. oven and aged for 70 hours to form an even Zn_0.97Al_0.03O colloid.

37.9180 g of Y(NO₃)₃.6H₂O and 0.4441 g of Eu(NO₃)₃.6H₂O were weighed and dissolved in deionized water at room temperature to prepare a 100 ml of Y, Eu aqueous solution of 1 mol/L with a doping concentration of Tb in Y of 1%. 4 ml of Y, Eu aqueous solution of 1.00 mol/L were measured, 1 ml of deionized water and 35 ml of anhydrous ethanol were added as solvent, 2.0 ml of Pd nano-particle solution of 0.01 mol/L was added, 3.0742 g of citric acid and 5 g of polyethylene glycol 10000 were added, stirred in a 60° C. water bath for 4 hours to obtain a clear precursor solution of Y, Eu colloid. The obtained precursor solution of Y, Eu colloid was placed in a 90° C. oven and aged for 40 hours to form an even Y, Eu colloid.

1 ml of resulting Zn_0.97Al_0.03O colloid was added into the Y, Eu colloid, the mixture was stirred in a 60° C. water bath for 2 hours, dried in a 130° C. oven for 59 hours, insulated in a 1100° C. muffle furnace for 2 hours in a carbon reducing atmosphere to obtain Y₂O₃:Eu phosphor doped with Pd nano-particle and Zn_0.97Al_0.03O.

EXAMPLE 12

6.9733 g of ZnSO4.7H₂O, 0.1283g of Al₂(SO₄)₃, and 1.5 ml C₂H₇NO were weighed and placed in a vessel at room temperature. A mixed solution containing ethanol and water with a volume ratio of 7:1 was added to make 50 ml, stirred at a 60° C. water bath for 5 hours to obtain a clear precursor solution of Zn_0.985Al_0.015O. The precursor solution of Zn_0.985Al_0.015O was placed in a 60° C. oven and aged for 90 hours to form an even Zn_0.985Al_0.015O colloid.

27.1780 g of oxalic yttrium, and 3.5099 g of oxalic acid terbium were weighed and dissolved in 20 ml of nitrate at 15° C. with stirring; deionized water was added to prepare a 100 ml of Y, Tb aqueous solution of 1 mol/L with a doping concentration of Tb of 10%. 10 ml of Y, Tb aqueous solution of 1.00 mol/L were measured, 30 ml of anhydrous ethanol were added as solvent, 0.8 ml of AgNO₃ solution of 0.1 mol/L was added, 7.6858 g of citric acid and 5 g of polyethylene glycol 10000 were added, stirred in a 60° C. water bath for 4 hours to obtain a clear precursor solution of Y, Tb colloid. The obtained precursor solution of Y, Tb colloid was placed in an 80° C. oven and aged for 50 hours to form an even Y, Tb colloid.

10 ml of resulting Zn_0.985Al_0.015O colloid was added into the Y, Tb colloid, the mixture was stirred in a 60° C. water bath for 2 hours, dried in a 100° C. oven for 53 hours, insulated in a 1300° C. muffle furnace under a hydrogen-nitrogen reducing atmosphere for 2 hours to obtain Y₂O₃:Tb phosphor doped with Ag nano-particle and Zn_0.985Al_0.15O.

EXAMPLE 13

2.4810 g of ZnC1₂.2H₂O, 0.1448 g of AlCl₃.6H₂O, and 1.5 ml C₄H₁₁NO₂ were weighed and placed in a vessel at room temperature. A mixed solution containing ethanol and water with a volume ratio of 3:1 was added to make 50 ml, stirred at a 70° C. water bath for 8 hours to obtain a clear precursor solution of Zn_0.96Al_0.04O. The precursor solution of Zn_0.96Al_0.04O was placed in a 60° C. oven and aged for 70 hours to form an even Zn_0.96Al_0.04O colloid.

76.5254 g of Y(NO₃)₃.6H₂O and 0.0892 g of Eu(NO₃)₃.6H₂O were weighed and dissolved in deionized water to prepare a 100 ml of Y, Eu aqueous solution of 2 mol/L with a doping concentration of Eu of 0.1%. 20 ml of Y, Eu aqueous solution of 2.00 mol/L were measured, 20 ml/L of anhydrous ethanol were added as solvent, 2.0 ml of Pd nano-particle solution of 0.01 mol/L was added, 7.6856 g of citric acid and 8 g of polyethylene glycol 10000 were added, stirred in a 50° C. water bath for 6 hours to obtain a clear precursor solution of Y, Eu colloid. The obtained precursor solution of Y, Eu colloid was placed in a 60° C. oven and aged for 60 hours to form an even Y, Eu colloid.

6.7 ml of resulting Zn_0.96Al_0.04O colloid was added into the Y, Eu colloid, the mixture was stirred in a 60° C. water bath for 2 hours, dried in a 130° C. oven for 59 hours, insulated in a 1200° C. muffle furnace for 2 hours to obtain Y₂O₃:Eu phosphor doped with Pd nano-particle and Zn_0.96Al_0.04O.

EXAMPLE 14

0.5460 g of Zn(CH₃COO)₂.2H₂O, 0.0047 g of Al(NO₃)₃.9H₂O, and 0.4 ml C₆H₁₅O₃N were weighed and placed in a vessel at room temperature. A mixed solution containing ethanol and water with a volume ratio of 4:1 was added to make 50ml, stirred at a 40° C. water bath for 5 hours to obtain a clear precursor solution of Zn_0.995Al_0.005O. The precursor solution of Zn_0.995Al_0.005O was placed in a 60° C. oven and aged for 90 hours to form an even Zn_0.995Al_0.005O colloid.

18.7675 g of Y(NO₃)₃.6H₂O and 0.4461 g of Eu(NO₃)₃.6H₂O were weighed and dissolved in deionized water at room temperature to prepare a 100 ml of Y, Eu aqueous solution of 0.5 mol/L with a doping concentration of Eu in Y of 2%. 8 ml of Y, Eu aqueous solution of 0.50 mol/L were measured, 32 ml of anhydrous ethanol were added as solvent, 0.8 ml of HAuCl₄ solution of 0.01 mol/L was added, 7.6856 g of citric acid and 2 g of polyethylene glycol 10000 were added, stirred in a 40° C. water bath for 6 hours to obtain a clear precursor solution of Y, Eu colloid. The obtained precursor solution of Y, Eu colloid was placed in a 90° C. oven and aged for 60 hours to form an even Y, Eu colloid.

0.4 ml of resulting Zn_0.995Al_0.005O colloid was added into the Y, Eu colloid, the mixture was stirred in a 60° C. water bath for 2 hours, dried in a 130° C. oven for 59 hours, insulated in an 1200° C. muffle furnace for 2 hours to obtain Y₂O₃:Eu phosphor doped with Au nano-particle and Zn_0.995Al_0.005O.

EXAMPLE 15

3.1937 g of Zn(CH₃COO)₂.2H₂O, 0.1688 g of Al(NO₃)₃.9H₂O, and 0.9 ml C₂H₇NO were weighed and placed in a vessel at room temperature. A methoxyethanol was added to make 50ml, stirred at a 60° C. water bath for 8 hours to obtain a clear precursor solution of Zn_0.97Al_0.03O. The precursor solution of Zn_0.97Al_0.03O was placed in a 60° C. oven and aged for 65 hours to form an even Zn_0.97Al_0.03O colloid.

10.7260 g of Y₂O₃ and 0.8798 g of Eu₂O₃ were weighed and dissolved in 27 ml of hydrochloric acid at 60° C. with stirring, deionized water was added to prepare a 100 ml of Y, Eu aqueous solution of 1 mol/L with a doping concentration of Eu in Y of 5%. 8 ml of Y, Eu aqueous solution of 1.00 mol/L were measured, 32 ml of anhydrous ethanol were added as solvent, 1.6 ml of Au nano-particle solution of 0.001 mol/L was added, 6.1485 g of citric acid and 5 g of polyethylene glycol 6000 were added, stirred in a 60° C. water bath for 4 hours to obtain a clear precursor solution of Y, Eu colloid. The obtained precursor solution of Y, Eu colloid was placed in a 70° C. oven and aged for 60 hours to form an even Y, Eu colloid.

26 ml of resulting Zn_0.97Al_0.03O colloid was added into the Y, Eu colloid, the mixture was stirred in a 75° C. water bath for 2 hours, dried in a 100° C. oven for 48 hours, insulated in an 800° C. muffle furnace for 2 hours to obtain Y₂O₃:Eu phosphor doped with Au nano-particle and Zn_0.97Al_0.03O.

EXAMPLE 16

2.9452 g of Zn(NO₃)₂.6H₂O, 0.0241 g of AlCl₃.6H₂O, and 0.6ml C₂H₇NO were weighed and placed in a vessel at room temperature. A methoxyethanol was added to make 50 ml, stirred at a 60° C. water bath for 7 hours to obtain a clear precursor solution of Zn_0.99Al_0.01O. The precursor solution of Zn_0.99Al_0.01O was placed in a 60° C. oven and aged for 56 hours to form an even Zn_0.99Al_0.01O colloid.

28.6899 g of oxalate yttrium and 1.7201 g of oxalic acid europium were weighed and dissolved in 20 ml of nitrate; deionized water was added to prepare a 100 ml of Y, Eu aqueous solution of 1 mol/L with a doping concentration of Eu of 5%. 20 ml of Y, Eu aqueous solution of 1.00 mol/L were measured, 20 ml of anhydrous ethanol were added as solvent, 0.4 ml of AgNO₃ solution of 0.1 mol/L was added, 7.6858 g of citric acid and 5 g of polyethylene glycol 10000 were added, stirred in a 60° C. water bath for 4 hours to obtain a clear precursor solution of Y, Eu colloid. The obtained precursor solution of Y, Eu colloid was placed in a 60° C. oven and aged for 60 hours to form an even Y, Eu colloid.

5 ml of resulting Zn_0.99Al_0.01O colloid was added into the Y, Eu colloid, the mixture was stirred in a 65° C. water bath for 2 hours, dried in a 100° C. oven for 48 hours, insulated in a 900° C. muffle furnace for 2 hours to obtain Y₂O₃:Eu phosphor doped with Ag nano-particle and Zn_0.99Al_0.01O.

EXAMPLE 17

4.2583 g of Zn(CH₃COO)₂.2H₂O, 0.2251 g of Al(NO₃)₃.9H₂O, and 2 ml C₄H₁₁NO₂ were weighed and placed in a vessel at room temperature. A methoxyethanol was added to make 50 ml, was added to make 50 ml , stirred at a 60° C. water bath for 4 hours to obtain a clear precursor solution of Zn_0.97Al_0.03O. The precursor solution of Zn_0.97Al_0.03O was placed in a 60° C. oven and aged for 78 hours to form an even Zn_0.97Al_0.03colloid.

37.5350 g of Y(NO₃)₃.6H₂O and 0.9061 g of Tb(NO₃)₃.6H₂O were weighed and dissolved in deionized water at room temperature to prepare a 100 ml of Y, Tb aqueous solution of 1 mol/L with a doping concentration of Tb in Y of 2%. 12 ml of Y, Tb aqueous solution of 1.00 mol/L were measured, 28 ml of anhydrous ethanol were added as solvent, 0.24 ml of Pt nano-particle solution of 0.001 mol/L was added, 9.2227 g of citric acid and 5 g of polyethylene glycol 10000 were added, stirred in a 60° C. water bath for 4 hours to obtain a clear precursor solution of Y, Tb colloid. The obtained precursor solution of Y, Tb colloid was placed in a 90° C. oven and aged for 56 hours to form an even Y, Tb colloid.

15 ml of resulting Zn_0.97Al_0.03O colloid was added into the Y, Tb colloid, the mixture was stirred in a 55° C. water bath for 2.5 hours, dried in a 150° C. oven for 90 hours, insulated in a 1300° C. muffle furnace for 0.5 hour in a carbon reducing atmosphere to obtain Y₂O₃:Tb phosphor doped with Pt nano-particle and Zn_0.97Al_0.03O.

EXAMPLE 18

6.9733 g of ZnSO4.7H₂O, 0.1283 g of Al₂(SO₄)₃, and 1.5 ml C₂H₇NO were weighed and placed in a vessel at room temperature. A mixed solution containing ethanol and water with a volume ratio of 7:1 was added to make 50 ml, stirred at a 60° C. water bath for 5 hours to obtain a clear precursor solution of Zn_0.985Al_0.15O. The precursor solution of Zn_0.985Al_0.015O was placed in a 60° C. oven and aged for 90 hours to form an even Zn_0.985Al_0.015O colloid.

27.1780 g of oxalic yttrium and 3.5099 g of oxalic acid terbium were weighed and dissolved in 20 ml of nitrate at 15° C. with stirring; deionized water was added to prepare a 100 ml of Y, Tb aqueous solution of 1 mol/L with a doping concentration of Tb of 10%. 10 ml of Y, Tb aqueous solution of 1.00 mol/L were measured, 30 ml of anhydrous ethanol were added as solvent, 0.1 ml of H₂PdCl₄ solution of 0.1 mol/L was added, 7.6858 g of citric acid and 5 g of polyethylene glycol 6000 were added, stirred in a 60° C. water bath for 4 hours to obtain a clear precursor solution of Y, Tb colloid. The obtained precursor solution of Y, Tb colloid was placed in an 80° C. oven and aged for 50 hours to form an even Y, Tb colloid.

10 ml of resulting Zn_0.985Al_0.015O colloid was added into the Y, Tb colloid, the mixture was stirred in a 80° C. water bath for 1 hour, dried in a 170° C. oven for 96 hours, insulated in a 800° C. muffle furnace under a carbon reducing atmosphere for 0.5 hour to obtain Y₂O₃:Tb phosphor doped with Pd nano-particle and Zn_0.985Al_0.015O.

EXAMPLE 19

9.6620 g of ZnSO4.7H₂O, 0.2395g of Al₂(SO₄)₃, and 4.7 ml C₆H₁₅O₃N were weighed and placed in a vessel at room temperature. A methoxyethanol was added to make 50ml, stirred at a 60° C. water bath for 5 hours to obtain a clear precursor solution of Zn_0.98Al_0.02O. The precursor solution of Zn_0.98Al_0.02O was placed in a 60° C. oven and aged for 60 hours to form an even Zn_0.98Al_0.02O colloid.

11.0647 g of Y₂O₃ and 0.3739 g of Tb₄O₇ were weighed and dissolved in 27 ml of hydrochloric acid at 100° C. with stirring; deionized water was added to prepare a 100 ml of Y, Tb aqueous solution of 1 mol/L with a doping concentration of Tb of 2%. 15 ml of Y, Tb aqueous solution of 1.00 mol/L were measured, 25 ml of anhydrous ethanol were added as solvent, 3.0 ml of Ag nano-particle solution of 0.001 mol/L was added, 5.7642 g of citric acid and 5 g of polyethylene glycol 10000 were added, stirred in a 50° C. water bath for 5 hours to obtain a clear precursor solution of Y, Tb colloid. The obtained precursor solution of Y, Tb colloid was placed in a 90° C. oven and aged for 60 hours to form an even Y, Tb colloid.

10 ml of resulting Zn_0.98Al_0.02O colloid was added into the Y, Tb colloid, the mixture was stirred in a 50° C. water bath for 2 hours, dried in a 180° C. oven for 85 hours, insulated in a 1300° C. muffle furnace under a carbon reducing atmosphere for 0.5 hour to obtain Y₂O₃:Tb phosphor doped with Ag nano-particle and Zn_0.98Al_0.02O.

EXAMPLE 20

7.2984 g of Zn(CH₃COO)₂2H₂O, 0.6565 g of Al(NO₃)₃.9H₂O, and 6 ml C₂H₇NO were weighed and placed in a vessel at room temperature. A mixed solution containing ethanol and water with a volume ratio of 6:1 was added to make 50 ml, stirred at a 70° C. water bath for 5 hours to obtain a clear precursor solution of Zn_0.95Al_0.05O. The precursor solution of Zn_0.95Al_0.05O was placed in a 60° C. oven and aged for 85 hours to form an even Zn_0.95Al_0.05O colloid.

31.1728 g of YCl₃ and 1.1198 g of TbCl₃.6H₂O were weighed and dissolved in deionized water at room temperature to prepare a 100 ml of Y, Tb aqueous solution of 1 mol/L with a doping concentration of Eu in Y of 3%. 4 ml of Y, Tb aqueous solution of 1.00 mol/L were measured, 36 ml of anhydrous ethanol were added as solvent, 2.0 ml of Pt nano-particle solution of 0.001 mol/L was added, 6.2125 g of citric acid and 5 g of polyethylene glycol 10000 were added, stirred in a 60° C. water bath for 5 hours to obtain a clear precursor solution of Y, Tb colloid. The obtained precursor solution of Y, Tb colloid was placed in a 60° C. oven and aged for 60 hours to form an even Y, Tb colloid.

4 ml of resulting Zn_0.95Al_0.05O colloid was added into the Y, Tb colloid, the mixture was stirred in a 75° C. water bath for 3.5 hours, dried in a 160° C. oven for 96 hours, insulated in a 1300° C. muffle furnace under a carbon reducing atmosphere for 6 hours to obtain Y₂O₃:Tb phosphor doped with Pt nano-particle and Zn_0.95Al_0.05O.

Although the invention has been described in language specific to structural features and/or methodological acts, it is to be understood that the invention defined in the appended claims is not necessarily limited to the specific features or acts described. Rather, the specific features and acts are disclosed as sample forms of implementing the claimed invention.

Claims

1. An yttrium oxide phosphor mixture comprising: M, Zn1-xAlxO and Y2O3: Re;wherein Re is at least one selected from Eu and Tb, M is at least one selected from the group consisting Ag, Au, Pt and Pd in the form of nano-particle, and 0<x≦0.05.

2. The yttrium oxide phosphor mixture according to claim 1, wherein the doping concentration of Re in Y2O3 is from 0.1% to 10%; the mole ratio of M to the sum of Re and Y is from 0.00002:1 to 0.01:1;the mole ratio of Zn1-xAlxO to the sum of Re and Y is from 0.01:1 to 2:1.

3. A preparation method of an yttrium oxide phosphor mixture, comprising the following steps: S1, preparing a Zn1-xAlxO colloid, wherein 0<x≦0.05;S2, preparing a Y, Re colloid containing metal nano-particle M or ion M, wherein Re is at least one selected from Eu and Tb, M is at least one selected from the group consisting Ag, Au, Pt and Pd; andS3, mixing the Zn1-xAlxO colloid with the Y, Re colloid containing M in water bath with stirring to produce a mixture colloid, aging and heat treating the mixture colloid to obtain the yttrium oxide phosphor.

4. The preparation method of the yttrium oxide phosphor mixture according to claim 3, wherein the step S1 comprises: weighing raw materials of zinc salt and aluminum salt, respectively; dissolving with a solvent; adding stabilizing agent to prepare a mixed solution having a total mole concentration of zinc ion and aluminum ion of 0.05 to 0.70 mol/L; stirring the mixed solution in a water bath of 40° C. to 70° C. for 4 to 8 hours to obtain a precursor solution of Zn1-xAlxO; placing the precursor solution of Zn1-xAlxO in a 60° C. to 90° C. oven and aging for 40 to 60 hours to obtain the Zn1-xAlxO colloid.

5. The preparation method of the yttrium oxide phosphor mixture according to claim 4, wherein the zinc salt is selected from at least one of the group consisting of Zn(CH3COO)2.2H2O, Zn(NO3)2.6H2O, ZnCl2.2H2O and ZnSO4.7H2O; the aluminum salt is selected from at least one of the group consisting of Al(NO3)3.9H2O, AlCl3.6H2O and Al2(SO4)3;the solvent is selected from at least one of the group consisting of C3H8O2 and aqueous ethanol solution; and the volume ratio of ethanol to deionized water of the aqueous ethanol solution is in a range of 3:1 to 7:1; andthe stabilizing agent is selected from at least one of the group consisting of C2H7NO, C4H11NO2 and C6H15O3N.

6. The preparation method of the yttrium oxide phosphor mixture according to claim 3, wherein the step S2 comprises: S21, weighing raw materials of Y and Re respectively according to a doping concentration of Re in Y2O3 of 0.1% to 10% to prepare a Y, Re solution having a sum ion concentration of 0.1 mol/L to 2.00 mol/L; wherein the Y, Re solution is a Y, Re aqueous solution or an aqueous ethanol solution;S22, measuring the Y, Re solution, adding ethanol, raw material of M, a complexing agent and a surfactant, successively, to prepare a Y, Re alcohol aqueous solution; wherein the ratio of water to alcohol in the Y, Re alcohol aqueous solution is from 1:1 to 9:1, the sum of mole concentration of Y and Re is 0.1 mol/L to 1.0 mol/L, the mole ratio of the complexing agent to the sum of Y and Re is from 1:1 to 5:1, the concentration of the surfactant is 0.05 mol/L to 20 mol/L; wherein deionized water can be added to prepare the Y, Re alcohol aqueous solution; andS23, stirring the Y, Re alcohol aqueous solution in a water bath of 40° C. to 60° C. for 4 to 6 hours, and placing the Y, Re alcohol aqueous solution in a 60° C. to 90° C. oven and aging for 56 to 90 hours to obtain the Y, Re colloid containing metal nano-particle M or ion M.

7. The preparation method of the yttrium oxide phosphor mixture according to claim 6, wherein the raw materials of Y and Re are metal oxides, hydrochloric acid salts, nitrates, or oxalates; the raw material of M is Ag, Au, Pt and Pd in the form of nano-particle;the raw material of M is aqueous or alcohol solution of AgNO3, HAuCl4, H2PtCl6, H2PdCl4;the complexing agent is citric acid; andthe surfactant is selected from at least one of the group consisting of polyethylene glycol 6000, polyethylene glycol 8000, polyethylene glycol 10000 and polyethylene glycol 20000.

8. The preparation method of the yttrium oxide phosphor mixture according to claim 7, wherein the metal oxides are Y2O3, Eu2O3, Tb4O7; the hydrochloric acid salts are YCl3.7H2O, EuCl3, TbCl3.6H2O;the nitrates are Y(NO3)3.6H2O, Eu(NO3)3.6H2O, Tb(NO3)3.6H2O.

9. The preparation method of the yttrium oxide phosphor mixture according to claim 7, wherein during the preparation of the Y, Re aqueous solution, if the hydrochloric acid salts or the nitrates are used as the raw materials of Y and/or Re, the raw materials of Y and/or Re are dissolved in a vessel directly; If the metal oxides or the oxalates are used as the raw materials of Y and/or Re, the metal oxides or the oxalates corresponding to the Y, Re are dissolved in a vessel with hydrochloric acid or nitric acid under a condition of 15° C. to 100° C. with stirring.

10. The preparation method of the yttrium oxide phosphor mixture according to claim 3, wherein in step S3, the ratio of the sum of molar amount of Zn and Al to the sum of molar amount of Re and Y in the mixture colloid is in a range of 0.01:1 to 2:1; the temperature of water bath is 15° C. to 80° C., the stirring time is 1 to 4 hours;the aging is placing the mixture colloid in a 100° C. to 200° C. oven for 48 to 96 hours; andthe heat treating is placing the mixture colloid in a crucible at 800° C. to 1300° C. for 0.5 to 6 hours under an air atmosphere or a reducing atmosphere.