Claims
- 1. A process for preparing particles of Zeolite L of improved mechanical strength comprising:
- (a) providing binderless preformed particles of Zeolite L, said particles prepared by reacting silica-bound particles containing preformed Zeolite L crystallites present in said silica-bound particles at a level of up to 95 wt % with an alkaline solution containing a source of alumina to convert the silica binder to Zeolite L; and
- (b) reacting said binderless preformed particles with an aqueous alkaline solution containing a source of alkali metal, at least 50 mole % of which alkali metal is potassium, and aluminum present in said solution at a molar ratio of aluminum, expressed as Al.sub.2 O.sub.3, to water of at least 0.0015.
- 2. The process of claim 1 wherein said Zeolite L crystallites present in said silica-bound particles of step (a) are in the form of cylinders with a mean diameter of at least 0.05 micron.
- 3. The process of claim 1 wherein said binderless preformed Zeolite L particles are in the form of tablets or extrudates.
- 4. The process of claim 1 wherein the alkali metal present in said aqueous alkaline solution of step (b) consists of potassium.
- 5. The process of claim 1 wherein the Zeolite L of step (a) is an aluminosilicate having the following formula, expressed as molar ratios of the constituent oxides in anhydrous form: (0.9-1.3)M.sub.2/n :Al.sub.2 O.sub.3 :XSiO.sub.2, wherein M is a cation of valence n and X=4 to 7.5.
- 6. The process of claim 1 wherein said aqueous alkaline solution of step (b) has an alkalinity, expressed as K.sub.2 O/H.sub.2 O molar ratio, of from 0.007 to 0.028.
- 7. The process of claim 1 wherein said alkalinity is from 0.011 to 0.022.
- 8. The process of claim 1, wherein said alkali metal present in said aqueous alkaline solution of step (b) comprises potassium and at least one other alkali metal, the molar ratio of potassium to said at least one other alkali metal, expressed as oxide K.sub.2 O/(M.sub.2 O+K.sub.2 O), being between 0.7 and 1.0, wherein M is said at least one other alkali metal.
- 9. The process of claim 1, wherein the molar ratio of aluminum, expressed as Al.sub.2 O.sub.3, to water present in said aqueous alkaline solution of step (b) is at least 0.002.
- 10. The process of claim 9 wherein said molar ratio is between 0.002 and 0.006.
- 11. The process of claim 1 wherein said binderless preformed particles consist of a plurality of individual zeolite L crystallites held together without the use of a non-zeolite binder.
- 12. The process of claim 1 wherein said reaction in step (b) is conducted at a temperature of from 100.degree. C. to 200.degree. C. for at least 12 hours.
- 13. The process of claim 12 wherein said reaction is conducted for 15 to 96 hours.
- 14. Particles of Zeolite L having improved mechanical strength prepared by the process of claim 1.
- 15. A catalyst comprising a catalytically active metal and the Zeolite L particles of claim 14.
- 16. The catalyst of claim 15 wherein sid catalytically active metal is selected from the group consisting of platinum and palladium, and comprises an amount of 0.1 to 6.0 wt. % of said catalyst, based on the total weight of said catalyst.
- 17. The catalyst of claim 16 wherein said catalytically active metal comprises an amount of 0.1 to 1.5 wt. % of said catalyst, based on the total weight of said catalyst.
- 18. The catalyst of claim 17 wherein said zeolite L is in the potassium form and said catalytically active metal is platinum comprising an amount of 0.4 to 1.2 wt. % of said catalyst, based on the total weight of said catalyst.
Priority Claims (1)
Number |
Date |
Country |
Kind |
8801067 |
Jan 1988 |
GBX |
|
Parent Case Info
This application is a Divisional of application Ser. No. 08/168,970, filed Dec. 16, 1993, which is a continuation of Ser. No. 07/600,281, filed Oct. 17, 1990, now abandoned, which is a continuation of Ser. No. 07/517,959, filed Apr. 30, 1990, now abandoned, which is a continuation of Ser. No. 07/297,456, filed Jan. 13, 1989, also abandoned.
US Referenced Citations (24)
Foreign Referenced Citations (33)
Number |
Date |
Country |
888365 |
Jul 1981 |
BEX |
40119 |
Nov 1981 |
EPX |
96479 |
Dec 1983 |
EPX |
109199 |
May 1984 |
EPX |
107389 |
May 1984 |
EPX |
142355 |
May 1985 |
EPX |
142347 |
May 1985 |
EPX |
142349 |
May 1985 |
EPX |
142354 |
May 1985 |
EPX |
142351 |
May 1985 |
EPX |
142353 |
May 1985 |
EPX |
145289 |
Jun 1985 |
EPX |
16775 |
Jan 1986 |
EPX |
184451 |
Jun 1986 |
EPX |
184450 |
Jun 1986 |
EPX |
185519 |
Jun 1986 |
EPX |
201856 |
Nov 1986 |
EPX |
284206 |
Sep 1988 |
EPX |
548567 |
Apr 1977 |
SUX |
1316311 |
May 1973 |
GBX |
2004764 |
Apr 1979 |
GBX |
1600927 |
Oct 1981 |
GBX |
2106483 |
Apr 1983 |
GBX |
2109359 |
Jun 1983 |
GBX |
2114150 |
Aug 1983 |
GBX |
2116450 |
Sep 1983 |
GBX |
2121427 |
Dec 1983 |
GBX |
2160517 |
Dec 1984 |
GBX |
2142648 |
Jan 1985 |
GBX |
2153840 |
Aug 1985 |
GBX |
2153384 |
Aug 1985 |
GBX |
2166972 |
May 1986 |
GBX |
8704365 |
Jul 1987 |
WOX |
Divisions (1)
|
Number |
Date |
Country |
Parent |
168970 |
Dec 1993 |
|
Continuations (3)
|
Number |
Date |
Country |
Parent |
600281 |
Oct 1990 |
|
Parent |
517959 |
Apr 1990 |
|
Parent |
297456 |
Jan 1989 |
|