The present disclosure relates to a zinc-based alloy coating and methods of improving cathodic protection and weldability to a metal surface. In particular, the zinc-based alloy coating and method are useful in providing cathodic protection to a press-hardenable steel (PHS) surface and reducing or eliminating liquid embrittlement susceptibility during or after welding for non-PHS ultra high-strength steels.
Since the early 2000's, the usage of PHS in the manufacture of lightweight vehicles has significantly increased. A great advantage of the press-hardening technology (also referred to as “hot stamping” or “hot press forming”) is its ability to produce complicated structural components with ultrahigh strength while avoiding issues caused by cold forming high-strength steels, such as increased springback and dimensional inaccuracy. There are two press-hardening methods: the direct press-hardening method and the indirect press-hardening method. In the direct press-hardening process, a blank of PHS is austenitized at a temperature above 850° C. for 3-10 min, and subsequently pressed and quenched at a rapid cooling rate (>25° C./s) to attain martensitic transformation. The indirect process includes a cold preforming step prior to the austenitization treatment. This preforming step reduces the amount of high temperature deformation, thus mitigating the cracking problem.
Current requirements for PHS are that its surface coating be able to prevent the steel from oxidation and decarburization during hot stamping/hot press forming, and able to provide press-hardened parts with corrosion protection in service. Various coatings and coating systems have been developed for PHS applications to meet these requirements. Of these coatings, an aluminum or aluminized coating is used, which consists of either pure aluminum (Type II) or aluminum with 7 wt. %-10 wt. % Si (Type I). However, such aluminized coatings are only able to provide a steel substrate with barrier protection. A shortcoming of this type of protection is that once the barrier coating is damaged or develops pores, the exposed areas of the steel substrate could be attacked with no further protection. After hot stamping/hot press forming, coating cracks and break-offs are often observed in such aluminized coatings due to the coating brittleness. Weldability and paintability of aluminized coatings are also generally poor after hot stamping/hot press forming.
Galvanized (GI) and galvannealed (GA) coatings have long been an excellent corrosion protection choice for automotive steel parts. These zinc-based coatings are able to offer cathodic protection to the steel substrate, thus possessing a great advantage in cut-edge protection. Moreover, conventional GI and GA coatings that are produced on continuous galvanizing lines (CGL) can readily retain the capability of cathodic protection even after experiencing a high temperature stamping process, however, zinc-coated PHS is generally limited to the indirect press-hardening or high temperature stamping process that is more time-consuming and requires additional equipment, thus increasing costs.
Thus, there remains a technical challenge of a direct-hardening process for zinc-coated PHS. The technical challenge with the direct-hardening process for zinc-coated PHS is twofold: zinc evaporation and micro-cracking. Since PHS blanks must be heated to an austenitization temperature above or close to the boiling temperature of zinc (906° C.) prior to stamping, zinc evaporation during hot stamping/hot press forming occurs. To suppress this zinc evaporation, one conventional approach is to apply a barrier layer onto the top of the zinc-based coating. The barrier layers can include silicone resin film (Japanese Patent Publication 2007-06378), zinc oxide (U.S. Pat. No. 7,673,485B2) and hexavalent chromium-containing overlay (US 2012/018437A1), for example. Applying a barrier layer onto a zinc-based coating results in a significant increase in cost and possibly gaseous hazards generated from the barrier layer during the hot-stamping process.
Another approach to curbing zinc evaporation is alloying the zinc coating with oxygen-affine elements. U.S. Pat. No. 8,021,497B2 relates to a method for producing a hardened steel part having cathodic corrosion protection. As per the patent, the cathodic protection is enabled by a zinc-based coating which is produced through a continuous coating process, either hot-dip galvanizing or an electrolytic process, with additions of one or more oxygen-affine elements including Mg, Si, Ti, Ca, Al and/or Mn in a total quantity of 0.1 wt. % to 15 wt. %. The purpose of adding one or more oxygen-affine elements is to form surface oxide, thereby suppressing zinc evaporation. However, it should be pointed out that the addition of Al to the zinc bath (typically ranging from 0.11 wt. % to 0.25 wt. %) is a common practice in continuous galvanizing production. During the hot dipping, the bath Al reacts with the steel strip to form a thin Fe2Al5Znx intermetallic layer. This intermetallic layer restrains the development of a brittle Fe—Zn intermetallic, thus enhancing coating adherence and formability. As a result, there is always a small amount of Al in conventional GI or GA coatings. During the hot stamping/hot press forming of a galvanized or galvannealed PHS, the Al in the coating would be oxidized into Al2O3 which acts as a protective layer to suppress zinc evaporation.
Manganese is another oxygen-affine element listed in U.S. Pat. No. 8,021,497B2, and it is also considered to play the same role as Al in suppressing zinc evaporation. In fact, manganese oxide is commonly present on the surfaces of press-hardened steel parts which have been previously galvanized or galvannealed (without any addition of Mn in the bath). Manganese comes from the press-hardenable steel substrate which typically contains 1.0 wt. %-1.5 wt. % Mn. During the austenitization treatment, Mn in the steel substrate diffuses into the zinc coating and is subsequently oxidized into manganese oxide which coexists with Al2O3 on the surface of hot press formed parts.
In addition to the above elements from the bath and/or from the steel substrate, part of the zinc in the coating is oxidized into ZnO which, along with aluminum oxide and manganese oxide, acts as a barrier to suppress zinc evaporation. In effect, a sufficient surface oxide layer is always formed on conventional GI/GA coatings as long as there is a sufficient amount of oxygen in the atmosphere.
Compared to zinc evaporation, micro-cracking is a far more severe issue that limits the practical application of galvanized coatings in the direct press-hardening of PHS. This issue results from so-called liquid metal induced embrittlement (LMIE) or liquid metal embrittlement (LME) (hereinafter LMIE and LME are used interchangeably), as is also observed in the welding of non-PHS and other grades of advanced high strength steel. It is generally understood that zinc coated steel after experiencing a high temperature stamping process or a press hardening process provides a coating that contains surface oxides (ZnO and Al2O3), a Γ phase (Zn—Fe intermetallic phase) and α(Fe, Zn) phase. The Γ phase contains about 70 wt. % Zn and transforms from a zinc-rich liquid phase. The α(Fe, Zn) phase typically contains 20 wt. % to 40 wt. % Zn. The resultant coating having zinc in these Γ and α(Fe, Zn) phases provides the cathodic protection to the steel substrate. The melting point of zinc is only about 420° C. During the austenitization treatment (>850° C.), the zinc-based coating inevitably becomes molten. Under stress-applied conditions (i.e. stamping conditions), the zinc-rich liquid promotes the formation and propagation of micro-cracks in the steel substrate, more likely along the grain boundaries of the steel. After being hot press formed, the zinc-rich liquid phase is present in the resultant coating as Γ phase which is readily distinguished from α(Fe, Zn) using conventional metallurgical techniques. However, the zinc-rich liquid (as Γ phase after solidification) formed in conventional GI and GA coatings during the austenitization treatment is most likely a main cause of LMIE, which promotes the inception and propagation of micro-cracks in the steel substrate. For example, a zinc-rich Γ phase was prevalent in the example coatings described in U.S. Pat. No. 8,021,497B2 as revealed in the images of the coating microstructures.
To overcome the cracking issue, one approach attempted was to minimize the portion of zinc-rich liquid in the resultant coating. Based on this approach, zinc is partially replaced with one or more alloying elements to result in a zinc alloy coating with a high solid-liquid transformation temperature (i.e. melting point). An example of such an approach is disclosed in U.S. Pat. No. 5,266,182 where a zinc alloy coating is provided containing at least 10 wt. % nickel (Ni). The Zn—Ni alloy coating is believed to consist mostly of a Γ-Zn21Ni5 phase. This intermetallic phase has a high melting point (880° C.) close to austenitization temperature so that the formation of liquid phase can be significantly reduced during the hot stamping/hot press forming. The introduction of that much nickel to a zinc bath greatly increases costs. A high nickel concentration also leads to the formation of a significant amount of dross at a typical galvanizing temperature, thus making it extremely difficult to produce the coating using the mainstream hot-dip galvanizing process.
Another approach to resolving the cracking issue is disclosed in US Patent Application 2014/0170438 A1 where a zinc alloy coating containing a very high concentration of manganese (Mn), for example at least 5 wt. % Mn, is provided. This patent application discloses that such a high amount of Mn addition in Zn would substantially increase the alloy melting point, thereby averting the issue of LMIE. However, due to the requirement for such high alloying additions of Mn, this coating can only be produced by an electrolytic process rather than by a continuous hot-dip process employing molten metals. Electrolytic coating production is generally more costly than continuous galvanizing production, and in addition, extra expense is incurred as a result of high alloying additions. For at least these reasons, the number of electro-galvanizing lines is fewer than that of CGL, thus limiting the production of these high alloy zinc coatings.
Another measure to reduce micro-cracking is to reduce the liquid phase by heat treating zinc-based coatings prior to hot stamping/hot press forming, which is essentially an indirect press-hardening or hot-stamping process. For example, US patent application 2014/0342181A1 discloses a method for producing zinc-coated steel strip for press-hardening applications, where prior to hot stamping/hot press forming, a galvannealed steel strip is heat treated at a temperature between 850° F. (454° C.) and 950° F. (510° C.) in a protective atmosphere (100% nitrogen (N2) or 95% N2 and 5% hydrogen (H2) to pre-alloy the coating. In a conventional CGL, however, there typically is no heating section available to subsequently (or in-line) heat treat the galvannealed steel strip in a protective atmosphere. Thus, this process would add considerable cost.
In one aspect of the present disclosure, a zinc bath composition is provided, the zinc bath composition comprising molten zinc, the molten zinc (Zn) comprising aluminum (Al) and manganese (Mn) or antimony (Sb), with no purposefully added iron.
In another object, alone or in combination with any one of the previous objects, the molten zinc comprises aluminum and manganese and formula (I) applies:
0.1+Mn (wt. %)/30≤Al≤0.3+Mn (wt. %)/20 (I).
In another object, alone or in combination with any one of the previous objects, the Mn and Sb are present, and formula (II) applies:
0.1+Mn (wt. %)/30+Sb (wt. %)/50≤Al≤0.3+Mn (wt. %)/20+Sb (wt. %)/50 (II).
In another object, alone or in combination with any one of the previous objects, Al is present at 0.12≤wt. % Al≤0.37 wt. %. In another object, alone or in combination with any one of the previous objects, Al is present at 0.19 wt. %≤Al≤0.37 wt. %. In another object, alone or in combination with any one of the previous objects, Al is present at 0.2≤wt. % Al≤0.37 wt. %. In another object, alone or in combination with any one of the previous objects, Mn is present at 0.30 wt. % to 1.2 wt. %. In another object, alone or in combination with any one of the previous objects, Sb is present at 0.30 wt. %≤Sb≤0.7 wt. %.
In another object of the present disclosure, a method of coating a substrate is provided, the method comprising the steps of: forming a bath comprising zinc and aluminum; the balance being at least one element selected from manganese and antimony; with no purposefully added iron; wherein when the molten zinc comprises aluminum (Al) and manganese (Mn) with the absence of antimony (Sb), formula (I) applies:
0.1+Mn (wt. %)/30≤Al≤0.3+Mn (wt. %)/20 (I); or
when Mn and Sb are both present, formula (II) applies:
0.1+Mn (wt. %)/30+Sb (wt. %)/50≤Al≤0.3+Mn (wt. %)/20+Sb (wt. %)/50 (II); and
providing a bath temperature of between 460° C. and 465° C.; introducing a substrate to the bath, the substrate entry temperature maintained at 5° C. to 20° C. lower than the bath temperature; and coating the substrate with a zinc coating comprising zinc and aluminum; the balance of the coating being at least one element selected from manganese and antimony. In one aspect, the bath comprises: 0.12 wt. %≤Al≤0.37 wt. %; and 0.2 wt. %≤Mn≤2.0 wt. %; and/or 0.2 wt. %≤Sb≤1.0 wt. %; no purposefully added iron; and the balance being Zn.
In one aspect of the present disclosure, the bath comprises: at least 0.19 wt. % up to 0.37 wt. % aluminum. In another object, alone or in combination with any one of the previous objects, Mn is present at 0.30 wt. % to 1.2 wt. %. In another object, alone or in combination with any one of the previous objects, Sb is present at 0.30 wt. %≤Sb≤0.7 wt. %.
In one aspect, the substrate to be coated is a boron-containing or a non-boron containing steel.
In another object, alone or in combination with any one of the previous objects, the substrate is pre-annealed prior to entry into the bath at a temperature between 500° C. and 900° C. for time between 5 seconds and 900 seconds and then cooled to a temperature of less than 485° C. In another object, alone or in combination with any one of the previous objects, the substrate is pre-annealed prior to entry into the bath at a temperature between 550° C. to 750° C. for a time between 10 seconds and 600 seconds. In another object, alone or in combination with any one of the previous objects, the substrate is pre-annealed in an atmosphere comprising N2 with a H2 content ranging from 5% to 30%.
In another object, alone or in combination with any one of the previous objects, the substrate is galvannealed at a temperature between 480° C. and 600° C. after removal from the bath. In another object, alone or in combination with any one of the previous objects, the substrate is galvannealed at a temperature between 520° C. and 580° C., with a holding time between 2 and 20 seconds. In another object, alone or in combination with any one of the previous objects, the substrate is galvannealed at a temperature between 520° C. and 580° C. with a holding time from 5 to 20 seconds.
In another object, a method of reducing or eliminating liquid metal induced embrittlement (LMIE) susceptibility of a steel during or after welding is provided, the method comprising contacting a steel sheet with the coating as described in any one of the previous objects, and reducing or eliminating LMIE susceptibility during or after welding. In one aspect, the steel sheet is: an advanced high strength steel (AHSS); transformation induced plasticity steel (TRIP); ultra-high strength steel containing retained austenite; medium carbon steel with or without added boron; or medium carbon, high manganese, high silicon steel. In another aspect, alone or in combination with any of the previous aspects, the method further comprises welding the steel sheet, and obtaining a weld nugget diameter size at or above the minimum nugget diameter size at a welding current that will produce the weld nugget size at or above the minimum nugget diameter size and with less than an expulsion current.
One objective of the present disclosure is to provide a solution to the technical problem of applying a zinc-based alloy coating to press-hardenable steel strip through a conventional continuous galvanizing line (CGL) without the detriment of increased cost, longer production time, or additional manufacturing steps that can be used in a direct press-hardening process at a high austenitization temperature, e.g., up to 950° C., and subsequently provide cathodic protection to the coated steel substrate.
The present disclosure provides a solution to this technical problem by providing a zinc-based alloy coating bath and method of coating for PHS where the Γ phase is reduced or eliminated in the resultant coating. Consequently, the effect of liquid metal induced embrittlement (LMIE), which is a main cause of micro-cracking in the press hardened steel parts, is averted or significantly reduced. In the presently disclosed process using the disclosed bath, zinc-rich liquid is minimized and thus, after being hot press formed, the GI and GA coatings, which can be produced on CGLs, can readily retain the capability of cathodic protection for the PHS substrate.
The press hardenable steel can be a complex phase steel, for example a dual phased PHS steel, a complex microstructure steel with fine complex precipitates, a TRIP steel, a PHS-ductile biphasic steel, and the like. Suitable steel substrates for the presently disclosed coating bath and coating method can be provided by using conventional steel casting, hot rolling, and cold rolling process techniques. For example, a continuous metal slab caster having a casting mold, such as but not limited to a compact strip production facility and introducing molten steel having a composition having elements within defined PHS ranges into the casting mold. The steel slabs can be hot rolled to form respective hot bands using hot rolling termination temperatures or finishing exit temperatures, for example ranging from (Ar3-20) ° C. to 1000° C. (1832° F.). Immediately after completing hot rolling, the hot rolled steel sheets can be water cooled at a conventional run-out table using cooling rates of at least 3° C./s (5.4° F./s) down to the coiling temperatures anywhere below 800° C. (about 1472° F.) ranging from 425° C. (797° F.) to 750° C. (1382° F.), and then can be coiled at the corresponding temperatures. After hot rolling and coiling, the hot bands can be pickled or otherwise surface treated to improve surface quality and then cold rolled to obtain a final thickness of the cold rolled steel sheet. Typically reduction is at least 25% up to 80% of the hot rolled steel sheet thickness. In one example, cold rolling can be performed so as to provide a cold rolled steel sheet of approximately 1.5 mm thickness. In another example, the cold rolling step can be performed at a conventional reversing cold mill using total cold reduction in a range between 30% and 70%.
In one aspect, a press-hardenable steel is used as the substrate. Exemplary press-hardenable steel useful in the current disclosure is a medium carbon, boron steel, such as some OEM automotive grade steels. For example, a medium carbon, boron steel comprising or consisting of 0.1-0.35 weight percent carbon, 1.0-2.5 weight percent manganese (Mn), 0.01-0.05 weight percent aluminum (Al), less than or equal to 0.5 weight percent silicon (Si) less than or equal to 0.5 weight percent chromium (Cr), 0.02-0.05 weight percent titanium (Ti), less than or equal to 0.1 weight percent niobium (Nb), less than or equal to 0.01 weight percent nitrogen (N), 0.0005-0.004 weight percent boron (B) and no purposefully added phosphorus and sulfur is used.
In another aspect, a medium carbon, non-boron, low manganese press hardenable steel can be used, for example, comprising or consisting of 0.17-0.25 weight percent carbon, 0.015-0.05 weight percent manganese, 0.015-0.05 weight percent aluminum, less than or equal to 0.06 weight percent titanium, less than or equal to 0.10 weight percent niobium (Nb) and no purposefully added boron, phosphorus, and sulfur is used.
In another aspect, a low carbon boron-containing press hardenable steel can be used, for example, comprising or consisting of 0.015-0.08 weight percent carbon, 0.025-0.045 weight percent manganese, 0.005-0.009 weight percent boron, with no purposefully added phosphorus and sulfur can be used.
Likewise, for reducing or eliminating liquid metal induced embrittlement susceptibility using the presently disclosed zinc alloy coating, a medium carbon, non-boron AHSS steel, comprising or consisting of 0.18-0.30 weight percent carbon, 1.5-3.0 weight percent manganese, 0.6-2.5 weight percent silicon, 0.015-2.0 weight percent aluminum, less than or equal to 0.15 weight percent titanium plus niobium (Ti+Nb), less than or equal to 1.2 weight percent chromium plus molybdenum (Cr+Mo), less than or equal to 0.2 weight percent copper (Cu) and no purposefully added phosphorus and sulfur can be used. Other examples of high-strength steels suitable for benefiting from reducing or eliminating the liquid metal induced embrittlement susceptibility are provided below.
In one example, a press hardenable steel useful in the current disclosure is a boron steel containing 0.20-0.25 weight percent carbon, 1.1-1.5 weight percent manganese (Mn), 0.02-0.06 weight percent Al, 0.02-0.05 weight percent titanium (Ti), 0.0005-0.0035 weight percent boron (B) as well as less than 0.5 weight percent silicon (Si) and 0.35 weight percent chromium (Cr). In another aspect, the press-hardenable steel useful in the current disclosure is absent intentionally added boron (e.g., recycled scrap steel) containing alloying additions such that PHS properties are obtained, as is known in the art.
To eliminate the Γ phase from the resultant coating on the PHS steel subsequent to hot stamping/hot press forming, hot forming, or press hardening (hereinafter collectively referred to as “press hardening”), the present disclosure controls bath chemistry and additional processing variables in the continuous galvanizing process. While it is likely that the presence of Γ phase benefits the cathodic protection due to its high zinc content (>60 wt. %), the presently disclosed bath and coating process nonetheless provides for the elimination or reduction of zinc-rich Γ phase in the resultant coating of zinc alloy coated PHS after being press hardened without loss of cathodic protection for the steel substrate.
In addition, the present bath and coating method minimizes the effect of LMIE while retaining the cathodic protection of the resultant coating for the steel substrate. The production of the presently disclosed zinc-based alloy coating can be readily incorporated in a conventional CGL. Exemplary conditions for a method of coating are provided under the following conditions.
In one exemplary aspect the zinc-based alloy coating is applied to a cold rolled steel strip through a continuous galvanizing line (CGL), however, other galvanizing processing techniques may be used. This zinc-based alloy coating is prepared under the following conditions, using a CGL as an exemplary processing embodiment, in order to minimize Γ phase (i.e. the liquid phase prior to solidification) in the resultant coating after the direct press-hardening process.
In the following description a cold rolled steel strip is used as the exemplary substrate, where the cold rolled steel sheet is prepared from casting to provide a hot rolled sheet, the hot rolling termination temperature or finishing exit temperature can be between (Ar3-30°) C. and 1000° C. (1832° F.) for example, followed by cooling after hot rolling at a mean cooling rate of at least about 3° C./s (5.4° F./s), for example, followed by coiling at a temperature below about 800° C. (about 1472° F.) down to ambient temperature. In one aspect, the coiling temperature is between about 425° C. (about 797° F.) and about 750° C. (about 1382° F.). The hot rolled sheet is subsequently cold rolled to the desired steel sheet thickness, with a cold reduction of at least 25%.
Other substrate forms can be used such as steel slab, hot rolled or cold rolled, wire, rebar and the like. The cold rolled steel strip can be hot dipped in the presently disclosed bath without being annealed. In one aspect, the steel sheet is annealed before hot-dipping using the following conditions. Any industrial annealing conditions are acceptable to carry out the present disclosure.
In one aspect, an annealing atmosphere consisting of 5% H2 and 95% N2 at a given dew point is used. Such a reducing environment is able to reduce iron oxide but inadequate to reduce the oxides formed from elements such as Al, Si and Mn that may be present in the steel substrate. For example, manganese is an alloying element that may be present in the press hardenable-steel substrate. During the annealing treatment, Mn present in the steel substrate or its surface is likely oxidized into MnO, which forms a thin film on the steel surface. As the MnO film cannot be reduced in the 5% H2 and 95% N2, annealing atmosphere, or other like annealing atmosphere, it stays on the steel strip during the hot-dipping. After the steel strip is galvanized, MnO residues remain at the steel/coating interface and may affect the surface quality of the galvanizing coating. During the austenitization stage of the hot-stamping process, the oxide can act as a barrier to restrain the diffusion between the iron in the steel substrate and the zinc in the coating.
A fast Fe—Zn diffusion is desired between the coating and the steel substrate so as to suppress zinc evaporation and to minimize the zinc liquid phase in the coating. In one aspect, the currently disclosed bath chemistry and coating method provides that the cold rolled steel strip is annealed through a heating cycle with a peak annealing temperature between 550° C. and 900° C. for between 5 seconds and 900 seconds. In another aspect, the cold rolled steel strip is annealed through a heating cycle with a peak annealing temperature between 550° C. and 750° C. for between 10 seconds and 600 seconds. At this annealing temperature range, the oxidation of alloying elements in the steel, such as Mn, Si and Al, would be significantly reduced or eliminated providing for improved diffusion between the substrate and the zinc coating.
The dew point is indicative of the oxygen partial pressure in the annealing atmosphere. A high dew point indicates a high oxygen partial pressure and vice versa. In a 5% H2—N2 atmosphere, a steel strip is typically annealed prior to hot dipping at a dew point of −30° C. (corresponding to an oxygen partial pressure of 5.6×10−24 atm) to avoid the oxidation of the steel iron. Increasing the dew point to some extent (e.g. from −30° C. to 0° C.) can keep the iron from oxidation while increasing the oxygen partial pressure. Advanced high strength steels, including PHS, typically containing high levels of oxidizing elements (e.g. Mn and Si) and if they are annealed at a high dew point (e.g. dew point of 0° C., corresponding to an oxygen partial pressure of 1.5×10−21 atm), internal oxidation occurs as there is a relatively high partial pressure, and oxygen is more likely driven into the steel and readily oxidizes alloying elements internally (i.e. under the steel surface). Internal oxidation provides improved coating adherence to the steel due to the lack of surface oxides and as a result, there is a benefit from the viewpoint of galvanizing. During the hot stamping/hot press forming of zinc-coated PHS, the absence of surface oxides is believed to reduce barriers to the diffusion between the steel iron and the coating zinc.
As a result, in one aspect, the current disclosure provides that a relatively high dew point in a range from −60° C. to 10° C. is employed for the annealing treatment of the press-hardenable steel strip prior to hot dipping so as to facilitate the subsequent Fe—Zn diffusion in the austenitization stage of the press hardening process. In another aspect, the current disclosure provides that a relatively high dew point in a range from −40° C. to 0° C. is employed for the annealing treatment of the press-hardenable steel strip.
In a continuous galvanizing process, the steel entry temperature (the steel temperature just before the steel strip is dipped into the bath) is typically maintained at a temperature approximately 1° C.-5° C. above the bath temperature. A higher steel entry temperature than that of the bath is generally understood to promote the Al—Fe reaction at the interface, thereby increasing the Al pickup and resulting in a well-established Fe2Al5Znx inhibition layer. However, for press-hardenable steels, a strong inhibition layer at the steel/coating interface is to be avoided in the presently disclosed method so as to maximize Fe—Zn diffusion during the hot-stamping process. Thus, in one aspect of the current disclosure, a bath chemistry and coating process of galvanizing press-hardenable steels provides for steel entry temperature that is maintained at a temperature approximately 5° C.-20° C. lower than the bath temperature. For example, if the bath temperature is 460° C., the steel entry temperature is provided in a range from 440° C. to 455° C.
For a galvanizing bath, an effective amount of aluminum (Al) (which is the amount of Al dissolved in the molten zinc bath) typically ranges from 0.15 wt. % to 0.25 wt. % so as to form a Fe2Al5Znx layer at the steel/coating interface. This interfacial layer plays a role in impeding the development of brittle Fe—Zn intermetallics—thus enhancing the coating adherence and formability. In one aspect of the presently disclosed method, an “inhibition” role of the press-hardenable steel substrate is substantially weakened to facilitate the Fe—Zn diffusion during the hot-stamping process. For press-hardenable steels, however, aluminum provides another role, e.g., the Al in the coating oxidizes into Al2O3 during the hot stamping/hot press forming, which acts as a protective layer on the surface of the resultant coating that suppress zinc evaporation.
A high bath Al level results in a coating with a high content of Al so as to promote the formation of Al2O3 during the hot-stamping process. However, there is an undesirable side effect resulting from a high bath Al level in a hot dipped zinc coating bath. The Al-rich inhibition layer would be overly developed at the steel/coating interface, making it difficult to break down during the hot stamping/hot press forming process. During the austenitization treatment, a fast diffusion of the zinc into the steel iron suppresses and/or competes with zinc evaporation and minimizes the liquid phase of zinc in the coating. If this Zn—Fe interaction is retarded by a strong interfacial layer, both zinc evaporation and the portion of liquid phase would consequently increase, which leads to undesirable effects.
The current disclosure overcomes this technical problem by providing the following technical solution. While the dissolved Al content in the presently disclosed bath is provided in a range from 0.12 wt. % to 0.50 wt. % Al so as to provide for the formation of sufficient Al2O3 during the hot-stamping process, nonetheless that amount of Al addition is such that the formation of a strong Al-rich inhibition layer at the substrate interface that would otherwise hinder the Fe—Zn diffusion is avoided or eliminated. To achieve this technical solution, the control of the bath Al wt. % alone is not sufficient. In the current disclosure, an amount of at least one element selected from Mn and antimony (Sb) is added to the bath in combination with the aforementioned dissolved Al content in the range from 0.12 wt. % to 0.50 wt. % Al with no purposefully added iron.
In one aspect, at least one element selected from Mn or Sb is used. When only one element is selected and that element is Mn, the following formula (I) applies:
[0.1+Mn (wt. %)/30]≤Al (wt. %)≤[0.3+Mn (wt. %)/20] (I).
When both Mn and Sb our employed in the bath, then formula (II) applies:
[0.1+Mn (wt. %)/30+Sb (wt. %)/50]≤Al (wt. %)≤[0.3+Mn (wt. %)/20+Sb (wt. %)/50] (II).
In one aspect, the total amount of Mn and/or Sb added to the bath is from about 0.2 wt. % to about 1.0 wt. %, and the dissolved Al content is in the range from 0.12 wt. % to 0.50 wt. % Al, the remainder being essentially zinc with no purposefully added iron.
In one aspect, the bath is from about 0.3 wt. % to about 1.0 wt. % total Mn and/or Sb, and the dissolved Al content is in the range from 0.12 wt. % to 0.50 wt. % Al, with no other purposefully added transition metals, the remainder being essentially zinc, and satisfying formula (I).
In another aspect, the bath is from about 0.3 wt. % to about 0.7 wt. % total Mn and/or Sb, and the dissolved Al content is in the range from 0.12 wt. % to 0.50 wt. %, the remainder being essentially zinc. In another aspect, the bath is from about 0.3 wt. % to about 0.7 wt. % total Mn and/or Sb, and the dissolved Al content is in the range from 0.12 wt. % to 0.50 wt. %, with no other purposefully added transition metals, the remainder being essentially zinc, and satisfying formula (I).
In another aspect, the bath is from about 0.5 wt. % to about 1.0 wt. % total Mn and/or Sb, and the dissolved Al content is in the range from 0.12 wt. % to 0.50 wt. %, the remainder being essentially zinc. In another aspect, the bath is from about 0.5 wt. % to about 1.0 wt. % total Mn and/or Sb, and the dissolved Al content is in the range from 0.12 wt. % to 0.50 wt. %, with no other purposefully added transition metals, the remainder being essentially zinc, and satisfying formula (I) or, if Sb is present, satisfying formula (II).
In another aspect, the bath is from about 0.5 wt. % up to 1.0 wt. % Mn and 0.3 wt. % up to 1.0 wt. % Sb, with the total wt. % of Mn+Sb≤1.0, and the dissolved Al content is in the range from 0.2 wt. % to 0.50 wt. % Al, the remainder being essentially zinc. In another aspect, the bath is from about 0.5 wt. % up to 1.0 wt. % Mn and 0.3 wt. % up to 1.0 wt. % Sb, with the total wt. % of Mn+Sb≤1.0, and the dissolved Al content is in the range from 0.2 wt. % to 0.50 wt. % Al, with no other purposefully added transition metals, the remainder being essentially zinc, and satisfying formula (II).
In another aspect, the bath is at least 0.5 wt. % up to about 1.0 wt. % Mn and the dissolved Al content is at least 0.2 wt. % up to 0.50 wt. %, the remainder being essentially zinc and satisfying formula (I). In another aspect, the bath is at least 0.5 wt. % up to about 1.0 wt. % Mn and the dissolved Al content is at least 0.2 wt. % up to 0.50 wt. %, with no other purposefully added transition metals, the remainder being essentially zinc and satisfying formula (I).
In one aspect, the bath is at least 0.2 wt. % to about 1.0 wt. % total Mn and/or Sb, and the dissolved Al content is in the range from 0.15 wt. % to 0.50 wt. % Al, with no other purposefully added transition metals, the remainder being essentially zinc and satisfying formula (I) and if Sb is present, satisfying formula (II). In another aspect, the bath is at least 0.2 wt. % to about 1.0 wt. % total Mn and/or Sb, and the dissolved Al content is at least 0.19 wt. % to 0.50 wt. % Al, with no other purposefully added transition metals, the remainder being essentially zinc and satisfying formula (I), and if Sb is present, satisfying formula (II). In another aspect, the bath is at least 0.2 wt. % to about 1.0 wt. % total Mn and/or Sb, and the dissolved Al content is at least 0.2 wt. % to 0.50 wt. % Al, with no other purposefully added transition metals, the remainder being essentially zinc and satisfying formula (I), and if Sb is present, satisfying formula (II).
In one aspect, the bath is at least 0.5 wt. % to about 0.7 wt. % total Mn and/or Sb, and the dissolved Al content is in the range from 0.15 wt. % to 0.50 wt. % Al, with no other purposefully added transition metals, the remainder being essentially zinc. In another aspect, the bath is at least 0.5 wt. % to about 0.7 wt. % total Mn and/or Sb, and the dissolved Al content is at least 0.19 wt. % to 0.50 wt. % Al, with no other purposefully added transition metals, the remainder being essentially zinc and satisfying formula (I), and if Sb is present, satisfying formula (II). In another aspect, the bath is at least 0.5 wt. % to about 0.7 wt. % total Mn and/or Sb, and the dissolved Al content is at least 0.2 wt. % to 0.50 wt. % Al, with no other purposefully added transition metals, the remainder being essentially zinc and satisfying formula (I), and if Sb is present, satisfying formula (II).
It has been disclosed that the addition of Mn in a galvanizing bath can shift the invariant point of (delta) δ (FeZn10)/(eta) η (Fe2Al5) in the Zn—Fe—Al ternary system to a higher Al level. With the addition of Mn in the presently disclosed bath, however, a higher than normal Al level is used to form a complete Fe2Al5Znx inhibition layer at the steel/coating interface. Alternatively, Sb can be employed so as to possibly interact with the bath Al, thus reducing the effectiveness of the Al-rich inhibition layer for the reasons stated above. The use of Mn and/or Sb additions in the presently disclosed bath is believed to ease the inhibition effect of the interfacial layer and facilitate Fe—Zn diffusion during the high temperature press hardening process. In addition, a small amount of Sb can be added (with or without Mn) to the galvanizing bath so as reduce the surface tension of molten zinc, thus improving the coating uniformity and smoothness of the PHS sheet.
To minimize the zinc-rich liquid phase in the resultant coating utilizing the presently disclosed method, it has heretofore been found to control the coating weight of the sheet in the CGL. Excessive zinc oxidation and a high portion of the zinc-liquid phase are more likely to result from a thick coating than from a thin coating. However, overly thin coatings may not be sufficient to withstand zinc evaporation and oxidation. In one aspect, the currently disclosed method targets a coating weight between 40 g/m2 and 120 g/m2. In another aspect, the currently disclosed method targets a coating weight between 60 g/m2 and 90 g/m2. These coating weights ensure that sufficient zinc for cathodic protection can be preserved in the resultant coating after the direct press-hardening process.
In one aspect, the coated steel sheet can be used immediately following the coating without pre-alloying or galvannealing. In another aspect, the coated steel sheet is galvannealed.
Typically, a conventional galvannealing (GA) process, the bath Al level is adjusted slightly lower than the bath Al level for a galvanizing (GI) process, e.g., between about 0.11 wt. % to about 0.14 wt. %, lower than the galvanizing bath Al level. The low Al level in the conventional GA bath is chosen to avoid formation of a complete Fe2Al5Znx inhibition layer to hinder the Fe—Zn diffusion. However, this low Al level is insufficient for PHS substrates and their use in subsequent press hardening applications.
Thus, to overcome this technical problem of the conventional methods, in one aspect of the current disclosure, the press-hardenable steel strip is reheated immediately following the hot dipping so as to promote the alloying process. In one aspect, the hot-dipped press hardenable steel strip is reheated using a high galvannealing temperature of between about 480° C. and about 600° C., with a holding time from 2 to 20 seconds to provide a pre-alloyed substrate. In another aspect, the hot-dipped press hardenable steel strip is reheated using a high galvannealing temperature of between about 520° C. and about 580° C., with a holding time from 5 to 10 seconds to provide a pre-alloyed substrate. Due to the Al content higher than 0.15 wt. % in the currently disclosed bath, the coating composition cannot be fully alloyed in a conventional galvannealing furnace and is referred to as a pre-alloyed coating. Compared to the unalloyed coating (i.e. galvanized coating), this pre-alloyed coating is more readily converted into zinc-containing α-Fe during the hot-stamping process, thus minimizing the zinc-rich liquid phase in the resultant coating. Thus, for at least one reason, the aforementioned combination of bath chemistry and processing conditions coordinate synergistically to provide a coating suitable for subsequent press hardening applications.
A steel or iron cast strand, for example, provided in a continuous metal slab caster can be used in the presently disclosed method. The cast strand, as shown by the arrow in
Alternately, the strand 28 may be directed to a cutting tool 38, such as but not limited to a shear, after the cast metal strand exits the withdrawal straightener 34 and is sufficiently solidified to be cut laterally (i.e., transverse to the direction of travel of the cast strand). As the strand 28 is cut into slabs, blooms, or billets, for example, the intermediate product may be transported away on rollers or other supports to be hot rolled.
During casting, water (or some other coolant) is circulated through the casting mold 20 to cool and solidify the surfaces of the cast strand 28 at the mold faces. The rollers of the withdrawal straightener 34 may also be sprayed with water, if desired, to further cool the cast strand 28. The resultant hot rolled steel may then processed through an annealing and hot dip coating system or galvanizing line.
In another embodiment, the hot rolled steel is cold rolled for use in the presently disclosed method. Thus, as shown in
With reference to
Zn baths were prepared using conventional methods. From a representative zinc bath of the present disclosure containing approximately 0.15 wt. % Al and 0.7 wt. % Mn, the top dross particles were taken for analysis. The analysis found that the top dross contained approximately 4.5 wt. % Al and 3.1 wt. % Mn. Medium carbon and non-boron containing steels were used, where medium carbon steels had the chemical composition (in weight percent): 0.170-0.250% C, 0.45-2.0% Mn, 0.015-0.05% Al, and absent intentionally added B, Ti, P, and S; and the low carbon and boron-containing steels had the chemical composition: 0.015-0.08% C, 0.20-1.0% Mn, 0.025-0.045% Al, 0.0005-0.0099% B and absent intentionally added P and S.
Galvanostatic Testing:
To evaluate the cathodic protection of the comparative and presently disclosed coatings, a galvanostatic test was performed to record the potential evolution of the coating versus test time at a fixed current density (12.7 mA/cm2). The potential evolution of the coating was then compared to that of bare PHS tested under the same condition. The galvanostatic testing was conducted in accordance with the procedure described in U.S. Pat. No. 8,021,497B2. An electrochemical cell with three electrodes, including working electrode (i.e., sample), reference electrode (saturated calomel electrode) and counter electrode (platinum mesh), was used for the testing. The electrolyte was made of deionized water with 100 g/L ZnSO4.5H2O and 200 g/L NaCl.
Comparative Example C1—Conventional GI coating: Press-hardenable steel sheet 100 was galvanized (GI) through a continuous galvanizing line (CGL) under conventional production conditions. The GI coating weight was approximately 70 g/m2. As shown in
Example 1 (According to the Present Disclosure): Prior to hot dipping, the press-hardenable steel sheet 100 was annealed in a N2-5% H2 atmosphere at a dew point of −40° C. through a heat cycle with a peak annealing temperature of 580° C. The steel entry temperature (prior to entering into the bath) was 450° C. The steel sheet was then galvanized according to the present invention. The GI coating weight was approximately 60 g/m2. Chemical analysis revealed that the content of bulk Al, Fe and Mn in the GI coating was 0.50 wt. %, 1.66 wt. % and 0.62 wt. %, respectively. However, the addition of manganese made it difficult to form a complete inhibition layer to prevent the formation of Zn—Fe intermetallic compound at the coating/steel interface. As shown in
Comparative example C2—Conventional GI coating: press hardened.
As shown in
Comparative Example C3—After press hardening process: Press-hardenable steel sheet 100 was galvanized with a conventional GI zinc coating under the same conditions as used for Comparative Example C1. The galvanized steel sheet was austenitized in air at 930° C. for 12 min prior to being press hardened as described above for C2.
Press-hardenable steel strip was hot dipped in a zinc bath containing 0.11 wt. % effective Al and then galvannealed (GA) on a CGL under conventional producing conditions. The original GA coating weight was about 80 g/m2. After being austenitized in air at 900° C. for 5 min, the galvannealed PHS sample was immediately press hardened as described above for C1.
Prior to hot dipping, the press-hardenable steel sheet was optionally annealed through a heat cycle in a N2-5% H2 atmosphere at a dew point of −40° C. The peak annealing temperature was 580° C. The steel sheet was then galvanized in a zinc bath with alloying additions as specified by Formula (I) in the present disclosure. After being austenitized in air at 930° C. for 5 min, the galvanized steel sheet with an original coating weight of about 90 g/m2 was immediately press hardened as described above for C2. As shown in
As shown in
The press-hardenable steel sheet was galvanized under the same conditions as used for Example 2, but the sheet was austenitized in air at 950° C. for 5 min prior to being press hardened as described above for C2.
Prior to hot dipping, the press-hardenable steel sheet was annealed in a N2-5% H2 atmosphere at a dew point of −40° C. through a heat cycle with a peak annealing temperature of 716° C. The steel sheet was then galvanized in a bath with alloying additions as specified by Formula (II) in the present disclosure. The original GI coating weight was 90 g/m2. Following an austenitization treatment in air at 950° C. for 5 min the galvanized steel sheet was immediately press hardened as described above for C2.
In this example, the press-hardenable steel sheet was annealed and hot dipped under the same conditions as in Example 4, but the hot-dipped steel sheet was subsequently galvannealed (GA) at 550° C. for 10 sec. The original GA coating weight was 120 g/m2. After being austenitized in air at 930° C. for 5 min, the galvannealed steel sheet was immediately press hardened as described above for C2. The resultant coating 79 consisted mainly of α(Fe, Zn) 71 and a layer of surface oxide, which was mostly peeled off after hot stamping/hot press forming The zinc content in the α(Fe, Zn) phase was determined to be 30%.
Press-hardenable steel sheet was galvanized under the same conditions as used for Example 1. The hot-dipped steel sheet was subsequently galvannealed (GA) at 520° C. for about 10 sec. The original GA coating weight was about 70 g/m2. After being austenitized in air at 930° C. for 6 min, the GA steel sheet was press hardened as described above for C2. As shown in
In this example, the steel sheet was galvanized in a zinc bath containing 0.11 wt. % Al and 0.64 wt. % Mn. This bath chemistry is outside the presently disclosed bath chemistry ranges, in accordance with Formula (I) (i.e. 0.1+Mn (wt. %)/30≤Al≤0.3+Mn (wt. %)/20). The coating produced from the Comparative Example C3 bath was overly thick with a coating weight of about 390 g/m2. The galvanized steel sheet of the Comparative Example C5 was austenitized in air at 920° C. for 5 min and was subsequently press hardened as described above for C2. Severe oxidation occurred on the press hardened part of the Comparative Example C5, resulting in the formation of excessive ZnO.
When the post press hardened coating consists mostly of α(Fe, Zn), the coating's potential is strongly affected by the zinc content in the α(Fe, Zn) phase. The coating's potential tends to be lower as the zinc content increases, thereby increasing the potential difference from bare PHS. To maximize the effectiveness of cathodic protection, a cathodic protection amount of zinc content in the α(Fe, Zn) phase is provided by the present composition and methods. In one aspect, the present disclosure provides for above 18 wt. %, above 19 wt. %, above 20% wt., above 21 wt. %, or above 22 wt. % of zinc content in the α(Fe, Zn) phase of the post press hardened coating to provide an effective amount of cathodic protection. In another aspect, the present disclosure provides for above 20 wt. % of zinc content in the α(Fe, Zn) phase of the post press hardened coating to provide an effective amount of cathodic protection
The term “about”, unless otherwise defined herein, is intended to include an upper and lower range of 10% of the stated value. Thus, “about 100,” for example, would include a range of 90 to 110 inclusive of the endpoints.
Micro-cracking from LME is a severe issue that limits the practical application of galvanized and galvannealed coatings in not only the direct press-hardening of PHS as discussed above. A primary phenomenon that has impeded the development of an acceptable welding strategy for a multitude of advanced high-strength steels (AHSS), including zinc-coated non-press-hardening steel, such as advanced high strength steel (AHSS); transformation induced plasticity steel (TRIP); TRIP bainitic ferrite (TBF) steel; ultra-high strength steel containing retained austenite; medium carbon steel with or without added boron; medium carbon, high manganese, high silicon steel; or quenching and partitioning (Q&P) processed AHSS; is liquid metal induced embrittlement within resistance spot welds of such steels. It is generally understood that zinc coated steel, after experiencing a high temperature welding process, leads to LME susceptibility, where the zinc-rich liquid of the coating promotes the formation and propagation of micro-cracks at the weld, heat affected zone, as well as the steel substrate during or after resistance spot welding of conventional GI and GA coatings. The presently disclosed zinc alloy coating, however, reduces or eliminates LME (reduces or eliminates LME susceptibility) during and after welding of a variety of grades of steel, due at least in part to the presence of at least manganese in the zinc alloy bath chemistry.
Thus a method of reducing or eliminating liquid metal induced embrittlement (LMIE) susceptibility of a steel during or after welding is provided. The method comprising contacting a steel sheet with the zinc alloy coating as described herein, and reducing or eliminating LMIE susceptibility during or after welding. Reducing or eliminating the liquid metal embrittlement susceptibility was determined for various samples of GI and GA grades of steel, including, steels containing retained austenite with a tensile strength higher than 780 MPa, higher than 900 MPa, higher than 1000 MPa, higher than 1180 MPa, as well steels with a tensile strength of around 2000 MPa.
For example, a steel sheet containing retained austenite with a thickness of about 1.2 mm and a tensile strength of higher than 1180 MPa was subjected to resistance spot welding using a current range of 6-12 kA, electrode diameter of about 4-10 mm, a weld force of approximately 2.0-6.0 kN, a weld time of between 100 to about 500 milliseconds (ms) and a hold time of between 60 to about 300 ms using a Rexroth welding controller C-clamp electrode gun. Under such conditions, a weld nugget diameter size (mm) at or above a minimum nugget diameter size (defined as: dm=4×(sheet thickness)1/2) at a welding current that produces a weld nugget diameter size at or above the minimum nugget diameter size with less than an expulsion current (a current at which expulsion occurs in the weld) is obtained.
Welded samples (GI and GA) with the zinc alloy coating presently disclosed, were imaged with an INSIZE ISM-PM200SB digital microscope and with a Clemex CMT D optical microscope. All of the welded GI samples were free of cracks in the weld, heat affected zone, and the base metal substrate indicating reduction and/or total elimination of LME susceptibility as a result of being coated with the presently disclosed zinc alloy coating. Only one weld (with expulsion occurred) of many welded GI samples showed a slight evidence of one single LME micro-crack. Thus, the presently disclosed zinc alloy coating provides reduction or elimination of liquid metal induced embrittlement susceptibility across a variety of grades of GI or GA steel, such as advanced high strength steel (AHSS), transformation induced plasticity steel (TRIP), TRIP bainitic ferrite (TBF) steel; ultra-high strength steel containing retained austenite, medium carbon steel (with or without added boron), medium carbon, high manganese, high silicon steel, or quenching and partitioning (Q&P) processed AHSS.
Although the present disclosure has been shown and described in detail with regard to only a few exemplary embodiments of the disclosure, it should be understood by those skilled in the art that it is not intended to limit the disclosure to specific embodiments disclosed. Various modifications, omissions, and additions may be made to the disclosed embodiments without materially departing from the novel teachings and advantages of the disclosure, particularly in light of the foregoing teachings. Accordingly, it is intended to cover all such modifications, omissions, additions, and equivalents as may be included within the scope of the disclosure as defined by the following claims.
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/US19/20154 | 2/28/2019 | WO | 00 |
Number | Date | Country | |
---|---|---|---|
62637102 | Mar 2018 | US |