Press hardened steels are typically high strength and have been used in automotive applications for reducing weight while improving safety performance. Hot stamped parts have mainly been made from either bare steel, which must have the oxide removed after stamping, or from steel with an aluminized coating. The aluminized coating provides a barrier form of corrosion protection. A zinc-based coating further provides hot stamped parts with active, or cathodic corrosion protection. For instance, hot dip galvanized steel typically includes a Zn—Al coating and hot dip galvannealed steel typically includes a Zn—Fe—Al coating. Due to the melting temperature of zinc, liquid zinc can be present during the hot stamping process and lead to cracking due to liquid metal embrittlement (LME). Time at the high temperature required for austenitization of the steel substrate prior to hot stamping allows for diffusion of iron into the galvannealed coating to avoid LME. However, during the time required to allow for sufficient iron diffusion, zinc in the coating can be lost due to vaporization and oxidation. This oxide may also exhibit poor adhesion and tend to flake off during stamping.
Disclosed herein is a pre-alloying heat treatment performed after galvannealing and prior to the hot stamping austenitization step. The pre-alloying allows for shorter time at the austenitization temperature to form a desired α-Fe phase in the coating by increasing the concentration of iron. This also decreases the loss of zinc, and a more adherent oxide exists after hot stamping.
The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate embodiments, and together with the general description given above, and the detailed description of the embodiments given below, serve to explain the principles of the present disclosure.
mom
Press hardened steel can be formed from boron-containing steel, such as the 22MnB5 alloy. Such a 22MnB5 alloy typically comprises between about 0.20 and about 0.25 C, between about 1.0 and about 1.5 Mn, between about 0.1 and about 0.3 Si, between about 0.1 and about 0.2 Cr, and between about 0.0005 and about 0.005 B. As apparent to one with ordinary skill in the art in view of the teachings herein, other suitable alloys can be used. Other suitable alloys can include any suitable press hardenable alloys that include a sufficient hardenability to produce a desired combination of strength and ductility for hot stamping. For example, similar alloys typically used in automotive hot stamping applications can be used. The alloy is processed into a cold rolled steel strip by typical casting, hot rolling, pickling, and cold rolling processes.
The cold rolled steel strip is then hot dip galvannealed to produce a Zn—Fe—Al coating on the steel strip. The coating weight is typically in the range of about 40 to about 90 g/m2 per side. Temperatures of the galvannealing furnace range from about 900 to about 1200° F. (about 482 to about 649° C.) and result in Fe levels in the coating of about 5 to about 15 wt %. Aluminum levels in the zinc pot range from about 0.10 to about 0.20 wt %, with the analyzed Al level in the coating at typically double the amount in the pot. Other suitable methods for galvannealing the steel strip will be apparent to one with ordinary skill in the art in view of the teachings herein.
The steel strip possessing the galvannealed coating is then given a pre-alloying heat treatment designed to increase the Fe level in the coating to between about 15 and about 25 wt %. This heat treatment has a peak temperature of about 850 to about 950° F. (about 454 to about 510° C.) with a dwell time of about 1 to about 10 hours, such as about 2 to about 6 hours. The pre-alloying heat treatment can be conducted through an open coil annealing practice. The pre-alloying heat treatment can be further conducted in a protective atmosphere. Such a protective atmosphere can include a nitrogen atmosphere. In some versions, the nitrogen atmosphere includes about 100% N2. In other versions, the nitrogen atmosphere includes about 95% N2 and about 5% H2. Other suitable methods for providing a pre-alloying heat treatment will be apparent to one with ordinary skill in the art in view of the teachings herein.
Once the galvannealed steel strip has been given the pre-alloying heat treatment, the steel strip is subjected to a hot stamping austenitization step. Hot stamping is well known in the art. Temperatures are typically in the range of about 1616 to about 1742° F. (about 880 to about 950° C.). Because of the pre-alloying heat treatment, time required at this austenitization temperature may be decreased. For instance, the time at the austenitization temperature can be between about 2 and about 10 minutes, or between about 4 and about 6 minutes. This forms a single phase α-Fe in the coating with approximately 30% Zn. Other suitable hot stamping methods will be apparent to one with ordinary skill in the art in view of the teachings herein.
A galvannealed steel coil was produced using the processes described above. A 22MnB5 steel coil was used having a thickness of about 1.5 mm. The galvannealed coating weight was about 55 g/m2. In this example, small panels of the galvannealed steel were given pre-alloy heat treatments in a nitrogen atmosphere at about 900° F. A first panel was not given the pre-alloy heat treatment, i.e., the pre-alloy treatment was for 0 hours, or “as-coated.” A second panel was given the pre-alloy heat treatment for about 1 hour. A third panel was given the pre-alloy heat treatment for about 4 hours. The pre-alloyed panels were then austenitized at about 1650° F. for about 4 minutes and quenched between water cooled flat dies to simulate the hot stamping process.
The effect of the pre-alloying treatment was shown in glow discharge spectroscopy (GDS) scans, which show chemical composition through the thickness of the coating. The GDS scans after pre-alloying treatments for 0, 1, and 4 hours are shown in
Zinc oxide formed during the austenitization treatment can be prone to flaking during hot stamping due to poor adhesion to the coating. Performing the pre-alloying heat treatment prior to austenitization and hot stamping can result in a more adherent oxide resistant to flaking. To measure this effect, panels processed according to the conditions described above, with pre-alloying times of about 0, 1, and 4 hours, were phosphated and e-coated in a laboratory system. The coated panels were given a cross-hatch and tape-pull test to test adherence.
While the present disclosure has illustrated by description several embodiments and while the illustrative embodiments have been described in considerable detail, it is not the intention of the applicant to restrict or in any way limit the scope of the appended claims to such detail. Additional advantages and modifications may readily appear to those skilled in the art.
The present application hereby claims the benefit of the provisional patent application of the same title, U.S. Ser. No. 61/824,791, filed on May 17, 2013, the disclosure of which is hereby incorporated by reference in its entirety.