Patent Application
20130126784
The present invention relates to luminescent materials and preparation methods thereof. More particularly, the invention relates to green luminescent materials of zinc silicate doped with manganese ions containing metal particles and preparation methods thereof.
In recent years, field emission devices have attracted much attention due to the advantages, such as low operating voltage, low power consumption, no deflection coil, no X-ray radiation, radiation resistance and magnetic interference resistance, etc. By exciting the luminescent material using field emission cathode ray, field emission light source of high luminance and good color rendering properties can be obtained, which can be applied to professional lighting, display, instructions, general lighting and other fields.
Preparation of fluorescent powders of great performance is a key to prepare field emission devices of excellent performance. At present, fluorescent materials provided in field emission devices are commonly luminescent materials of traditional cathode-ray tube and projection television kinescope, such as sulfide series, oxide series and oxysulfide series fluorescent powders. For example, Xiong Liangming et al., CN Patent. No. 200410025310.5 discloses a method for preparing green powders of zinc silicate doped with manganese ions by means of low-temperature solid phase reaction. Mesoporous silica, zinc salt and manganese salt in the +2 valence state are provided and used as raw materials, weigh accurately mesoporous silica and disperse in alcoholic solutions of zinc salt and manganese salt in the +2 valence state, after drying, under the protection of neutral gas, calcine at 750° C. to 950° C. to prepare green powders of zinc silicate doped with manganese ions of high efficiency by means of solid phase reaction. The green powders of zinc silicate doped with manganese ions prepared by such method are good in color purity, but low in luminous efficiency.
The technical problem of the present invention to be solved is to provide green luminescent materials of zinc silicate doped with manganese ions containing metal particles with good stability and high luminous intensity, and to provide preparation methods thereof.
The technical solution to solve the technical problem of the present invention is: to provide green luminescent materials of zinc silicate doped with manganese ions containing metal particles, said green luminescent materials of zinc silicate doped with manganese ions containing metal particles have the formula of Zn2-xSiO4: Mnx, My; wherein M is metal, x is in a range of 0.001≦x≦0.1, y is in a range of 0.00001≦y≦0.01.
The luminescent materials of the present invention, said metal M is one of Ag, Au and Pt, x is in a range of 0.001≦x≦0.08, y is in a range of 0.00001≦y≦0.005.
And, preparation methods of green luminescent materials of zinc silicate doped with manganese ions containing metal particles, comprising:
step 1: preparing silica aerogel containing metal particles;
step 2: selecting source compound of zinc, source compound of manganese and silica aerogel containing metal particles obtained in step 1 according to stoichiometric ratios, mixing to form mixture, said stoichiometric ratios of the source compounds are according to the molar ratio of corresponding elements in Zn2-xSiO4: Mnx, My, where M is metal, x is in a range of 0.001≦x≦0.1, y is in a range of 0.00001≦y≦0.01;
step 3: sintering the mixture obtained in step 2 at constant temperature, cooling and grinding to obtain said green luminescent materials of zinc silicate doped with manganese ions containing metal particles.
In the present invention, said preparation method of silica aerogel containing metal particles in said step 1 comprises: firstly, dissolving weighed silica aerogel in ethanol solution containing corresponding compound of metal, stirring at 50° C. to 75° C. for 0.5 to 3 hours, then sonicating for 10 min, drying at 60° C. to 150° C., grinding the dried raw materials well, calcining at 600° C. to 1300° C. for 0.5 to 3 hours. Said metal particle is one of Ag, Au and Pt; said corresponding compound of Ag is silver nitrate, said corresponding compound of Au is HAuCl4, said corresponding compound of Pt is HPtCl4.
In said step 2, said source compound of zinc is one of zinc oxide, zinc nitrate, zinc acetate and zinc oxalate; said source compound of manganese is one of manganese oxide, manganese acetate, manganese carbonate and manganese oxalate.
In said step 3, the sintering temperature is in the range of 1000 to 1400° C., the time of sintering is in the range of 1 to 10 hours, the sintering is carried out at constant temperature in the air.
Compared to the prior art, due to the addition of metal element to green luminescent materials of zinc silicate doped with manganese ions containing metal particles of the present invention, under the excitation of cathode ray, surface plasma resonance effect occurs on the interface among metal and Zn2SiO4:Mn, which improves effectively the luminescence property of Zn2SiO4:Mn and increases the luminance of the luminescent materials of the present invention. In addition, the preparation method of the present invention is simple, easy to operate, low-cost, of which the calcination temperature is low.
Further description of the present invention will be illustrated, which combined with embodiments in the drawings:
Further description of the present invention will be illustrated, which combined with embodiments in the drawings, in order to make the purpose, the technical solution and the advantages clearer. While the present invention has been described with reference to particular embodiments, it will be understood that the embodiments are illustrative and that the invention scope is not so limited.
The present invention provides green luminescent materials of zinc silicate doped with manganese ions containing metal particles, said green luminescent materials of zinc silicate doped with manganese ions containing metal particles have the formula of Zn2-xSiO4: Mnx, My; wherein M is metal, x is in a range of 0.001≦x≦0.1, y is in a range of 0.00001≦y≦0.01.
The luminescent materials of the present invention, said metal M is one of noble metals Ag, Au and Pt; x is in a range of 0.001≦x≦0.08, y is in a range of 0.00001≦y≦0.005.
Referring to
Step S01: preparing silica aerogel containing metal particles, herein, the aperture of said silica aerogel is in the range of 20 to 100 nm, the porosity is in the range of 92% to 98%;
Step S02: selecting source compound of zinc, source compound of manganese and silica aerogel containing metal particles obtained in step S01 according to stoichiometric ratios, mixing well to form mixture, said stoichiometric ratios of the source compounds are according to the molar ratio of corresponding elements in Zn2-xSiO4: Mnx, My, where M is metal, x is in a range of 0.001≦x≦0.1, y is in a range of 0.00001≦y≦0.01;
Step S03: sintering the mixture obtained in step S02 at constant temperature in the air, cooling to room temperature, and grinding to obtain said green luminescent materials of zinc silicate doped with manganese ions containing metal particles.
In the present invention, said preparation method of silica aerogel containing metal particles in said step S01 comprises: firstly, dissolving weighed silica aerogel in ethanol solution containing corresponding compound of metal, stirring at 50° C. to 75° C. for 0.5 to 3 hours, then sonicating for 10 min, drying at 60° C. to 150° C., grinding the dried raw materials well, calcining at 600° C. to 1300° C. for 0.5 to 3 hours. Said metal particle is one of Ag, Au and Pt; said corresponding compound of Ag is silver nitrate, said corresponding compound of Au is HAuCl4, said corresponding compound of Pt is HPtCl4.
In said step S02, said source compound of zinc is one of zinc oxide, zinc nitrate, zinc acetate and zinc oxalate; said source compound of manganese is one of manganese oxide, manganese acetate, manganese carbonate and manganese oxalate.
In said step S03, the sintering temperature is in the range of 1000 to 1400° C., the time of sintering is in the range of 1 to 10 hours.
Compared to the prior art, due to the addition of metal element to green luminescent materials of zinc silicate doped with manganese ions containing metal particles of the present invention, under the excitation of cathode ray, surface plasma resonance effect occurs on the interface among metal and Zn2SiO4:Mn, which improves effectively the luminescence property of Zn2SiO4:Mn and increases the luminance of the luminescent materials of the present invention. In addition, the preparation method of the present invention is simple, easy to operate, low-cost, of which the calcination temperature is low.
Special embodiments are disclosed as follows to demonstrate preparation methods of green luminescent materials of zinc silicate doped with manganese ions containing metal particles and the performances of it.
Weighing 0.3 g of silica aerogel, dissolving in 10 mL of ethanol solution containing 0.5×10−5 mol/L chloroauric acid (HAuCl4), stirring at 50° C. for 3 h, then sonicating for 10 min Drying at 60° C., and grinding the dried samples well, pre-calcining at 600° C. for 4 h. Then, weighing 1.5144 g of zinc nitrate, 0.0005 g of manganese carbonate and 0.2404 g of silica aerogel containing gold (Au), mixing well. Calcining in the air at 1000° C. and keep the temperature constant for 10 h, then cooling down to room temperature, new green light-emitting material Zn1.999SiO4: Mn0.001, Au0.00001 is obtained. The luminescent material with good luminescence property and color purity can emit green light under the excitation of cathode ray.
Weighing 1.0 g of silica aerogel, dissolving in 30 mL of ethanol solution containing 5.43×10−4 mol/L AgNO3, stirring at 70° C. for 0.5 h, then sonicating for 10 min Drying at 150° C., and grinding the dried samples well, pre-calcining at 1000° C. for 0.5 h. Then, weighing 1.1904 g of zinc oxalate (ZnC2O4), 0.0343 g of manganese oxalate (MnC2O4) and 0.2404 g of silica aerogel containing Ag, mixing well. Calcining in the air at 1200° C. and keep the temperature constant for 6 h, then cooling down to room temperature, new green light-emitting material Zn1.94SiO4: Mn0.06, Ag0.001 is obtained. The luminescent material with good luminescence property and color purity can emit green light under the excitation of cathode ray.
Weighing 1.0 g of silica aerogel, dissolving in 30 mL of ethanol solution containing 2.72×10−3 mol/L HPtCl4, stirring at 70° C. for 0.5 h, then sonicating for 10 min Drying at 150° C., and grinding the dried samples well, pre-calcining at 1000° C. for 0.5 h. Then, weighing 1.4093 g of zinc acetate (Zn(CH3CO2)2), 0.0554 g of manganese acetate (Mn(CH3CO2)2) and 0.2404 g of silica aerogel containing Pt, mixing well. Calcining in the air at 1300° C. and keep the temperature constant for 4 h, then cooling down to room temperature, new green light-emitting material Zn1.92SiO4: Mn0.08, Pt0.005 is obtained. The luminescent material with good luminescence property and color purity can emit green light under the excitation of cathode ray.
Weighing 0.4 g of silica aerogel, dissolving in 15 mL of ethanol solution containing 3.13×10−4 mol/L AgNO3, stirring at 60° C. for 1.5 h, then sonicating for 10 min Drying at 70° C., and grinding the dried samples well, pre-calcining at 800° C. for 2 h. Then, weighing 0.6486 g of zinc oxide (ZnO), 0.0037 g of manganese carbonate (MnCO3) and 0.2404 g of calcined silica aerogel containing Ag, mixing well. Calcining in the air at 1250° C. and keep the temperature constant for 4 h, then cooling down to room temperature, new green light-emitting material Zn1.992SiO4: Mn0.0089, Ag0.0007 is obtained. The luminescent material with good luminescence property and color purity can emit green light under the excitation of cathode ray.
Weighing 1.0 g of silica aerogel, dissolving in 30 mL of ethanol solution containing 5.43×10−3 mol/L HAuCl4, stirring at 70° C. for 0.5 h, then sonicating for 10 min Drying at 150° C., and grinding the dried samples well, pre-calcining at 1400° C. for 1 h. Then, weighing 0.6186 g of zinc oxide (ZnO), 0.0284 g of manganese oxide (MnO) and 0.2404 g of silica aerogel containing Au, mixing well. Calcining in the air at 1200° C. and keep the temperature constant for 4 h, then cooling down to room temperature, new green light-emitting material Zn1.9SiO4: Mn0.1, Au0.01 is obtained. The luminescent material with good luminescence property and color purity can emit green light under the excitation of cathode ray.
While the present invention has been described with reference to particular embodiments, it will be understood that the embodiments are illustrative and that the invention scope is not so limited. Alternative embodiments of the present invention will become apparent to those having ordinary skill in the art to which the present invention pertains. Such alternate embodiments are considered to be encompassed within the spirit and scope of the present invention. Accordingly, the scope of the present invention is described by the appended claims and is supported by the foregoing description.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/CN2010/074775 | 6/30/2010 | WO | 00 | 12/10/2012 |