Zinc powders for use in electrochemical cells

Abstract

A zinc powder for use in a zinc anode, negative electrode or electrochemical cell including zinc metal or zinc alloy particles. The zinc particles have a narrow particle size distribution and a major portion of the zinc particles having a well controlled chemistry and specific shape, such as teardrop, strand teardrop, acicular or spherical thereby providing improved discharge characteristics and reduced gassing.

Description

FIELD OF THE INVENTION

[0002] The present invention relates to zinc alloy powder for use in electrochemical cells. In particular, the present invention relates to zinc powders which provide enhanced performance in alkaline and zinc-air cells. The present invention also relates to a method for manufacturing such zinc alloy powder.

BACKGROUND OF THE INVENTION

[0003] Primary alkaline cells are often used in applications where long lasting, high-energy output is needed, such as electronic portable devices and camera flashes. The alkaline cell technology has evolved significantly over the past 10 years or so. For instance, lower mercury and mercury-free cells were introduced in the 90's. Additionally, the high-rate performance of alkaline cells is consistently improving for both manganese dioxide cathodes and zinc anodes.

[0004] Secondary, or rechargeable, zinc alkaline cells can also be used in similar applications as well as zinc-air cells. Those negative zinc electrodes are often similar to the zinc anodes of primary alkaline cells.

[0005] Alkaline cells typically use, and derive their name from, an aqueous solution of an alkaline electrolyte such as potassium hydroxide. In their initial state these electrolytes are typically in a liquid form and, as the majority of commercially available off-the-shelf alkaline batteries are dry cells having an immobilised electrolyte, a gelling agent is typically added to the electrolyte during fabrication. Common gelling agents include carboxymethylcellulose, polyacrylic acid, sodium polyacrylate and salts. Trace amounts of other additives, such as anti-gassing agents including indium compounds or organics may in some cases be added to the electrolyte to inhibit the evolution of hydrogen gas, an unwanted by-product of the cell self-discharge process associated with the corrosion of the zinc.

[0006] A predominant source of anodes, or negative electrodes, for household varieties of alkaline cells is zinc alloy powders mixed with a gelled potassium hydroxide/zinc oxide/water electrolyte. Indeed, zinc has a number of attributes which favour its use in the fabrication of anodes for disposable batteries including: a readily available supply of raw materials; low toxicity and a suitable electro-negativity or position in the galvanic series. Additionally, zinc-alkaline dry-cells typically have a low self discharge rate, good leakage resistance, good low temperature performance, relatively high capacity and relatively high energy density.

[0007] Conventionally, the fabrication of battery-grade zinc alloy powder is carried out using the well known processes of gas atomisation or centrifugal atomisation, and as such these technologies are in current use by most zinc powder producers throughout the world. In gas or centrifugal atomisation a melt of zinc alloy is first prepared by melting metallic zinc and adding alloying elements to molten zinc, then atomising the melt and finally classifying the produced powders according to the size of particles produced and desired. In conventional air atomisation, for example, the molten zinc alloy is forced through a narrow nozzle at the output of which jets of air collide with the molten zinc alloy, thereby forming the zinc particles.

[0008] Typically, the size distribution of the particles produced by the atomisation process may be controlled to some degree in the gas atomisation process, (i) by adjusting the metal to air ratio and, (ii) by classifying the produced powder, typically using mesh screens or the like, to remove particles which are either too fine or too coarse.

[0009] Although the above conventional methods provide a means for fabricating powders from zinc, in order to render an alkaline cell with optimised operating characteristics, the zinc powder must be of high-purity metallic zinc, have precise zinc alloying, and a narrow particle size distribution.

[0010] One of the drawbacks of the conventional means of fabrication is that, although the zinc alloy powder produced displays acceptable properties and characteristics and is suitable for use in constructing the anodes of alkaline cells, the wide particle size distribution may require sorting of the particles. Another drawback is that difficulties in modifying and controlling particle shape limits the ability to achieve specific density and particle packing, and consequently to achieve improved alkaline cell performance.

[0011] Alternative atomisation technologies have been developed or studied to improve product performance. One of these techniques is impulse atomisation as disclosed in U.S. Pat. No. 5,609,919 issued to Yuan et al, which describes a method and apparatus for producing particles from molten metal, including zinc, by forcing the molten metal through small apertures by applying regular train of impulses to the molten metal in the direction of the apertures and of sufficient amplitude to impel the molten metal through the apertures.

SUMMARY OF THE INVENTION

[0012] The present invention addresses the above and other drawbacks by providing for a method for making a battery grade zinc powder, the method comprising the steps of: (a) providing a molten zinc metal or a molten zinc alloy; (b) subjecting the molten zinc metal or molten zinc alloy to impulse atomisation to produce a powder made up of solid particles of zinc metal or zinc alloy in the for of a battery grade zinc powder; and (c) recovering the battery grade zinc powder.

[0013] There is also provided a battery-grade zinc powder comprising zinc metal or zinc alloy particles, the zinc metal or zinc alloy particles having a particle size distribution where the log normal slope of the not classified material is less than 2. A major portion of the particles are teardrop, acicular or stranded, or spherical.

[0014] Additionally, there is provided:

[0015] a battery grade zinc powder comprising stranded particles fabricated from a zinc metal, the stranded particles having a tap density of at most about 3.2 g/cc, preferably at most about 2.8 g/cc;

[0016] a battery grade zinc powder comprising tear drop particles fabricated from a zinc metal, the tear drop particles having a tap density of at most about 3.6 g/cc;

[0017] a battery grade zinc powder comprising spherical particles fabricated from a zinc metal, the spherical particles having a tap density of at least about 4.1 0 g/cc;

[0018] a battery grade zinc powder comprising particles fabricated from a zinc alloy, the alloy consisting essentially of zinc, aluminum, bismuth and indium, the particles having a surface oxidation of less than about 0.10%, preferably less than 0.06%;

[0019] a battery grade zinc powder comprising particles fabricated from a zinc alloy, the alloy consisting essentially of zinc, bismuth and indium, the particles having a surface oxidation of less than about 0.20%;

[0020] a battery grade zinc powder comprising particles fabricated from a zinc alloy, the alloy consisting essentially of zinc, bismuth, indium and lead, the particles having a surface oxidation of less than 0.10%, preferably less than about 0.06%; and

[0021] a battery grade zinc powder comprising particles fabricated from a zinc alloy, the alloy comprising zinc and aluminum, the particles exhibiting an alkaline aluminum loss of less than about 20% when immersed in KOH electrolyte.

[0022] There is also provided an anode for an electrochemical cell comprising the battery grade zinc powder, the zinc powder being suspended in a fluid medium, such as a gelled KOH electrolyte.

[0023] Additionally, there is provided an electrochemical cell comprising a cathode, an anode comprising the battery grade zinc powder and a separator electrically separating the cathode from the anode. In a particular embodiment the cathode comprises manganese dioxide and the fluid medium is a gelled KOH electrolyte. It further comprises a current collector inserted into the anode.

[0024] Finally, there is provided a LR-06 electrochemical cell comprising a positive terminal fabricated from a conductive material, a manganese dioxide cathode in electrical contact with the positive terminal, an anode comprising a battery grade zinc powder, the zinc powder being suspended in a gelled KOH electrolyte, a separator electronically separating the cathode and the anode, and a current collector inserted into the anode. When a load of 1 ohm is placed between the positive terminal and the current collector a cut-off voltage of 1.0 volts is reached in a time of greater than about 34 minutes, preferably at least about 42 minutes. Alternatively, when a current of 1 ampere is drawn by a load placed between the positive terminal and the current collector, a cut-off voltage of 1.0 volts is reached in a time of greater than about 36 minutes, at least about 45 minutes.

BRIEF DESCRIPTION OF THE DRAWINGS

[0025] FIG. 1 is a cut-way perspective view of an “AA” (or LR-06) electrochemical cell in accordance with an illustrative embodiment of the present invention;

[0026] FIG. 2 is a schematic diagram of an assembly for fabricating zinc powders according to impulse atomisation;

[0027] FIG. 3 provides particle size distributions for a variety of zinc powders fabricated using both impulse atomisation and air atomisation;

[0028] FIG. 4 provides illustrative embodiments of enhanced particle shapes for zinc powders;

[0029] FIGS. 5A through 5D provide an electron microscope images of enhanced particle shapes for zinc powders;

[0030] FIG. 5E provides a comparative electron microscope image of the particle shapes of zinc powders formed by conventional air atomisation;

[0031] FIGS. 6A through 6C provide an illustrative comparison of aspect ratios between zinc alloy powders formed using impulse atomisation and conventional air atomisation;

[0032] FIG. 7 provides the discharge curves of LR-06 cells containing zinc strands where 67% of zinc constitute the anode versus LR-06 cells containing 67% conventional zinc powder under 1.0 ohm continuous discharge;

[0033] FIG. 8 provides the discharge curves of LR-06 cells containing zinc strands where 62% of zinc constitute the anode versus LR-06 cells containing 67% conventional zinc powder under 1.0 ohm continuous discharge;

[0034] FIG. 9 provides the discharge curves of LR-06 cells containing zinc strands where 67% and 62% of zinc constitute the anode versus LR-06 cells containing 67% conventional zinc powder under 1 ampere continuous discharge;

[0035] FIG. 10 provides the discharge curves of LR-06 cells containing zinc strands where 62% of zinc constitute the anode versus LR-06 cells containing 67% conventional zinc powder under 3.9 ohm continuous discharge.

[0036] FIG. 11 provides the discharge curves of LR-06 cells containing zinc strands where 67% of zinc constitute the anode versus LR-06 cells containing 67% conventional zinc powder under 1.0 ohm continuous discharge.

[0037] FIG. 12 provides the discharge curves of LR-06 cells containing zinc strands where 67% of zinc constitute the anode versus LR-06 cells containing 67% conventional zinc powder under 1 ampere continuous discharge.

DETAILED DESCRIPTION OF THE ILLUSTRATIVE EMBODIMENTS

[0038] Referring to FIG. 1 an illustrative embodiment of an electrochemical cell in accordance with an illustrative embodiment of the present invention will now be described. The electrochemical cell, generally referred to using the reference numeral 10, is comprised of a gelled zinc anode 12 separated from a Manganese dioxide cathode 14 by a paper separator 16. A casing 18 typically fabricated from a conductive material such as steel (or PVC with a conductive lining) encases the cathode 14 and acts as the cathode current collector. The casing 18 is in electrical contact with the positive cap 20. An anode current collector 22 fabricated from a highly conductive material such as copper is inserted into the a gelled zinc anode 12 from the end opposite to that of the positive cap 20. The anode current collector 22 is in electrical contact with the negative cap 24. A layer of insulating material 26 separates the cathode 14 and casing 18 from coming into contact with the negative cap 24. Additionally, air vents 28 are provided for to allow any hydrogen gas which may evolve due to the corrosion of zinc to escape. The gelled zinc anode 12 is comprised of zinc alloy powder suspended in a potassium hydroxide (KOH) electrolyte treated with a gelling agent.

[0039] As discussed above, impulse atomisation allows the atomisation of zinc and zinc alloys into zinc powders with unique physical characteristics including, for example, the shape of the particles and the particle size distribution. Other unique properties are directly associated with the above characteristics, for example a variety of particle packing and densities varying between 0.5 and 4.6 g/cc can be achieved. Therefore, zinc and zinc alloys powder produced using impulse atomisation lend themselves exceptionally well to the fabrication of anodes and negative electrodes for electrochemical cells.

[0040] Use of these powders as a component in the anodes or negative electrodes of electrochemical cells provides zinc electrodes with low gassing rate in alkaline media, and a significant service increase under a variety of operating conditions, notably during high-rate discharge.

[0041] Referring now to FIG. 2 there is disclosed an assembly for fabricating zinc powders according to a modified version of impulse atomisation generally referred to using the numeral 30. The assembly comprises a tundish 32 of molten zinc metal 34 into which is placed a plunger 36. The tundish 32 is manufactured from refractory or metal capable of withstanding the temperature of the molten zinc alloy. The upper end 38 of the piston is attached to a source of vibration 40. Application of the vibrations to the plunger 36 causes the lower end 42 of the plunger 36 to move relative to the tundish 32 and an atomising plate 44 attached to the bottom of the tundish 32. The molten zinc metal 34 flows freely between the lower end 42 of the plunger 36 and the atomising plate 44. Movement of the lower end 42 of the plunger 36 relative to the atomising plate 44 causes the molten zinc metal 34 to be forced through small orifices as in 45 in the atomising plate 44 thereby forming zinc droplets of molten zinc 46. The molten zinc droplets pass through a particle formation chamber 48 into a cooling chamber 50 where they are cooled in air or another gas, collected, classified and packaged.

[0042] Impulse atomisation allows the dimensions of the particles to be accurately controlled using the orifices 45 in the atomisation plate 44, the position of the plunger 36, the frequency and amplitude of the vibrations applied to the plunger 36 and the atmosphere of the formation chamber 48.

[0043] On one hand, the length of travel of the plunger 36 (i.e. the amplitude of the vibrations applied to the plunger 36) in large measure dictates the length of segments of molten zinc alloy which are ejected into the formation chamber 48.

[0044] On the other hand, selection of an appropriate shape for the orifices 46 also allows for the shape of the particles to be controlled. In the case of elongate segments produced through a round or similar convex polyhedral shaped opening, the elongate segment will be thread-like or acicular. In the case of elongate segments produced through a slit, the elongate segments will be laminar, forming sheets, flat or curved, whose smallest lateral dimension is the thickness of the segment. In the case of more complicated aperture shapes, such as a cross, the smallest lateral dimension will be the thickness of one of the arms of the cross, but the length of the fluid segment may also be several times the width of the arms of the cross.

[0045] Additionally, parameters such as rate of cooling can be varied to promote the solidification of the elongated segments of molten zinc alloy solidify prior to their breaking up into spherical droplets. The rate of cooling depends on the surface tension of the zinc alloy, heat transfer from the zinc alloy and the gas through which the zinc alloy passes. For example, an acicular segment will produce an acicular powder if solidified before break up occurs.

[0046] The dimensions of the particles which can be produced using impulse atomisation can typically vary between 10 μm and 10 mm and is dependent on a number of input control parameters. Referring to FIG. 3, the size distribution typically obeys that of a log normal distribution and the slope of the distribution is proportional to the width of the distribution. It is evident from FIG. 3 that the width of the particle size distribution for particles formed using impulse atomisation is significantly narrower than the particle size distribution for particles formed using conventional atomisation techniques.

[0047] Narrower particle size distribution means that a significantly smaller portion of the produced powders are very fine (for example −325 mesh or smaller) or coarse (for example +40 mesh or greater) which in turn significantly reduces or eliminates the need for screening. As a consequence the amount of powder which is discarded is reduced which in turn improves production yield.

[0048] Log-normal slope (σ) of un-classified conventional air atomised zinc powder is typically above 2, more closely 2.4. Un-classified zinc powder produced by impulse atomisation has typically narrow size distribution and a log-normal slope (σ) below 2 and typically below 1.6.

[0049] As stated above, typical parameters of the process are the frequency and the force applied to the plunger, the size of the aperture in the atomising plate, the distance between the plunger and the atomising plate and the atmospheric conditions in which the metal droplets are cooled and solidify. By individually varying these parameters different particle shapes, size distributions, and powder densities can be achieved. Table 1, for example, provides examples of typical ranges for these parameters. Table 2 provides examples of how variation in these parameters may affect the powders obtained.

TABLE 1
	Force	Plunger	Atomising
Frequency	Applied	Distance	Apertures	Atmospheric
(Hz)	(newtons)	(mm)	(μm)	Conditions
20 to 1000	44.5 to 400	1 to 7	40 to 500	100% Air
	(10 to 90 lbf)			100% Nitrogen
				(or any
				other inert gas)
				100% Oxygen
				0 to 20% Oxygen
				(the remaining
				being inert gas)

[0050]

TABLE 2
Parameters	Impulse Atomisation Conditions
Frequency (Hz)	40	110	80
Force applied (lbf)	133.5 (30 lbf)	267 (60 lbf)	245 (55 lbf)
Aperture size (μm)	100	150	150
Atmosphere	Air	Air	0.25% O2
Powder	Strand	Strand	Spherical
characteristics
Tap Density (g/cc)	2.4	3.03	4.2

[0051] Shapes which can be formed using the impulse atomisation technique include spherical 52 (FIG. 5A), oblong 54 (not shown), teardrop as in 56, 58 and 60 (FIGS. 5B and 5C) and strands 62 (FIG. 5D). As confirmed by the samples tabled in Table 3 hereinbelow, these shapes greatly effect the packing and densities of the resulting powder. This is distinct from the shape of particles formed using conventional air atomisation which, referring to the example in FIG. 5E, are typically of an irregular shape (bone shape).

[0052] The ability to more accurately control the characteristics of the powders provides a greater control over the performance characteristics of the resultant electrochemical cells as measured in terms of discharge rate, gassing, etc.. For example, impulse atomisation allows spherical powders to be obtained where the packing is optimal and the density is very high which in turn provides for an increased connectivity between the metallic particles. On the other hand, by adjusting the conditions under which the droplets of molten zinc metal are formed, impulse atomisation also allows powders comprised of strands (i.e. particles which are acicular, very elongated and having a high aspect ratio) of zinc to be formed. Packing of the strands is achieved by intertwining the strands. This type of intertwining gives rise to a low density powder, while strand-like particles greatly increase the connectivity between particles when compared to spherical particles. Finally, by once again adjusting the conditions under which the droplets of molten zinc metal are formed, it has now been found that teardrop shaped particles with a variety of well-controlled aspect ratios can be formed which provide a favourable combination of both high apparent density and high connectivity, thereby uniting the advantages of both spherical and stranded forms.

[0053] In order to determine the densities, a series of test samples were prepared using both impulse atomisation and a conventional air atomisation and the resulting samples tested in regard to their density. The results are Tabled in Table 3.

TABLE 3
		Apparent	Tap
		Density (g/cc)	Density (g/cc)
Atomisation		(ASTM	(ASTM
process	Shape	#B212-99)	#B527-93)
Impulse	Strand very high AR	N/A	0.63
atomisation	Strand high AR	N/A	1.42
	Strand	1.82	2.02
	Strand	1.98	2.37
	Strand	2.45	2.59
	Strand	2.76	3.02
	Tear drop tailing	3.20	3.27
	Tear drop tailing	3.55	3.18
	Spherical	4.10	4.17
	Spherical	4.16	4.3
Conventional	Irregular/Bone shape	3.03	3.40
air atomisation

[0054] Apparent density is a measure of the free packing of the powder and was measured according to ASTM #B212-99. The apparent density is measured using a hall flowmeter. Note that in order for the hall flowmeter to measure the apparent density the material must flow through an aperture at the lower end of a funnel which forms part of the flowmeter, which the high and very high aspect ratio (AR) strands are unable to do. Tap density, on the other hand, is related to the packed density of the powder and was measured according to ASTM #B527-93.

[0055] Referring now to FIG. 6A, some typical distributions of the aspect ratios of stranded zinc alloy powders produced using impulse atomisation are shown. It is apparent from the graph that some very high aspect ratios are attainable using impulse atomisation. Zinc alloy powders produced using conventional air atomisation, on the other hand, and as graphed in FIG. 6B, and generally spherical particles, as graphed in FIG. 6C, have a relatively small aspect ratio.

[0056] One other benefit of impulse atomisation is that oxidation of the surface is greatly decreased due to the absence of atomising air jets, the corresponding reduction of air-zinc interactions and by the greatly increased rate of cooling. A variety of zinc alloy powders were prepared using impulse atomisation and conventional air atomisation and the amount of surface oxidation measured. The results are tabled in Table 4.

	TABLE 4
	Alloy Chemistry (ppm)	ZnO
					ZnO	Ratio to
Atomization process	Al	Bi	In	Pb	(%)	Reference
Impulse atomisation	50	100	200		0.03	0.25
process (strand shaped)	70	100	200		0.04	0.33
	60	100	200		0.03	0.25
	75	100	200		0.02	0.17
Conventional air	100	100	200		0.12	1
atomisation
Impulse atomisation		300	300		0.08	0.15
process (strand shaped)		300	300		0.16	0.30
		300	300		0.09	0.17
Conventional air		300	300		0.54	1
atomisation
Impulse atomisation		500	500	500	0.06	0.43
process (strand shaped)
Conventional air		500	500	500	0.14	1
atomisation

[0057] Note that in the table above the amount of zinc oxide produced is expressed relative to the total amount of zinc atomised. Experimental results show that oxidation is reduced up to 85% relative to that produced during conventional air atomisation. Indeed, when using air atomisation experimental results reveal that a dispersed nano-crystalline surface zinc oxide is formed during the initial stages, immediately after the molten zinc metal is pulverised by the air jets into metal droplets. The kinetics of oxidation are in large part determined by the oxidising conditions occurring around the zinc droplets in the atomisation spray.

[0058] The effect of oxidation on melt droplets is easily observed during the manufacture of metal powders from zinc alloyed with aluminum, bismuth and indium (ABI). Experimentation reveals that a significant portion of aluminum is instantaneously dissolved when an ABI powder produced using conventional air atomisation is immersed in alkaline solutions, and this without any significant evolution of hydrogen gas. Typically, 50% of added aluminum is lost during alkaline immersion, but this loss may reach up to 75% for some alloys containing about 200 ppm of aluminum, or depending upon atomisation parameters such as high melt or atomising air temperature. The effective aluminum concentration in zinc particles is therefore much lower.

[0059] Zinc alloying with some aluminum improves gassing, especially gassing after partial discharge. This effect is associated with the presence of aluminum in a metallic form, the amount of which is reduced when aluminum is oxidised.

[0060] It is apparent that a strong force is acting on the aluminum, aluminum oxidation. Therefore it seems likely that aluminum is reacting and accumulating on the droplet surface as an oxide according to this mechanism:

[0061] Fast aluminum oxidation occurs near the surface of zinc alloy droplet immediately following formation;

[0062] aluminum diffuses from bulk to the droplet's surface prior to particle solidification; and

[0063] further aluminum oxidation occurs until solidification is completed.

[0064] A controlled oxidation rate of the zinc droplets is demonstrated by the absence of dispersed nano-crystalline surface ZnO and by a significant drop in alkaline aluminum loss from the ABI alloy.

[0065] A series of samples of zinc alloy containing aluminum were prepared and zinc alloy powders formed using impulse atomisation and conventional air atomisation techniques. The powders were then immersed in a KOH electrolyte and the remaining Al then measured. The results are tabled in Table 5.

	TABLE 5
	Aluminium Content (ppm)
Atomisation		Al Remaining After
process	Alloyed Al	Immersion in KOH	Aluminium Ratio
Impulse	125	119	95%
atomisation	59	51	86%
Conventional air	109	54	49%
atomisation

[0066] It is apparent from the above results that the amount of aluminum lost to oxidation can be significantly reduced through the use impulse atomisation. It therefore follows that the use of impulse atomisation can also reduce zinc powder gassing significantly. The decrease in gassing rate is intimately associated with the alloying components, the atomisation conditions, the control of oxidation and environment during particle formation and the cooling rate of the particles.

[0067] In order to analyse the effects of impulse atomisation on gassing a series of samples of zinc alloy were prepared. These alloys were then used to fabricate powders using both the impulse atomisation techniques and conventional air atomisation techniques. The powders were then dispersed in a gelled KOH electrolyte and the gassing measured. The results are tabled in Table 6.

	TABLE 6
	Anode Mix Gassing
	(μl/g-d)
	Fresh	Partially
	Alloy Chemistry (ppm)	Anode	Discharged
Atomisation process	Bi	In	Al	Pb	Mix	Anode Mix
Impulse atomisation	300	300			7.1	42
process	300	300			4.2	37
Typical air	300	300			10	105
atomisation
Impulse atomisation	100	200	100		1.4	41
process	100	200	100		5.6	32
Typical air	100	200	100		6.0	30
atomisation
Impulse atomisation	100				13.2	112
process
Typical air	100				138	197
atomisation
Impulse atomisation	500	500		500	9.6	20
process
Typical air	500	500		500	4.8	77
atomisation

[0068] Note that the unit μl/g-d indicates the amount of hydrogen gas generated in micro litres per gram of zinc evolving from the anode per day.

[0069] Additionally, the fresh anode mix gassing is a measure of the hydrogen gas produced by fresh zinc within the anode kept at 71° C. for 24 hours, whereas partially discharged anode mix gassing is a measure of the hydrogen gas evolving from the residual mixture within the anode once the fresh zinc has been partially discharged and subsequently kept at 71° C. for 24 hours.

[0070] It is apparent from the above results that the gassing rates of anodes, or negative electrodes, fabricated from powdered zinc and an alkaline electrolyte such as potassium hydroxide (KOH), zinc oxide (ZnO) and a gelling agent are significantly reduced through impulse atomisation. For example, fabrication of zinc alloy particles using impulse atomisation and zinc alloyed with either bismuth, bismuth-indium, bismuth-indium-aluminium, or bismuth-indium-lead provided for reduced gassing rates significantly over powders fabricated using conventional air atomisation techniques.

[0071] In order to test performance a series of LR-06 test cells and LR-06 reference cells were assembled. All test cells and reference cells were assembled using identical manganese dioxide cathodes, current collectors and casings.

[0072] Anodes fabricated with a zinc alloy powder comprised of 100% zinc strands revealed significantly improved performance characteristics. FIG. 7 shows under a sustained load of 1 ohm the discharge voltage remains significantly higher for batteries having anodes or negative electrodes constructed using zinc alloys powders fabricated using impulse atomisation relative to the reference cells having anodes constructed of powders formed using conventional air atomisation. This is of course a benefit, in that many devices which operate such load conditions will indicate that the power source is depleted if the voltage drops below a threshold value.

[0073] Additionally, anodes fabricated with a zinc alloy powder comprised of 100% zinc strands revealed significantly improved performance characteristics. For example, referring to FIG. 8, in comparative tests with reference batteries having anodes comprised of zinc powders fabricated using conventional air atomisation techniques, reduction of the amount of zinc by weight used to fabricate the anodes or negative electrodes of an alkaline cell from 67% to 62% was achieved while using a powder comprised of zinc strands fabricated using impulse atomisation. The high rate performance with a load of 1 ohm also improved up to 20% when compared with the reference batteries.

[0074] Furthermore, FIG. 9 shows that under high current drain conditions (i.e. a sustained current drain of 1 ampere) with varying amounts of zinc by weight in the cells (67% and 62%), the discharge voltage remains significantly higher for batteries having anodes or negative electrodes constructed using zinc alloy powders such as ABI fabricated according to impulse atomisation relative to the reference batteries.

[0075] Finally, reduction in the amount of zinc by weight in the anode of an alkaline battery by approximately 10% (from 67% to 62%) while using zinc strands having large aspect ratio fabricated using impulse atomisation revealed that, during low rate conditions (i.e. under a continuous load of 3.9 ohms), the capacity of the cell was increased by approximately 5% over that of the reference batteries having anodes comprised of 67% by weight conventional air atomised zinc powders. The results for a low rate discharge are provided in FIG. 10.

[0076] In order to test the actual discharge rates of zinc powder anodes, two LR-06 cells were assembled: the first LR-06 having an anode from zinc powder fabricated using conventional air atomisation; and the second having an anode from a stranded zinc powder fabricated using impulse atomisation. The LR-06 cells were otherwise the same using the same magnesium dioxide cathode, separator, current collector and casing. Additionally, the anode included a zinc powder suspended in a gelled electrolyte comprising 98% by weight of KOH 40%/ZnO 3% and 2% by weight of polyacrylic acid (Carbopol™ 940) as gelling agent.

[0077] In order to test cell performance under constant continuous load, a load of 1 ohm was placed between the positive and negative terminals of the cells and the fluctuation in cell voltage measured over time. The results are graphed in FIG. 11. Similarly, in order to test the cell performance under constant continuous current, a continuous current of 1 ampere was drawn from the cell. The results are graphed in FIG. 12.

[0078] It will now be apparent to one of ordinary skill in the art that electrochemical cells with anodes fabricated from stranded powders exhibit superior performance characteristics over those fabricated using conventional air atomised powders. In particular, the 1.0V cut-off, which is typically used as an indicator to the electronics being supplied by the cell that the cell is depleted, was increased to 42 minutes from 34 minutes under the 1.0 ohm load (see FIG. 11) and to 45 minutes from 36 minutes given load conditions drawing a continuous current of 1 ampere (see FIG. 12).

[0079] A melt of zinc alloy was prepared by melting electrolytic 99.995% zinc metal. Pure zinc and a variety of zinc alloys, including zinc-bismuth (B alloy), zinc-bismuth-indium (BI alloy), zinc-aluminum-bismuth-indium (ABI alloy), zinc-bismuth-indium-calcium (BIC alloy) and zinc-bismuth-indium-lead (BIP alloy) were prepared and then atomised using both conventional air-atomisation techniques and impulse atomisation. Following atomisation the zinc metal powders were classified and tested.

[0080] A series of LR-06 cells were fabricated from powders derived from both the impulse atomisation process and conventional air atomisation process. The zinc anodes were fabricated from a zinc powder blended with a gelled electrolyte. The gelled electrolyte comprised 98% by weight of KOH 40%/ZnO 3% and 2% by weight of polyacrylic acid (Carbopol™ 940) as gelling agent.

[0081] Two varieties of gelled anodes were fabricated, the first comprising 67% by weight zinc powder and 33% by weight gelled electrolyte and the second comprising 62% by weight zinc powder and 38% by weight gelled electrolyte. The control anode was fabricated from 67% by weight zinc powder and 33% by weight of gelled electrolyte. Once the mix of zinc and gelled electrolyte was homogeneous, the resulting paste was inserted in LR06 alkaline cell to form the anode. Referring back to FIG. 1, the manner in which those cells were constructed is shown.

[0082] The zinc alloy powders were characterised and evaluated in terms LR06-cell performance at different zinc loads and the results tabled in Table 7 and Table 8. Note that the D50 column indicates the value below which 50% of the particles of zinc alloy powder produced were found. D50 was measured according to ASTM #214-99. Tap density, on the other hand, as stated above in reference to Table 4, is related to the packed density of the powder and was measured according to ASTM #B527-93.

	TABLE 7
	Particle Characteristics
	PSD	Density
	Image Analysis	(ASTM	(ASTM
	Average	Average	Average	#214-99)	#B527-93)
	Aspect	Width	Length	D50	Tap
Powder	Ratio	(μm)	(μm)	(μm)	Density
Type 1	10	166	1605	530	3.1
Type 2	11	207	2060	340	2.8
Type 3	20	101	1771	360	2.5
Type 4	14	134	1625	355	3.1
Type 5	18	160	2053	405	2.7
Type 6	20	96	1622	315	2.3
Type 7	21	125	1925	340	2.4
Type 8	22	93	1508	280	2.4
Type 9	23	106	1900	420	2.3
Type 10	20	105	1880	290	2.4
Type 11	18	91	1446	300	2.6
Type 12	19	87	1471	320	2.6
Type 13	21	84	1545	400	2.3
Reference	2	151	292	150	3.4

[0083]

	TABLE 8
	LR06 to 1.0 V Cut-Off vs.
	Reference (%)
	1000 mA	1 ohm
	Alloy Chemistry (ppm)	62%	67%	62%	67%
	Bi	In	Al	Pb	Ca	Zn	Zn	Zn	Zn
TYPe 1	300	300				95	96	97	99
Type 2	300	300				103	100	91	101
Type 3	300	300				101	101	100	102
Type 4	300	300				101	104	96	96
Type 5	300	300				92	98	100	99
Type 6	300	300				107	113	107	114
Type 7	300	300				107	107	107	107
Type 8	300	300				121	120	106	110
Type 9	100	200	100			106	115	123	125
Type 10	100	200	100			122	115	128	126
Type 11	100					97	98	100	94
Type 12	500	500		500		88	90	96	100
Type 13	250	250			150	108	115	110	114
Refer-	100	200	100			100	100	100	100
ence

[0084] Additionally, improved performance characteristics may also be derived from mixtures of the above produced zinc alloy powders. A given mixture is comprised of two or more types of zinc powders made by impulse atomisation or by impulse atomisation and conventional techniques and having different particle shapes and/or particle sizes distributed around different mean particle sizes which are then combined to form a hybrid powder. By adjusting the powder mix in terms of both particle size and shape the performance characteristics of a given electrochemical cell can be optimised.

[0085] Referring now to Table 9, powder fabricated using impulse atomisation was mixed with fine air atomised powder or conventional air atomised powder and tests performed in LR06 cells under two different regimes. The fine air atomised powder has a particle size distribution were 100% of the particles are less than 75 μm and the conventional air atomised powder has a particle size distribution within 425 μm and 54 μm.

	TABLE 9
	Air Atomised Powder	LR06 to 1.0 V Cut-Off vs.
	Added	Reference
	Fine	Conventional			1 W
Powder	Powder	Powder	1.5 W	1 A	Intermittent
Type 6	—	—	109%	113%	109%
	20%	—	114%	103%
	50%	—	130%	107%
	—	20%		102%	100%
	—	50%		99%	97%
Type 10	—	—	109%	115%	115%
	20%	—	131%	109%
	50%	—	116%	98%
	—	20%		116%	119%
	—	50%		107%	118%
Reference	—	—	100%	100%	100%

[0086] Furthermore, improved performance characteristics may also be achieve from derived formulations of the anode mix varying the concentration of gelling agent for instance. A stranded zinc powder was mixed with an electrolyte comprising varying amounts of the polyacrylic gelling agent Carbopol™ 940. The results are tabled in Table 10.

	TABLE 10
	Chemistry		LR06 to 1.0 V Cut-Off vs.
	(ppm)	Carbopol ™	Reference
Powder	Bi	In	(%)	1 A
Type 7	300	300	0.60%	107%
			0.30%	106%
			0.15%	112%

[0087] Although the present invention has been described hereinabove by way of an illustrative embodiment thereof, this embodiment can be modified at will, within the scope of the present invention, without departing from the spirit and nature of the subject of the present invention.

Claims

1. A method of making a battery grade zinc powder, said method comprising: (a) providing a molten zinc metal or a molten zinc alloy; (b) subjecting said molten zinc metal or molten zinc alloy to impulse atomisation to produce a powder made up of solid particles of zinc metal or zinc alloy in the form of a battery grade zinc powder; and (c) recovering said battery grade zinc powder.

2. The method of claim 1 wherein in step (b) the impulse atomisation has a frequency of between 20 and 1000 Hz, a force applied to the plunger of between about 44.5 and 40 newtons, a plunger distance of between 1 to 7 mm and atomising apertures of between 40 and 500 μm.

3. The method of claim 2 wherein in step (b) said particles are cooled in an atmosphere comprising a gas selected from the group consisting of air, inert gas, oxygen and a mixture of 0 to 20% oxygen with the remainder being inert gas.

4. The method of claim 3 wherein said inert gas is selected from the group consisting of nitrogen, helium, argon and any mix of nitrogen, helium and argon.

5. A battery-grade zinc powder comprising zinc metal or zinc alloy particles, said zinc metal or zinc alloy particles having a particle size distribution where the log normal slope of the not classified material is less than 2.

6. The battery-grade zinc powder of claim 5 wherein a major portion of said particles are teardrop.

7. The battery grade zinc powder of claim 6 wherein said particles have an average length between about 250 μm and 3000 μm, preferably between 500 μm and 2000 μm.

8. The battery-grade zinc powder of claim 6 wherein said particles have an aspect ratio between 2 and 30, preferably between 8 and 22.

9. The battery-grade zinc powder of claim 5 wherein a major portion of said particles are acicular or stranded.

10. The battery grade zinc powder of claim 9 wherein said particles have an average length between about 250 μm and 3000 μm, preferably between 500 μm and 2000 μm.

11. The battery-grade zinc powder of claim 9 wherein said particles have an aspect ratio between 2 and 30, preferably between 8 and 22.

12. The battery-grade zinc powder of claim 5 wherein a major portion of said particles are spherical.

13. The battery grade zinc powder of claim 5 wherein said particles have an average width between about 40 μm and 1000 μm, preferably between 40 μm and 200 μm.

14. The battery grade zinc powder of claim 5 further comprising a second zinc metal or zinc alloy powder having different average characteristics in term of aspect ratio, width and length.

15. The battery grade zinc powder of claim 5 further comprising up to about 50% of a fine zinc metal or zinc alloy powder having a particle size of less than about 75 μm.

16. The battery grade zinc powder of claim 15 wherein said fine zinc metal or zinc alloy powder is fabricated from the same zinc metal or zinc alloy as said zinc particles.

17. The battery grade zinc powder of claim 15 comprising up to about 20% of said fine zinc metal or zinc alloy powder.

18. The battery grade zinc powder of claim 5 further comprising up to about 50% of a second zinc metal or zinc alloy powder having an average aspect ratio of about 2 and a particle size distribution between about 54 μm and about 425 μm.

19. The battery grade zinc powder as in claim 18 wherein said second zinc powder is fabricated from the same zinc metal or zinc alloy as said zinc particles.

20. The battery grade zinc powder as in claim 18 comprising up to about 20% of said second zinc powder.

21. The battery grade zinc powder of claim 5 wherein the zinc powder is a zinc alloy comprising zinc, bismuth and indium.

22. The battery grade zinc powder of claim 21 wherein said zinc alloy comprises between about 50 to 1000 ppm, preferably between about 100 to 500 ppm, bismuth.

23. The battery grade zinc powder of claim 21 wherein said zinc alloy comprises between about 50 to 1000 ppm indium, preferably between about 100 to 500 ppm, indium.

24. The battery grade zinc powder of claim 21 wherein said zinc alloy further comprises aluminum.

25. The battery grade zinc powder of claim 24 wherein said zinc alloy further comprises calcium.

26. The battery grade zinc powder of claim 25 wherein said zinc alloy comprises between about 20 to 1000 ppm calcium, preferably between about 50 to 200 ppm, calcium.

27. The battery grade zinc powder of claim 24 wherein said zinc alloy further comprises lead.

28. The battery grade zinc powder of claim 27 wherein said zinc alloy comprises between 50 to 1000 ppm lead, preferably between about 50 to 500 ppm, lead.

29. The battery grade zinc powder of claim 24 wherein said zinc alloy comprises between about 20 to 1000 ppm aluminum, preferably between about 50 to 200 ppm, aluminum.

30. The battery grade zinc powder of claim 21 wherein said zinc alloy further comprises calcium.

31. The battery grade zinc powder of claim 30 wherein said zinc alloy comprises between about 20 to 1000 ppm calcium, preferably between about 50 to 200 ppm, calcium.

32. The battery grade zinc powder of claim 30 wherein said zinc alloy further comprises lead.

33. The battery grade zinc powder of claim 32 wherein said zinc alloy comprises between 50 to 1000 ppm lead, preferably between about 50 to 500 ppm, lead.

34. The battery grade zinc powder of claim 21 wherein said zinc alloy further comprises lead.

35. The battery grade zinc powder of claim 34 wherein said zinc alloy comprises between 50 to 1000 ppm lead, preferably between about 50 to 500 ppm, lead.

36. The battery grade zinc powder of claim 5 wherein said particles are fabricated using impulse atomisation.

37. The battery grade zinc powder of claim 36 wherein said impulse atomisation has a frequency of between 20 and 1000 Hz, a force applied to the plunger of between about 44.5 and 400 newtons, a plunger distance of between 1 to 7 mm and atomising apertures of between 40 and 500 μm.

38. The battery grade zinc powder of claim 37 wherein said particles are cooled in an atmosphere comprising a gas selected from the group consisting of air, inert gas, oxygen and a mixture of 0 to 20% oxygen with the remainder being inert gas.

39. The battery grade zinc powder of claim 38 wherein said inert gas is selected from the group consisting of nitrogen, helium, argon and any mix of nitrogen, helium and argon.

40. An anode for an electrochemical cell comprising the battery grade zinc powder of claim 5, the zinc powder being suspended in a fluid medium.

41. The anode of claim 40 wherein said fluid medium is a gelled KOH electrolyte.

42. The anode of claim 41 wherein said gelled KOH electrolyte comprises i) 98% by weight of KOH 40%/ZnO 3% and ii) 2% by weight of a gelling agent.

43. The battery grade zinc powder of claim 42 wherein said gelling agent is polyacrylic acid.

44. An electrochemical cell comprising a cathode, an anode comprising the battery grade zinc powder of claim 5 and a separator electrically separating said cathode from said anode.

45. The electrochemical cell of claim 44 wherein said separator is fabricated from a material selected from the group consisting of rayon or cellulose.

46. The electrochemical cell of claim 45 wherein said cathode comprises manganese dioxide, wherein said fluid medium is a gelled KOH electrolyte and further comprising a current collector inserted into said anode.

47. The electrochemical cell of claim 46 wherein said gelled KOH electrolyte comprises about 2% by weight of a gelling agent.

48. The electrochemical cell of claim 47 wherein said gelling agent is a polyacrylic acid.

49. A battery grade zinc powder comprising stranded particles fabricated from a zinc metal, said stranded particles having a tap density of at most about 3.2 g/cc, preferably at most about 2.8 g/cc

50. A battery grade zinc powder comprising tear drop particles fabricated from a zinc metal, said tear drop particles having a tap density of at most about 3.6 g/cc.

51. A battery grade zinc powder comprising spherical particles fabricated from a zinc metal, said spherical particles having a tap density of at least about 4.10 g/cc.

52. A battery grade zinc powder comprising particles fabricated from a zinc alloy, said alloy consisting essentially of zinc, aluminum, bismuth and indium, said particles having a surface oxidation of less than about 0.10%, preferably less than 0.06%.

53. A battery grade zinc powder comprising particles fabricated from a zinc alloy, said alloy consisting essentially of zinc, bismuth and indium, said particles having a surface oxidation of less than about 0.20%.

54. A battery grade zinc powder comprising particles fabricated from a zinc alloy, said alloy consisting essentially of zinc, bismuth, indium and lead, said particles having a surface oxidation of less than 0.10%, preferably less than about 0.06%.

55. A battery grade zinc powder comprising particles fabricated from a zinc alloy, said alloy comprising zinc and aluminum, said particles exhibiting an alkaline aluminum loss of less than about 20% when immersed in KOH electrolyte.

56. A LR-06 electrochemical cell comprising: a positive terminal fabricated from a conductive material; a cathode in electrical contact with said positive terminal; an anode comprising a battery grade zinc powder as defined in claim 5, said zinc powder being suspended in a gelled electrolyte; a separator electronically separating said cathode and said anode; and a current collector inserted into said anode; wherein when a load of 1 ohm is placed between said positive terminal and said current collector, a cut-off voltage of 1.0 volts is reached in a time of greater than about 34 minutes.

57. The LR-06 electrochemical cell of claim 56, wherein said cut-off voltage of 1.0 volts is reached in at least about 42 minutes.

58. A LR-06 electrochemical cell comprising: a positive terminal fabricated from a conductive material; a cathode in electrical contact with said positive terminal; an anode comprising battery grade zinc powder as defined in claim 5, said zinc powder being suspended in a gelled electrolyte; a separator electronically separating said cathode and said anode; and a current collector inserted into said anode; wherein when a current of 1 ampere is drawn by a load placed between said positive terminal and said current collector, a cut-off voltage of 1.0 volts is reached in a time of greater than about 36 minutes.

59. The LR-06 electrochemical cell of claim 58, wherein said cut-off voltage of 1.0 volts is reached in at least about 45 minutes.