Zinc silicate luminescent materials and related luminescent screen products

Abstract

Willemite (Zn2SiO4:Mn) is doped with one or more ions selected from the group formed by Gd3+, Eu2+, Co2+, Ce3+, Pr3+, Nd3+, Sm3+, Tb3+, Dy3+, Ho3+, Er3+, Tm3+ and Yb3+. This results in a increase in absorption and quantum yield and a decrease of the decay time.

Description

BACKGROUND OF THE INVENTION

The invention relates to a luminescent material comprising zinc silicate activated with Mn 2+ . The invention also relates to a luminescent screen, a plasma panel display and a discharge lamp.

A luminescent material comprising zinc silicate activated with Mn 2+ is known for instance from EP 0393754, to which U.S. Pat. No. 5,041,758 corresponds. Such a luminescent material is widely used in fluorescent lamps and in plasma display panels to convert exciting radiation into visible green light. In fluorescent lamps the luminescent material is mainly excited by radiation with a wavelength of 254 nm, whereas in plasma display panels the excitation takes place under the influence of VUV radiation (10 nm-200 nm). Although the efficiency of the conversion depends on the wavelength of the exciting radiation, it can be concluded that in both applications the overall efficiency of the conversion of the exciting radiation into visible green light is relatively poor. Furthermore the decay time of the luminescent material is too long for displaying e.g. motion pictures on a plasma display panel.

SUMMARY OF THE INVENTION

The invention aims to provide a luminescent material comprising zinc silicate activated with Mn 2+ , that converts exciting radiation within a wide range of wavelengths relatively efficiently into visible green light and has a relatively short decay time under VUV excitation.

In accordance with the invention, zinc silicate is doped with one or more dopant ions chosen from the group formed by Gd 3+ , Eu 2+ , Co 2+ , Ce 3+ , Pr 3+ , Nd 3+ , Sm 3+ , Tb 3+ , Dy 3+ , Ho 3+ , Er 3+ , Tm 3+ , and Yb 3+ .

It has been found that a luminescent material according to the invention has a relatively high absorption for exciting radiation within a wide range of wavelengths. Furthermore the quantum yield of luminescent materials is also relatively high. As a result, luminescent materials according to the invention show a relatively high overall efficiency of the conversion of exciting radiation into visible green light for exciting radiation within a wide range of wavelengths. It has further been found that a luminescent material according to the invention has a relatively short decay time under VUV excitation.

In case the zinc silicate is doped with a trivalent ion, the luminescent material preferably further comprises one or more ions chosen from the group formed by Li 1+ , Na 1+ and K 1+ . By choosing the amount of monovalent ions substantially equal to the amount of trivalent ions, it is realized that the luminescent material has no net electrical charge.

Good results have been found for luminescent materials wherein between 0.1% and 15% of the Zn 2+ ions of zinc silicate have been replaced by Mn 2+ ions.

Similarly good results have been obtained for luminescent materials wherein between 0.05% and 5% of the Zn 2+ ions of zinc silicate have been replaced by dopant ions.

Because of the properties described hereabove, a luminescent material according to the invention is very suitable to be used in a luminescent screen that is part of a plasma display panel or of a discharge lamp. More in particular, good results have been obtained for discharge lamps comprising a gastight lamp vessel containing mercury and gas.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

ZnO, SiO 2 , Mn-acetate.4H 2 O, GdCl 3 .6H 2 O and LiF (acting both as a charge compensator and as flux) are dispersed/dissolved in water using ultrasound waves. The suspension is then evaporated to dryness. The resulting mixture is then fired in a crucible at a temperature of 1200 C. under an atmosphere of 99% nitrogen mixed with 1% hydrogen. The temperature is first increased to 1200 C. with a rate of 4 C./minute, then maintained at 1200 C. for two hours and subsequently decreased to ambient temperature with a rate of 4 C./minute. The resulting luminescent material had a gadolinium content equal to 0.7 mol % and a manganese content equal to 11 mol %. Upon excitation with 254 nm radiation a quantum yield of 83% and an absorption of 94% was measured. Under identical conditions, in case of a luminescent material comprising no dopant ions but only 11 mol % of manganese (P1G1S manufactured by Kasei) the quantum yield was measured at 80% while the absorption was 95%.

The doped luminescent material and the luminescent material comprising no dopant were, also excited by means of a Ne/Xe plasma. The absorption was 95% and the quantum efficiency approximately 80%. Under these conditions the relative light output is defined as the ratio of the luminescent material emission integral and the Ne plasma line integral, the latter acting as an internal reference. The relative light output of the luminescent material containing no dopant was measured at 17.9, while the relative light output of the doped luminescent material was substantially higher at 29.9. When the luminescent materials were excited by excitation pulses having a pulse length of 0.5 msec., the decay time (defined as the time after which 90% of the excited manganese ions has relaxated) was measured at 9.9 msec. for the luminescent material comprising no dopant and 5.9 msec. for the doped luminescent material. When the luminescent materials were excited by excitation pulses having a pulse length of 20 msec., the decay times were respectively measured at 14.5 msec. and 8.0 msec. It can be concluded that the luminescent material according to the invention converts the exciting radiation into visible green radiation with a relatively high efficiency and also that the decay time of a luminescent material according to the invention is relatively short.

Claims

1. Luminescent material consisting essentially of zinc silicate activated with Mn2+, wherein the zinc silicate is doped with one or more dopant ions chosen from the group formed by Gd3+, Eu2+, Co2+, Ce3+, Pr3+, Nd3+, Sm3+, Tb3+, Dy3+, Ho3+, Er3+, Tm3+ and Yb3+.

2. Luminescent material according to claim 1 wherein between 0.1% and 15% of the Zn2+ ions of the zinc silicate have been replaced by the Mn2+ ions.

3. Luminescent material according to claim 1 wherein between 0.05% and 5% of the Zn2+ ions of the zinc silicate have been replaced by one or more of said dopant ions.

4. Luminescent material comprising zinc silicate activated with Mn2+, characterized in that the zinc silicate is doped with one or more dopant ions chosen from the group formed by Gd3+, Eu2+, Co2+, Ce3+, Pr3+, Nd3+, Sm3+, Tb3+, Dy3+, Ho3+, Er3+, Tm3+ and Yb3+, wherein the zinc silicate is doped with a trivalent ion and further comprises one or more ions chosen from the group formed by Li1+, Na1+ and K1+.

5. Luminescent material according to claim 4 wherein between 0.1% and 15% of the Zn2+ ions of the zinc silicate have been replaced by the Mn2+ ions.

6. Luminescent material according to claim 4, wherein between 0.05% and 5% of the Zn2+ ions of the zinc silicate have been replaced by dopant ions.

7. Luminescent screen comprising a luminescent material comprising zinc silicate activated with Mn2+, characterized in that the zinc silicate is doped with one or more dopant ions chosen from the group formed by Gd3+, Eu2+, Co2+, Ce3+, Pr3+, Nd3+, Sm3+, Tb3+, Dy3+, Ho3+, Er3+, Tm3+ and Yb3+, wherein the zinc silicate is doped with a trivalent ion and further comprises one or more ions chosen from the group formed by Li1+, Na1+ and K1+.

8. Plasma display panel comprising a luminescent screen as claimed in claim 7.

9. Discharge lamp comprising a luminescent screen as claimed in claim 7.

10. Discharge lamp according to claim 9, comprising a gastight lamp vessel containing mercury and gas.

11. Luminescent material comprising zinc silicate activated with Mn2+, wherein the zinc silicate is doped with one or more trivalent dopant ions chosen from the group consisting of Gd3+, Ce3+, Pr3+, Nd3+, Sm3+, Tb3+, Dy3+, Ho3+, Er3+, Tm3+ and Yb3+ and the zinc silicate further comprises one or more ions chosen from the group consisting of Li1+, Na1+ and K1+.

12. Luminescent material according to claim 11, wherein the amount of monovalent ions is substantially equal to the amount of trivalent ions.

13. Luminescent material according to claim 11, wherein between 0.1% and 15% of the Zn2+ ions of the zinc silicate have been replaced by the Mn2+ ions.

14. Luminescent material according to claim 11, wherein between 0.05% and 5% of the Zn2+ ions of the zinc silicate have been replaced by said one or more dopant ions.

15. Luminescent screen comprising a luminescent material, said material comprising zinc silicate activated with Mn2+, wherein the zinc silicate is doped with one or more trivalent dopant ions chosen from the group consisting of Gd3+, Ce3+, Pr3+, Nd3+, Sm3+, Tb3+, Dy3+, Ho3+, Er3+, Tm3+ and Yb3+ and the zinc silicate further comprises one or more ions chosen from the group consisting of Li1+, Na1+ and K1+.

16. Plasma display panel comprising a luminescent screen as claimed in claim 15.

17. Discharge lamp comprising a luminescent screen as claimed in claim 15.

18. Discharge lamp according to claim 17, comprising a gastight lamp vessel containing mercury and gas.