ZnWO4 PHOTOCATALYTIC MATERIAL WITH OXYGEN VACANCY AND PREPARATION METHOD THEREOF

Abstract

The invention belongs to the field of novel photocatalytic materials, and particularly relates to a ZnWO4 photocatalytic material containing oxygen vacancy. According to the material, absorption exists in a near infrared region of an ultraviolet-visible light diffuse reflection spectrum, wherein the wavelength range of the near infrared region is 780-2500 nm. The invention further relates to a preparation method of the ZnWO4 photocatalytic material containing oxygen vacancy. Na2WO4 and soluble zinc salt are used as raw materials, ZnWO4 crystals are formed through a hydrothermal crystallization reaction and then roasted in the presence of hydrogen so as to achieve partial reduction of ZnWO4, and then the ZnWO4 photocatalytic material containing oxygen vacancy is obtained.

Description

TECHNICAL FIELD

The invention belongs to the field of novel photocatalytic materials, and particularly relates to a ZnWO₄ photocatalytic material containing oxygen vacancy and a preparation method thereof.

BACKGROUND ART

With the growing consumption of fossil fuels, energy crises and environmental problems are caused, which increasingly limit the development of human societies, so that there is no delay in looking for alternative energy sources. Efficient and convenient utilization, conversion and storage of solar energy facilitate solving energy and environmental problems. A photocatalysis technology is a method of directly converting solar energy into chemical energy in the presence of a photocatalytic material. The photocatalysis technology can be used for hydrogen production by water decomposition and degradation of organic pollutants, and a reaction process is green and convenient, so that the photocatalysis technology has a great application prospect and provides new ideas for solving the energy crisis and environmental problems. Typical photocatalytic materials are mostly semiconductors, including TiO₂, ZnO, WO₃, CdS, BiVO₄, etc. While when these semiconductor materials are applied to a photocatalytic process, the problems of weak absorption of visible light, differential charge separation, photocorrosion, etc. often exist.

Transition metal tungstate, ZnWO₄, is a wide bandgap (>3.6 eV) semiconductor photocatalytic material featuring by high electron transport rate and long life of a photon-generated carrier. The ZnWO₄ photocatalytic material has extensive application prospects in the fields of photocatalytic degradation of organic pollutants, photocatalytic hydrogen production, photoluminescence materials, etc. However, the too wide bandgap of the ZnWO₄ photocatalytic material limits the photocatalytic capacity of the ZnWO₄ photocatalytic material under visible light, mainly reflected in the problems that the ZnWO₄ photocatalytic material is narrow in light absorption range and poor in charge separation.

The invention is intended to solve the foregoing problems.

SUMMARY OF THE INVENTION

The invention provides a ZnWO₄ photocatalytic material containing oxygen vacancy in a first aspect. According to the material, absorption exists in a near infrared region of an ultraviolet-visible light diffuse reflection spectrum, and the wavelength range of the near infrared region is 780-2500 nm.

ZnWO₄ is roasted in the presence of hydrogen so as to achieve partial reduction of ZnWO₄, and then the ZnWO₄ photocatalytic material containing oxygen vacancy is obtained.

Preferably, the roasting temperature is 350-600 DEG C. and the roasting time is 1-4 h.

Preferably, the temperature increasing rate during roasting is 1-5 DEG C./min.

The invention provides a preparation method of the ZnWO₄ photocatalytic material containing oxygen vacancy in a second aspect. According to the preparation method, Na2WO₄ and soluble zinc salt are used as raw materials, ZnWO₄ crystals are formed through a hydrothermal crystallization reaction and then roasted in the presence of hydrogen so as to achieve partial reduction of ZnWO₄, and then the ZnWO₄ photocatalytic material containing oxygen vacancy is obtained.

Preferably, the soluble zinc salt is ZnCl₂, Zn(CH₃COO)₂ or Zn(NO₃)₂, with the concentration range in hydrothermal crystallization mother liquor being 0.001-0.1 mol/L.

Preferably, the temperature range of the hydrothermal crystallization reaction is 120-200 DEG C., and the hydrothermal crystallization reaction time is 12-36 h.

In the invention, a typical ZnWO₄ photocatalytic material is synthesized by a hydrothermal process, and the oxygen vacancy is introduced by roasting and reducing in the presence of hydrogen, so that the ZnWO₄ photocatalytic material with oxygen vacancy is obtained, and the introduction amount of the oxygen vacancy is changed by regulating the roasting reduction temperature and time.

The specific preparation scheme is as follows:

(1) synthesis of a typical ZnWO₄ photocatalytic material by a hydrothermal process: by taking deionized water as a solvent, a 0.001-0.1 mol/L slat solution of zinc (ZnCl₂, Zn(CH₃COO)₂ and Zn(NO₃)₂) is mixed with a Na₂WO₄ solution having equivalent volume and concentration, stirring is carried out continuously for 30 min, and then a white suspension is obtained; the obtained white suspension is put in a hydrothermal reaction kettle, a reaction undergoes at 120-200 DEG C. for 12-36 h, and then cooling to room temperature is carried out; and then, a solid product in the hydrothermal reaction kettle is separated out and is washed with deionized water and ethanol for three times respectively, and subsequently drying and grinding are carried out, so that a corresponding ZnWO₄ photocatalytic material is obtained; and

(2) preparation of the ZnWO₄ photocatalytic material containing oxygen vacancy by roasting and reducing in the presence of hydrogen: the obtained typical ZnWO₄ photocatalytic material is put in a crucible, and is roasted in an atmosphere furnace under a hydrogen atmosphere at 350-600 DEG C. for 1-4 h, with the temperature increasing rate during roasting being 1-5 DEG C./min, and finally an obtained product is the ZnWO₄ photocatalytic material containing oxygen vacancy. The ZnWO₄ photocatalytic material containing oxygen vacancy and the preparation method have the following benefits:

(1) the visible light absorption capacity of ZnWO₄ is improved by introducing the oxygen vacancy, and the photocatalytic performance of ZnWO₄ is further improved; and

(2) the introduction amount of the oxygen vacancy can be regulated by changing the roasting and reduction time and temperature in the presence of hydrogen, so that the ZnWO₄ photocatalytic material containing oxygen vacancy meet the requirements of different application scenes.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is an X-ray diffraction spectrogram of a ZnWO₄ photocatalytic material containing oxygen vacancy.

FIG. 2 is an ultraviolet-visible light diffuse reflection spectrum (UV-VIS spectrum) of the ZnWO₄ photocatalytic material containing oxygen vacancy.

FIG. 3 shows the photocatalytic hydrogen production performance of the ZnWO₄ photocatalytic material containing oxygen vacancy in a lactic acid solution.

DETAILED DESCRIPTION OF THE INVENTION

The invention will be further described below in conjunction with the accompanying drawings and specific embodiments, and all used drugs are from commercial sources.

Example 1

(1) Synthesis of a typical ZnWO₄ photocatalytic material by a hydrothermal process: by taking deionized water as a solvent, 4 mmol Zn(CH₃COO)₂ and 4 mmol Na₂WO₄ are dissolved in 40 mL deionized water respectively, and a solution A and a solution B are obtained; the solution B is dropwise added to the solution A with stirring, the stirring is carried out continuously for 30 min, and then a white suspension is obtained; the obtained white suspension is put in a 100 mL hydrothermal reaction kettle, the hydrothermal reaction kettle is put in an oven, a thermostatic reaction undergoes at 180 DEG C. for 24 h, and then cooling to temperature is carried out; and then, a solid product in the hydrothermal reaction kettle is separated out by centrifugation and is washed with deionized water and ethanol for three times respectively, and subsequently drying and grinding are carried out, so that a corresponding ZnWO₄ photocatalytic material is obtained; and (2) preparation of the ZnWO₄ photocatalytic material containing oxygen vacancy by roasting and reducing in the presence of hydrogen: the obtained typical ZnWO₄ photocatalytic material is put in a crucible, and is roasted in an atmosphere furnace under a hydrogen atmosphere at 400 DEG C. for 2 h, with the temperature increasing rate during roasting being 2 DEG C./min, and finally an obtained product is the ZnWO₄ photocatalytic material containing oxygen vacancy.

Example 2

(1) Synthesis of a typical ZnWO₄ photocatalytic material by a hydrothermal process: by taking deionized water as a solvent, 2 mmol ZnCl₂ and 2 mmol Na₂WO₄ are dissolved in 40 mL deionized water respectively, and a solution A and a solution B are obtained; the solution B is dropwise added to the solution A with stirring, the stirring is carried out continuously for 30 min, and then a white suspension is obtained; the obtained white suspension is put in a 100 mL hydrothermal reaction kettle, the hydrothermal reaction kettle is put in an oven, a thermostatic reaction undergoes at 150 DEG C. for 24 h, and then cooling to temperature is carried out; and then, a solid product in the hydrothermal reaction kettle is separated out by centrifugation and is washed with deionized water and ethanol for three times respectively, and subsequently drying and grinding are carried out, so that a corresponding ZnWO₄ photocatalytic material is obtained; and (2) preparation of the ZnWO₄ photocatalytic material containing oxygen vacancy by roasting and reducing in the presence of hydrogen: the obtained typical ZnWO₄ photocatalytic material is put in a crucible, and is roasted in an atmosphere furnace under a hydrogen atmosphere at 500 DEG C. for 4 h, with the temperature increasing rate during roasting being 2 DEG C./min, and finally an obtained product is the ZnWO₄ photocatalytic material containing oxygen vacancy.

Example 3

Example 3 is a spectroscopy characterization and activity experiment on the ZnWO₄ photocatalytic material containing oxygen vacancy and a common ZnWO₄ photocatalytic material.

FIG. 1 is an X-ray diffraction spectrogram of the ZnWO₄ photocatalytic material containing oxygen vacancy and the common ZnWO₄ photocatalytic material which are prepared on the conditions of the example 1 and the example 2. It can be observed that the X-ray diffraction peak intensity after the oxygen vacancy is introduced is weakened generally.

FIG. 2 is an ultraviolet-visible light diffuse reflection spectrum of the ZnWO₄ photocatalytic material containing oxygen vacancy and the common ZnWO₄ photocatalytic material which are prepared on the conditions of the example 1 and the example 2. It can be observed that absorption of ZnWO₄ with the oxygen vacancy exists in a near infrared region, which shows that the oxygen vacancy exist in the material.

FIG. 3 is a performance evaluation experiment on the ZnWO₄ photocatalytic material containing oxygen vacancy and the common ZnWO₄ photocatalytic material, prepared on the conditions of the example 1 and the example 2, applied to a lactic acid photocatalytic hydrogen production reaction. The horizontal axis is reaction time and the longitudinal axis is a hydrogen evolution rate. Obviously, the activity of the ZnWO₄ photocatalytic material containing oxygen vacancy in the example 1 is increased by about 4 times compared with that of the typical ZnWO₄ photocatalytic material, and the activity of the ZnWO₄ photocatalytic material containing oxygen vacancy in the example 2 is increased by about 6 times compared with that of the typical ZnWO₄ photocatalytic material, which shows that after the oxygen vacancy is introduced, the ZnWO₄ photocatalytic activity is improved greatly.

Claims

1. A ZnWO4 photocatalytic material containing oxygen vacancy, characterized in that absorption exists in a near infrared region of an ultraviolet-visible light diffuse reflection spectrum of the material, wherein a wavelength range of the near infrared region is 780-2500 nm.

2. The ZnWO4 photocatalytic material containing oxygen vacancy of claim 1, characterized in that ZnWO4 is roasted in the presence of hydrogen so as to achieve partial reduction of ZnWO4, and then the ZnWO4 photocatalytic material containing oxygen vacancy is obtained.

3. The ZnWO4 photocatalytic material containing oxygen vacancy of claim 2, characterized in that a roasting temperature is 350-600 DEG C., and a roasting time is 1-4 h.

4. The ZnWO4 photocatalytic material containing oxygen vacancy of claim 2, characterized in that a temperature increasing rate during roasting is 1-5 DEG C./min.

5. A preparation method of the ZnWO4 photocatalytic material containing oxygen vacancy, characterized in that Na2WO4 and soluble zinc salt are used as raw materials, ZnWO4 crystals are formed through a hydrothermal crystallization reaction and then roasted in the presence of hydrogen so as to achieve partial reduction of ZnWO4, and then the ZnWO4 photocatalytic material containing oxygen vacancy is obtained.

6. The preparation method of claim 5, characterized in that the soluble zinc salt is ZnCl2, Zn(CH3COO)2 or Zn(NO3)2, with a concentration range in hydrothermal crystallization mother liquor being 0.001-0.1 mol/L.

7. The preparation method of claim 5, characterized in that the temperature range of the hydrothermal crystallization reaction is 120-200 DEG C., and a hydrothermal crystallization reaction time is 12-36 h.

8. The preparation method of claim 5, characterized in that an introduction amount of oxygen vacancy is changed by regulating the roasting temperature and a reduction time.