The present invention relates to a cap, closure, top or the like for a bottle intended to contain, for example, a fluid. It also relates to a process for manufacturing a cap or the like.
Plastic caps are conventionally manufactured from plastic materials that are converted in a thermoplastic injection moulding process that consists in melting the material in a regulated screw/barrel assembly and in pushing the material into a multi-cavity mould in order to enable the material to be formed and cooled.
Operators in this field are confronted with the costs of the plastic materials used which increase proportionally with the cost of hydrocarbons.
According to an aspect of the present invention there is provided a closure comprising a top plate and a sidewall depending from the periphery of the top plate, the closure including a sealing member which depends from the top plate within the sidewall, in which the top plate includes a foamed region which is restricted to being within a boundary defined by the sealing member, the sealing member being substantially unfoamed.
The sealing member may be formed integrally with the top plate. The sealing member may be, for example, a crab claw type seal or a plug seal.
Alternatively or additionally the sealing member may be formed separately from, and be attachable to, or located adjacent, the top plate.
Selective foaming via mould movements could be used in order to remain “inside” (i.e. between) the seal feature/s. This makes it possible to maintain dimensional repeatability and functional sealing performance. For example the sealing feature may be generally annular and the foamed region is restricted to being radially inwards of the feature.
The extremity of the foamed region is spaced from the sealing member by between 0.5 and 5 mm, for example between 1 mm and 2 mm. In other words foaming is induced inside the seal features and between 0.5 and 5 mm of gap is left to ensure seal performance is not altered or modified.
The present invention also provides a closure comprising a top plate and a sidewall, the closure including a sealing liner which depends from the top plate, in which at least part of the top plate includes a foamed region.
The liner may be generally disc-shaped or otherwise shaped so as to substantially cover the underside of the top plate.
The sidewall may comprise a screw thread formation. The screw thread formation extends radially inwards and the foamed plastics material may not extend beyond a boundary defined by the radial extent of the formation.
The foamed region may comprise a first layer formed of unfoamed plastics material, a second layer of foamed plastics material and a third layer of unfoamed plastics material, the second layer being positioned between the first layer and the third layer. Therefore a trilaminar structure is provided, with a central core and an outer layers either side of the core.
The second layer may be positioned approximately centrally with respect to the first and third layers.
The present invention also provides a wide mouth container lid comprising a closure as described herein.
The present invention also provides a jar lid comprising a closure as described herein.
The present invention also provides a flip top dispensing closure comprising a base and a lid connected by an integral hinge, the base comprising a top plate and a sidewall depending from the periphery of the top plate, the closure including a sealing member which depends from the top plate within the sidewall, in which the top plate includes a foamed region which is restricted to being within the sealing member whereby the sealing member is substantially unfoamed.
The lid may comprise a top plate with a depending sidewall and at least part of the lid has a foamed region.
The hinge may be formed from unfoamed plastics material.
In some embodiments the hinge portion consists of the unfoamed plastic material so that it has sufficient mechanical fatigue strength (or hinge endurance) properties in order to be stressed and folded several times without breaking during the opening and closure of the orifice.
In some aspects and embodiments the sidewall comprises a screw thread formation (for example a single or a multi-start thread).
The present invention also provides a closure comprising a top plate and a sidewall, the closure comprising a separate liner for providing a seal in use, the liner being secured or securable to the top plate and defining a non-sealing region of the top plate within the liner, in which at least part of the non-sealing region includes a foamed region.
At least part of the sidewall may have a foamed region.
The present invention also provides a closure comprising a top plate and a sidewall depending from the periphery of the top plate, in which at least part of the sidewall is formed from foamed plastics material.
At least part of the top plate may be formed from foamed plastics material.
The sidewall may comprise a screw thread formation.
Conventionally, in closures with a side skirt that has a screw thread formation the skirt is actually quite thick due to the fact that sufficient material must be used to limit the creation of “sink marks” on the outer surface of the skirt.
In some embodiments the foaming agent is present throughout the formulation i.e. in parts of the closure which will be subject to mould movement expansion and parts which will not. The present inventors have realised that it is possible to rely on the fact that the foaming agent makes it possible to compensate the sink marks in the skirt. Accordingly it is possible to make these parts of the closure thinner than normal whilst not suffering the problem of sink marks.
In one aspect of the present invention therefore, a closure is formed with a foamed core top plate and a reduced thickness sidewall.
Hence the foaming agent, added as a master batch, has two effects:
The present invention also provides a moulded closure formed from a foamable plastics material, the closure comprising a top plate and a sidewall, the plastics material forming part of the top plate being intentionally unfoamed and having an apparent density of R, the rest of the material forming the top plate being intentionally foamed and having an apparent density in the range of 0.2-0.9 R, for example in the range 0.4 R to 0.8 R, the sidewall including a screw thread formation, the material forming the sidewall at least in the region of the formation having an apparent density in the range 0.8-0.99*R whereby shrinkage has been compensated by natural foaming.
For example, for PP, R will be equal to 0.9 and for HDPE, R will be between 0.93 and 0.96.
Sink marks in injection moulded plastic closures can develop when material in the region of screw threads shrinks more than the material in the adjacent wall. The presence of the screw threads creates an effectively thicker region that cools more slowly than neighbouring regions. Differential rates of cooling result in a depression on the adjacent surface that is known as a sink mark.
Currently the maximum depth of a thread formation is up around 80% of the sidewall thickness if sink marks are to be avoided.
In embodiments of the present invention in which the sidewall comprises a screw thread formation the depth of the formation may be more than 80% of the depth of the sidewall. The use of a foamable plastics material means that depressions in the sidewall are compensated for by natural expansion of the foamable plastics material.
In some embodiments the formation depth may be up to 120% of the depth of the sidewall.
The present invention also provides a method of forming a closure as described herein, comprising the steps of: providing an injection mould with a fixed part and a mobile part; positioning the mould parts to define a first gap; injecting a foamable plastics material formulation to fill the first gap; and moving the mobile part to define a second gap so that the formulation expands to fill the second gap.
The ratio between the second gap and the first gap may be between 1.1 and 1.8. It is thus possible to obtain an average expansion ratio of the plastic material of the order of 10% to 80%.
The ratio between the second gap and the first gap may be between 1.3 and 1.7. The expansion ratio that can be achieved is then between 30% and 70%.
The method may further comprise an in-mould labelling step.
The present invention also provides a method of forming a moulded plastics closure, comprising the steps of
The top plate may be formed so as to include a depending sealing member. The sealing member may extend generally perpendicular to the parting line of the mould.
The method may further comprise the step of loading a label into the mould prior to injection moulding the body whereby to facilitate in-mould labelling of the body.
The present invention also provides a method of forming a moulded plastics closure, comprising the steps do
The present invention also provides a method of forming a moulded plastics closure, comprising the steps of
In some aspects and embodiments the present invention aims to reduce the costs by proposing a cap for a bottle intended to contain a fluid, the cap comprising at least a sealing portion (or top plate) and a lateral portion (or sidewall) intended to be fastened to the bottle, the sealing portion comprising along a direction substantially perpendicular to the lateral portion a first layer formed of unfoamed plastic material, a second layer formed of foamed plastic material and a third layer formed of unfoamed plastic material, the second layer being positioned between the first layer and the third layer.
Thus, the presence of the second layer made of foamed plastic material makes it possible to achieve a sufficient cap thickness to ensure that the necessary stiffness is obtained, while limiting the amount of raw materials used. A reduction in the weight of the caps then enables the reduction of the costs while retaining the functional, physical and chemical properties of the caps.
The expression “foamable plastics material” is understood in the present document to mean plastics material which is capable of foaming, either naturally or deliberately (for example by movement of a mould part).
The expression “foamed region” is understood in the present document to mean an area of a closure wall (such as a top plate or a sidewall) which has been caused to foam deliberately i.e. by a specific step in a moulding process, such as movement of a mould part.
The expression “unfoamed plastics material” is understood in the present document to mean a solid plastic material corresponding to “unfoamed plastic material” or “plain material” (density R).
The expression “foamed material” means material which has been caused to expand by movement of a mould part and a pressure released while the material is locally still molten (density between 0.2 R and 0.9 R).
The expression “expanded material” means material which expands into a mould cavity without movement of the mould i.e. naturally “swelling” to fill a gap and naturally taking up any shrinkage (density between 0.9 R and 0.99 R).
Closures formed in accordance with the present invention can have one or more regions of unfoamed material (intentionally unfoamed); expanded material (naturally foamed); and foamed material (intentionally foamed). Intentionally foamed regions will normally be formed from foamed as well as unfoamed material (e.g. a foamed core with unfoamed skins either side).
In the “thickness” of a foamed wall (e.g. top plate or side wall) may be a succession of skin—foamed core—skin.
Closures formed in accordance with the present invention may be obtained from a formulation comprising at least one polyolefin, for example polypropylene or polyethylene.
Closures formed in accordance with the present invention may be obtained from a formulation comprising at least one propylene-based polyolefin and at least one foaming agent in a proportion of active components of between 0.3% and 2.5% by weight introduced with a carrier.
This formulation leads to good foaming under the conditions of manufacture by thermal injection moulding via the use of a masterbatch which includes at least one foaming agent in dilute form in a matrix compatible with the resin converted. The homogenization and thermal activation of the foaming agent take place in a screw/barrel assembly.
When the cap is intended for applications in the food, pharmaceutical or paramedical field, the foaming agent is advantageously selected from endothermic agents such as citric acid, sodium bicarbonate or a mixture of these agents. In a preferred embodiment a mixture of citric acid and sodium bicarbonate is selected. The endothermic agent or mixture of endothermic agents is used in order to adjust the cell size.
In aspects and embodiments of the present invention the closure may be formed from plastics material having a melt flow index in the range of 20 to 50 g/10 min.
Preferably, the formulation comprises a melt flow index of between 20 and 50 g/110 min so that the sealing portion has an impact strength of 3.5 to 10 kJ/m2 in a notched Izod impact test at 23° C. These values are obtained according to the ISO 179/1 eA standard. Furthermore, such a melt flow index enables the formulation to be injected at relatively low temperatures, of the order of 200-210° C. This reduces the time needed for the cooling of the cap, which corresponds to the longest length of time in the process, so that the cycle time is substantially reduced.
The material of foamed portions may comprise an expansion ratio of between 30% and 70%. This makes it possible to achieve sufficient flexural stiffness despite a reduced amount of material by increasing inertia.
The top plate may have a thickness of between 1.3 and 1.7 mm so as to have an apparent flexural modulus of 800 to 1500 MPa. Indeed, this thickness of the top plate is critical considering the expansion ratio. If the thickness was smaller, the top plate could display failures in terms of mechanical stiffness so that the cap would not be able to be suitable for all uses.
According to one arrangement, the formulation used to manufacture closures in accordance with the present invention comprises a nucleating agent, such as nucleating talc, sodium benzoate (NaBz such as sodium 2,2′-methylenebis(4,6-di-tert-butylphenyl)phosphate from Asahi Denka Kogyo K. K., known commercially under the name NA-11®), a phosphate ester salt or a calcium metal salt (Hyperform® HPN-20E) in a proportion of between 300 and 1500 ppm.
The formulation may comprise a clarifying agent, such as a derivative of sorbitol (1,3:2,4-dibenzylidene sorbitol—DBS—Irgaclear D from CIBA or Millad 3905 from Milliken, 1,3;2,4-di-p-methyldibenzylidene sorbitol MDBS—Irgaclear DM from CIBA or Millad 3940 from Milliken, 1,3:2,4-di-m,p-methylbenzylidene sorbitol DMDBS, Millad 3988 from Milliken) in a proportion of between 500 and 2000 ppm or a derivative of nonitol (1,2,3-trideoxy-4,6:5,7-bis-O-[(4-propylphenyl)methylene]nonitol) in a proportion of between 3000 and 5000 ppm.
Different aspects and embodiments of the invention may be used separately or together.
Further particular and preferred aspects of the present invention are set out in the accompanying independent and dependent claims. Features of the dependent claims may be combined with the features of the independent claims as appropriate, and in combination other than those explicitly set out in the claims.
The present invention will now be more particularly described, by way of example, with reference to the accompanying drawings.
The example embodiments are described in sufficient detail to enable those of ordinary skill in the art to embody and implement the systems and processes herein described. It is important to understand that embodiments can be provided in many alternate forms and should not be construed as limited to the examples set forth herein.
Accordingly, while embodiment can be modified in various ways and take on various alternative forms, specific embodiments thereof are shown in the drawings and described in detail below as examples.
There is no intent to limit to the particular forms disclosed. On the contrary, all modifications, equivalents, and alternatives falling within the scope of the appended claims should be included. Elements of the example embodiments are consistently denoted by the same reference numerals throughout the drawings and detailed description where appropriate.
Unless otherwise defined, all terms (including technical and scientific terms) used herein are to be interpreted as is customary in the art. It will be further understood that terms in common usage should also be interpreted as is customary in the relevant art and not in an idealized or overly formal sense unless expressly so defined herein.
In the following description, all orientational terms, such as upper, lower, radially and axially, are used in relation to the drawings and should not be interpreted as limiting on the invention.
Unfoamed Material (i.e. Intentionally Unfoamed)
Expanded Material (i.e. Naturally Foamed)
Foamed Material (i.e. Intentionally Foamed)
In
In a first step molten (foamable) plastics material 5 is injected through a nozzle 10 into a cavity 15 formed by a fixed mould part 20 and a moving mould part 25.
In a second step the cavity fill is complete and a short holding phase is provided, during which time the outer skins of the plastics material cool and begin to solidify.
In a third step the moving mould part 25 is moved and the pressure drop causes foaming of the material in the enlarged cavity. As a result the material between the outer skins of the top plate 30 of the moulded closure foams.
In
The closure 450 of
In
In
The region 859 includes a sealing arrangement comprising an annular crab claw seal 858.
The closure is manufactured using a foamable plastics composition and by a core back process illustrated in
The sidewall 802 includes and internal screw thread formation 805. No specific foaming is induced in the sidewall. However, natural expansion of the inherently foamable material will compensate for any shrinkage in the area, in particular at the exterior of the sidewall adjacent the screw thread formation.
Referring to
Although illustrative embodiments of the invention have been disclosed in detail herein, with reference to the accompanying drawings, it is understood that the invention is not limited to the precise embodiments shown and that various changes and modifications can be effected therein by one skilled in the art without departing from the scope of the invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 1606842.1 | Apr 2016 | GB | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP17/59445 | 4/20/2017 | WO | 00 |