A POLYMERIZATION PROCESS FOR THE PRODUCTION OF HIGH DENSITY POLYETHYLENE

Information

  • Patent Application
  • 20160046739
  • Publication Number
    20160046739
  • Date Filed
    March 27, 2014
    10 years ago
  • Date Published
    February 18, 2016
    8 years ago
Abstract
The invention relates to a polymerization process for the production of high density polyethylene by polymerization of ethylene in the presence of a catalyst composition comprising a chromium compound, a support material wherein the alcohol is a primary alcohol having the formula (I) wherein R, R′ and R″ are the same or different and respectively represent a linear or branched N alkyl, cycloalkyl, phenyl or phenyl containing radicals comprising from 5 to 15 carbon atoms and wherein only one of R, R′ or R″ can be a hydrogen radical and/or wherein the alcohol is a secondary alcohol and/or a secondary cyclic alcohol. The catalyst composition may also comprise a titanium compound. The high density polyethylene may be applied in the production of blow molded articles.
Description

The invention is directed to a process for the production of high density polyethylene by polymerisation of ethylene in the presence of a chromium oxide based catalyst.


The production processes of LDPE, HDPE and LLDPE are summarised in “Handbook of Polyethylene” by Andrew Peacock (2000; Dekker; ISBN 0824795466) at pages 43-66. The catalysts can be divided in three different subclasses including Ziegler Natta catalysts, Phillips catalysts and single site catalysts. The various processes may be divided into solution polymerisation processes employing homogeneous (soluble) catalysts and processes employing supported (heterogeneous) catalysts. The latter processes include both slurry and gas phase processes.


A chromium oxide based catalyst, which is commonly referred to in the literature as “the Phillips catalyst”, can be obtained by calcining a chromium compound carried on an inorganic oxide carrier in a non-reducing atmosphere. The chromium oxide catalysis and the ethylene polymerisation with this specific catalyst are disclosed in “Handbook of Polyethylene” by Andrew Peacock at pages 61-64.


Pullukat et al. (Journal of Polymer Science; Polymer chemistry Edition; vol18, 2857-2866; 1980) discloses thermally activated ethylene polymerisation catalysts which contain chromium and titanium on silica.


It is a disadvantage of ethylene polymerisation catalysts which contain chromium and titanium on silica that they cannot be applied in the polymerisation of ethylene in a gas phase reactor process to obtain polymers with relatively low melt indices, for example in the range between 5 to 10 (MI21.6 kg), because said catalyst must be run at very low bed temperatures in a gas phase process. The temperature drops at this stage to a temperature in the range of 92 to 98 degrees Celsius resulting in a very low production rate.


It is the object of the present invention to provide a catalyst composition having a high activity in gas phase polymerisation processes while producing high density polyethylene (HDPE) of low melt index values.


The catalyst composition according to the invention comprises a chromium compound, an alcohol and a support material characterized in that


the alcohol is a primary alcohol having the formula:




embedded image


wherein R, R′ and R″ are the same or different and respectively represent a linear or branched alkyl, cycloalkyl, phenyl or phenyl containing radicals comprising from 5 to 30, preferably 5-15, carbon atoms and wherein only one of R, R′ or R″ is a hydrogen radical and/or


the alcohol is a secondary alcohol and/or


the alcohol is a secondary cyclic alcohol.


According to a preferred embodiment of the invention the alcohol is a secondary cyclic alcohol.


According to a preferred embodiment of the invention the catalyst composition applied in the process according to the invention comprises additionally a titanium compound.


According to a further preferred embodiment of the invention the primary alcohol is selected from cyclohexanemethanol, 2-ethylhexanol and 2,2-dimethylpropanol.


According to another preferred embodiment of the invention the secondary alcohol is selected from secondary alcohols having the formula:




embedded image


wherein R and R′ are the same or different and respectively represent a linear or branched alkyl, cycloalkyl, phenyl or phenyl containing radicals comprising from 5 to 30, preferably from 5 to 15, carbon atoms.


According to a further preferred embodiment of the invention the secondary alcohol is selected from 4-methyl-2-pentanol, 3-pentanol, 1,1-diphenylmethanol, and 1,1-diphenylethanol.


According to another preferred embodiment of the invention the secondary alcohol is selected from secondary cyclic alcohols having the formula:




embedded image


wherein n is from 1 to 13 and cyclic ring represent a linear or branched alkyl radical comprising 3-30 , preferably 3-15, carbon atoms or one or more phenyl or phenyl containing radicals.


According to a preferred embodiment of the invention the cyclic alcohol is selected from cyclohexanol, cyclopentanol, cycloheptanol and fluorenol.


It is possible to apply mixtures of alcohols for example a primary alcohol or a secondary alcohol can be mixed with a secondary cyclic alcohol.


Preferably the mixture comprises a secondary cyclic alcohol as the main component in combination with a smaller amount of either primary or secondary alcohol.


A preferred mixture comprises a secondary cyclic alcohol and a primary alcohol with a weight ratio primary alcohol : secondary cyclic alcohol ranging between 1:9 and 3:7.


The most preferred secondary cyclic alcohol is cyclohexanol.


The chromium compound can be selected from various organic and inorganic forms of chromium.


Preferably the chromium compound is selected from chromium acetate, chromium acetyl acetonate, chromium acetate hydroxide and chromium trioxide. Most preferably chromium acetate or chromium acetyl acetonate is applied.


The catalyst can be formed prior to the polymerization of ethylene or within the polymerization reaction zone and the applied alcohol must react with the activated chromium oxide (Cr6+) catalyst before introduction of ethylene.


Alcohols such as tertiary alcohols, for example t-butyl alcohol, and primary alcohols, for example ethanol, are not suitable to be applied in the present invention.


Suitable support materials include for example inorganic oxides of silica, alumina, silica-alumina mixture, thoria, zirconia and comparable oxides which are porous, have a medium surface area, and have surface hydroxyl groups. Supported chromium catalysts are described for example, in U.S. Pat. No. 2,825,721. The support may be modified so as to include cogels such as for example silica-titania or silica-alumina and by the replacement of silica by alumina or amorphous aluminum phosphates. The silica support may also be doped with chemical compounds containing for example aluminum, titanium, phosphorus, boron or fluorine.


According to a preferred embodiment of the invention the support material is a silica support material.


Preferably the spherical silicon oxide support material has a surface area (SA) larger than 150 m2/g and a pore volume (PV) larger than 0.8 cm3/g.


More preferably the spherical silicon oxide support material has a surface area (SA) in the range between 250 and 500 m2/g and a pore volume (PV) in the range between 1.1 and 2.0 cm2/g.


Suitable examples of titanium compounds include titanium compounds which are oxidizable to TiO2 under the activation conditions. Examples of suitable titanium compounds having the general formula Ti (OR1)nX4−n and Ti (R2)nX4−n.


Suitable titanium alkoxy compounds include for example tetraethoxy titanium, tetramethoxy titanium, tetrabutoxy titanium, tetrapropoxy titanium, titanium tetraisopropoxide, tetraisobutoxy titanium, tetrapentoxy titanium, triethoxychloro titanium, diethoxydichloro titanium , trichloethoxy titanium, methoxy titanium trichloride, dimethoxy titanium dichloride, ethoxy titanium trichloride, diethoxy titanium dichloride, propoxy titanium trichloride, dipropoxy titanium dichloride, butoxy titanium trichloride, butoxy titanium dichloride and titanium tetrachloride and mixtures thereof.


Suitable organic oxygen containing titanium compound may be represented by the general formula [TiOx (OR)·4−2x]·n in which R represents an organic radical, x ranges between 0 and 1 and n ranges between 1 and 6.


Suitable examples of organic oxygen containing titanium compounds include alkoxides, phenoxides, oxyalkoxides , condensed alkoxides, carboxylates and enolates.


According to a preferred embodiment of the invention the organic oxygen-containing titanium compounds is a titanium alkoxide.


Suitable alkoxides include for example Ti (OC2H5)4, Ti (OC3H7)4, Ti (OC4H9)4, and Ti (OC8H17)4.


According to a preferred embodiment of the invention the titanium compound is titanium tetraisopropoxide (Ti (OC3H7)4).


The treatment of the activated chromium oxide based catalyst with the specific alcohol provides a highly active catalyst which produces a high density polymer with lower melt index values.


The present catalyst composition exhibits higher activity and greater stability during the polymerization process.


It is a further advantage of the present invention that the obtained high molecular weight HDPE is suitable to be applied for the production of large-part blow molded articles, for example drums and jerry cans. Generally, HDPE grades for customer jerry can applications have a melt flow rate (190° C./21.6 kg) between 2 g/10 min and 10 g/10 min and a density between 945 kg/m3 and 955 kg/m3.


The presence of titanium may increase the activity of the catalyst, first by shortening the induction time, and then by allowing higher polymerization rates. Furthermore the presence of titanium may result in broadening the polymer molecular weight distribution (MWD) which can be useful in for example blow moulding applications.


The catalyst is prepared by the reaction of the chromium compound with the porous support, followed by the activation at high temperature in the presence of dry air and then by a reaction with the alcohol.


The titanium compound can be added to the unactivated chromium on silica catalyst followed by activation in dry air at high temperature, in order to convert Cr (3+) to Cr (6+). The alcohol is added to the activated Cr/Ti/SiO2 or Cr/SiO2 catalyst.


Preferably, the olefin polymerisation catalyst is prepared by pre contacting the supported activated chromium oxide based catalyst with the alcohol before introducing the catalyst into the reactor.


Generally, the molar ratio of alcohol to chromium ranges between 0.1:1 and 5:1.


Preferably, the molar ratio of alcohol to chromium ranges between 0.1:1 and 3:1.


Generally, the amount of chromium in the final catalyst ranges between 0.2 and 5% by weight, more preferably ranges between 0.3 and 2% by weight.


Generally, the catalyst drying temperature is within the range of 20-60° C.


The titanium in the catalyst will be present in an amount sufficient to increase the melt index ratio of the polymer produced. Generally, the titanium content of the catalyst can be in the range of from 0.1 to 10 weight percent, preferably in the range of from 0.1 to 6 weight percent.


The polymerization may be performed via a gas phase process or via a slurry process.


The process according to the invention may be applied for ethylene polymerization to medium and high density polyethylene and copolymers of ethylene with alpha-olefins having about 3 to 18 carbon atoms. The produced polyethylene may be HDPE and LLDPE.


The obtained HDPE is suitable to be applied in the production of large-part blow molded articles, for example drums and jerry cans and high molecular weight film applications.


U.S. Pat. No. 4,559,394 discloses a catalyst produced by contacting an activated silica-titania supported chromium composition with a tertiary alcohol and thereafter reactivating under relatively mild conditions. The catalyst offers the advantage of allowing polymerization at a lower reactor temperature to achieve a given melt flow.


U.S. Pat. No. 5,965,675 discloses a polymerization process using a chromium/titanium-containing catalyst and a taming agent selected from the group consisting of water, alcohols, aldehydes, ketones, esters, and organic acids and preferably ethanol, water or ethylacetate. The process is especially suitable for the production of polyethylene resins suitable for blow molding use. A disadvantage of this process is the lower productivity in the case that the taming agent is applied.


WO0218046 discloses a supported chromium catalyst system comprising reaction a chromium catalyst precursor with a functionalized support in a solvent to bind said chromium catalyst precursor to a functionalized support via at least one heteroatom attached to said support via an organic group. The support materials are acrylate polymer particles or styrene divinyl benzene polymer particles. Suitable examples of these polymer based supports, include p-hydroxymethylstyrene-co-divinylbenzene polymer, p-(1,2-dihydroxyethyl) styrene-co-styrene-co-divinylbenzene polymer and p-vinylphenol-co-styrene-co-divinylbenzene copolymer. Suitable chromium precursors are trisallyl-chromium, tris-(2-methylallyl) chromium or (Ph3SiO)2CrO2. In contrast to WO0218046 in the present invention the preferred support is silica support and a chromium precursor (for example, chromium acetate or chromium acetyl acetonate) is mixed with the silica support, then chromium/silica mixture is calcined/activated at high temperature (700° C. and above) in the presence of a dry air. The next step is the treatment of silica supported activated CrOx catalyst with an alcohol. In WO0218046 chromium is bond to the polymeric support via an organic group, while in the present invention chromium is bond to silica support directly.


The invention will be elucidated by means of the following non-limiting examples.







EXAMPLES

The properties of the polymers produced in the Examples were determined as follows:


The high load melt index (HLMI) is determined using the procedures of ASTM D-1238 Condition F using a load of 21.6 kg at a temperature of 190° C.


Bulk density was measured according to ASTM D-1895.


Polymer molecular weight and its distribution (MWD) were determined by Polymer Labs 220 gel permeation chromatograph (GPC). The chromatograms were run at 150° C. using 1,2,4-trichlorobenzene as the solvent with a flow rate of 0.9 ml/min. A refractive index detector is used to collect the signal for molecular weights. The software used is Cirrus from PolyLab for molecular weights from GPC. The calibration of the HT-GPC uses a Hamielec type calibration with broad standard and fresh calibration with each sample set.


Example I and Comparative Examples A-C Catalyst preparation
Comparative Example A

A silica supported chromium oxide based catalyst having

    • 0.38 wt % of chromium (chromium containing precursor is chromium (III) acetylacetonate),
    • 3.8 wt % of titanium (titanium containing precursor is titanium(IV isopropoxide),
    • a surface area of 300 m2/g and
    • a pore volume of 1.5 cm3/g.


was activated in an atmosphere of dry air at a temperature of 825° C. for 3 hours using a tube furnace. The orange catalyst obtained indicates the presence of hexavalent chromium atoms.


Example I

1 gram of previously activated catalyst according to Comparative Example A was placed in a 40 cm3 flask. 10 cm3 of isopentane was added to slurry the activated catalyst, then a 1M isopentane solution of cyclohexanol was added to the flask and the resultant mixture agitated. It then stood for 60 minutes at a temperature of 25° C. The slurry was dried under vacuum or using a nitrogen purge at a temperature of 25° C. The modified catalyst was stored under nitrogen until use. The catalyst was pale green in color. The mole ratio of cyclohexanol to chromium was 1:1.


Comparative Example B

The catalyst was prepared in the same manner as that in Example I except that cyclohexanone was applied instead of cyclohexanol. The catalyst was yellow-orange in color.


Comparative Example C

The catalyst was prepared according to the process in Example I except that t-butyl alcohol was applied instead of cyclohexanol. The catalyst was yellow-orange in color.


Example II and Comparative Examples D-F
Ethylene Polymerisation

An autoclave with a volume of 2 liters was purged with nitrogen at 150° C. for 30 minutes. After cooling the autoclave to 90° C., one liter of isopentane was introduced to the reactor and then the reactor was pressurized up to 20 bar with ethylene. Then 0.1 ml of TEAL solution (1M) was injected into the reactor to scavenge the impurities, followed by 0.20 g of the solid catalyst as described in Table 1 after being slurried in 20 cm3 of isopentane. The reactor temperature was raised to 100° C. Ethylene polymerization was carried out for 1 hour or until terminated sooner, with ethylene supplied on demand to maintain the total reactor pressure at 20 bars. Upon completion of the polymerization, the reactor was vented and cooled to ambient temperature to recover the polymer.

















TABLE 1











Productivity






Color of
Time
Polymer
gPE/gcat.
B.D.
HLMI



Catalyst
catalyst
(min)
Yield g
1 hr
g/cc
g/10 min.























D
A
orange
60
340
1700
0.36
2.2


II
I
green
53
340
1925
0.38
1.5


E
B
yellow-
60
164
820
0.34
7.4




orange


F
C
yellow-
60
156
780
0.36
9.1




orange









The results in Table 1 show that the catalysts with cyclohexanol produce ethylene polymers having a high load melt index (HLMI) lower than the catalysts without cyclohexanol under similar reaction conditions. Cyclohexanone and t-butyl alcohol treated chromium oxide based catalysts produced ethylene polymers having much higher HLMI under similar reaction conditions.
















TABLE 2







Catalyst
Mw
Mn
MWD
Mz
Mz + 1






















D
A
229163
17713
13
1142678
2380560


II
I
264231
17288
15
1455630
2989662


E
B
195581
14100
13.8
898309
1704393


F
C
177187
12832
13.8
881031
1736066









The results in Table 2 show that the catalyst used in the process according to the invention produces ethylene polymer having higher molecular weight, as well as higher Mz and Mz+1 value.


In Table 1:

    • Mz and Mz+1 are higher average molecular weights
    • Mw: weight-average molecular weight
    • Mn: number-average molecular weight
    • MWD (molecular weight distribution) is the ratio of weight-average molecular weight


(Mw) to number-average molecular weight (Mn), i.e., Mw/Mn and used as a measure of the broadness of molecular weight distribution of a polymer.


wherein

    • Mw is related to strength properties (tensile, impact resistance).
    • Mn is related to brittleness, flow properties.
    • Mz is related to elongation and flexibility.
    • Mz+1 is related to die swell.


Comparative Example G

Comparative Example A was repeated without titanium.


A silica supported chromium oxide based catalyst having

    • 0.3 wt % of chromium,
    • a surface area of 300 m2/g and
    • a pore volume of 1.5 cm3/g.


was activated in an atmosphere of dry air at a temperature of 750° C. for 3 hours using a tube furnace. The orange catalyst obtained indicates the presence of hexavalent chromium atoms.


Examples III-IV

Comparative Example G was repeated with use of cyclohexanol as indicated in Table 3 to obtain catalysts III-IV.


Example II was repeated with use of the catalysts III-IV and Comparative Example G.















TABLE 3









Productiv-

HLMI


cata-

Color of
Alcohol/Cr
ity gPE/
B.D.
(g/10


lyst
Alcohol
catalyst
molar ratio
gcat · 1 hr
(g/cc)
min.)







G
untreated
yellow

610
0.33
0.75


III
cyclohexanol
green

1:1

740
0.32
0.67


IV
cyclohexanol
green
1.5:1
670
0.32
0.65









Table 4 shows that the addition of cyclohexanol increases the productivity of the catalyst and lowers HLMI of the gained resin in the absence of titanium as well.


Example V and Comparative Example F

A comparison between a catalyst comprising a chromium oxide on silica (Cr =0.4 wt %; Ti=2 wt %) and the same catalyst with the exception that the catalyst is treated with ethanol instead of cyclohexanol gives the results according to Table 4.













TABLE 4







Alcohol/Cr
Productivity
B.D.


Catalyst
Alcohol
molar ratio
gPE/gcat. 1 hr
(g/cc)




















untreated

1185
0.32



cyclohexanol
1:1 
1825
0.34



ethanol
1:1.
950
0.31









The results in Table 5 show that cyclohexanol treated chromium oxide catalyst has higher productivity compared to the untreated chromium oxide catalyst, while ethanol treated catalyst productivity is much lower compared to the untreated catalyst.

Claims
  • 1. A polymerization process for the production of high density polyethylene by polymerization of ethylene in the presence of a catalyst composition comprising a chromium compound, an alcohol and a support material characterised in that the alcohol is a primary alcohol having the formula:
  • 2. A process according to claim 1 characterised in that the catalyst composition additionally comprises a titanium compound.
  • 3. A process according to claim 1, characterised in that the alcohol is a secondary alcohol having the formula:
  • 4. A process according to claim 3 characterised in that the secondary alcohol is selected from 4-methyl-2-pentanol, 3-pentanol, 1,1-diphenylmethanol, and 1,1-diphenylethanol.
  • 5. A process according to claim 1 characterised in that the alcohol is selected from secondary cyclic alcohols having the formula:
  • 6. A process according to claim 5 characterised in that the secondary cyclic alcohol is selected from cyclohexanol, cyclopentanol, cycloheptanol and fluorenol.
  • 7. A process according to claim 1 characterised in that the primary alcohol is selected from cyclohexanemethanol, 2-ethylhexanol and 2,2-dimethylpropanol.
  • 8. A process according to claim 1 characterised in that the support material is silica support material.
  • 9. A process according to claim 1 characterised in that the chromium compound is selected from chromium acetate, chromium acetyl acetonate, chromium acetate hydroxide and chromium trioxide.
  • 10. A process according to claim 2 characterised in that the titanium compound is a titanium alkoxide.
  • 11. An article prepared using the products obtained with the process according to claim 1.
  • 12. A blow molded article prepared using the products obtained with the process according to claim 1.
  • 13. A process according to claim 5 characterised in that the catalyst composition additionally comprises a titanium compound.
  • 14. A process according to claim 5 characterised in that the support material is silica support material.
  • 15. A process according to claim 5 characterised in that the chromium compound is selected from chromium acetate, chromium acetyl acetonate, chromium acetate hydroxide and chromium trioxide.
  • 16. A process according to claim 13 characterised in that the titanium compound is a titanium alkoxide.
  • 17. An article prepared using the products obtained with the process according to claim 5.
  • 18. A blow molded article prepared using the products obtained with the process according to claim 5.
Priority Claims (1)
Number Date Country Kind
13001636.3 Mar 2013 EP regional
PCT Information
Filing Document Filing Date Country Kind
PCT/EP2014/056119 3/27/2014 WO 00