The present invention relates to an aerial article according to the preamble of claim 1. It also relates to a method for application of the coating according to claim 10.
The invention relates to the aircraft industry and to aircraft service maintenance. The invention is not limited thereto, but could also be related to activities of commercial airline companies as well.
Current aerodynamic technologies for aircraft wings, vertical/horizontal stabilizers etc., comprising aerial articles, such as leading edges, airfoils, fairings, are often manufactured of composite material. However, such airframes, wings, leading edges, etc. are lacking sufficient and effective erosion protection functionality that supports laminar airflow. This will result in turbulent airflow over the airfoil, increasing the fuel consumption of the aircraft. The current solutions comprise steps, gaps, uneven surfaces, fastener protrusions, etc. An eroded leading edge must be replaced or covered by erosion protection tapes for providing a smoother aerodynamic surface. In some cases metal plates are riveted onto the leading edge and rivet heads cause turbulent airflow over the airfoil.
Different types of protective coatings are used. Tapes or metal coatings can be adhered or adhesively bonded onto the leading edge. A problem with such solutions is that moisture trapped within the composite wing will after some time cause delamination or bond breakage of the adhered coatings. Also the use of known technique results in an unnecessary high weight of the airfoil.
Plastic articles and components could be coated with a thin layer of metal for different reasons. In the aircraft industry, such coatings are subject for ongoing development.
Modern aircraft skins are mainly made of said composites (fibres and cured resin interacting with each other). They are built with a technique partly different from traditional aircraft comprising aluminium skins. The object is to achieve an aircraft of lower weight than those of aluminum alloys. However, wings of aluminium are more resistant to rain erosion than wings made of composites. During use, aircraft are subject for intense temperature changes, freeze and thaw cycles. An aircraft encounters a large amount of water during its flight, such as rains, clouds, fog etc. The structural (and/or aerial) articles of the aircraft, such as airfoils, leading edges, etc., are also subjected to extreme condensation, wherein water condenses within the composite structure and being in some cases trapped within the interior. Furthermore, the aircraft also meets weather hazards such as lightning strikes, rain erosion etc. All these phenomena negatively affect the performance of the aircraft. Water trapped within the aerial structure makes the aircraft heavy. A lightning strike may damage the aerodynamic surface of the aircraft. Rain erosion damages the aerodynamic surface of the article so that turbulent airflow over the aerodynamic surface of the airfoil may occur, which increases the fuel consumption. Also moisture diffuses into the composite. Freezing and thawing out regularly of the composite material will thereby negatively affect the aerodynamic performance of a modern aircraft.
GB 833 675 discloses a metallic layer interleaved with insulating layers of composite for protecting the leading edge of a wing.
US 2012/0082556 discloses an airfoil made of a composite material. The airfoil is adapted for a gas turbine engine. A metallic coating is disposed on at least one portion of the airfoil's composite surface. The application of a metallic coating onto the composite shown in US 2012/0082556 solves the problem how to provide a durable adhesion between the composite and the metal covering of the leading edge. The solution presented provides a metallic coating of nanocrystalline metal.
WO 2009/046084 discloses a metal coating applied over an airfoil of composite material for forming a lighting protection system aiming to improve reliability of current systems.
The object of the present invention is to provide an effective way of keeping the low weight of the aircraft, at the same time as the durability is high.
The object of the present invention is also to provide an aerial article that is cost-effective to use, having a low service cost for maintaining the erosion protection.
At the same time is it desirable to provide an aerial article, which can be used under extreme conditions, such as moisture diffusion (where moisture diffuses in the cured resin structure/composite of the structure), and which also can be used for meeting weather hazards such as lightning strikes, rain erosion etc., still providing a low fuel consumption of the aircraft.
The objective is thus to provide an aerial article, which comprises an erosion protective coating saving weight and fuel.
The object is thus to provide an aerial article, which over time long time maintain its smooth aerodynamic surface for promoting a natural laminar flow.
This has been achieved by the aerial article defined in the introduction and being characterized by the features of the characterizing part of claim 1.
Suitably, the coating partly or entirely covers the composite skin, wherein the coating is of such continuous porosity or sufficient degree of porosity to form an open area (diffusion passage way) through the metallic coating so that moisture transportation is permitted from the composite skin to the aerodynamic surface of the coating, and of such low porosity that erosion protection of the composite skin still is achieved during said use.
Preferably, the coating is applied onto the composite skin over an area corresponding with the stagnation point of the leading edge, wherein the coating is of such high porosity that moisture transportation is permitted from the cured resin skin to the aerodynamic surface, and of such low porosity that erosion protection of the composite skin still is achieved during said use.
In such way is achieved that the moisture embedded within the composite can diffuse out from the composite skin without being trapped in the interface between the coating and the composite outer surface. The article can be used under extreme weather conditions at low temperatures and being subjected to ice crystals, hail and rain without any cavitation erosion from the latter. The article can at the same time be used under weather conditions where temperature shifts from low temperature to high temperature or, in case of using the article as a part of an aerial vehicle, where the temperature shifts from cold outer environment to warm outer environment due to descend of the aerial vehicle towards the earth surface. Such shift in temperature will result in a temperature difference between the outer environment and the interior of the article and where the interior is of lower temperature than outside, condense is due inside the article. At the same time as the article can be protected from erosion, the adhesion of the metal coating is guaranteed to be adhered to the composite skin over a long life time since no moisture would be trapped between the coating and the composite skin. Moisture trapped in the interface would otherwise affect the adherence properties negatively. The porosity of the coating permits the transportation of moisture from the interface to the outer atmosphere outside the article. The coating provides porosity and an open area of the composite promoting moisture transportation from the composite to the atmosphere at the same time as the aerodynamic surface of the leading edge is erosion protected.
Suitably, the thickness of the coating is between about 1 μm to 100 μm.
Alternatively, the thickness of the coating is between about 75 μm to 500 μm.
Suitably, the porosity of the coating is about 2% to 40%, preferably 4% to 20%, for permitting a moisture transmission from the composite skin to the outer atmosphere.
Water vapor transmission is thereby permitted, wherein the moisture (water) can be transferred by diffusion through the coating. Thus, an article is provided with an erosion protection that provides aerodynamic efficiency (providing and maintaining a smooth outer surface) over a long time and which can be used under extreme weather conditions where cold outer environment momentary prevails and eroding hails hit the leading edge. Also, an article is provided that prevents moisture damage to the article structural parts since the moisture being permitted to be transferred through the erosion resistant coating. It is extremely important that all water trapped within the interior of the article can diffuse and also moisture within the composite skin per se.
Preferably, the porosity of the coating is lower in areas meeting the airflow, than in areas where the article extension follows the airstream during said use.
This means that the coating covering the leading edge has a more dense porosity than the coating covering the airfoil's (wing's) upper and lower side. Suitably, the porosity of the coating is lowest within the area of the stagnation points. In such way is weight saved due to the use of optimal use of proper density (determined by porosity) of the coating, i.e. it is determined not to use dense coating at places of the wing, where the erosion is near non-existent. At the same time the adhesion of the coating to the plastic or resin (or composite) of the substrate will be durable since water is permitted to be transferred through the erosion-resistant coating of metallic material and water will not be trapped in the interface between coating and substrate.
Suitably, the coating excludingly is of a metallic material.
In such way is achieved an article aerodynamic surface that can be polished to an extreme smooth and hard surface. The leading edge easy can be manufactured with or without any recess in the outer surface of the composite skin. In case of no recess there is a possibility to apply the coating onto the leading edge wherein the coating's outermost edges are finished to the same level as the composite skin aerodynamic surface. In case of using recess in the leading edge for encompassing the coating, the recess depth should be of the same measure as the thickness of the coating.
Preferably, the thickness of the metallic coating is about 1-2 μm.
Suitably, the thickness of the metallic coating is about 1-10 μm or thicker.
Preferably, the metal is titanium or aluminium or nickel.
In such way is achieved that a cost-effective production of the article is possible at the same time as the article will be of low weight. Titanium or other metal is possible to polish to an extraordinarily smooth surface.
Suitably, the metal is copper.
In such way it will be possible to efficient use the article skin and coating of the aircraft (such as a wing) for lightning protection. This means that prior art lightning protective copper meshes bonded to the aerial structure outer surface are not necessary. The present embodiment of providing a metal (e.g. copper) coating of a wing is a cost-effective way to produce a lightning protection conductive layer which keeps the energy outside avionics, fuel systems etc. at the same time as moisture will not be trapped within the composite. A carbon fiber epoxy skin normally serves as an electrical insulator and the present coating will, not only provide the transmission/diffusion of moisture from the interface, but also provide an additional electrical conductivity to the outside of the skin. The coating is therefore durable in view of lightning.
Preferably, the coating is applied as a strip having a width covering an area of a leading edge extending between leading edge stagnation points of low angle of attack and leading edge stagnation points of high angle of attack.
In such way is provided that when the aircraft is flying with a high angle of attack (for example during final approach), the area corresponding with the stagnation point of low angle of attack will be positioned at the point where the airflow is sweeping over the leading edge on the wing suction side. As the erosion protective cover protects the composite from erosion in this area during low angle of attack, the aerodynamic surface will be kept smooth, which is aerodynamically efficient during said final approach. Furthermore, as also the stagnation point of high angle of attack is protected, the leading edge at pressure side of the wing (leading edge under side) will have a smooth aerodynamic surface (laminar airflow) when the aircraft is in level flight. All stagnation points between the high angle of attack and the low angle of attack are covered by the strip coating.
Suitably, the coating is applied as a strip having a width at least covering an area of the leading edge extending between the leading edge stagnation points of zero angle of attack and essentially a distance further chordwise of the leading edge stagnation points of high angle of attack.
In such way is achieved that the stagnation points of zero angle of attack during accelerating take-off action on runway or landing, will be protected from erosion, which means that this surface of the leading edge (upper side towards suction side of the wing) will be smooth (resulting in laminar air flow) during both level flight and final approach.
Preferably, the coating essentially extends over the entire article.
In such way is achieved an article having a skin that is resistant against accidental drop of tools by service personal. Preferably, the coating is applied within areas of the article, such as service hatches, control airfoil surfaces etc. In such way is achieved that the aerodynamic surface of a wing, or leading edge especially, can be protected from erosion. At the same time, the conductivity of the coating provided for incorporating the coating into a lightning protection system of an aircraft.
This is also solved by a method as claimed by claim 10.
Thereby is achieved a cost-effective production of erosion resistant coating providing a moisture transportation.
Preferably, the method comprises a step of providing a recess in the composite skin for accommodating the coating, the recess is provided by compressing a lay-up against a forming surface of a forming tool, which surface exhibits a film or other protruding section.
Suitably, the coating is applied so that the outermost portion of the coating, adjacent the outer surface of the coating (aerodynamic surface), exhibits more dense (packed) metal molecules (or grains) for reaching an erosion protective outer surface, but not so dense that moisture is hindered to evaporate or transmit through said outermost portion.
Suitably, at the same time (for saving weight) the inner portion of the coating may exhibit less dense (packed) metal molecules (or grains) for still reaching the moisture transmission property.
Preferably, the coating is provided over the leading edge.
Suitably, the parameters for achieving the metallic coating exhibiting the proper porosity are selected from sprayed material temperature, velocity of the material impacting the substrate surface, the angle of impact, and also such parameter as the quantity of gas contacts and reaction between the metallic material and said gases under the deposition process. The inventors of the present application have surprisingly noticed that high-velocity of the atomized metallic material will produce upon impact flattened or flake formed metal particles or grains of extremely small size, the flake formed particles will give a thin layer property saving weight and the process parameters are set so that the coating properties are altered towards a well-defined pre-determined porosity of the metal coating.
Alternatively, the step of providing the erosion resistant coating material exhibiting said predetermined porosity is performed simultaneously with the step of applying the material onto the composite skin.
In such way is achieved that a method of spraying the article at the same time as the porosity properties are determined depending upon which outer surface portion of the article being sprayed, leading edge, trailing edge, stagnation points, suction side of wing, pressure side of wing, rudder fastening areas for lightning protection, etc. The leading edge is preferably coated with Al, Ti, MMC etc. by thermal spray coating or flame spraying.
Preferably, a finishing step of finishing the composite substrate surface is made before the step of applying the coating material. The finishing is preferably made by a surface treatment energizing the latter for satisfactory adhesion between the coating and substrate. By this means it is possible to keep the substrate temperature cool and unchanged and thereby no expansions of the substrate occur during the application.
Alternatively, the step of applying the material is made by thermal spray coating, such as plasma spray deposition.
Preferably, electro less plating is used for the application. The metal is in this case preferably nickel which is set with the proper porosity.
Suitably, the substrate surface is cleaned before application.
Preferably, the surface is thereafter subject for roughening for ensuring satisfactory bonding between the coating and the substrate.
Suitable, an area of the article not to be coated is masked.
Alternatively, a flame provider device is provided that melts a coating metallic material stock or metallic powder and thereafter atomized by a high-velocity gas-stream. The achieved well-defined porosity coating is finished for reaching a smooth aerodynamic surface. This can be made by grinding or polishing or by other means.
Suitably, the step of applying the material is made by vapor deposition, such as sputtering or sputtering deposition.
In such way an extreme thin metal coating can be achieved having the proper porosity, at the same time as it provides conductivity for lightning protection. In such case, it could be proper to use chromium, nickel, copper etc. or combinations of steel and other alloys.
Alternatively, the sputter deposition is made by means of a plasma application (e.g. bombardment) of the substrate to ensure a smooth aerodynamic surface.
Alternatively, plasma-based plating is used by accelerating ions from the plasma by a negative bias onto the substrate.
Suitably, a controlled potential release of bombarded gas provides the porosity percentage of the coating to about 2-40% porosity, preferably 10-30% porosity.
Preferably, the step of applying the material is made by ultra short pulsed laser deposition. In such way is used a technique that will be used in future more often for more industrial applications, such also for aircraft industry.
Alternatively, the step of applying the material onto the composite skin incorporates cold spray procedure for metal deposition.
Suitably, the application of the erosion resistant coating material is made by means of a portable applicator.
Thereby the aircraft already in service can be served in a cost-effective way and do not have to be demounted and transported to manufacture sites. In such way is achieved that in case the coating serves as a lightning protection system an eventual damage can be repaired by an adhesive exhibiting electrical conductive properties (by means of carbon nano tubes for example or other conductive nano filament structure added to e.g. epoxy system.
Alternatively, the applicator uses a portable vacuum chamber which is connected to the airframe. In such way is achieved a controllable environment surrounding the damage area.
Suitably, the coating is used separately or in combination on a surface of an aircraft serving as part of a lightning protection system, anti-icing/de-icing system or plasma generating system.
By using a metal having the same or similar thermal expansion properties as the plastic of the article, the aerodynamic surface can exhibit the proper smoothness over long time.
Suitably, a controlled potential release of bombarded gas of a plasma spray coating provides the porosity percentage of the coating to about 2-40% porosity, preferably 10-30% porosity.
Suitably, the parameters for achieving the metallic coating exhibiting the proper porosity are selected from sprayed material temperature, velocity of the material impacting the substrate surface, the angle of impact, and also such parameter as the quantity of gas contacts and reaction between the metallic material and said gases under the deposition process.
Alternatively, the porosity of the coating is lower in areas meeting the airflow, than in areas where the article extension follows the airstream during said use. This means that the coating covering the leading edge has a more dense porosity than the coating covering the airfoil of the wing's upper and lower side.
Suitably, the porosity of the coating is lowest within the area of the stagnation points. In such way is weight saved due to the use of optimal use of proper density (determined by porosity) of the coating, at the same time as the coating can be used for lightning protection of the article, de-icing/anti-icing and erosion protection at the same time.
Preferably, cavities of the coating (exhibiting the porosity) are filled with cured resin for achieving a smooth aerodynamic surface. Eventual moisture will diffuse, not only through the composite, but also through the cured resin of the cavities.
By experiments performed by the applicant the porosity percentage of the coating is suitably set to about 2-40% porosity, preferably 10-30% porosity. This will provide sufficient open areas of the composite facing the atmosphere for moisture transmission to the atmosphere, but still sufficient dense erosion protection coating for achieving natural laminar flow for long-life use of the aircraft.
The present invention will now be described by way of examples with references to the accompanying schematic drawings, of which:
a illustrates a leading edge of a wing comprising an erosion resistant coating;
b shows a transition area between the coating and the outer surface;
c shows another embodiment, where the composite skin comprises a recess;
d-1e illustrate method embodiments to provide a recess for the coating;
a-2b illustrate a coating according to further embodiment;
a illustrates a closer view of a porous coating of a composite skin laminate;
b illustrates a leading edge of a vertical stabilizer;
a-6b illustrate a method of applying an erosion resistant coating;
Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings, wherein for the sake of clarity and understanding of the invention some details of no importance are deleted from the drawings.
a schematically illustrates a leading edge 1 of a wing 3. The leading edge 1 comprises a composite skin 5. During use of the leading edge 1, the airflow a divides into an upper (suction) and lower (pressure) airflow streaming around the wing 3. The point where the airflow a impacts the leading edge 1 is called the stagnation point SP. Of course, there will be an indefinite number of stagnation points SP along the leading edge 1 following an imaginary line intersecting with the line of stagnation points SP.
The airflow will swirl at stagnation points and prior art aerodynamic surface of the leading edge at this point is critical in view of erosion during flight.
The
b schematically shows a transition area 15 between the coating 7 and the outer surface 13 of the composite skin 5. The transition area 15 comprises an end portion 17 of the coating 7 being polished to a smooth and level surface, which end portion 17 becomes thinner and thinner in a direction towards the exposed outer surface 13 of the composite skin 5. In such way no steps appear in the aerodynamic surface, which steps otherwise would produce turbulence.
d schematically illustrates a method for providing a recess for a thin metallic foil (thickness of 20 μm) recess (not shown) for application of a foil (not shown) onto a laminate (lay-up 77 of pre-pregs 78 being cured) of a leading edge. A forming tool 70 is provided with a forming surface 72. The forming surface 72 is arranged with a protruding section 74 corresponding with the position of the foil onto the leading edge, which foil is to be applied onto the laminate. The forming surface 72 exhibits a protrusion thickness 76 (20 μm) corresponding with the thickness of the foil. The lay-up 77 of pre-pregs 78 being applied onto the forming surface 72. The lay-up 77 is compressed and cured in the forming tool 70. The protruding section 74 will form the recess due to the compression. The formed surface of the finished composite laminate thus will exhibit a recess of 20 μm depth. This promotes a cost-effective production of leading edges, as all articles formed and cured by the forming tool 70 will have the appropriate recess corresponding with the thickness of the foil. Thereafter, the foil is adhered to the recess of the laminate by means of an adhesive.
e schematically illustrates a method for providing a coating (not shown) (cold sprayed onto the laminate of the leading edge) in a recess (not shown) of the laminate. In this embodiment the lay-up 77 is provided with a film 80 having a thickness t corresponding with the coating (10 μm). The film 80 will make an impression (corresponding with the recess) in the laminate 71 corresponding with the thickness of the film 80 when the lay-up 77 is compressed. The film 80 is provided with a release agent (not shown) so that it efficiently can be released from the laminate recess after curing. Thereafter the coating is sprayed in the recess. The forming tool 70 will efficient be modified to other coating thicknesses and coating extensions of the leading edge, as only the film 80 has to be exchanged in the forming tool so that the film corresponds with the desired thickness and extension.
a schematically illustrates a coating 7 according to another embodiment. The porosity of the coating is about 2% to 40%, preferably 4% to 20%, for permitting a moisture transmission MT from the interior of the aerial article 23 to the outer atmosphere OA via an open area of the composite where the coating (e.g. of the leading edge) is positioned. The open area of the composite thus faces the atmosphere (i.e. the composite area below the coating, which area due to the porosity of the coating is open to and exposed to the atmosphere) and is achieved by the said porosity of the coating. Moisture transmission is thereby permitted, wherein the moisture can be transferred by diffusion through the coating 7 at the same time as the porosity is selected such that erosion protection is achieved. In this embodiment (see also
a schematically illustrates a closer view of the composite skin 5 laminate of an airfoil 4 serving as an aerodynamic surface when the airfoil 4 is used. The laminate comprises a plurality of plies P1, P2, P3 etc. stacked onto each other. Each ply P1, P2, P3 etc. comprises a carbon fiber structure 27 differently oriented than fibers of other plies. A recess 21 is made in the outermost ply P1 and a coating 5 is applied to the recess 21. The recess 21 is positioned at the airfoil 4 in a position corresponding with the position of the stagnation point SP of the airfoil 4 leading edge 1 during level flight and is made along the leading edge. In this example, the coating 7 is relatively thick, about 1 mm, and the recess 21 is provided by just leaving out a portion of the outermost ply P1 in the actual area. The surrounding areas of the composite skin surrounding the recess 21 are masked and the coating 7 is applied by means of painting. The coating 7 comprises low weight titanium. The porosity of the coating 7 is about 20-30%. The inner portion 33 of the coating 7 comprises about 30% porosity, which being illustrated by means of cavities 29 which have larger total volume than the outer portion 31 of the coating 7. The cavities 29 are filled with cured resin for achieving a smooth aerodynamic surface.
a schematically illustrates a method of applying an erosion resistant coating 7 to a composite skin 5 of a wing. The coating 7 comprises a metallic material. The method includes the use of a portable spray nozzle 46 adapted to spray the material along the curvature of the airfoil and at a predetermined distance. The method for applying said material onto the composite skin is made by cold spray procedure. It is achieved by providing the erosion resistant coating material 45 in such way that it, when it has hardened on the composite skin 5, exhibits a predetermined porosity such that a moisture transportation during said use is possible from the composite skin 5 to the outer surface 9 of the coating 7, but still providing an erosion protection of the latter. The method according to this embodiment also comprises the step of applying the erosion resistant coating material 45 onto the composite skin 5 over a selected area of the article, in this case over the leading edge 1. Finally, the outer surface 9 of the coating 7 is polished (not shown), so that a smooth aerodynamic surface being achieved. Thereby is achieved a cost-effective production of erosion resistant coating 7 permitting a moisture transportation there through. In
In
The coating material is MMC (metal matrix composite). The coating 7 is bond to the outermost surface of a composite skin 5 of a wing 3. The laminate comprises several fiber reinforced cured resin plies P. The outermost surface of the laminate comprises a nano filament structure NF for reaching an extreme hardness of the aerodynamic surface. During use, the wing 3 meets the airflow a. Particles, such as dirt 61 in rain drops of the air, hit the wing 3, especially in the area of the leading edge 1. The coating 7 protects the airfoil from rain erosion in the outermost section OS of the leading edge 1, where the airflow a swirls. In this example, the coating 7 is applied thicker in the critical area of the leading edge 1, i.e. where the stagnation points SP are positioned at level flight. Transmission of moisture is permitted from the composite skin both in coated areas 7 (T″) and in areas without coating (T′).
The present invention is of course not in any way restricted to the preferred embodiments described above, but many possibilities to modifications, or combinations of the described embodiments, thereof should be apparent to a person with ordinary skill in the art without departing from the basic idea of the invention as defined in the appended claims. The recess of the composite skin of the leading edge can be achieved by machining, polishing, leaving out pre-preg tape in outermost ply, providing the forming and curing tool with a protrusion corresponding with the desired recess. Alternatively, if the coating thickness is about 1 μm or less, no recess is necessary. Alternatively, a foil or film, which exhibits the corresponding thickness as the coating, can be applied side by side/adjacent the coating and joining the latter for reaching a continuous curvature of the aerodynamic surface. The porosity of the coating is about 2% to 40%, preferably 4% to 20%, for permitting a moisture transmission from the interior of the aerial article to the outer atmosphere via an open area of the composite where the coating (e.g. of the leading edge) is positioned. The open area of the composite thus faces the atmosphere (i. e. the composite area below the coating, which area due to the porosity of the coating is open to and exposed to the atmosphere) and is achieved by the said porosity of the coating. Moisture transmission is thereby permitted, wherein the moisture can be transferred by diffusion through the coating at the same time as the porosity is selected such that erosion protection is achieved. Composite is defined as cured resin (plastic) comprising reinforcement fibers.