Patent Grant
10403436
This application claims the benefit of priority to Korean Patent Application No. 10-2016-0173764, filed on Dec. 19, 2016 in the Korean Intellectual Property Office, the disclosure of which is incorporated herein by reference in its entirety.
The present disclosure relates to an acrylic binder and a multilayer electronic component manufactured using the same, in which the acrylic binder may be an acrylic copolymer-graphene binder and the multilayer electronic component may be a multilayer ceramic capacitor (MLCC).
Generally, ceramic electronic components using a ceramic material, such as a capacitor, an inductor, a piezoelectric element, a varistor, or a thermistor may include a ceramic body formed of the ceramic material, an internal electrode formed in the ceramic body, and an external electrode installed on a surface of the ceramic body to be connected to the internal electrode.
Among the ceramic electronic components, a multilayer ceramic capacitor includes a plurality of dielectric layers that are stacked, internal electrodes aligned, having dielectric layers interposed therebetween, and external electrodes electrically connected to the internal electrodes.
According to Korean Patent Laid-Open Publication No. 10-2011-007797, to provide an MLCC having excellent reliability, in which the occurrence rate of cracking and blistering is low, at least one of the internal electrodes includes oxide containing Ni, but a dielectric sheet on which an internal electrode is printed is still at an ordinary technical level.
An aspect of the present disclosure may provide a multilayer electronic component having excellent mechanical properties and a thin thickness and an acrylic binder capable of implementing the multilayer electronic component having the above properties.
According to an aspect of the present disclosure, a multilayer electronic component includes: a body having a stacked structure in which a plurality of internal electrodes and dielectric layers are alternately stacked and external electrodes disposed on an outer surface of the body and connected to the internal electrodes. The dielectric layer includes a plurality of grains and graphene particles disposed at a boundary of the plurality of grains.
According to another aspect of the present disclosure, an acrylic binder may include an acrylic copolymer-graphene composite.
According to another aspect of the present disclosure, a dielectric material includes a plurality of grains and a composite including an acrylic copolymer and graphene particles.
The above and other aspects, features, and advantages of the present disclosure will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawings, in which:
Hereinafter, exemplary embodiments of the present disclosure will now be described in detail with reference to the accompanying drawings.
Hereinafter, the multilayer electronic component and the acrylic binder according to exemplary embodiments in the present disclosure will be described, but the exemplary embodiments of the present disclosure are not limited thereto.
Multilayer Electronic Component
Referring to
The first and second external electrodes 21 and 22 are respectively electrically connected to first and second internal electrodes 11a and 11b disposed in the body to configure a capacitor circuit. The conductive material contained in the first and second external electrodes is not particularly limited, but may include nickel (Ni), copper (Cu), and alloys thereof.
The body 1 may form the overall appearance of the multilayer electronic component and may have substantially a hexahedral shape, including an upper surface and a lower surface facing each other in a thickness direction T, a first end surface and a second end surface facing each other in a direction of a length L, and a first end surface and a second end surface facing each other in a width (W) direction, but is not limited thereto. Here, the thickness (T) direction means a stacking direction.
The body 1 may have a structure in which a plurality of internal electrodes 11a and 11b and a plurality of dielectric layers 12 may be alternately stacked along the stacking direction.
The internal electrodes 11a and 11b are formed of a conductive material but the material of the internal electrodes 11a and 11b may not be particularly limited. For example, the material of the internal electrodes 11a and 11b may include silver (Ag), nickel (Ni), copper (Cu), palladium (Pd), a silver-palladium (Ag—Pd) alloy, a gold (Au) alloy, and the like.
A thickness of the internal electrode may be properly set according to the purpose. The thickness of the internal electrode may be within a range from 100 nm to 600 nm. If the thickness of the internal electrode is within the above range, it may be advantageous to prevent the deterioration in the internal electrode and miniaturize the chip while having appropriate mechanical strength.
The internal electrode may be disposed on the upper surface of the dielectric layer 12 that includes a material having dielectric properties. In this case, as the material having the dielectric properties, a ceramic material may be preferably used.
Specifically, the dielectric layer 12 may include a perovskite type compound including Ba and Ti. In general, the perovskite type compound may be represented by the general formula AyBO3 (A: A site element, B: B site element, O: oxygen, y: ratio of A site element/B site element) of the crystal structure. For example, the dielectric layer may include BaTiO3.
The dielectric layer 12 may include Ca, Zr, Mn, and the like, in addition to Ba and Ti. In addition, the dielectric layer 12 may also include a rare earth element RE as a subcomponent.
The dielectric layer 12 may include dielectric grains 12a included in the dielectric layer by sintering, and an average particle size of the dielectric grains may be within a range from 30 nm to 200 nm. If the average particle size of the dielectric grain is smaller than 30 nm, it is difficult to realize a sufficient dielectric constant and if the dielectric particle size is larger than 200 nm, DC bias characteristics may be poor and an IR deterioration phenomenon may occur.
A shape of a dielectric grain 12a in the dielectric layer may mostly have a hexagonal cross section, but is not limited thereto.
A thickness of each of the dielectric layers 12 may be within a range from 100 nm to 1000 nm. If the thickness of each of the dielectric layers 12 is smaller than 100 nm, when a voltage is applied to the multilayer electronic component, an excessive electric field may be applied to the multilayer electronic component and thus an insulation resistance of the multilayer electronic component may deteriorate, such that the multilayer electronic component may not properly work as a capacitor and if the thickness of each of the dielectric layers 12 is larger than 1000 nm, the capacitance of the capacitor per unit area may be reduced, such that it may be difficult to implement the high capacity capacitor.
The dielectric layer 12 may include the dielectric grains 12a and graphene particles 12b.
The graphene particles 12b may be disposed at boundaries between the dielectric grains 12a. Here, the fact that the graphene particles are disposed at the boundary of the dielectric grains may mean that the graphene particles are disposed on an interface at which separate dielectric grains adjacent to each other are distinguished.
The graphene particles 12b may be included only in the dielectric layer and may not penetrate into the inside of the internal electrode disposed on the dielectric layer. Further, depending on the product, the graphene particles may be placed on a boundary line between the dielectric layer and the internal electrode. However, this may mean that the graphene particles are not placed inside the internal electrode but placed at the boundary of the dielectric grains.
The shape of the graphene particle 12b may have a plate shape or a ribbon shape. It is to be understood that the plate shape collectively refers to a structure capable of distinguishing between a major axis and a minor axis, and the ribbon shape generally refers to a long string shape.
The graphene particles 12b may be irregularly dispersed in the respective dielectric layers.
This is similar to the case where the graphene particles are discontinuously placed with other adjacent graphene particles.
The content of the graphene particles 12b may be within a range from 100 ppm to 5000 ppm based on the number of dielectric grains having a particle size of 50 nm or more in the dielectric layer. If the content of the graphene particles is less than 100 ppm, the mechanical properties such as tensile strength or elongation of the dielectric layer may be inadequate and thus the case where the dielectric layer includes the graphene particles may be little distinguished from the case where the dielectric layer does not include the graphene particles. When the content of the graphene particles is greater than 5000 ppm, however, an interlayer electrical connection path of the internal electrode may be generated because the graphene is a conductive material and thus a short circuit may occur.
On the other hand, residual carbon material derived from a PVB-based binder may not be included in the dielectric layer 12 at all. In general, if the dielectric layer is formed in a multilayer ceramic capacitor, the PVB-based binder may be mostly used. The reason is that the PVB-based binder serves to prevent a dielectric sheet from being torn because it has strength above a certain level when the dielectric sheet is molded into a PET film and then peeled off. However, the PVB-based binder may increase the amount of residual carbon in the final chip after the firing process.
However, the multilayer electronic component according to an exemplary embodiment in the present disclosure may not include the residual carbon derived from the PVB-based binder generally included in the dielectric layer at all. The reason is that when the dielectric layer is manufactured, the PVB-based binder is not used but the acrylic binder to be described below is used. In particular, since the acrylic binder forms a complex of graphene remaining in the dielectric layer together with an acrylic copolymer, it is possible to sufficiently secure the mechanical strength while significantly reducing the amount of residual carbon.
However, it is impossible to know the source of residual carbon in the dielectric layer and it is possible to indirectly deduce that the PVB-based binder is not used based on the significant decrease in the amount of residual carbon in the dielectric layer. Specifically, it may be seen that the amount of residual carbon is significantly reduced, based on 0.1 wt % or more and 10 wt % or less of carbon with respect to the entire content in the respective dielectric layers. In this case, although the amount of residual carbon tends to increase with an increase in the content of the dielectric material included to form the dielectric layer, for example, barium titanate, it may be preferable that the amount of residual carbon does not exceed 10 wt %, based on a total weight of the dielectric layer.
Hereinafter, the acrylic binder according to another exemplary embodiment in the present disclosure will be described in detail, using a simple process for manufacturing the above-described multilayer electronic component 100.
Acrylic Binder
An acrylic binder according to another exemplary embodiment in the present disclosure may include an acrylic copolymer-graphene composite.
The acrylic copolymer included in the acrylic copolymer-graphene composite may have the structure of
Referring to
A single composite may be provided by bonding the acrylic copolymer of
In the complex, the acrylic copolymer and graphene may undergo chemical and physical interactions such as hydrogen bonding and nucleophilic reaction to form the single composite.
Referring to
The body may be individually manufactured by printing the internal electrode on the ceramic green sheet 200 and alternately laminating a plurality of ceramic green sheets and internal electrodes and then performing the firing and the dicing thereon.
In this case, the body has a structure including the graphene included in the acrylic binder together with the material having the dielectric properties included in the ceramic green sheet. It may be preferable that the body does not include the material derived from the acrylic copolymer contained in the acrylic binder, which means that the body does not include unnecessary residues derived from the acrylic binder, for example, residual carbon or the like.
Then, as the operation of disposing an external electrode on an outer surface of the body, the typical external electrode forming operation, for example, dipping or the like, may be applied to complete the final multilayer electronic component.
The multilayer electronic component manufactured using the acrylic binder described above may have excellent mechanical and electrical properties because the amount of residual carbon is greatly reduced due to the use of a binder having a low thermal decomposition temperature and a fast decomposition rate. At the same time, the multilayer electronic component may greatly improve the mechanical strength by including the graphene particles derived from the acrylic binder in the dielectric layer and have a high dielectric constant due to the effect of the dielectric polarization or the thinness of the dielectric layer.
As set forth above, it is possible to provide a multilayer electronic component capable of simultaneously implementing the miniaturization and the improvement in reliability while implementing the high dielectric constant by increasing the polarization of the dielectric layer.
While exemplary embodiments have been shown and described above, it will be apparent to those skilled in the art that modifications and variations could be made without departing from the scope of the present invention as defined by the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2016-0173764 | Dec 2016 | KR | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 9334386 | Alsharaeh | May 2016 | B2 |
| 20130135789 | Kim | May 2013 | A1 |
| 20130184143 | Corral | Jul 2013 | A1 |
| 20150053900 | Kim | Feb 2015 | A1 |
| 20160126014 | Lee | May 2016 | A1 |
| 20170229251 | Moon | Aug 2017 | A1 |
| Number | Date | Country |
|---|---|---|
| 105575664 | May 2016 | CN |
| 10-1994-0002878 | Feb 1994 | KR |
| 10-2011-0007797 | Jan 2011 | KR |
| 10-2014-0060070 | May 2014 | KR |
| 10-2015-0128743 | Nov 2015 | KR |
| 2014158970 | Oct 2014 | WO |
| 2016042419 | Mar 2016 | WO |
| Entry |
|---|
| First Office Action issued in Chinese Application No. 201711089546.9 dated Jul. 3, 2019, with English translation. |
| Number | Date | Country | |
|---|---|---|---|
| 20180174756 A1 | Jun 2018 | US |