Addition of an additive to a drag reducing latex formulation to improve injection.
The use of polyalpha-olefins or copolymers thereof to reduce the drag of a hydrocarbon flowing through a conduit, and hence the energy requirements for such fluid hydrocarbon transportation, is well known. These drag reducing agents or DRAs have taken various forms in the past, including slurries or dispersions of ground polymers to form free-flowing and pumpable mixtures in liquid media.
A stable DRA (drag reducing agent) suspension is generally comprised of (1) DRA polymer particles, (2) liquid carrier, and (3) suspension aids.
In general, the DRA polymer may be obtained from solution polymerization of a water-insoluble monomer or a mixture of monomers which are subsequently precipitated to form the solid polymer particles, or from bulk polymerization (i.e., polymerization with no solvent) of said monomer(s) to form polymer which is subsequently ground into particles (which grinding may tend to degrade the polymer and its drag reduction efficiency), or produced by emulsion polymerization whereby the monomer(s) are dispersed with a large quantity of surfactant in a continuous liquid carrier prior to polymerization. The subsequent emulsion polymerization produces extremely small particles of polymer from the dispersed monomer.
The liquid carrier is preferentially a non-solvent for the DRA polymer and can vary widely, including aqueous and non-aqueous liquids, e.g., water or aqueous solutions of various pH and ionic strengths, alcohols and fatty alcohols, glycols and diols, glycol ethers, glycol esters, or mixtures of these.
Suspension aids are a necessity for DRA polymer suspensions made from solution or bulk polymerization, since such polymer particles are soft and tacky and will form films, when their unaltered surfaces come in mutual contact. Many suspension aids may be employed, e.g., stearic acid and stearate salts (magnesium stearate, calcium stearate), stearamides, polyolefin homopolymers and copolymers of various densities; oxidized polyethylene (PE); polystyrene and copolymers; carbon black and graphites; micronized polyphenyl sulfide (PPS), polypropylene oxide (PPO), polyamides, polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polyvinyl chloride (PVC); precipitated and fumed silicas; natural or synthetic clays, and organo-clays; aluminum oxides; boric acid; magnesium, calcium and barium phosphates, sulfates, carbonates or oxides, and the like. Many such suspension aids require heating to reach maximum effectiveness in a formulation. However, heating a process stream is economically disadvantageous in commercial production.
One common solution to preventing film formation is to coat the ground polymer particles with an anti-agglomerating agent. Cryogenic grinding of the polymers to produce the particles prior to or simultaneously with coating with an anti-agglomerating agent has also been used. However, some powdered or particulate DRA slurries require special equipment for preparation, storage and injection into a conduit to ensure that the DRA is completely dissolved in the hydrocarbon stream.
Gel or solution DRAs have also been tried in the past. However, these drag reducing gels also demand specialized injection equipment, as well as pressurized delivery systems. They are also limited to a bout 10% polymer as a maximum concentration in a carrier fluid due to the high solution viscosity of these DRAs. Thus, transportation costs of the DRA is considerable, since up to about 90% of the volume is inert material.
Thus, it would be desirable if a drag reducing agent could be developed which rapidly dissolves in the flowing hydrocarbon, which could minimize or eliminate the need for special equipment for preparation and incorporation into the hydrocarbon, and which could be injected into a pipeline without any issues.
A composition comprising a drag reducing latex formulation produced by emulsion polymerization to create solid particles dispersed in an aqueous medium and an additive. The use of the composition results in a decrease of film formation while injected through a pump head when compared to the drag reducing latex formulation injected through the pump head.
In an alternate embodiment the composition comprises an acrylate drag reducing latex formulation produced by emulsion polymerization to create solid particles dispersed in an aqueous medium and an additive. In this embodiment the additive is added in the range between 1% to 20% by weight, and the composition results in a decrease of film formation of at least 50% when compared to the acrylate drag reducing latex formulation injected through the pump head through a four hour time frame.
A method is also taught wherein a composition is injected through a pump head wherein the composition produces at least 50% less film formation through a four hour time frame than injection of a drag reducing latex formulation through the pump head. In this method the composition comprises the drag reducing latex formulation produced by emulsion polymerization to create solid particles dispersed in an aqueous medium and an additive.
In an alternate embodiment a method is taught where a composition is injected through a pump head wherein the composition produces at least 50% less film formation through a four hour time frame than injection of a drag reducing latex formulation through the pump head. In this method the composition comprises the acrylate drag reducing latex formulation produced by emulsion polymerization to create solid particles dispersed in an aqueous medium and an additive added in the range between 1% to 20% by weight.
The invention, together with further advantages thereof, may best be understood by reference to the following description taken in conjunction with the accompanying drawings.
None
A composition comprises a drag reducing latex formulation produced by emulsion polymerization to create solid particles dispersed in an aqueous medium and an additive. The use of the composition results in a decrease of film formation while injected through a pump head when compared to the drag reducing latex formulation injected through the pump head.
In this embodiment the drag reducing latex formulation is any known drag reducing latex formulation that would create a film formation when injected through a pump head. The film formation on the pump head causes clogging of the pump head and an inability for the drag reducing latex formulation to be injected. The problem of film formation is particularly evident when utilizing latex drag reducing formulations for hydrocarbons. The problem is even more evident when using acrylate based drag reducing latex formulation. It is important to note that the drag reducing latex formulations decrease the drag of the hydrocarbon fluid they are injected into without significantly altering the viscosity of the hydrocarbon fluid.
The additive that is added to the drag reducing latex formulation is any additive that would cause the composition to result in a decrease of film formation of at least 10% when compared to the drag reducing latex formulation injected through the pump head through a four hour time frame. In alternate embodiment it has been shown that the decrease of film formation of the composition can range from 10%, 20%, 30%, 40%, 50%, 60%, 70%, 80% even 90% or higher over the drag reducing latex formulation injected through a similar pump head through a four hour time frame.
The pump head can be any pump head currently known in the art capable of injecting a drag reducing latex formulation. Commonly known pumps currently in use include packed reciprocating plunger pumps, high-pressure hydraulically actuated diaphragm pumps or even pneumatically driven plunger pumps.
In one embodiment the additive can be a single chemical additive or mixture of more than one chemical additive. The additive can be an ester derivative, which is capable of reducing film formation when injected through a pump head. In an alternate embodiment the additive is an ester derivative of a polyol or an ester derivative of a poly(carboxylic acids) or combinations of these ester deriviatives such that there is one or more ester functionality on the individual molecules. In one embodiment the additive is a 2,2,4-trimethyl-1,3-pentanediol diisobutyrate, bis(2ethylhexyl) adipate, glyceryl tributyrate, trimethyl pentanediol monoisobutyrate, dibutyl phthalate, dioctyl phthalate, glyceryl triacetate, dioctyl azelate, epoxidized tallate, triisooctyl trimellitate, triisononyl trimellite epoxidized soybean oil, dibutyl phthalate, butyl benzyl phthalate, dihexyl phthalate, C6-C11 phthalate, diisononyl phthalate, diisodecyl phthalate, ditridecyl phthalate or combinations of these additives. The additive can be added to the drag reducing latex formulation in the range between 1% to 8% or 1% to 10% or even 1% to 20% by weight. The upper limit of adding the additive to the drag reducing latex formulation is limited by the economics and the lowered efficiency of the drag reducing latex formulation as a whole due to the dilution of the active drag reducing latex formulation.
The addition of the additive to the drag reducing latex formulation is not dependent upon the method of manufacturing the drag reducing latex formulation. The additive can be incorporated prior to the reaction into the reagent mixture or it can be added and mixed into the drag reducing latex formulation as a post-additive.
In an alternate embodiment the composition comprises an acrylate drag reducing latex formulation produced by emulsion polymerization to create solid particles dispersed in an aqueous medium and an additive comprising 2,2,4-trimethyl-1,3-pentanediol diisobutyrate. In this embodiment the additive is added in the range between 1% to 8% by weight, and the composition results in a decrease of film formation of at least 50% when compared to the drag reducing latex formulation injected through the pump head through a four hour time frame.
A method is also taught wherein a composition is injected through a pump head wherein the composition produces at least 30% less film formation through a four hour time frame than injection of a drag reducing latex formulation through the pump head. In this method the composition comprises the drag reducing latex formulation produced by emulsion polymerization to create solid particles dispersed in an aqueous medium and an additive.
In an alternate embodiment a method is taught where a composition is injected through a pump head wherein the composition produces at least 30% less film formation through a four hour time frame than injection of a drag reducing latex formulation through the pump head. In this method the composition comprises the acrylate drag reducing latex formulation produced by emulsion polymerization to create solid particles dispersed in an aqueous medium and an additive of 2,2,4-trimethyl-1,3-pentanediol diisobutyrate added in the range between 1% to 8% by weight.
In this example a peristaltic pump is used to simulate the injection of drag reducing latex formulation through a pump head. In each of these examples a latex meth(acrylate) drag reducer was utilized. The rate of flow through the peristaltic pump was 40 cc/min over a time frame of four hours. The flex tubing of the peristaltic pump was weighed prior to the pumping and post pumping to determine the build up of film formation inside the flex tubing.
The preferred embodiment of the present invention has been disclosed and illustrated. However, the invention is intended to be as broad as defined in the claims below. Those skilled in the art may be able to study the preferred embodiments and identify other ways to practice the invention that are not exactly as described herein. It is the intent of the inventors that variations and equivalents of the invention are within the scope of the claims below and the description, abstract and drawings are not to be used to limit the scope of the invention.
This application is a non-provisional application which claims the benefit of and priority to U.S. Provisional Application Ser. No. 61/414,298 filed Nov. 16, 2010, entitled “Additives for Improving DRA Injection,” which is hereby incorporated by reference in its entirety.