Adhesive composition and method for bonding to rubber

Abstract
An adhesive composition of the present invention comprises (A) a conjugated diene polymer having a weight-average molecular weight of 500 to 100,000 and (B) an electron pair-donating basic compound; or comprises (A) A conjugated diene polymer having a weight-average molecular weight of 500 to 100,000, (C) a compound having in its molecule three or more functional groups selected from the group consisting of acryloyloxy group, methacryloyloxy group and groups represented by the following formula I: 1
Description


TECHNICAL FIELD

[0001] The present invention relates to an adhesive composition and a bonding method using the adhesive composition, and particularly, to an adhesive composition for rubbers, a method for bonding a rubber to an adherend via the adhesive composition by vulcanizing adhesion optionally after irradiating the adhesive composition with ultraviolet light, etc., a rubber-reinforcing material produced by the bonding method, and a rubber article using the rubber-reinforcing material.



BACKGROUND ART

[0002] Generally, rubbers have a high elongation and a low elastic modulus and have been practically made into composites with other materials such as plastics to make the best use of their properties. To produce such composites advantageously, a rubber and an adherend are integrally bonded by the vulcanization of the rubber, because such a method is easily and simply applicable even when the adhesive surface is geometrically complicated. To ensure an adhesion force, there are known various methods including the surface treatment of plastic adherends, the modification of components of adhesive composition, etc.


[0003] In conventional rubber bonding methods; using an adhesive composition, there have been extensively used solvent type adhesives comprising a rubber-containing adhesive composition and a solvent such as water and an organic solvent. The solvent is used to make the adhesive composition into liquid state, thereby ensuring a void-free coating of the adhesive composition on the adherend. To enhance the resistance to cohesive failure of the adhesive composition so as to prevent the adhesive joint from being broken by a stress such as dynamic strain, the solvent is frequently removed by evaporation, etc. in the adhesion step for hardening the adhesive layer. The adhesive composition requiring the removal of the solvent upon hardening the adhesive layer fails to utilize the solvent as an effective component after the adhesive-bonding, and often necessitates a solvent treatment for environmental protection. Therefore, the use of a solvent-free adhesive composition or an adhesive composition in which the solvent is incorporated into the adhesive layer in the adhesion step for hardening the adhesive composition is desired.


[0004] There has been conventionally known a bonding method using, as the adhesive composition of the above type, an adhesive composition containing a monomer that is polymerizable by the irradiation of radiation such as ultraviolet light, visible light and electron beam or by the application of external energy such as heat. In this method, the adhesive composition is in a liquid state when applied on the surface of adherend to thereby minimize adhesive defects due to voids, and the adhesive layer with a network cross-linked structure is formed by the polymerization of monomer in the adhesive-bonding treatment. Regarding the method of bonding rubber using the adhesive composition of this type, Japanese Patent Application Laid-Open No. 55-145768 (DE 2916909C) discloses that: a coating compound comprising at least one liquid hydrocarbon polymer having a double bond and (or), if required, at least one polyamine derivative is rapidly or completely made into network structure by the irradiation of ionizing radiation such as electron beam without external heating, thereby ensuring its good adhesion to a rubber substrate. It is further described in the document that: the coating compound may be applied to a completely vulcanized molded article and then made into network structure, or alternatively may be applied on a crude mixture not yet made into network structure and then made into network structure simultaneously with the crude mixture. The document proceeds that: in the latter treatment, if the vulcanization is conducted by the irradiation of electron beam, the use of sulfur as a vulcanizing agent and (or) a vulcanization accelerator for making the crude mixture into network structure can be omitted. The proposed method relates to making the rubber component and the adhesive composition into network structure to firmly bond onto rubber, and is characterized that the use of sulfur as a vulcanizing agent and (or) a vulcanization accelerator can be omitted in making the rubber and the adhesive composition into network structure. However, as a result of the studies on the adhesive composition and the bonding method of the present invention, the inventors have found that in the case of making the adhesive composition into network structure by the optional irradiation with irradiation such as ultraviolet light, visible light and electron beam, when the heating is made while bringing an unvulcanized rubber into press-contact with the adhesive composition, sulfur migrates from the rubber into the adhesive composition, thereby achieving a strong adhesion due to the sulfur-assisted cross-linking reaction.



DISCLOSURE OF INVENTION

[0005] In view of the above circumstances; an object of the present invention is to provide a novel adhesive composition capable of creating an excellent adhesion between a rubber and an adherend simultaneously with the vulcanization of the rubber, a bonding method using the adhesive composition, a rubber-reinforcing material having an improved adhesion between the rubber and the adherend, and a rubber article produced by using the rubber-reinforcing material.


[0006] As a result of extensive researches in view of the above object, the inventors have found that a strong and durable rubber-to-adherend adhesion is attained by coating the adherend with a specific adhesive composition, and vulcanizing an unvulcanized rubber while bringing it into press-contact with the adhesive composition optionally after irradiating the adhesive composition with ultraviolet light or radiation. The present invention has been accomplished on the basis of this finding.


[0007] Thus, the present invention provides an adhesive composition for rubbers comprising (A) a conjugated diene polymer having a weight-average molecular weight of 600 to 100,000 and (B) an electron pair-donating basic compound.


[0008] The present invention further provides an ultraviolet- or radiation-curable adhesive composition for rubbers comprising (A) a conjugated diene polymer having a weight-average molecular weight of 500 to 100,000, (C) a compound having in its molecule three or more functional groups selected from the group consisting of acryloyloxy group, methacryloyloxy group and terminal groups represented by the following formula I:
2


[0009] wherein R1 is C2-C5 alkylene group; R2 is hydrogen or C1-C2 alkyl group; and m is an integer of 0 to 5, and (D) a compound having in its molecule one or two groups selected from the group consisting of acryloyloxy group and methacryloyloxy group.


[0010] The present invention still further provides a method for bonding a rubber to an adherend via the adhesive composition mentioned above, comprising: coating at least a part of a surface of the adherend with the adhesive composition to form an adhesive layer, and vulcanizing an unvulcanized rubber while bringing it into press-contact with the adhesive layer, optionally after irradiating the adhesive layer with ultraviolet light or radiation.


[0011] The present invention still further provides a rubber-reinforcing material produced by the above method, and a rubber article particularly a tire reinforced by the rubber-reinforcing material.







BRIEF DESCRIPTION OF DRAWINGS

[0012]
FIG. 1 is a graph showing a heat-of-reaction curve as measured by a differential scanning calorimeter which shows accelerated vulcanization of methacrylated polybutadiene as a conjugated diene polymer by 4-vinylpyridine as an electron pair-donating basic compound.







BEST MODE FOR CARRYING OUT THE INVENTION

[0013] The first adhesive composition of the present invention comprises (A) a conjugated diene polymer having a weight-average molecular weight of 500 to 100,000 and (B) an electron pair-donating basic compound.


[0014] The upper limit of the weight-average molecular weight (Mw) of the component A is not particularly restricted unless the adhesive composition shows an excessively high viscosity and becomes difficult to be processed. However, when exceeding 100,000, the coating of the adhesive composition tends to be difficult. When the Mw is less than 500, a sufficient adhesiveness cannot be sometimes atained by the vulcanization of the press-contacted unvulcanized rubber. Considering the above, Mw is preferably 500 to 100,000.


[0015] The conjugated diene polymer as the component A may include conjugated diene homopolymers, conjugated diene copolymers and modified polymers or copolymers thereof. Examples of the conjugated diene monomers include 1,3-butadiene, isoprene and 1,3-hexadiene, with 1,3-butadiene being preferred. The conjugated diene copolymers are preferably conjugated diene-aromatic vinyl copolymers. The aromatic vinyl monomer may be styrene or α-methylstyrene, with styrene being preferred. The conjugated diene polymer preferably contains in its main molecular chain units containing a carbon-carbon double bond having hydrogen at its allyl position so as to provide sites capable of easily forming cross-link by the cross-linking reaction with sulfur. Examples of the conjugated diene polymers include polyisoprene, polybutadiene, styrene-butadiene copolymers and isoprene-butadiene copolymers. It is preferred for the conjugated diene polymer to be in a liquid state at a blending temperature for preparing the adhesive composition and particularly even at 0° C. or lower in view of good workability and easiness of the mixing step for preparing the adhesive composition. It is also preferred to be in a liquid state with a low vapor pressure even at 50° C. or higher. However, the liquid state of the conjugated diene polymer at the blending temperature is not critical as long as the conjugated diene polymer presents in a liquid state in the resultant adhesive composition.


[0016] Also usable are modified polymers produced by introducing functional groups having a radically-polymerizable unsaturated double bond into ends of the conjugated diene polymers. Examples of the functional groups include vinyl group, acryloyl group, methacryloyl group, acryloyloxy group, methacryloyloxy group and allyl group. Particularly preferred as the modified polymer are butadiene polymers having at their ends acryloyl group, methacryloyl group, acryloyloxy group or methacryloyloxy group. The modified polymers are available as commercial products or trade samples.


[0017] For example, acrylated polybutadienes produced by introducing acryloyl group (CH2═CHCO—) into the ends of butadiene polymers are available from Osaka Yuki Kagaku Kogyo, Co., Ltd. under the trademark “BAC45” (Mw of polybutadiene moiety: 2,800; viscosity: 3.4 Pa.s; saponification value: about 49). Also, methacrylated polybutadienes represented by the following formula:
3


[0018] are available from Ricon Resins Inc. under the trademarks “RIACRYL3100” (Mw: 5,100; number of methacryloyl(oxy) groups; 2/molecular chain), “RIACRYL3500” (Mw: 6,800; number of methacryloyl groups: 9/molecular chain) and “RIACRYL3801” (Mw: 3,200; number of methacryloyl(oxy) groups: 8/molecular chain).


[0019] The electron pair-donating basic compound as the component B: may include compounds containing nitrogen atom having a lone pair or compounds capable of producing compounds having a lone pair by thermal decomposition.


[0020] Examples of the compounds containing nitrogen atom having a lone pair include amine compounds such as (a) aromatic canines, (b) aldehyde amines, (c) guanidines, (d) thiouric acids, (e) heterocyclic amines and () polymerizable monomers having aliphatic amine residues or heterocyclic amine residues and further having a carbon-carbon double bond. The aromatic amines (a) may include amino-containing aromatic compounds such as aniline, m-phenylenediamine and 2,4-toluylenediamine. The aldehyde amines (b) may include n-butylaldehyde aniline. The guanidines (c) may include diphenylguanidine and di-o-tolylguanidine. The thiouric acids (d) may include thiocarbanilide, diethylthiourea and tetramethylthiourea. The heterocyclic amines (e) may include compounds having a nitrogen-containing heterocyclic ring such as pyridine and 2-methylimidazole. The polymerizable monomers (I) may include 2-vinylpyridine, 4-vinylpyridine, m-(N,N-dimethylamino)styrene, p-(N,N-dimethylamino)styrene, acrylamide, methacrylamide, N-methylacrylamide, N-isopropylacrylamide, N-n-butylacrylamide, N-n-octylacrylamide, N,N-dimethylacrylamide, 1-vinylimidazole, allylamine, 2,5-distyrylpyridine, 2-dimethylaminoethylmethacrylate, N-vinyl-2-pyrrolidone, 2-vinyl-2H-indazole, 4-diisopropylamino-1-butene, trans-2-butene-1,4-diamine, 2-vinyl-4,6-diamino-1,3,5-triazine, 4-methyl-5-vinylthiazole, N-vinylformamide, N,N-dimethylaminoethylacrylate, N,N-diethylaminopropylacrylamide, acryloylmorpholine, and N,N-diethylacrylamide.


[0021] In addition to the above compounds, also usable as the compounds containing nitrogen atom having a lone pair are (g) aliphatic amines and (h) amine compounds other than the compounds (a) to (g). Examples of the aliphatic noes (g) include aliphatic monoamines such as dibutylamine; diamines such s ethylenediamine; and high-molecular amines such as polyethylenepolyamine. Examples of the amine compounds on) other than the compounds (a) to (g) include substituted amine compounds having acrylated or methacrylated primary or secondary amino groups.


[0022] Of the compounds (a) to (h) containing nitrogen atom having a lone pair, preferred are the compounds (a) to (f), and more preferred are the compounds (e) and (f).


[0023] The compounds capable of producing compounds containing a structure having a lone pair by thermal decomposition are preferably known vulcanization accelerators, for example, disulfide compounds such as tetramethylthiuram disulfide. The compounds capable of producing compounds containing a structure having a lone pair by thermal decomposition are preferably decomposed upon vulcanization for adhesion at a vulcanization temperature of 130 to 180° C.


[0024] When vulcanizing the unvulcanized rubber while bringing it into press-contact with the adhesive lyaer which is formed by coating at least a part of the surface of the adherend with the adhesive composition, the sulfur in the unvulcanized rubber migrates into the adhesive layer to create a strong adhesion between the adherend and the rubber because of the co-vulcanization of the component A and the rubber component. The component B catalyzes the reaction between the unsaturated moieties of the component A and the sulfur migrating from the unvulcanized rubber. The vulcanization accelerating effect of the component B can be confirmed from the heat-of-reaction curve measured by a differential scanning calorimeter at a temperature rise rate of 5° C./min. A comparative composition comprising a mixture of 100 parts by weight of the component A and 3 parts by weight of sulfur (but containing no component B) shows no peak of reaction heat attributable to the vulcanization in a temperature range of 190° C. or lower of its heat-of-reaction curve. On the contrary, a mixture of 100 parts by weight of the adhesive composition of the present invention and 3 parts by woight of sulfur shows a peak of reaction heat attributable to the vulcanization in a temperature range of 190° C. or lower of its heat-of-reaction curve. At the reaction temperature of 190° C. or lower, the vulcanization generally proceeds dominantly by a ring opening reaction caused by the vulcanization accelerator or electron pair-donating base rather than by the radical vulcanization. In an adhesive composition containing a component having a relatively acidic end group such as (meth)acryloyl group, the electron pair-donating base is difficult to participate in the vulcanization. Therefore, the addition of the electron pair-donating base (component B) is required to facilitate the vulcanization.


[0025] The donating of electron pair from the electron pair-donating base (component B) to the sulfur-based vulcanizing agent such as cyclic sulfur S8 means occurrence of donor-acceptor interaction. Therefore, the amount of sulfur migrating from the unvulcanized rubber into the adhesive composition vanes depending upon the content of tho electron pair-donating base in the adhesive composition and its basicity against sulfur. In this regard, the inventors have found that the amount of migrating sulfur generally increases with increading amount of the electron pair-donating base and increasing basicity against sulfur. When the amount of sulfur distributed in the adhesive layer of the adhesive composition increases, the amount of sulfur present at a boundary between the adhesive layer and the rubber also increases to enhance the bonding by the sulfur vulcanization. Therefore, the addition of the electron pair-donating base (component B) is required to facilitate the migration of the vulcanizing agent into the adhesive composition.


[0026] The addition amount of the component B varies depending upon the electron pair-donating capability of the base, and is preferably 0.2 to 50 parts by weight based on 100 parts by weight of the component A. When less than 0.2 part by weight, the component B fails to show the vulcanization accelerating effect. When more than 50 parts by weight, physical properties of the adhesive composition are deteriorated because of excessive vulcanization.


[0027] The adhesive composition may optionally contain the following component C (30 to 80 parts by weight based on 100 parts by weight of the component A) and/or the component D (3 to 60 parts by weight based on 100 parts by weight of the component A).


[0028] The component (C) is a compound having, per one molecule, three or more, preferably 3 to 8 functional groups which is cross-linkable by the irradiation with ultraviolet light or radiation. Examples of the preferred functional groups include acryloyloxy group, methacryloyloxy group and functional groups represented by the formula I:
4


[0029] wherein R1 is C2-C5 alkylene group, preferably ethylene group or propylene group; R2 is hydrogen or C1-C3 alkyl group, preferably hydrogen or methyl group; m is an integer of 0 to 5, preferably 1 to 3, with the groups represented by the formula I being more preferred. Examples of the compounds having three or more acryloyloxy or methacryloyloxy groups include esters of a tri- or more valent polyhydric alcohol and acrylic or methacrylic acid. The polyhydric alcohol preferably used may be glycerol, trimethylolethane, trimethylolpropane, diglycerol, pentaerythritol and dipentaerythritol. The compounds having three or more functional groups represented by the formula I are commercially available and exemplified by pentaerythritol polyethoxyacrylate having the following formula:
5


[0030] wherein m x a=3 and a+b=3, available from Nippon Kayaku Co., Ltd. under the trademark “KAYARAD TPA-330”; pentaerythritol polypropoxyacrylate available from Nippon Kayaku Co., Ltd. under the trademarks “KAYARAD TPA-320” and “KAYARAD TPA-330”; dipentaerythritol polyacrylate available from Arakawa Kagaku Kogyo Co., Ltd. under the trademark “BEAMSET 700”; and pentaerythritol polyacrylate available from Arakawa Kagaku Kogyo Co., Ltd. under the trademark “BEAMSET 710.”


[0031] The component (D) serves as a viscosity modifier, and is preferably a mono- or di-functional liquid compound having one or two functional groups which is radically polymerizable by the irradiation of ultraviolet light or radiation, Of these compounds, preferred are polyoxyalkylene derivatives having one or two acryloyloxy or methacryloyloxy groups in one molecule. Such viscosity modifiers may be commercially available. Examples of the monofunctional compounds include phenoxypolyethylene glycol monoacrylate represented by the formula:
6


[0032] wherein n is 4, available from Shin-Nakamura Kagaku Kogyo Co., Ltd. under the trademarks “AMP-60G” and “APG-400”; tetrahydrofurfuryl monoacrylate available from SARTOMER Inc. under the trademark “SR-285”; and isooctyl monoacrylate available from SARTOMER Inc. under the trademark “SR-440.” Examples of the difunctional low-molecular compounds include polypropylene glycol diacrylate represented by the formula:
7


[0033] wherein m+n=7, available from Shin-Nakamura Kagaku Kogyo Co., Ltd. under the trademark “APG-400”; and polypropylene glycol dimethacrylate available from Shin-Nakamura Kagaku Kogyo Co., Ltd. under the trademark “9PG.”


[0034] The adhesive composition may also optionally contain an appropriate low-viscosity liquid having a racial reactivity according to processing requirements.


[0035] Further, the adhesive composition may optionally contain at least one additive selected from the group consisting of epoxy compounds, inorganic fillers and high-molecular fillers in a total amount of 10 to 40 parts by weight based on 100 parts by weight of the component A.


[0036] The epoxy compounds are cross-linked by heating to impart ductility and toughness to the adhesive composition. Examples thereof include novolak epoxy resins produced by epoxidating a condensate of a phenol compound and formaldehyde, and novolak phenol resins produced by introducing an epoxy or (meth)acrylic group into a condensate of a phenol compound and formaldehyde. Commercially available epoxy compounds are exemplified by epoxy novolak acrylate (trademark “ENA”) and novolak acrylate having epoxy and carboxyl groups (trademark “ENC”) which are available from Kagawa Chemical Co., Ltd.


[0037] The inorganic fillers and the high-molecular fillers are preferably added to reduce production costs of the adhesive composition, simultaneously with imparting ductility and toughness thereto. Examples of the inorganic fillers include clay, silica, talc, and carbon black. Commercially available clay is exemplified by montmorillonite clay available from NANOCOR INC. under the trademarks “Nanomer PGW”, “Nanomer PGA”, “Nanomer PGV” and “Nanomer PGN.” Examples of the high-molecular fillers include copolymers of isobutylene and maleic anhydride, modified polybutadienes, and modified acrylonitrile-butadiene copolymers. Commercially available high-molecular fillers are exemplified by copolymers of isobutylene and maleic anhydride available from Kuraray Co., Ltd. under the trademarks “ISOBAN 10”, “ISOBAN 04” and “ISOBAN 110”, amine-modified acrylonitrile-butadiene copolymer (trademark “HYCAR ATBN 1300×16”) and carboxyl-modified acrylonitrile-butadiene copolymer (trademark “HYCAR CTBN 1300×8”) available from Ube Industries, Ltd.


[0038] The second adhesive composition of the present invention comprises (A) a conjugated diene polymer having a weight-average molecular weight of 500 to 100,000, (C) a compound having in its colocule three or more functional groups cross-linkable by the irradiation of ultraviolet light or radiation, and (D) a viscosity modifier. The components A, C and D are the same as those mentioned above. Therefore, the details thereof are omitted here.


[0039] The blending amounts of the components A, C and D are not particularly restricted as long as a strong bonding force between the adherend and rubber is attained, and preferably 30 to 80 parts by weight for the components C and 3 to 60 parts by weight for the component D each based on 100 parts by weight of the component A.


[0040] The second adhesive composition may further contain at least one additive selected from the group consisting of epoxy compounds, inorganic fillers, high-molecular fillers and basic compounds in a total amount of 10 to 40 parts by weight based on 100 parts by weight of the component A. The epoxy compounds, inorganic fillers and high-molecular fillers may be selected from those optionally added to the first adhesive composition. Also, the basic compounds may be selected from those used as the component B in the first adhesive composition.


[0041] In addition, the second adhesive composition preferably contains a pbotoinitiator such as 2,4-diethylthioxanthone (for example, “KAYACURE DETX-S,” trademark, available from Nippon Kayaku Co., Ltd.) and isoamyl p-dimethylaminobenzoate (for example, “KAYACURE DMBI,” trademark available from Nippon Kayaku Co., Ltd.) in an amount of 0.1 to 10 parts by weight based on 100 parts by weight of the component A. Further, the second adhesive composition may contain sulfur (for example, powdery sulfur available from Karuizawa Seisakusho Co., Ltd,), a vulcanization accelerator (for example, mercaptobenzothiazole available from Flexys Inc. under the trademark “Perkacit MBT PDR-D”, and disulfide available from Akuzo Inc. under the trademark “Lucidol S-50”), or peroxide, each in an amount of 0.1 to 3 parts by weight based on 100 parts by weight of the component A.


[0042] The material of the adherend to be bonded to the rubber is not particularly restricted, and is preferably thermoplastic resin. Examples of the thermoplastic resins include polyamides, polyesters, polyolefins such as polypropylene and polyethylene, polycarbonates, polyacrylates, styrene resins such as ABS resin, and vinyl chloride resins. Of these thermoplastic resins, preferred are polyesters having a high mechanical strength which are not easily bonded to rubbers by ordinary methods. The plastic adherend to be used in the present invention may be in any form such as film, fibers, non-woven fabric, monofilament cord and multifilament cord, and may be extrued articles or injection-molded articles.


[0043] In the bonding method of the present invention, the adhesive composition is applied to at least a part of a surface of the adherend, for example, one surface of a sheet-like adherend, by immersion; brushing, casting, spraying, roll-coating, knife-coating, etc., to form a coating film. The surface of the adherend may be treated in advance by electron bean, microwave, corona discharge, plasma treatment, etc. The thickness of the adhesive composition layer is preferably 0.5 to 50 μm and more preferably 1 to 10 μm.


[0044] The adhesive composition layer is then irradiated with ultraviolet light or radiation. The radiation may include electron beam, gamma ray, etc., and may be irradiated by known methods. In general the exposure dose is 100 to 3,000 mJ/cm2 and the exposure time is 1 to 30 s for the ultraviolet light irradiation, and the exposure dose is 2 to 50 Mad and the exposure time is 0.5 to 30 s for the electron beam irradiation. The adhesive composition is hardened to some extent by the radical reaction induced by the irradiation. The irradiation of ultraviolet light or radiation can be omitted for the first adhesive composition. By heating at 140 to 190° C. for 10 to 30 min while bringing an unvulcanized rubber into press-contact with the adhesive composition layer under a pressure of 5 to 50 kgf/cm2, co-vulcanization reaction occurs between the base polymer (component A) of the adhesive composition and the rubber, resulting in a strong adhesion between the adhesive composition and the rubber.


[0045] In the bonding method of the present invention, it is preferred to form an undercoat layer (primer layer) on at least a part of the surface of the adherend, and then form the coating film of the adhesive composition thereon. The thickness of the undercoat layer is preferably 1 to 10 μm. As the undercoat composition, there may be used known suitable adhesives according to the material of the adherend. Although not particularly restricted, the undercoat composition preferably comprises (E) 100 parts by weight of a compound having a bisphenol backbone represented by the following formula II:
8


[0046] wherein R3 and R4 are each independently hydrogen or C1-C3 alkyl group, preferably hydrogen or methyl group; and n is an integer of 1 to 3, and (F) 5 to 50 parts by weight of a compound having in its molecule three or more acryloyloxy and/or methacryloyloxy groups.


[0047] The component E preferably has, in addition to the bisphenol backbone represented by the formula II, an end group represented by the following formula III:
9


[0048] wherein R5 is C2-C5 alkylene group, preferably ethylene group; and p is an integer of 1 to 5, preferably 1 to 3.


[0049] The component E may be commercially available as ethoxylated bisphenol F diactylate represented by the formula:
10


[0050] wherein m+n=4 (available from Nippon Kayaku Co., Ltd. under the trademark “KAYARAD R-712”), ethoxylated bisphenol A diacrylate (available from Nippon Kayaku Co., Ltd. under the trademark “KAYARAD R-551”), ethoxylated bisphenol A dimethacrylate (available from SARTOMER Inc. under the trademarks “SR-348”, “SR-480” and “SR9036”), and ethoxylated bisphenol A diacrylate (available from Arakawa Kagaku Kogyo Co., Ltd. under the trademark “BEAMSET 750”).


[0051] As the component F, there may be used the same compounds as used as the component C of the adhesive composition.


[0052] To enhance the strength of the coating film, the undercoat composition may contain a conjugated diene polymer selected from those as used for the component A of the adhesive composition in an amount of 0.5 to 10 parts by weight based on 100 parts by weight of the component E, and may also contain, if desired, the viscosity modifier and the photoinitiator mentioned above in amounts of 5 to 30 parts by weight and 0.1 to 5 parts by weight, respectively, based on 100 parts by weight of the Component E. Further, the undercoat composition may contain a styrene monomer as a radical reaction promoter in an amount of 1 to 20 parts by weight based on 100 parts by weight of the component E, In addition to the above components, the undercoat composition may further contain at least one additive selected from the group consisting of the same opoxy compounds, inorganic fillers, high-molecular fillers and basic compounds as described in connection with the adhesive composition in a total amount of 5 to 10 parts by weight based on 100 parts by weight of the component E.


[0053] The surface of the undercoat layer formed from the above composition is preferably irradiated with ultraviolet light or radiation.


[0054] In a preferred embodiment of the present invention, a composite having a laminated structure of adherend/undercoat layer/adhesive composition layer/rubber is produced by forming the undercoat layer on the surface of the adherend; laminating the adhesive composition layer on the undercoat layer; irradiating, if desired, the adhesive composition layer with ultraviolet light or radiation; and performing vulcanization while bringing an unvulcanized rubber into press-contact.


[0055] The rubber used in the present invention is not particularly restricted. Examples of the rubber include natural rubbers; conjugated diene synthetic rubbers such as polyisoprene synthetic rubber (IR), polybutadiene rubber (BR), styrene-butadiene copolymer rubber (SBR), acrylonitrile-butadiene rubber (NBR), chloroprene rubber (CR) and butyl rubber (IIR); ethylene-propylene copolymer rubber (EPM); ethylene-propylene-diene copolymer rubber (EPDM); and polysiloxane rubbers, with natural rubbers and conjugated diene synthetic rubbers being preferred. These rubbers may be used in combination of two or more.


[0056] The rubber may be vulcanized in the presence of a vulcanizing agent. Examples of the vulcanizing agents include sulfur; thiuram polysulfide compounds such as tetramethylthiuram disulfide and dipentamethylenethiuram tetrasulfide; 4,4-dithiomorpholine; p-quinone dioxim; cyclic sulfur imides; and peroxides, with sulfur being preferred.


[0057] The rubber may contain, in addition to the above components, various additives ordinarily used in rubber industries, for example, fillers such as carbon black and silica, vulcanization accelerators such as aluminum hydroxide, antioxidants and softeners. The rubber may be made into a composite with particles, fibers and cloths of various materials.


[0058] The present invention is described in more detail by reference to the following examples. However, it should be noted that the following examples are only illustrative and not intended to limit the invention thereto.


[0059] A composite of a rubber and an adherend was prepared by the following method, and subjected to various tests.


[0060] 1. Polyester Film/Rubber Composite


[0061] An undercoat composition shown in Table 1 was applied onto one surface of a 100 μm-thick polyethylene terephthalate film (available from Teijin Limited under the trademark “TETRON TYPE-O”) using a film coater to form an undercoat layer, which was then irradiated with ultraviolet light (for 5 s at an intensity of 500 mJ/cm2 and for 10 s at an intensity of 1,000 mJ/cm2) using an ultraviolet irradiation apparatus (“ECS-301G1” available from EYE GRAPHICS Co., Ltd.), or irradiated with electron beam (exposure dose: 40 or 25 MRad) using an electron beam irradiation apparatus (“ELECTROCURTAIN CB250/15/180L” available from EYE GRAPHICS Co., Ltd.).


[0062] Next, the treated undercoat layer was coated with an adhesive composition shown in Table 1 using a film coater to form an adhesive layer, After ultraviolet irradiation (for 5 s at an intensity of 500 mJ/cm2 and for 10 s at an intensity of 1,000 mJ/cm2) or electron beam irradiation (exposure dose: 7, 15 or 20 MRad) or without irradiation, the vulcanization was performed under the following conditions to obtain a 80 mm x 80 mm polyester film/rubber composite.


[0063] Unvulcanized Rubber


[0064] thickness: 2.3 mm
1formulation: shown in the following table.Formulationpart by weightNatural rubber100Carbon black40Stearic acid2Petroleum softening agent2Zinc white5Antioxidant**1.5N-t-butyl-2-benzothiazolylsulfenamide1.2Diphenylguanidine0.75Sulfur2.5**N-phenyl-N-isopropyl-p-phenylenediamine


[0065] Vulcanization Conditions:


[0066] Contact pressure: 15 kg/cm2


[0067] Vulcanizing temperature: 160° C.


[0068] Vulcanizing time: 20 min


[0069] 2. Polyester Cord/Rubber Composite


[0070] In continuous manner, a polyethylene terephthalate tire cord having a twisting structure of 1,500 d/2, a ply twist number of 39 turn/10 cm and a cable twist number of 39 turn/10 cm was immersed in the undercoat composition shown in Table 1 and passed between squeeze rolls to remove the excess undercoat composition. Then, the tire cord was passed through a photo-curing zone of an ultraviolet irradiation apparatus at a speed of 150 cm/min to irradiate the undercoat layer with ultraviolet light (for 10 s at an intensity of 1,000 mJ/cm2).


[0071] The obtained tire cord having the ultraviolet-cured undercoat layer was immersed in the adhesive composition shown in Table 1 and passed between squeeze rolls to remove the excess adhesive composition. Then, the tire cord was passed through a photo-curing zone of an ultraviolet irradiation apparatus at a speed of 150 cm/min to irradiate the adhesive composition layer with ultraviolet light (for 10 s at an intensity of 1,000 mJ/cm2).


[0072] The adhesive-treated polyester cord was embedded in a 2.3 mm-thick unvulcanized rubber having tho formulation as shown in the above Table, and vulcanized under a pressure of 20 kgf/cm2 at 160° C. for 20 min to obtain a polyester cord/rubber composite.


[0073] 3. Nylon Cord/Rubber Composite


[0074] The same procedure as in the production of the polyester cord/rubber composite was repeated except for using a tire cord having a twisting structure of 1,260 d/2, a ply twist number of 39 turn/10 cm and a cable twist number of 39 turn/10 cm and irradiating the undercoat layer with electron beam (exposure dose: 40 MRad) to obtain a nylon cord/rubber composite.


[0075] 4. Film Peel Test


[0076] The polyester film/rubber composite was cut into 25 mm in width to prepare a test specimen for peel test.


[0077] The test specimen was tested for peeling between the rubber layer and the polyester film at a peel angle of 180° (T-peel) and a peel rate of 50 mm/min to measure a peel strength. The area ratio of the adhering rubber (rubber adhesion rate) to the surface area of the film after peeling was measured to rank the rubber adhesion according to the following table. The results are shown in Table 1.
2RanksRubber adhesion rateCondition of film after peelingA+BrokenA100-80%Not brokenB 80-60%Not brokenC 60-40%Not brokenD 40-20%Not brokenE 20-0%Not broken


[0078] 5. Cord Tensile Test


[0079] The tire cord was dug out of each of the polyester cord/rubber composite and nylon cord/rubber composite, and peeled off from each composite at a rate of 30 cm/min to measure a peel resistance, which was employed as the adhesion strength (tension). The area ratio of the adhering rubber to the surface area of the cord after peeling was measured to rank the rubber adhesion according to the following table. The results are shown in Table 1.
3RanksRubber adhesion rateCondition of cord after peelingA+BrokenA100-80%Not brokenB 80-60%Not brokenC 60-40%Not brokenD 40-20%Not brokenE 20-0%Not broken


[0080] 6. Heat-of-Reaction Curve


[0081] The respective adhesive compositions were irradiated with ultraviolet light (for 5 s at an intensity of 500 mJ/cm2) to prepare films. Each film was cut into small pieces and screened by a 30 mesh metallic sieve to obtain each powder. Each 100 parts by weight of powder was uniformly kneaded with 3 parts by weight of insoluble sulfur (under 80 mesh) to prepare each specimen.


[0082] A stainless steel pressure pan containing the specimen was set in a differential scanning calorimeter. The temperature was held at 70° C. at which vulcanization does not initiate for 5 min, and then raized at a rate of 5° C./min to measure the heat of reaction (W/g) and prepare a heat-of-reaction curve from the measured results.


[0083] An example of the heat-of-reaction curves thus prepared is illustrated in FIG. 1. The formulation of each specimen is shown below.
4Formulation of SpecimenAdhesive composition(part by weight)Component AComponent BSulfur (part by weight) 0% VP10003 5% VP955310% VP9010315% VP8515320% VP80203Component A: Methacrylated polybutadiene (RIACRYL3100) Component B: 4-vinylpyridine


[0084] As seen from FIG. 1, the curve for the composition (0% VP) containing no component B (electron pair-donating basic compound: 4-vinylpyridine) showed a flat base line with no peak in a temperature region of 190° C. or lower, especially 180° C. or lower. In the curves for the compositions that were added with the component B, shoulder peaks (indicated by arrows) attributable to the vulcanization reaction appeared in a temperature region of 120 to 190° C. The inflection point of each shoulder peak calculated by differential method is shown in Table 1 as the heat-of-reaction peak temperature.


[0085] 7. Migrating Amount of Sulfur (Rubber→Adhesive Composition)


[0086] The polyester film/rubber composite prepared in the manner described above was cut in the direction perpendicular to the surface thereof. The cut film was cross-sectionally observed by a scanning electron microscope coupled with an X-ray analyzer to count the fluorescent X-ray from sulfur in the rubber layer, adhesive layer and film layer. The amount of sulfur migrated from the rubber layer into the adhesive layer was evaluated by whether the sulfur content in the adhesive layer is high or low as compared to the average distribution of sulfur content in the rubber layer.


[0087] 8. Pneumatic Tire


[0088] A polyethylene terephthalate tire cord having a twisting structure of 1,500 d/2, a ply twist number of 39 turn/10 cm and a cable twist number of 39 turn/10 cm was immersed in the undercoat composition shown in Table 1 and passed through squeeze rolls to remove the excess undercoat composition. Then, the tire cord was passed through a photo-curing zone of an ultraviolet irradiation apparatus at a speed of 150 cm/min to irradiate the resultant undercoat layer with ultraviolet light (for 10 s at an intensity of 1,000 mJ/cm2).


[0089] The tire cord having the ultraviolet-cured undercoat layer was immersed in the adhesive composition shown in Table 1 and passed through squeeze rolls to remove the excess adhesive composition. Then, the tire cord was passed through a photo-curing zone of an ultraviolet irradiation apparatus at a speed of 150 cm/min to irradiate the resultant adhesive layer with ultraviolet light (for 10 s at an intensity of 1,000 mJ/cm2), thereby preparing adhesive-treated polyester cords of Comparative Example 14 and Example 37.


[0090] The adhesive-coated polyester cords of Comparative Example 14 and Example 37 were respectively used as a single carcass ply to produce a pneumatic radial tire having a size of 155R13.


[0091] 9. Adhesion Strength of Polyester Cord/Rubber Composite after Tire Running


[0092] Each tire of Comparative Example 14 and Example 37 was seated on a rim prescribed in JIS D4202, and mounted to an ordinary passenger car for running on a flat asphalt road surface at a speed of 30 km/h over 10 km (preliminary running). The tire of Example 37 was further run on usual road over 10,000 km. The tenacity (N) of the cord after running was measured according to JIS L1017. A sample of 100 mm long in the ply cord direction and 25 mm long in the circumferential direction was cut out by a knife from the side portion of each tire. The cord was dug up from the sample and peeled off from the side rubber at a speed of 30 cm/min to measure the peel resistance (N) which is shown as the adhesion strength in the following tables. Separately, a tire was produced using an RFL formulation which was ordinarily used as a tire cord adhesive and run in the same manner as in the tire of Example 37. The cord tenacity and the adhesion strength of the tire after running are also shown in the folloiwng tables as the reference.
5RunningCord tenacityAdhesion strengthdistanceafter runningafter running(km)(N)(N/cord)Comparative Example 14102283(control tire)Example 3710,01024221(inventive tire)RFL composition10,01023920(reference)


[0093]

6









TABLE 1-1













Com. Ex. 1
Ex. 1
Ex. 2














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer
















Component A








RIACRYL 3801*1


RIACRYL 3500*2


RIACRYL 3100*3


BAC45*4
12
50
12
50
12
50


Component D


Monofunctional compound


SR-285*8
10

10

10


SR-440*9

15


AMP-60G*10


Styrene
5

5

5


Polyfunctional compound


9PG*11

15

13

13


APG-400*12
15

15

15


Component E


SR-348*13
30

30

30


KAYARAD R551*14





5


BEAMSET 750*15


KAYARAD R-712*16


Component B


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine



20

15


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine


Acrylamide


N-vinyl pyrrolidone


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17


KAYARAD TPA-320*18


KAYARAD TPA-330*19
20
10
20
10
20
10


BEAMSET 710*20


BEAMSET 700*21


Epoxy compound


ENA*6


High-molecular filler


HYCARATBN*5 1300 × 16


ISOBAN 10*7
5
5
5
2
5
2


VIRON 300*27


Inorganic filler


NANOMER PGW*22

2

2

2


Photoinitiator


KAYACURE DETX-S*23
3
3
3
3
3
3


KAYACURE DMBI*24










Adherend
Polyester film
Polyester film
Polyester film













Radiation conditions








UV exposure (mJ/cm2)
500
500
500
500
500
500


UV exposure time (s)
5
5
5
5
5
5


EB exposure (MRad)
0
0
0
0
0
0










Results of film peel test





Peel strength (N/25 mm)
8
249
231


Rubber adhesion
E
A+
A


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion





Results of differential


scanning calorimetry


Heat-of-reaction peak
None




temp. (° C.)


Analysis by scanning


electron microscope-


X-ray analyzer


Sulfur content in
Lower than rubber




adhesive composition
layer










[0094]

7









TABLE 1-2













Ex. 3
Ex. 1
Com. Ex. 2














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer
















Component A








RIACRYL 3801*1


RIACRYL 3500*2


RIACRYL 3100*3




5


BAC45*4
12
45
12
50


Component D


Monofunctional compound


SR-285*8
10

10


SR-440*9


AMP-60G*10

13


9
54


Styrene
5

5

6


Polyfunctional compound


9PG*11


APG-400*12
15

15
13
9
18


Component E


SR-348*13
30

30


KAYARAD R551*14


BEAMSET 750*15


KAYARAD R-712*16

10

10
15


Component B


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine

15

10


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine





15


Acrylamide


N-vinyl pyrrolidone


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17




20
7


KAYARAD TPA-320*18


KAYARAD TPA-330*19
20
10
20
10


BEAMSET 710*20


BEAMSET 700*21


Epoxy compound


ENA*6




20


High-molecular filler


HYCAR ATBN*5 1300 × 16




6


ISOBAN 10*7
5
2
5
2
5


VIRON 300*27




2
3


Inorganic filler


NANOMER PGW*22

2

2


Photoinitiator


KAYACURE DETX-S*27
3
3
3
3
3
3


KAYACURE DMBI*24










Adherend
Polyester film
Polyester film
Polyester film













Radiation conditions








UV exposure (mJ/cm2)
500
500
500
500
500
500


UV exposure time (s)
5
5
5
5
5
5


EB exposure (MRad)
0
0
0
0
0
0










Results of film peel test





Peel strength (N/25 mm)
220
224
20


Rubber adhesion
A
A
E


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion





Results of differential


scanning calorimetry


Heat-of-reaction peak


None


temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive


Lower than rubber


composition layer


layer










[0095]

8









TABLE 1-3













Ex. 5
Ex. 6
Ex. 7














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer
















Component A








RIACRYL 3801*1


RIACRYL 3500*2


RIACRYL 3100*3
5
10
5
19
5
34


BAC45*4


Component D


Monofunctional compound


SR-285*8



5


SR-440*9


AMP-60G*10
9
25
9
3
9
3


Styrene
6
3
6
6
6
5


Polyfunctional compound


9PG*11


APG-400*12
9
18
9
18
9
18


Component E


SR-348*13


KAYARAD R551*14


BEAMSET 750*15


KAYARAD R-712*16
15

15
4
15


Component B


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine

2

2

6


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine

25

20

18


Acrylamide


N-vinylpyrrolidone


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17
20
7
20
15
20
9


KAYARAD TPA-320*18


KAYARAD TPA-330*19


BEAMSET 710*20


BEAMSET 700*21


Epoxy compound


ENA*6
20
5
20
5
20
2


High-molecular filler


HYCAR ATBN*5 1300 × 16
6

6

6


ISOBAN 10*7
5

5

5


VIRON 300*27
2
2
2


Inorganic filler


NANOMER PGW*22




2
2


Photoinitiator


KAYACURE DETX-S*23
3
3
3
3
3
3


KAYACURE DMBI*24










Adherend
Polyester film
Polyester film
Polyester film













Radiation conditions








UV exposure (mJ/cm2)
500
500
500
500
500
500


UV exposure time (s)
5
5
5
5
5
5


EB exposure (MRad)
0
0
0
0
0
0










Results of film peel test





Peel strength (N/25 mm)
63
72
206


Rubber adhesion
D
D
B


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion





Results of differential


scanning calorimetry


Heat-of-reaction peak

160° C.



temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive

Lower than rubber



composition layer

layer










[0096]

9









TABLE 1-4













Ex. 8
Ex. 9
Ex. 10














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer
















Component A








RIACRYL 3801*1


RIACRYL 3500*2


RIACRYL 3100*3
5
45
5
55
5
67


BAC45*4


Component D


Monofunctional compound


SR-285*8


SR-440*9


AMP-60G*10
9

9

9


Styrene
6
3
6

6


Polyfunctional compound


9PG*11


APG-400*12
9
18
9
18
9
12


Component E


SR-348*13


KAYARAD R551*14


BEAMSET 750*15


KAYARAD R-712*16
15
3
15

15


Component B


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine

15

15

15


Acrylamide


N-vinylpyrrolidone

4


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17
20
7
20
7
20
4


KAYARAD TPA-320*18


KAYARAD TPA-330*19


BEAMSET 710*20


BEAMSET 700*21


Epoxy compound


ENA*6
20

20

20


High-molecular filler


HYCAR ATBN*5 1300 × 16
6

6

6


ISOBAN 10*7
5

5

5


VIRON 300*27
2
2
2
2
2


Inorganic filler


NANOMER PGW*22


Photoinitiator


KAYACURE DETX-S*23
3
3
3
3
3
2


KAYACURE DMBI*24










Adherend
Polyester film
Polyester film
Polyester film













Radiation conditions








UV exposure (mJ/cm2)
500
500
500
500
500
500


UV exposure time (s)
5
5
5
5
5
5


EB exposure (M Rad)
0
0
0
0
0
0










Results of film peel test





Peel strength (N/25 mm)
257
260
186


Rubber adhesion
A+
A+
B


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion





Results of differential


scanning calorimetry


Heat-of-reaction peak
150° C.




temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur contant in adhesive
Higher than




composition layer
rubber layer










[0097]

10









TABLE 1-5













Ex. 11
Com. Ex. 3
Ex. 12














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer
















Component A








RIACRYL 3801*1


RIACRYL 3500*2




10
57


RIACRYL 3100*3
5
81
5
100


BAC45*4


Component D


Monofunctional compound


SR-285*8


SR-440*9


AMP-60G*10
9

9

12


Styrene
6

6

6


Polyfunctional compound


9PG*11


APG-400*12
9
5
9
0
12
18


Component E


SR-348*13


KAYARAD R551*14


BEAMSET 750*15




10


KAYARAD R-712*16
15

15

20


Component (B)


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine

9



15


Acrylamide


N-vinylpyrrolidone


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17
20
3
20
0


KAYARAD TPA-320*18


KAYARAD TPA-330*19




24
7


BEAMSET 710*20


BEAMSET 700*21


Epoxy compound


ENA*6
20

20


High-molecular filler


HYCARATBN*5 1300 × 16
6

6


ISOBAN 10*7
5

5


VIRON 300*27
2

2


Inorganic filler


NANOMER PGW*22




3


Photoinitiator


KAYACURE DETX-S*27
3
2
3
0
3
3


KAYACURE DMBI*24










Adherend
Polyester film
Polyester film
Polyester film


Radiation conditions













UV exposure (mJ/cm2)
1000
1000
1000
1000
1000
500


UV exposure time (sec)
10
10
10
10
10
5


EB exposure (MRad)
0
0
0
0
0
0










Results of film peel test





Peel strength (N/25 mm)
98
8
270


Rubber adhesion
C
E
A


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion


Results of differential


scanning calorimetry


Heat-of-reaction peak

None



temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer








Sulfur content in adhesive-
Lower than rubber-


composition layer
layer










[0098]

11









TABLE 1-6













Com. Ex. 4
Ex. 13
Com. Ex. 5














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer
















Component A








RIAGRYL 3801*1
10
50
10
50
5
42


RIACRYL 3500*2


RIACRYL 3100*3


BAC45*4


Component D


Monofunctional compound


SR-285*8
2
15
2


SR-440*9




10
15


AMP-60G*10


Styrone


Polyfunctional compound


9PG*11


APG-400*12

20

17
8
20


Component E


SR-348*13


KAYARAD R551*14




32


BEAMSET 750*15
35

35


KAYARAD R-712*16


Component B


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine
8

8


Acrylamide


N-vinylpyrrohidone



18


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17


KAYARAD TPA-320*18


KAYARAD TPA-330*19


BEAMSET 710*20
20
12
20
12


BEAMSET 700*21




25
18


Epoxy compound


ENA*6
10

10

10


High-molecular filler


HYCAR ATBN*5 1300 × 16




5


ISOBAN 10*7
12

12


VIRON 300*27


Inorganic filler


NANOMER PGW*22




3
3


Photoinitiator


KAYACURE DETX-S*23


KAYACURE DMBI*24
3
3
3
3
2
2










Adherend
Polyester film
Polyester film
Polyester film













Radiation conditions








UV exposure (mJ/cm2)
500
500
500
500
1000
1000


UV exposure time (s)
5
5
5
5
10
10


EB exposure (MRad)
0
0
0
0
0
0










Results of film peel test





Peel strength (N/25 mm)
6
254
13


Rubber adhesion
E
A+
E


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion





Results of differential


scanning calorimetry


Heat-of-reaction peak





tomp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive





composition layer










[0099]

12









TABLE 1-7













Ex. 14
Com. Ex. 6
Ex. 15














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer
















Component A








RIACRYL 3801*1
5
42


RIACRYL 3500*2


10
60
10
42


RIACRYL 3100*3


BAC45*4


Component D


Monofunctional compound


SR-285*8


SR-440*9
10
5


10


AMP-60G*10


Styrene


10
3


Polyfunctional compound


9PG*11


14

14


APG-400*12
8
15

15

20


Component E


SR-348*13


KAYARAD R551*14
32



18


BEAMSET 750*15


KAYARAD R-712*18


36

18


Component B


Amine compound


Dibutylamine




4
23


Ethylenediamine

15


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine


4


Acrylamide


N-vinylpyrrolidone


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17



8

8


KAYARAD TPA-320*18


12

12


KAYARAD TPA-330*19


6

6
5


BEAMSET 710*20


BEAMSET 700*21
25
18


Epoxy compound


ENA*6
10

6

6


High-molecular filler


HYCAR ATBN*5 1300 × 16
5


10


ISOBAN 10*7


VIRON 300*27


Inorganic filler


NANOMER PGW*22
3
3

2


Photoinitiator


KAYACURE DETX-S*23


2
2
2
2


KAYACURE DMBI*24
2
2










Adherend
Polyester film
Polyester film
Polyester film













Radiation conditions








UV exposure (mJ/cm2)
1000
1000
1000
500
1000
500


UV exposure time (s)
10
10
10
5
10
5


EB exposure (MRad)
0
0
0
0
0
0










Results of film peel test





Peel strength (N/25 mm)
190
22
178


Rubber adhesion
B
E
B


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion





Results of differential


scanning calorimetry


Heat-of-reaction peak
156° C.

159° C.


temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive
Higher than

Higher than


composition
rubber layer

rubber layer










[0100]

13









TABLE 1-8













Ex. 16
Ex. 17
Ex. 18














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer

















Component A








RIACRYL 3801*1


RIACRYL 3500*2
10
45
10
45
10
45


RIACRYL 3100*3


BAC45*d


Component D


Monofunctional compound


SR-285*8


SR-440*9


10
3
10
3


AMP-60G*10


Styrene
10
3


Polyfunctional compound


9PG*11
14

14

14


APG-400*12

15

15

15


Component E


SR-348*13


KAYARAD R551*14
18

18

18


BEAMSET 750*15


KAYARAD R-712*16
18

18

18


Component B


Amine compound


Dibutylamino


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26
4


Aniline

15

20


Pyridine


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine


4


Acrylamide


N-vinylpyrrolidone




4


Vulcanization accelerator


Diphenylguanidine





15


2-methylimidazole


Component C or F


KAYARAD THE-330*17

8

8

8


KAYARAD TPA-320*18
12

12

12


KAYARAD TPA-330*19
6

6

6


BEAMSET 710*20


BEAMSET 700*21


Epoxy compound


ENA*6
6

6

6


High-molecular filler


HYCARATBN*5 1300 × 16

10

5

10


ISOBAN 10*7


VIRON 300*27


Inorganic filler


NANOMER PGW*22

2

2

2


Photoinitiator


KAYACURE DETX-S*23
2
2
2
2
2
2


KAYACURE DMBI*21










Adherend
Polyester film
Polyester film
Polyester film


Radiation conditions













UV exposure (mJ/cm2)
1000
500
1000
500
1000
500


UV exposure time (s)
10
5
10
5
10
5


EB exposure (MRad)
0
0
0
0
0
0


Results of film peel test










Peel strength (N//25 mm)
159
204
188


Rubber adhesion
C
B
B


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion





Results of differential


scanning calorimetry


Heat-of-reaction peak





temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive
Higher than
Higher than



composition layer
rubber layer
rubber layer










[0101]

14









TABLE 1-9













Ex. 19
Ex. 20
Ex. 21














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer
















Component A








RIACRYL 3801*1


RIACRYL 3500*2
10
45
10
45
10
45


RIACRYL 3100*3


BAC45*4


Component D


Monofunctional compound


SR-285*8


SR-440*9
10
3
10
3
10
3


AMP-60G*10


Styrene


Polyfunctional compound


9PG*11
14

14

14


APG-400*12

15

15

15


Component E


SR-348*13


KAYARAD R551*14
18

18

18


BEAMSET 750*15


KAYARAD R-712*16
18

18

18


Component B


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine


Tetramethylthiourea

15


Polymerizable monomer


4-vinylpyridine


Acrylamide




4
15


N-vinylpyrrolidone


Vulcanization accelerator


Diphenylguanidine
4


2-methylimidazole


4
15


Component C or F


KAYARAD THE-330*17

8

8

8


KAYARAD TPA-320*18
12

12

12


KAYARAD TPA-330*19
6

6

6


BEAMSET 710*20


BEAMSET 700*21


Epoxy compound


ENA*6
6

6

6


High-molecular filler


HYCAR ATBN*5 1300 × 16

10

10

10


ISOBAN 10*7


VIRON 300*27


Inorganic filler


NANOMER PGW*22

2

2

2


Photoinitiator


KAYACURE DETX-S*28
2
2
2
2
2
2


KAYACURE DMBI*24










Adherend
Polyester film
Polyester film
Polyester film













Radiation conditions








UV exposure (mJ/cm2)
1000
500
1000
500
1000
500


UV exposure time (s)
10
5
10
5
10
5


EB exposure (MRad)
0
0
0
0
0
0










Results of film peel test





Peel strength (N/25 mm)
147
152
227


Rubber adhesion
C
C
A


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion





Results of differential


scanning calorimetry


Heat-of-reaction peak





temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive
Higher than
Higher than
Higher than


composition layer
rubber layer
rubber layer
rubber layer










[0102]

15









TABLE 1-10













Ex. 22
Com. Ex. 7
Ex. 23














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer
















Component A








RIACRYL 3801*1


RIACRYL 3500*2
10
45
10
54
10
54


RIACRYL 3100*3


BAC45*4


Component D


Monofunctional compound


SR-285*8


SR-440*8
10
3
10

10


AMP-60G*10


Styrone



23


Polyfunctional compound


9PG*11
14


APG-400*12

15
14
14
14
14


Component E


SR-348*13


KAYARAD R551*14
18

18

18


BEAMSET 750*15


KAYARAD R-712*16
18

18

18


Component B


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine





23


Acrylamide


N-vinylpyrrolidone
4
15
4

4


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17

8


KAYARAD TPA-320*18
12

12
6
12
6


KAYARAD TPA-330*19
6

6

6


BEAMSET 710*20


BEAMSET 700*21


Epoxy compound


ENA*6
6

6

6


High-molecular filler


HYCAR ATBN*5 1300 × 16

10


ISOBAN 10*7


VIRON 300*27


Inorganic filler


NANOMER PGW*22

2


Photoinitiator


KAYACURE DETX-S*23
2
2
2
3
2
3


KAYACURE DMBI*24










Adherend
Polyester film
Polyester film
Polyester film













Radiation conditions








UV exposure (mJ/cm2)
1000
500
1000
500
1000
500


UV exposure time (sec)
10
5
10
5
10
5


EB exposure (MRad)
0
0
0
0
0
0










Results of film peel test





Peel strength (N/25 mm)
208
15
229


Rubber adhesion
A
E
A


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion





Results of differential


scanning calorimetry


Heat-of-reaction peak





temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive





composition layer










[0103]

16









TABLE 1-11













Com. Ex. 8
Ex. 24
Ex. 25














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer
















Component A








RIACRYL 3801*1


RIACRYL 3500*2
10
53
10
53
10
53


RIACRYL 3100*3


BAC45*4


Component D


Monofunctional compound


SR-285*8

5

4

3


SR-440*9
10

10

10
5


AMP-60G*10


Styrene

14

8

6


Polyfunctional compound


9PG*11


APG-400*12
14
14
14
14
14
14


Component E


SR-348*13


KAYARAD R551*14
18

18

18


BEAMSET 750*15


KAYARAD R-712*16
18

18

18


Component B


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine



6

10


Acrylamide


N-vinylpyrrolidone
4

4

4


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17


KAYARAD TPA-320*18
12
6
12
6
12
6


KAYARAD TPA-330*19
6

6

6


BEAMSET 710*20


BEAMSET 700*21


Epoxy compound


ENA*6
6
5
6
6
6


High-molecular filler


HYCAR ATBN*6 1300 × 16


ISOBAN 10*7


VIRON 300*27


Inorganic filler


NANOMER PGW*22


Photonitiator


KAYACURE DETX-S*23
2
3
2
3
2
3


KAYACURE DMBI*24










Adherend
Polyester film
Polyester film
Polyester film













Radiation conditions








UV exposure (mJ/cm2)
1000
500
1000
500
1000
500


UV exposure time (s)
10
5
10
5
10
5


EB exposure (MRad)
0
0
0
0
0
0










Results of film peel test





Peel strength (N/25 mm)
14
100
259


Rubber adhesion
E
C
A+


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion





Results or differential


scanning calorimetry


Heat-of-reaction peak

167
160


temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive

Higher than
Higher than


composition layer

rubber layer
rubber layer










[0104]

17









TABLE 1-12













Ex. 26
Ex. 27
Ex. 28














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer
















Component A








RIACRYL 3801*1


RIACRYL 3500*2
10
53
10
38
10
29


RIACRYL 3100*3


BAC45*4


Component D


Monofunctional compound


SR-285*8


SR-440*9
10

10

10


AMP-60G*10

4


Styrene

3


Polyfunctional compound


9PG*11


APG-400*12
14
14
14
14
14
10


Component E


SR-348*13


KAYARAD R551*14
18

18

18


BEAMSET 750*15


KAYARAD R-712*16
18

18

18


Component B


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine

14

39

53


Acrylamide


N-vinylpyrrolidone
4

4

4


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17


KAYARAD TPA-320*18
12
6
12
6
12
5


KAYARAD TPA-330*19
6

6

6


BEAMSET 710*20


BEAMSET 700*21


Epoxy compound


ENA*6
6
3
6

6


High-molecular filler


HYCAR ATBN*5 1300 × 16


ISOBAN 10*7


VIRON 300*27


Inorganic filler


NANOMER PGW*22


Photopolymerization


initiator


KAYACURE DETX-S*23
2
3
2
3
2
3


KAYACURE DMBI*24










Adherend
Polyester film
Polyester film
Polyester film













Radiation conditions








UV exposure (mJ/cm2)
1000
500
1000
500
1000
500


UV exposure time (s)
10
5
10
5
10
5


EB exposure (MRad)
0
0
0
0
0
0










Results of film peel test





Peel strength (N/25 mm)
245
233
162


Rubber adhesion
A
A
B


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion





Results of differential


scanning calorimetry


Heat-of-reaction peak

144



temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive

Higher than



composition layer

rubber layer










[0105]

18









TABLE 1-13













Com. Ex. 9
Ex. 29
Ex. 30














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer
















Component A








RIACRYL 3801*1


RIACRYL 3500*2
10

10
44
10
44


RIACRYL 3100*3


BAC45*4


Component D


Monofunctional compound


SR-285*8


SR-440*9
10

10

10


AMP-60G*10


Styrene


Polyfunctional compound


9PG*11


APG-400*12
14

14
14
14
14


Component E


SR-348*13


KAYARAD R551*14
18

18

18


BEAMSET 750*15


KAYARAD R-712*16
18

18

18


Component B


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine



10

10


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine

100

23

23


Acrylamide


N-vinylpyrrolidone
4

4

4


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17


KAYARAD TPA-320*18
12

12
6
12
6


KAYARAD TPA-330*19
6

6

6


BEAMSET 710*20


BEAMSET 700*21


Epoxy compound


ENA*6
6

6

6


High-molecular filler


HYCAR ATBN*5 1300 × 16


ISOBAN 10*7


VIRON 300*27


Inorganic filler


NANOMER PGW*22


Photoinitiator


KAYACURE DETX-S*23
2

2
3
2
3


KAYACURE DMBI*24










Adherend
Polyester film
Polyester film
Polyester film













Radiation conditions








UV exposure (mJ/cm2)
1000
500
0
0
0
0


UV exposure time (s)
10
5
0
0
0
0


EB exposure (MRad)
0
0
40
20
40
15










Results of film peel test





Peel strength (N/25 mm)
13
231
224


Rubber adhesion
E
A
A


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion





Results of differential


scanning calorimetry


Heat-of-reaction peak





temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive





composition layer










[0106]

19









TABLE 1-14













Ex. 31
EX. 32
Ex. 33














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer

















Component A








RIACRYL 3801*1


RIACRYL 3500*2
10
47
10
47
10
47


RIACRYL 3100*3


BAC45*4


Component D


Monofunctional compound


SR-285*8


SR-440*9
10

10

10


AMP-60G*10


Styrene


Polyfunctional compound


9PG*11


APG-400*12
14
14
14
14
14
14


Component E


SR-348*13


KAYARAD R551*14
18

18

18


BEAMSET 750*15


KAYARAD R-712*16
18

18

18


Component B


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine

10

10

10


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine

23

23

23


Acrylamide


N-vinylpyrrolidone
4

4

4


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17


KAYARAD TPA-320*18
12
6
12
6
12
6


KAYARAD TPA-330*19
6

6

6


BEAMSET 710*20


BEAMSET 700*21


Epoxy compound


ENA*6
8

8

8


High-molecular filler


HYCARATBN*5 1300 × 16


ISOBAN 10*7


VIRON 300*27


Inorganic filler


NANOMER PGW*22


Photoinitiator


KAYACURE DETX-S*27


KAYACURE DMBI*24










Adherend
Polyester film
Polyester film
Polyester film













Radiation conditions








UV exposure (mJ/cm2)
1000
0
1000
0
0
0


UV exposure time (s)
10
0
10
0
0
0


EB exposure (MRad)
0
15
0
7
25
7










Results of film peel test





Peel strength (N/25 mm)
239
215
244


Rubber adhesion
A
A
A


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion





Results of differential


scanning calorimetry


Heat-of-reaction peak





temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive





composition










[0107]

20

















Com. Ex. 10
Com. Ex. 11
Ex. 34














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer

















Component A








RIACRYL 3801*1


RIACRYL 3500*2
10

10
47


RIACRYL 3100*3




10
54


BAC45*4


Component D


Monofunctional compound


SR-285*8


SR-440*9
10
44
10
30
10


AMP-60G*10


Styrene


Polyfunctional compound


9PG*11


APG-400*12
14
14
14
14
14
14


Component E


SR-348*13


KAYARAD R551*14
18

18

18


BEAMSET 750*15


KAYARAD R-712*16
18

18

18


Component B


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine

10


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine

23



23


Acrylamide


N-vinylpyrrolidone
4

4

4


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17


KAYARAD TPA-320*18
12
6
12
6
12
6


KAYARAD TPA-330*19
6

6

6


BEAMSET 710*20


BEAMSET 700*21


Epoxy compound


ENA*6
6

6

8


High-molecular filler


HYCAR ATBN*5 1300 × 16


ISOBAN 10*7


VIRON 300*27


Inorganic filler


NANOMER PGW*22


Photoinitiator


KAYACURE DETX-S*23
2
3
2
3
0
3


KAYACURE DMBI*24










Adherend
Polyester film
Polyester film
Polyester film













Radiation conditions








UV exposure (mJ/cm2)
0
0
0
0
0
0


UV exposure time (s)
0
0
0
0
0
0


EB exposure (MRad)
40
7
40
7
20
0










Results of film peel test





Peel strength (N/25 mm)
9
13
 86


Rubber adhesion
E
E
D


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion





Results of differential


scanning calorimetry


Heat-of-reaction peak


142


temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive


Higher than


composition layer


rubber layer










[0108]

21









TABLE 1-16













Ex. 35
Ex. 36
Com. Ex. 12














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer

















Component A








RIACRYL 3801*1


RIACRYL 3500*2


RIACRYL 3100*3
10
54
10
54
10


BAC45*4


Component D


Monofunctional compound


SR-285*8


SR-440*9
10

10

10
54


AMP-60G*10


Styrene


Polyfunctional compound


9PG*11


APG-400*12
14
14
14
14
14
14


Component E


SR-348*13


KAYARAD R551*14
18

18

18


BEAMSET 750*15


KAYARAD R-712*16
18

18

18


Component B


Amine compound


Dibutylamine



10


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine



13

23


Acrylamide


N-vinylpyrrolidone
4

4

4


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole

23


Component C or F


KAYARAD THE-330*17


KAYARAD TPA-320*18
12
6
12
6
12
6


KAYARAD TPA-330*19
6

6

6


BEAMSET 710*20


BEAMSET 700*21


Epoxy compound


ENA*6
6

6

6


High-molecular filler


HYCAR ATBN*5 1300 × 16


ISOBAN 10*7


VIRON 300*27


Inorganic filler


NANOMER PGW*22


Photoinitiator


KAYACURE DETX-S*23
2
3
2
3
2
3


KAYACURE DMBI*24










Adherend
Polyester film
Polyester film
Polyester film













Radiation conditions








UV exposure (mJ/cm2)
1000
0
1000
0
1000
0


UV exposure time (s)
10
0
10
0
10
0


EB exposure (MRud)
0
0
0
0
40
0










Results of film peel test





Peel strength (N/25 mm)
189
175
16


Rubber adhesion
B
B
E


Results of cord tensile test


Cord tension (N/cord)





Rubber adhesion





Results of differential


scanning calorimetry


Heat-of-reaction peak





temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive





composition layer










[0109]

22









TABLE 1-17













Com. Ex. 13
Com. Ex. 14
Ex. 37














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer

















Component A








RIACRYL 3801*1


RIACRYL 3500*2


RIACRYL 3100*3
10
54
5
55
5
55


BAC45*4


Component D


Monofunctional compound


SR-285*8


SR-440*9
10
23


AMP-60G*10


9

9


Styrene



17


Polyfunctional compound


9PG*11


APG-400*12
14
14
9
18
9
18


Component E


SR-348*13


KAYARAD R551*14
18


BEAMSET 750*15


KAYARAD R-712*16
18

20

20


Component B


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


Aniline


Pyridine


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine





17


Acrylamide


6

6


N-vinylpyrrolidone
4


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17


15
7
15
7


KAYARAD TPA-320*18
12
6


KAYARAD TPA-330*19
6


BEAMSET 710*20


BEAMSET 700*21


Epoxy compound


ENA*6
6

20

20


High-molecular filler


HYCAR ATBN*5 1300 × 16


6

6


ISOBAN 10*7


7

7


VIRON 300*27


Inorganic filler


NANOMER PGW*22


Photoinitiator


KAYACURE DETX-S*23
2
3
3
3
3
3


KAYACURE DMBI*24










Adherend
Polyester film
Polyester cord
Polyester cord













Radiation conditions








UV exposure (mJ/cm2)
1000
0
1000
1000
1000
1000


UV exposure time (s)
10
0
10
10
10
10


EB exposure (MRad)
40
0
0
0
0
0










Results of film peel test





Peel strength (N/25 mm)
11




Rubber adhesion
E




Results of cord tensile test


Cord tension (N/cord)

4
22


Rubber adhesion

E
A


Results of differential


scanning calorimetry


Heat-of-reaction peak





temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive





composition layer










[0110]

23









TABLE 1-18













Ex. 38
Ex. 39
Ex. 40














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer

















Component A








RIACRYL 3801*1




6
50


RIACRYL 3500*2
6
50


RIACRYL 3100*3


6
56


BAC45*4


Component D


Monofunctional compound


SR-285*8
8



10


SR-440*9


10
8


AMP-60G*10
5
15



10


Styrene




6


Polyfunctional compound


9PG*11
12



14


APG-400*12

20
10
10

20


Component E


SR-348*13
32


KAYARAD R551*14


20


BEAMSET 750*15


KAYARAD R-712*16




30


Component B


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25


FUJICURE 5100*26


10


Aniline


Pyridine

5

15


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine


Acrylamide


N-vinylpyrrolidone


9


10


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17





8


KAYARAD TPA-320*18


KAYARAD TPA-330*19
20
7


BEAMSET 710*20




15


BEAMSET 700*21


10
8


Epoxy compound


ENA*8


20


High-molecular filler


HYCAR ATBN*5 1300 × 16


ISOBAN 10*7




5


VIRON 300*27
14



10


Inorganic filler


NANOMER PGW*22


2

2


Photoinitiator


KAYACURE DETX-S*23
3
3


2
2


KAYACURE DMBI*24


3
3










Adherend
Polyester cord
Polyester cord
Polyester cord













Radiation conditions








UV exposure (mJ/cm2)
1000
1000
1000
1000
1000
1000


UV exposure time (s)
10
10
10
10
10
10


EB exposure (MRad)
0
0
0
0
0
0










Results of film peel test





Peel strength (N/25 mm)





Rubber adhesion





Results of cord tensile test


Cord tension (N per cord)
15
20
19


Rubber adhesion
B
A
B


Results of differential


scanning calorimetry


Heat-of-reaction peak





temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive





composition layer










[0111]

24









TABLE 1-19













Ex. 41
Ex. 42
Ex. 43














Undercoat
Adhesive
Undercoat
Adhesive
Undercoat
Adhesive



layer
layer
layer
layer
layer
layer

















Component A








RIACRYL 3801*1


RIACRYL 3500*2


RIACRYL 3100*3


6
56
6
56


BAC45*4
5
50


Component D


Monofunctional compound


SR-285*8
10


SR-440*9


AMP-60G*10

15
15
8
15
8


Styrene


Polyfunctional compound


9PG*11


APG-400*13
10
15
15
10
15
10


Component E


SR-348*13
32


KAYARAD R551*14


20

20


BEAMSET 750*15


KAYARAD R-712*16


Component B


Amine compound


Dibutylamine


Ethylenediamine


TOMIDE 252*25
10

10

10


FUJICURE 5100*26


Aniline


Pyridine

10


Tetramethylthiourea


Polymerizable monomer


4-vinylpyridine



16

16


Acrylamide


N-vinylpyrrolidone


Vulcanization accelerator


Diphenylguanidine


2-methylimidazole


Component C or F


KAYARAD THE-330*17
20
7


KAYARAD TPA-320*18


KAYARAD TPA-330*19


BEAMSET 710*20


BEAMSET 700*21


12
8
12
8


Epoxy compound


ENA*6
10

20

20


High-molecular filler


HYCAR ATBN*5 1300 × 16


ISOBAN 10*7


VIRON 300*27


Inorganic filler


NANOMER PGW*22


Photoinitiator


KAYACURE DETX-S*23
3
3


KAYACURE DMBI*24


2
2
2
2










Adherend
Polyester cord
Polyester cord
Nylon cord













Radiation conditions








UV exposure (mJ/cm2)
1000
1000
1000
1000
0
1000


UV exposure time (s)
10
10
10
10
0
10


EB exposure (MRad)
0
0
0
0
40
0










Results of film peel test





Peel strength (N/25 mm)





Rubber adhesion





Results of cord tensile test


Cord tension (N/cord)
16
22
24


Rubber adhesion
B
A
A


Results of differential


scanning calorimetry


Heat-of-reaction peak





temp. (° C.)


Analysis by scanning


electron microscope-X-ray


analyzer


Sulfur content in adhesive





composition layer






Component A




*1 to *3Methacrylate-grafted polybutadiene




*4Methacrylate-terminated polybutadiene




Component D




Monofunctional compound




*8Tetrahydrofuryl monoacrylate




*9Isooctyl acrylate




*10Phenoxypolyethylene glycol monoacrylate




Polyfunctional compound




*11Polypropylene glycol dimethacrylate




*12Polypropylene glycol diacrylate




Component E




*13Ethoxylated bisphenol A dimethacrylate




*14Ethoxylated bisphenol A diacrylate




*15Ethoxylated bisphenol A diacrylate




*16Ethoxylated bisphenol F diacrylate




Component B




*25Aliphatic polyamine




*26Modified aliphatic polyamine




Component C or F




*17Pentaerythritol polyethoxyacrylate




*18 and *19Pentaerythritol polypropoxyacrylate




*20Pentaerythritol polyacrylate




*21dipentaerythritol polyacrylate




Epoxy compound




*6Epoxy novolak acrylate




High-molecular filler




*5Amine-modified acrylonitrile butadiene copolymer




*7Copolymer of isobutylene and maleic anhydride




*27Thermoplastic high-molecular polyester resin




Inorganic filler




*22Montmorillonite clay




Photoinitiator




*232,4-diethylthioxanthone




*24Isoamyl p-dimethylaminobenzoate









INDUSTRIAL APPLICABILITY

[0112] In the process of bonding a rubber to an adherend through the adhesive composition according to the present invention, the adhesive composition is irradiated with ultraviolet light or radiation and then the vulcanization is preformed while bringing an unvulcanized rubber into press-contact with the adhesive composition, thereby achieving an excellent adhesion between the rubber and the adherend. Accordingly, the present invention is useful for the production of a rubber-reinforcing material or a rubber article which require a good adhesion between the rubber and the adherend.


Claims
  • 1. An adhesive composition comprising (A) a conjugated diene polymer having a weight-average molecular weight of 500 to 100,000 and (B) an electron pair-donating basic compound.
  • 2. The adhesive composition according to claim 1, wherein the electron pair-donating basic compound B is contained in an amount of 0.2 to 50 parts by weight based on 100 parts by weight of the conjugated diene polymer A.
  • 3. The adhesive composition according to claim 1 or claim 2, wherein a mixture comprising 100 parts by weight of the adhesive composition and 3 parts by weight of sulfur shows a heat-of-reaction curve in which a peak of reaction heat attributable to a vulcanization reaction is observed in a temperature region of 190° C. or lower when measured at a temperature rise rate of 5° C./min by a differential scanning calorimeter, said peak being not observed in a heat-of-reaction curve for a mixture comprising 100 parts by weight of the conjugated diene polymer A and 3 parts by weight of sulfur as measured under the same conditions as above.
  • 4. The adhesive composition according to any one of claims 1 to 3, wherein when a composite that is prepared by bonding the adhesive composition and a sulfur-containing adherend rubber mixture is measured for a count of fluorescent X-ray from sulfur atom in a cross section parpendicular to a bonding surface by using an electron microscope and an X-ray analyzer, a count due to sulfur atom in an adhesive layer is larger than an average distribution of count due to sulfur atom in the adherend rubber.
  • 5. The adhesive composition according to any one of claims 1 to 4, further comprising (C) a compound having in its molecule three or more functional groups that are cross-linkable by irradiation of ultraviolet light or radiation and/or (D) a compound having in its molecule one or two functional groups that are radically-polymerizable by irradiation of ultraviolet light or radiation.
  • 6. The adhesive composition according to any one of claims 1 to 5, wherein an end group of the conjugated diene polymer A is selected from the group consisting of vinyl group, acryloyl group, methacryloyl group, acryloyloxy group, methacryloyloxy group and allyl group.
  • 7. The adhesive composition according to any one of claims 1 to 5, wherein an end group of the conjugated diene polymer A is acryloyloxy gpr or methacryloyloxy group.
  • 8. The adhesive composition according to any one of claims 1 to 7, wherein the electron pair-donating basic compound B is a compound containing nitrogen atom having a lone pair or a compound capable of forming a compound containing a structure having a lone pair by thermal decomposition.
  • 9. The adhesive composition according to claim 8, wherein the compound containing nitrogen atom having a lone pair is an amine compound or a polymerizable monomer having an aliphatic amine residue or a heterocyclic amine residue and further having a carbon-carbon double bond.
  • 10. The adhesive composition according to claim 9, wherein the amine compound is selected from the group consisting of an aliphatic amine, an aromatic amine, an aldehydeamine, a guanidine compound, a thiouric acid compound and a heterocyclic amine.
  • 11. The adhesive composition according to claim 10, wherein the aliphatic amine is dibutylamine, ethylenediamine or polyethylenepolyamine; the aromatic amine is aniline, m-phenylenediamine or 2,4-toluylenediamine, the aldehydeamine is n-butylaldehydeaniline; the guanidine compound is diphenylguanidine or di-o-tolylguanidine; the thiouric acid compound is thiocarbanilide, diethylthiourea or tetramethylthiourea; and the heterocyclic amine is pyridine or 2-methylimidazole.
  • 12. The adhesive composition according to claim 9, wherein the polymerizable monomer is at least one compound selected from the group consisting of 2-vinylpyridine, 4-vinylpyridine, m-(N,N-dimethylamino)styrene, p-(N,N-dimethylamino)styrene, acrylamide, methacrylamide, N-methylacrylamide, N-isopropylacrylamide, N-n-butylacrylamide, N-n-octylacrylamide, N,N-dimethylacrylamide, 1-vinylimidazole, allylamine, 2,5-distyrylpyridine, 2-dimethylaminoethylmethacrylate, N-vinyl-2-pyrrolidone, 2-vinyl-2H-indazole, 4-diisopropylamino-l-butene, trans-2-butene-1,4-diamine, 2-vinyl-4,6-diamino-1,3,5-triazine, 4-methyl-5-vinylthiazole, N-vinylformamide, N,N-dimethylaminoethyl acrylate, N,N-dimethylaminopropylacrylamide, acryloylmorpholine, and N,N-diethylacrylamide.
  • 13. The adhesive composition according to claim 8, wherein the compound capable of forming a compound containing a structure having a lone pair by thermal decomposition is a vulcanization accelerator.
  • 14. The adhesive composition according to claim 8, wherein the compound capable of forming a compound containing a structure having a lone pair by thermal decomposition is tetramethylthiuram disulfide.
  • 15. The adhesive composition according to claim 5, wherein the compound C is contained in an amount of 30 to 80 parts by weight based on 100 parts by weight of the conjugated diene polymer A.
  • 16. The adhesive composition according to claim 5 or 15, wherein the compound C includes acryloyl- and/or methacryloyl-modified novolak resins.
  • 17. The adhesive composition according to any one of claims 1 to 16, further comprising at least one additive selected from the group consisting of epoxy compounds, inorganic fillers and high-molecular fillers.
  • 18. An ultraviolet- or radiation-curable adhesive composition comprising (A) a conjugated diene polymer having a weight-average molecular weight of 500 to 100,000, (C) a compound having in its molecule three or more functional groups selected from the group consisting of acryloyloxy group, methacryloyloxy group and groups represented by the following formula I:
  • 19. The ultraviolet- or radiation-curable adhesive composition according to claim 18, wherein an end group of the conjugated diene polymer A is selected from the group consisting of vinyl group, acryloyl group, methacryloyl group, acryloyloxy group, methacryloyloxy group and allyl group.
  • 20. The ultraviolet, or radiation-curable adhesive composition according to claim 18, wherein an end group of the conjugated diene polymer A is acryloyloxy group or methacryloyloxy group.
  • 21. The ultraviolet- or radiation-curable adhesive composition according to any one of claims 18 to 20, wherein the compounds C is contained in an amount of 30 to 80 parts by weight and the compound D is contained in an amount 3 to 60 parts by weight, each based on 100 parts by weight of the conjugated diene polymer A.
  • 22. The ultraviolet- or radiation-curing adhesive composition according to any one of claims 18 to 21, further comprising at least one additive selected from the group consisting of epoxy compounds, inorganic fillers, high-molecular fillers and basic compounds.
  • 23. A method for bonding rubber to an adherend, comprising: coating at least a part of a surface of the adherend with the adhesive composition as set forth in any one of claims 1 to 22 to form an adhesive layer; optionally irradiating the adhesive layer with ultraviolet light or radiation; and vulcanizing an unvulcanized rubber while bringing the unvulcanized rubber into press-contact with the adhesive layer, thereby bonding the rubber to the adherend through the adhesive composition.
  • 24. The method according to claim 23, wherein the adhesive composition as set forth in any one of claims 1 to 17 is used to form the adhesive layer, and the vulcanization is performed without irradiating the adhesive layer with ultraviolet light or radiation.
  • 25. The method according to claim 23, wherein the adhesive composition as set forth in any one of claims 18 to 22 is used to form the adhesive layer, and the vulcanization is performed after irradiating the adhesive layer with ultraviolet light or radiation.
  • 26. The method according to claim 25, wherein the radiation is electron beam or gamma ray.
  • 27. The method according to any one of claims 23 to 26, wherein the adherend is made of a plastic material.
  • 28. The method according to claim 27, wherein the plastic material is selected from the group consisting of films, fibers, non-woven fabrics, monofilament cords, multifilament cords and resin molded articles.
  • 29. The method according to any one of claims 23 to 28, wherein the rubber is a diene rubber.
  • 30. The method according to any one of claims 23 to 29, wherein a vulcanizing agent for the rubber is sulfur.
  • 31. The method according to any one of claims 23 to 30, wherein the adhesive layer is formed on an undercoat layer which is formed in advance on at least a part of the surface of the adherend.
  • 32. The method according to claim 31, wherein the adhesive layer is formed after irradiating the undercoat layer with ultraviolet light or radiation.
  • 33. The method according to claim 31 or 32, wherein the undercoat layer is made of an undercoat composition comprising (E) a compound having a bisphenol backbone represented by the following formula II:
  • 34. The method according to claim 33, wherein the undercoat composition contains at least one additive selected from the group consisting of epoxy compounds, inorganic fillers, high-molecular fillers and basic compounds.
  • 35. A rubber-reinforcing material produced by the method as set forth in any one of claims 23 to 34.
  • 36. A rubber article produced using the rubber-reinforcing material as set forth in claim 35.
  • 37. A tire produced using the rubber-reinforcing material as set forth in claim 35.
Priority Claims (1)
Number Date Country Kind
2001-152527 May 2001 JP
PCT Information
Filing Document Filing Date Country Kind
PCT/JP02/04953 5/22/2002 WO