Patent Grant
7825056
The invention relates to zeolitic compositions usable in particular for adsorbing water and, optionally, H2S and/or CO2 present in gas or liquid mixtures.
The use of zeolites, also called molecular sieves, is a common practice in gas purification methods, particularly for selectively removing molecules such as water or H2S. These molecules are thereby adsorbed on these porous solids. The latter are then regenerated by a desorption step generally carried out by passing a hot gas on these solids. During these various steps, side reactions may occur, and this applies in particular to the following reaction when the gas (for example natural gas) contains both H2S and CO2:
H2S+CO2→COS+H2O
Although this reaction is fairly slow, it can be promoted by thermodynamic shift, the water being adsorbed by the zeolite, and by a catalytic effect.
According to P. H. Turnock et al., Proceedings of the Gas Conditioning Conference (1972), 22, B, the rate of formation of COS depends on the type of molecular sieve, particularly on its crystal structure, its composition, the raw materials and binder used, and its method of preparation. Several examples are provided, but without revealing the nature of these zeolites: some zeolites adsorb H2S well, but form a large amount of COS, while others form little COS but adsorb very little H2S.
Cines et al., C.E.P. (August 1976), p 89, shows that under identical conditions, a 13X (or NaX) zeolite forms more COS than a 4A (or NaA) zeolite, which itself forms more than a 5A (or CaA) zeolite. This is corroborated by Lutz W et al., Gas Separation & Purification (1990), Vol 4, p 190 and in Separation Technology, edited by E. F. Vansant (1994), p 143, who show that this reaction is promoted by zeolites exchanged with sodium cation. Fellmuth et al., Zeolites (1987), Vol 7, p 367 states that this is particularly true when the sodium cation content is higher than 60% for X zeolite and higher than 40% for A zeolite.
Trent R. E. et al., Proceedings Laurence Reid Gas Conditioning Conference (1993), 43rd, 239-60, teaches that a 3A (KA) zeolite forms less COS than a 4A (NaA) zeolite.
Although less corrosive and toxic than H2S, COS is undesirable in merchant natural gas, because, in the presence of traces of moisture, it may re-form corrosive H2S. Moreover, in natural gas processing units, when recovering hydrocarbon cuts by liquefaction, COS is found in the propane cut due to its similar boiling point. For example, a gas containing 2% propane must have less than 0.1 ppmv COS in order to have less than 5 ppmv in the liquefied propane. It is therefore necessary to limit the formation of COS during gas processing on zeolite, in order to avoid the need subsequently to reprocess the liquefied propane.
In certain processes, a zeolite is used to remove both the water and H2S present in the gas. A 5A type of molecular sieve is then preferably used, agglomerated with a clay-type binder, thereby promoting the COS formation reaction as little as possible, but its formation is difficult to avoid completely. EP 783.362 in the name of the applicant describes such a technical solution.
Furthermore, units exist in which the gas containing H2S and CO2 is only dehydrated and not desulfurized: this is the case, for example, of reservoirs in which the liquid fraction of the hydrocarbons is produced and not its gaseous fraction. In this case, acid gas is reinjected into the reservoir to enhance oil production by maintaining the pressure in the natural reservoir. In order to reinject the acid gas, however, it must be dehydrated to protect the compressors of the unit against corrosion and/or to transport the gas by pipeline without the risk of forming gas hydrates. In general, no other gases are available on site and dehydrated acid gas is therefore also used to regenerate the adsorbents. In this particular case, the adsorbent is intensively used because of the acidic, hot (>250° C.) and humid atmosphere, conditions favorable both to hydrothermal degradation (loss of the zeolite crystal structure) and to attack of the clay binders (mechanical deterioration). On the conventional synthetic zeolites listed above, these two mechanisms cause a rapid decrease in the adsorption capacity and higher pressure drops, demanding frequent replacement of the feeds.
Some natural zeolites are known for withstanding these conditions better. In the book “Natural zeolites, Ed. L. B. Sand & F. A. Mumpton, 1976”, p 327, R. A. Sheppard stated that mordenite or chabazite can be used to remove H2S, CO2 or water from an acid gas, particularly the Bowie chabazite sold by UCC under the name AW 500. M. W. Ackley et al. (PRAXAIR), Microporous and mesoporous Materials, 61, p 25 (2003) states on p 32 that AW 500 is a chabazite agglomerated with a binder.
To remove traces of water and CO2 present in natural gas, U.S. Pat. No. 4,935,580 uses clinoptilolite. U.S. Pat. No. 5,164,076 teaches that the removal of H2S present in a gas, at temperatures between 150 and 220° C., is more effective with clinoptilolite than with 4A zeolite, the Ba or K exchanged forms of clinoptilolite being preferred because the Na and Ca forms adsorb virtually no H2S. This is corroborated by A. Sirkecioglu et al., Sep. Sci. Technol. 30 (13), p 2747-2762 (1995) which states that all the cationic forms of clinoptilolite adsorb SO2 whereas H2S is equally well adsorbed on the K and H forms, but very little on the Na and Ca forms.
In industrial practice, it is found that clinoptilolite is little used for drying gas because it has much lower adsorption capacities than other zeolites, such as chabazite, for example.
Other applications exist requiring the drying of acid gases, of the pure H2S type or H2S—CO2 mixtures, when the latter are used as reaction gases, for example for the synthesis of mercaptans. For the synthesis of products using such acid gases (for example synthesis of mercaptans) to yield the purest possible products, it is also preferable for the formation of byproducts such as COS to be minimized during the drying of these gases on a zeolite. Such a zeolite must also withstand these particularly severe acidic conditions.
Zeolites are also employed for drying or purifying other chemical species such as alcohols, mercaptans, etc., in which byproducts are not desired. However, experience proves that this may occur for the same reasons as those mentioned for COS, that is, the thermodynamic shift of a reversible reaction by the adsorption of water or H2S formed, combined with a potential catalytic effect of the zeolite. This could lead to the formation of species such as dialkyl ether or dialkyl sulfide by the following reactions:
2ROH→ROR+H2O
or 2RSH→RSR+H2S
The invention relates to zeolitic compositions which do not have the drawbacks mentioned above, that is, which do not promote side reactions, particularly those leading to the formation of COS, when contacted with gas mixtures containing H2S and CO2.
The zeolitic compositions according to the invention comprise:
{circle around (1)} at least one zeolite which can be selected from A, X and/or Y zeolites (which are synthetic zeolites) and/or from zeolites of the chabazite type (which are natural zeolites), regardless of the associated cation or cations on one and/or the other of these zeolites, and {circle around (2)} at least one zeolite of the clinoptilolite type, and regardless of the associated cation or cations, which may be different or not from that or those of the zeolite or zeolites as defined in {circle around (1)}.
Preferably, the zeolite or zeolites as defined in {circle around (1)} accounts for at least 50% and, advantageously, between 70 and 90%, of the total zeolitic mass of the composition of the invention, the zeolite or zeolites as defined in {circle around (2)} accounting for up to 50% and, advantageously, between 10 and 30%, of the total zeolitic mass of said composition.
The zeolitic compositions according to the invention may be in powder form but, preferably, are in the form of beads, extrudates or yarn, and in general, in the form of agglomerates of average particle size distribution generally lower than or equal to several mm.
A further subject of the present invention is a method for obtaining the zeolitic compositions described above.
The zeolitic compositions of the invention in powder form can be prepared simply by intimate mixing of powders of zeolites {circle around (1)} and {circle around (2)}
The zeolitic compositions of the invention can be prepared in the form of agglomerates, by starting with a powdery intimate mixture of zeolites {circle around (1)} and {circle around (2)} which are agglomerated by means known to a person skilled in the art, for example, in the form of beads or extrudates, with or, preferably, without the use of an additional clay binder, the clinoptilolite acting as the binder.
In this case, only a very small amount of additional water is added to the mixture of powders of zeolites {circle around (1)} and {circle around (2)} to form a uniform paste, and optionally, one or more shaping additives, for example, carboxymethylcellulose or lignosulfonate. After this shaping, the zeolitic compositions are then dried, activated by conventional methods of a person skilled in the art.
The various zeolitic phases can be identified by their X-ray spectrum.
The average particle size distribution of these agglomerated zeolitic compositions is generally about 0.4 mm to 5 mm and advantageously between 1 and 3 mm.
The zeolitic compositions of the invention comprising at least chabazite and at least clinoptilolite have the additional advantage of withstanding the acidic conditions particularly well, more specifically in the presence of gases which are both hot (temperature about 200-300° C.) and/or humid (saturated with water) and/or acidic (containing high H2S and/or CO2, contents typically of about several percent). Compared with a chabazite type of zeolite such as AW 500 agglomerated with a clay, they have about 10% greater water adsorption capacity.
The present invention further relates to the use of the zeolitic compositions described above for adsorbing water and, optionally, H2S and/or CO2 present in gas or liquid mixtures, and particularly present in natural gas and in acid gases.
In order to remove both water and H2S from a low acid natural gas (<1% H2S), while preventing the formation of COS, particular use can be made of a zeolitic composition according to the invention based on 5A zeolite and clinoptilolite and/or a zeolitic composition of the invention based on chabazite and clinoptilolite.
To simply remove water from a low acid natural gas (<1% H2S), while preventing the formation of COS, use can be made of any zeolitic composition of the invention, and preferably, a composition according to the invention based on 3A zeolite and clinoptilolite.
In order to remove the water from a high acid natural gas (>1% H2S), or a gas essentially composed of H2S and CO2, while preventing the formation of COS, a composition of the invention based on 3A zeolite and clinoptilolite will be used, and preferably, a composition of the invention based on chabazite and clinoptilolite, for obtaining better resistance to acid gases.
The zeolitic compositions of the invention can also be employed for drying other chemical species such as alcohols, mercaptans, etc., for which byproducts are undesirable. For such applications, it is preferable to use compositions of the invention based on 3A zeolite and clinoptilolite.
In examples 1 to 3 below, the invention is illustrated for the dehydration of an acid gas containing both H2S and CO2. In example 4, the invention is illustrated for the dehydration of an alcohol.
Several zeolites and zeolitic compositions of different quality and from different sources are compared, their main properties being listed in Table 1. All these tested products were used in the form of yarn 1.6 mm in diameter; they were all used after an activation step at 550° C.
The properties of these zeolites were determined by conventional methods. The bulk densities were measured on untamped product. The water adsorption capacities, called H50, were measured by a static method in which the zeolite is placed in a closed chamber for 24 h in equilibrium with a controlled atmosphere with 50% relative humidity at ambient temperature. The water adsorption capacity was recorded by differential weighing.
Unless otherwise indicated, the proportions in the examples are weight proportions.
For reference, 2 commercial zeolites were used, that is, 3A zeolite sold by CECA under the trade name NK 30 consisting of 80% of 3A zeolite (KA, potassium exchange rate=42%) and clay binder, and chabazite-type zeolite sold under the trade name AW 500 by UOP.
The various natural zeolites listed in the above table (chabazites and clinoptilolites) originate from different sources; their properties are listed in Table 2 below.
This test serves to measure the formation of COS during the drying of a natural gas containing both H2S and CO2. The test is performed on a pilot unit which reproduces conditions very similar to industrial operation.
Composition of the gas to be treated:
Column:
Adsorption conditions:
Desorption Conditions:
During the adsorption step, the water content leaving the column is checked by a moisture analyzer of the Panametrics brand and the H2S, CO2 and COS contents are checked by an in-line chromatograph.
The water content is lower than 1 ppmv (detection limit of the instrument) up to the breakthrough which is followed up to a value of 70 ppmv. The COS contents may vary during the adsorption step, particularly because of the change in the water adsorption front in the column. Table 3 below shows the maximum COS values measured during these tests on the various products tested. These values were measured over several cycles, and in all cases at least after two adsorption cycles:
For information, the theoretical maximum COS concentration value obtained if thermodynamic equilibrium is reached without water adsorption (gas phase equilibrium) is calculated at 55 ppmv; this calculation is made using the thermodynamic equilibrium constant K=3.842×10−6 at 43° C. according to the work of E. Terres et al., Angewandte Chemie, 1932, No. 52-53, p 795.
It may be observed that all the conventional adsorbents broadly exceed this latter value, which proves the equilibrium shift by water adsorption. A 3A sieve, even if it does not adsorb H2S and O2, forms up to 300 ppmv of COS, a chabazite agglomerated with a clay binder forms more than 450 ppmv of COS. The same chabazite, but agglomerated with a clinoptilolite in a composition of the invention, forms much less COS: 150 ppmv (CHA-d) or less (CHA-a to CHA-c).
In addition to the H50 values in Table 1 which illustrate the performance of these zeolites and zeolitic compositions tested, and Table 2 showing that a clinoptilolite alone only has a H50 of 9-10, the water adsorption capacities are calculated, expressed as the weight of water adsorbed per unit volume of zeolite, calculated from the curves of peaking water up to the value of 10 ppmv. A mean is calculated on cycles 5 to 25. The results are given in Table 4 below in terms of comparative performance compared with NK30:
It is observed that the chabazites agglomerated with a clay only yield 64-66% of the performance of a 3A zeolite, whereas a composition of the invention (CHA-d) reaches 89% of the performance of 3A zeolite.
The samples of the various adsorbents are unloaded from the pilot column at the level of one of the following 3 zones: gas inlet (E), mid-column (M) and gas outlet (S). Each sample is then characterized according to its mechanical strength and its content of fines (<0.8 mm) formed. The mechanical strength results are expressed as a % of the value of the original product. They are listed in Table 5 below:
It is found that 3A zeolite deteriorates more rapidly mechanically; the pilot tests also had to be stopped due to an excessive increase in the pressure drop, preventing the continuation of the tests. It may be observed that the results are particularly dramatic in the gas inlet zone (E), which corresponds to the zone most saturated with wet (and acid) hot gas during the countercurrent thermal desorption step.
The CHA-d of the invention displays similar behavior to the CHA-i agglomerated with clay, that is, without faster deterioration of its mechanical strength. On these two products, the tests were continued after reloading in the pilot column without any problem of pressure drop increase.
The reactivity of a commercial NK30 sieve described in Table 1 is compared with a zeolitic composition of the invention consisting of 80% 3A zeolite and 20% clinoptilolite a, of which the properties are listed in Table 2.
80 g of adsorbent are placed in a tube-in-shell reactor 63 cm in height and 1.5 cm in diameter. The reactor is heated under nitrogen at atmospheric pressure so that the temperature in the adsorbent bed reaches 130° C. A flow of 135 ml/h of liquid is sent, consisting of 96% ethanol and 4% water. This liquid evaporates in the column; the water is adsorbed on the solid, causing slight heating thereof by about 30° C. At the reactor outlet, a condenser cooled to −35° C. is placed to properly trap all the volatile compounds that may have formed in contact with the solid. Samples are taken per fraction and analyzed by gas chromatography coupled with mass spectrometry. The products detected are essentially acetaldehyde, diethyl ether and ethylene oxide.
The impurities contents (expressed in mg/l) obtained
* for the commercial NK30 sieve are listed in Table 6 below:
* and in Table 7 below for the 3A sieve agglomerated with 20% clinoptilolite according to the invention:
| Number | Date | Country | Kind |
|---|---|---|---|
| 04 03371 | Mar 2004 | FR | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/FR2005/000780 | 3/30/2005 | WO | 00 | 9/29/2006 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2005/094985 | 10/13/2005 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3411888 | Drost et al. | Nov 1968 | A |
| 4329160 | Sherman | May 1982 | A |
| 4925460 | Coe et al. | May 1990 | A |
| 4935580 | Chao et al. | Jun 1990 | A |
| 4964889 | Chao | Oct 1990 | A |
| 5164076 | Zarchy et al. | Nov 1992 | A |
| 5587003 | Bulow et al. | Dec 1996 | A |
| 5938819 | Seery | Aug 1999 | A |
| 6284021 | Lu et al. | Sep 2001 | B1 |
| 6638340 | Kanazirev et al. | Oct 2003 | B1 |
| 7300899 | Weston et al. | Nov 2007 | B2 |
| 20020014457 | Smith et al. | Feb 2002 | A1 |
| Number | Date | Country |
|---|---|---|
| 1179461 | Apr 1998 | CN |
| 9710314 | Mar 1997 | WO |
| 03053546 | Jul 2003 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20070214959 A1 | Sep 2007 | US |